    • 专利摘要:
    A terminal material is composed of a base material and a plurality of plating layers provided on the base material and containing an Sn-plating layer as its outermost layer. When the plating layers include an Ni-plating layer, the plating layers are formed so that the Sn-plating layer does not come in contact with the Ni-plating layer. A crimp portion of a crimp terminal is formed of the terminal material.
    公开号:US20010008709A1
    申请号:US08/959,448
    申请日:1997-10-28
    公开日:2001-07-19
    发明作者:Nobuyuki Asakura；Kei Fujimoto
    申请人:Yazaki Corp；
    IPC主号:C23C28-023
    专利说明:
    [0001] The present invention relates to an electric wire terminal material, and particularly relates to an electric wire crimp terminal material and a terminal using the terminal material. [0001]
    [0002] A crimp terminal is used as an electric wire terminal such as a terminal which is excellent in connecting an electric wire to a suspender. Heretofore, a material having an Sn-plating layer provided on a base material composed of Cu or a Cu alloy such as brass is used as a material used for production of the crimp terminal. However, the terminal formed from the aforementioned material having an Sn-plating layer has a disadvantage that if the terminal is used under a high temperature for a long time, an oxide film is produced on a contact surface, that is, on a surface of the Sn-plating layer, to thereby increase contact resistance. [0002]
    [0003] As a material to eliminate the aforementioned disadvantage, Japanese Patent Unexamined Publication No. Hei. 8-7960 discloses a terminal material in which in order to prevent easily oxidizable components of a base material from being diffused in the Sn-plating layer, an Ni-plating layer or a Co-plating layer is provided as an under layer, and the Sn-plating layer is provided on the under layer to thereby prevent the production of an oxide film. [0003]
    [0004] The present inventors have found the following about the aforementioned terminal material having an Ni-plating layer as its under layer as disclosed in the aforementioned Publication. That is, the Ni-plating layer and the Sn-plating layer are diffused into each other to form an intermetallic compound; the intermetallic compound is easily oxidized when exposed to a high temperature; and a crimp portion of a crimp terminal formed of the material is difficult to be kept in an air-shielded contact state, so that contact resistance in the crimp portion still increases to make it impossible to eliminate the aforementioned disadvantage fundamentally. This means that the aforementioned terminal material cannot secure the long-term reliability at the terminal crimp portion. [0004] SUMMARY OF THE INVENTION
    [0005] Therefore, an object of the present invention is to provide a novel terminal material. [0005]
    [0006] Another object of the present invention is to provide a terminal material suitable for a material for a crimp portion of a crimp terminal. [0006]
    [0007] A further object of the present invention is to provide a terminal material capable of forming a crimp portion in which contact resistance hardly increases and long-term connection reliability is improved even in the case where the crimp portion is exposed to a high temperature for a long time. [0007]
    [0008] A further object of the present invention is to provide a terminal having a crimp portion formed of the aforementioned terminal material. [0008]
    [0009] The foregoing objects of the present invention can be achieved by a terminal material characterized in that a plurality of plating layers containing an Sn-plating layer as its outermost layer are provided on a base material, and when an Ni-plating layer is provided, the plating layers are formed so that the Sn-plating layer does not come in contact with the Ni-plating layer, and can be achieved by a terminal having a crimp portion formed of the terminal material. [0009]
    [0010] The terminal material according to the present invention is configured so that a plurality of plating layers containing an Sn-plating layer as its outermost layer are provided, and even when an Ni-plating layer is provided, for example, a Cu-plating layer is provided between the Sn-plating layer and the Ni-plating layer so that the Sn-plating layer does not come in contact with the Ni-plating layer. Accordingly, no intermetallic compound is produced between Sn and Ni. Furthermore, oxidizable matters in the base material are prevented from being diffused into the Sn-plating layer. Accordingly, even in the case where the crimp portion of the terminal formed of the terminal material is exposed to a high temperature, the production of an oxide film at the contact portion is prevented so that the increase of contact resistance is reduced greatly. [0010] BRIEF DESCRIPTION OF THE DRAWINGS
