    • 专利摘要:
    A one-step rapid manufacturing process is used to create three dimensional prototyping parts. Material such as metal, ceramics and the like powder, and wire, and the like, is delivered to a laser beam-material interaction region where it is melted and deposited on a substrate. The melted and deposited material is placed on a XYZ workstation. Three dimensional parts are created by moving the XYZ workstation relative to the laser beam while simultaneously feeding powdered alloys, first in the XY and then in the Z plane. Beam shaping focussing optics can be used to tailor the intensity distribution of the laser beam to the requirements of the deposition layers, and can be used to create parts with desired mechanical or thermodynamic properties. Additional beam splitting and recombining optics can be used to allow powder to be fed at a perpendicular angle to the substrate.
    公开号:US20010002287A1
    申请号:US09/731,993
    申请日:2000-12-07
    公开日:2001-05-31
    发明作者:Aravinda Kar；Srikanth Sankaranarayanan；Franz-Josef Kahlen
    申请人:University of Central Florida；
    IPC主号:C23C26-02
    专利说明:
    [0001] This invention relates to part manufacturing, and in particular to a one step rapid manufacturing method and system to create three dimensional (3D) prototyping parts where material such as metal, ceramics and the like, is delivered to a laser beam interaction region in powderized form or as a wire where it is melted on a substrate the latter of which is moved in the three translational directions (X, Y, and Z directions). This invention is Continuation-In-Part of U.S. Provisional application Ser. No. 60/071,252 filed Jan. 12, 1998. [0001] BACKGROUND AND PRIOR ART
    [0002] Rapid tool manufacturing techniques such as Selective Laser Sintering, Stereolithography, and rapid prototyping are the techniques generally used for the rapid recreation of parts. However, these techniques create parts that are generally suitable for use in space and design studies and not for real world applications. Furthermore, these tool manufacturing techniques generally require soft tools, molds and casting to often create plastic type fabricated parts with many inherent problems since these techniques do not use the same materials as the original part to be recreated. The prior known manufacturing techniques are prone to create fabricated parts different from the original parts. For example, if one were to use stereolithography to manufacturer a plastic fan wheel, the resultant part would have different surface characteristics and weights than an aluminum flywheel that is desired to be duplicated. Important characteristics such as flow separation points, efficiency of operation, pressure ratio over the blades, mass flow therethrough, will be different. Also plastic parts created by stereolithography cannot operate in high temperature environments. Thus, plastic car exhaust parts created by stereolithography manufacturing techniques would not be useful for the high temperature environments of vehicle engine emissions. Furthermore, these plastic fabricated parts would have a very short lifespan in chemically active environments. [0002]
    [0003] Using a casting manufacturing technique creates a part having a homogeneous uniform material. Thus, casted parts exhibit uniform mechanical and thermophysical properties throughout their structure. Casted parts cannot have materials with graded (varied) compositions. Casted parts may crack and break down in applications where increased strength characteristics are needed such as along the center axle region of the fly wheel example. [0003]
    [0004] The prior known techniques are not useful for refurbishing damages to existing parts (e.g. camshafts) nor for fixing localized damage such as scratches on existing parts. Furthermore, the known manufacturing techniques are not useful for providing any wear resistant coatings to existing parts. [0004]
    [0005] The prior known techniques involve a number of steps for parts fabrication, including sintering, mold and die casting, using material mixtures containing materials other than the original material, or using support structures during fabrication. [0005]
    [0006] Many U.S. Patents have been proposed but fail to overcome all the problems presented above. See for example: U.S. Pat. Nos. 5,189,781 to Weiss et al.; 5,314,003 and 5,393,613 to Mackay; and 5,316,580 to Deckard employ predeposited powder in a flat bed which is leveled in a form and melted by a scanning laser beam; 5,384,523 to Masuda; 5,385,780 to Lee sinters polymer powder; 5,398,193 to de Angelis requires masks to make parts, also, the process creates sharp boundaries between two different materials; 5,475,617 to Castonguay; and 5,622,577 to O'Connor requires two different processing chambers, and also employs a predeposited powder. Although, in recent years, several processes were developed which enable the user to fabricate parts from stronger materials than commonly used in conventional Rapid Prototyping processes, or even to fabricate parts with a metal content. These processes do not solve all of the problems stated above. Some of these techniques can take as many as nine (9) or more steps to fabricate the final part. From an end users point of view, this is a very time-consuming and costly option. [0006]
    [0007] Several related but overly complex tools have been suggested in the past. See for example 5,239,160 to Sakura et al. (Five-Axis Table); 4,726,715 and 4,803,335 to Steen et al. (powder delivery); 4,724,299 to Hammeke (Laser Spray Nozzle); 5,453,329 and 5,477,025 to Everett et al. (Powder Nozzle and Abrasive Particle Deposition). These inventions present an “overkill” in terms of their operation, usage, maintenance, and operating costs. [0007]
    [0008] The Mechanical Engineering Magazine March 1997 edition describes many of the prior art techniques. Ashley, Steve, “From CAD art to rapid metal tools”, Mechanical Engineering, March 1997, pages 82-87, introduces a similar process, called LENS (Laser Engineered Net Shaping) by Sandia National Laboratories. Major limitations of LENS are the restrictions of being able to fabricate extruded parts only (having no undercuts nor overhangs. Also, the process is based on using four powder delivery nozzles. Rapid Manufacturing is capable of creating undercuts and overhangs, also, the alignment of the powder delivery to the focussed laser beam is easier as the powder is delivered by one nozzle only. In addition, the introduction of turbulences into the shield gas flow, due to aligning and interaction of multiple shield gas jets is eliminated. The LENS-process is distinctly different from the Rapid Manufacturing process of the subject invention described here, in that it requires an enclosure around the laser beam -material powder interaction region to create a non-oxidizing environment. The preferred embodiment for LENS appears to be Argon shield gas, whereas the Rapid Manufacturing of the subject invention process has worked successfully with different shield gases, such as Helium and Nitrogen. Also, for the Rapid Manufacturing process of the subject invention, it is optional to use the same material as base substrate and for the deposition whereas LENS apparently is preferentially used for same material combinations. Finally, LENS so far does not incorporate real-time sensor feed back. [0008]
    [0009] None of the prior art know to the subject inventors comprises all the desirable features of: full fabrication out of the original material, fabrication in one step, without a dependence on support structures. [0009] SUMMARY OF THE INVENTION
    [0010] The first objective of the present invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts on a need-be basis, wherein the geometry of the part/tool to be manufactured can be stored on a computer hard drive/disk. [0010]
    [0011] The second object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts without using support structures and allowing for the realization of undercuts and overhangs. [0011]
    [0012] The third object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts where the local composition of the parts can be graded (varied) increased and lowered along metallurgical limitations. If the requirements for a component call for high strength in one region and high thermal conductivity in another region, the powder composition can be varied accordingly. [0012]
    [0013] The fourth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts that allows for worn damaged parts to be refurbished and reprocessed to fix damaged and scratched areas. [0013]
    [0014] The fifth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts, for coating parts to enhance wear resistance. [0014]
    [0015] The sixth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts that does not require an enclosure with inert gases to avoid oxidation during the fabrication of parts. Shield gas is delivered coaxially to the laser beam to create a non-oxidizing environment at the location where the material is deposited. [0015]
