    • 专利摘要:
    The present invention provides a method of manufacturing an organic electrolyte electrochemical cell comprising at least one electrochemical couple made up of two electrodes sandwiching a solid film of porous polymer containing said electrolyte, each electrode comprising a porous layer containing an electrochemically active material and a binder, the method comprising the following steps: ü a polymer is put into solution in a solvent and said solution is spread in the form of a film on a support; ü said film of solution is immersed in a volatile is non-solvent that is miscible with said solvent in order to precipitate said polymer and said polymer film is dried to eliminate said non-solvent; and ü said couple made up of said polymer film placed between said electrodes and in contact therewith, and impregnated with said electrolyte, is compressed while being heated to a temperature less than or equal to the temperature at which said polymer film starts to melt so as to obtain incomplete melting of said polymer, said electrodes becoming unseparable after cooling.
    公开号:US20010008735A1
    申请号:US09/031,780
    申请日:1998-02-27
    公开日:2001-07-19
    发明作者:Xavier Andrieu；Francois Boudin
    申请人:Alcatel SA；
    IPC主号:H01M10-0565
    专利说明:
    [0001] The present invention relates to a method of manufacturing an organic electrolyte electrochemical cell of structure that is unitary, i.e. in with the various component elements are connected together so as to form a single whole. [0001] BACKGROUND OF THE INVENTION
    [0002] Organic electrolyte cells, in particular lithium cells are presently the subject of rapid and major development because of the high energy density they make available and because of their long lifetime. They are particularly suitable for use in objects of small dimensions. [0002]
    [0003] Traditional cells are made up of solid electrodes sandwiching a porous separator containing liquid electrolyte. Because of the risk of leakage, such cells are ill-suited to consumer portable equipment. [0003]
    [0004] As a result cells have been proposed that include an electrolyte that is made solid by being immobilized in a polymer matrix. However, over time electrical contact between the various components of the generator degrades, particularly if gas is given off. In order to limit that phenomenon, the cell is held in a compressed state by a rigid metal container, thereby increasing the weight of the cell. Attempts have therefore been made to interconnect the various components of the generator so that electrical contact between them is guaranteed under all circumstances. [0004]
    [0005] One method of making an electrochemical cell in which the various layers are bonded together is proposed in U.S. Pat. No. 5,540,741. To constitute a first electrode, a paste is deposited on a conductive support, the paste being formed of an electrochemically active material and a polymer solution. After it has dried, the electrode is covered in a layer of a solution of a plasticizer and a copolymer of a vinylidene fluoride and of hexafluoropropylene (VDF-HFP) to form the separator. The resulting assembly is covered in a second electrode constituted by a sheet of lithium made elsewhere. Pressing is performed at a temperature of at least 150° C., causing the copolymer to melt completely and thus leading to a non-porous material. The plasticizer is subsequently extracted by means of a solvent that is inert relative to the polymer. On being used, the cell is impregnated by the electrolyte which occupies the void left between the polymer chains by removal of the plasticizer. [0005]
    [0006] That method suffers from the drawback of giving rise to large changes in dimensions during manufacture of the cell. During extraction, the structure collapses, thus leading to a dense material. Consequently impregnation with the electrolyte takes place slowly. Thereafter impregnation leads to the VDF-HFP copolymer swelling in the presence of the electrolyte solvent. Such changes in dimensions give rise to tightening and unsticking phenomena that are harmful to the electrical continuity of the resulting cell. [0006] OBJECTS AND SUMMARY OF THE INVENTION
    [0007] An object of the present invention is to provide a method of making an electrochemical cell of unitary structure which minimizes variations in dimensions. [0007]
    [0008] The present invention provides a method of manufacturing an organic electrolyte electrochemical cell comprising at least one electrochemical couple made up of two electrodes sandwiching a solid film of porous polymer containing said electrolyte, each electrode comprising a porous layer containing an electrochemically active material and a binder, the method comprising the following steps: [0008]
    [0009] ü a polymer is put into solution in a solvent; [0009]
    [0010] ü a said solution is spread in the form of a film on a support; [0010]
    [0011] Ü said film of solution is immersed in a volatile non-solvent that is miscible with said solvent in order to precipitate said polymer; [0011]
    [0012] ü said polymer film is dried to eliminate said non-solvent; and [0012]
    [0013] ü said couple made up of said polymer film placed between said electrodes and in contact therewith, and impregnated with said electrolyte, is pressed while being heated to a temperature less than or equal to the temperature at which said polymer film starts to melt so as to obtain incomplete melting of said polymer, said electrodes becoming unseparable after cooling. [0013]
