    The invention relates to apparatus for manufacturing an optical fiber preform from a tube of vitreous material, the apparatus comprising: means for holding said tube during manufacture of said preform; and heater means supplying said tube with the heat energy required for manufacturing said preform. According to the invention, diffuser means are disposed around at least one of the ends of said tube to trap and diffuse light radiation generated in said tube by said heater means. The invention also applies to apparatus for drawing an optical fiber from a preform.
    公开号:US20010008078A1
    申请号:US09/280,394
    申请日:1999-04-05
    公开日:2001-07-19
    发明作者:Didier Pezet；Gerard Lavanant
    申请人:Alcatel SA；
    IPC主号:C03B37-01486
    专利说明:
    [0001] The invention relates to apparatus for manufacturing an optical fiber preform, the apparatus comprising a glassmakers' lathe for holding a glass tube by means of chucks clamped to the two ends of the tube, gas feed means for injecting gaseous compounds into the inside of the tube via a leakproof connection at one end of the tube, and a source of the energy required for causing the gaseous compounds to be deposited inside the tube or for collapsing the tube after deposition has been completed. [0001] BACKGROUND OF THE INVENTION
    [0002] In such a device, heat energy from the source is transmitted to the leakproof connection via the corresponding end of the glass tube. This connection has a sealing gasket which is thus raised to a high temperature while the gaseous compounds are being deposited or while the tube is being collapsed. Unfortunately, it is very important for the gasket to maintain good sealing so as to prevent any risk of the gaseous compounds being exhausted into the medium surrounding the apparatus, and to avoid any contamination of the deposit by the surrounding medium. [0002]
    [0003] A known solution to the problem of the leakproof connection between the gas feed means and the end of the tube being overheated consists in designing a gasket of a complex shape and in making it out of special materials so as to guarantee that the connection remains sealed at the temperatures generated by a blowtorch. Unfortunately, that solution increases the cost of manufacturing a preform. [0003]
    [0004] Another known solution to the above problem consists in holding the glass tube on the lathe by means of a tubular endpiece. In this way, the end of the tube is located at a certain distance from the leakproof connection and the corresponding chuck which come into contact only with the tubular endpiece. The inside diameter of the endpiece is slightly greater than the outside diameter of the glass tube and it is assembled thereto by adhesive acting on an overlap zone where the glass tube is received in the tubular endpiece. This establishes a discontinuity which enables a large part of the heat energy to be dissipated by means of the end section of the glass tube. Nevertheless, that solution also increases cost due to making and assembling the endpiece. [0004]
    [0005] After a preform has been subjected to an internal deposition method, similar problems arise when the preform is collapsed. At that time, the preform is held at its ends by the chucks. While the preform is being heated by the heater means for the purpose of collapsing it, the thermal radiation generated by the heater means heats the chucks that are holding the preform, thereby running a risk of the chucks becoming jammed. [0005]
    [0006] Finally, similar problems arise when drawing an optical fiber from a preform. At that time, the preform is held vertically at one of its ends by means of a chuck. While the preform is being heated by the fiber-drawing oven, the thermal radiation it generates heats the chuck that is holding the preform and that also can run the risk of the chuck becoming jammed. [0006] OBJECTS AND SUMMARY OF THE INVENTION
    [0007] An object of the invention is to solve the problem of the leakproof connection between the gas feed unit and the end of the glass tube overheating in apparatus for manufacturing a preform, and to do in a manner that combines effectiveness and low cost. [0007]
    [0008] Another object of the invention is to solve the problem of overheating the means for holding a preform while it is being collapsed or while a fiber is being drawn therefrom. [0008]
    [0009] To this end, the invention provides apparatus for manufacturing an optical fiber preform from a tube of vitreous material, the apparatus comprising: [0009]
    [0010] means for holding said tube during manufacture of said preform; and [0010]
    [0011] heater means supplying said tube with the heat energy required for manufacturing said preform, [0011]
    [0012] wherein diffuser means are placed around at least one of the ends of said tube to trap and diffuse light radiation generated in said tube by said heater means. [0012]
