    • 专利摘要:
    Ferro-manganese is decarburized from a carbon content of as high as 7.5% down to 2% or less by blowing an oxidizing gas into the melt in two stages through one or more immersed tuyeres protected with a peripheral fluid introduced into said tuyeres, utilizing temperatures between 1650 DEG and 1750 DEG C.
    公开号:SU1050570A3
    申请号:SU792711900
    申请日:1979-01-16
    公开日:1983-10-23
    发明作者:Салей Жан；Жан Леруа Пьер；Массон Жан-Марсель；Андрей Фатерстон Робер；Петрус Рус Поль；Адриан Герик Уильям
    申请人:Крезо-Луар (Фирма)；С.А.Манганес Амкор Л.Т.Д. (Фирма)；
    IPC主号:
    专利说明:

    The invention relates to metallurgy and can be used to discard the production of ferromanganese with a high carbon content. In the present sh | foko, the refining of molten iron and steel melts in converters equipped with blowing lances immersed in the melt is known. The closest to the invention according to the technical essence and the achieved result is cnoqo6 raffin for ferromanganese in the liquid state, including the purging of the metal melt with pure acid, water vapor and inert gas from the bottom of the melt pool by means of submersible tuyeres, where starting with carbon content in the melt 6-7.5%, the melt is blown with pure oxygen to a carbon content of 23.5% at a temperature, the melt is 165O 1750 ° C with a further decrease in the content of the loss to 1.2-1.6% and the temperature of the melt 167O-1710 ° C by blowing the melt at the same volumetric ratio,%: pure oxygen up to 50, water vapor not less than 30 and inert gas {70). The disadvantages of this method are the transition of a significant fraction of 1 | manganese in the slag, and the loss of manganese in the result during the purge. In addition, the considered method allows to obtain carbon content in ferromanganese - less than 1.2%. The aim of the invention is to reduce the carbon content in the melt below 1.2%, increase the efficiency of decarburization and reduce the loss of manganese. This goal is achieved by the fact that according to the method of refining the ferro-manganese in a liquid state, including the 1 lithium blend of the metal, 1 M oxygen, steam and melting gas from the bottom of the bath by means of submersible lances, in -KOTOpot, starting with carbon content in the melt. from 6-7.5%, the melt is blown with pure oxygen to a carbon content of 2-3.5% at a melting temperature of VA 165O-1750 ° C with a further reduction of carbon to 1.2-1.6% and temperature to 167O-1710 With a way to melt a brush at the same time with pure oxygen and water vapor with or without inert gas in the following volume ratio,%: pure oxygen up to 5O, water vapor is not. less than 30%, and inert gas up to 70, starting with a carbon content of 1.2%, melt:, sweep to the final specified content of uterod together with pure oxygen simultaneously with WATER vapor and inert gas, which are supplied separately or in a mixture, in the following volume ratio ,%: pure oxygen up to 25, water vapor ZO-5O and inert gas 30-70, 1f WHAT the melt temperature is maintained within. 1660-1720 C, and the tuyeres are protected by the introduction of a cooling fluid along the periphery of the stream, followed by a dry outlet into the melt. In addition, the slag after the OKuq stage and the decarbonation of the souting is converted into a fluid state by introducing silicon oxide, or aluminum oxide, or calcium fluoride, then Shpak is fed to a reduction furnace. In this case, the unrecovered slag is left in the metallurgical aggregate, carbon-containing ferromanganese is introduced onto the slag by the next batch and the slag is reduced, during the first blasting phase. The essence of the invention is to use at every moment in the optimal ratios of pure acid, genus, water vapor and inert gas of nitrogen or argon. Example. 14) the ferromargash melt is melted with an initial content of 6.57% to the final content of Uterod, 7–4% of the coagulator, with a capacity of 6 tons of conditions, given in the tablegaw. The weight of the loaded romargants is 5720 kg, the weight of the ferromanganese after casting is 4750 kg, the metal yield is 83, O4%; yield of manganese 85.56%. Technical and economic efficiency, the invention boils down to an increase in the efficiency of decarburization and a reduction in i loss of manganese.
