    • 专利摘要:

    公开号:WO1984000762A1
    申请号:PCT/EP1983/000214
    申请日:1983-08-05
    公开日:1984-03-01
    发明作者:Peter James Corbett；Robert William Rance
    申请人:Dow Chemical Rheinwerk Gmbh；
    IPC主号:C08F2-00
    专利说明:
    [0001] AQUEOUS DISPERSIONS COMPRISING COLLOIDAL SIZED PARTICLES OF A POLYMER AND AN ADDITIVE AND A METHOD FOR THEIR PREPARATION.
    [0002] The present invention relates to an aqueous, polymer, dispersion and a method for the preparation of an aqueous dispersion, particuiar. y to a method for preparing an aqueous polymer dispersion comprising colloidal size polymer particles and a dispersible, water-insoluble additive and to an aqueous dispersion comprising colloidal size polymer particles and colloidal size particles comprising a water-insoluble antioxidant.
    [0003] Aqueous dispersions of colloidal size, polymer particles have a variety of commercial applications such as coatings, e.g., paints or films, adhesives, and the like.
    [0004] Conventionally , the aqueous polymer dispersions are prepared by admixing an emulsion polymeri zabl e monomer, a surfactant and a water soluble polymerization initiator in water and sub sequently subjecting the admixture to conditions sufficient to polymerize the monomer, thereby forming an aqueous dispersion of the resulting polymer particles (often, such dispersions are referred to as latexes). To facilitate the formation of polymer particles having a uniform size, often, the surfactant is added initially and then in increments during the polymerization. AIternatively, a polymerization seed i.e. small particles of generally less than about 800 Å, which serve as a l oc i for subsequent polymerization is em pl oyed.
    [0005] In general, the resulting latex, as prepared, does not exhibit the required properties for subsequent end use application and one or more additive materials are post-added to the latex tu impart desirable properties thereto. For example, for oxidation sensitive polymers, an anti-oxidant is commonly added to the latex to improve the latex's heat and oxygen stability. Other common additives post-added to a latex include plasticizers , pigments, coalescents, flame retardants, and the like. Since many of these additives are not soluble in water, to uniformly disperse the additive throughout the latex, prior to its addition to the latex, it is generally prepared as a dispersion in water using mechanical means. Unfortunately, the mechanical means required to form an aqueous dispersion of small particles of the additive are generally energy and capital intensive. Moreover, the additive particles formed by mechanical dispersion are relatively large (e.g. , 4 μ or larger) and do not form a stable dispersion. Therefore, upon storage, the additive particles tend to separate, i.e., settle or cream, from the remainder of the latex, thereby causing handling problems and resulting in a non-uniform dispersion.
    [0006] Methods for incorporating an additive in a latex other than by post-addition have been proposed. For example, U.S. Patent 2,700,026 discloses the preparation of a latex having a plasticizer incorporated therein by dispersing a monomer-plasticizer solution in an aqueous medium to form an oil-in-water emulsion and subsequently polymerizing the monomer. Similarly, U.S. Patent 3,228,830 discloses a method for incorporating a biocidally active, organic derivative of 10-phenoxarsine in a latex. The method comprises forming a solution of a polymerizabl e monomer and the active organic derivative, subseqjently dispersing the monomer/derivative solution in an aqueous liquid containing the necessary polymerization aids and then polymerizing the monomer. Unfortunately, the dispersed oil/monomer droplets are of an undesirably large size (e.g. , from 0.5 to 1.5 microns) which often de! eteriously affects the properties and the stability of the resulting product. Another method for preparing a latex having dispersed particles of an additive distributed therethrough is disclosed in U.S. Patent 3,316,199. In said method, a heated solution (e.g., 50-85°C) of a polymerizabl e monomer, a poly (α-olefin) pl as t i ci ze r and, optionally, a surfactant, is dispersed in a heated, aqueous solution of an emulsifier. The resulting dispersion is then subjected to a high shear mixer, subse quently added to an aqueous solution containing a catalyst and polymerization subsequently conducted. Unfortunately, the disclosed method requires a variety of pre-heating steps and an energy intensive, mechanical homogeni zation .
    [0007] An alternative method for preparing a latex is disclosed in British Patent Specification 1527,312 of J. Ugelstad. In said method, an aqueous mixture containing an emulsifier (surfactant) and water-insoluble solvent for the monomers to be polymerized is homogenized. The monomer to be polymerized and a water-soluble polymerization initiator are added to the resulting homogenized mixture and polymerization subsequently conducted. In said method, the water-insoluble solvent imbibes the polymerizable monomer and serves as the Site for polymerization. In such manner, the solvent, which solvent can be a comonomer or an additive (various plasticizers and an epoxy stabilizer for vinyl Chloride polymers being specifically disclosed) becomes an integral part of the final latex. Unfortunately, the described process still requires an energy intensive, mechanical homogenization or dispersion step. Moreover, without using sophisticated and expensive equipment, the resulting latex particles are generally relatively large particles which often results in a dacrease in the stability and a change in the properties in the products, e.g., films, prepared therefrom.
