    • 专利摘要:
    Selected novel partially fluorinated α,ω-dienes can be free radically (co)polymerized to form polymers in which cyclic structures are present. The polymers are useful for films, coatings and molded parts.
    公开号:US20010000182A1
    申请号:US09/730,434
    申请日:2000-12-05
    公开日:2001-04-05
    发明作者:Zhen-Yu Yang
    申请人:Zhen-Yu Yang；
    IPC主号:C08F14-185
    专利说明:
    [1] 1. This invention concerns polymers made from selected partially fluorinated dienes, in which the repeat units are cycloaliphatic. Also disclosed are novel monomers for making these polymers. TECHNICAL BACKGROUND
    [2] 2. Free radical polymerizations which include nonconjugated dienes (and bis vinyl ethers) usually yield polymers which are crosslinked because of the “separate” reaction of each of the double bonds with the free radicals in the reactions. However, it is known that in some instances perfluorinated or partially fluorinated compounds containing two such double bonds do not form crosslinked polymers, but form polymers containing cyclic structures.
    [3] 3. U.S. Pat. Nos. 5,326,917, 5,313,003, 5,260,492, 4,897,457, J. E. Fearn, et al., J. Polym. Sci. A-1, vol. 4, p. 131-140 (1966) and D. W. Brown, et al., J. Polym. Sci. A-2, vol. 7, p. 601-608 (1969) all describe the polymerization of partially or fully fluorinated compounds containing two double bonds which give polymers having cyclic structures. The instant monomers and polymers are not disclosed therein.
    [4] 4. D. J. Burton, et al., J. Fluorine Chem., vol. 50, p. 257-264 (1990) describe the synthesis of 1,1,2,3,3-pentafluoro-1,5-heaxdiene. No homologs are described. SUMMARY OF THE INVENTION
    [5] 5. This invention concerns a polymer, comprising, one or more of the repeat units
    [6] 6. or one or more of the repeat units
    [7] 7. or both.
    [8] 8. This invention also concerns a compound of the formula
    [9] 9. CF2═CFCF2CF(CF3)CH2CH═CH2 or CF2═CFCF(CF3)CF2CH2CH═CH2.
    [10] 10. DETAILS OF THE INVENTION
    [11] 11. The compounds CF2═CFCF2CF(CF3)CH2CH═CH2 or CF2═CFCF(CF3)CF2CH2CH═CH2 can be free radically polymerized to polymers containing one or more cyclic structures. When the monomer is CF2═CFCF2CF(CF3)CH2CH═CH2, a polymer with one or more of the repeat units (IA), (IB), and (IC) is produced. When the monomer is CF2═CFCF(CF3)CF2CH2CH═CH2, a polymer with one or more of the repeat units (IIA), (IIB) and (IIC) is produced. The synthesis of these two monomers is described in Examples 1-3. These 2 compounds may be separated from their mixture by methods known in the art, such as gas chromatography or liquid phase chromatography.
    [12] 12. These monomers may be polymerized by themselves to form homopolymers, or copolymerized with other monomers to form copolymers. By “comprising” in describing these polymers is meant that they contain the above cyclic repeat units, plus any other repeat units from other monomers. Suitable comonomers include fluorinated and unfluorinated compounds such as tetrafluoroethylene, hexafluoropropylene, vinylidene fluoride, perfluoro(methyl vinyl ether), perfluoro(propyl vinyl ether), methyl vinyl ether, propylene, ethylene, chlorotrifluoroethylene, and perfluoro(2,2-dimethyl- 1,3-dioxole). Preferred comonomers are tetrafluoroethylene, perfluoro(propyl vinyl ether) and perfluoro(2,2-dimethyl-1,3-dioxole), and tetrafluoroethylene is especially preferred.
    [13] 13. The homo- and copolymers described herein are useful for films, coatings, and for molded articles. Such items can be made by standard techniques. Since these polymers are at least partially fluorinated, they have superior chemical resistance, and in many cases superior thermal properties.
    [14] 14. The polymerizations described herein may be done by methods well known to the artisan, see for instance polymerizations methods described in H. Mark, et al., Ed., Encyclopedia of Polymer Science and Engineering, vol. 16, John Wiley & Sons, New York, 1989, p. 577-648. The polymerizations may be done neat, in aqueous emulsion or suspension, in solution or organic suspension. They may be done in batch, semibatch or continuous operations. A free radical polymerization initiator is used, suitable initiators including peroxides such as perfluoro(propionyl peroxide) (3P), azonitriles such as azobis(isobutylronitrile) (AIBN), and redox initiators such as persulfate-bisulfite. As is well known, the process is run at a temperature at which the initiator generates free radicals.