    [0016] The seventh object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts that does not require an enclosure with inert gases to avoid oxidation during the fabrication of parts. Non-oxidizing carrier gas is used to deliver material powder(s) to the laser beam to create a non-oxidizing environment at the location where the material(s) are deposited. [0016]
    [0017] The eighth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts where material powder(s) is delivered to the deposition region by one nozzle only, eliminating the alignment and powder and carrier gas distribution problems associated with multiple nozzle setups. [0017]
    [0018] The ninth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts where a non-oxidizing shield gas is supplied coaxially to the laser beam and material(s) in form of a wire is delivered to the deposition region. [0018]
    [0019] The tenth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts where material(s) in form of a wire(s) is delivered the deposition region. [0019]
    [0020] The eleventh object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts where a processing laser beam (and its' intensity distribution) is shaped by beam shaping optics or adaptive optics such that desired product properties can be achieved during parts fabrication, without post-processing. [0020]
    [0021] The twelfth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts where the powder stream or the material wire is delivered coaxially to the processing laser beam. [0021]
    [0022] The thirteenth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts that allows for surface alloying of existing parts. [0022]
    [0023] The fourteenth object of this invention is to provide for the one-step method and system for the manufacturing of three dimensional metal and composite parts where the new part can be joined with the substrate (forming an add-on to an existing part) or can be created without attaching to the substrate. [0023]
    [0024] A preferred embodiment of the invention has three-dimensional structures being formed by a layer by layer deposition process. The first layer was formed in the X-Y planes and the subsequent layers were formed on one another to build the structure in the Z-direction. The dimensions of the components were controlled by a XYZ translational stage interfaced to a computer. 3-D computer images were created using Motion Control Interface Firmware (MCIF) software and down loaded to the controller of the XYZ stage. [0024]
    [0025] The invention can be connected to a visual feature and geometry recognition system which records, examines, slices, and runs the computer controlled system for parts creation. [0025]
    [0026] For a fiber-optic beam delivery multiple-location application, processing can be realized by assigning different tasks to different fiber optics. One fiber head can deliver the laser beam for powder deposition while other fiber heads can deliver the beams for additional processing (cutting, drilling, welding, and the like). This concept utilizes the different materials processing features of lasers, and in the process eliminates the necessity for moving components from one workstage to another, it also shortens the time required for the processing as some tasks can be carried out simultaneously by different fiber heads. [0026]
    [0027] Beam shaping optics can be used to create non-symmeteric laser beams, such as but not limited to elliptical, triangular lines and the like, before processing. A laser beam can be spread along the line of material deposition; the region of highest laser beam intensity (front) provides the energy required for material melting whereas the trailing portion of the laser beam (decreasing intensity) imposes a thermal gradient upon the deposited material during its re-solidification. An advantage of this setup is that the trailing part of the beam provides the environment (spatial, temporal) for the material cooling rate and, as a consequence, for phase formation during re-solidification. This is effectively a phase of post-processing during which, e.g., the hardness of the material will be determined. [0027]
    [0028] The beam shaping of the subject invention is not limited to applications in Rapid Manufacturing, but can also be applied to other processes such as but not limited to laser welding, surface treatments, and the like. [0028]
    [0029] Further objects and advantages of this invention will be apparent from the following detailed description of a presently preferred embodiment which is illustrated schematically in the accompanying drawings. [0029] BRIEF DESCRIPTION OF THE FIGURES
    [0030] FIG. 1 shows a preferred embodiment layout of the one step rapid manufacturing system invention. [0030]
    [0031] FIG. 2 shows the beam delivery system of a laser source, beam delivery optics and beam focussing optics used in the manufacturing system of FIG. 1. [0031]
    [0032] FIG. 3 shows an alternative beam delivery system of a laser source, fiber optic cable, and beam focussing optics/fiber output coupler for use in the manufacturing system of FIG. 1. [0032]
    [0033] FIG. 4 is an enlarged view of the XYZ workstation used in the manufacturing system of FIG. 1. [0033]
    [0034] FIG. 5 is an enlarged view of the powder feeder and carrier gas connection in the system of FIG. 1. [0034]
    [0035] FIG. 6 is a view of the computer control system used in the manufacturing system of FIG. 1. [0035]
    [0036] FIG. 7 shows the shield gas connection used in the manufacturing system of FIG. 1. [0036]
    [0037] FIG. 8 shows an example of Multiple-Application systems using Nd:YAG lasers. [0037]
    [0038] FIG. 9A shows a graph of laser beam length versus intensity for an example of a Laser Beam Shape tailored to the parts' selected properties. [0038]
    [0039] FIG. 9B shows a graph of laser beam width versus intensity for an example of a Laser Beam Shape tailored to the parts' selected properties. [0039]
    [0040] FIG. 10 shows an example of Multiple-Application systems using diode lasers. [0040]
    [0041] FIG. 11 shows a laser beam being split into two separate parts and being recombined into a desired (selected) shape by reflective elements while powder is fed coaxially to the processing region perpendicular to the substrate. [0041] DESCRIPTION OF THE PREFERRED EMBODIMENT
    [0042] Before explaining the disclosed embodiment of the present invention in detail it is to be understood that the invention is not limited in its application to the details of the particular arrangement shown since the invention is capable of other embodiments. Also, the terminology used herein is for the purpose of description and not of limitation. [0042]
    [0043] FIG. 1 shows a preferred embodiment layout [0043] 1 of the one step rapid manufacturing system invention. FIG. 2 shows the beam delivery system 100 of a laser source 110, beam delivery optics and beam focussing optics used in the manufacturing system of FIG. 1.
    [0044] Referring to FIGS. 1 and 2, a CO[0044] 2 laser 110 (having a continuous wave or pulsed wave) can be operated at a power level of 345 W, generated a top-hat shaped laser beam directed towards the beam delivery optics 120 (reflective mirror)which reflects the beam towards a focussing unit 130, here displayed as a lens but could be replaced by other reflective optics, such as but not limited to a parabolic mirror, spherical mirror, adaptic optic, and the like, to form a spot beam point to the top surface of the XYZ Workstage 200 (shown and described in greater detail in reference to FIG. 4). For safety reasons, the laser beam path can be enclosed by transmission tubes 150 from the shutter 115 to the beam focussing optics 130. The shutter 115 can be moved into and out of the laser beam by computer 410 and controller 420.
    [0045] FIG. 4 is an enlarged view of the XYZ workstation [0045] 200 used in the manufacturing system of FIG. 1. Three stepping motors 228, 224 and 234 can be used to translate movement in the X, Y, and Z directions, respectively. The types of stepping motors can be “Intelligent Motion Systems, Inc., Stepping motor, manufacture no. M2-3424-S. Components 217 are threaded rods, each having outer diameters of approximately 0.6 inches, and a thread width of approximately 0.1 inches. Work table 205 is used to place the substrate (not shown) thereon. The scissor-type parts 210 are used for structural support of the elevated work table 205 and to avoid an angular motion, units 212 and 214 are used for structural stability of the scissors 210 and to enable a rotating scissor axis, respectively. 222 and 232 are mounting struts for the stepping motors 228, 224 in the X and Y direction, respectively. Components 205, 210, 212, 222 and 232 can be made from aluminum, and component 214 can be a stainless steel rod. If the table is elevated in the Z-direction, the scissors 210 open up and prevent angular motion of the work table 205 in the XY-plane. Motions in X and Y directions are initiated by stepping motors 228, 224 and the whole work stage is translated in the selected direction(s).