    [0014] The invention presents numerous advantages over known methods. Because the polymer film is impregnated with electrolyte, its porosity is conserved during the sticking step. The mean size of the pores lies in the range 0.1 μm to 1 μm. The porous volume is large, constituting 30% to 95% of the volume of the film. [0014]
    [0015] The pressing temperature is selected so that melting of the polymer film remains incomplete and restricted mainly to the surface. The film adheres on the electrodes as soon as the sticking surface has softened sufficiently. Consequently, dimensions do not change during sticking, and the porous volume is not significantly altered. In addition, when electrolyte impregnation takes place after sticking, the film is observed to swell, and this is avoided by the method of the invention. [0015]
    [0016] In an implementation of the method of the invention, the support used is an inert support. [0016]
    [0017] The polymer film has good mechanical strength since the polymer itself contains less than 30% of the electrolyte solvent, with the major portion being contained in the pores. [0017]
    [0018] In a first variant, said polymer film and each of said electrodes is impregnated with said electrolyte, and then said polymer film is placed between electrodes and in contact therewith to form said couple. [0018]
    [0019] In a second variant, said polymer film is placed between said electrodes and in contact therewith to form said couple, and said couple is then impregnated with said electrolyte. [0019]
    [0020] In another implementation of the method of the invention, at least one of said electrodes is used as the support as follows: [0020]
    [0021] ü said solution is spread on the surface of said porous layer of one of said electrodes in the form of a film; [0021]
    [0022] ü said film is immersed in a volatile non-solvent that is miscible with said solvent; [0022]
    [0023] ü said film is dried to eliminate said non-solvent; [0023]
    [0024] ü said electrode including said film is impregnated with said electrolyte; [0024]
    [0025] ü the film side of said electrode is covered in an electrode impregnated with said electrolyte to form an electrochemical couple; and [0025]
    [0026] ü said couple is pressed while being heated to a temperature less than or equal to the temperature at which said film begins to melt, so as to obtain incomplete melting of said polymer, said electrodes becoming unseparable after cooling. [0026]
    [0027] In yet another implementation of the method of the invention, both of said electrodes are used as the support, as follows: [0027]
    [0028] ü said solution is spread in the form of a film on the surface of said porous layer of each of said electrodes; [0028]
    [0029] ü each of said films is immersed in a volatile non-solvent that is miscible with said solvent; [0029]
    [0030] ü said films are dried to eliminate said non-solvent; [0030]
    [0031] ü said electrodes including said films are impregnated with said electrolyte; [0031]
    [0032] ü said electrodes are placed together so that said films are in contact to form an electrochemical couple; and [0032]
    [0033] ü said couple is pressed while being heated to a temperature lower than or equal to the temperature at which said film begins to melt so as to obtain incomplete melting of said polymer, said electrodes becoming unseparable after cooling. [0033]
    [0034] Using the electrodes as the support for making the polymer film makes it possible to avoid subsequent handling, and thus makes it possible to deposit films that are thinner. The method is thus simplified and made more reliable, and the final product has better performance. [0034]
    [0035] Said polymer is selected from: polyvinylidene fluoride; polyvinyl chloride; polymethylmethacrylate; cellulose acetate; a polysulfone; a polyether; a polyolefin; and from an alloy of polyvinylidene fluoride with a polymer selected from a polysulfone, polymethylmethacrylate, polyvinylpyrolidone, a copolymer of vinylidene fluoride and ethane tetrafluoride, and a copolymer of vinylacetate and of vinylalcohol. [0035]
    [0036] The preferred one of said polymers is polyvinylidene fluoride (PVDF). PVDF has the advantage of exhibiting very little swelling in the presence of solvent, thus limiting dimensional changes during the manufacture of the electrochemical cell. [0036]
    [0037] Said solvent is an organic solvent selected from; cyclohexanone; dichloromethane; dimethylacetamide (DMA); dimethylformamide (DMF); hexamethylphosphoramide (HMPA); dimethylsulfoxide (DMSO); triethylphosphate (TEP); N-methylpyrolidone (NMP); and mixtures thereof. It is desirable for the interaction between the polymer and the solvent to be weak. [0037]
    [0038] It is preferable to use an organic solvent in which the polymer dissolves without difficulty and which can easily be eliminated by heating to a moderate temperature without running any risk of damaging the active material. [0038]
    [0039] The selected polymer is put into a concentrated solution in the solvent. The concentration of the polymer must not be too high since that is one of the parameters which determines the porosity of the film; it is preferable for the solution to contain at least 50% solvent. [0039]
    [0040] The polymer in solution is deposited on the surface of the support by any known method such as immersion, coating, spraying, etc. . . . . If the surface presents irregularities and a certain amount of pores, they are smoothed over by the solution and they facilitate bonding of the film. [0040]