    [0011] FIG. 1 is a schematic sectional view showing an embodiment of a terminal material according to the present invention. [0011]
    [0012] FIG. 2 is a schematic sectional view showing another embodiment of a terminal material according to the present invention. [0012]
    [0013] FIG. 3 is a schematic sectional view showing a terminal material produced in Comparative Example 1. [0013]
    [0014] FIG. 4 is a schematic sectional view showing a terminal material produced in Comparative Example 2. [0014]
    [0015] FIG. 5 is a schematic sectional view showing an embodiment of a terminal according to the present invention. [0015]
    [0016] FIG. 6 is a schematic sectional view showing another embodiment of a terminal according to the present invention. [0016] DETAILED DESCRIPTION OF THE INVENTION
    [0017] Preferred embodiments of the present invention will be described below with reference to the drawings. [0017]
    [0018] In a terminal material according to the present invention, a plurality of plating layers containing an Sn-plating layer as its outermost layer are provided on a base material composed of Cu or a Cu alloy such as brass. Examples of the plating layers other than the Sn-plating layer include a Cu-plating layer, an Ni-plating layer, and a Pb—Ni-alloy-plating layer. Above all, the Cu-plating layer and the Ni-plating layer are preferred. However, when an Ni-plating layer is provided, the structure of the plating layers is determined so that the Ni-plating layer does not come in contact with the Sn-plating layer which is the outermost layer. [0018]
    [0019] FIGS. 1 and 2 show preferred configurations of plating layers of terminal materials according to the present invention. [0019]
    [0020] A terminal material [0020] 1 in FIG. 1 has
    [0021] (A) a Cu-plating layer [0021] 11 provided on a base material 10, and an Sn-plating layer 12 as the outermost layer provided thereon.
    [0022] A terminal material [0022] 2 in FIG. 2 has
    [0023] (B) an Ni-plating layer [0023] 13 provided on a base material 10, a Cu-plating layer 11 provided thereon, and an Sn-plating layer 12 as the outermost layer provided thereon.
    [0024] The preferred thicknesses of the aforementioned plating layers are as follows. [0024]
    [0025] The above case (A): [0025]
    [0026] Cu-plating layer thickness 0.5 to 1.0 μm [0026]
    [0027] Sn-plating layer thickness 1.0 to 3.0 μm [0027]
    [0028] The above case (B): [0028]
    [0029] Ni-plating layer thickness 1.0 to 3.0 μm [0029]
    [0030] Cu-plating layer thickness 0.5 to 1.0 μm [0030]
    [0031] Sn-plating layer thickness 1.0 to 3.0 μm [0031]
    [0032] The predetermined plating layers are formed on a base material by a plating method which is commonly known, so that each of the aforementioned terminal materials according to the present invention can be produced. [0032]
    [0033] Each of the terminal materials according to the present invention is used suitably as a material for forming a crimp portion of an electric wire crimp terminal. [0033]
    [0034] That is, as described above, the present invention provides a terminal, preferably an electric wire crimp terminal, which has: [0034]
    [0035] (1) a crimp portion formed of one of the aforementioned terminal materials; and [0035]
    [0036] (2) a contact portion. [0036]
    [0037] Hereinafter, the aforementioned terminal material will be referred to as a crimp portion material. [0037]
    [0038] The contact portion of the terminal according to the present invention is formed of a terminal material (hereinafter also referred to as contact portion material simply) in which a plurality of plating layers preferably containing an Sn-plating layer or an Au-plating layer as its outermost layer are provided on a base material. [0038]
    [0039] Here, preferred examples of the plurality of plating layers in the aforementioned contact portion material include: [0039]
    [0040] (C) an Ni-plating layer and an Sn-plating layer; [0040]
    [0041] (D) an Ni-plating layer and an Au-plating layer; [0041]
    [0042] (E) a Cu-plating layer, an Ni-plating layer and an Sn-plating layer; and [0042]
    [0043] (F) a Cu-plating layer, an Ni-plating layer and an Au-plating layer; [0043]