    [0008] In View of the aforementioned deficiencies , it remains highly desirable to prepare a latex having an additive dispersed therethrough, which additive is not susceptible to sedimentation or creaming, without the need for a mechanical dispersion Operation. Accordingly, in one aspect the present invention is a method for the preparation of a polymer composition comprising an aqueous dispersion of colloidal size polymer particles and an additive. Said method comprises the step of polymerizing an emulsion polymerizable monomer in an aqueous polymerization medium, said polymerization being conducted such that at least a po'rtion of the polymerization occurs in the presence of a water-insoluble additive, said water-insoluble additive having been added to an aqueous liquid which forms all or part of the aqueous polymerization medium as an inherently dispersible solution of the additive and a surfactant. By the term "inherently dispersible" is meant that the additive/surfactant solution can be dispersed in water as colloidal size particles having a size of less than 1000 Å without requiring significant agitation, i.e., a drop of the solution, when deposited on the surface of water contained by a beaker or other suitable Container, becomes dispersed, without agitation, as colloidal size particles. Therefore, by properly selecting the type and amount of surfactant, the additive can be readily dispersed using ordinary mixing, i.e., a separate homogeni zation step is not required, to form particles of a relatively smal 1 size, i.e., less then 1000 A. In another aspect, the additive comprises a waterinsoluble antioxidant and the present invention is a stable polymer composi tion comprising an aqueous dispersion of (a) colloidal size polymer particles and (b) additive particles comprising a water-insoluble antioxidant, said additive particles being separate and distinct from the polymer particles with a particle size of less than 1000 A and being stable against Sedimentation and creaming.
    [0009] Surprisingly, emulsion polymeri zable monomers can unexpectedly be polymerized in the presence of the smal 1 size dispers additive particles to form a synthetic polymer emulsion (latex) having a polymer particle of a desirably small size (e.g. , from 1000-4000 8) without the presence of the additive si gni fi cantly and adversely affecting the polymerization reaction. In the resulting emulsion, the additive can be (1) uni formly distributed throughout the resulting polymer latex as separate and distinct, stable particles dispersed throughout the aqueous phase, (2) as an integral part of the resulting polymer particles or (3) as a combination thereof (i .e. , a portion existing as separate and distinct particles and a portion exis ting as an integral part of the polymer particles), thereby imparting the desired properties to the latex and/or products prepared therefrom.
    [0010] For example, a latex comprising an antioxidant can be prepared with the antioxidant being uniformly dispersed throughout the aqueous phase of the resulting emulsion as separate and distinct particles of an average particle size of less than 1000 Å. AIternatively, additives such as organic pigments or dyes become an integral part of the polymer particles of the resulting latex.
    [0011] The resulting polymer compositions are unexpectedly stable when compared to a latex composition in which the additive has been mechanically homogenized and post-added thereto. In addition, since the additive is uniformly distributed through the polymer composition, the polymer composition exhibits desirable properties.
    [0012] The monomers employed in the practice of the present invention are general ly those monomers capable of being polymerized using emulsion polymerization techniques. Such monomers are well known in the art and reference is made thereto for the purposes of this invention. Merely for the purposes of illustration, reference is made to Polymer Processes, edited by Calvin E. Schildknecht, published in 1956 by Interscience Publishers, Incorporated, New York, Chapter IV, "Polymerization in Emulsions" By H. Leverne Williams. In Table II on pages 122-133 of Schildknecht are listed diverse kinds of monomers which can be emulsions polymerized alone (homopolymers) or in mixtures (copolymers) to form aqueous dispersions of colloidal sized, polymer particles (said dispersions commonly being referred to as latexes) which dispersions can be employed in the practice of this invention. Representative polymers useful herein include those derived from the monovinylidene aromatics such as styrene, α-methyl styrene and the like; esters of α,β-ethylenically unsaturated esters of a carboxylic acid such as ethylacryl ate and methyl methacrylate; alkadienes such as 1 ,3-conjugated diene, e.g., butadiene or isoprene; vinyl esters of an unsaturated carboxyl ic acid such as vinyl acetate and mixtures of one or more such monomers. Also of interest are polymers derived from one or more emulsion polymerizabl e monomers with a monomer which is not normally homopolymerizabl e using emulsion polymerization techniques such as an α,β -ethyl enically unsaturated carboxylic acid, e.g. , acrylic acid; or an unsaturated nitrile, e.g., acry lonitri 1 e. Of particuiar interest herein are the polymers derived from the monovinylidene aromatics, particularly styrene; the esters of an unsaturated carboxylic acid, particularly ethylacrylate and methylmethacryl ate; and the alkadienes, particularly, 1,3 butadiene, with copolymers of these monomers, particularly copolymers of a monovinylidene , preferably styrene, and an alkadiene, preferably
    [0013] 1,3 butadiene, being most preferred.
