美国专利US20010008654A1 Zinc alloys yielding anticorrosive coatings on ferrous materials

专利PDF首页>>美国专利

专利附录

专利说明

权利要求

类似技术

同族专利

引用文献

法律状态

优先权

专利摘要:
The present invention relates to a zinc alloy yielding anti-corrosive coatings on ferrous materials; characterized as consisting of zinc plus its usual impurities and possibly aluminium and/or lead as well as alloying metals consisting of between x and y % of nickel together with between v and w % of at least one of the metal: vanadium and chrome wherein: x is equal to or higher than 0.001, preferably higher than 0.04, y is lower than or equal to 0.6, preferably lower than 0.2, v is equal to or higher than 0.001, preferably higher than 0.03, w is lower than or equal to 0.6, preferably lower than 0.04.
公开号:US20010008654A1
申请号:US09/341,069
申请日:1997-12-23
公开日:2001-07-19
发明作者:Manuel B. Ferrero；Pedro M. Tierra Royo；Jeaninne Billiet；Wilhelmus J.A.M. Sprang
申请人:NEDCOAT GROUP BV；Floridienne Chimie SA；Otto Junker GmbH；Siegener Verzinkerei Holding GmbH；Industrial Galvanizadora SA；Bammens Groep BV；
IPC主号:C23C2-06

