    • 专利摘要:
    Methods of forming face plate assemblies are described. In one implementation, a substrate is patterned with photoresist and a first phosphor-comprising material is formed over first surface areas of the substrate. The photoresist is stripped leaving some of the first phosphor-comprising material over substrate areas other than the first areas. Photoresist is again formed over the substrate and processed to expose second substrate areas which are different from the first substrate areas. In a preferred aspect, processing the photoresist comprises using a heated aqueous developing solution comprising an acid, e.g. lactic acid, effective to dislodge and remove first phosphor-comprising material from beneath the developed photoresist. A second phosphor-comprising material is formed over the substrate and the exposed second areas, with trace deposits being left over other substrate areas. The photoresist is subsequently stripped leaving some of the second phosphor-comprising material over substrate areas other than the first and second areas. Photoresist is again formed over the substrate and processed to expose third substrate areas which are different from the first and second areas. In a preferred aspect, processing the photoresist comprises using a heated aqueous developing solution comprising an acid, e.g. lactic acid, effective to dislodge and remove first and second phosphor-comprising material from beneath the removed photoresist. A third phosphor-comprising material is formed over the substrate and the exposed third areas.
    公开号:US20010001193A1
    申请号:US09/760,191
    申请日:2001-01-12
    公开日:2001-05-17
    发明作者:Jefferson Nemelka
    申请人:Nemelka Jefferson O.；
    IPC主号:C23C26-00
    专利说明:
    [2] 2. The present invention relates to methods of forming a face plate assembly of a color display. BACKGROUND OF THE INVENTION
    [3] 3. Field emission displays and cathode ray tubes are types of color displays which can function by having a layer of phosphor-comprising material applied on an internal surface of a face plate known as an anode, cathodeluminescent screen, display screen, or display electrode. Color displays typically include three different types of phosphor, namely red, green, and blue (RGB), which, when excited in various combinations, produce colors for presentation through the face plate of the display. The phosphor-comprising material is typically oriented or arranged in a series of pixels. Pixels are typically discrete areas of phosphor-comprising material formed on the internal surface of the face plate.
    [4] 4. A technique by which such areas are provided on a face plate involves the use of photolithographic techniques to pattern the phosphor-comprising material. Typically, a faceplate will be coated with a thin layer of conductive material, generally Indium Tin Oxide (ITO). This conductive layer of material is coated with a layer of photoresist, which in turn, is used to pattern phosphor-comprising material into a color array of pixels. It may also serve for patterning black matrix material into a pixel pattern. Black matrix material is used in order to give greater contrast in color displays. Pixels, or holes, will be opened up in the photoresist using photolithographic techniques, thereby exposing distinct regions of the conductive material. The photolithographic techniques used to open the pixels or holes in the photoresist typically involve the use of developer solutions. For negative resists, developer solutions selectively dissolve and remove regions of the photoresist that have not been exposed to radiation actinic to the photoresist used. The black matrix and phosphor-comprising materials can then be electrophoretically deposited into the holes opened in the photoresist. The conductive layer is used as an electrode for depositing phosphor-comprising materials through electrophoresis. Electrophoresis, or electrophoretic deposition, in simply the migration of charged particles through a solution under the influence of an applied electric field applied by immersing two electrodes in the solution. Exemplary methods of depositing black matrix material and phosphor-comprising material are described in U.S. Pat. No. 4,891,110, the disclosure of which is incorporated by reference. Exemplary color displays are described in U.S. Pat. Nos. 5,712,534, 5,705,079, 5,697,825 and 5,688,438, the disclosures of which are incorporated by reference.
    [5] 5. Photolithographic color patterning of a display typically involves the use of incident radiation, photomasks, and wet-chemical developers to selectively expose various pixels for deposition of black matrix material and different colors of phosphor-comprising material therein. Despite the use of these developers, electrophoretic deposition of powdered materials such as manganese carbonate and phosphor-comprising material can result in trace deposits undesirably remaining over adjacent areas or pixels. Such trace deposits can result in black spots and color cross-contamination with undesired color phosphor remaining in adjacent pixels dedicated to other colors, thus leading to color bleed and a less desirable display.
    [6] 6. This invention arose out of concerns associated with improving the methods by which phosphor-comprising material is formed over face plates of color displays. This invention also arose out of concerns associated with providing improved color displays. SUMMARY OF THE INVENTION
    [7] 7. Methods of forming face plate assemblies are described. In one implementation, a substrate is patterned with photoresist and a first phosphor-comprising material is formed over first surface areas of the substrate. The photoresist is stripped leaving some of the first phosphor-comprising material over substrate areas other than the first areas. Photoresist is again formed over the substrate and processed to expose second substrate areas which are different from the first substrate areas. In a preferred aspect, processing the photoresist comprises using a heated aqueous developing solution comprising an acid, e.g. lactic acid, effective to dislodge and remove first phosphor-comprising material from beneath the developed photoresist. A second phosphor-comprising material is formed over the substrate and the exposed second areas, with trace deposits being left over other substrate areas. The photoresist is subsequently stripped leaving some of the second phosphor-comprising material over substrate areas other than the first and second areas. Photoresist is again formed over the substrate and processed to expose third substrate areas which are different from the first and second areas. In a preferred aspect, processing the photoresist comprises using a heated aqueous developing solution comprising an acid, e.g. lactic acid, effective to dislodge and remove first and second phosphor-comprising material from beneath the removed photoresist. A third phosphor-comprising material is formed over the substrate and the exposed third areas. BRIEF DESCRIPTION OF THE DRAWINGS
    [8] 8. Preferred embodiments of the invention are described below with reference to the following accompanying drawings.
    [9] 9.FIG. 1 is a diagrammatic sectional view of a substrate comprising a portion of a face plate assembly of a color display.
    [10] 10.FIG. 2 is a view of the FIG. 1 substrate at a different processing step.
    [11] 11.FIG. 3 is a view of the FIG. 2 substrate at a different processing step.