    [0044] wherein the plating layers are provided on a base material in the aforementioned order. Incidentally, in each of the examples (D) and (F), an example in which a Pb—Ni-plating layer is provided between the Ni-plating layer and the Au-plating layer is preferred. Further, the aforementioned base material may be composed of Cu or a Cu alloy such as brass, similarly to the case of the crimp portion material of the present invention which was described above in detail. [0044]
    [0045] Preferred thicknesses of the respective plating layers of the aforementioned contact portion materials are as follows. [0045]
    [0046] The above case (C): [0046]
    [0047] Ni-plating layer thickness 1.0 to 3.0 μm [0047]
    [0048] Sn-plating layer thickness 1.0 to 3.0 μm [0048]
    [0049] The above case (D): [0049]
    [0050] Ni-plating layer thickness 0.1 to 0.5 μm [0050]
    [0051] Au-plating layer thickness 0.1 to 0.5 μm [0051]
    [0052] The above case (E): [0052]
    [0053] Cu-plating layer thickness 0.5 to 1.0 μm [0053]
    [0054] Ni-plating layer thickness 1.0 to 3.0 μm [0054]
    [0055] Sn-plating layer thickness 1.0 to 3.0 μm [0055]
    [0056] The above case (F): [0056]
    [0057] Cu-plating layer thickness 0.5 to 1.0 μm [0057]
    [0058] Ni-plating layer thickness 1.0 to 3.0 μm [0058]
    [0059] Au-plating layer thickness 0.1 to 0.5 μm [0059]
    [0060] The thickness of a Pd—Ni layer provided as occasion demands is preferably 0.5 to 3.0 μm. [0060]
    [0061] The aforementioned contact portion material is preferred in that the material has a function of suppressing diffusion from the terminal base material to the surface layer and a function of preventing the production of any oxide film in the surface contact portion. [0061]
    [0062] Plating layers are formed by a known plating method so that the contact portion material described above in detail can be produced in the same manner as the crimp portion material. [0062]
    [0063] Further, as combinations of plating layers of the crimp portion material and plating layers of the contact portion material, a combination of (A) and (E) or a combination of (A) and (F) (FIG. 5), and a combination of (B) and (C) or a combination of (B) and (D) (FIG. 6) are preferred in terms of easiness in the production of the terminal according to the present invention and in terms of performance of the terminals of the invention. [0063]
    [0064] The terminal according to the present invention is constituted by a crimp portion formed of the aforementioned crimp portion material, and a contact portion formed of the aforementioned contact portion material. A preferred method for producing the terminal will be described below. [0064]
    [0065] The same base material is used for the crimp portion and the contact portion, and plating is applied to predetermined positions on the base material so as to form a crimp portion material and a contact portion material in the predetermined positions respectively. The resulting material is press-molded into a predetermined terminal shape, or partial plating is further applied to a predetermined position in the way of molding. Then, the resulting material is molded into the final form of a terminal. Thus, a terminal according to the present invention can be produced. [0065]
    [0066] Even if the aforementioned terminal according to the present invention is exposed to a high temperature atmosphere for a long time as an electric wire crimp terminal, the increase of contact resistance in the crimp portion is lightened greatly so that it is excellent in long-term continuous reliability. [0066] EXAMPLES
    [0067] The present invention will be described below on the basis of examples, but the scope of the present invention is not limited to those examples. [0067] Example 1
    [0068] A terminal material (crimp portion material) having a structure shown in FIG. 2 was produced. Here, the thicknesses of the respective plating layers were as follows. [0068]
    [0069] Sn-plating layer: 1.0 to 3.0 μm [0069]
    [0070] Cu-plating layer: 0.5 to 1.0 μm [0070]
    [0071] Ni-plating layer: 1.0 to 3.0 μm [0071]
    [0072] Further, a base material was brass. [0072]
    [0073] The terminal material and an electric wire (oxygen-free copper) were connected while the crimping condition was changed (C/H: 1.00 mm (low), 1.15 mm (medium), 1.30 mm (high)). After the resulting material was then left in an oven at 120° C. for 500 hours, contact resistance at the crimp portion was measured. The result is shown in Table 1. [0073] Comparative Example 1
    [0074] Example 1 was repeated except that the Cu-plating layer and the Ni-plating layer in Example 1 were exchanged to each other as shown in FIG. 3 so that the Sn-plating layer [0074] 12 and the Ni-plating layer 13 contacted each other directly. The result is shown in Table 1. Comparative Example 2 Prior Art