专利说明:
[0001] The present invention is related to zinc alloys yielding anticorrosive coatings on ferrous materials, consisting of zinc, plus its usual impurities and possibly aluminium or lead together with alloying metals: nickel as well as vanadium and/or chrome. [0001] BACKGROUND OF THE INVENTION
[0002] Corrosion is a frequent but undesirable process in certain metals. To avoid corrosion the metals are usually coated with a layer of zinc. [0002]
[0003] There are different methods known and used to coat steel and other metals with zinc and zinc alloys, such as: hot dip galvanising, zinc spraying, etc. One of the oldest methods still in use for economical and technical reasons is the so-called hot dip galvanising process. [0003]
[0004] Hot dip galvanising basically consists of the immersion, for a few minutes, of ferrous materials in a molten zinc bath at a temperature of between 430 and 560° C. [0004]
[0005] Hot dip immersion produces a physicochemical mechanism by which a diffusion process takes place between the base iron of the parts and the zinc. [0005]
[0006] The zinc coating gives the necessary good corrosion resistance to ferrous metals. [0006]
[0007] In general, a zinc coating obtained by hot dip galvanising consists of several layers: an internal alloy of iron and zinc which adheres to the surface of the ferrous material, and an external layer, consisting almost entirely of pure zinc, according to the composition of the bath, called the Eta phase. In the interior layer, formed by the diffusion of zinc into the ferrous material, up to three zones or sub-layers can be distinguished, identified by their different iron contents. The sub-layer closest to the base material is called the Gamma phase and contains 21 to 28% iron. Next is the Delta phase, which contains from 6% to 11% iron, and finally the Zeta phase which contains approximately 6% iron. [0007]
[0008] Depending on the composition of the ferrous material of the part to be coated, the Zeta phase varies greatly in thickness and often tends to pass through to the external layer consisting mainly of pure zinc. [0008]
[0009] When e.g. construction grade steel is galvanized in a conventional zinc bath, without additional alloying metals, a galvanised coating with a relatively thin Delta phase and a Zeta layer are produced. The Zeta layer consists of large column crystals and reaches out to very near to the surface of the coating, while the Eta layer of pure zinc is almost non-existent. [0009]
[0010] The resulting coating layer has very low adherence because of the thick iron rich Zeta phase. [0010] PRIOR ART
[0011] PATENT ABSTRACTS OF JAPAN, vol. 096, no. 007, Jul. 31, 1996 & JP 08 060329 A (KOBE STEEL LTD) concerns the production of galvannealed steel sheet in a continuous hot-dip process wherein the zinc coating bath contains Al, as well as Ni, Co and/or Ti. [0011]
[0012] PATENT ABSTRACTS OF JAPAN, vol. 018, no. 052 (C-1158), Jan. 27, 1994 & JP 05 271892 A (NISSHIN STEEL CO. LTD), describes a method for controlling galvanising bath. The aim of this invention is to reduce the influence of aluminium on the zinc bath in continuous hot-dip galvanising of steel sheet by the Ni addition. The coating bath contains Zn, Al and Ni. [0012]
[0013] PATENT ABSTRACTS OF JAPAN, vol. 017, no. 345 (C-1077), Jun. 30, 1993 & JP 05 044006 A (NIPPON STEEL CORP) is related to the production of alloyed hot-dip galvanising steel sheet having excellent workability and corrosion resistance. The galvanising bath contains Al and V. [0013]
[0014] PATENT ABSTRACTS OF JAPAN, vol. 017, no. 678 (C-1141), Dec. 13, 1993 & JP 05 222502 A (KAWASAKI STEEL CORP) concerns Zn—Cr—Al series hot-dip galvanised steel excellent in corrosion and peeling resistance and its manufacture. The goal of this invention is to obtain hot-dip galvanised steel using Zn—Cr—Al alloy with an excellent corrosion and peeling off resistance. On the surface of the steel to be galvanized is previously deposited a substance containing phosphorous. [0014]
[0015] PATENT ABSTRACTS OF JAPAN, vol. 016, no. 168 (C-0932), Apr. 22, 1992 & JP 04 013856 A (NIPPON STEEL CORP), describes the production of galvannealed steel sheet having a superior corrosion resistance in a continuous hot-dip. The galvanising bath consists in a Zn—Al—Cr alloy and includes a subsequent heat treatment at about 510° C. [0015]
[0016] PATENT ABSTRACTS OF JAPAN, vol. 018, no. 114 (C-1171), Feb. 24, 1994 & JP 05 306445 A (NIPPON STEEL CORP) is related to the manufacture of P-containing high strength galvannealed steel sheet. The phosphorous content is 0.01-0.2% and the composition of the bath is zinc, aluminium and one or-two of the following elements: Mn, Mg, Ca, Ti, V, Cr, Co and Ce. [0016]
[0017] The document GB 1 493 224 A (ITALSIDER SPA) concerns a zinc-based alloy of continuous coating of wire and steel sheet using the Sendzimir technique. The coating bath consists in Zn, Al, Mg, Cr, Ti. [0017]
[0018] The document EP 0 042 636 A (CENTRE RECHERCHE METALLURGIQUE) is about a process characterized by the use of a coating bath containing zinc with the addition of one or two of the following elements: Al, Be, Ce, Cr, La, Mg, Mn, Pb, Sb, Si, Sn, Ta, Ti, Te and Th to obtain over the first coating a supplementary protection layer formed by stable compounds. [0018]
[0019] None of these documents suggest the use of nickel together with vanadium and/or chrome as alloying metals for zinc. [0019] AIMS OF THE INVENTION
[0020] The aims of the invention are to provide improved zinc base alloys used to coat parts made of ferrous material having a superior corrosion resistance. [0020]
[0021] Surprisingly, it was found that these aims could be achieved by means of specific alloying metals, more particularly by means of zinc alloy yielding anticorrosive coatings on ferrous materials characterized as consisting of zinc plus its usual impurities and possibly aluminium and/or lead as well as alloying metals consisting of between x and y% of nickel together with between v and w% of at least one of the metals: vanadium and chrome wherein: [0021]
[0022] x is equal to or higher than 0.001, preferably higher than 0.04, [0022]
[0023] y is lower than or equal to 0.6, preferably lower than 0.2, [0023]
[0024] v is equal to or higher than 0.001, preferably higher than 0.03, [0024]
[0025] w is lower than or equal to 0.6, preferably lower than 0.04. [0025]
[0026] All the indicated percentages are expressed as % w/w throughout the specification and claims. [0026]
[0027] Without being bound by the explanations given, Applicants have observed that the use of these alloys produces a much thinner Zeta layer, resulting in an improvement of its mechanical resistance, and a relatively much thicker Eta layer, resulting in an important increase in the corrosion resistance of the coating. Vanadium giving generally better results than chrome is also usually preferred. [0027]
[0028] Preferably, the zinc content of the alloy is at least 90% and more preferably at least 95% and the aluminium content is equal to or lower than 0.25%, and more preferably between 0.001 and 0.25%, while the lead content is between 0 and 2% and more usually below 1.2%. [0028]
[0029] The most frequent “impurity” in zinc bath is iron and iron may thus be present in quantities up to the solubility limit of Fe in zinc bath at the different operation temperatures. [0029]
