    • 专利摘要:
    Single-wall carbon nanotubes are produced from carbon vapor in the presence of nickel-cobalt catalyst vapor, and the carbon vapor and the nickel-cobalt catalyst vapor are constantly generated from a carbon pellet and a nickel-cobalt pellet under radiation of YAG laser beams so that the single-wall carbon nanotubes are constant in diameter.
    公开号:US20010001654A1
    申请号:US09/177,790
    申请日:1998-10-23
    公开日:2001-05-24
    发明作者:Masako Yudasaka；Sumio Iijima
    申请人:NEC Corp；
    IPC主号:B82Y30-00
    专利说明:
    [0001] This invention relates to a carbon nanotube and, more particularly, to a process for producing a carbon nanotube and a laser ablation apparatus used therein. [0001] DESCRIPTION OF THE RELATED ART
    [0002] A typical example of the process for producing carbon nanotubes is disclosed by Andreas Thess et al in “Crystalline Ropes of Metallic Carbon Nanotubes”, Science, vol. 273, pages 483 to 487, Jul. 26, 1996. Metal catalyst particle such as nickel-cobalt alloy is mixed with graphite powder at a predetermined percentage, and the mixture is pressed so as to obtain a pellet. A laser beam is radiated to the pellet. The laser beam evaporates the carbon and the nickel-cobalt alloy, and the carbon vapor is condensed in the presence of the metal catalyst. Single-wall carbon nanotubes are found in the condensation. A problem is encountered in the prior art process in that the single-wall carbon nanotubes are not constant in diameter. [0002] SUMMARY OF THE INVENTION
    [0003] It is therefore an important object of the present invention to provide a process for producing single-wall carbon nanotubes, which is uniform in diameter. [0003]
    [0004] The present inventors contemplated the problem inherent in the prior art process, and noticed that the ratio between the carbon vapor and the metal catalyst vapor was varied with time due to absorption of the laser light. The graphite powder was black, and took up the laser light rather than the metal catalyst. The laser light thus absorbed raised the temperature rapidly rather than the metal catalyst, and the metal catalyst was left in the surface portion. The metal catalyst layer reflected the laser light, and the graphite powder was less sublimated. This resulted in that the purity of carbon was not uniform. For this reason, the carbon nanotubes did not become constant in diameter. [0004]
    [0005] To accomplish the object, the present invention proposes to independently evaporate carbon and metal catalyst. [0005]
    [0006] In accordance with one aspect of the present invention, there is provided a process for producing carbon nanotubes comprising the steps of preparing a source of carbon vapor and a source of catalyst vapor physically separated from each other, radiating laser beams to the source of carbon vapor and the source of catalyst vapor so as to generate a carbon vapor/ cluster and a catalyst vapor/cluster, and allowing the carbon vapor/cluster to be mixed with the catalyst vapor/cluster so as to form the carbon vapor/cluster into carbon nanotubes. [0006]
    [0007] In accordance with another aspect of the present invention, there is provided a laser ablation system for producing carbon nanotubes comprising a reactor having an air-tight chamber where a source of carbon vapor and a source of catalyst vapor are separately provided, a laser beam generator provided for the reactor and radiating laser beams to the source of carbon vapor and the source of catalyst vapor for producing a carbon vapor/cluster and a catalyst vapor/cluster from the source of carbon vapor and the source of catalyst vapor, respectively, an evacuating sub-system connected to the reactor for evacuating a gaseous mixture from the air-tight chamber, a carrier gas supply sub-system connected to the reactor supplying carrier gas to the air-tight chamber for forming a carrier gas flow in the air-tight chamber, and a collector provided in the carrier gas flow and capturing carbon nanotubes formed from the carbon vapor/cluster in the presence of the catalyst vapor/cluster and carried on the carrier gas flow. [0007] BRIEF DESCRIPTION OF THE DRAWINGS
    [0008] The features and advantages of the process and the laser ablation apparatus will be more clearly understood from the following description taken in conjunction with the accompanying drawings in which: [0008]
    [0009] FIGS. 1A to [0009] 1C are schematic views showing a process for producing carbon nanotubes according to the present invention; and
    [0010] FIG. 2 is a schematic view showing a carbon pellet and metal catalyst pellet independently radiated with laser beams. [0010] DESCRIPTION OF THE PREFERRED EMBODIMENT
    [0011] FIGS. 1A to [0011] 1C illustrate a process for producing carbon nanotubes embodying the present invention. The process starts with preparation of a carbon pellet 1, a metal catalyst pellet 2 and a laser ablation system 3. The carbon pellet 1, the metal catalyst pellet 2 and the laser ablation system 3 are detailed hereinbelow with reference to FIG. 1A.