    [12] 12.FIG. 4 is an enlarged view of the FIG. 3 substrate at a different processing step.
    [13] 13.FIG. 5 is a view of the FIG. 4 substrate at a different processing step.
    [14] 14.FIG. 6 is a view of the FIG. 5 substrate at a different processing step.
    [15] 15.FIG. 7 is a view of the FIG. 6 substrate at a different processing step.
    [16] 16.FIG. 8 is a view of the FIG. 7 substrate at a different processing step.
    [17] 17.FIG. 9 is a view of the FIG. 8 substrate at a different processing step.
    [18] 18.FIG. 10 is a view of the FIG. 9 substrate at a different processing step.
    [19] 19.FIG. 11 is a view of the FIG. 10 substrate at a different processing step.
    [20] 20.FIG. 12 is a view of the FIG. 11 substrate at a different processing step.
    [21] 21.FIG. 13 is a view of the FIG. 12 substrate at a different processing step.
    [22] 22.FIG. 14 is a view of the FIG. 13 substrate at a different processing step.
    [23] 23.FIG. 15 is a view of the FIG. 14 substrate at a different processing step.
    [24] 24.FIG. 16 is a view of the FIG. 15 substrate at a different processing step.
    [25] 25.FIG. 17 is a view of the FIG. 16 substrate at a different processing step.
    [26] 26.FIG. 18 is a view of the FIG. 17 substrate at a different processing step.
    [27] 27.FIG. 19 is a view of the FIG. 18 substrate at a different processing step. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
    [28] 28. This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (Article 1, Section 8).
    [29] 29. Referring to FIG. 1, a substrate is shown generally at 20 and comprises a portion of a face plate assembly of a color display. Substrate 20 includes an outer surface 22.
    [30] 30. Referring to FIG. 2, a layer 24 is formed over surface 22 and comprises a conductive material such as indium tin oxide.
    [31] 31. Referring to FIG. 3, a layer 25 is formed over substrate 20 and comprises a masking material such as photoresist.
    [32] 32. Referring to FIG. 4, layer 25 is patterned to define a plurality of openings (not specifically designated) over the substrate.
    [33] 33. Referring to FIG. 5, black matrix material 27 is formed over the substrate and within the openings in layer 25.
    [34] 34. Referring to FIG. 6, layer 25 is removed and leaves the deposited black matrix material over the substrate. Such material defines substrate areas over which phosphor-comprising material is to be deposited.
    [35] 35. Referring to FIG. 7, a layer 26 is formed over substrate 20 and comprises a masking material such as photoresist. While positive photoresists can be used, negative photoresists such as polyvinyl alcohol are preferred.
    [36] 36. Referring to FIG. 8, layer 26 is patterned to define a first plurality of openings 28 over first substrate areas 30.
    [37] 37. Referring to FIG. 9, a first phosphor-comprising material 32 is formed over the substrate and within first openings 28 over first substrate areas 30. Phosphor-comprising material 32 is also formed in trace amounts over patterned masking layer 26 and second and third substrate areas 34, 38. Phosphor-comprising material 32 is preferably electrophoretically deposited over first substrate areas 30. Generally, an electrophoretic solution is made up of a nonaqueous liquid, such as isopropyl alcohol, and an electrolyte, such as a salt of magnesium, zinc, aluminum, lanthanum, cerium, or yttrium. The phosphor-comprising material is typically an inorganic material with certain impurities or dopants. Examples of commonly used red, green, and blue phosphor-comprising materials are Y2O3:Eu, Zn2SiO4:Mn, and ZnS:Ag, respectively.
    [38] 38. An exemplary solution used for electrophoretic deposition is as follows: Component Weight PercentIsopropyl Alcohol 99.5 Mg2(NO3)2 0.1 Y2O3:Eu 0.4
    [39] 39. An electrode is ideally immersed in a room temperature solution along with the substrate to be coated. An electric field is applied between two electrodes such that the substrate is at a negative potential relative to the other electrode. Typically, a voltage differential of 200 Volts is applied to the two electrodes for about one minute, during which time the phosphor-comprising material is deposited on the substrate. An exemplary first phosphor-comprising material is Y2O3:Eu.
    [40] 40. Referring to FIG. 10, first patterned masking layer 26 is removed or stripped from over substrate 20 as by plasma gas, wet chemical, or thermal methods which are known. For example, polyvinyl alcohol can be stripped using an aqueous, hydrogen peroxide solution or by baking in air at 400° C. The removal of the masking layer undesirably leaves trace amounts 36 of first phosphor-comprising material 32 over the substrate in areas other than first areas 30, e.g. over second areas 34 and third areas 38. For purposes of the continuing discussion, adjacent substrate areas 30, 38 comprise first portions of the surface of the face plate over which first phosphor-comprising material is deposited. Second substrate area 34 comprises a second portion of the surface over which trace amounts of the first phosphor-comprising material are deposited.
    [41] 41. Referring to FIGS. 11 and 12, a second layer 40 of masking material is formed over substrate 20 and phosphor-comprising material 32, 36. In the illustrated example, second masking layer 40 comprises photoresist, with negative photoresist being preferred. Second portions of layer 40, i.e. those portions of the photoresist which are formed over the second surface portions defined by substrate areas 34, are masked while first portions of the photoresist, i.e. those portions over second areas 30, 38 are exposed to selected light or light processed as indicated by the grouped arrows. After light exposure, the mask is removed. The first and second photoresist portions are accordingly light processed differently.