    [0046] FIG. 5 is an enlarged view of the powder feeder and carrier gas connection [0046] 300 used in the system of FIG. 1, and includes a powder feeding unit 310 and the carrier gas connection 338 of FIG. 1. FIG. 5 includes an enlarged view 320 of the restricted orifice 327 for the powder flow. Powder feeder 310 can be an Accurate volumetric powder feeder having a motor 312, a helix 314 for powder delivery, a pipe extension 316 for the helix 314, and a container 318 for the powder 319. The powder 319 is fed from the container 318 by the helix 314 into a funnel 320 with a restricted orifice 327. The restriction 327 serves as a fine tuner for the powder flow rate, and can be a disk with a variable diameter center hole. Funnel 320 serves as a pre-mixer for different powders being used for parts fabrication, and is an averager for potential fluctuations in the powder feed rate from the helix 314. If only one powder 319 is used, the funnel 320 can be omitted. The configuration of FIG. 5 allows for plural adjacent powder feeder(s) 310 to feed powder 319 into the same funnel 320. After the powder 319 passes through the orifice 327, it falls down into the delivery tube 390 (having an inner diameter of approximately 3 mm), where it mixes with the low-volume carrier gas 330 supplied by tube 338. Carrier gas 330 can be chosen from gases such as but not limited to nitrogen, helium, argon, and the like, and having a flow rate of approximately 1 to approximately 20 liters per minute proportional to powder flow rates. The carrier gas 330 provides for an even powder flow and mixing of different powders through the delivery tube 390. Depending upon the powder flow rate, powder 319 exits the delivery tube 390 through a channel 395 (FIG. 1) having a diameter of approximately 1.5 mm at an angle of approximately 30 to approximately 50 degrees with respect to the laser beam B.
    [0047] FIG. 7 shows the shield gas connection [0047] 500 used in the manufacturing system of FIG. 1. Referring to FIG. 7, shield gas 510, such as Argon, and the like, flows at a rate of approximately 15 liters per minute through flow tube 505 into beam transmission tube 150. The interaction between the laser-heated material and surrounding air will cause oxide formation resulting in oxide particles in the finished part, which is detrimental to the mechanical strength of the part. To prevent this argon gas 510 is used as a shielding gas. The shielding gas 510 serves two purposes, first to cool the lens 130, second to provide effective shielding against oxidation at the laser interaction zone.
    [0048] Referring to FIGS. 1, 5, and [0048] 7, powder 319 coming out of the feeder nozzle 395 interacts immediately with the laser beam to form liquid droplets and gets deposited on the substrate. (See FIG. 8 for a basic drawing of the substrate 170 and some deposited layers 175). The flow rate of the shielding gas 510 is also kept low to prevent driving away the powder particles 319 from the interaction zone. The surface of the substrate 170 was placed at the focal point f1, of lens 130.
    [0049] FIG. 6 is an over view of the computer control system [0049] 400 used in the manufacturing system of FIG. 1. Laser 100 (FIG. 2), 100′ (FIG. 3), the powder delivery components 310 (FIGS. 1, 5), the XYZ workstage 200 (FIGS. 1, 4), the selection and positioning of the beam focussing and delivery optics 120 (FIGS. 1, 2, 7) 130 (FIG. 2), and the fiber optics (FIG. 3), and the shield gas flow rates 510 (FIGS. 1, 7) and carrier gas flow rate 330 (FIGS. 1, 5) are controlled by a computer 410, here an IBM compatible Pentium P5-120. Controller 420 is separately connected by lines 421, 422, 423, 424, 425, 426, 427, 428, 429 to the system components 100, 100′, 120, 130, 200, 310, 330, 510 using standard line interface connections. Computer 410 controls the open and close cycle of the laser shutter 115 (FIG. 2), the shield gases 510, the carrier gases 330, as well as the flow rates of these gasses 330, 510. Computer 410 was operated using Motion Control Interface Firmware (MCIF) software, suitable for operation with Windows 3.1x, Windows 95 and Windows 98.
    [0050] FIG. 3 shows an alternative beam delivery system [0050] 100′ of a laser source 110′, fiber optic cable 120′, and beam focussing optics 130′ and fiber output coupler 130′ for use in the manufacturing system of FIG. 1.
    [0051] Referring to FIGS. [0051] 1, 3-7, laser 110′ can be a Nd:YAG laser with a shutter 115′. The operating ranges (power, intensity, distribution in the beam are similar to the one for a CO2 laser, and can be used with fiber optic cables 120′, focussing optics 130′, and fiber output coupler 140′ similar to those described above. In operation, the Nd:YAG laser 110′ takes the place of the CO2 laser 110, the fiber optic cable 120′ and fiber output coupler 130′ has the same function and the delivery of the processing laser beam to the substrate only, the parts fabrication and the process control are not affected.
    [0052] FIG. 8 shows an example of a multiple application system, illustrated by an optical fiber output coupler [0052] 140′ processing a powder flow 319 and forming a layered structure 175 on substrate 170 (on top of XYZ workstage 200. Simultaneously, a second optical fiber output coupler 180′ connected a laser source 100/100′ can be used to drill a hole 195 into the fabricated part 175/170.
    [0053] FIGS. [0053] 9A-9B, show graphical distributions of a laser beam intensity being distributed asymmetrically with the laser beam. FIG. 9A shows a graph of laser beam length versus intensity for an example of a Laser Beam Shape tailored to the parts' selected properties. Referring to FIG. 9A, the ramped high laser beam intensity 700 provides a sufficient local energy density to melt the powder material while simultaneously imposing a thermal gradient 710 on the solidifying and solidified deposited layer.
    [0054] FIG. 9B shows a graph of laser beam width versus intensity for an example of a Laser Beam Shape tailored to the parts' selected properties. By providing an asymmetric intensity distribution along the direction of the laser beam motion [0054] 720 and 730 of FIG. 9B, one can force different features (for example increased/decreased hardness) on both sides of the deposited material.
    [0055] FIGS. 9A and 9B show that by using asymmetric components in the beam delivery system (e.g. lenses focussing the beam into an elliptical spot, adaptics optics, and the like), it is possible to tailor the intensity distribution in the beam to the requirements at the deposition region or to create parts with pre-selected mechanical or thermodynamic properties, e.g., by superimposing a thermal gradient on to the deposited layer or by heat treating and/or preheating the previously deposited layers. [0055]
    [0056] FIG. 11 shows a laser beam [0056] 160 being directed at a set of reflective optics in wedge form 810, the sharp corner 812 of the wedge 810 being placed in the path of the laser beam 160. The laser beam 160 is reflected at R1 towards a second set of reflective optics 820, form there the beam R2 is directed at the substrate 170 where material powder 319 is to be melted. Splitting up the beam 160 allows for space to deliver the powder or the wire such that it can be delivered perpendicular to the substrate 170 allowing for true coaxial feeding.