    [0012] The carbon pellet is formed from graphite. The graphite consists of carbon, and is shaped into the carbon pellet by using a standard pelleting machine. The carbon pellet [0012] 1 has a plate-like configuration, and is 10 millimeters long and 3 to 5 millimeters wide.
    [0013] The metal catalyst pellet [0013] 2 is formed of nickel-cobalt alloy. The nickel and the cobalt are regulated to the atomic ratio of 1:1. Nickel, cobalt, platinum, palladium and alloys thereof are available for the metal catalyst. The alloy contains at least two elements selected from nickel, cobalt, platinum and palladium. The metal catalyst is also shaped into a plate-like configuration by suing the pelleting machine, and is equal in dimensions to the carbon pellet 1.
    [0014] The laser ablation system [0014] 3 includes a reactor 3 a, an evacuating sub-system 3 b, an inert gas supply sub-system 3 c, a laser beam generator 3 d, a heater 3 e, a collector 3 f, a spacer 3 g (see FIGS. 1B and 1C) and a controller 3 h. The evacuating sub-system 3 b and the inert gas supply sub-system 3 c create vacuum in the reactor, and cause inert gas to flow through the reactor 1 as indicated by arrows AR1. The heater 3 e maintains the inside of the reactor 3 a at a predetermined temperature range. The carbon pellet 1 and the metal catalyst pellet 2 are separately provided inside the reactor, and the spacer 3 g of quartz plate is provided between the carbon pellet 1 and the metal catalyst pellet 2. The spacer 3 g is 0.3 millimeter thick. The laser beam generator 3 d radiates laser beams 3 r/ 3 s to the carbon pellet 1 and the metal catalyst pellet 2, respectively. Carbon vapor and catalyst vapor are generated from the carbon pellet 1 and the metal catalyst pellet 2, respectively, and condensate is captured by the collector 3 f. The process sequence is controlled by the controller 3 h.
    [0015] The reactor [0015] 3 a is formed of quartz or ceramic, and has a cylindrical configuration. Any material is available for the reactor 3 a in so far as it is hardly eroded in the ambience created in the reactor 3 a. Although the reactor 3 a is not limited to the cylindrical configuration, the cylindrical configuration is desirable.
    [0016] The evacuating sub-system [0016] 3 b includes a rotary vacuum pump 3 i, a pipe 3 j connected between the reactor 3 a and the rotary vacuum pump 3 i and an electromagnetic flow control valve 3 k inserted into the pipe 3 j. On the other hand, the inert gas supply sub-system 3 c includes a reservoir tank 3 m for inert gas such as, for example, argon gas, a pipe connected between the reservoir tank 3 m and the reactor 3 a and an electromagnetic flow control valve 3 o inserted into the pipe 3 n. The electromagnetic flow control valve 3 o supplies the argon gas to the inlet nozzle 3 p at 0.2 to 0.5 litter per minute, and the argon gas is blown off into the reactor 3 a. The rotary vacuum pump 3 i evacuates the argon gas, and the electromagnetic flow control valve 3 k maintains the argon gas in the reactor 3 a at 500 torr to 600 torr.