    [42] 42. Referring to FIG. 13, photoresist from over the second surface portions, e.g. second substrate areas 34, is removed with a developing solution which is effective in dislodging and removing remnant first phosphor-comprising material 36 (FIG. 12) from the substrate beneath the removed photoresist. In the illustrated and preferred embodiment, the removal of the photoresist and remnant first phosphor-comprising material takes place by exposing the substrate to a heated aqueous solution comprising a phosphor-removing material which is sufficient to outwardly expose second areas 34 through photodevelopment. Such aqueous developing solution preferably includes an acid having a concentration of less than about 10% by volume, at a temperature from between about 25° C. to 50° C. Even more preferably, the aqueous solution has a temperature from between about 35° C. to 40° C., and an acid concentration of less than about 1% by volume. A preferred acid is lactic acid, while other acids such as acetic, glycolic, phosphoric, or hydrochloric acids can be utilized. A suitable solution constituent is available from Shipley Company located at 455 Forest Street, Marlborough, Mass., and sold under the trade name “Eagle 2005 Developer” and bearing the product code 15020. The solution constituent includes the following component parts (with volume percentages being indicated parenthetically): water (24-25), lactic acid (22-23), and polyglycol (53-54). The preferred aqueous solution was formed by providing about four percent of the “Eagle 2005 Developer” by volume into about 96 percent water by volume.
    [43] 43. In another embodiment, unexposed regions of photoresist can be treated with a suitable developing solution which is sufficient to remove the photoresist, but not trace material 36 (FIG. 12). Subsequently, to dislodge and remove the trace material over the substrate, the substrate can be further exposed to the heated aqueous solution mentioned above. The presence of an acid, preferably an organic acid, in the solution is believed to destroy the weak bonds that hold the phosphor-comprising material 36 to the substrate, thereby making it possible for the elevated temperature solution to draw the phosphor-comprising material into the bulk of the solution. The use of some inorganic acids, such as hydrochloric acid, can be equally as effective, though its use may be limited due to possible corrosive effects relative to conductive layer 22.
    [44] 44. Other types of photoresists can be used which employ organic-based developers which do not effectively dislodge and remove the trace deposits of the phosphor-comprising material. In these instances, the use of the preferred heated, aqueous solution can effectively dislodge and remove the phosphor-comprising material 36 from the exposed substrate areas.
    [45] 45. Use of the preferred, heated, aqueous solution can effectively remove the phosphor-comprising material 36, thereby leaving behind a clean substrate area 34 for deposition of a second color phosphor-comprising material.
    [46] 46. Developing the photoresist as just described forms a second patterned masking layer over substrate 20 which leaves or defines a second plurality of openings 42 over second substrate areas 34. Use of the preferred solution is effective to substantially, e.g. around 95%, if not completely, remove any remnant first phosphor-comprising material from over second substrate areas 34.
    [47] 47. Referring to FIG. 14, a second phosphor-comprising material 44 is formed over substrate 20 within openings 42 and over second areas 34. Phosphor-comprising material 44 is preferably electrophoretically deposited over second substrate areas 34. Preferred processing conditions for electrophoretically depositing phosphor-comprising material 44 are the same as those used for the first phosphor-comprising material, with an exception being that the phosphor-comprising material is different, for example, ZnSiO4:Mn, green. Trace amounts 46 of phosphor-comprising material 44 can be deposited over masking layer 40.
    [48] 48. Referring to FIG. 15, second masking layer 40 is developed or otherwise stripped from over substrate 20 as described above. Such can undesirably leave remnant second phosphor-comprising material 46 over the substrate including areas other than the second areas, particularly within third substrate areas 38 over remnant first phosphor-comprising material 36 and over areas 30. Trace deposits tend to accumulate over areas 38, where the lower topography creates regions that can trap the material.
    [49] 49. Referring to FIG. 16, a third masking layer 48 is formed over substrate 20 and over third substrate areas 38. Third masking layer 48 preferably comprises photoresist, with negative photoresist being preferred. The photoresist is subsequently light processed (second light processed), which exposes it to radiation actinic to the particular photoresist being used. In the illustrated example, photoresist over the first portion of the substrate surface (e.g., over areas 30, 38) is light processed differently such that photoresist over areas 38 is not exposed.
    [50] 50. Referring to FIG. 17, photoresist from over some of the first portion, e.g. area 38, is removed with a developing solution which is effective to also remove, preferably completely, remnant first and second phosphor-comprising material 36, 46 (FIG. 16) from the substrate beneath the stripped photoresist. Such is accomplished utilizing the preferred, heated aqueous solution described above comprising a phosphor-removing material which is effective to remove both first and second phosphor-comprising materials. Exemplary aqueous solutions can, and preferably do comprise those solutions described above. Removal of material of the third masking layer constitutes forming a third patterned masking layer which leaves or defines a third plurality of openings 50 over third substrate areas 38. It will be appreciated that different individual materials can have their own stripping solution.
    [51] 51. Referring to FIG. 18, a third phosphor-comprising material 52 is formed over substrate 20 within openings 50 and over substrate areas 38. Such material can also be deposited in trace amounts over layer 48. Phosphor-comprising material 52 is preferably electrophoretically deposited over third substrate areas 38. Preferred processing conditions for electrophoretically depositing phosphor-comprising material 52 are the same as those used for the first and second phosphor-comprising materials, with an exception being that the third phosphor-comprising material comprises a different color, e.g. ZnS:Ag, blue.
    [52] 52. Referring to FIG. 19, photoresist 48 is subsequently stripped as described above to provide the color display face plate assembly.
    [53] 53. The above-described processing methodologies can significantly reduce the risk that trace amounts of phosphor-comprising material are deposited over areas other than those specific areas which are intended. Accordingly, displays with better color purity and uniformity are provided.
    [54] 54. In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents.
    权利要求:
    Claims (60)
    [1" id="US-20010001193-A1-CLM-00001] 1. A method of forming a face plate assembly of a color display comprising:
    forming a phosphor-comprising material over a surface of the face plate;
    forming photoresist over the phosphor comprising material; and
    removing photoresist from over portions of the face plate surface with a heated aqueous developing solution effective to also remove phosphor-comprising material from the substrate beneath said removed photoresist during said removing.
    [2" id="US-20010001193-A1-CLM-00002] 2. The method of
    claim 1 , wherein said developing solution comprises an inorganic acid.
    [3" id="US-20010001193-A1-CLM-00003] 3. The method of
    claim 2 , wherein said inorganic acid comprises phosphoric acid.
