    • 专利摘要:
    The present invention relates to methods of producing wool or animal hair material with improved properties such as shrink-proofed (anti-felting tendency), increased whiteness, improved dyeability, increased softness and/or reduced pilling tendency, the method comprising the steps of treating wool, wool fibres or animal hair material in a process selected from the group consisting of plasma treatment processes and the Delhey process, and subjecting the wool or animal hair material to a treatment with a proteolytic enzyme (a protease), preferably a serine protease, more preferably a subtilisin, in an amount effective for improving the properties.
    公开号:US20010003220A1
    申请号:US08/870,459
    申请日:1997-06-06
    公开日:2001-06-14
    发明作者:Lone Dybdal；Elisabeth Heine；Hartwig Hocker
    申请人:Novo Nordisk AS；
    IPC主号:D06M11-48
    专利说明:
    [0001] This application is a continuation application of PCT/DK95/00517 filed Dec. 21, 1995 and claims priority under 35 U.S.C. 119 of Danish application 1451/94 filed Dec. 21, 1994, the contents of which are fully incorporated herein by reference. [0001] FIELD OF INVENTION
    [0002] The present invention relates to a method of providing wool or animal hair with improved properties, e.g. reduced felting, increased whiteness, reduced pilling tendency, improved softness and improved dyeing characteristics, by enzymatic treatment. More specifically, the method comprises subjecting the wool or animal hair material to a plasma treatment and a treatment with a proteolytic enzyme, i.e. a protease. [0002] BACKGROUND OF THE INVENTION
    [0003] For many years, the wool industry has tried to develop methods to reduce felting of wool which do not result in release of damaging substances to the environment. Recent developments have pointed towards low-temperature plasma treatment or the Delhey process as possible solutions to this problem. [0003]
    [0004] Thus, it is known to treat wool fibre material with electrical gas discharges (socalled plasma), i.e. in a dry process. Plasma treatment provides a changed surface finish of the wool fibre which reduces the tendency to felt, improves the printability and accelerates the dyeability of the wool. The use of plasma treatment in textile finishing, especially in wool finishing, is highly advantageous, since the process potentially is an environmentally acceptable alternative to the conventional chlorination finishing processes, cf. Byrne, K. M. et al.: [0004] Corona discharge treatment of wool-commercial implications in DWI Report, (1992), vol. 109, p. 589-599, (Aachener Textiltagung 1991).
    [0005] In textile finishing, the applicable plasma treatment is a low-temperature or unbalanced plasma treatment (“cold plasma” treatment), in particular the corona discharge treatment and glow discharge treatment, cf. Thomas, H. et al.: [0005] Environmentally friendly finishing processes for wool by pretreatment with electrical discharges in gas (plasma) in ITB vol. 2, 1993. The corona discharge treatment is carried out under atmospheric conditions and is a weak-current discharge providing an oxidation, and thereby a polarization, of the fibre surface. The glow discharge treatment is carried out under reduced pressure, i.e. producing electrons of higher energy than is possible in the corona discharge treatment, and may modify the fibre surface more intensively.
    [0006] Accordingly, the plasma treatment provides to the wool or animal hair material reduced felting tendency and improved dying characteristics without the use of damaging chemicals and without wastewater (dry process). Also, the treatment provides improved shrink-proof properties to the treated material which, however, at present cannot meet the demands of the end-users. Furthermore, the treatment may reduce the soft handle of the wool or animal hair material. [0006]
    [0007] Published Japanese Patent Application Tokkai Hei 4-327274 discloses a method for a shrink-proofing treatment of e.g. wool fibers by subjecting the fibers to a low-temperature plasma treatment followed by treatment with a shrink-proofing resin, e.g. block-urethane resin, polyamide epochlorohydrin resin, glyoxalic resin, ethylene-urea resin or acrylate resin, and then a weight reducing treatment with a proteolytic enzyme for obtaining a softening effect. [0007]
    [0008] The Delhey process is described in DE-A-43 32 692 and in J. Delhey: PhD Thesis, RWTH Aachen (1994). In this process the wool is treated in an aqueous solution of hydrogenperoxide in the presence of soluble wolframate, optionally followed by treatment in a solution or dispersion of synthetic polymers, for improving the anti-felting properties of the wool. However, neither does this treatment meet the demands of the end-users. [0008]
    [0009] It is the object of the present invention to provide a method for treating wool or animal hair material to obtain wool or animal hair material with reduced felting tendency, improved softness, increased whiteness, reduced pilling tendency and/or improved dyeing characteristics, in an easy and a purely biological way without the use of environmentally damaging chemicals or resins. [0009] SUMMARY OF THE INVENTION
    [0010] Surprisingly, it has been found that certain properties of plasma-treated or Delhey-treated wool or animal hair may be improved by subjecting the plasma-treated or Delhey-treated wool or animal hair to a treatment with a proteolytic enzyme in an amount effective for providing the desired effect. Depending on the special characteristics of the actual wool subjected to the treatment according to the present invention, the improved properties can be reduction of felting tendency, higher whiteness, reduction of pilling tendency, improvement of softness, or improvement of dyeing characteristics. [0010]
    [0011] Thus, according to the present invention it is possible to obtain good and satisfactory shrink-proofing properties without the use of a shrink-proofing polymer resin by treating the wool or animal hair material with a proteolytic enzyme either prior to or after a plasma treatment, preferably a low-temperature plasma treatment, or prior to or after a Delhey-treatment. Further to the improved shrink-proofing or anti-felting properties, the enzyme treatment can also improve the dyeing characteristics of the wool or animal hair material, provide a convenient bleaching (improved whiteness) and a reduced tendency of pilling, and provide the regain of the soft handle of the treated material. [0011]
    [0012] Accordingly, the present invention relates to a method for producing wool or animal hair material with improved properties comprising the steps of [0012]
    [0013] a. pretreating wool, wool fibres or animal hair material in a process selected from the group consisting of plasma treatment processes and the Delhey process, and [0013]
    [0014] b. subjecting the pretreated wool or animal hair material to a treatment with a proteolytic enzyme (a protease) in an amount effective for improving the properties. [0014]
    [0015] It is contemplated that the treatment with a proteolytic enzyme can take place prior to the plasma treatment or after the plasma treatment, either in a separate step or e.g. in combination with the scouring or the dyeing of the wool or animal hair material. Further, a surfactant or a softener can be present in the enzyme treatment step, or a separate step wherein the wool or animal hair material is subjected to a softening treatment can be applied. [0015]
    [0016] By using the method of the present invention, it is possible to eliminate the use of environmentally damaging chemicals, since the present method is only using environmetally-friendly biological substances, and obtain improved properties of the treated wool or animal hair material which are highly desired by the end-user. [0016]
    [0017] In another aspect, the present invention further relates to wool or animal hair material which has been treated according to the method of the present invention. [0017] DETAILED DESCRIPTION OF THE INVENTION
    [0018] In the present context, the terms “shrink-proof” and “anti-felting” are intended to mean a highly reduced tendency to shrinkage or felting after soaking, washing or rinsing the material in question as compared to the tendency of shrinking or felting of material which has not been subjected to a shrink-proof or anti-felting treatment. More specifically, the present invention provides a method for producing wool or animal hair material having improved shrink-proof or anti-felting properties. [0018]
    [0019] Preferably, the shrink-proof improvement of plasma and enzyme treated wool or animal hair material corresponds to an area shrinkage which is less than 10%, more preferably less that 8%, more preferably less that 7%, more preferably less that 5%, even more preferably less than 3%, especially less that 2%, after 2 cycles of ISO 5A; or to an area shrinkage of less than 15%, more preferably less than 10%, more preferably less that 8%, even more preferably less than 6%, especially less that 5%, after 5 cycles of ISO 5A; measured according to the IWS Test Method 31. [0019]
    [0020] Preferably, the shrink-proof improvement of wool or animal hair material treated in the Delhey process followed by an enzymatic treatment corresponds to an area shrinkage which is less than 25%, more preferably less that 20%, more preferably less that 15%, more preferably less that 12%, more preferably less that 10%, more preferably less than 8%, even more preferably less than 5%, especially less that 2%, after 2 cycles of ISO 5A, or to an area shrinkage of less than 20%, more preferably less that 15%, more preferably less than 12%, even more preferably less than 10%, especially less that 9%, after 5 cycles of ISO 5A, measured according to the IWS Test Method 31. [0020]