    [0041] In a first variant, the surface of said porous layer is impregnated with a wetting agent before it is covered in said film. The wetting agent may be a volatile organic solvent, for example. [0041]
    [0042] In a second variant, said solution of a polymer in a solvent also contains a wetting agent at a concentration of less than 10% by weight of said polymer. The agent serves to improve penetration and distribution of the electrolyte in the polymer film. [0042]
    [0043] In a third variant, said solution of a polymer in a solvent also includes a small quantity of a non-solvent, said quantity being insufficient to cause the polymer to be precipitated. The presence of a small quantity of a weak non-solvent facilitates three-dimensional organization of the polymer while it is being precipitated. [0043]
    [0044] The term “non-solvent” is used to designate a liquid in which the polymer is not soluble (a “strong” non-solvent) or is soluble to a small extent only (a “weak” non-solvent) at the operating temperature. When the selected non-solvent is water, either pure or in a mixture, said temperature lies in the range 5° C. to 80° C. [0044]
    [0045] Said non-solvent is selected from: water, ethanol, ethylene-glycol, glycerol, acetone, proplyene carbonate, dichloromethane, ethyl acetate, butanol, pentanol, acetonitril, and mixtures thereof. If the selected non-solvent is water, the method of the invention has the advantage of not polluting the environment and of facilitating solvent recycling. [0045]
    [0046] The film is put into contact with the non-solvent. The solvent is then replaced by the non-solvent with which it is miscible, thereby causing the polymer to be precipitated. Subsequent recovery of the solvent extracted by the non-solvent is thus facilitated. A porous film of solid polymer then covers the surface of the electrode. It suffices to evaporate off the non-solvent and possibly a portion of residual solvent by moderate heating. [0046]
    [0047] Said electrolyte comprises a lithium salt dissolved in an organic solvent. The organic solvent comprises a mixture of ethers and/or esters, the esters being selected from linear carbonates, and cyclic carbonates having more than four carbon atoms, such as propylene, ethylene, butylene, diethyl, and dimethyl carbonates, and mixtures thereof, for example. [0047]
    [0048] The lithium salt is selected from: lithium perchlorate LiClO[0048] 4, lithium hexafluoroarsenate LiAsF6, lithium hexafluorophosphate LiPF6, lithium tetrafluoroborate LiBF4, lithium trifluoromethanesulfonate LiCP3SO3, lithium trifluoromethanesulfonimide LiN(CF3SO2)2 (LiTFSI), and lithium trifluoromethanesulfonmethide LiC(CF3SO2)3.
    [0049] When the polymer is PVDF, heating is preferably performed at a temperature lying in the range 90° C. to 100° C. The coagulated polymer film is entirely stable up to a temperature of 75° C. and it melts above 105° C. Melting does not take place at a precise temperature, but spreads over a temperature range. It starts at the beginning of the range and does not become complete until the end thereof. It is therefore preferable to operate immediately before or at the beginning of the range. It is also known that PVDF in the raw state melts at above 150° C. [0049]
    [0050] Pressing is preferably performed at a pressure lying in the range 9.81N/cm[0050] 2 to 98.1N/cm2.
    [0051] The present invention also provides an electrochemical cell made by the method of the invention, including an anode in which said electrochemically active material is a carbon-containing material suitable for inserting lithium in its structure and selected from graphite, coke, vitreous carbon, carbon black, and active carbon, and said polymer is polyvinylidene fluoride. [0051]
    [0052] The present invention also provides an electrochemical cell made by the method of the invention, including a cathode in which said electrochemically active material is an oxide of a transition metal selected from vanadium oxide, lithium-containing oxides of manganese, nickel, and cobalt, and mixtures thereof, and said polymer is polyvinylidene fluoride. [0052] BRIEF DESCRIPTION OF THE DRAWINGS
    [0053] Other characteristics and advantages of the present invention appear from the following implementations that are naturally given by way of illustrative and non-limiting example, and from the accompanying drawings, in which: [0053]
    [0054] ü FIG. 1 is a diagrammatic section view of a button type cell made by the method of the invention; [0054]
    [0055] ü FIG. 2 shows the impedance spectrum of the cell of the invention, with the imaginary portion Z″ being plotted up the ordinate in ohms and with the real portion Z′ being plotted along the abscissa in ohms; [0055]
    [0056] ü FIG. 3 shows how the voltage of the cell of the invention varies during cycling, the voltage U of the cell being plotted up the ordinate in volts, and time t being plotted along the abscissa in hours; and [0056]
    [0057] ü FIG. 4 shows how the capacity of a cell of the invention varies during cycling, with the capacity C of the cell being plotted up the ordinate in μAh, and with the number of cycles N being plotted along the abscissa. [0057] MORE DETAILED DESCRIPTION
    [0058] EXAMPLE 1 [0058]
    [0059] The method of the invention was used to make a button type lithium rechargeable electrochemical cell A as shown in FIG. 1. [0059]
    [0060] The anode [0060] 1 was made of a porous layer 2 deposited on a copper collector 3. The porous layer 2 contained graphite as its electrochemically active material, and a binder which was polyvinylidene fluoride (PVDF).