    [0057] In a beam splitting application, the laser beam [0057] 160 can be split into two or more parts by placing a reflective element such as those previously described, into the beam path (here illustrated in two parts). In the place where the unreflected laser beam would have propagated, powder is delivered to the deposition region at an angle of approximately 90 degrees with respect to the substrate 170 surface. Using suitable reflective elements such as those previously described, the reflected parts of the beam are directed at a point where the powder flow hits the substrate surface and are recombined there. This enables a true coaxial powder feeding system, benefits of which are the mutual independence of the powder flow direction and the direction of substrate translation (feeding powder “before or after” the laser beam). Furthermore, this setup allows one to recombine the laser beam into its original shape or, depending on the process requirements, it allows one to create an overlap of selected parts of the laser beam by adjusting the second set of reflective elements. Thereby, it is possible to alter the maximum available intensity for a given high power laser. This beam shaping offers similar advantages as those previously described.
    [0058] The invention can be used to perform surface alloying on components, e.g., it is possible to change for example, mild steel into stainless steel by mixing the missing elements into the top surface of the material. [0058]
    [0059] Furthermore, the invention can be used for various substrate joining. Here, joining the deposited material with the substrate is optional and process-dependent. One can create an “add-on” to an existing part. However, it is possible that one wants to remove the created part as easily as possible. For example, a stainless steel part can be formed on an aluminum surface, and the laser power can be chosen such that the steel powder is melted but the aluminum substrate is not. Also, vice versa, one can create an aluminum part on a steel surface because steel is a worse conductor of thermal energy than aluminum, thereby most of the energy supplied would be used for the creation of the part. [0059]
    [0060] Although the preferred embodiments describe using CO[0060] 2 lasers and Nd:YAG lasers, the invention can use other high power lasers (i.e. Nd-based solid state lasers), and diode lasers, and the like. The invention works with continuous and pulsed lasers that supply sufficient intensity for material melting.
    [0061] Similarly the subject invention can use various shield gases such as but not limited to nitrogen, argon, and helium. [0061]
    [0062] Although, the preferred embodiments describe using various alloy powders, other powders can be used such as but not limited to combinations of niobium, titanium, steels, tool steels, copper, tungsten, aluminum, nickel, alloys thereof, ceramics, and cermets. [0062]
    [0063] While the invention has been described, disclosed, illustrated and shown in various terms of certain embodiments or modifications which it has presumed in practice, the scope of the invention is not intended to be, nor should it be deemed to be, limited thereby and such other modifications or embodiments as may be suggested by the teachings herein are particularly reserved especially as they fall within the breadth and scope of the claims here appended. [0063]
    权利要求:
    Claims (31)
    [1" id="US-20010002287-A1-CLM-00001] 1. A one-step/method of fabricating three dimensional (3-D) parts from metal and composite parts, comprising the steps of:
    (a) focussing a high power laser beam into a spot location;
    (b) feeding material powder into the spot location coaxially to the laser beam;
    (c) forming a first deposition layer by directly melting the material powder with the laser beam on a surface supported by an XYZ workstage platform that translates in the XY plane direction; and
    (d) forming a second deposition layer on top of the first deposition layer with steps (a) and (b) and by displacing the XYZ workstage platform in the Z plane direction, wherein steps (a), (b), and (c) are used to determine length, width, and thickness of each layer in order to form selected fabricated 3-D parts.
    [2" id="US-20010002287-A1-CLM-00002] 2. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , further comprising the step of:
    controlling steps (a), (b), (c) and (d) with a computer.
    [3" id="US-20010002287-A1-CLM-00003] 3. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , wherein the laser beam of step (a) is:
    a CO2 laser.
    [4" id="US-20010002287-A1-CLM-00004] 4. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , wherein the material powder of step (b) includes:
    an alloy material formed from two different material powders.
    [5" id="US-20010002287-A1-CLM-00005] 5. The one-step method of fabricating three dimensional (3-D) parts of
    claim 4 , wherein the alloy material includes:
    stainless steel powder and copper powder.
    [6" id="US-20010002287-A1-CLM-00006] 6. The one-step method of fabricating three dimensional (3-D) parts of
    claim 4 , wherein the alloy material includes:
    aluminum powder and copper powder.
    [7" id="US-20010002287-A1-CLM-00007] 7. The one-step method of fabricating three dimensional (3-D) parts of
    claim 4 , wherein the alloy material includes:
    titanium powder and copper powder.
    [8" id="US-20010002287-A1-CLM-00008] 8. The one-step method of fabricating three dimensional (3-D) parts of
    claim 4 , wherein the alloy material includes:
    titanium powder and aluminum powder.
    [9" id="US-20010002287-A1-CLM-00009] 9. The one-step method of fabricating three dimensional (3-D) parts of
    claim 4 , wherein the alloy material includes:
    stainless steel powder and aluminum powder.
    [10" id="US-20010002287-A1-CLM-00010] 10. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , further comprising the step of:
    providing a shield gas to the laser beam to prevent oxidation in the directly melted material powder.
    [11" id="US-20010002287-A1-CLM-00011] 11. The one-step method of fabricating three dimensional (3-D) parts of
    claim 10 , wherein the shield gas is chosen from at least one of:
    argon gas, nitrogen gas and helium gas.
    [12" id="US-20010002287-A1-CLM-00012] 12. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , further comprising the steps of:
    providing a carrier gas to deliver the material powder to the spot location.
    [13" id="US-20010002287-A1-CLM-00013] 13. The one-step method of fabricating three dimensional (3D) parts of
    claim 12 , wherein the carrier gas is further used as a shield gas at the first deposition layer and the second deposition layer.
    [14" id="US-20010002287-A1-CLM-00014] 14. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , wherein the laser beam of step (a) is:
    a Nd:YAG laser.
    [15" id="US-20010002287-A1-CLM-00015] 15. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , wherein step (a) further includes:
    an adaptive optic for focussing the high beam power laser; and
    a fiber optic cable and output coupler.
    [16" id="US-20010002287-A1-CLM-00016] 16. A one-step system of fabricating three dimensional (3-D) parts from metal and composite parts, comprising:
    a laser for forming a high power beam into a spot location;
    means for feeding material powder into the spot location coaxially to the laser beam;
    an XYZ translation support means for forming forming plural deposition layers having different thicknesses, from the laser beam and the material powder; and
    a computer for controlling the laser, the material powder feeding means and the XYZ translation support means in order to form selected fabricated 3-D parts in one step.
    [17" id="US-20010002287-A1-CLM-00017] 17. The one-step system of
    claim 16 , wherein the laser beam includes
    a continuous wave CO2 laser with a shutter, and beam delivery optics and beam focussing optics, wherein the laser shutter, the beam delivery optics and the beam focussing optics are separately and simultaneously controlled by the computer.
    [18" id="US-20010002287-A1-CLM-00018] 18. The one-step system of
    claim 16 , wherein the laser beam includes:
    a Nd:YAG laser with a shutter connected to an fiber optic cable and output coupler, and beam delivery optics and beam focussing optics, wherein the laser shutter, the optic cable, the output coupler, the beam delivery optics and the beam focussing optics are separately and simultaneously controlled by the computer.