    [0017] The laser beam generator [0017] 3 d generates laser light, and radiates laser beams 3 r/ 3 s to the carbon pellet 1 and the metal catalyst pellet 2, respectively. The laser beam generator 3 d includes a laser light emitting element formed of Nd contained single crystalline YAG (Yttrium Aluminum Garnet), and the laser light emitting element radiates laser light pulses 3 r/ 3 s. The laser light has 532 nanometer wavelength, and oscillates at 10 Hz. The pulse width ranges from 7 nanoseconds to 10 nanoseconds, and the power is regulated to 1.2 to 9.2 J/pulse. The laser beams 3 r/ 3 s has cross section of 0.2 cm2.
    [0018] The heater [0018] 3 e heats the reactor 3 a, and the controller 3 h maintains the inside of the reactor 3 a around 1200 degrees in centigrade. The heater 3 e may be implemented by an oven.
    [0019] When the carbon pellet [0019] 1, the metal catalyst pellet 2 and the laser ablation system 3 are prepared, an operator inserts the carbon pellet 1 and the metal catalyst pellet 2 into the reactor 3 a. The carbon pellet 1 and the metal catalyst pellet 2 symmetrically decline with respect to the center line of the reactor 3 a, and the major surface of the carbon pellet 1 is opposed through the spacer 3 g to the concave surface of the metal catalyst pellet 2 as shown in FIG. 2.
    [0020] The reactor [0020] 3 a is closed, and the rotary vacuum pump 3 i evacuates the air from the reactor 3 a. When the vacuum is developed in the reactor 3 a, the inert gas supply system 3 c supplies the argon gas at 0.5 litter/minute. The evacuating sub-system 3 b cooperates with the inert gas supply system 3 c, and maintain the inside of the reactor 3 a at 600 mmHg. The argon gas flows from the nozzle 3 p toward the collector 3 f.
    [0021] Subsequently, the laser beam generator [0021] 3 d radiates the laser beams 3 r/ 3 s to the carbon pellet 1 and the metal catalyst pellet 2. In this instance, the pulse width and the power are adjusted to 10 nanosecond and 50 mJ/pulse cm2. The laser beams 3 r/ 3 s directly heat the carbon pellet 1 and the metal catalyst pellet 2, and carbon vapor/cluster 4 and nickel-cobalt vapor/cluster 5 are constantly generated from the carbon pellet 1 and the metal catalyst pellet 2, respectively, as shown in FIG. 1B.
    [0022] The argon gas carries the carbon vapor/cluster [0022] 4 and the nickel-cobalt vapor/cluster 5 toward the collector 3 f. The carbon vapor/cluster 4 are mixed with the nickel-cobalt vapor/cluster 5, and forms into single-wall carbon nanotubes 6. The single-wall carbon nanotubes 6 are carried toward the collector 3 f, and are captured by the collector 3 f as shown in FIG. 1C. The carbon vapor/cluster 4 and the nickel-cobalt vapor/cluster 5 are constant in mass, and keeps the content of carbon in the condensate or the single-wall carbon nanotubes 6 constant. This results in the constant diameter of the single-wall carbon nanotubes 6.
    [0023] As will be appreciated from the foregoing description, the carbon pellet [0023] 1 and the metal catalyst pellet 2 are used in the process according to the present invention, and make the single-wall carbon nanotubes constant in diameter.
    [0024] Although particular embodiments of the present invention have been shown and described, it will be apparent to those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the present invention. [0024]
    [0025] It is required for the process according to the present invention to separately vaporize the carbon and the metal catalyst. However, this requirement does not means the carbon and the metal catalyst respectively formed into pellets. The carbon and the metal catalyst may be in the form of powder. [0025]
    [0026] The carbon pellet and the metal catalyst pellet may have a semi-column configuration. [0026]
    权利要求:
    Claims (16)
    [1" id="US-20010001654-A1-CLM-00001] 1. A process for producing carbon nanotubes, comprising the steps of:
    a) preparing a source of carbon vapor and a source of catalyst vapor physically separated from each other;
    b) radiating laser beams to said source of carbon vapor and said source of catalyst vapor so as to generate a carbon vapor/cluster and a catalyst vapor/cluster;
    c) allowing said carbon vapor/cluster to be mixed with said catalyst vapor/cluster so as to form said carbon vapor/cluster into carbon nanotubes.