    Stage a18- (IOO%)., OO
    , 38 Mp, 81,71685
    5.5 (46%) 6.5 С54%) О
    Stage b
    Cj-1.24, 35
    2.6 (20.8%) 5 (37%) 5.7 (42.2%)
    Stage 0
    t4) ,, 85
    Psula final additives and rapping in bucket
    Cg "0.74, 55
    1685
    1710
    1570
    权利要求:
    Claims (3)
    [1]
    1. METHOD FOR REFINING FERROMARGANESE IN A LIQUID CONDITION- !, Research Institute, including purging a metal melt * with pure oxygen, water vapor. and inert gas from the bottom of the melt bath by means of submersible tuyeres, in which, starting from the carbon content of the melt from 6-7.5%, the melt is purged with pure oxygen to a carbon content of 23.5% at a melt temperature of 1650-175 ° C with a further decrease in the content carbon up to 1.2-1.6% and temperatures up to 1670-171О ° С by blowing j melt simultaneously with pure oxygen and a water core with or without inert; gas in the following volume ratio,%: pure oxygen up to 501), water vapor * at least 30, and inert reptile up to 70, which means that. *
    .............
    that, in order to reduce the carbon content in the melt below 1.2%, increase the efficiency of decarburization and reduce manganese losses, starting from the carbon content of 1.2%, the melt is blown to the final predetermined carbon content together with pure oxygen at the same time as water vapor and inert gas, which are supplied separately or in a mixture in the following volume ratio,%: pure oxygen up to 25, water vapor 30-50 and inert gas 30-70, the temperature being. the melt is maintained within 1660-1720 ° C. and the tuyeres are protected by the introduction of coolant along the periphery of the coolant flow, followed by its exit into the melt.
    [2]
    2. The method according to π. 1, on the basis of the fact that, in order to recover-. days of manganese * contained in slag, as a result of reduction of slag oxides after oxidation stages and decarburization | The liquids are brought into a fluid state by introducing silicon oxide, or aluminum oxide, or calcium fluoride, then the slag is fed to a reduction electric furnace.
    [3]
    3. The method according to claim 1, with the fact that the unreduced slag is left in the metallurgical unit, carbon-containing ί · ι ferromanganese of the next portion of the charge is introduced into this slag and the recovery is carried out--
    1k during the first purge phase.
    SU <„> 1050570
    I 1050570 2
    类似技术:
    公开号 | 公开日 | 专利标题
    CA2525559C|2011-07-26|Method for recovering metallic elements, especially metallic chromium, from slag containing metal oxides in an electric-arc furnace
    JP5954551B2|2016-07-20|Converter steelmaking
    KR100749023B1|2007-08-14|Method for refining extra low phosphorous steel in converter
    SU1050570A3|1983-10-23|Method for refining ferromanganese in liquid state
    US3791819A|1974-02-12|Production of stainless steels
    SU1487819A3|1989-06-15|Method of converting copper matte
    US4363657A|1982-12-14|Process for obtaining manganese- and silicon-based alloys by silico-thermal means in a ladle
    US4165234A|1979-08-21|Process for producing ferrovanadium alloys
    US2639984A|1953-05-26|Continuous cupola-bessemer process
    JP6962934B2|2021-11-05|Method for producing medium-low carbon ferromanganese and medium-low carbon ferromanganese