    [15] 15. In the Examples, the following abbreviations are used:
    [16] 16. AIBN—azobis(isobutyronitrile)
    [17] 17. CFC-122—1,1,2-trichloro-1,2,2-trifluoroethane
    [18] 18. DSC—differential scanning calorimetry
    [19] 19. DMF—N,N-dimethylformamide
    [20] 20. PDD—perfluoro(2,2-dimethyl-1,3-dioxole)
    [21] 21. TGA—thermogravimetric analysis
    [22] 22. Glass transition temperatures were taken as the beginning of the transition, while melting points were taken as the peak of the melting endotherm. The heating rate for the DSC was 20° C./min. EXAMPLE 1 Preparation of ClCF2ClCFCF2CFICF3 and CF2ClCFClCF(CF3)CF2I
    [23] 23. A mixture of 280 g of CF2ClCFClI and 400 g of CF3CF═CF2 was heated in a autoclave at 200° C. for 15 hours. The reaction mixture (367.4 g) was distilled on a 91 cm spinning band column to give 19 g of bp 64 to 98° C., 99.2 g of CF2ClCFClI, bp 99 to 101° C., 8.5 g of bp 61° C./5.3 kPa to 75° C./5.3 kPa and 199 g of CF2ClCFClCF2CFICF3 and CF2ClCFClCF(CF3)CF2I in a 94 to 6, bp 75° C./5.3 kPa. 19F NMR for major product: −62.0 to −64.8 (m, 2F), −72.5 (m, −72.9 (m) ( total 3F), −99.6 (m), −101.0 (dm, J=275 Hz), −105.1 (dm, J=275 Hz) (total 2F), −125.7 (m), −129.0 (m), (total 1F), −138.5 (m), −142.8 (m) (total 1F).
    [24] 24. HRMS: calcd for C5F9Cl2I: 427.8278. Found: 427.8272. EXAMPLE 2 Preparation of CF2ClCFClCFCF3CH2CHICH2OAc and CF2ClCFCICF(CF3)CF2CH2CHICH2OAc
    [25] 25. A mixture 20 g of allyl acetate 43 g of a mixture CF2CICFClCF2CFICF3 and CF2ClCFClCF(CF3)CF2I in a 94 to 6, 1.5 g of copper powder and 60 mL of hexane was stirred at 72° C. overnight. After removal of solids, the filtrate was evaporated to give 63.2 g of residue, which was distilled to give 26.7 g of 1 to 1 adducts, bp 80° C./12 Pa. IR: 1752 (s), 1229 (s), 1169 (s), 1047 (s). HRMS: calcd for C10H8O2F9Cl2-I: 400.9756. Found: 400.9705. EXAMPLE 3 Preparation of CF2═CFCF2CF(CF3)CH2CH═CH2 and CF2═CFCF(CF3)CF2CH2CH═CH2
    [26] 26. To a stirred solution of 9.0 g of Zn and 30 mL of DMF was slowly added 24 g of 1 to 1 adducts of Example 2 at 80° C. After the resulting mixture was stirred at 80° C. for 5 hours, volatiles were distilled out and collected in a −78° C. receiver at 1.3 kPa. The distillate was washed with water, NaCl solution and dried over MgSO4 and redistilled to give 9.8 g of product, bp 102-103° C.