    [0021] The IWS Test Method 31 which is available from The International Wool Secretariat is applicable to all washable wool textiles and to intermediate products including tops, hand knitting yarn, machine knitting yarn, weaving yearn and fabric for cut and sew use. The test may be used to determine the relaxation and the felting behaviour of an intermediate product. The relaxation shrinkage is determined from the dimensions of the sample befor and after subjecting the sample to wet relaxation with mild agitation. This relaxation is achieved by the International Standards Organisation International Standard ISO 6330 7A programme but differs in that the load is reduced to 1 kg. After relaxation, the felting shrinkage is determined from the dimensions of the sample before and after subjecting it to a severe agitation. This agitation is achieved by the ISO 6330 5A programme but differs in that the load is reduced to 1 kg. The number of cycles of the 5A programme to which the sample is subjected is determined by the end use of the product. In the case of intermediate products, tops are made up into yarn of a given count; yarns (including those made from the forementioned top) are made up into single jersey fabric of a standard cover factor. The single jersey knitted fabric is then tested according to the principles indicated above. [0021]
    [0022] Alternatively, the anti-felting improvement corresponds to a felt-ball density at or below 0.04, measured according to the Aachen felt-ball test IWTO-20-69. This test was developed at the Deutsche Wollforschungsinstitut, Aachen, in 1960, and is applicable to wool and mixtures of wool and synthetic fibers which can be brought into a loose condition. The principle of the test is the following: 1 g wool and 50 ml of a buffer (pH 7) is placed in a standard 150 ml steel beaker which is then shaken three-dimensionally for a given period of time. The loose wool will form a ball, and the diameter of the felt ball is measured. The larger the felting tendency of the wool is, the smaller is the measured diameter of the resulting felt ball, and the higher is the density. [0022]
    [0023] In the present context, the term “whiteness” is intended to mean how white the wool is or looks by visual determination. The degree of whiteness can conveniently be measured in a Datacolor 3890 Spectral photometer (CIELAB system). [0023]
    [0024] More specifically, the present invention provides a method for producing wool or animal hair material having improved whiteness. It is believed that the improved whiteness is due to the enzymatic treatment step which leads to an improvement of the degree of whiteness of the enzymatically treated wool. [0024]
    [0025] Preferably, the thus improved whiteness of wool or animal hair material treated in the Delhey process followed by an enzymatic treatment corresponds to an improvement in whiteness degree of at least 10 CIE units, more preferably of at least 12 CIE units, measured in the Datacolor 3890 Spectral photometer (CIELAB system). [0025]
    [0026] Also, the improved whiteness of plasma and enzyme treated wool or animal hair material corresponds to an improvement in whiteness degree of at least 8 CIE units, more preferably of at least 10 CIE units, measured in the Datacolor 3890 Spectral photometer (CIELAB system). [0026]
    [0027] In the present context, the terms “dye-uptake” or “dyestuff absorption” are intended to mean the capability of wool immersed in a dye bath to absorb the available soluble dyestuff. [0027]
    [0028] More specifically, the present invention provides a method for producing wool or animal hair material having improved dye-uptake or dyestuff absorption. It is believed that the improved dye-uptake or dyestuff absorption is partly due to the enzymatic treatment step which leads to an improvement of the capability of the enzymatically treated wool to absorb the dyestuff. [0028]
    [0029] Preferably, the improved dyeability of the produced wool or animal hair material corresponds to an increase of the colour depth by at least 2 DL (units), more preferably at least 3 DL (units), measured relative to a reference after competitive dyeing in 2% Lanasol Blue 8G. [0029]
    [0030] In the present context, the term “loss of bundle strength tenacity” is intended to mean the reduction of the bundle strength tenacity of a fiber bundle material, i.e. wool or animal hair material, which is a result e.g. of any modifications or damages suffered during processes such as dyeing, bleaching and conventional shrink-proof treatments. [0030]
    [0031] More specifically, the present invention provides a method for producing wool or animal hair material with improvement of one or more of the mentioned properties and with a limited loss of bundle strength tenacity. [0031]
    [0032] Preferably, the loss of bundle strength of the wool or animal hair material subjected to the method of the present invention corresponds to a difference in bundle strength tenacity of the produced wool or animal hair material and bundle strength tenacity of the untreated material of less than 20%, more preferably less than 10%, especially less than 6%, measured according to IWTO-32-82(E). This standard which was prepared by the “Bundle Strength of Fibres” Working Group of the IWTO Technical Committee and adopted in 1979 is intended for the determination of the tenacity of wool in the form of bundles of parallel fibres in the direction of extension, with a jaw separation of 3.20 mm, 5.00 mm or 10.00 mm. [0032]
    [0033] Further, the present invention provides a method for producing wool or animal hair material of improved softness, preferably a softness at least corresponding to the softness of untreated wool. [0033]
    [0034] In the present context, the term “reduced pilling tendency” is intended to mean a permanent (and excellent) resistance to formation of pills on the surface of the treated wool or animal hair material in comparison with corresponding material which has not been subjected to the method of the present invention. The tendency to pilling formation may be tested according to the Swiss norm SN 198525, published in 1990 by Schweizerische Normen-Vereinigung, Kirchenweg 4, Postfach, CH-8032 Zürich, Switzerland, which describes a test of pilling-resistance for textiles which in turn is based on the Swiss norms SNV 95 150 (Textiles—Standard climatic conditions and test conditions for the physical tests under standard climate conditions) and SN 198 529 (Testing of textiles—“Scheuerfestigkeit”—Martindale method). The results of the test is expressed in terms of “pilling notes” which is a rating on a scale from pilling note 1 (heavy pill formation) to pilling note 5 (no or very little pill formation), allowing ½ pilling notes. [0034]
    [0035] In another aspect, the present invention provides a method for producing wool or animal hair material having a reduced pilling tendency. [0035]
    [0036] The substrate material [0036]
    [0037] The method of the invention can be applied to any desirable animal hair product. The commercially most interesting animal hair is wool, e.g. from sheep, camel, rabbit, goat, lama, i.e. such as merino wool, shetland wool, cashmere wool, alpaca wool, mohair. [0037]
    [0038] The wool or animal hair material subjected to the method of the invention can be top, fiber, yarn, or woven or knitted fabric. The treatment with proteolytic enzymes can also be carried out on loose flock or on garment made from wool or animal hair material which has previously been plasma treated. [0038]
    [0039] It should be emphasized that wool and other animal hair are products of biological origin. The material may vary greatly e.g. in chemical composition and structure depending on the living conditions and health of the animal. Accordingly, the effect(s) obtained by subjecting wool or other animal hair products to the method of the present invention may also vary in accordance with the properties of the starting material. [0039]
    [0040] The process [0040]
    [0041] Basically, the present invention is carried out in two steps. [0041]
    [0042] The plasma treatment step is a low-temperature treatment, preferably a corona discharge treatment or a glow discharge treatment, vide supra. [0042]
    [0043] This low-temperature plasma treatment is carried out by using a gas, preferably a gas selected from the group consisting of air, oxygen, nitrogen, ammonia, helium, or argon. Conventionally, air is used but it may be advantageous to use any of the other indicated gasses. [0043]
    [0044] Preferably, the low-temperature plasma treatment is carried out at a pressure between about 0.1 torr and 5 torr for from about 2 seconds to about 300 seconds, preferably for about 5 seconds to about 100 seconds, more preferably from about 5 seconds to about 30 seconds. [0044]
    [0045] The Delhey process is described in J. Delhey: PhD Thesis RWTH Aachen 1994; and in DE-A-43 32 692 and is carried out as follows: [0045]
    [0046] The wool is treated in an aqueous solution of hydrogen peroxide (0.1-35% (w/w), preferably 2-10% (w/w)), in the presence of a 2-60% (w/w), preferably 8-20% (w/w) of a catalyst (preferably Na[0046] 2WO4), and in the presence of a nonionic wetting agent. Preferably, the treatment is carried out at pH 8-11, and room temperature. The treatment time depends on the concentrations of hydrogen peroxide and catalyst, but is preferably 2 minutes or less.
