    • 专利摘要:
    When molding of a heat-curable resin such as unsaturated polyester resin and the like is conducted by means of the casting method, concavities in the molded product generated as a result of the curing shrinkage of this resin are prevented. A central core member comprising ABS resin or the like is disposed in advance within mold, a heat-curable resin liquid is injected thereinto, and heated, and at this time, an amount of expansion in the volume of central core member is caused which corresponds to the amount of volume shrinkage resulting from curing of the heat-curable resin, and the expansion of the central core member is synchronized with the curing shrinkage of the heat-curable resin.
    公开号:US20010009308A1
    申请号:US09/330,919
    申请日:1999-06-11
    公开日:2001-07-26
    发明作者:Shigeru Kinpara；Yoshiyuki Sato；Hisayoshi Osumi；Senji Suzuki
    申请人:Yamaha Corp；
    IPC主号:B29C39-405
    专利说明:
    [0001] 1. Field of the Invention [0001]
    [0002] The present invention relates to a manufacturing method for molded products comprising a heat-curable resin (thermo-setting resin) such as unsaturated polyester resin, epoxy resin, urethane resin, diallylphthalate resin, or the like, which is capable of preventing the occurrence of voids or concavities (concave portions) on the surface of the molded products caused by the shrinkage in volume accompanying the curing of the heat-curable resin. [0002]
    [0003] 2. Description of the Related Art [0003]
    [0004] This type of heat-curable resin experiences a comparatively large volume shrinkage during curing, so that for example, unsaturated polyester resin shrinks by as much as 7%. For this reason, when molded products are molded using a injection method, “concavities” are generated as a result of this volume shrinkage, and this produces concave defects in the surface of the molded products, so that unsatisfactory products result. [0004]
    [0005] A method has been proposed as a solution to this problem in which the mold is placed under pressure during molding, and the volume of the molding space (cavity) of the mold is reduced in accordance with the decrease in volume resulting from curing. However, in this molding method, an apparatus for applying pressure is required, and furthermore, when the walls of the mold are curved, the pressure does not act uniformly over the entire surface of the mold, and it is impossible to completely prevent concavities. [0005]
    [0006] Accordingly, it is an object of the present invention to avoid the generation of concavities (voids) in the surface of molded products when heat-curable resin is molded using the casting method. [0006] SUMMARY OF THE INVENTION
    [0007] The present invention provides a method in which a central core member is placed in advance within a mold, heat-curable resin liquid is injected around the central core member within the mold, and when the mold is heated and curing of the resin is conducted, and an increase in volume is generated in the central core member which is in correspondence with the reduction in volume of the heat-curable resin as a result of curing. The present invention also provides a manufacturing method for heat-curable resin molded products in which three necessary factors are controlled: the selection of the central core member, the adjustment of the curing rate of the heat-curable resin, and the setting of the temperature of the mold. [0007]
    [0008] Accordingly, in accordance with the manufacturing method for heat-curable resin molded products of the present invention, even when a heat-curable resin having a large amount curing shrinkage, such as unsaturated polyester resin or the like, is employed, it is possible to produce molded products having a satisfactory finish without concavities in the surfaces thereof. Furthermore, in comparison with the conventional manufacturing method in which pressure was applied to the mold, it is possible to prevent the generation of concavities even when the shape of the molded product is complex, having curved surfaces or the like. It is not necessary to apply pressure to the mold, so that it is possible to simplify the manufacturing installation, and it is also possible to extend the lifespan of the mold. [0008] BRIEF DESCRIPTION OF THE DRAWINGS
    [0009] FIG. 1 is a schematic structural diagram showing an example of the manufacturing method of the present invention. [0009]
    [0010] FIG. 2 is a schematic structural diagram showing an example of the manufacturing method of the present invention. [0010]
    [0011] FIG. 3 is a graph showing the changes over time in the expansion of the central core member and the curing shrinkage of the heat-curable resin in the present invention. [0011] DESCRIPTION OF THE PREFERRED EMBODIMENTS
    [0012] Hereinbelow, the present invention will be explained in detail. [0012]
    [0013] FIG. 1 and FIG. 2 serve to indicate an example of the manufacturing method of the present invention; they indicate an example in which a molded product which is cylindrical or doughnut-shaped is produced. [0013]
    [0014] In the figures, reference [0014] 1 indicates a mold for molding, and this mold 1 has a structure which is divided into two parts, and in the inner part thereof, a cavity 2 forming the molding space is formed.