[0030] When the ferrous material is galvanized in a zinc alloy according to the invention, the coating structure is very different from that obtained when galvanized without said alloying metals. The Delta phase is very similar in appearance, but the Zeta layer, normally consisting of large column crystals, has been transformed into a relatively thin layer of crystals as a result of the inhibiting (levelling) action of the alloying metals, nickel, vanadium, and/or chrome. A thick layer of zinc also appears (Eta phase) which, otherwise, is much thinner when galvanising without said alloying metals. The new galvanised structure, with a relatively thin Delta and Zeta layers, increases the ductility and adherence of the coating, as well as the corrosion resistance due to the relatively greater thickness of the external layer of zinc. [0030]
[0031] The alloys according to the invention may be used with different types of steel, especially those having a high content of Si and/or P and/or Al, as they reduce the reactivity thereof, in addition to enhancing corrosion resistance. [0031]
[0032] The galvanising of ferrous material using the alloys of the invention are typically performed by batch hot-dip galvanising processes, although the use of a continuous hot-dip galvanizing process is also contemplated. [0032] EXAMPLES
[0033] Series of tests were conducted on steel sheets whose dimensions are: 200×100×3.5 mm, with the following coatings: [0033]
[0034] Hot-dip galvanized samples in a bath which composition was: 0.005% Al, 0.150% Ni, 0.045% V and the balance Zn. Samples are named “A-1” o “A-10”. The working method and galvanizing tests characteristics are given hereafter and in Table I. [0034]
[0035] Hot-dip galvanized samples in a bath with the following composition: 0.004% Al and the balance Zn. These samples are nominated as: “B-1” to “B-10”. Working method and galvanizing tests characteristics are given hereafter and in Table II. [0035]
[0036] All corrosion tests were conducted according to ASTM-B-117-90. [0036]
[0037] The results of Table I and Table II are shown in FIG. 1. [0037] Working Method
[0038] 1. Degreasing: 6% aqueous solution Galva Zn-96, during 20 min. [0038]
[0039] 2. Pickling: 50% Hydrochloric acid, until total clean. [0039]
[0040] 3. Rinsing: In water (pH=7) [0040]
[0041] 4. Fluxing: 1 min. at 80° C. [0041]
[0042] 5. Drying: Electric oven: 5 min. at 120° C. [0042]
[0043] 6. Galvanizing: See Tables. For all tests Immersion/Extraction V in/out=2/2 m/min. [0043]
[0044] 7. Cooling: In the air [0044] Steel Composition
[0045] 0,075%C, 0,320%Mn, 0,020%Si, 0,012%S, 0,013%P, 0,040%AL, 0,020%Cr, 0,020%Ni, 0,035%Cu [0045]
[0046] The microstructure of the coatings was examined under optical microscopy, using clear field and polarised light techniques on samples etched with nital at 2% (nitric acid at 2% in ethanol) and under scanning electron microscope (SEM) on polished sections. The distribution and analyses of the elements was determined by X ray spectrometry (EDS) and glow discharge optical spectroscope (GDOS). With the two techniques, EDS and GDOS, it was possible to observe that the alloying metals nickel and vanadium are sited mainly between the Delta and Zeta phases of the coating, restricting the growth of both intermetallic phases. This results in a more homogeneous coating with a thinner intermetallic layer, which provides great adherence and ductility, increasing the mechanical resistance of the coating. It also produces an external zinc layer which is thicker and more compact, thus greatly improving corrosion resistance. [0046]
[0047] To estimate the adherence of the coating, which reflects its mechanical resistance, the ASTM A-123 standard hammer test was used. The results of these tests show the strong adherence of the coatings obtained using the inventions. The coating did not fracture between the two hammer blows, while the zinc coating without alloying metals fractured under the same conditions. [0047]
[0048] To compare the corrosion resistance of conventional galvanised coatings with those obtained using the protocols of the invention, accelerated corrosion tests were undertaken. The results are to be found in FIG. 1. [0048]
[0049] The graph shows the initial coating thickness required to resist corrosion in a salt-spray chamber, in accordance with the ASTM B-1 17-90 standard, for the time shown along the X-axis. [0049]
[0050] The results on the left-hand (which represents substantially a parabolic curve) are the resistance values of a galvanised zinc product without alloy to be found in Table II. The results on the right-hand (which represents substantially a straight line) are the values given by a galvanised product using the alloy shown in Table I. [0050]
[0051] The graph shows that for the minimum thickness accepted as an industrial standard, 40 μm, the conventionally galvanised product resists for 400 hours, while the galvanised product with alloys, subject to the invention, resists corrosion for over 1300 hours. 70 μm of conventional galvanised product resists for some 600 hours, while a product coated in accordance with the invention resists corrosion for more than 2300 hours. With conventional galvanising, increasing the coating to a thickness of over 140 μm does not improve resistance to more than 900 hours, while galvanising with the alloy subject to the invention would make it possible to obtain corrosion resistance of over 2400 hours, with an increased thickness of slightly more than 70 μm. [0051]
[0052] With a minimum thickness of 40 μm, the invention offers a level of corrosion resistance which would need a thickness of much more than 160 μm if conventionally galvanised. This clearly shows that the invention not only improves the mechanical and, corrosion resistances spectacularly, but also allows a saving in the consumption of zinc of more than 75%. [0052]
[0053] Further comparisons of a composition according to the invention and the other compositions have been conducted under operation conditions as mentioned below: [0053]
[0054] 1. Degreasing: Cetenal 70 and 9590 [0054]
[0055] 2. Rinsing: in water (pH=7) [0055]
[0056] 3. Pickling: until clean [0056]
[0057] 4. Rinsing: in water (pH=7) [0057]
[0058] 5. Fluxing: 1 minute, G105 200 g/l T=cold [0058]
[0059] 6. Drying: Above the bath until dry [0059]
[0060] 7. Galvanizing: T=440° C., t[0060] _im=varies V_in/out=10/10 m/min
[0061] The other operation conditions and results are mentioned in Table III hereafter. [0061]
[0062] Having described in detail the nature of the invention, and having given practical examples of its use, it should be noted that modifications may be made thereto, as long as such do not represent a substantial change to the characteristics claimed below. [0062] TABLE I (Invention)Thickness of Hours until Example Temperature T immersion the coating appearance of Nos. (° C.) (sec) (μm) 5% red rust A1 442 120 42.8 1540 A2 440 140 60.3 1540 A3 439 160 68.3 1600 A4 440 200 74.4 1600 A5 439 260 80.2 1650 A6 440 400 87.5 1850 A7 441 500 93.4 2120 A8 439 600 106.9 2200 A9 440 800 113.4 2100 A10 440 1000 129.6 2400
[0063] [0063] TABLE II (Conventional)Thickness of Hours until Example Temperature T immersion the coating appearance of Nos. (° C.) (sec) (μm) 5% red rust B1 441 30 42.8 430 B2 441 60 60.3 590 B3 440 90 68.3 650 B4 441 120 74.4 690 B5 440 150 80.2 720 B6 441 180 87.5 760 B7 439 240 93.4 800 B8 441 300 106.9 820 B9 440 480 113.4 840 B10 442 600 129.6 890
[0064] [0064] TABLE III Composition of the Number of coating Zinc bath hours before 5% Sample thickness Temperature [% w/w] red rust occurs number [μm] [° C.] Ni V Pb Al Fe [hours] 1 61 440 0.190 0.000 0.070 0.002 0.008 450 2 61 440 0.183 0.040 0.052 0.006 0.009 1150