    [2" id="US-20010001654-A1-CLM-00002] 2. The process as set forth in
    claim 1 , in which said source of carbon vapor and said source of catalyst vapor are provided as a carbon pellet and a catalyst pellet, respectively.
    [3" id="US-20010001654-A1-CLM-00003] 3. The process as set forth in
    claim 2 , in which said carbon pellet is formed of graphite, and said catalyst pellet is formed of material selected from the group consisting of nickel, cobalt, platinum, palladium and alloys containing at least two of said nickel, said cobalt, said platinum and said palladium.
    [4" id="US-20010001654-A1-CLM-00004] 4. The process as set forth in
    claim 2 , in which a spacer is provided between said carbon pellet and said catalyst pellet.
    [5" id="US-20010001654-A1-CLM-00005] 5. The process as set forth in
    claim 1 , in which a YAG laser forms said laser beams.
    [6" id="US-20010001654-A1-CLM-00006] 6. The process as set forth in
    claim 5 , in which said YAG laser forms laser pulse trains for said laser beams, respectively, and said laser pulse trains have a wavelength of 532 nanometers, a frequency of 10 Hz, a pulse width of 7 to 10 nanoseconds and a power of 1.2 to 9.1 J/pulse.
    [7" id="US-20010001654-A1-CLM-00007] 7. The process as set forth in
    claim 1 , in which a carrier gas flows through said source of carbon vapor and said source of catalyst vapor so as to mix said carbon vapor/cluster with said catalyst vapor/cluster in said step c).
    [8" id="US-20010001654-A1-CLM-00008] 8. The process as set forth in
    claim 7 , in which said carrier gas is an inert gas, and said inert gas flows at 0.2 to 0.5 litter per minute at 500 to 600 torr.
    [9" id="US-20010001654-A1-CLM-00009] 9. The process as set forth in
    claim 1 , in which said carbon vapor/cluster is formed into said carbon nanotubes at 1200 degrees in centigrade.
    [10" id="US-20010001654-A1-CLM-00010] 10. A laser ablation system for producing carbon nanotubes, comprising:
    a reactor having an air-tight chamber where a source of carbon vapor and a source of catalyst vapor are separately provided;
    a laser beam generator provided for said reactor and radiating laser beams to said source of carbon vapor and said source of catalyst vapor for producing a carbon vapor/cluster and a catalyst vapor/cluster from said source of carbon vapor and said source of catalyst vapor, respectively;
    an evacuating sub-system connected to said reactor for evacuating a gaseous mixture from said air-tight chamber;
    a carrier gas supply sub-system connected to said reactor supplying carrier gas to said air-tight chamber for forming a carrier gas flow in said air-tight chamber; and
    a collector provided in said carrier gas flow and capturing carbon nanotubes formed from said carbon vapor/cluster in the presence of said catalyst vapor/cluster and carried on said carrier gas flow.
    [11" id="US-20010001654-A1-CLM-00011] 11. The laser ablation system as set forth in
    claim 10 , in which said reactor is formed of a material selected from the group consisting of quartz and ceramics.
    [12" id="US-20010001654-A1-CLM-00012] 12. The laser ablation system as set forth in
    claim 10 , in which said laser beam generator produces laser pulse trains from a YAG laser for said laser beams, and the laser pulse trains have a wavelength of 532 nanometers, a frequency of 10 Hz, a pulse width of 7 to 10 nanoseconds and a power of 1.2 to 9.1 J/pulse.
    [13" id="US-20010001654-A1-CLM-00013] 13. The laser ablation system as set forth in
    claim 12 , further comprising a heater for heating said air-tight chamber to at least 1200 degrees in centigrade.
    [14" id="US-20010001654-A1-CLM-00014] 14. The laser ablation system as set forth in
    claim 10 , in which a carbon pellet and a catalyst pellet serve as said source of carbon vapor and said source of catalyst vapor, respectively.