    [0015] A central core member [0015] 3 which is cylindrical or doughnut-shaped is disposed within the cavity 2 of this mold 1. This central core member 3 becomes unitary with the heat-curable resin which is injected into the cavity 2 in a later process and forms a part of the molded product; concretely, the member comprises a resin material such as epoxy resin, foaming urethane resin, PPS resin (polyphenylene sulfide), polycarbonate resin, ABS resin, and the like, and the shape thereof is controlled by the shape of the molded product. Furthermore, it is preferable that the dimensions of the central core member 3 be determined so that it occupies 70- 99% of the volume of the finished molded product.
    [0016] The attachment of the central core member [0016] 3 within the cavity 2 is accomplished using a suspension pin or the like provided within mold 1.
    [0017] Next, mold [0017] 1 is closed, and as shown in FIG. 2, a heat-curable resin liquid 5 in an uncured state is injected from gate 4, and this fills the interior of cavity 2.
    [0018] Unsaturated polyester resin, urethane resin, epoxy resin, or diallylphthalate resin may be employed as the heat-curable resin used herein. These heat-curable resins are all employed mixed with a curing agent or a curing promoter, and it is important that the type or amount of curing agent or curing promoter or the like which is employed be appropriately altered in order to obtain the necessary curing rate and curing temperature described hereinbelow. [0018]
    [0019] When the filling of heat-curable resin liquid [0019] 5 is completed, mold 1 is heated by the heaters 6, 6 . . . which are contained within mold 1, and by means of this, the heat-curable resin liquid 5 is heated and cured, and a molded product is obtained in which the central core member 3 and the heat-curable resin become unitary.
    [0020] In this curing process, as described hereinbelow, it is important to control the mold temperature which governs the temperature of the central core member [0020] 3 and the heat-curable resin liquid 5 within the cavity 2, and especially to control a rate of increase in the temperature of the mold, and a temperature which the mold attains (hereinafter referred to as a final temperature).
    [0021] Once the curing of the heat-curable resin has been completed, mold [0021] 1 is cooled, and the mold is opened to extract the molded product.
    [0022] In the manufacturing method of the present invention, during the operations described above from the initiation of curing to the completion of curing, in response to the amount of shrinkage in the volume accompanying the curing of the heat-curable resin, an increase in volume is generated in the central core member [0022] 3 which is either equal to or slightly greater than the amount of shrinkage in the volume of the resin.
    [0023] The amount of shrinkage in the volume of the heat-curable resin as a result of curing differs depending on the type of resin; however, this is not dependent on the curing temperature or rate of curing. Accordingly, if the volume of heat-curable resin liquid [0023] 5 which fills the interior of cavity 2 is fixed, then the shrinkage volume can be obtained by calculation.
    [0024] On the other hand, the increase in volume of central core member [0024] 3 is determined by the material comprising the central core member 3 and the temperature thereof. Accordingly, in obtaining the amount of volume expansion required in central core member 3, it is possible to calculate this if the selection of the material and the final temperature within mold 1 are determined.
    [0025] Generally, the mold [0025] 1 is categorized into two types, namely, an open type mold which does not close an injection aperture even when the curing process is conducted, and a closed type mold which closes the injection aperture during the curing. In the open type mold, the resin moves out of the aperture during curing when the volume expansion takes place in the central core member 3. In order to reliably prevent concavities in the molded product, it is insufficient to simply compensate for the shrinkage in the volume with an expansion of the volume of the central core member 3 at the point at which the heat-curable resin is completely cured.
    [0026] In other words, as shown in FIG. 3, during the period from the initiation of curing of the heat-curable resin to the completion of curing thereof, an amount of volume increase in central core member [0026] 3 which corresponds to the increase in the amount of volume shrinkage, takes place approximately at the same time when the heat-curable resin is cured. In the closed type mold, the volume expansion in the center core member 3 which is equal to or slightly greater than the amount of shrinkage in the volume of the resin.