    [19" id="US-20010002287-A1-CLM-00019] 19. The one-step system of
    claim 16 , further comprising:
    a carrier gas supply having an adjustable flow rate for delivering the material powder to the spot location, wherein the carrier supply and the flow rate are separately and simultaneously controlled by the computer.
    [20" id="US-20010002287-A1-CLM-00020] 20. The one-step system of
    claim 16 , further comprising:
    a shield gas supply having an adjustable flow rate for being applied to the laser beam to prevent oxidation in the directly melted material powder, wherein the shield gas supply and flow rate are separately and simultaneously controlled by the computer.
    [21" id="US-20010002287-A1-CLM-00021] 21. The one-step system of
    claim 20 , wherein the shield gas is chosen from at least one of:
    argon gas, nitrogen gas and helium gas.
    [22" id="US-20010002287-A1-CLM-00022] 22. The one-step system of
    claim 16 , wherein the material powder includes:
    stainless steel powder and copper powder.
    [23" id="US-20010002287-A1-CLM-00023] 23. The one-step system of
    claim 16 , wherein the material powder includes:
    stainless steel powder and aluminum powder.
    [24" id="US-20010002287-A1-CLM-00024] 24. The one-step system of
    claim 16 , wherein the material powder includes at least two powders chosen from at least one of:
    niobium, titanium, steels, tool steels, copper, tungsten, aluminum, nickel, alloys thereof, ceramics, and cermets.
    [25" id="US-20010002287-A1-CLM-00025] 25. The one-step system of
    claim 16 , wherein the laser can be chosen from at least one of:
    a Nd-based solid state laser and a diode laser.
    [26" id="US-20010002287-A1-CLM-00026] 26. The one-step system of
    claim 16 , further comprising:
    lens means for beam shaping the laser to tailor intensity distribution of the laser beam for the deposition layers.
    [27" id="US-20010002287-A1-CLM-00027] 27. The one-step system of
    claim 16 , further comprising:
    reflective and refractive means for beam shaping the laser to form pre-selected mechanical and thermodynamic properties in the selected fabricated 3-D parts by heating the deposition layers.
    [28" id="US-20010002287-A1-CLM-00028] 28. The one-step system of
    claim 16 , further comprising:
    means for splitting the laser beam into at least two angled beams each of which is not perpendicular to a substrate at the spot location; and
    a perpendicular delivery means for feeding the metal powder at an angle of approximately 90 degrees to the substrate, wherein the metal powder is delivered in between the two angled beams; and
    means for recombining the two angled beams at the spot location on the substrate.
    [29" id="US-20010002287-A1-CLM-00029] 29. The one step system of
    claim 16 , further comprising:
    means for performing surface alloying on metal components.
    [30" id="US-20010002287-A1-CLM-00030] 30. The one-step system of
    claim 16 , wherein the material powder includes:
    ceramic powder.
    [31" id="US-20010002287-A1-CLM-00031] 31. The one-step method of fabricating three dimensional (3-D) parts of
    claim 1 , wherein the material powder of step (b) includes:
    ceramic material.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6526327B2|2003-02-25|One-step rapid manufacturing of metal and composite parts
    Gibson et al.2015|Directed energy deposition processes
    US6811744B2|2004-11-02|Forming structures from CAD solid models
    US6316744B1|2001-11-13|Machining head and process for the surface machining of workpieces by means of a laser beam
    US6391251B1|2002-05-21|Forming structures from CAD solid models
    US6143378A|2000-11-07|Energetic additive manufacturing process with feed wire
    US6504127B1|2003-01-07|Laser consolidation methodology and apparatus for manufacturing precise structures
    US6269540B1|2001-08-07|Process for manufacturing or repairing turbine engine or compressor components
    US6756561B2|2004-06-29|Laser consolidation apparatus for manufacturing precise structures
    AU754346B2|2002-11-14|Apparatus and methods for laser cladding
    US4818562A|1989-04-04|Casting shapes
    EP0416852B1|1997-07-16|Multiple material systems and assisted powder handling for selective beam sintering
    US5993554A|1999-11-30|Multiple beams and nozzles to increase deposition rate
    US5296062A|1994-03-22|Multiple material systems for selective beam sintering
    JP4112625B2|2008-07-02|High-speed manufacturing system using laser melting of raw materials
    EP0289116A1|1988-11-02|Method and device for casting powdered materials
    JP2003127238A|2003-05-08|Selective laser sintering wherein filling scan is interleaved
    US20040020625A1|2004-02-05|Fabrication of customized die inserts using closed-loop direct metal deposition |
    Paul et al.2018|Metal additive manufacturing using lasers
    KR20190004702A|2019-01-14|Sputtering target assembly having a graded intermediate layer and method of making
    US20030075529A1|2003-04-24|Focusing optics for adaptive deposition in rapid manufacturing
    Su et al.2003|Investigation of fully dense laser sintering of tool steel powder using a pulsed Nd: YAG | laser
    US7342195B2|2008-03-11|Customizable ion fusion formation system and process
    CA2215940C|2006-06-13|Laser sintering apparatus for producing coatings and dense metal parts
    EP3766604A1|2021-01-20|Method and device for purging an additive manufacturing space
    同族专利:
    公开号 | 公开日
    US6526327B2|2003-02-25|
    US6203861B1|2001-03-20|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    EP1402978A1|2002-09-27|2004-03-31|The University of Queensland|Infiltrated aluminum preforms|
    US20050173380A1|2004-02-09|2005-08-11|Carbone Frank L.|Directed energy net shape method and apparatus|
    US20070183918A1|2004-03-16|2007-08-09|Degussa Ag|Method and device for producing three-dimensional objects using laser technology and for applying an absorber using an ink jet method|
    US20070238056A1|2004-04-27|2007-10-11|Degussa Ag|Method and Device for Production of Three-Dimensional Objects by Means of Electromagnetic Radiation of Electromagnetic Radiation and Application of an Absorber by Means of an Ink-Jet Method|
    US7682578B2|2005-11-07|2010-03-23|Geo2 Technologies, Inc.|Device for catalytically reducing exhaust|
    US7682577B2|2005-11-07|2010-03-23|Geo2 Technologies, Inc.|Catalytic exhaust device for simplified installation or replacement|
    US7722828B2|2005-12-30|2010-05-25|Geo2 Technologies, Inc.|Catalytic fibrous exhaust system and method for catalyzing an exhaust gas|