    [0075] Example 1 was repeated except that the Cu-plating layer in Example 1 was not provided as shown in FIG. 4 so that the Sn-plating layer [0075] 12 and the Ni-plating layer 13 contacted each other directly, and except that contact resistance was also measured after the terminal material was left for 120 hours. The result is shown in Tables 1 and 2. TABLE 1 Connection Resistance (mΩ) Initial Crimping Condition (C/H)Value Low Medium High Example 1 0.4 0.4 0.9  25 Com. 0.4 0.4 3.3 400 Example 1 Com. 0.4 — 3.3 — Example 2
    [0076] [0076]TABLE 2 Contact Resistance (mΩ)Initial Value 120 hours 500 hours Comparative 0.4 3.0 3.3 Example 2
    [0077] It is apparent from Tables 1 and 2 showing the results of the aforementioned Example and Comparative Examples that, when the terminal material according to the present invention is used for the crimp portion of the terminal, the increase of contact resistance is lightened greatly even in the case where the crimp portion is exposed to a high temperature. This fact means that the long-term connection reliability of the aforementioned crimp portion according to the present invention is secured. Furthermore, these data also show that the crimp condition (C/H) under which the long-term connection reliability is secured is wide-ranged. [0077]
    [0078] When the terminal material according to the present invention is used for a crimp portion of a crimp terminal, the contact resistance hardly increases even in the case where the crimp portion is exposed to a high temperature. Consequently, the long-term connection reliability of the aforementioned crimp portion is secured in a wide range of the crimp condition (C/H). [0078]
    权利要求:
    Claims (16)
    [1" id="US-20010008709-A1-CLM-00001] 1. A terminal material comprising:
    a base material; and
    a plurality of plating layers provided on said base material and containing an Sn-plating layer as its outermost layer.
    [2" id="US-20010008709-A1-CLM-00002] 2. A terminal material according to
    claim 1 , wherein said plating layers are composed of a Cu-plating layer and said Sn-plating layer, and said plating layers are provided on said base material in an order mentioned above.
    [3" id="US-20010008709-A1-CLM-00003] 3. A terminal material according to
    claim 1 , wherein said base material is composed of a material selected from the group consisting of Cu and Cu alloys.
    [4" id="US-20010008709-A1-CLM-00004] 4. A terminal material according to
    claim 1 , wherein said terminal material constitutes a crimp portion of an electric wire crimp terminal.
    [5" id="US-20010008709-A1-CLM-00005] 5. A terminal comprising:
    a crimp portion formed of a terminal material recited in
    claim 1 .
    [6" id="US-20010008709-A1-CLM-00006] 6. A terminal according to
    claim 5 , further comprising a contact portion formed of a terminal material including said base material and a plurality of contact portion plating layers provided on said base material, an outermost layer of said contact portion plating layers being a layer selected from the group consisting of an Sn-plating layer and an Au-plating layer.
    [7" id="US-20010008709-A1-CLM-00007] 7. A terminal according to
    claim 6 , wherein:
    said contact portion plating layers of said terminal material of said contact portion are composed of layers selected from the group consisting of (1) an Ni-plating layer and an Sn-plating layer, (2) an Ni-plating layer and an Au-plating layer, (3) a Cu-plating layer, an Ni-plating layer and an Sn-plating layer, and (4) a Cu-plating layer, an Ni-plating layer and an Au-plating layer; and
    the respective layers of said contact portion plating layers are provided on said base material in an order mentioned above.
    [8" id="US-20010008709-A1-CLM-00008] 8. A terminal according to
    claim 5 , wherein said terminal is an electric wire crimp terminal.
    [9" id="US-20010008709-A1-CLM-00009] 9. A terminal material comprising:
    a base material; and
    a plurality of plating layers provided on said base material, said plating layers containing an Sn-plating layer as its outermost layer and an Ni-plating layer, and said plating layers being constituted so that said Sn-plating layer is prevented from coming in contact with said Ni-plating layer.
    [10" id="US-20010008709-A1-CLM-00010] 10. A terminal material according to
    claim 9 , wherein said plating layers are composed of said Ni-plating layer, a Cu-plating layer and said Sn-plating layer, said plating layers being provided on said base material in an order mentioned above.