    [0014] The additives suitably employed in the practice of the present invention are water-insoluble, but water dispersable materials. By the term "water-insoluble" it is meant, that, at the concentrations employed, at least a portion of the additive does not form a true solution in water, i.e., individual molecules of the additive are not dispersed throughout the water. Preferably, essentially none of the additives is soluble in water, with said additive having a water solubility of less than 0.1 gram (g) per liter (1) of water at 25° C, more preferably a water solubility of less than 0.05 g/l water at 25° C. The term "water dispersible" means that the additive is capable of being dispersed in an aqueous liquid as colloidal size particles and is meant to include those materials which require the use of a dispersing aid, e.g., surfactant, to form such dispersion, as well as those materials which can be dispersed in water or other aqueous liquid without the need for a dispersing aid. The aqueous liquid can be water (including alkaline or acid aqueous Solutions or aqueous salt Solutions) or a solution of water and a water miscible liquid, preferably a polar liquid such as a Tower alkanol, e.g., methanol , ethanol or propanol, a Tower ketone, e.g., acetone or methyl ethyl ketone; an ether such as diethyl ether; and the like.
    [0015] Dispersible, water-insoluble additives commonly added to a latex or other polymeric composi ti ons , usually at low concentrations, to preform a specific function or alter the properties of the latex and/or product prepared therefrom, are often advantageousTy employed herein. Representati ve of such materials are antioxi dants . As used herein, the term "antioxidant" refers generally to a material which is capable of retarding the degradation of a polymer due to its reaction with oxygen such as by the reaction with the peroxy radicals formed by the reaction of the polymer with oxygen to form a stable (i.e., unreactive) moiety-as well as to a material which is capable of measurably reducing the rate of polymerization or terminating polymer chain growth. Represeutati ve antioxidants include substituted phenols such as styrenated phenol , halo- substituted phenols and bisphenols, the alkyl substituted phenols and bisphenols including the alkylated p-cresols such as 2,6 di-tert butyl-p cresol , alkylated styrenated phenol , 6-tert butyl 2,4-dimethyl phenol , 4,4-butyl idene-bis (6-tert butyl -m-cresol), aryl substituted phenols, blends of the alkyl-and aryl substituted phenols and the like; nitrogen containing phenolic derivatives and aryl amines such as N,N-dicyclohexyl-p-phenylenediamine, 4,4-diaminodiphenyl methane, alkyl-aryl -p-phenylenedf amines and the like; quinones such as 2 ,5-di-tert-butylquinol , thiourea; tributyl thiourea and the like. Mixtures of two or more antioxidants can also advantageously be employed. Generally preferred antioxidants include the water-insoluble substituted phenols and bisphenols, including blends of the alkyl and aryl-substituted phenols, more particularly the alkylated-p-cresols ; and the aryl amines, with the alkyl ated-p-cresol s being the most preferred antioxidant employed herein. Other additives include pigments, dyes or colorants such as anthraquinone , azo and xanthane dyes and organic pigments such as diazo pigments and quinocridoπe; fungicides such as chlorinated and nitrated benzenes and synthetic fungicides such as oxathine and pyrimidines; plasticizers such as dioctyl phtalate; coalescing aids, UV absorbers and the like. In addition, other dispersible, water-insoluble materials not normally in corporated within a polymer latex composition such as pesticides, e.g., cypermethrin; pharmaceutics and the like can also be employed as the dispersed water-insoluble additive.
    [0016] The additive employed in the practice of the present invention is dependent on a variety of factors, particularly, the desired properties of the final polymer composition and/or the products prepared therefrom. Specifically, if antioxidant properties are desired, an antioxidant in employed. AI ternati vely , the polymer composition can be prepared using two or more additives. For example, both an antioxidant and dye are employed to prepare a tinted latex exhibiting antioxidant properties.. In general , the method of the present invention is particularly advaπtageous in preparing a polymer composition having an antioxidant, particularly an alkylated-p-cresol or a pigment, dye or color incorporated herein.
    [0017] The additives are employed in an effective amount, i.e. , an amount sufficient to impart the desired properties to the finished latex. Such conceπtrations will vary depeπding on a variety of factors including the specific additive employed and the desired properties of the polymeric composition and/ or products prepared therefrom and is readily determined by a skilled artisan. In general , the additive will advantageously be employed in amounts varying from 0.01 to 20, preferably 0.1 to 5, weight percent based on the total weight of the polymer. In the practice of the present invention, the additive is admixed with a surfactant to form an inherently dispersible solution. If more than one additive is employed (e.g. , an anti-oxidant and a pigment) the two additives and the surfactant are admixed, if possible, to form one inherently dispersible solution or, al ternatively, an inherently dispersible, addivitve/surfactant solution is prepared from each additive. The term surfactant is used conventional ly herein and is intended to mean any surface active agent which reduces surface tension when dissolved in water or an aqueous solution or which reduces interfacial tension between two Tiquids or between a liquid and a solid. IncTuded within said terms are those compounds conventi onally called detergents, wetting agents and emulsifiers. Illustrative examples of such surfactants are those presented in McCutcheon's "Detergents and Emulsifiers" edited by J . W . McCutcheon, published in 1976 by John W. McCutcheon, Inc. , Morristown, N.J.