    [0027] In order to meet the conditions described above, firstly, the selection of the material of central core member [0027] 3, secondly, the preparation composition, which stipulates the curing rate and curing temperature of the heat-curable resin liquid 5, and thirdly, the setting of the rate of increase of temperature of mold 1 and the final temperature, which stipulate the temperature of central core member 3 and the temperature of the heat-curable resin, are required.
    [0028] By selecting an appropriate combination of these three, it is possible to completely prevent the concavities in the molded products. [0028]
    [0029] These appropriate combinations are determined by preparatory molding experiments. [0029]
    [0030] Furthermore, in general, a method is possible in which a central core member comprising a resin having a large coefficient of linear expansion, for example, ABS resin, polycarbonate resin, or the like, is combined with a heat-curable resin having a large amount of shrinkage during curing, for example, unsaturated polyester resin, and a method exists in which, when a central core member [0030] 3 comprising a resin having a small coefficient of linear expansion, for example, PPS resin, foaming polyurethane resin, or the like, is employed, a preparation composition having a slow rate of curing and a high curing temperature is employed as the heat-curable resin, the mold is slow, and the final temperature is set so as to be high.
    [0031] Hereinbelow, concrete combinations of central core members [0031] 3, mixtures of heat-curable resins and mold temperatures (final temperatures) are shown together with the state of occurrence of concavities in the molded products. (1) Central Core MemberName of Material Linear Expansion Coefficient Epoxy resin 4 × 10−5 Foaming urethane resin 3 × 10−5 PPS resin 2 × 10−5 Polycarbonate resin 7 × 10−5 ABS resin 8 × 10−5
    [0032] [0032] (2) Heat-curable Resin Preparation, Curing Shrinkage Ratio Unsaturated polyester resin Unsaturated polyester 100 parts by weight Methyl ethyl ketone peroxide 0.5-1.5 parts by weight (10.0-10.5% active oxygen) Cobalt naphthenate 0.5 parts by weight (cobalt mass conversion 6%) Ester type reaction promoter 0.2-0.4 parts by weight Volume shrinkage ratio 7% Urethane Resin Polyether 100 parts by weight Isocyanate 10-50 parts by weight Volume shrinkage ratio 6.0% Epoxy Resin Epoxy resin 100 parts by weight Amine type curing agent 30 parts by weight Volume shrinkage ratio 4.5%
    [0033] In table 1, the state of occurrence of concavities in the surfaces of molded products is shown when the molding was conducted while altering the combination of the central core members and heat-curable resins and the mold temperatures. In Table 1, when the depth of the surface concavities were measured as a percentage of the thickness of the resin layer, 0 indicates 0.05%, while Δ indicates 0.5- 2%, and X indicates greater than 2%. [0033] TABLE 1 Central Core Heat-curable Mold Temperature Attained (° C.) Member Resin 60 80 100 120 140 Epoxy resin Unsaturated X Δ 0 0 0 polyester Epoxy resin Urethane Δ Δ 0 0 0 Epoxy resin Epoxy Δ 0 0 0 0 Foaming urethane Unsaturated X X Δ 0 0 resin polyester Foaming urethane Urethane X Δ 0 0 0 resin Foaming urethane Epoxy X 0 0 0 0 resin PPS resin Unsaturated X X X Δ 0 polyester PPS resin Urethane X X Δ Δ 0 PPS resin Epoxy X X Δ 0 0 PC resin Unsaturated 0 0 0 0 0 polyester PC resin Urethane 0 0 0 0 0 PC resin Epoxy 0 0 0 0 0 ABS resin Unsaturated 0 0 0 — — polyester ABS resin Urethane 0 0 0 — — ABS resin Epoxy 0 0 0 — —
    [0034] As is clear from the results shown in Table 1, when a central core member comprising a material having a small thermal expansion ratio was combined with a heat-curable resin having a large curing shrinkage ratio, it was necessary to set the final temperature by the mold to a sufficiently high level, while when a central core member was employed comprising a material having a large thermal expansion ratio, there was not such a relationship with the curing shrinkage ratio of the heat-curable resin, and concavities were not generated even when the final temperature by the mold was low. [0034]
    [0035] In this molding method for heat-curable resins, by means of a heat-induced expansion of the volume of the central core member [0035] 3 which was equal to or greater than the amount of shrinkage in volume induced by curing generated during the molding of the heat-curable resin, compensation was performed constantly over the period of time from the initiation of curing to the completion of curing, therefore concavities were not generated in the surface of the heat-curable resin molded products, and molded products were produced which had good finished surfaces.