    [27] 27.19F NMR: −91.0 (ddt, J=53.8 Hz, J=38.0 Hz, J=5.9 Hz, 1F), −75.6 (m, 3F), −106.2 (ddtd, J=116.0 Hz, J=53.8 Hz, J=27.4 Hz, J=5.8 Hz, 1F), −113.5 (dm, J=27.4 Hz, 2F), −180.9 (m, 1F), −186.2 (dm, J=116.0 Hz, 1F). 1H NMR: 5.80 (m, 1H), 5.30 (m, 2H), 2.85 (m, 2H). IR: 3043 (w), 1789.0 (s), 1652 (w), 1366 (s), 1316 (s), 1221 (s), 1193 (s). HRMS: calcd for C8H5F9: 272.0247. Found: 272.0239. EXAMPLE 4 Homopolymerization of a mixture of 94 to 6 ratio of CF2═CFCF2CF(CF3)CH2CH═CH2 and CF2═CFCF(CF3)CF2CH2CH═CH2 initiated by bis(perfluoropropionyl) peroxide
    [28] 28. A 25 mL glass ampul fitted with a Teflon® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1,1,2-trichlorotrifluoroethane and 0.71 g of the title compounds. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N2 alternately six times, contents of the sealed ampul were stirred at 40° C. for 4 hours. The white heterogeneous mixture was filtered and washed with ethyl acetate and dried under vacuum at 100° C. to give 0.50 g of polymer.
    [29] 29. The IR spectrum of this polymer showed no absorption at around 1790 and 1650 cm−1 which could be attributed to double bonds in the polymer. This polymer was insoluble in acetone, ethyl acetate, DMF and hexafluorobenzene. The polymer had a glass transition temperature of 130° C., and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 430° C. in nitrogen and 400° C. in air, respectively, when heated at 20° C./minute. EXAMPLE 5
    [30] 30. Homopolymerization of a mixture of 94 to 6 ratio of CF2═CFCF2CF(CF3)CH2CH═CH2 and CF2═CFCF(CF3)CF2CH2CH═CH2 initiated by initiated by AIBN
    [31] 31. A glass ampul fitted with a Teflon® coated stir bar was charged with 7 mg of AIBN, 0.72 g of the title compound. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N2 alternately six times, contents of the sealed ampul were stirred at 75° C. for 48 hours. The white heterogeneous solution were filtered and washed with CFC113 and dried under vacuum at 110° C. to give 0.35 g of polymer.
    [32] 32. This polymer was insoluble in acetone, ethyl acetate, DMF and hexafluorobenzene. The polymer had a glass transition temperature of 130° C., and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 430° C. in nitrogen and 400° C. in air, respectively, when heated at 20° C./minute. EXAMPLE 6 Copolymerization of a mixture of 94 to 6 ratio of CF2═CFCF2CF(CF3)CH2CH═CH2 and CF2═CFCF(CF3)CF2CH2CH═CH2 with perfluoropropyl vinyl ether (PPVE)
    [33] 33. A 25 mL glass ampul fitted with a Teflon® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1,1,2-trichlorotrifluoroethane, 0.71 g of the title compounds and 0.71 g of PPVE. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N2 gas six times, contents of the sealed ampul were stirred at 40° C. overnight. The white solid was washed with methanol and dried under vacuum at 100° C. to give 0.50 g of polymer. The polymer had a glass transition temperature of 131.6° C. and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 410° C. in nitrogen and 390° C. in air, respectively, when heated at 20° C./minute. EXAMPLE 7 Copolymerization of a mixture of 94 to 6 ratio of CF2═CFCF2CF(CF3)CH2CH═CH2 and CF2═CFCF(CF3)CF2CH2CH═CH2 with perfluoro-2,2-dimethyl-1,3-dioxole (PDD)
    [34] 34. A 25 mL glass ampul fitted with a Teflon® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1,1,2-trichlorotrifluoroethane and 0.65 g of the title compounds and 0.8 g of PDD. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N2 alternately six times, contents of the sealed ampul were stirred at 40° C. overnight. White solids was washed with ethyl acetate and dried under vacuum at 100° C. to give 0.86 g of polymer. The polymer had a glass transition temperature of 139.1° C. and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 470° C. in air when heated at 20° C./minute. EXAMPLE 8 Copolymerization of a mixture of 94 to 6 ratio of CF2═CFCF2CF(CF3)CH2CH═CH2 and CF2═CFCF(CF3)CF2CH2CH═CH2 with Chlorotrifluoroethylene
    [35] 35. A 25 mL glass ampul fitted with a Teflon® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1,1,2-trichlorotrifluoroethane and 0.65 g of the title compounds and 1.0 g of chlorotrifluoroethylene. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N2 alternately six times, contents of the sealed ampul were stirred at 40° C. overnight. White solids was washed with ethyl acetate and dried under vacuum at 100° C. to give 0.52 g of polymer. The polymer had a glass transition temperature of 127° C. and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 385° C. in nitrogen when heated at 20° C./minute. EXAMPLE 9 Copolymerization of a mixture of 94 to 6 ratio of CF2═CFCF2CF(CF3)CH2CH═CH2 and CF2═CFCF(CF3)CF2CH2CH═CH2 with CF2═CFOCF2CF(CF3)OCF2CF2SO2F (PSEPVE)
    [36] 36. A 25 mL glass ampul fitted with a Teflon® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1,1,2-trichlorotrifluoroethane and 0.65 g of the title compounds and 0.85 g of PSEPVE. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N2 alternately six times, contents of the sealed ampul were stirred at 40° C. overnight. The white solid was washed with ethyl acetate and dried under vacuum at 100° C. to give 0.60 g of polymer. The polymer had glass transition temperatures of 127.6° C., 190.3° C. and 364° C. and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 400° C. in nitrogen when heated at 20° C./minute.