    [4" id="US-20010001193-A1-CLM-00004] 4. The method of
    claim 2 , wherein said inorganic acid comprises hydrochloric acid.
    [5" id="US-20010001193-A1-CLM-00005] 5. The method of
    claim 1 , wherein said developing solution comprises an organic acid.
    [6" id="US-20010001193-A1-CLM-00006] 6. The method of
    claim 5 , wherein said organic acid comprises lactic acid.
    [7" id="US-20010001193-A1-CLM-00007] 7. The method of
    claim 5 , wherein said organic acid comprises acetic acid.
    [8" id="US-20010001193-A1-CLM-00008] 8. The method of
    claim 5 , wherein said organic acid comprises glycolic acid.
    [9" id="US-20010001193-A1-CLM-00009] 9. The method of
    claim 5 , wherein said developing solution has a concentration of said organic acid of less than about ten percent by volume.
    [10" id="US-20010001193-A1-CLM-00010] 10. The method of
    claim 9 , wherein said developing solution is heated to a temperature from between about 25° C. to 50° C.
    [11" id="US-20010001193-A1-CLM-00011] 11. The method of
    claim 9 , wherein said developing solution is heated to a temperature from between about 35° C. to 40° C.
    [12" id="US-20010001193-A1-CLM-00012] 12. The method of
    claim 5 , wherein said developing solution has a concentration of said organic acid of less than about one percent by volume.
    [13" id="US-20010001193-A1-CLM-00013] 13. The method of
    claim 12 , wherein said organic acid comprises lactic acid.
    [14" id="US-20010001193-A1-CLM-00014] 14. The method of
    claim 1 further comprising:
    after said developing, forming a second phosphor-comprising material over said surface;
    forming photoresist over said face plate surface;
    second developing said photoresist from over different portions of the face plate surface with a developing solution effective to also remove first and second phosphor-comprising material from the substrate beneath said removed photoresist during said second developing; and
    forming a third phosphor-comprising material over said different portions of the face plate surface.
    [15" id="US-20010001193-A1-CLM-00015] 15. The method of
    claim 14 , wherein said developing and said second developing comprise using developing solutions comprising an organic acid.
    [16" id="US-20010001193-A1-CLM-00016] 16. A method of forming a face plate assembly of a color display comprising:
    forming a phosphor-comprising material over a substrate comprising a portion of a face plate assembly of a color display, the material being formed over first substrate areas and second substrate areas; and
    after said forming, exposing the substrate to an aqueous solution comprising phosphor-removing material effective to remove phosphor-comprising material from over said second areas and outwardly expose said second areas.
    [17" id="US-20010001193-A1-CLM-00017] 17. The method of
    claim 16 further comprising:
    prior to said forming of said phosphor-comprising material, forming photoresist over the substrate, said photoresist defining areas within which said phosphor-comprising material is to be formed; and
    prior to said exposing of the substrate to said aqueous solution, removing photoresist from over the substrate with a photoresist developing solution.
    [18" id="US-20010001193-A1-CLM-00018] 18. The method of
    claim 16 , wherein said phosphor-removing material comprises an inorganic acid.
    [19" id="US-20010001193-A1-CLM-00019] 19. The method of
    claim 16 , wherein said phosphor-removing material comprises an organic acid.
    [20" id="US-20010001193-A1-CLM-00020] 20. The method of
    claim 19 , wherein said aqueous solution is heated to a temperature from between about 25° C. to 50° C.
    [21" id="US-20010001193-A1-CLM-00021] 21. The method of
    claim 19 , wherein said aqueous solution comprises less than about ten percent of said organic acid by volume.
    [22" id="US-20010001193-A1-CLM-00022] 22. The method of
    claim 16 , wherein said phosphor-removing material comprises lactic acid.
    [23" id="US-20010001193-A1-CLM-00023] 23. The method of
    claim 22 , wherein said aqueous solution comprises less than about ten percent of said lactic acid by volume.
    [24" id="US-20010001193-A1-CLM-00024] 24. The method of
    claim 16 further comprising:
    after said exposing, forming a second phosphor-comprising material over said second areas;
    exposing said substrate to an aqueous solution comprising a phosphor-removing material effective to remove first and second phosphor-comprising materials from over and outwardly expose third substrate areas which are different from said first and second substrate areas; and
    forming a third phosphor-comprising material over the exposed third substrate areas.
    [25" id="US-20010001193-A1-CLM-00025] 25. A method of forming a face plate assembly of a color display comprising:
    providing a substrate comprising a portion of a face plate assembly of a color display and having a patterned masking layer thereover defining a plurality of openings over first substrate areas;
    forming a phosphor-comprising material over the first substrate areas; and
    after forming the phosphor-comprising material, exposing the substrate to an aqueous solution comprising phosphor-removing material effective to remove phosphor-comprising material from over and outwardly expose second substrate areas which are different from the first substrate areas.
    [26" id="US-20010001193-A1-CLM-00026] 26. The method of
    claim 25 , wherein said aqueous solution is heated to a temperature from between about 25° C. to 50° C.
    [27" id="US-20010001193-A1-CLM-00027] 27. The method of
    claim 25 , wherein said aqueous solution comprises less than about ten percent of an organic acid by volume.
    [28" id="US-20010001193-A1-CLM-00028] 28. The method of
    claim 27 , wherein said organic acid comprises lactic acid.
    [29" id="US-20010001193-A1-CLM-00029] 29. The method of
    claim 25 further comprising prior to exposing said substrate to said aqueous solution, forming a second masking layer over said substrate, wherein said aqueous solution is effective to remove portions of said second masking layer from over said second substrate areas.
    [30" id="US-20010001193-A1-CLM-00030] 30. The method of
    claim 29 , wherein said second masking layer comprises negative photoresist and further comprising prior to said exposing, light processing photoresist other than those portions which are removed from over said second substrate areas.