    [0036] Hereinbelow, concrete examples will be given; however, the present invention is not limited to the concrete examples described. In particular, the linear expansion coefficient of the resin selected for the central core member varied depending on the preparation, so that the preparation and the heating temperature of the mold should be determined in accordance with this. [0036] EXAMPLE 1
    [0037] Using the central core member, heat-curable resin (preparation), and mold heating conditions shown in Table 2, molding was conducted, and a good molded product was obtained which had no concavities. The temperature attained by the mold was set to 100° C. so that the amount of shrinkage of the unsaturated polyester resin and the amount of expansion of the epoxy resin central core member were identical. Furthermore, the rate of increase in the temperature in the mold and the preparation of the unsaturated polyester resin (the curing rate) were determined so that the expansion of the central core member and the shrinkage of the resin were synchronized. [0037] TABLE 2 Central core member Epoxy resinHeat-curable resin Unsaturated polyester 100 parts  Methyl ethyl ketone peroxide 1.5 parts Cobalt naphthenate 0.5 parts Ester type reaction promoter 0.4 parts Mold conditions Attained 100° C., initially 25° C., Increase by 20° C./minute Heating time 12 minutes EXAMPLE 2
    [0038] Molding was conducted using central core member, the heat-curable resin (preparation) and the mold heating conditions shown in Table 3, and a good molded product with no concavities was obtained. Because the expansion ratio of the foaming urethane resin was small, the final temperature by the mold was set to 120° C., so that the amount of shrinkage and the amount of expansion were identical. Furthermore, the rate of increase in the temperature of the mold and the preparation of the unsaturated polyester resin (the curing rate) were determined so that the expansion of the central core member and the shrinkage of the resin were synchronized. [0038] TABLE 3 Central core member Foaming urethane resinHeat-curable resin Unsaturated polyester 100 parts  Methyl ethyl ketone peroxide 1.5 parts Cobalt naphthenate 0.5 parts Ester type reaction promoter 0.4 parts Mold conditions Attained 120° C., initially 25° C., increase by 20° C./minute Heating time 14 minutes EXAMPLE 3
    [0039] Molding was conducted using the central core member, heat-curable resin (preparation), and mold heating conditions shown in Table 4, and a good molded product with no concavities was obtained. The thermal expansion ratio of the polycarbonate resin was large, and the amount of shrinkage in the epoxy resin was small, so that an attained mold temperature of 60° C. was sufficient. Furthermore, the rate of temperature increase and the epoxy resin preparation (curing rate) were determined so that the expansion of the central core member and the shrinkage of the resin were synchronized. [0039] TABLE 4 Central core member Polycarbonate resinHeat-curable resin Epoxy 100 parts Amine  30 partsMold conditions Attained 60° C., initially 25° C., increase by 8° C./minute Heating time 12 minutes COMPARATIVE EXAMPLE 1
    [0040] Molding was conducted using the central core member, heat-curable resin (preparation), and mold heating conditions shown in Table 5, and concavities were generated in the molded product. The attained temperature of the mold was low, at 40° C., and the expansion of the epoxy resin of the central core member was small, so that it was not possible to compensate for the shrinkage of the unsaturated polyester resin. [0040] TABLE 5 Central core member Epoxy resinHeat-curable resin Unsaturated polyester 100 parts  Methyl ethyl ketone peroxide 1.5 parts Cobalt naphthenate 0.5 parts Ester type reaction promoter 0.4 parts Mold conditions Attained 40° C., initially 25° C., increase by 20° C./minute Heating time 30 minutes COMPARATIVE EXAMPLE 2
    [0041] Molding was conducted using the central core member, heat-curable resin (preparation), and mold heating conditions shown in Table 6 and concavities were generated in the molded product. The rate of increase in the temperature of the mold was low, so that the expansion of the central core member was delayed. On the contrary, a large amount of the methyl ethyl ketone peroxide curing agent was mixed with the unsaturated polyester resin, so that the curing rate was high. For this reason, the curing shrinkage of the resin was not synchronized with the expansion of the central core member, and thus the expansion of the central core member was delayed. [0041] TABLE 6 Central core member Epoxy resinHeat-curable resin Unsaturated polyester 100 parts  Methyl ethyl ketone peroxide 3.0 parts Cobalt naphthenate 0.5 parts Ester type reaction promoter 0.4 parts Mold conditions Attained 80° C., initially 25° C., Increase by 2° C./minute Heating time 40 minutes
    权利要求:
    Claims (3)
    [1" id="US-20010009308-A1-CLM-00001] 1. A method of manufacturing heat-curable resin molded products, comprising the steps of:
    disposing a central core member within a mold; and
    injecting heat-curable resin around said central core member within said mold;
    heating said mold to cure said heat-curable resin, wherein
    volume expansion is generated in said central core member which corresponds to an amount of volume shrinkage induced by curing in said heat-curable resin.