    [0018] The surfactants most advantageously employed in preparing the additive dispersions are dependent on a variety of factors including the specific additive employed and the method by which the polymeric latex is to be prepared, particularly the surfactant employed in the preparation of the latex. Specifically, the surfactant used in the preparation of the additive dispersion is necessarly compatible with the surfactant and other polymerization aids employed in the latex polymerization. Although any anionic, cationic, nonionic or amphoteric surfactant or compatible mixtures thereof can be employed, in general , anionic or nonionic surfactants are employed, with the preferred surfactants or surfactant combinations employed in the preparation of the additive dispersion containing a nonionic surfactant. Representative nonionic surfactants include the reaction product of an alkylene oxide particularly ethylene oxide or a combination of ethylene oxide and propylene oxide with alkylated phenols or long chain, e.g., about 6 to about 20 carbon atoms , fatty alcohols, fatty acids, alkyl mercaptans and primary amines; monoesters, e.g., the reaction product of polyethylene glycol with a longchain carboxylic acid with polyglycol ethers of polyhydric alcohol . Preferred nonionic surfactants possess an HLB value of at least 5 and less than 25, more preferably less than 20. Surfactant combinations of one or more nonionic surfactant or one or more nonionic surfactant with one or more anionic surfactant such as calcium dodecyl benzene sulfonate can also preferably be employed.
    [0019] The surfactant/additive solution is prepared using amounts of surfactant and additive such that the additive can be dispersed in water, without significant agitation, as a dispersion of colloidal size particles having a particle size of less than 1000 Å. As used therein, the particle size is the number average particle size as determinated by microscopic techniques, e.g., wet cell techniques using a transmission electron microscope at a magnification of at least 50,000 X. Since such methods are. often inconclusive and time consuming, for the purposes of this invention, the dispersed additive particles are presumed to have a number average particle size of less than 1000 A when essentially all, i.e., at least about 90 weight percent of the additive, can be separated from an aqueous dispersion containing same using con ventional serum replacement techniques such as exeenpli fied in Example I using a filter pore size of 1000 Å.
    [0020] Although the amounts of surfactant and additive will generally vary depending primarily on the specific additive and surfactant employed, in general, the surfactant/addi tive solution will contain from 40 to 99, preferably from 45 to 90, weight percent of surfactant ard from 1 to 60, preferably from 10 to 55 weight percent of additive, said weight percents being based on the total weight of the surfactant and additive. In one embodiment for preparing the polymer composition, an aqueous dispersion of the colloidal size, particles comprising the additive or additives is employed as the aqueous polymerization medium. In said method, the aqueous dispersion of the additive particles will contain the polymerization aids necessary to con duct the emulsion polymerization. The monomers to be polymerized are subsequently added using batchwise, incremental (i.e., added as two or more shots during the polymerization process) or con tinuous addition to the polymerization medium and polymerization subsequently conducted. In a second embodiment, but less preferably, the additive is added coincident with, but separate from, or subsequent to the addition of the monomers to be polymerized but prior to complete polymerization to an aqueous polymerization medium containing the necessary polymerization aids. In still another embodiment, a portion of the additive is dispersed in the polymerization medium prior to the monomer and a portion thereof added coincident with, but separate from, the monomer using batchwise, incremental or continuous addition, with continuous addition beginning subsequent to initial polymerization being preferred. Addition of the additive is then stopped previous to complete polymerization of the monomer. During the addition of the monomers and the additive, the polymerization reaction medium is advantageously maintained as an essentially uniform mixture, typically, by mild agitation. If more than one additive is employed, all or any number of the additives can be dispersed in the aqueous polymerization medium coincident with the monomers. Specifically , one or more additive can be in the aqueous polymerization mixture prior to the addition of the monomer thereto with one or more other additive being added to the polymerization medium coincident with the monomers.
    [0021] The polymerization of the polymerizabl e monomers is conducte at conditions sufficient to polymerize the monomers and form a stable polymer dispersion. The stability of the polymeric dispersion is determined by subjecting the polymeric dispersion, as a 10 weight percent, solids level to extended storage in a closed Container, without agitation, and periodically examining the Container for a distinct bottom or top layer. Although the stability of the dispersion will vary de pending upon the additive and its particle size, in general, the dispersion is presumed to be stable if no significant Sedimentation or creaming is observed after the dispersion has been stored for a two week period. In many instances, no significant Sedimentation or creaming in the dispersion of this invention is observed after storage periods of up to one month, preferably two months or more. By way of comparison, significant Separation is often exhibited by a polymeric dispersion within the first week of storage and generally within two weeks or less, when the polymeric dispersion is prepared by post-adding an aqueous dispersion of the additive prepared using conventional mechanical homogenization techniques which result in particles having a size of 3000 Å or more.
    [0022] During said polymerization, if the additive is an antioxidant material the additive will generally remain as separate and distinct particles dispersed throughout the aqueous medium of the polymeric composition. Such separate and distinct particles are evidenced by (1) the observance of distinct particles separate from the polymer latex particles (except for a possible surface attraction between the additive and the latex polymer particles) under magnification of at least 50,000 x using wet cell type techniques or (2) the ability to separate the additive particles from the latex particles using serum replacement techniques such as described in Example 1. AI ternatively , using other additives such as iorganic soluble pigments, dyes or plasticizers, the additive is generally soluble with the monomers and/or resulting polymer snd becomes an integral portion of the particle comprising the resulting polymer. However, additive particles formed upon dispersing the additive surfactant solution are relatively small, (i.e., less than 1000 A, preferably less than 700 Å) polymej particles of a desirable small size, e.g., from 1500 to 3000 A are easily prepared. In general, the polymerization is conducted in the presence of polymerization aids conventionally employed heretofore in the emulsion polymerization preparation of polymers provided they are compatible with the additive and the surfactant used in p re pa ri ng the additive/surfactant solution. Such polymerization aids are well known in the art and include emulsifiers (in addition to any surfactant employed in preparing the aqueous dispersion) and polymerization initiators. Preferred polymerization initiators include the conventional chemical initiators useful .as free radical gene rators such as the azo compounds, e.g., azob isizobutyroni trile; bisulfites; persulfates; peroxygen compounds, e.g., propyl per carbonate and benzoyl peroxide; and the like. The initiators are employed in an effective amount, i.e., an amount sufficient to cause polymerization. This effective amount is dependent primarly on the monomers being polymerized but generally varies from 0.05 to 5, preferably from 0.1 to 3, weight percent, said weight percent being based on the total weight of the polymeri zabl e monomer em ployed.