    权利要求:
    Claims (10)
    [1" id="US-20010000182-A1-CLM-00001] 1. A polymer, comprising, one or more of the repeat units
    [2" id="US-20010000182-A1-CLM-00002] 2. The polymer as recited in
    claim 1 which comprises one or more of repeat units (IA), (IB) or (IC).
    [3" id="US-20010000182-A1-CLM-00003] 3. The polymer as recited in
    claim 1 which comprises one or more of repeat units (IIA), (IIB) or (IIC).
    [4" id="US-20010000182-A1-CLM-00004] 4. The polymer as recited in
    claim 1 which is a copolymer.
    [5" id="US-20010000182-A1-CLM-00005] 5. The polymer as recited in
    claim 4 wherein a comonomer is one or more of tetrafluoroethylene, hexafluoropropylene, vinylidene fluoride, perfluoro-(methyl vinyl ether), perfluoro(propyl vinyl ether), methyl vinyl ether, propylene, ethylene, chlorotrifluoroethylene, or perfluoro(2,2-dimethyl-1,3-dioxole).
    [6" id="US-20010000182-A1-CLM-00006] 6. The polymer as recited in
    claim 4 wherein a comonomer is one or more of tetrafluoroethylene, perfluoro(propyl vinyl ether) or perfluoro-(2,2-dimethyl-1,3-dioxole).
    [7" id="US-20010000182-A1-CLM-00007] 7. The polymer as recited in
    claim 4 wherein a comonomer is tetrafluoroethylene.
    [8" id="US-20010000182-A1-CLM-00008] 8. A compound of the formula CF2═CFCF2CF(CF3)CH2CH═CH2 or CF2═CFCF(CF3)CF2CH2CH═CH2.
    [9" id="US-20010000182-A1-CLM-00009] 9. The compound as recited in
    claim 8 of the formula CF2═CFCF2CF(CF3)CH2CH═CH2.
    [10" id="US-20010000182-A1-CLM-00010] 10. The compound as recited in
    claim 8 of the formula CF2═CFCF(CF3)CF2CH2CH═CH2.
    类似技术:
    公开号 | 公开日 | 专利标题
    US5646223A|1997-07-08|Perfluorodioxoles, the preparation process thereof, and homopolymers and copolymers therefrom
    US5763552A|1998-06-09|Hydrogen-containing flourosurfacant and its use in polymerization
    US5310838A|1994-05-10|Functional fluoropolymers
    RU2269506C2|2006-02-10|Fluorovinyl ethers and polymers prepared therefrom
    EP0674612B1|1997-12-03|Fluorinated monomers and polymers
    US5260492A|1993-11-09|Fluorinated monomers and polymers
    US6335408B1|2002-01-01|Copolymers of perfluorodioxoles
    US6255543B1|2001-07-03|Partially fluorinated polymers
    EP0783533B1|1998-08-05|Partially fluorinated polymers and process therefor
    US5475071A|1995-12-12|Partially fluorinated polymers and process therefor
    US6469185B1|2002-10-22|Perfluorodioxoles
    US6300526B1|2001-10-09|Hydro-fluoroalkylvinylethers and process for obtaining them
    CA2123693C|2004-03-23|New thermoplastic fluorocopolymers and the fluoromonomers used for their preparation
    US5336741A|1994-08-09|Fluorinated polymer and monomers
    US5478904A|1995-12-26|Polymers of vinyl |
    US5648566A|1997-07-15|Methyleneperfluorocycloalkanes and their use in the production of thermoplastic fluororesins
    同族专利:
    公开号 | 公开日
    JP3993239B2|2007-10-17|
    US6214955B1|2001-04-10|
    JP2000511192A|2000-08-29|
    WO1997045464A1|1997-12-04|
    US6255543B1|2001-07-03|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US4897457A|1987-08-14|1990-01-30|Asahi Glass Company Ltd.|Novel fluorine-containing cyclic polymer|