    [2" id="US-20010009308-A1-CLM-00002] 2. A method of manufacturing heat-curable resin molded products according to
    claim 1 , wherein
    expansion of said central core member and curing shrinkage of said heat-curable resin takes place approximately at the same time.
    [3" id="US-20010009308-A1-CLM-00003] 3. A method of manufacturing heat-curable resin molded products according to
    claim 1 , wherein
    said central core member is selected from the group consisting of epoxy resin, foaming urethane resin, PPS (polyphenylene sulfide) resin, polycarbonate resin, ABS resin; and
    said heat-curable resin is selected from the group consisting of unsaturated polyester resin, urethane resin, epoxy resin, diallylphthalate resin, wherein
    a curing agent and/or a curing promoter is mixed with said heat-curable resin in an amount efficient to adjust the curing rate and the curing temperature;
    said heating is conducted at the temperature in the range of 20- 140° C.
    类似技术:
    公开号 | 公开日 | 专利标题
    US5662996A|1997-09-02|Method for manufacturing self-supporting synthetic trim parts and thus manufactured trim parts
    US6468460B2|2002-10-22|Method for manufacturing heat-curable resin molded product
    KR20140071915A|2014-06-12|Method and device for producing of a form part
    US4419307A|1983-12-06|Method for manufacturing heat-insulating member and device therefor
    US4765935A|1988-08-23|Method for foaming insulations in refrigerators and the like
    US4957684A|1990-09-18|Soft molding method
    KR20030084652A|2003-11-01|Method for producing of -especially- soles in the mechanical production of soles
    US5059361A|1991-10-22|Method for the production of structural elements of thermosetting plastics material, particularly component parts for motor vehicle bodies, by injection moulding
    US5399303A|1995-03-21|Method of controlling resin molding conditions
    JP3463608B2|2003-11-05|Manufacturing method of thermosetting resin molded products
    US20020066174A1|2002-06-06|Device and method for molding motor coils
    JP3264318B2|2002-03-11|Injection mold
    JP3161935B2|2001-04-25|Molding method for resin molded products
    JP3498640B2|2004-02-16|Manufacturing method of thermosetting synthetic resin molded product
    RU2050283C1|1995-12-20|Method of moulding products from composite materials
    JPS59213115A|1984-12-03|Manufacture of low voltage molded transformer
    JPH068349A|1994-01-18|Method for molding rubber product
    JPH069811Y2|1994-03-16|In-mold coating equipment
    JP2745830B2|1998-04-28|Method for manufacturing synthetic resin hollow structure
    JPH02140107A|1990-05-29|Molding method for laminated cushion body
    CA2144263A1|1995-09-12|Method and device for producing molded articles
    KR960015286B1|1996-11-07|Method for producing epoxy insulating article
    JP4264682B2|2009-05-20|Manufacturing method of hard sponge rubber molded product
    JPH05293867A|1993-11-09|Injection molding device
    JP3165277B2|2001-05-14|Sink prevention resin molding die equipment
    同族专利:
    公开号 | 公开日
    DE19929182B4|2005-02-17|
    US20030052439A1|2003-03-20|
    DE19929182A1|2000-01-20|
    US6468460B2|2002-10-22|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20040130070A1|2002-01-17|2004-07-08|Olaf Abels|Method and device for controlling the shrink behavior of plastic materials during primary shaping|