    [31" id="US-20010001193-A1-CLM-00031] 31. The method of
    claim 29 , wherein said aqueous solution comprises less than about ten percent of an organic acid by volume.
    [32" id="US-20010001193-A1-CLM-00032] 32. The method of
    claim 29 further comprising forming a second phosphor-comprising material over said second substrate areas and thereafter, exposing said substrate to an aqueous solution comprising phosphor-removing material effective to remove second phosphor-comprising material from over and outwardly expose third substrate areas which are different from the second substrate areas.
    [33" id="US-20010001193-A1-CLM-00033] 33. The method of
    claim 32 further comprising:
    prior to exposing said third substrate areas, forming a third masking layer over said substrate;
    wherein said aqueous solution which is effective to remove second phosphor-comprising material is also effective to remove portions of said third masking layer from over said third substrate areas; and
    after said exposing of said third substrate areas, forming a third phosphor-comprising material over said third substrate areas.
    [34" id="US-20010001193-A1-CLM-00034] 34. A method of forming a face plate assembly of a color display comprising:
    forming a matrix material over a surface of a face plate, said matrix material defining a plurality of areas over which phosphor-comprising material is to be formed;
    forming a phosphor-comprising material over the face plate within one of said areas;
    forming photoresist over the matrix material and the phosphor-comprising material;
    exposing selected portions of the photoresist to radiant energy;
    developing unexposed portions of the photoresist with a developing solution effective to remove said unexposed portions from over areas which are different from said one area;
    after said developing, treating said different areas with a heated aqueous solution comprising a phosphor-removing material effective to remove trace deposits of said phosphor-comprising material within said different areas.
    [35" id="US-20010001193-A1-CLM-00035] 35. The method of
    claim 34 , wherein said heated aqueous solution comprises an acid having a concentration less than about ten percent by volume.
    [36" id="US-20010001193-A1-CLM-00036] 36. The method of
    claim 35 , wherein said acid comprises an organic acid.
    [37" id="US-20010001193-A1-CLM-00037] 37. The method of
    claim 35 , wherein said acid comprises an inorganic acid.
    [38" id="US-20010001193-A1-CLM-00038] 38. A method of forming a face plate assembly of a color display comprising:
    electrophoretically depositing a first phosphor-comprising material on first portions of a surface of a face plate, at least some of said first phosphor-comprising material forming on second portions of said surface;
    forming photoresist over the first phosphor-comprising material received on the first and second portions of said surface;
    light processing the photoresist on the first and second portions differently;
    after said light processing, stripping photoresist from over the second portions of the face plate surface with a stripping solution effective to also remove first phosphor-comprising material from the substrate beneath said stripped photoresist during said stripping; and
    after the stripping, electrophoretically depositing a second phosphor comprising material on the second portions of said surface.
    [39" id="US-20010001193-A1-CLM-00039] 39. The method of
    claim 38 , wherein said stripping solution comprises an aqueous solution comprising an organic acid.
    [40" id="US-20010001193-A1-CLM-00040] 40. The method of
    claim 39 , wherein said organic acid comprises lactic acid.
    [41" id="US-20010001193-A1-CLM-00041] 41. The method of
    claim 39 , wherein said organic acid comprises acetic acid.
    [42" id="US-20010001193-A1-CLM-00042] 42. The method of
    claim 39 , wherein said aqueous solution has a concentration of said organic acid of less than about ten percent by volume.
    [43" id="US-20010001193-A1-CLM-00043] 43. The method of
    claim 39 , wherein said aqueous solution has a concentration of said organic acid of less than about one percent by volume.
    [44" id="US-20010001193-A1-CLM-00044] 44. The method of
    claim 39 , further comprising:
    after electrophoretically depositing said second phosphor-comprising material, forming photoresist at least over said first portion of said surface;
    second light processing said photoresist on said first portion differently;
    after said second light processing, second stripping said photoresist from over and outwardly exposing some of said first portion of said surface with a stripping solution effective to also remove first and second phosphor-comprising material from the substrate beneath said stripped photoresist during said second stripping; and
    after said second stripping, electrophoretically depositing a third phosphor-comprising material on said exposed first portion.
    [45" id="US-20010001193-A1-CLM-00045] 45. A method of forming a face plate assembly of a color display comprising:
    forming a first phosphor-comprising material over a surface of the face plate;
    forming negative photoresist over the first phosphor-comprising material;
    masking first portions of the negative photoresist while leaving second portions exposed;
    exposing the second portions to selected light;
    after the exposing, removing the mask;
    after removing the mask, exposing the negative photoresist to a solution comprising aqueous organic acid effective to strip the non-light-exposed photoresist and first phosphor-comprising material therebeneath from over the face plate surface; and
    after stripping the non-light-exposed photoresist and first phosphor-comprising material therebeneath, forming second phosphor-comprising material at least over the surface of the face plate from which the non-light-exposed photoresist and first phosphor-comprising material was stripped.
    [46" id="US-20010001193-A1-CLM-00046] 46. The method of
    claim 45 , wherein said organic acid comprises lactic acid.
    [47" id="US-20010001193-A1-CLM-00047] 47. The method of
    claim 45 , wherein said organic acid comprises lactic acid having a concentration of less than about ten percent by volume.
    [48" id="US-20010001193-A1-CLM-00048] 48. A method of forming a face plate assembly of a color display comprising:
    providing a substrate having a first patterned masking layer defining a first plurality of openings over first substrate areas, the substrate comprising a portion of a face plate assembly of a color display;
    forming a first phosphor-comprising material over the first substrate areas;
    removing the first patterned masking layer;
    forming a second patterned masking layer over the substrate defining a second plurality of openings over second substrate areas which are different from the first substrate areas, said forming of the second patterned masking layer comprising exposing the substrate to a phosphor-removing solution which is effective to remove at least some of any remnant first phosphor-comprising material from within the second openings over said second substrate areas; and
    forming a second phosphor-comprising material over the second substrate areas.