    [0061] The cathode [0061] 4 was made up of a porous layer 5 deposited on an aluminum collector 6. The porous layer 5 contained a mixed nickel and lithium oxide as its electrochemically active material and a binder constituted by polyvinylidene fluoride (PVDF).
    [0062] A polymer solution was prepared contained 50% by weight of PVDF, 60% by weight of triethylphosphate (TEP) as solvent, and 25% by weight of tetrahydrofuran (THF) which acts as a diluant to adjust the viscosity of the solution. The solution was spread in the form of a film on an inert support, e.g. an aluminum sheet, a plate of glass or of PTFE, etc. . . . [0062]
    [0063] The THF was evaporated off in order to trigger three-dimensional organization of the polymer chains and facilitate precipitation of the polymer. The film was immersed in a non-solvent which was water, thereby causing the polymer to precipitate. A porous PVDF membrane [0063] 7 was thus obtained which was dried in air and which is suitable in that state for being conserved until it is used.
    [0064] When the cell was assembled, the porous membrane [0064] 7 and the electrodes 1, 4 were dried under a vacuum respectively at 60° C. and 120° C. and then impregnated with electrolyte. The electrolyte was made up of a solvent constituted by an equal-weight mixture of propylene carbonate (PC) and ethylene carbonate (EC), in which lithium hexafluoroarsenate LiAsF6 was dissolved.
    [0065] The cathode [0065] 4, the membrane 7, and the anode 1 were superposed in that order and maintained under pressure at a temperature of 95° C. for 10 seconds. The resulting assembly was placed in a cup 8 closed by a cover 9 to form a button type cell 10.
    [0066] The impedance spectrum [0066] 20 of the cell was plotted over the range 0.1 Hz to 65,000 Hz as shown in FIG. 2 for an electrode area of 1.13 cm 1. It can be seen that polarization resistance was low, of the order of 50 Ω/cm2.
    [0067] The cell [0067] 10 was cycled at a rate of Ic/20 where Ic corresponds to the rate that enables the cell to be discharged in one hour. Curve 30 in FIG. 3 and curve 40 in FIG. 4 show respectively how the voltage and the capacity of the cell varied during said cycling.
    [0068] EXAMPLE 2 [0068]
    [0069] A button type lithium rechargeable electrochemical cell B was made in accordance with the invention having electrodes analogous to those of Example 1 and containing the same electrolyte, however it was made in a different manner. [0069]
    [0070] After being fabricated, the electrodes were dried under a vacuum at 120° C. and then covered in respective films of solution containing 15% by weight PVDF, 60% by weight triethylphosphate (TEP) as volatile solvent, and 25% by weight tetrahydrofuran (THF). [0070]
    [0071] After the THP had been evaporated off, the film was immersed in a non-solvent which was water, thereby causing the polymer to precipitate. A porous PVDF membrane was thus obtained which was dried in air. [0071]
    [0072] The electrodes had their faces covered in the polymer film placed together and they were maintained under pressure at a temperature of 95° C. for 10 seconds. The assembly obtained in that way was placed in a cup closed by a cover to form the button type cell B. [0072]
    [0073] EXAMPLE 3 [0073]
    [0074] A button type lithium rechargeable electrochemical cell C was made in accordance with the invention, having electrodes analogous to those of Example 1 and containing the same electrolyte, but it was made in a different manner. [0074]
    [0075] After being fabricated, the electrodes were dried under a vacuum at 120° C, and then covered in respective films of a solution containing 25% by weight PVDF and 87.5% TEP. [0075]
    [0076] After being allowed to drip dry, each electrode was immersed for 20 minutes in water which is a strong non-solvent in order to cause the polymer to precipitate. The electrode was then dried in air, initially at 35° C. and then at 120° C. to remove all traces of water. This produced a very adhesive layer of solid PVDP having a thickness of 50 μm and porosity of 75%. [0076]
    [0077] The faces of the electrodes carrying the polymer films were put together and the electrodes were held together under pressure at a temperature of 95° C. for 10 seconds. The resulting assembly was placed in a cup closed by a cover to form button type cell C. [0077]
    [0078] EXAMPLE 4 [0078]
    [0079] A button type lithium rechargeable electrochemical cell D was made in accordance with the invention having electrodes analogous to those of Example 1 and containing the same electrolyte, but made in a different manner. [0079]