    US20120266814A1|2011-04-20|2012-10-25|Rolls-Royce Plc|Laser beam intensity distribution|
    US20130183493A1|2011-07-21|2013-07-18|Evonik Degussa Gmbh|Component properties through beam shaping in the laser sintering process|
    US8604381B1|2006-10-12|2013-12-10|Purdue Research Foundation|Integrated laser material processing cell|
    DE102012107297A1|2012-08-08|2014-06-18|Ralph Stelzer|Working method for producing three-dimensional workpiece under e.g. normal atmosphere, involves fully hardening applied layers of powdered materials at laser beam incidence on workpiece surface after introducing liquid or binding agent|
    US20140259589A1|2013-03-15|2014-09-18|Rolls-Royce Corporation|Repair of gas turbine engine components|
    WO2014150365A1|2013-03-15|2014-09-25|United Technologies Corporation|Additive manufacturing baffles, covers, and dies|
    DE102013226298A1|2013-12-17|2015-06-18|MTU Aero Engines AG|Exposure to generative production|
    CN104907562A|2015-06-05|2015-09-16|湖南华曙高科技有限责任公司|Equipment for manufacturing three-dimensional object|
    WO2016026706A1|2014-08-20|2016-02-25|Etxe-Tar, S.A.|Method and system for additive manufacturing using a light beam|
    JP2016521195A|2013-03-15|2016-07-21|パイロテック インコーポレイテッド|Ceramic filter|
    EP3112134A4|2014-03-31|2017-08-09|Mitsubishi Heavy Industries, Ltd.|Three-dimensional lamination device and three-dimensional lamination method|
    DE102016205437A1|2016-04-01|2017-10-05|MTU Aero Engines AG|Device and method for producing or repairing a three-dimensional object|
    US20180009166A1|2015-12-25|2018-01-11|Technology Research Association Future Additive Manufacturing|Three-dimensional laminating and shaping apparatus, control method of three-dimensional laminating and shaping apparatus, and control program of three-dimensional laminating and shaping apparatus|
    EP3315241A1|2016-10-31|2018-05-02|mobil-mark GmbH|Laser processing device|
    US10046394B2|2014-09-16|2018-08-14|The Penn State Research Foundation|Method for manufacturing overhanging material by pulsed, voxel-wise buildup|
    CN111014667A|2019-11-07|2020-04-17|上海汉邦联航激光科技有限公司|Preparation method of throttler|
    US10799975B2|2016-02-29|2020-10-13|Rolls-Royce Corporation|Directed energy deposition for processing gas turbine engine components|US4299860A|1980-09-08|1981-11-10|The United States Of America As Represented By The Secretary Of The Navy|Surface hardening by particle injection into laser melted surface|
    IT1179061B|1984-08-20|1987-09-16|Fiat Auto Spa|PROCEDURE FOR CARRYING OUT A TREATMENT ON METAL PIECES WITH THE ADDITION OF A VALUE MATERIAL AND WITH THE USE OF A POWER LASER|
    FR2605310B1|1986-10-16|1992-04-30|Comp Generale Electricite|METHOD FOR REINFORCING CERAMIC WORKPIECES BY LASER TREATMENT|
    AT116179T|1986-10-17|1995-01-15|Univ Texas|METHOD AND DEVICE FOR PRODUCING MOLDED BODIES BY PARTIAL INTERSTERING.|
    US5132248A|1988-05-31|1992-07-21|The United States Of America As Represented By The United States Department Of Energy|Direct write with microelectronic circuit fabrication|
    US5216616A|1989-06-26|1993-06-01|Masters William E|System and method for computer automated manufacture with reduced object shape distortion|
    DE3935009A1|1989-10-20|1991-04-25|Inst Nat Sciences Appliq|DEVICE FOR THE LASER PLASMA COATING|
    US5189781A|1990-08-03|1993-03-02|Carnegie Mellon University|Rapid tool manufacturing|
    JPH04100689A|1990-08-14|1992-04-02|Tsubakimoto Chain Co|Quintaxial table for laser beam machine|
    JPH0534425B2|1990-09-10|1993-05-24|Kogyo Gijutsuin||
    JPH04169905A|1990-11-01|1992-06-17|Fanuc Ltd|Coordinate transform system for three-dimensional laser|
    US5147680A|1990-11-13|1992-09-15|Paul Slysh|Laser assisted masking process|
    US5385780A|1990-12-05|1995-01-31|The B. F. Goodrich Company|Sinterable mass of polymer powder having resistance to caking and method of preparing the mass|
    US5314003A|1991-12-24|1994-05-24|Microelectronics And Computer Technology Corporation|Three-dimensional metal fabrication using a laser|
    FR2688803B1|1992-03-23|1994-05-06|European Gas Turbines Sa|METHOD FOR COATING A NOTCH OF A NICKEL ALLOY PIECE BY LASER.|
    US5688564A|1992-07-23|1997-11-18|Institut Polytechnique De Sevenans|Process for the preparation and coating of a surface|
    US5313542A|1992-11-30|1994-05-17|Breault Research Organization, Inc.|Apparatus and method of rapidly measuring hemispherical scattered or radiated light|
    US5449536A|1992-12-18|1995-09-12|United Technologies Corporation|Method for the application of coatings of oxide dispersion strengthened metals by laser powder injection|
    US5398193B1|1993-08-20|1997-09-16|Alfredo O Deangelis|Method of three-dimensional rapid prototyping through controlled layerwise deposition/extraction and apparatus therefor|
    US5837960A|1995-08-14|1998-11-17|The Regents Of The University Of California|Laser production of articles from powders|
    US5622577A|1995-08-28|1997-04-22|Delco Electronics Corp.|Rapid prototyping process and cooling chamber therefor|US7765022B2|1998-06-30|2010-07-27|The P.O.M. Group|Direct metal deposition apparatus utilizing rapid-response diode laser source|
    US20020110649A1|2000-05-09|2002-08-15|Skszek Timothy W.|Fabrication of alloy variant structures using direct metal deposition|
    US6756561B2|1999-09-30|2004-06-29|National Research Council Of Canada|Laser consolidation apparatus for manufacturing precise structures|
    US6534134B1|1998-11-20|2003-03-18|University Of Puerto Rico|Apparatus and method for pulsed laser deposition of materials on wires and pipes|
    EP1173304B1|2000-02-28|2005-07-20|Hydro Aluminium Deutschland GmbH|Method for producing a surface-alloyed cylindrical, partially cylindrical or hollow cylindrical component|
    WO2001085368A1|2000-05-09|2001-11-15|Usf Filtration And Separations Group, Inc.|Apparatus and method for drawing continuous fiber|
    EP1296776A4|2000-06-01|2004-12-08|Univ Texas|Direct selective laser sintering of metals|
    GB0028557D0|2000-11-23|2001-01-10|Innovative Materials Proc Tech|Fabrication method and apparatus|
    JP2002316363A|2001-02-16|2002-10-29|Fuji Photo Film Co Ltd|Optical shaping device and exposure unit|
    EP1234625A1|2001-02-21|2002-08-28|Trumpf Werkzeugmaschinen GmbH + Co. KG|Process and apparatus for producing a shaped body by selective laser sintering|
    US6710280B2|2001-05-22|2004-03-23|The P.O.M. Group|Focusing optics for adaptive deposition in rapid manufacturing|
    US6680456B2|2001-06-09|2004-01-20|Honeywell International Inc.|Ion fusion formation|