    [0047] After the oxidative treatment, the wool is rinsed with water. [0047]
    [0048] For removal of residual hydrogen peroxide, and optionally for additional bleaching, the wool may be treated further in acidic solutions of reducing agents (sulphites, phosphites etc.). [0048]
    [0049] The enzyme treatment step is preferably carried out for between about 1 minute and about 120 minutes; preferably at a temperature of between about 20° C. and about 60° C., more preferably between about 30° C. and about 50° C. Alternatively, the wool can be soaked in or padded with an aqueous enzyme solution and then subjected to steaming at a conventional temperature and pressure, typically for about 30 seconds to about 3 minutes. [0049]
    [0050] The proteolytic enzyme treatment is carried out in an acidic or neutral or alkaline medium which may include a buffer. [0050]
    [0051] It may be advantageous to carry out the enzyme treatment step in the presence of one or more conventional anionic, non-ionic or cationic surfactants. An example of a useful nonionic surfactant is Dobanol (from Henkel AG). [0051]
    [0052] Further, the wool or animal hair material may be subjected to an ultrasound treatment, either prior to or simultaneous with the treatment with a proteolytic enzyme. The ultrasound treatment may advantageously be carried out at a temperature of about 50° C. for about 5 minutes. [0052]
    [0053] It is contemplated that the reaction rate of the enzyme treatment step can be increased by increasing the temperature of the enzyme bath during the treatment, i.e. the total treatment time can be reduced. [0053]
    [0054] The amount of proteolytic enzyme used in the enzyme treatment step is preferably between about 0.2 w/w % and about 10 w/w %, based on the weight of the wool or animal hair material. [0054]
    [0055] It is to be understood that, to reduce the number of treatment steps, the enzyme treatment can be carried out during dyeing or scouring of the wool or animal hair material, simply by adding the protease to the dyeing, rinsing or scouring bath. [0055]
    [0056] Preferably, the enzyme treatment is carried out after the plasma treatment but the two treatment steps may also be carried out vice versa. [0056]
    [0057] It should be noted that the handle of plasma treated wool or animal hair is generally harsher than that of untreated wool. The enzyme treatment provides a softer handle, due to weight loss, and a reduction of stiffness of the fibres. Also, the enzyme treatment may improve the uptake of softeners, thereby improving the softening effect of additional treatments with softeners. The softness obtained by enzymatic treatment and softening agents is more durable than that obtained with softening agents alone. [0057]
    [0058] It is also well-known that plasma treatment or Delhey treatment may provide a certain shrink-proofing. The degree thereof is increased after an enzyme treatment. It is believed that the plasma treatment or Delhey treatment provides the oxidation and lipid removal necessary for the access of protease to the wool fibre surface. [0058]
    [0059] It has been established that plasma treatment and Delhey treatment have several advantages for the dyeing properties of wool. One of these advantages is the faster absorption of dyestuff at lower temperatures and an improved dye-bath exhaustion. The dye absorption is further improved by the enzyme treatment. [0059]
    [0060] The enzyme [0060]
    [0061] A useful proteolytic enzyme for the method of the present invention is any enzyme having proteolytic activity at the actual process conditions. Thus, the enzyme may be a proteolytic enzyme of plant origin, e.g. papain, bromelain, ficin, or of animal origin, e.g. trypsine and chymotrypsine, or of microbial origin, i.e. bacterial or fungal origin or from yeasts. It is to be understood that any mixture of various proteolytic enzyme may be applicable in the process of the invention. [0061]
    [0062] In a preferred embodiment of the invention, the proteolytic enzyme is a serine-protease, a metallo-protease, or an aspartate-protease. A serine protease is an enzyme which catalyzes the hydrolysis of peptide bonds, and in which there is an essential serine residue at the active site. They are inhibited by diisopropylfluorophosphate, but in contrast to metalloproteases, are resistant to ethylene diamino tetraacetic acid (EDTA) (although they are stabilized at high temperatures by calcium ions). They hydrolyze simple terminal esters and are similar in activity to eukaryotic chymotrypsin, also a serine protease. A more narrow term, alkaline protease, covering a sub-group, reflects the high pH optimum of some of the serine proteases, from pH 9.0 to 11.0 The serine proteases usually exhibit maximum proteolytic activity in the alkaline pH range, whereas the metallo-proteases and the aspartate-proteases usually exhibit maximum proteolytic activity in the neutral and the acidic pH range, respectively. [0062]
    [0063] A sub-group of the serine proteases are commonly designated as subtilisins. A subtilisin is a serine protease produced by Gram-positive bacteria or fungi. The amino acid sequence of a number of subtilisins have been determined, including at least six subtilisins from Bacillus strains, namely, subtilisin 168, subtilisin BPN, subtilisin Carlsberg, subtilisin DY, subtilisin amylosacchariticus, and mesentericopeptidase, one subtilisin from an actinomycetales, thermitase from [0063] Thermoactinomyces vulgaris, and one fungal subtilisin, proteinase K from Tritirachium album. A further subgroup of the subtilisins, subtilases, have been recognised more recently. Subtilases are described as highly alkaline subtilisins and comprise enzymes such as subtilisin PB92 (MAXACAL®, Gist-Brocades NV), subtilisin 309 (SAVINASE®, Novo Nordisk A/S), and subtilisin 147 (ESPERASE®, Novo Nordisk A/S).
    [0064] In the context of this invention, a subtilisin variant or mutated subtilisin protease means a subtilisin that has been produced by an organism which is expressing a mutant gene derived from a parent microorganism which possessed an original or parent gene and which produced a corresponding parent enzyme, the parent gene having been mutated in order to produce the mutant gene from which said mutated subtilisin protease is produced when expressed in a suitable host. [0064]
    [0065] These mentioned subtilisins and variants thereof constitute a preferred class of proteases which are useful in the method of the invention. An example of a useful subtilisin variant is a variant of subtilisin 309 (SAVINASE®) wherein, in position 195, glycine is substituted by phenylalanine (G195F or [0065] 195Gly to 195Phe).
    [0066] Conveniently, conventional fermented commercial proteases are useful. Examples of such commercial proteases are Alcalase® (produced by submerged fermentation of a strain of [0066] Bacillus licheniformis), Esperase® (produced by submerged fermentation of an alkalophilic species of Bacillus), Rennilase® (produced by submerged fermentation of a non-pathogenic strain of Mucor miehei), Savinase® (produced by submerged fermentation of a genetically modified strain of Bacillus), e.g. the variants disclosed in the International Patent Application published as WO 92/19729, and Durazym® (a protein-engineered variant of Savinase®). All the mentioned commercial proteases are produced and sold by Novo Nordisk A/S, DK-2880 Bagsvaerd, Denmark. Other preferred serine-proteases are proteases from Nocardiopsis, Aspergillus, Rhizopus, Bacillus alcalophilus, B. cereus, N. natto, B. vulgatus, B. mycoide, and subtilins from Bacillus, especially proteases from the species Nocardiopsis sp. and Nocardiopsis dassonvillei, such as those disclosed in the International Patent Application published as WO 88/03947, especially proteases from the species Nocardiopsis sp., NRRL 18262, and Nocardiopsis dassonvillei, NRRL 18133. Yet other preferred proteases are the serine proteases from mutants of Bacillus subtilins disclosed in the International Patent Application No. PCT/DK89/00002 and in the International Patent Application published as WO 91/00345, and the proteases disclosed in EP 415 296 A2.
    [0067] Another preferred class of proteases are the metallo-proteases of microbial origin. Conveniently, conventional fermented commercial proteases are useful. Examples of such a commercial protease is Neutrase® (Zn) (produced by submerged fermentation of a strain of [0067] Bacillus subtilis), which is produced and sold by Novo Nordisk A/S.
    [0068] Other useful commercial protease enzyme preparation are Bactosol™ WO and Bactosol™ SI, available from Sandoz AG, Basle, Switzerland; Toyozyme™, available from Toyo Boseki Co. Ltd., Japan; and Proteinase K™ (produced by submerged fermentation of a strain of Bacillus sp. KSM-K16), available from Kao Corporation Ltd., Japan. [0068]
    [0069] The softeners [0069]
    [0070] It may be desirable to treat the wool or animal hair material with a softening agent, either simultaneous with the treatment with a proteolytic enzyme or after the plasma treatment and treatment with a proteolytic enzyme. The softener treatment may be necessary in cases where most of the natural fatty matter of the fibre surface has been removed e.g. as a result of the scouring or plasma treatment. Thus, in order to eliminate a possible dry, harsh handle of the fibre, it may be required to re-apply a low concentration of fatty material to the fibre surface in the form of a softener or softening agent. [0070]
    [0071] The softeners conventionally used on wool are usually cationic softeners, either organic cationic softeners or silicone based products, but anionic or non-inoc softeners are also useful. [0071]
    [0072] Examples of useful softeners are polyethylene softeners and silicone softeners, i.e. dimethyl polysiloxanes (silicone oils), H-polysiloxanes, silicone elastomers, aminofunctional dimethyl polysiloxanes, aminofunctional silicone elastomers, and epoxyfunctional dimethyl polysiloxanes, and organic cationic softeners, e.g. alkyl quaternary ammonium derivatives. [0072]
    [0073] The invention is further illustrated in the following non-limiting examples. [0073] EXAMPLE 1
    [0074] In this working example, the effects on the property of materials were described by the following methods: [0074] Shrinkage: IWTO-20-69: Method for determination of the felting properties of loose wool and top. A reduced felt-ball density corresponds to less felting. Degree of W-CIE (from 1986). The more positive the resulting CIE whiteness: number is, the more white is the wool (−0.3 is more positive than −5). Dyeability: Dyeing of samples:
    [0075] The samples were immersed into a dyeing solution of 2% (w/v) Lanasol Blau 8G (from Giba-Geigy), with liquor ratio 1:13. The dye-bath was brought to the boiling point, and held at boiling temperature for 10 min. Samples were then washed once with tap water and once with distilled water, and dried. Sample and reference were dyed in the same dye-bath (competitive dyeing). [0075]
    [0076] Colorimetric evaluation of colour differences: [0076]
    [0077] The colour of the samples was evaluated in terms of CIE-LAB/D65 coordinates by means of a Datacolor Tex flash 200. The sample coordinates were registered as difference values relative to the corresponding reference. A more negative DL value refers to a darker shade; a more positive DH value refers to a more blue shade. [0077]
    [0078] The applied scoured wool top was 20 μm merino, with pH value of 9.7, and a degree of whiteness (W-CIE) of −10.7. [0078]
    [0079] Four different plasma-enzyme processes were tested. In all processes, the plasma and enzyme treatment of the invention was carried out as follows: [0079]
    [0080] Plasma treatment [0080]
    [0081] The wool was initially subjected to a low-temperature plasma treatment with the following parameters: [0081] Excitation frequency: 4-5 kHz Pressure: 1 mbar Time: 20 sec. Gas: air.