    [49" id="US-20010001193-A1-CLM-00049] 49. The method of
    claim 48 , wherein said phosphor-removing solution comprises an aqueous organic acid solution.
    [50" id="US-20010001193-A1-CLM-00050] 50. The method of
    claim 49 , wherein said solution comprises a concentration of less than about ten percent lactic acid by volume.
    [51" id="US-20010001193-A1-CLM-00051] 51. The method of
    claim 48 further comprising:
    forming a third patterned masking layer over the substrate defining a third plurality of openings over third substrate areas which are different from said second substrate areas, said forming of said third patterned masking layer comprising exposing said substrate to a phosphor-removing solution which is effective to remove at least some of any remnant first and second phosphor-comprising materials from within the third openings over said third substrate areas; and
    forming a third phosphor-comprising material over said third substrate areas.
    [52" id="US-20010001193-A1-CLM-00052] 52. The method of
    claim 51 , wherein both of said phosphor-removing solutions comprise aqueous organic acid solutions having a concentration of less than about ten percent organic acid by volume.
    [53" id="US-20010001193-A1-CLM-00053] 53. The method of
    claim 52 , wherein the organic acid in one of said solutions comprises lactic acid.
    [54" id="US-20010001193-A1-CLM-00054] 54. A method of forming a face plate assembly of a color display comprising:
    providing a substrate having a first patterned masking layer defining a first plurality of openings over first substrate areas, the substrate comprising a portion of a face plate assembly of a color display and comprising second substrate areas;
    forming a first phosphor-comprising material within the first openings over the first substrate areas and over the first patterned masking layer over the second substrate areas;
    removing the first patterned masking layer and leaving some first phosphor-comprising material over the substrate in the second substrate areas,
    forming a second patterned masking layer comprising photoresist over the substrate leaving a second plurality of openings over the second substrate areas, said forming of the second patterned masking layer comprising exposing the substrate to a photoresist-developing solution which is effective to substantially remove second masking layer material and the first phosphor-comprising material from over said second substrate areas; and
    forming a second phosphor-comprising material over the second substrate areas.
    [55" id="US-20010001193-A1-CLM-00055] 55. The method of
    claim 54 , wherein said photoresist-developing solution comprises an aqueous organic acid solution.
    [56" id="US-20010001193-A1-CLM-00056] 56. The method of
    claim 55 , wherein said photoresist-developing solution comprises a concentration of less than about ten percent lactic acid by volume.
    [57" id="US-20010001193-A1-CLM-00057] 57. The method of
    claim 55 , wherein said photoresist-developing solution comprises a concentration of less than about ten percent acetic acid by volume.
    [58" id="US-20010001193-A1-CLM-00058] 58. The method of
    claim 54 further comprising:
    removing said second patterned masking layer and leaving some second phosphor-comprising material over the substrate in third substrate areas;
    forming a third patterned masking layer comprising photoresist over said substrate leaving a third plurality of openings over said third substrate areas, said forming of said third patterned masking layer comprising exposing the substrate to a photoresist-developing solution which is effective to substantially remove third masking layer material and first and second phosphor-comprising material from over said third substrate areas; and
    forming a third phosphor-comprising material within said third openings over said third substrate areas.
    [59" id="US-20010001193-A1-CLM-00059] 59. The method of
    claim 58 , wherein both of said developing solutions comprise aqueous organic acid solutions.
    [60" id="US-20010001193-A1-CLM-00060] 60. The method of
    claim 59 , wherein one of the solutions comprises a concentration of lactic acid of less than about ten percent by volume.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6406603B2|2002-06-18|Methods of forming a face plate assembly of a color display
    US6759181B2|2004-07-06|Protective layer for corrosion prevention during lithography and etch
    US6153075A|2000-11-28|Methods using electrophoretically deposited patternable material
    US6296750B1|2001-10-02|Composition including black matrix material
    US6540898B2|2003-04-01|Method and system for manufacture of field emission display
    EP0684627A1|1995-11-29|Anode comprising an opaque electrically insulating material, for use in a field emission device
    EP0949650B1|2004-02-25|Light-emitting device
    US3957609A|1976-05-18|Method of forming fine pattern of thin, transparent, conductive film
    US5466358A|1995-11-14|Method of forming a fluoresecent screen by electrodeposition on a screen panel of a field emission display
    US6113449A|2000-09-05|Method of fabricating a front plate for a plasma display panel
    US5611719A|1997-03-18|Method for improving flat panel display anode plate phosphor efficiency
    GB2221087A|1990-01-24|Method of manufacturing phosphor screens for cathode ray tubes
    US6471842B1|2002-10-29|Methods of depositing phosphor molecules and forming field emission display devices