    [0013] The invention also provides an apparatus for drawing an optical fiber from a preform, the apparatus comprising: [0013]
    [0014] means for holding one end of said preform; and [0014]
    [0015] means for lowering said preform as held by said end through a fiber drawing oven; [0015]
    [0016] wherein diffuser means are disposed around said end of said preform to trap and diffuse light radiation generated in said end by said fiber drawing oven. [0016]
    [0017] The heat energy supplied by the heater means propagates along the tube or the preform towards its ends mainly in the form of light radiation. The heat energy which is thus trapped and diffused by the diffuser means is therefore not transmitted to the leakproof connection or to the supporting chuck, thereby contributing to reducing the heating thereof. [0017]
    [0018] Advantageously, the diffuser means has a refractive index close to that of the tube. By way of example, it can likewise be made of a vitreous material. This makes it possible to obtain good transmission of the radiation between the tube and the diffuser means. [0018]
    [0019] Also advantageously, a liquid film can be inserted between the diffuser means and the tube. The light radiation passes from the tube to the diffuser means via the liquid film, and the diffuser means diffuses it to the surrounding medium. This increases the amount of light radiation that is transmitted from the tube to the diffuser means. The liquid film can have a refractive index that is close to that of the tube and of the diffuser means. [0019]
    [0020] The invention makes it quick and easy to place the diffuser means on the glass tube, thereby making savings in equipment costs and in machine time costs. In addition, the risk of breaking the glass tube while the diffuser means is being mounted is considerably reduced compared with sticking on a tubular endpiece. [0020] BRIEF DESCRIPTION OF THE DRAWINGS
    [0021] Other characteristics and advantages of the invention will appear on reading the following description of an embodiment of the invention as shown by the drawings. In the figures: [0021]
    [0022] FIG. 1 is a diagram showing apparatus of the invention for manufacturing a preform; [0022]
    [0023] FIG. 2 is an enlarged view of FIG. 1 showing the diffuser means of the invention; and [0023]
    [0024] FIG. 3 is a diagram showing apparatus of the invention for drawing a fiber from a preform. [0024] MORE DETAILED DESCRIPTION
    [0025] A method of manufacturing a preform, e.g. the method known under the initials MCVD (for modified chemical vapor deposition) is implemented by means of apparatus comprising, FIG. 1, a glassmakers' lathe [0025] 1 which holds a silica-based tube 3 via two chucks 5A and 5B clamped onto the two ends 3A and 3B of the glass tube 3, and which cause it to rotate, R, about its axis. A gas feeder 7 serves to inject oxygen O2 charged with the vapors of compounds such as silicon tetrachloride SiCl4 and germanium tetrachloride GeCl4, for example, to be injected into the inside of the silica tube 3. A blowtorch 9 heats the silica tube 3 and moves in translation T therealong in the same direction as the direction in which the gaseous compounds flow. In FIG. 1, this direction is from the end 3A clamped in the chuck 5A towards the end 3B clamped in the chuck 5B. On coming close to the end 3B, the blowtorch 9 returns quickly to its starting point to begin a new pass.
    [0026] The blowtorch [0026] 9 supplies the heat energy required for depositing gaseous compounds inside the glass tube. In the heating zone closest to the blowtorch 9, the gaseous compounds react, forming particles which then deposit on the inside wall of the silica tube 3 downstream from the blowtorch 9 in the gas flow direction. The deposited particles are then vitrified by the blowtorch 9 as it moves along the silica tube 3.
    [0027] At the end of deposition, the silica tube [0027] 3 has a cladding precursor formed by the first-deposited layers and a core precursor formed by the last-deposited layers. The gas feeder 7 is then turned off so as to stop injecting gas. The operation of collapsing the silica tube 3 then begins, during which the blowtorch 9 raises the temperature of the silica tube 3 so as to soften the silica and cause the tube to shrink. After a “starting” pass, the blowtorch 9 is moved very slowly so as to close up the silica tube in the form of a solid preform, which preform may optionally be recharged, i.e. additional silica-based layers may optionally be deposited thereon.
    [0028] Communication between the gas feeder [0028] 7 and the silica tube 3 takes place at the end 3A of the tube via a leakproof connection 13 which includes an O-ring gasket 13A. It is very important for the gasket to be leakproof so as to prevent any risk of the gaseous compounds being rejected into the medium surrounding the apparatus and conversely any risk of the MCVD deposition being contaminated by the surrounding medium.