    [0023] The emulsifiers employed in preparing the latex polymer particles are advantageously compatible, emulsifiers (including anionic, nonionic cationic or amphoteric surfactants or mixtures thereof) employed heretofore in emulsion polymerization processes. An anionic surfactant or mixtures of one or more nonionic surfactant with an anionic surfactant are often preferably employed. Representative anionic surfactants includes sodium lauryl sulfate, sodium dioctyl sulfo succinate, dephenyl oxide sulfonate, and the like. A representative cationic surfactant is hexadecyl tri methyl ammonium bromide and representative nonionic surfactants include the alkoxylated phenols as described herei nbefore. The amount of surfactant most advantageously employed is dependent on a variet of factors and easily determined by one skilled in the art. In general, from 0.1 to 5, preferably from 0.2 to 3 weight percent, of the emulsifiers are employed (this is in addition to any surfactant employed in preparing the aqueous additive dispersion) based on the weight of the polymeri zabl e monomer. Optionally, other polymerization aids such as chain transfer agents, chelating agents, acids, bases or salts to provide a described pH or possibly buffered system and the like may also be employed. Depending typically on the polymerization techniques employed, any or all the additives, including any portion thereof can be added to the polymerization medium prior to the polymerizable monomers or coincident therewith and the techniques most advantageously employed are easily determined by a person skilled in the art.
    [0024] The polymerization is conducted using temperatures sufficiently high to initiate and continue polymerization of the monomer or monomers being polymerized but less than that temperature which causes des tabilization of the additive dispersion or at which the polymer decomposition exceeds the polymer formation rate. In general, the polymerization temperature will vary from 50 to 120° C. At these temperatures, polymerization usually requires from 3 to 10 hours. Following completion of polymerization, the resulting polymer composition is a stable, uniform aqueous dispersion of polymer particles and additive particles. The compositions can be employed as prepared or be subsequently mixed with various adjuncts such as plasticizers, fillers such as fibers, coalescing agents, reactive resins, and the like.
    [0025] Adjuncts conventionally employed and their effects are well known in the art and reference is made thereto for the purposes of the present invention.
    [0026] The following examples are set forth to illustrate the invention and shoüld not be employed to limit its. scope. In the examples, all parts and percentages are by weight unless otherwise specified.
    [0027] Examgle No. 1
    [0028] An additive surf actant/solution is prepared by admixing. (1)10 parts of an antioxidant blend comprising (a) 1.4 parts of a partially hindered phenol sold as Wingstay L by Goodyear Tire and Rubber Co. and (b) 8.6 parts of di tridecyl thiodipropionate (DTDTDP) and (2) 20 parts of a surfactant blend comprising (a) 13.3 parts of a blend comprising the calcium salt of alkyl ben zene sulfonic acid, a (p-nonylphenol hydroxy poly ( oxyethylene) ) and a block polymer of propylene and ethylene oxide sold as Tensiofix 7416 by Tensia Co. and (b) 6.7 parts of octylphenol polyethoxyethanol sold as Triton X 165 by Rohm and Haas.
    [0029] To a suitably sized flask equipped with an agitator, heating and cooling means, thermometer and addition funnels is added 655 parts of water, 30 parts of the additive/surfactant solution, 0.1 parts of a chelating agent, 2.2 parts of a diphenyl oxide sulfonate surfactant sold as Dowfax 2Al by The Dow Chemical Company, 30 parts of a chain transfer agent and 20 parts of an unsaturated carboxylic acid. A monomer feed comprising 480 parts of styrene, 500 parts of 1.3-butadiene and 80 parts of a chain transfer agent is continuously added to the flask over a 4.25 hour period. Simultaneous with said addition, an aqueous feed comprising 335 parts water, 0.1 parts of a chelating agent, 33.8 parts of Dowfax 2A1 and 1.1 parts of sodium hydroxide is continuously added to the flask. Following the addition of both streams, a mixture of 17.2 parts of deionized water and 0.7 parts of a persulfate free-radical initiator is added as a shot to the flask. During the addition of the aqueous and monomer feeds and for an additional 2 hour period, the contents of the flask are continuously agitated and maintained at a temperature of 90º C. At the end of this period, the polymerization is essentially complete and the flask cooled to ambient temperatures, i.e., a temperature from 18 - 25° C.