    [0080] After being fabricated, the electrodes were dried under a vacuum at 120° C. and then covered in respective films of a solution comprising 9.1% by weight PVDF, 54.5% NMP, and 36.4% ethanol. [0080]
    [0081] After being allowed to drip dry, each electrode was immersed in water at 80° C., and subsequently dried in air at 35° C. A layer of solid PVDF having 25% porosity was obtained. [0081]
    [0082] The faces of the electrodes carrying the polymer films were put together and the electrodes were held together under pressure at a temperature of 95° C. for 10 seconds. The assembly obtained in this way was placed in a cup closed by a cover to form button type cell D. [0082]
    [0083] Naturally, the present invention is not limited to button format cells, and any type of cell having plane electrodes can be envisaged. In addition, because of the flexibility of the electrode-separator assembly, the invention can also be applied to spiral-wound type cells. It can be used for making electrodes having any known electrochemically active electrode material and any of the usual polymer binders. [0083]
    权利要求:
    Claims (24)
    [1" id="US-20010008735-A1-CLM-00001] 1. A method of manufacturing an organic electrolyte electrochemical cell comprising at least one electrochemical couple made up of two electrodes sandwiching a solid film of porous polymer containing said electrolyte, each electrode comprising a porous layer containing an electrochemically active material and a binder, the method comprising the following steps:
    ü a polymer is put into solution in a solvent;
    ü said solution is spread in the form of a film on a support;
    ü said film of solution is immersed in a volatile non-solvent that is miscible with said solvent in order to precipitate said polymer;
    ü said polymer film is dried to eliminate said non-solvent; and
    ü said couple made up of said polymer film placed between said electrodes and in contact therewith, and impregnated with said electrolyte, is pressed while being heated to a temperature less than or equal to the temperature at which said polymer film starts to melt so as to obtain incomplete melting of said polymer, said electrodes becoming unseparable after cooling.
    [2" id="US-20010008735-A1-CLM-00002] 2. A method according to
    claim 1 , in which said support is an inert support.
    [3" id="US-20010008735-A1-CLM-00003] 3. A method according to
    claim 2 , in which said polymer film and each of said electrodes is impregnated with said electrolyte, and then said polymer film is placed between electrodes and in contact therewith to form said couple.
    [4" id="US-20010008735-A1-CLM-00004] 4. A method according to
    claim 2 , in which said polymer film is placed between said electrodes and in contact therewith to form said couple, and said couple is then impregnated with said electrolyte.
    [5" id="US-20010008735-A1-CLM-00005] 5. A method according to
    claim 1 , in which said support is one of said electrodes.
    [6" id="US-20010008735-A1-CLM-00006] 6. A method according to
    claim 5 , in which said electrode including said polymer film is impregnated with said electrolyte, and then said electrode is covered on the same side as said film with the other of said electrodes impregnated with said electrolyte to form said couple.
    [7" id="US-20010008735-A1-CLM-00007] 7. A method according to
    claim 1 , in which each of said electrodes is used as a support.
    [8" id="US-20010008735-A1-CLM-00008] 8. A method according to
    claim 7 , in which each of said electrodes including said polymer film is impregnated with said electrolyte, after which said electrodes are put together to form said couple in such a manner that said films are in contact.
    [9" id="US-20010008735-A1-CLM-00009] 9. A method according to
    claim 5 , in which the surface of said electrode porous layer is impregnated with a wetting agent prior to being covered in said film.
    [10" id="US-20010008735-A1-CLM-00010] 10. A method according to
    claim 1 , in which said solution of a polymer in a solvent further contains a wetting agent at a concentration of less than 10% by weight of said polymer.
    [11" id="US-20010008735-A1-CLM-00011] 11. A method according to
    claim 1 , in which said solution of a polymer in a solvent further includes a small quantity of a non-solvent, said quantity being insufficient to cause the polymer to be precipitated.
    [12" id="US-20010008735-A1-CLM-00012] 12. A method according to
    claim 1 , in which said solution of a polymer in a solvent contains at least 50% by weight of said solvent.