    [0029] In the invention, diffuser means in the form of a circularly cylindrical ring [0029] 15 are placed around the silica tube 3 close to the leakproof connection 13, downstream from the chuck 5A clamped to the end 3A of the silica tube 3. As mentioned above, the ring 15 can itself be made of silica so as to have a refractive index that is substantially equal to that of the tube 3 so that the change of index at the interface is negligible.
    [0030] A liquid is inserted between the glass ring and the tube so as to form a film [0030] 17 (see FIG. 2). The heat energy supplied by the blowtorch 9 during deposition or during collapsing propagates along the silica tube 3 towards its ends 3A and 3B mainly in the form of light radiation. By means of the liquid film 17, this light radiation passes from the tube 3 to the ring 15 which diffuses it into the surrounding medium. The heat energy that is trapped and diffused in this way by the silica ring 15 is therefore not transmitted to the leakproof connection 13, thereby contributing to reducing heating thereof. The presence of the liquid film 17 increases the transmission of the light radiation between the two parts.
    [0031] The liquid film [0031] 17 can likewise have a refractive index that is substantially equal to that of the glass ring 15 and of the glass tube 3. As can be seen in FIG. 2, the ring 15 is held in place relative to the tube 3 by means of two O-rings 19 which also hold the liquid film 17 between the ring 15 and the tube 3. By using lip gaskets, mounted in appropriate housings formed in the silica ring 15, it is possible to guarantee constant clearance relative to the silica tube 3. The liquid film 17 is distributed uniformly at the interface between the two pieces, thereby further contributing to good transmission of light radiation.
    [0032] In a variant embodiment of the invention, the liquid film [0032] 17 is inserted in contact with a surface 15I of the ring 15 which is carefully polished so as to further increase the transmission of light radiation through the interface between the ring and the tube. Provision is also made to frost the side faces 15A and 15B and the outside face 15E of the silica ring 15 so as to increase the diffusion of light radiation in the form of heat into the medium surrounding the apparatus for manufacturing the preform.
    [0033] Provision can also be made to cool the silica ring [0033] 15 by means of a compressed air blower 21 for maintaining the liquid film 17 at a temperature such that its refractive index remains substantially constant and equal to that of the ring 15 and of the tube 3. A deflector 23 prevents the cold air delivered by the blower 21 from disturbing heating of the silica tube 3 by the blowtorch 9.
    [0034] The invention is also applicable to apparatus for drawing an optical fiber from a preform. Apparatus of this type comprises (see FIG. 3) lowering means [0034] 25 for lowering a preform 27 through a fiber drawing oven 9′. The lowering means 25 comprise a blind chuck 5′ which is mounted to move in translation parallel to a fiber drawing axis L so as to displace the preform 27 by means of a glass bar 3′ that is clamped at one end in the chuck 5′ and welded at its other end to the preform 27.
    [0035] According to the invention, a glass ring [0035] 15′ is placed around the glass bar 3′ and located close to the chuck 5′ to trap and diffuse light radiation generated in the glass bar 3′ by the fiber drawing oven 9′.
    [0036] As mentioned above, the ring [0036] 15′ placed around the bar 3′ has a refractive index that is substantially equal to that of the bar 3′ so that the change of index at the interface is negligible. A liquid is then inserted between the glass ring and the bar 3′ so as to form a film 17. The heat energy supplied by the oven 9′ propagates along the bar 3′ mainly in the form of light radiation. By means of a liquid film 17, this light radiation is transmitted from the bar 3′ to the ring 15′ which diffuses it into the surrounding medium. The heat energy which is thus trapped and diffused by the silica ring 15′ is therefore not transmitted to the blind chuck 5′, thereby contributing to reducing its heating and to preventing any risk of it jamming. It is therefore no longer necessary to use a blind chuck that is made of refractory steel.