    [0030] The resulting dispersion is subjected to a steam distillation Operation to remove any residual unpolymeri zed monomers and the pH of the aqueous dispersion adjusted to 9. Upon analysis resulting dispersion is found to be 45.5 percent solids and the dispersed polymer particles contained therein to have a number average particle size of 1,430 Å as determined by conventional light scattering techniques. The composition is designated in Sample No. 1. To ascertain whether the antioxidant particles remained separate and distinct during the polymerization process, a 10 part portion of the resulting dispersion is admixed with 90 parts of distilled water. The diluted dispersion is subsequently placed in a serum exchange cell of 400 millimeters (ml) capacity. The cell comprises a cylindrical polycarbonate reservoir held be tween two polyacetal plates. The cell is fitted with a Nuclepore membrane filter with 1000 A diameter holes. The filtration membrane is supported on the bottom of the cell. A Teflon coated stirring bar rotates close to the membrane surface to prevent clogging of the pores by the polymer particles and to assure a steady flow rate over long periods of time. A total of 10 exchange volumes of distilled water are passed continuously through the membrane over a 48 hour period. Samples of the dilute dispersion are subjected to differential thermal analyses prior to , during and subsequent to the serum exchange procedure. Finally, waste material, collected on the membrane is also subjected to differential thermal analysis. The initial dilute dispersion shows a retention time as measured by the differential thermal analysis techniques of 41 minutes. After 900 ml of distilled water have passed through the cell, the dilute dispersion exhibits a retention time of about 30 minutes. After 1500 ml of distilled water have passed through the cell , the dilute dispersion shows a retention time of only 8 minutes with degradation beginning immediately. After 4000 ml of d i s ti l l ed water have passed through the cell, the retention time is only 4 minutes with degradation also beginning immediately. Essentially no latex particles are found to pass through the filter. As evidenced by the fact that the antioxidant protection is slöwly being diminished., with essentially no protection being detected after ΪO exchange volumes (4000 ml) the antioxidant and any other additives whi ch provide antioxidant protection are clearly being progressive! y removed from the dispersion during serum replacement. Therefore, the antioxidant is shown to exist as separate and distinct colloidal sized particles having a particle size of less than 1000 E.
    [0031] In a similar manner, a second polymer composition (Sample No, 2) is prepared except that the antioxi dant/surfactant solution eonsists of 10 parts of an antioxidant blend comprising 1.4 parts of the partially hindered phenol and 8.6 parts of the ditri decylthiodipropionate and 20 parts of a nonylphenol ethoxylate sold as Dowfax 9N10 by The Dow Chemical Company.
    [0032] Comgaratiye Example: For purposes of comparison, an aqueous dispersion of a polymer which dispersion contains no antioxidant particles is prepared using the same monomeric constituents as employed in the preparation of Samples Nos. 1 and 2 and employing conventional emulsion polymerization techniques. An aqueous dispersion of 10 parts of an antioxidant blend comprising 1.4 parts of the hindered phenol and 8.6 parts of DTDTDP is prepared by mechanically homogenizing the antioxidant blend in 7.4 parts water containing 0.7 parts of a sodium lauryl sulfate surfactant. The resulting dispersion comprises antioxidant particles having a number average particle size of about 4000 Å. A 3.2 part portion of this mechanically homogenized dispersion is added to a 100 part portion of the polymer dispersion to form a conventi onal , antioxidant containing, polymer dispersion. (Sample No. C).
    [0033] Each of the resulting polymer compositions are evaluated for stability, i.e. , creaming or sedimentati on of the antioxidant particles, antioxidant protection, dry and wet tensile strains, elongation, swelling index and heat ceiling properties. The results of this testing are set forth in Table 1.
    [0034]
    [0035] As evidenced by the data recorded in Table I, the polymeric compositions of the present invention wherein the polymer is prepared in the presence of an aqueous polymerization medium containing disperse antioxidant particles having a size of less than a 1000 Å, exhibit surprisingly better stability and antioxidant properties than a polymer composition wherein the antioxidant is dispersed by mechanical homogeni zation techniques and subsequently added to the finished polymer latex composition. In addition, the other latex properties are essentially equivalent.
    [0036] Example No. 2
    [0037] In a manner similar to the preparation of Sample No. 1, various polymer compositions are prepared in the presence of an aqueous dispersion of colloidal sized antioxidant particles, said aqueous dispersion being prepared using the various antioxidant/surfactant Solutions set forth in Table II. The surfactants used in conducting the emulsion polymerization, as well as the percent solids and the polymer particle size of the resulting polymer composition are also presented in Table II.
    [0038]
    [0039] As evidenced by the data presented in Table II, the polymerization is not significantly effected by the designated variations in the antioxidant surfactant blend. On further testing of the resulting polymer compositions, all polymer compositions exhibit exceptional stability and antioxidant properties when compared to a polymer composition having an aqueous dispersion of the antioxidant added thereto which aqueous dispersion has been prepared by the mechanical homogeni zation of the antioxidant in an aqueous liquid In addition, upon subsequently testing each of the compositions using serum replacement techniquss, thε dispersed antioxidant par ticles are found to be separate and distinct from the polymer par ticles and to have a particle size of less than 1000 Å.