    [13" id="US-20010008735-A1-CLM-00013] 13. A method according to
    claim 1 , in which said polymer is selected from polyvinylidene fluoride; polyvinyl chloride; polymethylmethacrylate; cellulose acetate; a polysulfone; a polyether; a polyolefin; and from an alloy of polyvinylidene fluoride with a polymer selected from a polysulfone, polymethylmethacrylate, polyvinylpyrolidone, a copolymer of vinylidene fluoride and ethane tetrafluoride, and a copolymer of vinylacetate and of vinylalcohol.
    [14" id="US-20010008735-A1-CLM-00014] 14. A method according to
    claim 1 , in which said solvent is an organic solvent selected from: cyclohexanone; dichloromethane; dimethylacetamide; dimethylformamide; hexamethylphosphoramide; dimethylsulfoxide; triethylphosphate; N-methylpyrolidone; and mixtures thereof.
    [15" id="US-20010008735-A1-CLM-00015] 15. A method according to
    claim 1 , in which said non-solvent is selected from: water, ethanol, ethyleneglycol, glycerol, acetone, proplyene carbonate, dichloromethane, ethyl acetate, butanol, pentanol, acetonitril, and mixtures thereof.
    [16" id="US-20010008735-A1-CLM-00016] 16. A method according to
    claim 1 , in which said electrolyte contains an organic solvent comprising a mixture of ethers and/or esters, the esters being selected from linear carbonates and cyclic carbonates having more than 4 carbon atoms.
    [17" id="US-20010008735-A1-CLM-00017] 17. A method according to
    claim 1 , in which said electrolyte includes a lithium salt selected from lithium perchlorate, lithium hexafluoroarsenate, lithium hexafluorophosphate, lithium tetrafluoroborate, lithium trifluoromethanesulfonate, lithium trifluoromethanesulfonimide, lithium trifluoromethanesulfonmethide, and mixtures thereof.
    [18" id="US-20010008735-A1-CLM-00018] 18. A method according to
    claim 1 , in which heating is performed at a temperature lying in the range 90° C. to 100° C.
    [19" id="US-20010008735-A1-CLM-00019] 19. A method according to
    claim 1 , in which pressing is performed at a pressure lying in the range 9.18N/cm2 to 98.1N/cm2.
    [20" id="US-20010008735-A1-CLM-00020] 20. An electrochemical cell made by the method according to
    claim 1 , in which said polymer film has pores of average size lying in the range 0.1 μm to 1 μm.
    [21" id="US-20010008735-A1-CLM-00021] 21. An electrochemical cell made by the method according to
    claim 1 , in which said polymer film has a pore volume representing 30% to 95% of the volume of said film.
    [22" id="US-20010008735-A1-CLM-00022] 22. An electrochemical cell made by the method according to
    claim 1 , including an anode in which said electrochemically active material is a carbon-containing material suitable for inserting lithium in its structure and selected from graphite, coke, vitreous carbon, carbon black, and active carbon, and said polymer is polyvinylidene fluoride.
    [23" id="US-20010008735-A1-CLM-00023] 23. An electrochemical cell made by the method according to
    claim 1 , including a cathode in which said electrochemically active material is an oxide of a transition metal selected from vanadium oxide, lithium-containing oxides of manganese, nickel, and cobalt, and mixtures thereof, and said polymer is polyvinylidene fluoride.