    [11" id="US-20010008709-A1-CLM-00011] 11. A terminal material according to
    claim 9 , wherein said base material is composed of a material selected from the group consisting of Cu and Cu alloys.
    [12" id="US-20010008709-A1-CLM-00012] 12. A terminal material according to
    claim 9 , wherein said terminal material constitutes a crimp portion of an electric wire crimp terminal.
    [13" id="US-20010008709-A1-CLM-00013] 13. A terminal comprising:
    a crimp portion formed of a terminal material recited in
    claim 9 .
    [14" id="US-20010008709-A1-CLM-00014] 14. A terminal according to
    claim 13 , further comprising a contact portion formed of a terminal material including said base material and a plurality of contact portion plating layers provided on said base material, an outermost layer of said contact portion plating layers being a layer selected from the group consisting of an Sn-plating layer and an Au-plating layer.
    [15" id="US-20010008709-A1-CLM-00015] 15. A terminal according to
    claim 14 wherein:
    said contact portion plating layers of said terminal material of said contact portion are composed of layers selected from the group consisting of (1) an Ni-plating layer and an Sn-plating layer, (2) an Ni-plating layer and an Au-plating layer, (3) a Cu-plating layer, an Ni-plating layer and an Sn-plating layer, and (4) a Cu-plating layer, an Ni-plating layer and an Au-plating layer; and
    the respective layers of said contact portion plating layers are provided on said base material in an order mentioned above.
    [16" id="US-20010008709-A1-CLM-00016] 16. A terminal according to claims 13, wherein said terminal is an electric wire crimp terminal.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6451449B2|2002-09-17|Terminal material and terminal
    US6326052B1|2001-12-04|Ceramic capacitor
    CA2092636C|1997-06-10|Bulk metal chip resistor
    US3621442A|1971-11-16|Terminal connection of electronic devices
    US6183885B1|2001-02-06|Fitting-type connection terminal
    US5981090A|1999-11-09|Pins for electronic assemblies
    KR100452469B1|2004-10-08|Solid electrolytic capacitor and method of manufacturing the same
    EP0331182B1|1990-09-26|Process for manufacturing a compact-stranded wire conductor for wire harnesses
    CA2240239A1|1999-12-10|Tin coated electrical connector
    JP3701448B2|2005-09-28|Mating type connection terminal
    GB2097173A|1982-10-27|Stabilized multifilament superconductor
    JP4636453B2|2011-02-23|Electrical contact strip
    KR19990082048A|1999-11-15|Apparatus used in electronic control apparatus and manufacturing method
    JPH0855521A|1996-02-27|Conductive member and its manufacture
    US3641300A|1972-02-08|Electrical contact
    JP2006501615A|2006-01-12|Electrical contact
    JP2000294053A|2000-10-20|Stabilized compisite superconductive wire and its manufacture
    WO2017126283A1|2017-07-27|Vehicle-mounted electronic module, card edge connector, and connector
    EP0538019A2|1993-04-21|Lead frame for a semiconductor device
    US3596030A|1971-07-27|Composite electric element of silver-cadmium oxide alloy contact
    JPH1060666A|1998-03-03|Tin or tin alloy-plated copper alloy for multipole terminal and its production
    US6323544B1|2001-11-27|Plated leadframes with cantilevered leads
    JP2974704B2|1999-11-10|Contact device for change over contact relay
    JPH10223290A|1998-08-21|Connecting terminal
    CA1308151C|1992-09-29|Electrical contact
    同族专利:
    公开号 | 公开日
    DE19747756C2|2000-05-31|
    CN1184344A|1998-06-10|