    [15" id="US-20010001654-A1-CLM-00015] 15. The laser ablation system as set forth in
    claim 14 , in which said catalyst pellet is formed of a material selected from the group consisting of nickel, cobalt, platinum, palladium and alloys containing at least two metals of said nickel, said cobalt, said platinum and said palladium.
    [16" id="US-20010001654-A1-CLM-00016] 16. The laser ablation system as set forth in
    claim 10 , in which said carrier gas supply system includes a source of inert gas, and said evacuating sub-system and said carrier gas supply system cooperate with each other so as to flow an inert gas at 0.2 to 0.5 litter per minute at 500 to 600 torr in said air-tight chamber.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6331690B1|2001-12-18|Process for producing single-wall carbon nanotubes uniform in diameter and laser ablation apparatus used therein
    US6689192B1|2004-02-10|Method for producing metallic nanoparticles
    US4619691A|1986-10-28|Method of manufacturing ultra-fine particles
    TW200307759A|2003-12-16|Copper and/or zinc alloy nanopowders made by laser vaporization and condensation
    US20030141179A1|2003-07-31|Method for manufacturing carbon nanotubes
    US4409511A|1983-10-11|Phase transition cooled window for broad beam electron gun
    KR20010016692A|2001-03-05|Method for manufacturing fine spherical particles by controlling particle coalescence using laser beam heating
    JP2001089117A|2001-04-03|Method for producing carbon nano-tube and laser target
    Chen et al.2001|Low–power plasma torch method for the production of crystalline spherical ceramic particles
    JP3423639B2|2003-07-07|Method and apparatus for producing carbon nanotube
    JP2005126257A|2005-05-19|Method for manufacturing carbon nanotube
    JP2005053720A|2005-03-03|Method for producing carbon nanotube
    CN1128098C|2003-11-19|Process for preparing nm-class single-wall carbon tubes by high-power continuous CO2 laser
    JPH0680410A|1994-03-22|Apparatus for producing carbon soot
    JP6860834B2|2021-04-21|Manufacturing members and equipment for carbon nanohorn assemblies
    JP2505375B2|1996-06-05|Method and apparatus for forming compound film
    US20210229999A1|2021-07-29|Continuous production method of fibrous carbon nanohorn aggregate
    JP2505376B2|1996-06-05|Film forming method and apparatus
    Ristić et al.2012|Diamond synthesis by lasers: recent progress
    JP6841333B2|2021-03-10|Manufacturing equipment for carbon nanohorn aggregates
    JPH11263610A|1999-09-28|Production of carbon nanotube
    KR100360281B1|2002-11-09|Apparatus of vapor phase-synthesis for diamond and synthesizing method using the same
    JPWO2020158665A1|2021-12-02|Parts and manufacturing method for continuous manufacturing of carbon nanobrushes
    JP2004526652A|2004-09-02|Method for producing shell-shaped carbon fine particles
    JP2021147309A|2021-09-27|Method and device for producing boron nitride nanotubes
    同族专利:
    公开号 | 公开日
    US6331690B1|2001-12-18|
    JPH11180707A|1999-07-06|
    JP3077655B2|2000-08-14|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US6422450B1|1999-03-01|2002-07-23|University Of North Carolina, The Chapel|Nanotube-based high energy material and method|
    US20040247515A1|2003-06-05|2004-12-09|Lockheed Martin Corporation|Pure carbon isotropic alloy of allotropic forms of carbon including single-walled carbon nanotubes and diamond-like carbon|
    US20060237301A1|2003-08-08|2006-10-26|Takeshi Azami|Apparatus for producing nanocarbon, method for producing nanocarbon and method for collecting nanocarbon|US5126200A|1986-08-18|1992-06-30|E. I. Du Pont De Nemours And Company|Laser assisted fiber growth|