    [0082] Enzyme treatment [0082]
    [0083] The pretreated wool was immersed into phosphate solution (0.1 M; pH 8), liquor ratio 1:20. After immersion, Nocar-diopsis sp., NRRL 18262, protease was added to the liquor at a dosage of 0.12 g/kg wool. The enzyme was allowed to act for 45 min respectively 120 min at 50° C., then the wool was washed in water and dried. In all cases, a plasma treated reference sample was prepared by a corresponding treatment in buffer only. [0083]
    [0084] Process no. 1 [0084]
    [0085] Enzyme treatment directly after plasma treatment. [0085]
    [0086] Results: [0086] Degree of Colorimetric Felt-ball Treatment whiteness evaluation after dyeing test density time: (CIE) (CIELAB/D65) (g/cm3) 45 min Reference −6.4 — 0.126 Enzyme treated −0.3  DL = −3.2 0.098 DH = 0.7 120 min Reference −11.2  — 0.113 Enzyme treated −2.8  DL = −6.8 ≦0.041  DH = 6.0
    [0087] Process no. 2 [0087]
    [0088] With the purpose of removing adjacent material from the plasma treated wool before the enzyme treatment, an ultra sound treatment was carried out between the plasma and enzyme treatment: [0088] Treatment medium: Pure water Liquor ratio: 1:20 Temperature: 40° C. Frequency: 35 kHz Treatment time: 5 min
    [0089] Then washing, drying, and enzyme treatment. [0089]
    [0090] Results: [0090] Degree of Colorimetric Felt-ball Treatment whiteness evaluation after dyeing test density time: (CIE) (CIELAB/D65) (g/cm3) 45 min Reference −5.7 — 0.115 Enzyme treated −4.5 DH = 2.4 0.104 120 min Reference −9.9 — 0.112 Enzyme treated −2.8 DL = −8.1 ≦0.041  DH = 4.4
    [0091] Process no. 3: [0091]
    [0092] In order to remove material adhering to the surface of the plasma treated wool before the enzyme treatment, a surfactant treatment was carried out between the plasma and enzyme treatment: [0092]
    [0093] Treatment medium: 0.1% Dobanol (nonionic surfactant from Henkel AG) in water [0093]
    [0094] Liquor ratio: 1:20 [0094]
    [0095] Temperature: 40° C. [0095]
    [0096] Treatment time: 5 min [0096]
    [0097] Then washing, drying, and enzyme treatment. [0097]
    [0098] Results: [0098] Degree of Colorimetric Felt-ball Treatment whiteness evaluation after dyeing test density time: (CIE) (CIELAB/D65) (g/cm3) 45 min Reference −4.8 — 0.102 Enzyme treated −3.3 DH = 0.9 0.087 120 min Reference −9.0 — 0.102 Enzyme treated  0.6  DL = −3.1 0.050 DH = 4.6
    [0099] Process no. 4: [0099]
    [0100] For removal of adjacent material from the plasma treated wool before the enzyme treatment, an ultra sound treatment with surfactant was carried out between the plasma and enzyme treatment: [0100] Treatment medium: 0.1% Dobanol in water Liquor ratio: 1:20 Temperature: 40° C. Frequency: 35 kHz Treatment time: 5 min
    [0101] Then washing, drying, and enzyme treatment. [0101]
    [0102] Results: [0102] Degree of Colorimetric Felt-ball Treatment whiteness evaluation after dyeing test density time: (CIE) (CIELAB/D65) (g/cm3) 45 min Reference −5.1 — 0.101 Enzyme treated −3.2  DL = −4.2 0.088 DH = 2.5 120 min Reference −6.5 — 0.098 Enzyme treated  2.1 DL = −6.5 ≦0.041  DH = 5.7
    [0103] The results shown in the tables of the processes 1-4 demonstrate that the enzyme treatment in all cases resulted in increased whiteness, increased colour depth, and felting reduction. [0103] EXAMPLE 2
    [0104] I.1 Wool material [0104]
    [0105] a) Plasma treated and reference wool knitted fabric. The fabric parameters were as follows: [0105]
    [0106] fineness: 24 μm [0106]
    [0107] yarn count: tex 25×1 [0107]
    [0108] cover factor: 0.71 [0108]
    [0109] knitted on circular-knitting machine Maxi Jack (Trabal, Spain) [0109]
    [0110] fabric weight 250 g/m[0110] 2
    [0111] standard finishing procedure (scouring, stenter dyeing, decatizing) [0111]
    [0112] dry cleaning (to remove all softeners, surface active agents) [0112]
    [0113] treatment in air plasma: tratment time 60s, voltage ˜800 V, current 2.2 A [0113]
    [0114] b) Untreated woven fabric, plain weave, for fastness testing. Area weight 127 g/m[0114] 2.
    [0115] I.2 Enzyme material [0115]
    [0116] The enzyme used was protease NOVOZYM 654 from Novo Nordisk A/S, DK-2880 Bagsvaerd, batch 94-12. [0116]
    [0117] I.3 Enzyme treatment [0117]
    [0118] The enzyme treatment was performed in dyeing machines. The samples were either prepared according to IWS test method 31 and then enzyme treated or the samples were first enzyme treated and then prepared according to IWS 31. [0118]
    [0119] In the first case the samples were of double thickness and 300 mm×400 mm in size sewn together at the edges. The samples were enzymatically treated in the Ahiba Turbomat 1000. 500 ml Tris-(hydroxymethyl)-aminomethane-acetate buffer pH 8 were added to 65 g of the knitted and sewn sample (liquor ratio 1:7.7) 0.166% (owf) NOVOZYM 654 were incubated with the wool at a temperature of 50° C. for 120 min (resp. 60 min). The inactivation of the enzyme was performed at 85° C. for 10 min. The samples were rinsed with tap water for 20 min. References were treated under the same conditions with buffer without addition of enzyme. [0119]
    [0120] In the second case the knitted fabric was enzymatically treated as one piece in the Ahiba Turbocolor dyeing machine. The liquor ratio was 1:7.9 and the rinsing was performed in the dyeing machine for 30 min. Besides these conditions the treatment parameters were equal to those given above. After the enzyme treatment fabric pieces at a size of 225×300 mm were sewn together and prepared for IWS TM 31. [0120]
    [0121] In the case of woven fabric 300×300 mm samples were prepared in single layer. A cuff was formed prior to the TM 31 test by folding two sides along lines 20 mm from the edge. [0121]
    [0122] I.4 The Delhey process /1/ [0122]
    [0123] Immediately prior to the use the treatment solution was prepared as follows: 50 ml H[0123] 2O2 (35% v/v) and 53 g Na2WO4×2 H2O in 550 ml H2O with 3 g Laventin LNB (BASF) (corresponding to 20 g fabric) were mixed together. 15 s later a sample of woven fabric was wetted in the solution and squeezed in a foulard to a weight increase of 75%. After a reaction time of 2 min the sample was rinsed under tap water and air dried.
    [0124] I.5 IWS test method 31 [0124]
    [0125] The dimension measurements were performed after relaxation (1×7A), after felting shrinkage (2×5A) and after felting shrinkage (5×5A). Sample sizes according to I.3. [0125]
    [0126] I.6 Determination of the weight loss [0126]
    [0127] The weight loss of the samples was determined by measuring the dry weight of the samples prior to and after the enzyme or buffer treatment. Part of the samples were dried at 110° C. for 4 h, cooled down in a desiccator and weighed. [0127]
    [0128] I.7 Degree of whiteness [0128]
    [0129] The degree of whiteness was measured at a Datacolor 3890 calorimeter (Datacolor, Marl, Germany). The degree of whiteness is given as W-CIE. [0129]
    [0130] I.8 Dye uptake [0130]
    [0131] Fabrics were dyed with 2% Lanasol Blue 8G in small batches (4 ml, 2×200 mg woven fabric, 2×500 mg knitted fabric, 10′ at 100° C.). The buffer respectively untreated and the enzyme treated samples were dyed in competition. The colour measurements were performed at the Datacolor 3890 colorimeter. The values given are difference values DL (colour depth). [0131]
    [0132] I.8 Wettability testing (Drop testing /2/) [0132]
    [0133] Destilled water (0.25 g) is dropped from a height of 40 mm onto the stretched fabric and the time is stopped when the drop is fully soaked (no more reflectance on the surface). A mean value of 3 measurements was taken. [0133]
    [0134] II. Results [0134]
    [0135] II.1 Determination of the relaxation and felting shrinkage in washing of the wool samples [0135]
    [0136] II.1.1 Plasma treated knitted wool fabric samples [0136]
    [0137] The results of the relaxation and felting shrinkage of the 225×300 mm of size plasma treated wool samples treated with enzymes respectively buffer are listed in Table 1 (1×7A, 2×5A) and Table 2 (1×7A, 5×5A). [0137] TABLE 1 Relaxation (1 × 7A) and felting shrinkage (2 × 5A) of the plasma treated wool samples treated with 0.166% (owf) NOVOZYM 654 respectively buffer for 120 min (sample size 225 × 300 mm) Felting Area Relaxation/% shrink-age % shrinkage/% Total Samples Width Length Width Length Relaxation Shrinkage shrinkage/% X/% Reference 4.78 −11.32 1.11 −17.54 −6.00 −16.24 −22.24 fabric 5.95 −11.92 0.01 −17.05 −5.26 −17.04 −22.30 −22.27 Plasma 5.90 −12.27 5.90 −12.62 −5.65 −5.98 −11.63 treated 5.72 −12.27 6.23 −12.69 −5.85 −5.67 −11.52 −11.6 fabric Plasma + 5.08 −8.09 5.32 −12.13 −2.60 −6.16 −8.76 buffer 4.09 −7.99 4.69 −10.77 −3.57 −5.57 −9.14 −8.95 Plasma + 5.29 −8.36 3.95 −8.45 −2.63 −4.17 −6.80 enzyme 3.77 −6.63 4.35 −9.23 −2.61 −4.48 −7.09 −6.95