    US6451449B2|2002-09-17|
    JPH10134869A|1998-05-22|
    CN1090392C|2002-09-04|
    KR100277614B1|2001-01-15|
    DE19747756A1|1998-05-28|
    KR19980033263A|1998-07-25|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20020064677A1|2000-09-18|2002-05-30|Hiroyuki Moriuchi|Electric connector|
    GB2381963A|2001-11-13|2003-05-14|Yazaki Corp|Plated electrical terminal|
    US20060040569A1|2004-08-18|2006-02-23|Yazaki Corporation|Low insertion-force connector terminal, method of producing the same and substrate for the same|
    US20110003520A1|2008-03-19|2011-01-06|Shuichi Kitagawa|Terminal for connector and method of producing the same|
    US20110003167A1|2008-03-19|2011-01-06|Shuichi Kitagawa|Metallic material for a connector and method of producing the same|
    US20110045713A1|2008-06-30|2011-02-24|Autonetworks Technologies, Ltd.|Crimp terminal, terminal-equipped electric wire with the crimp terminal, and methods for producing them|
    US20110237113A1|2010-03-25|2011-09-29|Stephan Gassauer|Conductor insertion plug|
    US8574722B2|2011-05-09|2013-11-05|Tyco Electronics Corporation|Corrosion resistant electrical conductor|
    US9224550B2|2012-12-26|2015-12-29|Tyco Electronics Corporation|Corrosion resistant barrier formed by vapor phase tin reflow|
    US9666956B2|2014-05-19|2017-05-30|Yazaki Corporation|Minute current crimping terminal and minute current wire harness|
    EP3249753A1|2016-05-24|2017-11-29|Delphi Technologies, Inc.|Electrical contact element|
    US11038291B2|2018-06-01|2021-06-15|Toshiba Mitsubishi-Electric Industrial Systems Corporation|Insulating cover|
    US11171428B2|2018-10-22|2021-11-09|Yazaki Corporation|Terminal metal part with protective film layers to suppress galvanic corrosion|DE2356351C3|1973-11-12|1980-07-03|Siemens Ag, 1000 Berlin Und 8000 Muenchen|Process for the production of a hot-dip tinned wire for electrotechnical purposes|
    US4189204A|1978-03-16|1980-02-19|Eaton Corporation|Integrated wire termination system with reflow bonded retainer|
    JPS6019630B2|1979-07-18|1985-05-17|Nippon Mining Co||
    US4503131A|1982-01-18|1985-03-05|Richardson Chemical Company|Electrical contact materials|
    JPS5936954A|1982-08-25|1984-02-29|Hitachi Cable Ltd|Lead frame for semiconductor|
    US5129143A|1982-11-29|1992-07-14|Amp Incorporated|Durable plating for electrical contact terminals|
    JPS59145537A|1984-02-08|1984-08-21|Hitachi Ltd|Semiconductor device|
    US4785137A|1984-04-30|1988-11-15|Allied Corporation|Novel nickel/indium/other metal alloy for use in the manufacture of electrical contact areas of electrical devices|
    JPS60262449A|1984-06-08|1985-12-25|Hitachi Ltd|Lead frame for semiconductor|
    JPH0428932B2|1984-08-16|1992-05-15|Suzuki Sogyo Kk||
    US4756467A|1986-04-03|1988-07-12|Carlisle Corporation|Solderable elements and method for forming same|
    JPH068053B2|1986-09-19|1994-02-02|株式会社日立製作所|Thermal head|
    JPS63114083A|1986-10-30|1988-05-18|Hitachi Cable|Lead frame for connector|
    JPS63121693A|1986-11-10|1988-05-25|Hitachi Cable Ltd|Terminal for connector|
    JPH0815103B2|1987-01-09|1996-02-14|住友電気工業株式会社|Spot welding method for metal terminals|
    JPS63250036A|1987-04-06|1988-10-17|Yazaki Corp|Material for fuse|
    JP2833026B2|1989-07-05|1998-12-09|上村工業株式会社|Electroless tin plating method|
    US5069979A|1990-03-19|1991-12-03|Mitsubishi Denki Kabushiki Kaisha|Plated copper alloy material|
    US5235743A|1990-07-11|1993-08-17|Yazaki Corporation|Method of manufacturing a pair of terminals having a low friction material on a mating surface to facilitate connection of the terminals|