    [24" id="US-20010008735-A1-CLM-00024] 24. An electrochemical cell made by the method according to
    claim 1 , including an anode in which said electrochemically active material is graphite, a cathode in which said electrochemically active material is a mixed oxide of nickel and lithium, said binder is polyvinylidene fluoride, and said porous polymer film is made of polyvinylidene fluoride.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6423447B1|2002-07-23|Non-aqueous electrolyte secondary battery and method of production of the same
    JP4629902B2|2011-02-09|Method for manufacturing lithium secondary battery
    US6280878B1|2001-08-28|Electrode and lithium secondary battery using this electrode
    US6051343A|2000-04-18|Polymeric solid electrolyte and lithium secondary cell using the same
    JP3665544B2|2005-06-29|Composition for forming separator of lithium secondary battery and method for producing lithium secondary battery using the same
    US6261721B1|2001-07-17|Cell having a separator comprising a macroporous matrix and a porous polymer
    US6787269B2|2004-09-07|Nonaqueous electrolyte and nonaqueous electrolyte secondary battery
    JP3563646B2|2004-09-08|Electrochemical device
    US6861175B2|2005-03-01|Nonaqueous electrolyte and nonaqueous electrolyte secondary battery
    US6268087B1|2001-07-31|Method of preparing lithium ion polymer battery
    KR100477885B1|2005-03-18|Method of making lithium ion polymer battery and porous polymeric electrolte
    JP2000149997A|2000-05-30|Nonaqueous electrolyte secondary battery and its manufacture
    US6364916B2|2002-04-02|Method of manufacturing an organic electrolyte electrochemical cell of unitary structure
    JP3443773B2|2003-09-08|Manufacturing method of non-aqueous electrolyte secondary battery
    JP4660105B2|2011-03-30|Nonaqueous electrolyte secondary battery
    WO2001089023A1|2001-11-22|A lithium secondary battery comprising a super fine fibrous polymer electrolyte and its fabrication method
    KR20190078525A|2019-07-04|Method of manufacturing electrode assembly for lithium secondary battery
    JPH09199136A|1997-07-31|Nonaqueous electrolyte secondary battery
    JP2001319693A|2001-11-16|Nonaqueous-electrolyte secondary battery
    JP2000195522A|2000-07-14|Nonaqueous electrolyte seconday battery
    JP3516133B2|2004-04-05|Manufacturing method of non-aqueous electrolyte secondary battery
    JP4235285B2|2009-03-11|Organic electrolyte battery
    JP2002042883A|2002-02-08|Nonaqueous electrolyte secondary battery
    WO2001091222A1|2001-11-29|A lithium secondary battery comprising a polymer electrolyte fabricated by a spray method and its fabrication method
    JPH10223255A|1998-08-21|Manufacture of polymer electrolyte secondary battery
    同族专利:
    公开号 | 公开日
    JPH10255849A|1998-09-25|
    US6364916B2|2002-04-02|
    DE69809993T2|2003-09-04|
    DE69809993D1|2003-01-23|
    EP0871234A1|1998-10-14|
    FR2760292B1|1999-04-02|
    EP0871234B1|2002-12-11|
    FR2760292A1|1998-09-04|
    CA2228782A1|1998-09-03|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20030005577A1|2001-06-18|2003-01-09|Japan Storage Battery Co., Ltd.|Process for the production of non-aqueous electrolyte battery|
    US20100323244A1|2009-06-23|2010-12-23|A123 Systems, Inc.|Battery electrodes and methods of manufacture|
    CN103208372A|2013-04-11|2013-07-17|东华大学|Method for preparing solid-state supercapacitor|US3023261A|1959-11-18|1962-02-27|Arnold S Louis|Monolithic electrode-separator structure for electrochemical cells|
    US4384047A|1980-03-28|1983-05-17|Pennwalt Corporation|Porous vinylidene fluoride polymer membrane and process for its preparation|
    EP0038885A1|1980-04-25|1981-11-04|Exxon Research And Engineering Company|Microcellular heterocyclic polymer structures|
    US4524509A|1983-04-07|1985-06-25|Tiegel Manufacturing Co.|Enveloping a battery plate by a dip process and product produced thereby|
    EP0243653B1|1986-03-24|1994-01-05|W.R. Grace & Co.-Conn.|Cathodic electrode|
    US4885007A|1988-08-01|1989-12-05|Tiegel Manufacturing|Dip process for enveloping a battery plate|
    JPH0353460A|1989-07-20|1991-03-07|Yuasa Battery Co Ltd|Electrochemical device|
    JPH04204522A|1990-11-30|1992-07-24|Tonen Corp|Electrolytic thin film|
    JPH05283106A|1992-03-30|1993-10-29|Nippon Telegr & Teleph Corp <Ntt>|Battery positive electrode sheet, its manufacture, fully-solid secondary battery|