    [0138] [0138] TABLE 2 Relaxation (1 × 7A) and felting shrinkage (5 × 5A) of the plasma treated wool samples treated with 0.166% (owf) NOVOZYM 654 respectively buffer for 120 min (sample size 225 × 300 mm)Felting Total shrinkage/% Area shrinkage/% shrin- Samples Width Length Relaxation Shrinkage kage/% X/% Reference −10.80 −30.39 −6.00 −44.47 −50.47 50.20 −10.73 −30.63 −5.26 −44.65 −49.91 Plasma 1.89 −18.06 −5.65 −15.83 −21.48 2.33 −17.00 −5.85 −14.30 −20.15 −20.82 Plasma + 7.87 −18.22 −2.60 −8.92 −11.52 buffer 7.37 −18.20 −3.57 −9.49 −13.06 −12.30 Plasma + 6.32 −12.72 −2.63 5.60 −8.23 enzyme 6.88 −14.02 −2.61 −6.18 −8.79 −8.51
    [0139] The relaxation and felting shrinkage of the bigger wool samples are listed in Tables 3 and 4. [0139] TABLE 3 Relaxation (1 × 7A) and felting shrinkage (2 × 5A) of the reference/plasma treated wool samples treated with 0.166% (owf) NOVOZYM 654 respectively buffer for 120 min (sample size 300 × 400 mm)Relaxation/% Felting shrinkage/% Area shrinkage/% TotalSamples Width Length Width Length Relaxation Shrinkage shrinkage/% X/% Reference + 3.74 −6.21 0.90 −16.76 −2.24 −15.71 −17.95 buffer Plasma + 2.28 −4.86 6.01 −13.50 −2.47 −6.68 −9.15 buffer Ref. + 2.84 −3.95 1.95 −14.21 −1.0 −11.98 −12.98 enzyme 1.20 −3.69 4.56 −15.72 −2.45 −10.44 −12.89 −12.94 Plasma + 2.11 −4.26 4.34 −7.45 −2.06 −2.79 −4.85 enzyme 1.93 −3.29 5.79 −9.25 −1.29 −2.92 −4.21 −4.53
    [0140] [0140] TABLE 4 Relaxation (1 × 7A) and felting shrinkage (5 × 5A) of the reference/plasma treated wool samples treated with 0.166% (owf) NOVOZYM 654 respectively buffer for 120 min (sample size 300 × 400 mm)Felting Area shrinkage/% Total shrinkage/% Relaxa- shrin-Samples Width Length tion Shrinkage kage/% X/% Reference + −11.09 −27.36 −2.24 −41.5 −43.74 buffer Plasma + 2.30 −20.16 −2.47 −17.4 −19.87 buffer Ref. + −7.15 −24.75 −1.00 −33.67 −34.67 enzyme −5.23 −25.46 −2.45 −32.02 −34.47 −34.57 Plasma + 5.56 −11.84 −2.06 −5.62 −7.68 enzyme 6.19 −13.94 −1.29 −6.89 −8.18 −7.93
    [0141] From these results it can be deduced that the enzyme treatment leads to an additional reduction of the felting shrinkage of plasma treated wool. In the case of the 225×300 mm samples the additional reduction amounts to 40% (22.8% for the buffer treatment) and in the case of the 300×400 mm samples it amounts to 61% (21% for the buffer treatment) for the 2×5A testing. But also in the case of the reference knitted wool fabric the felting shrinkage is reduced by the enzyme treatment. [0141]
    [0142] Plasma treated and reference knitted fabric samples (300×400 mm, double sewn) were also treated with 0.83% owf Novozym 654 for 120 and 60 min. The results of the relaxation and felting shrinkage are listed in Tables 5a-d. [0142] TABLE 5a Relaxation (1 × 7A) and felting shrinkage (2 × 5A) of the reference/plasma treated wool samples treated with 0.83% (owf) NOVOZYM 654 respectively buffer for 120 min (sample size 300 × 400 mm)Relaxation/% Felting shrinkage/% Area shrinkage/% TotalSamples Width Length Width Length Relaxation Shrinkage shrinkage/% X/% Reference + 2.23 −6.15 1.02 −18.05 −3.78 −16.85 −20.63 buffer Plasma + 1.64 −6.77 7.32 −10.17 −5.02 −2.11 −7.13 buffer Ref. + 2.08 −6.17 3.41 −15.24 −4.96 −11.31 −16.27 enzyme 1.72 −5.65 3.04 −14.48 −3.45 −11.00 −14.45 −15.36 Plasma + 1.72 −5.55 4.85 10.31 −3.73 −4.96 −8.69 enzyme 3.38 −6.68 4.00 −8.47 −3.07 −4.13 −7.20 −7.95
    [0143] [0143] TABLE 5b Relaxation (1 × 7A) and felting shrinkage (2 × 5A) of the reference/plasma treated wool samples treated with 0.83% (owf) NOVOZYM 654 respectively buffer for 60 min (sample size 300 × 400 mm)Relaxation/% Felting shrinkage/% Area shrinkage/% TotalSamples Width Length Width Length Relaxation Shrinkage shrinkage/% X/% Reference + 1.99 −5.57 0.87 −17.33 −3.47 −16.31 −19.78 buffer Plasma + 1.18 −7.60 6.00 −11.83 −6.33 −5.12 −11.45 buffer Reference + 0.85 −4.18 4.30 −14.92 −3.29 −9.98 −13.27 enzyme 1.10 −1.19 2.89 −16.87 −0.08 −13.49 −13.57 −13.42 Plasma + 4.00 −6.30 3.70 −7.56 −2.05 −3.58 −5.63 enzyme 1.27 −4.77 5.46 −7.79 −3.44 −1.90 −5.34 −5.49
    [0144] [0144] TABLE 5c Relaxation (1 × 7A) and felting shrinkage (5 × 5A) of the reference/plasma treated wool samples treated with 0.83% (owf) NOVOZYM 654 respectively buffer for 120 min (sample size 300 × 400 mm)Felting Area shrinkage/% Total shrinkage/% Relaxa- Shrink- shrink-Samples Width Length tion age age/% X/% Reference + −9.91 −29.41 −3.78 −42.23 −46.01 buffer Plasma + 7.69 −16.22 −5.02 −7.28 −12.30 buffer Ref. + −5.01 −24.13 −4.96 −30.35 −35.31 enzyme −5.50 −24.73 −3.45 −31.59 −35.04 −35.2 Plasma + 8.78 −14.68 −3.73 −4.61 −8.34 enzyme 5.96 −11.56 −3.07 −4.91 −7.98 −8.2
    [0145] [0145] TABLE 5d Relaxation (1 × 7A) and felting shrinkage (5 × 5A) of the reference/plasma treated wool samples treated with 0.83% (owf) NOVOZYM 654 respectively buffer for 60 min (sample size 300 × 400 mm)Felting Area shrinkage/% Total shrinkage/% Relaxa- Shrink- shrink-Samples Width Length tion age age/% X/% Reference + −12.09 −29.63 −3.47 −45.30 −48.77 buffer Plasma + 5.70 −18.35 −6.33 −11.60 −17.93 buffer Reference + −3.60 −24.91 −3.29 −29.41 −32.70 enzyme −3.24 −25.77 −0.08 −32.36 −32.44 −32.6 Plasma + 8.16 −13.42 −3.44 −4.16 −7.60 enzyme 5.72 −12.39 −2.05 −5.96 −8.01 −7.8
    [0146] In the case of the (2×5A) testing the reduction of shrinkage caused by the enzyme treatment of the untreated wool fabric amounts to 25%. In the case of the incubation of plasma treated wool with 0.83% owf Novozym for 120 min the shrinkage was not reduced but even slightly enhanced. On the contrary if the treatment time is reduced to 60 min with 0.83% Novozym 654 the total shrinkage is reduced by 50%. Using higher enzyme concentrations the treatment time is decisive for the antifelting effect. [0146]
    [0147] II.1.2 Woven fabric treated according to the Delhey process [0147]
    [0148] These trials were carried out on woven fabric. The results of the relaxation and felting shrinkage of the 300×300 mm (280×280 mm) of size Delhey samples treated with enzymes/buffer are shown in Table 6. [0148] TABLE 6a Relaxation (1 × 7A) and felting shrinkage (2 × 5A) of the Delhey or untreated samples treated with 0.166% (owf) NOVOZYM 654 or buffer, respectively (sample size 280 × 280 mm)Relaxation/% Felting shrinkage/% Area shrinkage/% TotalSamples Width Length Width Length Relaxation Shrinkage shrinkage/% X/% Untreated −2.53 −2.63 −12.00 −8.88 −5.23 −21.95 −27.18 reference −2.69 −2.72 −12.49 −7.70 −5.48 −21.15 −26.63 −26.91 Delhey 0.24 −1.60 −2.30 −5.16 −1.36 −7.58 −8.94 treated −0.24 −1.09 −2.23 −4.90 −1.33 −7.24 −8.55 −8.75 reference Buffer 0.05 −0.89 −1.34 −3.62 −0.84 −5.01 −5.85 treated 0.35 −0.85 −1.52 −4.21 −0.50 −5.79 −6.29 −6.07 Delhey (120′) Enzyme 0.24 −0.24 0 −1.96 −0 −1.96 −1.96 treated Delhey 0.90 0.05 0 −1.89 0.95 −1.89 −0.94 −1.45 (120′) 0.166%
    [0149] [0149] TABLE 6b Relaxation (1 × 7A) and felting shrinkage (5 × 5A) of the Delhey or untreated samples treated with 0.166% (owf) NOVOZYM 654 respectively buffer (sample size 280 × 280 mm)Felting Area shrinkage/% Total shrinkage/% Relaxa- Shrink- shrink-Samples Width Length tion age age/% X/% Untreated −31.10 −28.02 −5.23 −67.83 −73.06 reference −31.19 −25.98 −5.48 −65.27 −70.75 −71.9 Delhey −12.02 −16.31 −1.36 −30.29 −31.65 treated −10.83 −16.92 −1.33 −29.58 −30.91 −31.3 reference Buffer −8.41 −11.81 −0.84 −21.21 −22.05 treated −10.61 −14.50 −0.50 −26.65 −27.15 −24.6 Delhey (120′) Enzyme −1.80 −7.00 −0 −8.93 −8.93 treated Delhey (120′) −1.50 −6.52 0.95 8.11 −7.16 −8.0 0.166%
    [0150] 2×5A: The treatment according to Delhey reduces the total shrinkage of the woven fabric used already by approximately 70%. By the enzyme treatment (120 min., 0.166% owf enzyme) the shrinkage is further reduced by >80%. The total reduction of shrinkage achieved with the combined process amounts to 95%. [0150]
    [0151] II.2 Degree of whiteness [0151]