    JPH0484449A|1990-07-27|1992-03-17|Shinko Electric Ind Co Ltd|Tab tape|
    JPH04145606A|1990-10-05|1992-05-19|Murata Mfg Co Ltd|Winding type inductor|
    JPH051367A|1991-06-24|1993-01-08|Mitsubishi Electric Corp|Copper alloy material for electric and electronic equipment|
    JPH08167442A|1992-05-29|1996-06-25|Amp Inc|Palladium-plated electric contact|
    JPH06125026A|1992-10-12|1994-05-06|Ngk Spark Plug Co Ltd|Terminal structure and input-output terminal member and wiring board using it|
    US5307562A|1992-11-06|1994-05-03|The Whitaker Corporation|Method for making contact|
    DE9216717U1|1992-12-08|1993-02-11|W.C. Heraeus Gmbh, 6450 Hanau, De||
    JPH087960A|1994-06-16|1996-01-12|Sumitomo Electric Ind Ltd|Terminal material|
    JPH08165582A|1994-12-13|1996-06-25|Sumitomo Electric Ind Ltd|Terminal material|
    US5916695A|1995-12-18|1999-06-29|Olin Corporation|Tin coated electrical connector|
    US5780172A|1995-12-18|1998-07-14|Olin Corporation|Tin coated electrical connector|
    DE19606116A1|1996-02-20|1997-08-21|Berkenhoff Gmbh|Electrical contact elements|
    US5667659A|1996-04-04|1997-09-16|Handy & Harman|Low friction solder electrodeposits|
    US5849424A|1996-05-15|1998-12-15|Dowa Mining Co., Ltd.|Hard coated copper alloys, process for production thereof and connector terminals made therefrom|
    US6083633A|1997-06-16|2000-07-04|Olin Corporation|Multi-layer diffusion barrier for a tin coated electrical connector|
    JP6151035B2|2013-02-04|2017-06-21|レック株式会社|timer|US6204065B1|1997-03-27|2001-03-20|Ngk Insulators, Ltd.|Conduction assist member and manufacturing method of the same|
    US20050037229A1|2001-01-19|2005-02-17|Hitoshi Tanaka|Plated material, method of producing same, and electrical / electronic part using same|
    JP2007177330A|2001-01-19|2007-07-12|Furukawa Electric Co Ltd:The|Plated material, method of producing the same, and electrical/electronic parts using the same|
    JP4514012B2|2001-01-19|2010-07-28|古河電気工業株式会社|Plating material, manufacturing method thereof, and electric / electronic parts using the same|
    JP2007204854A|2001-01-19|2007-08-16|Furukawa Electric Co Ltd:The|Plated material, method of producing the same, and electrical/electronic part using the same|
    JP4514061B2|2001-01-19|2010-07-28|古河電気工業株式会社|Plating material, manufacturing method thereof, and electric / electronic parts using the same|
    TW575688B|2001-01-19|2004-02-11|Furukawa Electric Co Ltd|Metal-plated material and method for preparation thereof, and electric and electronic parts using the same|
    JP2002226982A|2001-01-31|2002-08-14|Dowa Mining Co Ltd|Heat resistant film, its manufacturing method, and electrical and electronic parts|
    JP3562719B2|2001-11-13|2004-09-08|矢崎総業株式会社|Terminal|
    JP2003151668A|2001-11-13|2003-05-23|Yazaki Corp|Terminal|
    JP2004006065A|2002-03-25|2004-01-08|Mitsubishi Shindoh Co Ltd|Fitting type connector terminal for electrical connection|
    JP4046642B2|2003-03-26|2008-02-13|財団法人くまもとテクノ産業財団|Metal materials for electronic parts that prevent whisker generation|
    JP4014528B2|2003-03-28|2007-11-28|日本碍子株式会社|Heat spreader module manufacturing method and heat spreader module|
    JP2004300524A|2003-03-31|2004-10-28|Dowa Mining Co Ltd|Sn-COATED COPPER OR COPPER ALLOY MEMBER AND ITS MANUFACTURING METHOD|
    CN100407503C|2003-08-30|2008-07-30|富士康电脑接插件有限公司|Terminal and its electroplating method|
    TWI252877B|2003-09-03|2006-04-11|Hon Hai Prec Ind Co Ltd|Terminal and method of plating the same|