    JP2003080604A|2001-09-10|2003-03-19|Fuji Photo Film Co Ltd|Laminate shaping apparatus|
    EP1470265A2|2002-01-24|2004-10-27|H.C. Starck Inc.|Refractrory metal and alloy refining by laser forming and melting|
    US6593540B1|2002-02-08|2003-07-15|Honeywell International, Inc.|Hand held powder-fed laser fusion welding torch|
    US7045738B1|2002-10-01|2006-05-16|Southern Methodist University|Powder delivery system and method|
    US7020539B1|2002-10-01|2006-03-28|Southern Methodist University|System and method for fabricating or repairing a part|
    US7160475B2|2002-11-21|2007-01-09|Fei Company|Fabrication of three dimensional structures|
    US7163550B2|2003-03-26|2007-01-16|Scimed Life Systems, Inc.|Method for manufacturing medical devices from linear elastic materials while maintaining linear elastic properties|
    AT370832T|2003-05-01|2007-09-15|Objet Geometries Ltd|RAPID PROTOTYPING APPARATUS|
    US9022037B2|2003-08-11|2015-05-05|Raydiance, Inc.|Laser ablation method and apparatus having a feedback loop and control unit|
    US7361171B2|2003-05-20|2008-04-22|Raydiance, Inc.|Man-portable optical ablation system|
    JP4267378B2|2003-06-11|2009-05-27|トヨタ自動車株式会社|Laser welding method and apparatus for resin member, and laser welding member|
    US7367969B2|2003-08-11|2008-05-06|Raydiance, Inc.|Ablative material removal with a preset removal rate or volume or depth|
    US8173929B1|2003-08-11|2012-05-08|Raydiance, Inc.|Methods and systems for trimming circuits|
    US8921733B2|2003-08-11|2014-12-30|Raydiance, Inc.|Methods and systems for trimming circuits|
    US20050065502A1|2003-08-11|2005-03-24|Richard Stoltz|Enabling or blocking the emission of an ablation beam based on color of target|
    US7143769B2|2003-08-11|2006-12-05|Richard Stoltz|Controlling pulse energy of an optical amplifier by controlling pump diode current|
    US20050038487A1|2003-08-11|2005-02-17|Richard Stoltz|Controlling pulse energy of an optical amplifier by controlling pump diode current|
    US6940037B1|2003-08-25|2005-09-06|Southern Methodist University|System and method for controlling welding parameters in welding-based deposition processes|
    US6995334B1|2003-08-25|2006-02-07|Southern Methodist University|System and method for controlling the size of the molten pool in laser-based additive manufacturing|
    US7115514B2|2003-10-02|2006-10-03|Raydiance, Inc.|Semiconductor manufacturing using optical ablation|
    WO2005089090A2|2003-10-14|2005-09-29|North Dakota State University|Direct write and freeform fabrication apparatus and method|
    US7666522B2|2003-12-03|2010-02-23|IMDS, Inc.|Laser based metal depositionof implant structures|
    US7001672B2|2003-12-03|2006-02-21|Medicine Lodge, Inc.|Laser based metal deposition of implant structures|
    US7413847B2|2004-02-09|2008-08-19|Raydiance, Inc.|Semiconductor-type processing for solid-state lasers|
    US7618880B1|2004-02-19|2009-11-17|Quick Nathaniel R|Apparatus and method for transformation of substrate|
    US8617965B1|2004-02-19|2013-12-31|Partial Assignment to University of Central Florida|Apparatus and method of forming high crystalline quality layer|
    US20050212694A1|2004-03-26|2005-09-29|Chun-Ta Chen|Data distribution method and system|
    KR100621786B1|2004-05-12|2006-09-14|고등기술연구원연구조합|High energy density beam welding system using molten metal droplet jetting|
    US7268063B1|2004-06-01|2007-09-11|University Of Central Florida|Process for fabricating semiconductor component|
    US7419887B1|2004-07-26|2008-09-02|Quick Nathaniel R|Laser assisted nano deposition|
    US20060049153A1|2004-09-08|2006-03-09|Cahoon Christopher L|Dual feed laser welding system|
    US7349452B2|2004-12-13|2008-03-25|Raydiance, Inc.|Bragg fibers in systems for the generation of high peak power light|
    US7951632B1|2005-01-26|2011-05-31|University Of Central Florida|Optical device and method of making|
    US7524345B2|2005-02-22|2009-04-28|Saint-Gobain Abrasives, Inc.|Rapid tooling system and methods for manufacturing abrasive articles|
    US7867302B2|2005-02-22|2011-01-11|Saint-Gobain Abrasives, Inc.|Rapid tooling system and methods for manufacturing abrasive articles|
    US7875091B2|2005-02-22|2011-01-25|Saint-Gobain Abrasives, Inc.|Rapid tooling system and methods for manufacturing abrasive articles|
    JP4311364B2|2005-03-18|2009-08-12|セイコーエプソン株式会社|Droplet discharge device|
    US20060266745A1|2005-05-31|2006-11-30|Honeywell International, Inc.|Gas shielding apparatus and method of use|
    DE102005030067A1|2005-06-27|2006-12-28|FHS Hochschule für Technik, Wirtschaft und soziale Arbeit St. Gallen|Apparatus for producing objects using generative method, e.g. selective laser sintering, has system for generating mist of fluid between electromagnetic component and process chamber|
    US8135050B1|2005-07-19|2012-03-13|Raydiance, Inc.|Automated polarization correction|
    US7245419B2|2005-09-22|2007-07-17|Raydiance, Inc.|Wavelength-stabilized pump diodes for pumping gain media in an ultrashort pulsed laser system|
    US7308171B2|2005-11-16|2007-12-11|Raydiance, Inc.|Method and apparatus for optical isolation in high power fiber-optic systems|
    US20070122560A1|2005-11-30|2007-05-31|Honeywell International, Inc.|Solid-free-form fabrication process including in-process component deformation|
    US7444049B1|2006-01-23|2008-10-28|Raydiance, Inc.|Pulse stretcher and compressor including a multi-pass Bragg grating|
    US8189971B1|2006-01-23|2012-05-29|Raydiance, Inc.|Dispersion compensation in a chirped pulse amplification system|
    CN100404174C|2006-01-24|2008-07-23|华中科技大学|Preparation method for quick preparing functional gradient material|
    US7822347B1|2006-03-28|2010-10-26|Raydiance, Inc.|Active tuning of temporal dispersion in an ultrashort pulse laser system|
    US8617669B1|2006-04-20|2013-12-31|Partial Assignment to University of Central Florida|Laser formation of graphene|
    US7811914B1|2006-04-20|2010-10-12|Quick Nathaniel R|Apparatus and method for increasing thermal conductivity of a substrate|
    US8232687B2|2006-04-26|2012-07-31|Raydiance, Inc.|Intelligent laser interlock system|
    US7951412B2|2006-06-07|2011-05-31|Medicinelodge Inc.|Laser based metal depositionof antimicrobials to implant surfaces|
    US8067303B1|2006-09-12|2011-11-29|Partial Assignment University of Central Florida|Solid state energy conversion device|
    WO2008154045A1|2007-06-12|2008-12-18|Rolls-Royce Corporation|System, methods, and apparatus for repair of components|
    US8076607B2|2007-06-27|2011-12-13|Ross Technology Corporation|Method and apparatus for depositing raised features at select locations on a substrate to produce a slip-resistant surface|