    [0037] The above-described variants apply in like manner to apparatus of the invention for drawing a glass fiber from a preform. [0037]
    [0038] The invention is not limited to the embodiments described above. [0038]
    [0039] In particular, the space between the diffuser means and the preform need not be occupied by a liquid film but can be occupied by the ambient medium. Under such circumstances, it is preferable to ensure that the diffuser means fits on the preform with small tolerance. [0039]
    [0040] In another alternative, the liquid film could be replaced by an index-matching gel or by appropriate running in. [0040]
    权利要求:
    Claims (12)
    [1" id="US-20010008078-A1-CLM-00001] 1. Apparatus for processing an elongate workpiece of optical vitreous material, the apparatus comprising:
    means for holding said workpiece during said processing; and
    heater means supplying said workpiece with heat energy required for said processing,
    wherein diffuser means are placed around at least one end of said workpiece to trap and diffuse light radiation generated in said workpiece by said heater means.
    [2" id="US-20010008078-A1-CLM-00002] 2. Apparatus according to
    claim 1 , wherein said diffuser means has a refractive index close to that of said workpiece.
    [3" id="US-20010008078-A1-CLM-00003] 3. Apparatus according to
    claim 2 , wherein said diffuser means are made of a vitreous material.
    [4" id="US-20010008078-A1-CLM-00004] 4. Apparatus according to
    claim 1 , wherein a liquid film is inserted between said diffuser means and said workpiece.
    [5" id="US-20010008078-A1-CLM-00005] 5. Apparatus according to
    claim 4 , wherein said liquid film has a refractive index close to that of said diffuser means and of said workpiece.
    [6" id="US-20010008078-A1-CLM-00006] 6. Apparatus according to
    claim 4 , wherein said liquid film is inserted in contact with a polished surface of said diffuser means.
    [7" id="US-20010008078-A1-CLM-00007] 7. Apparatus according to
    claim 1 , wherein said diffuser means possesses frosted surfaces.
    [8" id="US-20010008078-A1-CLM-00008] 8. Apparatus according to
    claim 1 , wherein said diffuser means are held fixed relative to said workpiece by gaskets.
    [9" id="US-20010008078-A1-CLM-00009] 9. Apparatus according to
    claim 8 , wherein said gaskets are lip gaskets.
    [10" id="US-20010008078-A1-CLM-00010] 10. Apparatus according to
    claim 1 , wherein a blower blows air over said diffuser means.
    [11" id="US-20010008078-A1-CLM-00011] 11. Apparatus according to
    claim 1 , wherein said workpiece is a tube for manufacturing an optical fiber preform.
    [12" id="US-20010008078-A1-CLM-00012] 12. Apparatus according to
    claim 1 , wherein said workpiece is an optical fiber preform.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6053013A|2000-04-25|Apparatus and method for overcladding optical fiber preform rod and optical fiber drawing method
    CA1054795A|1979-05-22|Optical fibres
    CA2301116C|2006-12-05|Method of and apparatus for manufacturing an optical fiber preform
    US20050000251A1|2005-01-06|Particle deposition system and method
    WO2003011779A1|2003-02-13|Method for fabricating a low polarization mode dispersion optical fiber
    US4968339A|1990-11-06|Method of fluorine doped modified chemical vapor deposition
    US6314767B2|2001-11-13|Apparatus for manufacturing an optical fiber preform and including a ring for trapping and diffusing light radiation
    US20020078714A1|2002-06-27|Method and apparatus for continuously manufacturing optical preform and fiber
    US5076824A|1991-12-31|Method of making fiber optical preform with pyrolytic coated mandrel
    KR20040076775A|2004-09-03|Method and apparatus for efficient dehydration in mcvd process
    US5039325A|1991-08-13|Method for consolidating doped glass using an encapsulating structure
    KR100277358B1|2001-01-15|Optical fiber base material manufacturing apparatus and method by chemical vapor deposition
    CN101274815B|2012-05-02|Method for welding together a primary preform and a silica bar
    US20200255322A1|2020-08-13|Enhanced Particle Deposition System and Method
    US20060016226A1|2006-01-26|Glass-body-heating apparatus and production method of optical fiber preform incorporaing the apparatus
    US20030089133A1|2003-05-15|Method of forming a glass article by collapsing an annular passage of a preform during draw
    KR100334781B1|2002-05-02|Fabrication device of optical fiber preform and method thereof
    NL2014519B1|2017-01-25|A rotary feed-through for mounting a rotating substrate tube in a lathe, a CVD lathe and a corresponding method using the CVD lathe.