权利要求:
Claims (9)
[1" id="US-20010008654-A1-CLM-00001] 1. Zinc alloy intended for anti-corrosive coatings on ferrous materials, consisting of 0-0.25% aluminium, 0-1.2% lead, 0.001-0.6% nickel and 0.001-0.6% vanadium, balance being zinc and usual impurities.
[2" id="US-20010008654-A1-CLM-00002] 2. Zinc alloy according to
claim 1 wherein the nickel content is 0.04-0.2%.
[3" id="US-20010008654-A1-CLM-00003] 3. Zinc alloy according to
claim 1 or
2 wherein the vanadium content is 0.03-0.04%.
[4" id="US-20010008654-A1-CLM-00004] 4. Zinc alloy according to any of the
claims 1 to
3 wherein the zinc content is at least 90%.
[5" id="US-20010008654-A1-CLM-00005] 5. Zinc alloy according to any of the
claims 1 to
4 wherein the zinc content is at least 95%.
[6" id="US-20010008654-A1-CLM-00006] 6. Zinc alloy according to any of the
claim 1 to 5, wherein the aluminium content is 0.001-0.25%.
[7" id="US-20010008654-A1-CLM-00007] 7. Zinc alloy according to any of the
claims 1 to
6 , wherein the lead content is 0-1.2%.
[8" id="US-20010008654-A1-CLM-00008] 8. Process for yielding anti-corrosive coatings on ferrous materials wherein
claims 1 to
7 are applied in a batch hot-dip galvanising process.
[9" id="US-20010008654-A1-CLM-00009] 9. Process for yielding anti-corrosive coatings on ferrous materials wherein the alloys according to any of the
claims 1 to
7 are applied in a continuous hot-dip galvanising process.