    [0040] Example 3 An additive/surfactant solution is prepared by admixing 10 parts of an organic soluble pigment sold as Automate Green by Williams and 10 parts of a surfactant blend of 5 parts Tensio fix 7416 and 5 parts of Triton X-165. The additive/surfactant solution is admixed with 655 parts water, 0.1 parts of a chelating agent, 2.2 parts of an emulsifier, 20 parts of an unsaturated carboxylic acid and 30 parts of a chain transfer agent. A monomer feed comprising 480 parts of styrene, 500 parts of 1.3-butadiene and 80 parts of a chain transfer agent is continuously added to the flask over a 4.25 hour period. Simultaneous with said addition,an aqueous feed comprising 333 parts water, 0.1 parts of sodiumhydroxide and 5.6 parts of a free-radical initiator is continuously added to the flask. Following the addition of.both streams, a mixture of 17. 2 parts or oeiomzed water anc 0.7 parts of a periulfate free-radical initiator is added as a shot to the flask. During the 2 hour period, the Contents of the flask are continuously agitated and maintained at a temperature of 90° C. At thε end of this period, the polymerization is essentially complete and the flask cooled to ambient temperatures, i.e., a temperature from 18 - 25° C.
    [0041] The resulting dispersion is subjectεd to a steam distillation Operation to remove any residual uπpolymeri zed monomers and the pH of the aqueous dispersion adjusted to 9. Upon analysis resulting dispersion is found to be 42.9 percent solids and the dispersed polymer particles contained thergin have a desirable number average particle size of only 1680 Å as determined by con ventional light scattering technniques.
    [0042] The resulting polymer dispersion possesses a uniform lightblue color when applied as a film or coating such as to a paper surface or surface of a wood veneer and subsequently dried, the dispersion imparts a green color paper or wood surface.
    [0043] Upon subjecting a portion thereof to a serum replacement technique such as described in Example 1, the pigment is found to comprise an integral part of the disperse particles comprising the polymer due to the fact that there is no Separation of the pigment from the polymer particles.
    [0044] A second portion of the resulting polymer dispersion is diluted to 10 percent solids and s-tored in a closed container at ambient temperatures. No creaming or Sedimentation is found after storage for 2 months.
    [0045] Using the method of this Example, a stable pigmented latex having suitably small size polymer particles is readily prepared without the necessity of post-adding the pigment.
    [0046] Examgle 4
    [0047] In a manner similar to Example 3 except that the additive/surfactant solution comprises 10 parts of diisooctyl phthalate plasticizer and 10 parts of a polyoxyethylene sorbitan monolaurate, a stable, polymer dispersion is prepared. The resulting dispersion has 47.4 weight percent solids and a particle size of 1200 Å. When a portion of the dispersion is diluted to 10 percent solids essentially no settling or creaming is detected after storage of two months. Examgle 5
    [0048] In a manner similar to Example 3 except that the additive/ surfactant solution comprises 10 parts of cypermethrin, a pesticid and 10 parts of a surfactant blend of 5 parts Tensiofix 7416 and 5 parts Triton X-165, a stable polymer dispersion is prepared. The resulting dispersion possesses 45,8 weight percent solids and the disperse, polymer-containing particles are found to have a particle size of 1630 Å. Upon testing using serum replacement techniques, the pesticide is found to be an integral part of the disperse, polymer-containi ng, particles. When a portion of the dispersion is diluted to 10 percent solids, essentially no settling or creaming is detected after storage of two months.
    权利要求:
    ClaimsC L A I M S
    1. A method for preparing a polymer composition comprising an aqueous dispersion of colloidal size polymer particles and an additive, said method compris ing the step of polymerizing an emulsion polymeri zabl e monomer in an aqueous polymeri zation medium, said polymerization being conducted such that at least a portion of the polymerization occurs in the presence of a water-insoluble additive, said water-insoluble additive having been dispersed in an aqueous liquid which forms al l or part of the aqueous polymerization medium as an inherently dispersible solution of the additive and a surfactant.
    2. The method of Claim 1 wherein the solution of the additive and the surfactant comprises from 40 to 99 weight percent surfactant and 1 to 60 weight percent of additive , said weight percents being based on the total weiqht of the additive and surfactant.
    3. The method of Claim 2 wherein the additive/surf actant solution is dispersed in an aqueous polymerization medium and the monomers to be polymerized are subsequently added thereto.
    4. The method of Claim 2 wherein the addi ti ve/surf actant solution is added coincident, but separate from, the monomers to be polymerized.
    5. The method of Claim 2 wherein a portion of the additive/ surfactant solution is dispersed in the aqueous polymerization medium prior to the addition of the monomers thereto and a portion of the additive/surfactant solution is added coincident with, but separate from, the monomers.
    6. The method of Claim 1 wherein the additive is an anti-oxidant and the polymerization is conducted at conditions such that the antioxidant is dispersed throughout the resulting polymer dispersion as separate and distinct particles having a number average particle size of less than 1000 Å.
    7. The method of Claim 1 wherein the additive is a pigment, dye or colorant and the polymerization is conducted at conditions such that it becomes an integral part of the polymercontaining particles.
    8. A polymer composition comprising an aqueous dispersion of (a) colloidal size polymer particles and (b) additive particles comprising a water-insoluble antioxidant, -said additive particles being separate and distinct from the polymer particles with a particle size of less than 1000 A.