    JP2624985B2|1997-06-25|Manufacturing method of high refractive index difference micro core base material
    KR19980075318A|1998-11-16|Optical fiber base material over cladding method and optical fiber drawing method
    JPH0781957A|1995-03-28|Furnace for vitrifying quartz glass fine particle and vitrifying method thereof
    同族专利:
    公开号 | 公开日
    FR2776997B1|2000-05-12|
    US20010032483A1|2001-10-25|
    FR2776997A1|1999-10-08|
    US6314767B2|2001-11-13|
    EP0949214A1|1999-10-13|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20190119144A1|2017-10-23|2019-04-25|Ofs Fitel, Llc|System and Method For Straightening And Elongating A Glass Core Rod|US1701541A|1924-03-29|1929-02-12|Charles Eisler|Construction of incandescent lamps|
    US3427143A|1965-06-08|1969-02-11|Heights Lab Glass Inc|Apparatus for forming a helically shaped glass tube|
    DE2935347A1|1979-08-31|1981-03-26|Siemens AG, 1000 Berlin und 8000 München|METHOD FOR PRODUCING GLASS FOR FIBER GLASS FIBER LOW DAMPING|
    US4286978A|1980-07-03|1981-09-01|Corning Glass Works|Method for substantially continuously drying, consolidating and drawing an optical waveguide preform|
    US4317667A|1981-01-05|1982-03-02|Western Electric Co., Inc.|Method and apparatus for fabricating lightguide preforms|
    US4347069A|1981-03-11|1982-08-31|Western Electric Company, Inc.|Method of supplying fluid to a rotating tube|
    US4389231A|1981-06-01|1983-06-21|Western Electric Company, Inc.|Method for supplying fluid to a rotating tube|
    DE3507727A1|1985-03-05|1986-09-11|AEG KABEL AG, 4050 Mönchengladbach|Device for clamping a rotatable reaction vessel|
    US4971614A|1988-09-29|1990-11-20|At&T Bell Laboratories|Method and apparatus for making optical fiber preform rods|
    DE3921086A1|1989-06-28|1991-01-03|Kabelmetal Electro Gmbh|METHOD FOR THE PRODUCTION OF LIGHT-WAVE GUIDES WITH MELTING OF A TUBE PIPE ONTO A RAW PREFORM|
    US5244485A|1991-04-30|1993-09-14|The Furukawa Electric Co., Ltd.|Method of manufacturing a silica glass preform|
    GB2291643B|1994-07-21|1998-01-28|Pirelli General Plc|Optical fibre preforms|
    KR0162604B1|1994-10-07|1999-04-15|김광호|Optical fiber preform making method|US6658896B2|2002-01-18|2003-12-09|Sunoptic Technologies Llc|Method of making a fiberoptic light guide|
    法律状态:
    1999-06-08| AS| Assignment|Owner name: ALCATEL, FRANCE Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:PEZET, DIDIER;LAVANANT, GERARD;REEL/FRAME:010006/0805;SIGNING DATES FROM 19990325 TO 19990401 |
    2005-06-02| REMI| Maintenance fee reminder mailed|
    2005-11-14| LAPS| Lapse for failure to pay maintenance fees|
    2005-12-14| STCH| Information on status: patent discontinuation|Free format text: PATENT EXPIRED DUE TO NONPAYMENT OF MAINTENANCE FEES UNDER 37 CFR 1.362 |
    2006-01-10| FP| Expired due to failure to pay maintenance fee|Effective date: 20051113 |
    优先权:
    申请号 | 申请日 | 专利标题
    FR9804229A|FR2776997B1|1998-04-06|1998-04-06|DEVICE FOR MANUFACTURING AN OPTICAL FIBER PREFORM COMPRISING A RING FOR TRAPPING AND DIFFUSING LIGHT RADIATION|
    FR9804229||1998-04-06||US09/886,125| US20010032483A1|1998-04-06|2001-06-22|Apparatus for manufacturing an optical fiber preform and including a ring for trapping and diffusing light radiation|
    [返回顶部]