    KR100277492B1|2001-01-15|Color filter for liquid crystal display and its manufacturing method
    JP2000509186A|2000-07-18|Method of making a color screen for FEDs and other cathodoluminescent displays
    KR0124479B1|1997-12-26|Metal thin plate cleaning method and cleaning device
    Kwon et al.2000|Fabrication of Full‐Color Phosphor Screen by Electrophoretic Deposition for Field Emission Display Application
    KR100241155B1|2000-02-01|Method of black matrix for fed
    US7005239B2|2006-02-28|Method of forming metal line
    KR100444517B1|2004-08-16|METHOD OF FABRICATING ElECTRODE IN PLASMA DISPLAY PANEL
    KR19980023338A|1998-07-06|Electrode of flat plate
    JP3277387B2|2002-04-22|Manufacturing method of cathode ray tube
    KR100300392B1|2001-10-22|Anode of flat display device and manufacturing method thereof
    JPH06349404A|1994-12-22|Forming method of fluorescent screen in cathode-ray tube
    JPH0643470A|1994-02-18|Method for correcting transparent conductive layer for liquid crystal display element
    同族专利:
    公开号 | 公开日
    US6319381B1|2001-11-20|
    US20010024683A1|2001-09-27|
    US6383696B2|2002-05-07|
    US6406603B2|2002-06-18|
    US20020003090A1|2002-01-10|
    US6458260B2|2002-10-01|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    KR100851269B1|2001-06-11|2008-08-08|사이픽스 이미징, 인코포레이티드|Process of manufacturing electrophoretic multicolor displays and displays obtained therewith|
    US20140231855A1|2011-08-29|2014-08-21|Osram Opto Semiconductors Gmbh|Method for producing a light-emitting diode and light-emitting diode|US3681223A|1970-07-27|1972-08-01|Corning Glass Works|Electrophoretic deposition of color phosphors|
    US3904502A|1973-03-05|1975-09-09|Westinghouse Electric Corp|Method of fabricating a color display screen employing a plurality of layers of phosphors|
    US3858083A|1973-05-07|1974-12-31|Gte Sylvania Inc|Cathode ray tube screen structure|
    JPS52107766A|1976-03-08|1977-09-09|Toshiba Corp|Manufacture of color picture tube fluorescent surface|
    US4251610A|1979-11-02|1981-02-17|Tektronix, Inc.|Method of making multicolor CRT display screen with minimal phosphor contamination|
    DE3600899A1|1986-01-15|1987-07-16|Licentia Gmbh|Process for cleaning glassy fluorescent screen supports|
    US4751172A|1986-08-01|1988-06-14|Shipley Company Inc.|Process for forming metal images|
    US4891110A|1986-11-10|1990-01-02|Zenith Electronics Corporation|Cataphoretic process for screening color cathode ray tubes|
    JPS6417352A|1987-07-10|1989-01-20|Mitsubishi Electric Corp|Manufacture of fluorescent screen of cathode ray tube|
    JP2717736B2|1991-06-10|1998-02-25|日本石油株式会社|Manufacturing method of color filter|
    JP2949392B2|1992-09-07|1999-09-13|日石三菱株式会社|Manufacturing method of color filter|
    JP3304579B2|1993-12-28|2002-07-22|大日本印刷株式会社|Manufacturing method of color filter|
    JPH0822768A|1994-07-07|1996-01-23|Hitachi Ltd|Cleaning method for color cathode-ray tube panel|
    US5582703A|1994-12-12|1996-12-10|Palomar Technologies Corporation|Method of fabricating an ultra-high resolution three-color screen|
    WO1998018147A1|1996-10-17|1998-04-30|Philips Electronics N.V.|Method of manufacturing a color display device comprising color-filter layers|
    US6046539A|1997-04-29|2000-04-04|Candescent Technologies Corporation|Use of sacrificial masking layer and backside exposure in forming openings that typically receive light-emissive material|EP1231500B1|1996-07-19|2007-03-07|E-Ink Corporation|Electronically addressable microencapsulated ink|
    KR100476043B1|1999-06-21|2005-03-10|비오이 하이디스 테크놀로지 주식회사|FED device and method for manufacturing the same|
    US6933098B2|2000-01-11|2005-08-23|Sipix Imaging Inc.|Process for roll-to-roll manufacture of a display by synchronized photolithographic exposure on a substrate web|
    TW556044B|2001-02-15|2003-10-01|Sipix Imaging Inc|Process for roll-to-roll manufacture of a display by synchronized photolithographic exposure on a substrate web|
    US6885495B2|2000-03-03|2005-04-26|Sipix Imaging Inc.|Electrophoretic display with in-plane switching|
    US20070237962A1|2000-03-03|2007-10-11|Rong-Chang Liang|Semi-finished display panels|
    US7715088B2|2000-03-03|2010-05-11|Sipix Imaging, Inc.|Electrophoretic display|
    US6831770B2|2000-03-03|2004-12-14|Sipix Imaging, Inc.|Electrophoretic display and novel process for its manufacture|
    US7158282B2|2000-03-03|2007-01-02|Sipix Imaging, Inc.|Electrophoretic display and novel process for its manufacture|
    US6930818B1|2000-03-03|2005-08-16|Sipix Imaging, Inc.|Electrophoretic display and novel process for its manufacture|
    US7052571B2|2000-03-03|2006-05-30|Sipix Imaging, Inc.|Electrophoretic display and process for its manufacture|
    US7233429B2|2000-03-03|2007-06-19|Sipix Imaging, Inc.|Electrophoretic display|
    US6865012B2|2000-03-03|2005-03-08|Sipix Imaging, Inc.|Electrophoretic display and novel process for its manufacture|
    US7557981B2|2000-03-03|2009-07-07|Sipix Imaging, Inc.|Electrophoretic display and process for its manufacture|
    US8282762B2|2001-01-11|2012-10-09|Sipix Imaging, Inc.|Transmissive or reflective liquid crystal display and process for its manufacture|
    US6795138B2|2001-01-11|2004-09-21|Sipix Imaging, Inc.|Transmissive or reflective liquid crystal display and novel process for its manufacture|
    US7385751B2|2001-06-11|2008-06-10|Sipix Imaging, Inc.|Process for imagewise opening and filling color display components and color displays manufactured thereof|