    DE4219764A1|1992-06-17|1993-12-23|Bayer Ag|Cyclopolymerizable fluorine compounds, process for their preparation and thermoplastic fluoropolymers obtainable therefrom|
    US5326917A|1992-12-21|1994-07-05|E. I. Du Pont De Nemours And Company|Fluorinated monomers and polymers|
    US5260492A|1992-12-21|1993-11-09|E. I. Du Pont De Nemours And Company|Fluorinated monomers and polymers|
    US5557018A|1994-09-27|1996-09-17|E. I. Du Pont De Nemours And Company|Partially flourinated polymers and process therefor|
    US5475071A|1994-09-27|1995-12-12|E. I. Du Pont De Nemours And Company|Partially fluorinated polymers and process therefor|US20030181616A1|2002-02-12|2003-09-25|Brian Thomas|Halogenated monomers and polymers and process for making same|
    WO2007142244A1|2006-06-07|2007-12-13|Asahi Glass Company, Limited|Novel polyfluorodiene, method for producing the same, and novel fluorine-containing polymer|
    US7456314B2|2006-12-21|2008-11-25|E.I. Du Pont De Nemours And Company|Partially fluorinated ionic compounds|
    US8415070B2|2006-12-21|2013-04-09|E I Du Pont De Nemours And Company|Partially fluorinated cyclic ionic polymers and membranes|
    US7943715B2|2007-02-28|2011-05-17|Sumitomo Chemical Company, Limited|Diene polymer and process for producing the same|
    JP2010139518A|2007-03-30|2010-06-24|Asahi Glass Co Ltd|Resist polymer|
    CN101646696B|2007-03-30|2012-07-04|旭硝子株式会社|Novel fluorine-containing compound, fluorine-containing polymer, and method for producing the compound|
    US8071254B2|2007-12-27|2011-12-06|E. I. Du Pont De Nemours And Company|Crosslinkable fluoropolymer, crosslinked fluoropolymers and crosslinked fluoropolymer membranes|
    US20100093878A1|2007-12-27|2010-04-15|E.I. Du Pont De Nemours And Company|Crosslinkable fluoropolymer, crosslinked fluoropolymers and crosslinked fluoropolymer membranes|
    法律状态:
    2001-06-14| STCF| Information on status: patent grant|Free format text: PATENTED CASE |
    2004-12-21| FPAY| Fee payment|Year of fee payment: 4 |
    2008-12-04| FPAY| Fee payment|Year of fee payment: 8 |
    2012-12-05| FPAY| Fee payment|Year of fee payment: 12 |
    2015-04-15| AS| Assignment|Owner name: THE CHEMOURS COMPANY FC, LLC, DELAWARE Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:E. I. DU PONT DE NEMOURS AND COMPANY;REEL/FRAME:035432/0023 Effective date: 20150414 |
    2015-06-10| AS| Assignment|Owner name: JPMORGAN CHASE BANK, N.A., NEW YORK Free format text: SECURITY AGREEMENT;ASSIGNORS:THE CHEMOURS COMPANY FC LLC;THE CHEMOURS COMPANY TT, LLC;REEL/FRAME:035839/0675 Effective date: 20150512 |
    2018-04-04| AS| Assignment|Owner name: THE CHEMOURS COMPANY FC, LLC, DELAWARE Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:JPMORGAN CHASE BANK, N.A., AS ADMINISTRATIVE AGENT;REEL/FRAME:045845/0913 Effective date: 20180403 |
    优先权:
    申请号 | 申请日 | 专利标题
    US1849396P| true| 1996-05-28|1996-05-28||
    US09/194,282|US6214955B1|1996-05-28|1997-05-27|Partially fluorinated polymers|
    US09/730,434|US6255543B1|1996-05-28|2000-12-05|Partially fluorinated polymers|US09/730,434| US6255543B1|1996-05-28|2000-12-05|Partially fluorinated polymers|