    [0152] The two different sample dimensions of the knitted fabric result from the realization that in the case of the 300×400 mm samples (of double thickness) the rinsing by tap water after the enzyme treatment was less effective, documented in the lower degree of whiteness of the enzyme treated samples (Table 7a) and in a weight increase after treatment (not documented). It seems that residual enzyme and protein fragments were inactivated but not completely removed from the fabric. [0152]
    [0153] Therefore wool samples were treated and rinsed in single fabric thickness. Furthermore, the rinsing was performed in the Ahiba Turbocolor machine where the tap water is pressed through the fabric (Table 7b). [0153]
    [0154] In Table 7c the results of the whiteness measurements for the woven fabric samples treated according to Delhey/1/ and enzyme/buffer posttreated are listed. [0154] TABLE 7 Degree of whiteness of the plasma treated, reference and enzyme posttreated materiala) 300 × 400 mm, knitted fabric treated and washed double sewn: time, enzyme conc. W-CIE ΔW-CIE X references untreated  2.3 — plasma  1.4 — 120 min., 0.166% owf untreated  1.9 −0.4  1.9 −0.4 −0.4 plasma  0.3 −1.1  0.5 −0.9 −1.0 60 min., 0.83% owf untreated −2.2 −4.5 −2.1 −4.4 −4.5 plasma −2.9 −4.3 −2.0 −3.4 −3.9 120 min., 0.83% owf untreated −2.8 −5.1 −2.2 −4.5 −4.8 plasma −2.2 −3.6 −3.3 −4.7 −4.2 references, buffer treated 120′ untreated −0.1 −2.4 plasma  0.5 −0.9 60′ untreated −0.1 −2.4 plasma  0.6 −0.8 samples W-CIE ΔW-CIE b) 225 × 300 mm, knitted fabric treated in single layer and washed in double layer plasma treated reference  1.4 — buffer treated plasma  1.7  0.3 fabric (120′) enzyme treated plasma  4.0  2.6 fabric (120′, 0.166% owf Novozym 654) c) Delhey process, woven fabric 280 × 280 mm reference untreated 15.5 reference Delhey treated  9.6 −5.9 buffer treated 15.8  0.3 Delhey (120′) enzyme treated 27.8 12.3 Delhey (120′, 0.166% owf Novozym 654)
    [0155] In contrast to the samples enzymatically treated in double layer, the plasma treated knitted wool samples treated in one layer with enzymes show an enhanced degree of whiteness compared to the reference. [0155]
    [0156] After the Delhey process (performed as given in I.4) the degree of whiteness of the samples is lower than that of the corresponding reference. The values are increased again by the following buffer treatment and after the enzyme treatment the degree of whiteness is increased by ΔW-CIE value of 12.3. [0156]
    [0157] II.3 Dyeability of the samples [0157]
    [0158] Fabrics treated were dyed with Lanasol Blue 8G in competition with the corresponding reference and the colour differences (DL values) of the respective sample pairs were measured (Table 8). [0158] TABLE 8 Colour differences of the samples and references dyed in competitionSamples corresponding reference/sample DL Woven fabric −10.2  untreated/Delhey treated buffer treated Delhey/- −7.1 enzyme treated Delhey Delhey treated/- −4.0 enzyme treated Delhey Knitted fabric Untreated/enzyme treated −6.1 Plasma/buffer treated plasma 120′ −3.6 Buffer treated plasma/- −0.5 enzyme treated plasma (0.166%, 120′)
    [0159] The biggest difference in the dye uptake is observed in the case of the Delhey treated fabric compared to the untreated fabric. The enzyme treated Delhey samples show a higher uptake than the Delhey treated reference. [0159]
    [0160] In the case of the plasma treated samples the dye uptake is further enhanced by the enzyme treatment. [0160]
    [0161] II.4 Evaluation of the handle [0161]
    [0162] In general the handle of the enzyme treated samples is better than that of the reference. Thus, a tendency is visible and perceptible with rising enzyme concentration, the samples become softer. In these cases the treatment time plays a minor role. [0162]
    [0163] II.5 Wettability [0163]
    [0164] The samples that were used in the dyeing test (II.3) were also tested for wettability (Table 9). In this test it became obvious that either the plasma treatment or the capillary forces along the fabric were not equal. It could also be possible that the dry cleaning prior to the plasma treatment was not effective enough. In the case of the only plasma treated knitted fabric e.g., 3 different values for soaking were measured (11.33 min, 10 sec, 5.45 min). Both sides of the fabric were tested. The fabric is heterogeneous regarding the wettability. Only in the case of the enzyme posttreated plasma treated fabric the soaking was rapid and equal (50, 45 and 42 sec). But, only for one side of the fabric. During the enzyme treatment the fabric was rolled up round the support in the dyeing machine. Thus, part of the fabric is more exposed to the liquor although the liquor is pumped (outside to inside) through the roll. This might be the reason for the different wetting behaviour of the enzyme posttreated samples. [0164]
    [0165] The samples treated by the Delhey process do not show a rapid soaking. But the wettability is enhanced compared to the untreated reference. [0165] TABLE 9 Results of the wettability testing of the differently treated wool samplesI II III IV V VI VII VIII IX1 ∞ ∞ 50 sec >10 min 11.33 min >10 min >10 min >10 min >10 min 2 ∞ ∞ 45 sec >10 min   10 sec >10 min >10 min >10 min 3 ∞ ∞ 42 sec >10 min  5.45 min >10 min >10 min >10 min x ∞ ∞ 46 sec >10 min >10 min >10 min >10 min >10 min wetted wetted wetted wetted below drop below drop below drop below drop
    权利要求:
    Claims (27)
    [1" id="US-20010003220-A1-CLM-00001] 1. A method of producing wool or animal hair material with improved properties comprising the steps of
    a. treating wool, wool fibres or animal hair material in a process selected from the group consisting of plasma treatment processes and the Delhey process, and
    b. subjecting the wool or animal hair material to a treatment with a proteolytic enzyme in an amount effective for improving the properties.
    [2" id="US-20010003220-A1-CLM-00002] 2. The method according to
    claim 1 , wherein the plasma treatment is a low-temperature treatment, preferably a corona discharge treatment or a glow discharge treatment.
    [3" id="US-20010003220-A1-CLM-00003] 3. The method according to
    claim 1 , wherein the process is the Delhey process.
    [4" id="US-20010003220-A1-CLM-00004] 4. The method according to
    claim 2 , wherein the improved property of the produced wool or animal hair material is an improved shrink-proof or anti-felting property, preferably corresponding to an area shrinkage of less than 10%, more preferably less that 8%, more preferably less than 7%, more preferably less that 5%, even more preferably less than 3%, especially less that 2%, after 2 cycles of ISO 5A, or to an area shrinkage of less than 15%, more preferably less than 10%, more preferably less that 8%, even more preferably less than 6%, especially less that 5%, after 5 cycles of ISO 5A, measured according to the IWS Test Method 31; or to a felt-ball density at or below 0.04, measured according to the Aachen felt-ball test IWTO-20-69.
    [5" id="US-20010003220-A1-CLM-00005] 5. The method according to
    claim 3 , wherein the improved property of the produced wool or animal hair material is an improved shrink-proof or anti-felting property, preferably corresponding to an area shrinkage of less than 25%, more preferably less that 20%, more preferably less that 15%, more preferably less that 12%, more preferably less that 10%, more preferably less than 8%, even more preferably less than 5%, especially less that 2%, after 2 cycles of ISO 5A, or to an area shrinkage of less than 20%, more preferably less that 15%, more preferably less than 12%, even more preferably less than 10%, especially less that 9%, after 5 cycles of ISO 5A, measured according to the IWS Test Method 31.
    [6" id="US-20010003220-A1-CLM-00006] 6. The method according to
    claim 2 , wherein the improved property of the produced wool or animal hair material is an improved whiteness degree, preferably corresponding to an improvement of at least 8 CIE units, more preferably of at least 10 CIE units measured in a Datacolor 3890 Spectral photometer (CIELAB system).
    [7" id="US-20010003220-A1-CLM-00007] 7. The method according to
    claim 3 , wherein the improved property of the produced wool or animal hair material is an improved whiteness degree, preferably corresponding to an improvement of at least 10 CIE units, more preferably of at least 12 CIE units, measured in a Datacolor 3890 Spectral photometer (CIELAB system).