    US6972893B2|2001-06-11|2005-12-06|Sipix Imaging, Inc.|Process for imagewise opening and filling color display components and color displays manufactured thereof|
    US6788452B2|2001-06-11|2004-09-07|Sipix Imaging, Inc.|Process for manufacture of improved color displays|
    US7492505B2|2001-08-17|2009-02-17|Sipix Imaging, Inc.|Electrophoretic display with dual mode switching|
    US7038670B2|2002-08-16|2006-05-02|Sipix Imaging, Inc.|Electrophoretic display with dual mode switching|
    TW539928B|2001-08-20|2003-07-01|Sipix Imaging Inc|An improved transflective electrophoretic display|
    US7252749B2|2001-11-30|2007-08-07|The University Of North Carolina At Chapel Hill|Deposition method for nanostructure materials|
    US6821799B2|2002-06-13|2004-11-23|University Of Cincinnati|Method of fabricating a multi-color light emissive display|
    US8023071B2|2002-11-25|2011-09-20|Sipix Imaging, Inc.|Transmissive or reflective liquid crystal display|
    TWI297089B|2002-11-25|2008-05-21|Sipix Imaging Inc|A composition for the preparation of microcups used in a liquid crystal display, a liquid crystal display comprising two or more layers of microcup array and process for its manufacture|
    US7564615B2|2004-12-14|2009-07-21|Electronics And Telecommunications Research Institute|Color electrophoretic display|
    US9327216B2|2012-11-12|2016-05-03|Whirlpool Corporation|Customizable multi-stage water treatment system|
    US9314716B2|2012-11-12|2016-04-19|Whirlpool Corporation|Customizable multi-stage water treatment assembly|
    USD750738S1|2014-10-23|2016-03-01|Michael T. Baird|Set of mounting lugs for a water filter|
    USD750739S1|2014-11-05|2016-03-01|Michael T. Baird|Set of mounting lugs for a water filter|
    法律状态:
    2002-09-12| STCF| Information on status: patent grant|Free format text: PATENTED CASE |
    2003-06-10| CC| Certificate of correction|
    2006-03-13| FPAY| Fee payment|Year of fee payment: 4 |
    2010-03-18| FPAY| Fee payment|Year of fee payment: 8 |
    2014-03-05| FPAY| Fee payment|Year of fee payment: 12 |
    2016-05-12| AS| Assignment|Owner name: U.S. BANK NATIONAL ASSOCIATION, AS COLLATERAL AGENT, CALIFORNIA Free format text: SECURITY INTEREST;ASSIGNOR:MICRON TECHNOLOGY, INC.;REEL/FRAME:038669/0001 Effective date: 20160426 Owner name: U.S. BANK NATIONAL ASSOCIATION, AS COLLATERAL AGEN Free format text: SECURITY INTEREST;ASSIGNOR:MICRON TECHNOLOGY, INC.;REEL/FRAME:038669/0001 Effective date: 20160426 |
    2016-06-02| AS| Assignment|Owner name: MORGAN STANLEY SENIOR FUNDING, INC., AS COLLATERAL AGENT, MARYLAND Free format text: PATENT SECURITY AGREEMENT;ASSIGNOR:MICRON TECHNOLOGY, INC.;REEL/FRAME:038954/0001 Effective date: 20160426 Owner name: MORGAN STANLEY SENIOR FUNDING, INC., AS COLLATERAL Free format text: PATENT SECURITY AGREEMENT;ASSIGNOR:MICRON TECHNOLOGY, INC.;REEL/FRAME:038954/0001 Effective date: 20160426 |
    2017-06-08| AS| Assignment|Owner name: U.S. BANK NATIONAL ASSOCIATION, AS COLLATERAL AGENT, CALIFORNIA Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE REPLACE ERRONEOUSLY FILED PATENT #7358718 WITH THE CORRECT PATENT #7358178 PREVIOUSLY RECORDED ON REEL 038669 FRAME 0001. ASSIGNOR(S) HEREBY CONFIRMS THE SECURITY INTEREST;ASSIGNOR:MICRON TECHNOLOGY, INC.;REEL/FRAME:043079/0001 Effective date: 20160426 Owner name: U.S. BANK NATIONAL ASSOCIATION, AS COLLATERAL AGEN Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE REPLACE ERRONEOUSLY FILED PATENT #7358718 WITH THE CORRECT PATENT #7358178 PREVIOUSLY RECORDED ON REEL 038669 FRAME 0001. ASSIGNOR(S) HEREBY CONFIRMS THE SECURITY INTEREST;ASSIGNOR:MICRON TECHNOLOGY, INC.;REEL/FRAME:043079/0001 Effective date: 20160426 |
    2018-07-13| AS| Assignment|Owner name: JPMORGAN CHASE BANK, N.A., AS COLLATERAL AGENT, ILLINOIS Free format text: SECURITY INTEREST;ASSIGNORS:MICRON TECHNOLOGY, INC.;MICRON SEMICONDUCTOR PRODUCTS, INC.;REEL/FRAME:047540/0001 Effective date: 20180703 Owner name: JPMORGAN CHASE BANK, N.A., AS COLLATERAL AGENT, IL Free format text: SECURITY INTEREST;ASSIGNORS:MICRON TECHNOLOGY, INC.;MICRON SEMICONDUCTOR PRODUCTS, INC.;REEL/FRAME:047540/0001 Effective date: 20180703 |
    2018-08-23| AS| Assignment|Owner name: MICRON TECHNOLOGY, INC., IDAHO Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:U.S. BANK NATIONAL ASSOCIATION, AS COLLATERAL AGENT;REEL/FRAME:047243/0001 Effective date: 20180629 |
    2019-10-09| AS| Assignment|Owner name: MICRON TECHNOLOGY, INC., IDAHO Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:MORGAN STANLEY SENIOR FUNDING, INC., AS COLLATERAL AGENT;REEL/FRAME:050937/0001 Effective date: 20190731 |
    2019-11-12| AS| Assignment|Owner name: MICRON TECHNOLOGY, INC., IDAHO Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:JPMORGAN CHASE BANK, N.A., AS COLLATERAL AGENT;REEL/FRAME:051028/0001 Effective date: 20190731 Owner name: MICRON SEMICONDUCTOR PRODUCTS, INC., IDAHO Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:JPMORGAN CHASE BANK, N.A., AS COLLATERAL AGENT;REEL/FRAME:051028/0001 Effective date: 20190731 |
    优先权:
    申请号 | 申请日 | 专利标题
    US09/096,365|US6319381B1|1998-06-11|1998-06-11|Methods of forming a face plate assembly of a color display|
    US09/398,835|US6406603B2|1998-06-11|1999-09-16|Methods of forming a face plate assembly of a color display|
    US09/760,191|US6458260B2|1998-06-11|2001-01-12|Methods of forming a face plate assembly of a color display|US09/760,191| US6458260B2|1998-06-11|2001-01-12|Methods of forming a face plate assembly of a color display|
    [返回顶部]