    LU87880A1|1991-01-24|1992-10-15|Europ Communities|METHOD FOR DEPOSITING A THIN FILM BY PHOTO-ABLATION|
    US5300203A|1991-11-27|1994-04-05|William Marsh Rice University|Process for making fullerenes by the laser evaporation of carbon|
    US5591312A|1992-10-09|1997-01-07|William Marsh Rice University|Process for making fullerene fibers|
    US5424054A|1993-05-21|1995-06-13|International Business Machines Corporation|Carbon fibers and method for their production|
    US5547748A|1994-01-14|1996-08-20|Sri International|Carbon nanoencapsulates|
    US5406906A|1994-01-18|1995-04-18|Ford Motor Company|Preparation of crystallographically aligned films of silicon carbide by laser deposition of carbon onto silicon|
    US6183714B1|1995-09-08|2001-02-06|Rice University|Method of making ropes of single-wall carbon nanotubes|
    US5993697A|1996-05-14|1999-11-30|The Regents Of The University Of California|Metallic carbon materials|
    US6221330B1|1997-08-04|2001-04-24|Hyperion Catalysis International Inc.|Process for producing single wall nanotubes using unsupported metal catalysts|
    US6045769A|1997-12-08|2000-04-04|Nanogram Corporation|Process for carbon production|
    US6156256A|1998-05-13|2000-12-05|Applied Sciences, Inc.|Plasma catalysis of carbon nanofibers|
    US6203864B1|1998-06-08|2001-03-20|Nec Corporation|Method of forming a heterojunction of a carbon nanotube and a different material, method of working a filament of a nanotube|
    US6139919A|1999-06-16|2000-10-31|University Of Kentucky Research Foundation|Metallic nanoscale fibers from stable iodine-doped carbon nanotubes|
    CN1128098C|2000-05-23|2003-11-19|广东工业大学|Process for preparing nm-class single-wall carbon tubes by high-power continuous CO2 laser|EP1068149A4|1998-03-24|2009-10-21|Silverbrook Res Pty Ltd|Method for construction of nanotube matrix material|
    JP3422302B2|1999-09-22|2003-06-30|日本電気株式会社|Method for producing carbon nanotube and laser target|
    US6495116B1|2000-04-10|2002-12-17|Lockheed Martin Corporation|Net shape manufacturing using carbon nanotubes|
    JP3639808B2|2000-09-01|2005-04-20|キヤノン株式会社|Electron emitting device, electron source, image forming apparatus, and method of manufacturing electron emitting device|
    JP3658346B2|2000-09-01|2005-06-08|キヤノン株式会社|Electron emitting device, electron source and image forming apparatus, and method for manufacturing electron emitting device|
    JP3610325B2|2000-09-01|2005-01-12|キヤノン株式会社|Electron emitting device, electron source, and method of manufacturing image forming apparatus|
    JP3639809B2|2000-09-01|2005-04-20|キヤノン株式会社|ELECTRON EMITTING ELEMENT, ELECTRON EMITTING DEVICE, LIGHT EMITTING DEVICE, AND IMAGE DISPLAY DEVICE|
    JP3634781B2|2000-09-22|2005-03-30|キヤノン株式会社|Electron emission device, electron source, image forming device, and television broadcast display device|
    KR100684823B1|2000-11-23|2007-02-20|삼성에스디아이 주식회사|The method for growing carbonnanotube for field emitter of Field Emission Display|
    JP3897794B2|2001-03-27|2007-03-28|キヤノン株式会社|Method for manufacturing electron-emitting device, electron source, and image forming apparatus|
    JP3768908B2|2001-03-27|2006-04-19|キヤノン株式会社|Electron emitting device, electron source, image forming apparatus|
    CN100454471C|2001-03-27|2009-01-21|佳能株式会社|Catalyst used to form carbon fiber, method of making the same and electronic transmitting device|