    US20050046322A1|2003-09-01|2005-03-03|Ha-Jin Kim|Carbon-nano tube structure, method of manufacturing the same, and field emitter and display device each adopting the same|
    US20080191387A1|2005-05-03|2008-08-14|Stork Sp Aerospace B.V.|Device for Injecting a Resin Into at Least One Fibre Layer of a Fibre-Reinforced Product to be Manufactured|US3790421A|1970-07-08|1974-02-05|Plexawood Inc|Composite articles and methods of making the same|
    AT350899B|1974-03-04|1979-06-25|Rank Xerox Ltd|COPY MACHINE|
    US4040670A|1975-04-10|1977-08-09|Perma Rain Irrigation, Inc.|Method of molding a skate wheel having a polyester core and a polyurethane case and the product thereof|
    US4824723A|1986-06-02|1989-04-25|General Electric Company|Flame resistant electrical insulating material|
    US4949457A|1988-08-03|1990-08-21|Warner-Lambert Company|Soft resilient razor handle|
    JPH0295387A|1988-09-30|1990-04-06|Hamada Enterp:Kk|Head of golf club and its manufacture|
    US4949487A|1988-11-03|1990-08-21|Fadil Kibarer|Illuminated display|
    JPH0645158B2|1990-06-20|1994-06-15|株式会社極東商会|Integrated resin molding method for insert parts that slide in the housing|
    US5286320A|1991-11-18|1994-02-15|Owens-Corning Fiberglas Technology Inc.|Method for making a pultruded panel|
    FR2693249B1|1992-07-03|1994-09-16|Hutchinson|Method of connecting tubes or pipes, fittings and similar devices obtained by its implementation.|
    US5753165A|1993-12-21|1998-05-19|Yamauchi Corporation|Process for producing a hard roll|
    US5474721A|1994-04-12|1995-12-12|Stevens; Robert B.|Method of forming an expanded composite|
    US5529839A|1994-07-13|1996-06-25|Caine Corporation|Elongate composite structural member and method of making|
    DE19634360C2|1996-08-26|1999-04-08|Grammer Formteile Gmbh|Process for producing a composite molded part|US6767489B2|2002-07-29|2004-07-27|Lexmark International, Inc.|Method to mold round polyurethane rollers free of injection gates, parting lines and bubbles|
    US20050244600A1|2004-04-28|2005-11-03|Wycech Joseph S|Method and apparatus for forming a finished article of manufacture and a finished article of manufacture made by a new and novel process|
    DE102004033138B4|2004-07-08|2007-11-22|Franz Josef Summerer|Method and device for producing a two- or multi-component plastic molding|
    US20060247638A1|2005-04-29|2006-11-02|Sdgi Holdings, Inc.|Composite spinal fixation systems|
    CN109651802A|2018-12-06|2019-04-19|江西江铃集团奥威汽车零部件有限公司|A kind of foamed material of automotive seat and its preparation method and application|
    法律状态:
    1999-06-11| AS| Assignment|Owner name: YAMAHA CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KINPARA, SHIGERU;SATO, YOSHIYUKI;OSUMI, HISAYOSHI;AND OTHERS;REEL/FRAME:010045/0092;SIGNING DATES FROM 19990427 TO 19990517 |
    2002-10-03| STCF| Information on status: patent grant|Free format text: PATENTED CASE |
    2006-03-31| FPAY| Fee payment|Year of fee payment: 4 |
    2010-04-14| FPAY| Fee payment|Year of fee payment: 8 |
    2014-03-26| FPAY| Fee payment|Year of fee payment: 12 |
    优先权:
    申请号 | 申请日 | 专利标题
    JP10-181195||1998-06-26||
    JP18119598||1998-06-26||US10/159,905| US20030052439A1|1998-06-26|2002-05-31|Method for manufacturing heat-curable resin molded product|
    [返回顶部]