    US7391116B2|2003-10-14|2008-06-24|Gbc Metals, Llc|Fretting and whisker resistant coating system and method|
    CN1868096B|2003-10-16|2010-10-13|Abb研究有限公司|Coatings of Mn+1AXn material for electrical contact elements|
    US20050249969A1|2004-05-04|2005-11-10|Enthone Inc.|Preserving solderability and inhibiting whisker growth in tin surfaces of electronic components|
    US20050249968A1|2004-05-04|2005-11-10|Enthone Inc.|Whisker inhibition in tin surfaces of electronic components|
    JP4378334B2|2005-09-09|2009-12-02|日本碍子株式会社|Heat spreader module and manufacturing method thereof|
    KR100758013B1|2006-01-06|2007-09-11|한양대학교 산학협력단|Electric contact and processing method of the same|
    JP4934456B2|2006-02-20|2012-05-16|古河電気工業株式会社|Plating material and electric / electronic component using the plating material|
    JP2009097053A|2007-10-19|2009-05-07|Hitachi Ltd|Metal strip, connector, and mehod of manufacturing metal strip|
    JP5089452B2|2008-03-19|2012-12-05|古河電気工業株式会社|Connector terminal and manufacturing method thereof|
    JP5415707B2|2008-03-19|2014-02-12|古河電気工業株式会社|Metal material for connector and manufacturing method thereof|
    CN101978562B|2008-03-19|2013-04-03|古河电气工业株式会社|Metallic material for connector and process for producing the metallic material for connector|
    JP5246503B2|2009-02-23|2013-07-24|住友電装株式会社|Terminal fitting|
    TWM379095U|2009-09-30|2010-04-21|Elitegroup Computer Sys Co Ltd|Conductive pin structure of main board and connector|
    TW201114114A|2009-10-14|2011-04-16|Hon Hai Prec Ind Co Ltd|Electrical connector contact and electroplating method thereof|
    TWI420753B|2009-12-31|2013-12-21|Hon Hai Prec Ind Co Ltd|Electrical connector contact|
    JP5394963B2|2010-03-26|2014-01-22|株式会社神戸製鋼所|Copper alloy and conductive material for connecting parts|
    IT1403926B1|2011-02-09|2013-11-08|Cembre Spa|ELECTRICAL CONNECTOR FOR THE CONNECTION OF ELECTRIC CABLES TO ELECTRICAL TERMINALS.|
    JP2012190603A|2011-03-09|2012-10-04|Sumitomo Wiring Syst Ltd|Terminal fitting|
    DE102011088211A1|2011-12-12|2013-06-13|Robert Bosch Gmbh|Contact element and method for its production|
    WO2013108874A1|2012-01-20|2013-07-25|矢崎総業株式会社|Electrical connector and method for producing same|
    CN102851714B|2012-09-14|2016-02-03|小米科技有限责任公司|Production method of the outer drain terminal of a kind of metal and products thereof|
    JP6268408B2|2013-06-24|2018-01-31|オリエンタル鍍金株式会社|Plating material manufacturing method and plating material|
    DE102016100803A1|2016-01-19|2017-07-20|Phoenix Contact Gmbh & Co. Kg|Multilayer system with tin-based layers|
    WO2019087926A1|2017-10-30|2019-05-09|三菱マテリアル株式会社|Anticorrosive terminal material, anticorrosive terminal, and electric wire end structure|
    DE102018203800B4|2018-03-13|2019-11-21|Te Connectivity Germany Gmbh|Contact pin and arrangement for connecting electrical conductors made of copper and aluminum|
    法律状态:
    1997-10-28| AS| Assignment|Owner name: YAZAKI CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ASAKURA, NOBUYUKI;FUJIMOTO, KEI;REEL/FRAME:008806/0465 Effective date: 19971021 |
    2002-08-29| STCF| Information on status: patent grant|Free format text: PATENTED CASE |
    2006-02-17| FPAY| Fee payment|Year of fee payment: 4 |
    2010-03-03| FPAY| Fee payment|Year of fee payment: 8 |
    2014-02-19| FPAY| Fee payment|Year of fee payment: 12 |
    优先权:
    申请号 | 申请日 | 专利标题
    JP8-288468||1996-10-30||
    JPHEI.8-288468||1996-10-30||
    JP8288468A|JPH10134869A|1996-10-30|1996-10-30|Terminal material and terminal|
    [返回顶部]