    9. The composition of Claim 8 wherein the antioxidant comprises at least one water-insoluble phenol or bis-phenol.
    10. The composition of Claim 9 wherein the antioxidant is an alkylated-p-cresol.
    11. The composition of Claim 10 wherein the antioxidant is ditridecylthiopropionate.
    类似技术:
    公开号 | 公开日 | 专利标题
    AU2016231634B2|2018-05-17|New reactive surfactants for emulsion polymerization, pigment dispersion, and UV coatings
    US5310778A|1994-05-10|Process for preparing ink jet inks having improved properties
    Arshady1992|Suspension, emulsion, and dispersion polymerization: A methodological survey
    US6126731A|2000-10-03|Polymerizable ink composition
    US5624973A|1997-04-29|Polymers having substantially nonporous bicontinuous structures prepared by the photopolymerization of microemulsions
    US4680200A|1987-07-14|Method for preparing colloidal size particulate
    EP0203724B1|1991-10-09|Verfahren zur Herstellung von Polymerteilchen
    DE69504650T3|2007-01-11|Verfahren zur herstellung von wässrigen polymer-zusammensetzungen
    JP3938795B2|2007-06-27|改良されたポリマー形成方法
    US5369163A|1994-11-29|Process for preparing large dimension emulsion polymer particles, polymer product and uses thereof
    US6534597B2|2003-03-18|Polymerizable compounds and use thereof
    US5036109A|1991-07-30|Polymeric particles and their preparation
    US5618888A|1997-04-08|Process for preparing emulsion polymers having a hollow structure
    US7030175B2|2006-04-18|Ink jet latex having reactive surfactant stabilization
    JP4624665B2|2011-02-02|インクジェットインクの耐久性を改善する特定のコア−シェルポリマー添加剤
    AU662814B2|1995-09-14|Aqueous polymer dispersion
    CA1153484A|1983-09-06|Sequential emulsion polymerization process andstructured particle latexes produced thereby
    US4680332A|1987-07-14|Ink jet compositions and process for preparation thereof
    KR100337054B1|2002-11-25|수성코어-쉘라텍스중합체
    US8735518B2|2014-05-27|Aqueous dispersions of polymers which comprise a fluorescent dye, process for their production and their use for marking materials
    DE69732158T2|2005-06-02|Tintenstrahl-Aufzeichnungsflüssigkeit
    Holmberg1992|Polymerizable surfactants
    KR0171604B1|1999-03-30|1~50㎛ 범위의 균일한 크기를 갖는 중합체 입자 제조공정
    ES2215084T3|2004-10-01|Emulsiones polimericas acuosas, polimodales, de multiples etapas.
    FI68408C|1985-09-10|Foerfarande foer framstaellning av en vattenemulsion eller -dispersion av ett delvis vattenloesligt material och eventuellt vidare omvandling av den framstaellda dispersionen eller emulsionen till en polymerdispersion dao det delvis vattenloesliga materialet aer en polymeriserbar monomer samt anvaendning av sao framstaellda monodispersa polymerpartiklar som toing i xerografi
    同族专利:
    公开号 | 公开日
    AU557410B2|1986-12-18|
    AU1882083A|1984-03-07|
    DE3273788D1|1986-11-20|
    JPS59501368A|1984-08-02|
    EP0100793B1|1986-10-15|
    AT22900T|1986-11-15|
    EP0100793A1|1984-02-22|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US3069375A|1957-10-04|1962-12-18|Du Pont|Aqueous polymerization of carboxylic monomer using colloidal silica and resulting product|
    EP0011190A1|1978-11-14|1980-05-28|Bayer Ag|Füllstoffhaltige, vernetzte Perlpolymerisate|EP0978521A2|1998-07-23|2000-02-09|Elf Atochem S.A.|Verfahren zur suspensionspolymerisation von acryl monomeren|JPS5845456B2|1975-04-14|1983-10-11|Dow Chemical Co||
    DE2516183A1|1975-04-14|1976-10-28|Dow Chemical Co|Durch isothiouroniumkationen stabilisierte latices und deren verwendung zur bildung von ueberzuegen|
    US4512360A|1982-11-29|1985-04-23|Chronister Clyde H|Fabricated ball valve|US4680200A|1985-07-22|1987-07-14|The Dow Chemical Company|Method for preparing colloidal size particulate|
    US4835034A|1987-07-06|1989-05-30|Cruz Francisco A|Insulation board and composite sheet|
    JPH02261839A|1989-03-30|1990-10-24|Ciba Geigy Ag|Storage stable non-sedimentary emulsion and its production|
    CA2056188C|1990-11-30|2003-01-21|Jose M. Sosa|Polymerization of monovinylaromatic compounds|
    法律状态:
    1984-03-01| AK| Designated states|Designated state(s): AU JP US |
    优先权:
    申请号 | 申请日 | 专利标题
    EP19820200995|EP0100793B1|1982-08-06|1982-08-06|Wässrige Dispersionen, die kolloidale Partikel eines Polymers und einen Füllstoff enthalten und Verfahren zu deren Herstellung|AU17757/83A| AU573726B2|1983-07-20|1983-07-20|Thermoplasttic resin foam|
    [返回顶部]