类似技术:

公开号 | 公开日 | 专利标题

JP4457667B2|2010-04-28|Surface-treated steel sheet

KR100586437B1|2006-06-08|Zn-Al-Mg-Si ALLOY PLATED STEEL PRODUCT HAVING EXCELLENT CORROSION RESISTANCE AND METHOD FOR PREPARING THE SAME

EP1184478B1|2010-05-19|Surface treated steel product prepared by tin-based plating or aluminum-based plating

KR20040007718A|2004-01-24|High-strength alloyed aluminum-system palted steel sheet and high-strength automotive part excellent in heat resistance and after-painting corrosion resistance

KR101636443B1|2016-07-05|HOT-DIP Al-Zn COATED STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME

US6458425B2|2002-10-01|Zinc alloys yielding anticorrosive coatings on ferrous materials

RU2675437C2|2018-12-19|Method for improving high-manganese steel strip weldability and coated steel strip

JPH05320952A|1993-12-07|High strength cold rolled steel sheet excellent in corrosion resistance after coating

EP0632141B1|1998-03-04|Surface treated steel sheet and method therefore

JP2002146502A|2002-05-22|Galvanized high strength steel having good appearance

JP3485410B2|2004-01-13|Manufacturing method of hot-dip aluminized steel sheet with excellent heat blackening resistance

JP2627788B2|1997-07-09|High corrosion resistance hot-dip zinc-aluminum alloy coated steel sheet with excellent surface smoothness

MXPA99006234A|2000-05-01|Zinc alloys yielding anticorrosive coatings on ferrous materials

JP2756547B2|1998-05-25|Hot-dip Zn-based plating of hard-to-plate steel sheet

CZ209499A3|2000-06-14|Zinc alloys providing anticorrosive coatings to iron materials

JP2001020050A|2001-01-23|HOT DIP Zn-Al-Mg PLATED STEEL EXCELLENT IN CORROSION RESISTANCE IN NONCOATED PART AND COATED EDGE PART AND ITS PRODUCTION

JP3198900B2|2001-08-13|Manufacturing method of thin galvanized steel sheet

JP2579705B2|1997-02-12|Galvanized steel sheet with excellent formability

JP2765078B2|1998-06-11|Alloyed hot-dip coated steel sheet and method for producing the same

JP3159017B2|2001-04-23|Manufacturing method of thin galvanized steel sheet

JP3016333B2|2000-03-06|Cold drawn steel sheet for deep drawing excellent in corrosion resistance and method for producing the same