    CA2110097C|1992-11-30|2002-07-09|Soichiro Kawakami|Secondary battery|
    US5460904A|1993-08-23|1995-10-24|Bell Communications Research, Inc.|Electrolyte activatable lithium-ion rechargeable battery cell|
    JPH06302314A|1993-04-01|1994-10-28|Wr Grace & Co Connecticut|Battery separator|
    US5514461A|1993-10-05|1996-05-07|Kureha Chemical Industry Co., Ltd.|Vinylidene fluoride porous membrane and method of preparing the same|
    US5503946A|1994-09-29|1996-04-02|Arthur D. Little, Inc.|Particulate interface for electrolytic cells and electrolytic process|
    US5437692A|1994-11-02|1995-08-01|Dasgupta; Sankar|Method for forming an electrode-electrolyte assembly|
    FR2729009B1|1994-12-28|1997-01-31|Accumulateurs Fixes|BIFUNCTIONAL ELECTRODE FOR ELECTROCHEMICAL GENERATOR OR SUPERCAPACITOR AND ITS MANUFACTURING PROCESS|
    JP3385516B2|1995-01-18|2003-03-10|日本電池株式会社|Non-aqueous polymer battery and method for producing polymer film for non-aqueous polymer battery|
    TW342537B|1995-03-03|1998-10-11|Atochem North America Elf|Polymeric electrode, electrolyte, article of manufacture and composition|
    JPH0922727A|1995-07-06|1997-01-21|Toshiba Battery Co Ltd|Manufacture of lithium secondary battery of hybrid solid polymer electrolyte type|
    US5637421A|1995-09-13|1997-06-10|The Johns Hopkins University|Completely polymeric charge storage device and method for producing same|
    US5840087A|1996-09-18|1998-11-24|Bell Communications Research, Inc.|Method for making laminated rechargeable battery cells|
    JP3225871B2|1996-12-26|2001-11-05|三菱電機株式会社|Manufacturing method of lithium ion secondary battery|
    FR2760292B1|1997-03-03|1999-04-02|Alsthom Cge Alcatel|METHOD FOR MANUFACTURING AN ORGANIC ELECTROCHEMICAL ELECTROCHEMICAL GENERATOR HAVING A UNIT STRUCTURE|FR2760292B1|1997-03-03|1999-04-02|Alsthom Cge Alcatel|METHOD FOR MANUFACTURING AN ORGANIC ELECTROCHEMICAL ELECTROCHEMICAL GENERATOR HAVING A UNIT STRUCTURE|
    WO1999045604A1|1998-03-04|1999-09-10|Valence Technology, Inc.|Methods for preparing electrochemical cells using solvent extraction techniques|
    KR100327096B1|1999-05-19|2002-03-06|이철상|preparation of porous polymer film, hybrid-type polymer electrolytes and lithium secondary polymer batteries using the polymer film, and the preparation thereof|
    TW512554B|2001-12-18|2002-12-01|Ind Tech Res Inst|A method for adhesion of wound electrodes or electrode|
    US20050287425A1|2004-06-25|2005-12-29|Celgard Inc.|Li/MnO2 battery separators with selective ion transport|
    JP2010198987A|2009-02-26|2010-09-09|Sumitomo Chemical Co Ltd|Manufacturing method of power storage device, and power storage device|
    DE102014226394A1|2014-12-18|2016-06-23|Bayerische Motoren Werke Aktiengesellschaft|Process for producing a lithium-ion cell|
    KR20210047145A|2019-10-21|2021-04-29|주식회사 엘지화학|Method for preparing electrode assembly, electrode assembly therefrom, and electrochemical device comprising the same|
    法律状态:
    1998-06-15| AS| Assignment|Owner name: ALCATEL ALSTHOM COMPAGNIE GENERALE D'ELECTRICITE, Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ANDRIEU, XAVIER;BOUDIN, FRANCOIS;REEL/FRAME:009251/0940 Effective date: 19980313 |
    1999-07-20| AS| Assignment|Owner name: ALCATEL, FRANCE Free format text: CHANGE OF NAME;ASSIGNOR:ALCATEL ALSTHOM COMPAGNIE GENERALE D'ELECTRICITE;REEL/FRAME:010084/0223 Effective date: 19980914 |
    2005-02-11| AS| Assignment|Owner name: SAFT FINANCE S.AR.L., LUXEMBOURG Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ALCATEL (FORMERLY KNOWN AS ALCATEL ALSTHOM COMPAGNIE GENERALE D'ELECTRICITE);REEL/FRAME:015667/0875 Effective date: 20040114 |
    2005-09-23| FPAY| Fee payment|Year of fee payment: 4 |
    2009-09-28| FPAY| Fee payment|Year of fee payment: 8 |
    2013-11-08| REMI| Maintenance fee reminder mailed|
    2014-04-02| LAPS| Lapse for failure to pay maintenance fees|
    2014-04-28| STCH| Information on status: patent discontinuation|Free format text: PATENT EXPIRED DUE TO NONPAYMENT OF MAINTENANCE FEES UNDER 37 CFR 1.362 |
    2014-05-20| FP| Expired due to failure to pay maintenance fee|Effective date: 20140402 |
    优先权:
    申请号 | 申请日 | 专利标题
    FR97-02494||1997-03-03||
    FR9702494A|FR2760292B1|1997-03-03|1997-03-03|METHOD FOR MANUFACTURING AN ORGANIC ELECTROCHEMICAL ELECTROCHEMICAL GENERATOR HAVING A UNIT STRUCTURE|
    [返回顶部]