    [8" id="US-20010003220-A1-CLM-00008] 8. The method according to
    claim 1 , wherein the improved property of the produced wool or animal hair material is an improved dyeability, preferably corresponding to an increase of the colour depth by at least 2 DL (units), more preferably at least 3 DL (units), measured relative to an untreated reference after competitive dyeing in 2% Lanasol Blue 8G.
    [9" id="US-20010003220-A1-CLM-00009] 9. The method according to
    claim 1 , wherein the loss of bundle strength tenacity of the produced wool or animal hair material, as compared to the bundle strength tenacity of the untreated material, preferably is less than 20%, more preferably less than 10%, most preferably less than 8%, especially less than 6%, measured according to IWTO-32-82.
    [10" id="US-20010003220-A1-CLM-00010] 10. The method according to
    claim 1 , wherein the improved property of the produced wool or animal hair material is improved softness, preferably a softness at least corresponding to the softness of untreated wool.
    [11" id="US-20010003220-A1-CLM-00011] 11. The method according to
    claim 1 , wherein the improved property of the produced wool or animal hair material is a reduced pilling tendency.
    [12" id="US-20010003220-A1-CLM-00012] 12. The method according to
    claim 2 , wherein the low-temperature plasma treatment is carried out by using a gas selected from the group consisting of air, oxygen, nitrogen, ammonia, helium, or argon.
    [13" id="US-20010003220-A1-CLM-00013] 13. The method according to
    claim 2 , wherein the low-temperature plasma treatment is carried out for from about 2 seconds to about 300 seconds, preferably for about 5 seconds to about 100 seconds, more preferably from about 5 seconds to about 30 seconds; and/or at a pressure between about 0.1 torr and 5 torr.
    [14" id="US-20010003220-A1-CLM-00014] 14. The method according to
    claim 1 , wherein the treatment with a proteolytic enzyme preferably is carried out for between about 1 minute and about 120 minutes; and/or preferably at a temperature of between about 20° C. and about 70° C., more preferably between about 30° C. and about 60° C., especially between about 40° C. and about 60° C.
    [15" id="US-20010003220-A1-CLM-00015] 15. The method according to
    claim 1 , wherein the treatment with a proteolytic enzyme is carried out in an acidic or neutral or alkaline medium, optionally in the presence of one or more anionic, non-ionic or cationic surfactants.
    [16" id="US-20010003220-A1-CLM-00016] 16. The method according to
    claim 1 , wherein the wool or animal hair material is further subjected to an ultrasound treatment, either prior to or simultaneous with the treatment with a proteolytic enzyme.
    [17" id="US-20010003220-A1-CLM-00017] 17. The method according to
    claim 1 , wherein the wool or animal hair material is subjected to a treatment with a softener or softening agent, either simultaneous with the treatment with a proteolytic enzyme or after the plasma treatment and treatment with a proteolytic enzyme.
    [18" id="US-20010003220-A1-CLM-00018] 18. The method according to
    claim 1 , wherein the proteolytic enzyme is of plant origin such as papain, bromelain and ficin, or of animal origin such as trypsine.
    [19" id="US-20010003220-A1-CLM-00019] 19. The method according to
    claim 1 , wherein the proteolytic enzyme is of microbial origin such as a bacterial protease, a fungal protease and a protease producible by or derivable from yeasts.
    [20" id="US-20010003220-A1-CLM-00020] 20. The method according to
    claim 19 , wherein the proteolytic enzyme is a serine protease, preferably a subtilisin, more preferably a subtilisin derived from Bacillus or from Tritirachium album.
    [21" id="US-20010003220-A1-CLM-00021] 21. The method according to
    claim 20 , wherein the serine protease is selected from subtilisin PB92, subtilisin 309 and subtilisin 147.
    [22" id="US-20010003220-A1-CLM-00022] 22. The method according to
    claim 21 , wherein the serine protease is a subtilisin variant of subtilisin 309 having the glycine in position 195 substituted with phenylalanine (G195F).
    [23" id="US-20010003220-A1-CLM-00023] 23. The method according to
    claim 20 , wherein the serine protease is producible by or derived from a strain of B. licheniformis, B. alcalophilus, B. cereus, B. natto, B. vulgatus or B. mycoide.
    [24" id="US-20010003220-A1-CLM-00024] 24. The method according to
    claim 20 , wherein the serine protease is a protease producible by or derivable from a strain belonging to a genus selected from Nocardiopsis, Aspergillus, Rhizopus and Mucor.
    [25" id="US-20010003220-A1-CLM-00025] 25. The method according to
    claim 24 , wherein the protease is producible by or derivable from a strain of Nocardiopsis sp. or Nocardiopsis dassonvillei, preferably from a strain of Nocardiopsis sp., more preferably from Nocardiopsis sp., NRRL 18133.
    [26" id="US-20010003220-A1-CLM-00026] 26. The method according to
    claim 1 , wherein the amount of proteolytic enzyme preferably is between about 0.2 w/w % and about 10 w/w %, based on the weight of the wool or animal hair material.
    [27" id="US-20010003220-A1-CLM-00027] 27. Wool or animal hair material which has been treated according to the method of
    claim 1 .
    类似技术:
    公开号 | 公开日 | 专利标题
    US6258129B1|2001-07-10|Method for enzymatic treatment of wool
    EP0943028B1|2007-08-22|Alkaline enzyme scouring of cotton textiles
    EP0885311B1|2006-11-29|Enzyme treatment to enhance wettability and absorbency of textiles
    US6099588A|2000-08-08|Method for treatment of wool
    US6051033A|2000-04-18|Method for enzymatic treatment of wool
    EP0946812B1|2004-04-21|Process for improved shrink resistance in wool
    AU757109B2|2003-02-06|A method for enzymatic treatment of wool
    US6140109A|2000-10-31|Method for enzymatic treatment of wool
    MXPA97004549A|1998-07-03|Method for the enzymatic treatment of the l
    EP0911441A1|1999-04-28|Process for cellulase treatment
    MXPA99005625A|2000-01-01|Process for improved shrink resistance in wool
    同族专利:
    公开号 | 公开日
    BR9510216A|1997-11-04|
    US6258129B1|2001-07-10|
    AU4298696A|1996-07-10|
    EP0799344A1|1997-10-08|
    JPH10511437A|1998-11-04|
    PL321426A1|1997-12-08|
    CN1170448A|1998-01-14|
    PL184544B1|2002-11-29|
    TR199501643A2|1996-07-21|
    NZ297747A|2000-01-28|
    HUT77196A|1998-03-02|
    AU5012199A|1999-11-25|
    CN1095008C|2002-11-27|
    AU738094B2|2001-09-06|
    MX9704549A|1997-10-31|
    MA23754A1|1996-07-01|
    WO1996019611A1|1996-06-27|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    WO2005121438A2|2004-06-11|2005-12-22|Valtion Teknillinen Tutkimuskeskus|Method for modifying polyamide|
    US20080282478A1|2005-08-10|2008-11-20|David Malcolm Lewis|Improvements in and Relating to Wool Treatment|
    CN102965956A|2012-10-19|2013-03-13|江南大学|Wool worsted fabric compound enzyme padding-steaming stacking anti-felting finishing technology|
    CN102965958A|2012-10-31|2013-03-13|江南大学|Wool product two-bath process anti-felting treatment technology based on composite bio-enzyme|JPH0154471B2|1982-02-12|1989-11-20|Kurashiki Boseki Kk||
    DE3881033T2|1987-10-28|1993-12-02|Schoeller Hardturm Ag Zuerich|ENZYMATIC TREATMENT OF WOOL.|
    GB8820561D0|1988-08-31|1988-09-28|Precision Proc Textiles Ltd|Method for treatment of wool|
    JP2905311B2|1991-04-24|1999-06-14|ユニチカ株式会社|Shrinkproof processing method of animal hair fiber products|
    DE4332692C1|1993-09-25|1994-07-28|Deutsches Wollforschinst|Printing pretreatment or anti felting treatment of wool|
    HUT77196A|1994-12-21|1998-03-02|Novo Nordisk A/S|A method for enzymatic treatment of wool|
    DE19616776C1|1996-04-26|1997-09-18|Bayer Ag|Non felting finish for woollens|HUT77196A|1994-12-21|1998-03-02|Novo Nordisk A/S|A method for enzymatic treatment of wool|
    US6051033A|1998-05-20|2000-04-18|Novo Nordisk Brochem North America Inc.|Method for enzymatic treatment of wool|
    TR200003419T2|1998-05-20|2001-03-21|Novo Nordisk Biochem North America, Inc.|Method for enzymatic treatment of wool|
    CA2243011C|1998-07-13|2007-02-13|Life Science Technology Group, Inc.|Odor control agent for carpet and the like and method of use thereof|