    JP3703415B2|2001-09-07|2005-10-05|キヤノン株式会社|ELECTRON EMITTING ELEMENT, ELECTRON SOURCE, IMAGE FORMING APPARATUS, AND METHOD FOR MANUFACTURING ELECTRON EMITTING ELEMENT AND ELECTRON SOURCE|
    JP3605105B2|2001-09-10|2004-12-22|キヤノン株式会社|Electron emitting element, electron source, light emitting device, image forming apparatus, and method of manufacturing each substrate|
    JP3710436B2|2001-09-10|2005-10-26|キヤノン株式会社|Electron emitting device, electron source, and manufacturing method of image display device|
    US6645628B2|2001-11-13|2003-11-11|The United States Of America As Represented By The Secretary Of The Air Force|Carbon nanotube coated anode|
    US6774333B2|2002-03-26|2004-08-10|Intel Corporation|Method and system for optically sorting and/or manipulating carbon nanotubes|
    CA2385802C|2002-05-09|2008-09-02|Institut National De La Recherche Scientifique|Method and apparatus for producing single-wall carbon nanotubes|
    KR20030013351A|2002-10-18|2003-02-14|이영희|Carbon Nanotube synthesis method using Local Heating Pyrolysis|
    JP4514130B2|2002-12-20|2010-07-28|株式会社アルネアラボラトリ|Optical pulse laser|
    ES2223290B1|2003-08-01|2006-04-16|Universidade De Vigo|METHOD FOR THE PRODUCTION OF NANOHILOS IN ENVIRONMENTAL CONDITIONS.|
    US8075863B2|2004-05-26|2011-12-13|Massachusetts Institute Of Technology|Methods and devices for growth and/or assembly of nanostructures|
    JPWO2006073099A1|2005-01-06|2008-06-12|日本電気株式会社|Method for producing carbon-based material|
    CA2500766A1|2005-03-14|2006-09-14|National Research Council Of Canada|Method and apparatus for the continuous production and functionalization of single-walled carbon nanotubes using a high frequency induction plasma torch|
    CN100418876C|2005-08-19|2008-09-17|清华大学|Device and method for preparing array of Nano carbon tube|
    FI120450B|2007-03-21|2009-10-30|Beneq Oy|Apparatus for producing nanotubes|
    US8449858B2|2009-06-10|2013-05-28|Carbon Solutions, Inc.|Continuous extraction technique for the purification of carbon nanomaterials|
    US8454923B2|2009-06-10|2013-06-04|Carbon Solutions, Inc.|Continuous extraction technique for the purification of carbon nanomaterials|
    BR112012002233A2|2009-07-31|2019-09-24|Massachustts Institute Of Tech|systems and methods related to the formation of carbon based nanostructures.|
    US8524139B2|2009-08-10|2013-09-03|FEI Compay|Gas-assisted laser ablation|
    WO2011066288A2|2009-11-25|2011-06-03|Massachusetts Institute Of Technology|Systems and methods for enhancing growth of carbon-based nanostructures|
    WO2012091789A1|2010-10-28|2012-07-05|Massachusetts Institute Of Technology|Carbon-based nanostructure formation using large scale active growth structures|
    JP6373284B2|2013-02-28|2018-08-15|エヌ１２ テクノロジーズ， インク．Ｎ１２ Ｔｅｃｈｎｏｌｏｇｉｅｓ， Ｉｎｃ．|Nano-structured film cartridge-based dispensing|
    CN104294407A|2014-10-15|2015-01-21|北京化工大学|Shaft core focused carbon fiber graphitization furnace through laser tunnel reflection method|
    法律状态:
    1998-10-23| AS| Assignment|Owner name: NEC CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YUDASAKA, MASAKO;IIJIMA, SUMIO;REEL/FRAME:009551/0831 Effective date: 19981005 |
    2002-04-03| STCB| Information on status: application discontinuation|Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |
    优先权:
    申请号 | 申请日 | 专利标题
    JP9-352833||1997-12-22||
    JP09352833A|JP3077655B2|1997-12-22|1997-12-22|Apparatus and method for producing carbon nanotube|US09/562,959| US6331690B1|1997-12-22|2000-05-03|Process for producing single-wall carbon nanotubes uniform in diameter and laser ablation apparatus used therein|
    [返回顶部]