    US8114693B1|2007-09-18|2012-02-14|Partial Assignment University of Central Florida|Method of fabricating solid state gas dissociating device by laser doping|
    US8367962B2|2007-10-26|2013-02-05|Ariel Andre Waitzman|Automated welding of moulds and stamping tools|
    US8362392B2|2008-02-05|2013-01-29|Pratt & Whitney Canada Corp.|Method for drilling holes according to an optimized sequence|
    US20090289382A1|2008-05-22|2009-11-26|Raydiance, Inc.|System and method for modifying characteristics of a contact lens utilizing an ultra-short pulsed laser|
    US8125704B2|2008-08-18|2012-02-28|Raydiance, Inc.|Systems and methods for controlling a pulsed laser by combining laser signals|
    EP2356688A1|2008-12-02|2011-08-17|University Of Central Florida|Energy conversion device|
    EP2317076B1|2009-10-30|2018-02-14|Ansaldo Energia IP UK Limited|A method for repairing a gas turbine component|
    EP2317079B1|2009-10-30|2020-05-20|Ansaldo Energia Switzerland AG|Abradable coating system|
    EP2317075B1|2009-10-30|2013-01-02|Alstom Technology Ltd|Method for repairing a gas turbine component|
    EP2319641B1|2009-10-30|2017-07-19|Ansaldo Energia IP UK Limited|Method to apply multiple materials with selective laser melting on a 3D article|
    WO2011055373A1|2009-11-03|2011-05-12|The Secretary, Department Of Atomic Energy,Govt.Of India.|Niobium based superconducting radio frequencycavities comprising niobium components joined by laser welding; method and apparatus for manufacturing such cavities|
    WO2011056892A1|2009-11-03|2011-05-12|Applied Spectra, Inc.|Method for real-time optical diagnostics in laser ablation and laser processing of layered and structured materials|
    US10119195B2|2009-12-04|2018-11-06|The Regents Of The University Of Michigan|Multichannel cold spray apparatus|
    MX2012006392A|2009-12-04|2012-08-23|Univ Michigan|Coaxial laser assisted cold spray nozzle.|
    WO2011071601A1|2009-12-08|2011-06-16|Husky Injection Molding Systems Ltd|Hot-runner system having manifold assembly manufactured in accordance with free-form fabrication process|
    US8740598B2|2009-12-08|2014-06-03|Husky Injection Molding Systems Ltd.|Multi-property injection molding nozzle for a hot-runner system|
    US8884184B2|2010-08-12|2014-11-11|Raydiance, Inc.|Polymer tubing laser micromachining|
    US9120181B2|2010-09-16|2015-09-01|Coherent, Inc.|Singulation of layered materials using selectively variable laser output|
    DE102011007067A1|2011-04-08|2012-10-11|Siemens Aktiengesellschaft|Method for selective laser melting and installation for carrying out this method|
    US10201877B2|2011-10-26|2019-02-12|Titanova Inc|Puddle forming and shaping with primary and secondary lasers|
    GB201118698D0|2011-10-28|2011-12-14|Laser Fusion Technologies Ltd|Deposition of coatings on subtrates|
    FR2987293B1|2012-02-27|2014-03-07|Michelin & Cie|METHOD AND APPARATUS FOR REALIZING THREE-DIMENSIONAL OBJECTS WITH IMPROVED PROPERTIES|
    US9059079B1|2012-09-26|2015-06-16|Ut-Battelle, Llc|Processing of insulators and semiconductors|
    WO2014117097A2|2013-01-28|2014-07-31|National Oilwell Varco, L.P.|Accurate placement of powders to form optimized polycrystalline diamond cutter elements and cutting tools|
    UA79828U|2013-03-05|2013-04-25|Илья Петрович Кулишко|Method of manufacturing molds|
    US9539764B2|2013-03-15|2017-01-10|United Technologies Corporation|Usage of a witness mark to distinguish support structure from part|
    JP6571638B2|2013-06-10|2019-09-04|レニショウ パブリック リミテッド カンパニーＲｅｎｉｓｈａｗ Ｐｕｂｌｉｃ Ｌｉｍｉｔｅｄ Ｃｏｍｐａｎｙ|Selective laser solidification apparatus and method|
    GB201310398D0|2013-06-11|2013-07-24|Renishaw Plc|Additive manufacturing apparatus and method|
    CN103399405B|2013-07-17|2016-07-06|苏州大学|A kind of laser wide-band cladding device and method|
    CN103624258B|2013-11-11|2015-08-05|西安交通大学|A kind of laser metal forming system and method manufacturing large angle of inclination part|
    US9620667B1|2013-12-10|2017-04-11|AppliCote Associates LLC|Thermal doping of materials|
    US9601641B1|2013-12-10|2017-03-21|AppliCote Associates, LLC|Ultra-high pressure doping of materials|
    DE102014207510B4|2014-04-17|2021-12-16|Kennametal Inc.|Cutting tool and method for producing a cutting tool|
    DE102014207507B4|2014-04-17|2021-12-16|Kennametal Inc.|Cutting tool and method for producing a cutting tool|
    EP3006138A1|2014-10-09|2016-04-13|Linde Aktiengesellschaft|Method for layered production of a metallic workpiece by means of laser assisted additive manufacturing|
    US9643282B2|2014-10-17|2017-05-09|Kennametal Inc.|Micro end mill and method of manufacturing same|
    JP6804298B2|2014-11-14|2020-12-23|株式会社ニコン|Modeling equipment|
    CN111054920A|2014-11-14|2020-04-24|株式会社尼康|Molding device and molding method|
    US10279578B2|2016-06-21|2019-05-07|Washington State University|Additive manufacturing of composite materials with composition gradient|
    DE102016222210A1|2016-11-11|2018-05-17|Siemens Aktiengesellschaft|Process for additive production with designation of a construction platform by reference points|
    US10253417B2|2017-01-30|2019-04-09|United Technologies Corporation|System and method for applying abrasive grit|
    US11154956B2|2017-02-22|2021-10-26|General Electric Company|Method of repairing turbine component using ultra-thin plate|
    WO2019183574A1|2018-03-23|2019-09-26|Lawrence Livermore National Security, Llc|Additive manufacturing|
    US20190388968A1|2018-06-22|2019-12-26|Lincoln Global, Inc.|Flexible hybrid additive manufacturing for specified alloy creation|
    CN109536943B|2018-11-02|2020-07-14|昆明理工大学|Laser cladding coating powder and preparation method thereof|
    法律状态:
    2006-07-07| FPAY| Fee payment|Year of fee payment: 4 |
    2010-08-24| FPAY| Fee payment|Year of fee payment: 8 |
    2014-10-03| REMI| Maintenance fee reminder mailed|
    2015-02-25| LAPS| Lapse for failure to pay maintenance fees|
    2015-03-23| STCH| Information on status: patent discontinuation|Free format text: PATENT EXPIRED DUE TO NONPAYMENT OF MAINTENANCE FEES UNDER 37 CFR 1.362 |
    2015-04-14| FP| Expired due to failure to pay maintenance fee|Effective date: 20150225 |
    优先权:
    申请号 | 申请日 | 专利标题
    US7125298P| true| 1998-01-12|1998-01-12||
    US09/221,553|US6203861B1|1998-01-12|1998-12-28|One-step rapid manufacturing of metal and composite parts|
    US09/731,993|US6526327B2|1998-01-12|2000-12-07|One-step rapid manufacturing of metal and composite parts|US09/731,993| US6526327B2|1998-01-12|2000-12-07|One-step rapid manufacturing of metal and composite parts|