    SU648118A3|1979-02-15|Method of producing alloy steel
    US6314123B1|2001-11-06|Method for continuous smelting of solid metal products
    SU1484297A3|1989-05-30|Method of producing steels with low carbon content
    US4348227A|1982-09-07|Process for producing steel with low hydrogen content in a through-blowing oxygen converter
    US4141723A|1979-02-27|Process for producing stainless steel
    EP0099713B1|1988-02-24|A method for protecting tuyères for refining a molten iron
    SU985063A1|1982-12-30|Method of producing steel in electric arc furnace
    RU2118376C1|1998-08-27|Method of producing vanadium slag and naturally vanadium-alloyed steel
    SU652234A1|1979-03-15|Method of obtaining vanadiun alloys
    RU2140458C1|1999-10-27|Vanadium cast iron conversion method
    RU2015173C1|1994-06-30|Steel melting method
    RU1774958C|1992-11-07|Method of smelting steel in two-vat smelting unit
    SU1071643A1|1984-02-07|Method for smelting steel in oxygen convertor
    SU1560561A1|1990-04-30|Method of steel melting in converter with combined blowing
    SU881143A1|1981-11-15|Method of producing vanadium alloys
    同族专利:
    公开号 | 公开日
    JPS5497521A|1979-08-01|
    AU4321779A|1979-07-26|
    US4192675A|1980-03-11|
    DE2901707A1|1979-07-19|
    DE2901707C2|1988-09-22|
    IN150342B|1982-09-18|
    ZA79169B|1980-02-27|
    BE873534A|1979-07-17|
    FR2414559B1|1980-08-22|
    FR2414559A1|1979-08-10|
    AU517352B2|1981-07-23|
    NO150889B|1984-09-24|
    OA06151A|1981-06-30|
    BR7808567A|1979-08-07|
    JPH0124855B2|1989-05-15|
    NO784377L|1979-07-18|
    CA1119412A|1982-03-09|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    NL296346A|1962-08-07|
    GB1253581A|1968-02-24|1971-11-17|Maximilianshuette Eisenwerk|Improvements in processes and apparatus for making steel|
    DE1916945C3|1969-04-02|1980-04-17|Eisenwerk-Gesellschaft Maximilianshuette Mbh, 8458 Sulzbach-Rosenberg|Use of the jacket gas process for refining pig iron to steel|
    US4021233A|1971-10-06|1977-05-03|Uddeholms Aktiebolag|Metallurgical process|
    BE792732A|1972-01-13|1973-03-30|Elektrometallurgie Gmbh|PROCESS FOR RAPIDLY DECARBURATION OF IRON ALLOYS BY MEANS OF OXYGEN|
    US3990888A|1972-10-06|1976-11-09|Uddeholms Aktiebolag|Decarburization of a metal melt|
    SU648121A3|1975-07-11|1979-02-15|Гезельшафт Фюр Электрометаллурги Мбх |Method of decarbonating high-carbon ferromanganese or ferrochrome|
    DE2531034C2|1975-07-11|1983-09-15|GfE Gesellschaft für Elektrometallurgie mbH, 4000 Düsseldorf|Process for decarburizing high-carbon ferro-manganese or high-carbon ferrochrome|US4662937A|1984-05-28|1987-05-05|Nippon Steel Corporation|Process for production of high-manganese iron alloy by smelting reduction|
    JPH062922B2|1984-06-18|1994-01-12|新日本製鐵株式会社|Method for producing carbon unsaturated high manganese iron alloy|
    JPH062923B2|1984-07-16|1994-01-12|新日本製鐵株式会社|Method for producing low phosphorus high manganese iron alloy by smelting reduction|
    JPH0558050B2|1986-03-31|1993-08-25|Kobe Steel Ltd|
    BE1005461A3|1991-10-16|1993-08-03|Wurth Paul Sa|High-carbon ferromanganese refining method and installation|
    WO2021177021A1|2020-03-06|2021-09-10|Ｊｆｅスチール株式会社|Method for producing low-carbon ferromanganese|
    法律状态:
    优先权:
    申请号 | 申请日 | 专利标题
    FR7801171A|FR2414559B1|1978-01-17|1978-01-17|
    [返回顶部]