    DE19858734A1|1998-12-18|2000-06-21|Bayer Ag|Non-felting wool for production of textiles is obtained by plasma pretreatment and optional treatment with aqueous dispersion of self-dispersing isocyanate, followed by treatment with softener and non-slip finish|
    US6099588A|1999-02-23|2000-08-08|Novo Nordisk Biochem North America, Inc.|Method for treatment of wool|
    US20020022860A1|2000-08-18|2002-02-21|Borillo Thomas E.|Expandable implant devices for filtering blood flow from atrial appendages|
    GB0029932D0|2000-12-06|2001-01-24|Woolmark Europ Ltd|Fibrillation of natural fibres|
    WO2003097927A1|2002-05-21|2003-11-27|Universidade Do Minho|Treatment of animal hair fibers with modified proteases|
    FI119700B|2002-12-16|2009-02-13|Suedwolle Gmbh & Co Kg|Industrial biotechnological wool finishing process and woolen fabric produced by this method|
    US8343213B2|2003-12-23|2013-01-01|Sadra Medical, Inc.|Leaflet engagement elements and methods for use thereof|
    US8579962B2|2003-12-23|2013-11-12|Sadra Medical, Inc.|Methods and apparatus for performing valvuloplasty|
    US8182528B2|2003-12-23|2012-05-22|Sadra Medical, Inc.|Locking heart valve anchor|
    US8052749B2|2003-12-23|2011-11-08|Sadra Medical, Inc.|Methods and apparatus for endovascular heart valve replacement comprising tissue grasping elements|
    US8840663B2|2003-12-23|2014-09-23|Sadra Medical, Inc.|Repositionable heart valve method|
    US20120041550A1|2003-12-23|2012-02-16|Sadra Medical, Inc.|Methods and Apparatus for Endovascular Heart Valve Replacement Comprising Tissue Grasping Elements|
    US8603160B2|2003-12-23|2013-12-10|Sadra Medical, Inc.|Method of using a retrievable heart valve anchor with a sheath|
    US7959666B2|2003-12-23|2011-06-14|Sadra Medical, Inc.|Methods and apparatus for endovascularly replacing a heart valve|
    US7381219B2|2003-12-23|2008-06-03|Sadra Medical, Inc.|Low profile heart valve and delivery system|
    US7988724B2|2003-12-23|2011-08-02|Sadra Medical, Inc.|Systems and methods for delivering a medical implant|
    US9526609B2|2003-12-23|2016-12-27|Boston Scientific Scimed, Inc.|Methods and apparatus for endovascularly replacing a patient's heart valve|
    US7780725B2|2004-06-16|2010-08-24|Sadra Medical, Inc.|Everting heart valve|
    WO2006046878A1|2004-10-28|2006-05-04|Canesis Network Limited|Production of fine particulates from keratin fibres|
    US20070213813A1|2005-12-22|2007-09-13|Symetis Sa|Stent-valves for valve replacement and associated methods and systems for surgery|
    BR112012021347A2|2008-02-26|2019-09-24|Jenavalve Tecnology Inc|stent for positioning and anchoring a valve prosthesis at an implantation site in a patient's heart|
    EP3238661B1|2008-10-10|2019-05-22|Boston Scientific Scimed, Inc.|Medical devices and delivery systems for delivering medical devices|
    PT2488690E|2009-10-16|2014-09-03|Univ Masarykova|Method for improving felting properties of animal fibres by plasma treatment|
    CN101781852B|2010-01-20|2012-02-22|江南大学|Method for conducting wool fabric anti-felting treatment through two-bath process by using imidazolium chloride ionic liquid/protease|
    IT1398167B1|2010-02-16|2013-02-14|Rovero|STORAGE DYEING PROCESSOF TEXTILE ARTICLES INCLUDING A TREATMENT PHASE WITH IONIZED GAS OR PLASMA.|
    CN102191690B|2010-03-12|2013-05-01|香港纺织及成衣研发中心|Processing method of anti-pilling textile|
    US9333075B2|2010-09-10|2016-05-10|Symetis Sa|Valve replacement devices, delivery device for a valve replacement device and method of production of a valve replacement device|
    ITTV20110160A1|2011-11-17|2013-05-18|Benind S P A|METHOD OF TREATMENT OF SEMI-FINISHED WOOL.|
    US8951243B2|2011-12-03|2015-02-10|Boston Scientific Scimed, Inc.|Medical device handle|
    US20130255325A1|2012-03-30|2013-10-03|Deckers Outdoor Corporation|Wool pile fabric including security fibers and method of manufacturing same|
    US9883941B2|2012-06-19|2018-02-06|Boston Scientific Scimed, Inc.|Replacement heart valve|
    ITBO20130339A1|2013-06-28|2014-12-29|Veneto Nanotech S C P A|METHOD OF CONDITIONING MATERIAL IN FIBER WOOL|
    CN105491978A|2013-08-30|2016-04-13|耶拿阀门科技股份有限公司|Radially collapsible frame for a prosthetic valve and method for manufacturing such a frame|
    EP2856896A1|2013-09-23|2015-04-08|Life Science TGO, SRL|Impregnated odour control products and methods of making the same|
    CN104256931B|2014-08-26|2016-02-10|湖州圣绒服饰有限公司|A kind of preparation method of environmental protection goat fleecy sweatshirt|
    US9901445B2|2014-11-21|2018-02-27|Boston Scientific Scimed, Inc.|Valve locking mechanism|
    US10449043B2|2015-01-16|2019-10-22|Boston Scientific Scimed, Inc.|Displacement based lock and release mechanism|
    US9861477B2|2015-01-26|2018-01-09|Boston Scientific Scimed Inc.|Prosthetic heart valve square leaflet-leaflet stitch|
    US9788942B2|2015-02-03|2017-10-17|Boston Scientific Scimed Inc.|Prosthetic heart valve having tubular seal|
    WO2016126524A1|2015-02-03|2016-08-11|Boston Scientific Scimed, Inc.|Prosthetic heart valve having tubular seal|
    US10285809B2|2015-03-06|2019-05-14|Boston Scientific Scimed Inc.|TAVI anchoring assist device|
    US10426617B2|2015-03-06|2019-10-01|Boston Scientific Scimed, Inc.|Low profile valve locking mechanism and commissure assembly|
    US10080652B2|2015-03-13|2018-09-25|Boston Scientific Scimed, Inc.|Prosthetic heart valve having an improved tubular seal|
    US10195392B2|2015-07-02|2019-02-05|Boston Scientific Scimed, Inc.|Clip-on catheter|
    US10335277B2|2015-07-02|2019-07-02|Boston Scientific Scimed Inc.|Adjustable nosecone|
    US10179041B2|2015-08-12|2019-01-15|Boston Scientific Scimed Icn.|Pinless release mechanism|
    US10136991B2|2015-08-12|2018-11-27|Boston Scientific Scimed Inc.|Replacement heart valve implant|
    CN105369635A|2015-11-19|2016-03-02|德清县伊得利丝绸有限公司|Anti-pilling cashmere sweater production method|
    CN105544181B|2015-12-30|2017-08-25|江阴市长泾花园毛纺织有限公司|It is a kind of hydrophilic shrinkproof two-sided|
    US10342660B2|2016-02-02|2019-07-09|Boston Scientific Inc.|Tensioned sheathing aids|
    US10583005B2|2016-05-13|2020-03-10|Boston Scientific Scimed, Inc.|Medical device handle|
    EP3454795A1|2016-05-13|2019-03-20|JenaValve Technology, Inc.|Heart valve prosthesis delivery system and method for delivery of heart valve prosthesis with introducer sheath and loading system|
    US10201416B2|2016-05-16|2019-02-12|Boston Scientific Scimed, Inc.|Replacement heart valve implant with invertible leaflets|
    WO2018140740A1|2017-01-27|2018-08-02|Deckers Outdoor Corporation|Sheared wool fleece and method for making sheared wool fleece utilizing yarn knitting|
    EP3573579A1|2017-01-27|2019-12-04|JenaValve Technology, Inc.|Heart valve mimicry|
    EP3634311A1|2017-06-08|2020-04-15|Boston Scientific Scimed, Inc.|Heart valve implant commissure support structure|
    EP3661458A1|2017-08-01|2020-06-10|Boston Scientific Scimed, Inc.|Medical implant locking mechanism|
    CN111225633A|2017-08-16|2020-06-02|波士顿科学国际有限公司|Replacement heart valve coaptation assembly|
    JP2021511144A|2018-01-19|2021-05-06|ボストン サイエンティフィック サイムド，インコーポレイテッドＢｏｓｔｏｎ Ｓｃｉｅｎｔｉｆｉｃ Ｓｃｉｍｅｄ，Ｉｎｃ．|Induction mode indwelling sensor for transcatheter valve system|
    EP3749252A1|2018-02-07|2020-12-16|Boston Scientific Scimed, Inc.|Medical device delivery system with alignment feature|
    法律状态:
    1997-10-30| AS| Assignment|Owner name: NOVO NORDISK A/S, DENMARK Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DYBDAL, LONE;HEINE, ELIZABETH;HOCKER, HARTWIG;REEL/FRAME:008788/0357;SIGNING DATES FROM 19970617 TO 19970624 |
    2001-12-27| AS| Assignment|Owner name: NOVOZYMES A/S, DENMARK Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:NOVO NORDISK A/S;REEL/FRAME:012463/0868 Effective date: 20011029 |
    2005-07-11| LAPS| Lapse for failure to pay maintenance fees|
    2005-08-10| STCH| Information on status: patent discontinuation|Free format text: PATENT EXPIRED DUE TO NONPAYMENT OF MAINTENANCE FEES UNDER 37 CFR 1.362 |
    2005-09-06| FP| Expired due to failure to pay maintenance fee|Effective date: 20050710 |
    优先权:
    申请号 | 申请日 | 专利标题
    DK1451/94||1994-12-21||
    DK145194||1994-12-21||
    PCT/DK1995/000517|WO1996019611A1|1994-12-21|1995-12-21|A method for enzymatic treatment of wool|
    [返回顶部]