EP1186679A1|2002-03-13|Hot-dip galvanising alloy and process

KR20060074170A|2006-07-03|The method of developing hot dip galvannealed steel sheet of transformation induced plasticity steel with good adhesion property

JP2627788C|1999-11-15|

JPH06220612A|1994-08-09|High corrosion resistance stainless steel sheet plated with al-ti by vapor deposition

同族专利:

公开号 | 公开日

CA2275243A1|1998-07-09|

ES2183238T3|2003-03-16|

DK0951575T3|2002-12-16|

TR199901461T2|2001-03-21|

DE69714773T2|2003-04-24|

DE69714773D1|2002-09-19|

AT222297T|2002-08-15|

EP0951575A1|1999-10-27|

AU734221B2|2001-06-07|

US6458425B2|2002-10-01|

EP0951575B1|2002-08-14|

PT951575E|2002-12-31|

SK91599A3|2000-06-12|

HU0003932A2|2001-03-28|

EP0852264A1|1998-07-08|

IL130284D0|2000-06-01|

AU5985698A|1998-07-31|

JP2001508500A|2001-06-26|

HU0003932A3|2001-05-28|

BR9714245A|2000-04-18|

HU222318B1|2003-06-28|

PL334350A1|2000-02-28|

IL130284A|2002-08-14|

PL185615B1|2003-06-30|

WO1998029576A1|1998-07-09|

引用文献:

公开号 | 申请日 | 公开日 | 申请人 | 专利标题

US20070119715A1|2005-11-25|2007-05-31|Sacks Abraham J|Corrosion Resistant Wire Products and Method of Making Same|

US20100291404A1|2007-04-27|2010-11-18|Chien-Tsung Ou|Lead-free hot-dip galvanizing method and product|

US20110048585A1|2008-01-28|2011-03-03|Tamotsu Toki|Heat treated galvannealed steel material and a method for its manufacture|US3630792A|1969-04-28|1971-12-28|Cominco Ltd|Process for the production of colored coatings|

BE754256A|1969-10-25|1970-12-31|Stolberger Zink Ag|PURE ZINC ALLOY|

IT1036986B|1975-06-13|1979-10-30|Centro Speriment Metallurg|STEEL ALLOY AND COATED ALLOY PRODUCTS|

LU81061A1|1979-03-19|1980-10-08|Centre Rech Metallurgique|GALVANIZATION PROCESS|

BE883723A|1980-06-09|1980-12-09|Centre Rech Metallurgique|METHOD FOR THE SURFACE TREATMENT OF SURFACES PROTECTED BY A METAL COATING|

US4812371A|1986-11-17|1989-03-14|Nippon Steel Corporation|Zn-Al hot-dip galvanized steel sheet having improved resistance against secular peeling of coating|

JP3068307B2|1992-02-17|2000-07-24|川崎製鉄株式会社|Zn-Cr-Al-based hot-dip galvanized steel excellent in corrosion resistance and exfoliation resistance and method for producing the same|

JP2978947B2|1992-03-25|1999-11-15|日新製鋼株式会社|Management method of hot dip galvanizing bath|

JP2971243B2|1992-05-01|1999-11-02|新日本製鐵株式会社|Method for producing high strength galvannealed steel sheet containing P|

JP2707478B2|1992-08-24|1998-01-28|新日本製鐵株式会社|High corrosion resistant multi-layer electroplated steel sheet|

US5597656A|1993-04-05|1997-01-28|The Louis Berkman Company|Coated metal strip|

AU730209B2|1997-06-06|2001-03-01|N.V. Umicore S.A.|Galvanizing of reactive steels|WO2004020684A1|2002-08-28|2004-03-11|Umicore|Zinc alloy and process for hot-dip galvannealing of steel|

BR0318164B1|2003-03-07|2012-10-02||Nickel-zinc coated wire mesh and mesh manufacturing method.|

ES2427155T3|2006-02-02|2013-10-29|Ck Metals Co., Ltd.|Hot dip zinc galvanizing bath and zinc plated iron product|

CA2669074A1|2006-06-09|2007-12-21|Teck Cominco Metals Ltd.|High-aluminum alloy for general galvanizing|

EA020263B1|2009-01-21|2014-09-30|Сумитомо Метал Индастриз, Лтд.|Curved metallic material and process for producing same|

JP6022433B2|2013-12-03|2016-11-09|日新製鋼株式会社|Method for producing hot-dip Zn alloy-plated steel sheet|

法律状态:
1999-09-02| AS| Assignment|Owner name: INDUSTRIAL GALVANIZADORA S.A., SPAIN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FERRERO, MANUEL BERNAL;ROYO, PEDRO MIGUEL TIERRA;BILLIET, JEANINNE;AND OTHERS;REEL/FRAME:010300/0240 Effective date: 19990608 Owner name: FLORIDIENNE CHIMIE S.A., BELGIUM Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FERRERO, MANUEL BERNAL;ROYO, PEDRO MIGUEL TIERRA;BILLIET, JEANINNE;AND OTHERS;REEL/FRAME:010300/0240 Effective date: 19990608 Owner name: OTTO JUNKER GMBH, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FERRERO, MANUEL BERNAL;ROYO, PEDRO MIGUEL TIERRA;BILLIET, JEANINNE;AND OTHERS;REEL/FRAME:010300/0240 Effective date: 19990608 Owner name: SIEGENER VERZINKEREI HOLDING GMBH, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FERRERO, MANUEL BERNAL;ROYO, PEDRO MIGUEL TIERRA;BILLIET, JEANINNE;AND OTHERS;REEL/FRAME:010300/0240 Effective date: 19990608 Owner name: BAMMENS GROEP B. V., NETHERLANDS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FERRERO, MANUEL BERNAL;ROYO, PEDRO MIGUEL TIERRA;BILLIET, JEANINNE;AND OTHERS;REEL/FRAME:010300/0240 Effective date: 19990608 |

2002-02-01| AS| Assignment|Owner name: NEDCOAT GROUP BV, NETHERLANDS Free format text: CHANGE OF NAME;ASSIGNOR:BAMMENS GROUP BV;REEL/FRAME:012568/0989 Effective date: 20010315 |

2002-05-01| AS| Assignment|Owner name: NEDCOAT GROUP BV, NETHERLANDS Free format text: EXTRACT FROM THE COMMERCIAL REGISTER OF THE CHAMBER OF COMMERCE AND INDUSTRIES FOR UTRECHT EN OMSTREKEN SHOWING THE ADDRESS AND OTHER LEGAL PARTICULARS OF NEDCOAT GROUP BV.;ASSIGNOR:NEDCOAT GROUP BV;REEL/FRAME:012862/0240 Effective date: 20020422 |

2002-11-18| AS| Assignment|Owner name: NEDCOAT GROUP BV, NETHERLANDS Free format text: EXTRACT FROM THE COMMERCIAL REGISTER OF THE CHAMBER OF COMMERCE AND INDUSTRIES FOR ROTTERDAM SHOWING THE ADDRESS AND OTHER LEGAL PARTICULARS OF NEDCOAT GROUP BV;ASSIGNOR:NEDCOAT GROUP BV;REEL/FRAME:013496/0732 Effective date: 20020722 |

2006-04-19| REMI| Maintenance fee reminder mailed|

2006-10-02| LAPS| Lapse for failure to pay maintenance fees|

2006-11-01| STCH| Information on status: patent discontinuation|Free format text: PATENT EXPIRED DUE TO NONPAYMENT OF MAINTENANCE FEES UNDER 37 CFR 1.362 |

2006-11-28| FP| Expired due to failure to pay maintenance fee|Effective date: 20061001 |

优先权:

申请号 | 申请日 | 专利标题

EP97100008.8||1997-01-02||

EP97100008||1997-01-02||

EP97100008A|EP0852264A1|1997-01-02|1997-01-02|Zinc alloys yielding anticorrosive coatings on ferrous materials|

PCT/EP1997/007296|WO1998029576A1|1997-01-02|1997-12-23|Zinc alloys yielding anticorrosive coatings on ferrous materials|