    • 专利摘要:
    This invention is a vertical liquid crystal aligning agent which can form the liquid crystal aligning film excellent in the vertical alignment property of a liquid crystal, and being excellent in high voltage retention characteristics, low residual DC, and printability, when it used as a liquid crystal aligning film, (A) Tetracarboxylic dianhydride represented by the following formula (1) (B) Provided is a liquid crystal aligning agent containing at least one of a polyamic acid produced by reacting a diamine represented by the following formula (2) and an imidized polymer produced by dehydrating and closing the polyamic acid. (Wherein R 1 is a halogen atom, an alkyl group having 1 to 10 carbon atoms or a fluoroalkyl group having 1 to 10 carbon atoms and a is an integer of 0 to 4) (Wherein X is a divalent organic group and R 2 is a monovalent organic group having an alicyclic skeleton having 4 to 40 carbon atoms)
    公开号:KR20010098921A
    申请号:KR1020010022839
    申请日:2001-04-27
    公开日:2001-11-08
    发明作者:도시유끼 아끼이께；쯔요시 히라이
    申请人:마쯔모또 에이찌；제이에스알 가부시끼가이샤；
    IPC主号:
    专利说明:

    Liquid Crystal Alignment Agent {Liquid Crystal Aligning Agent}
    [9] The present invention relates to a liquid crystal aligning agent. More specifically, it relates to the liquid crystal aligning agent which is excellent in voltage retention characteristics, low afterimage, and printability, and has the vertical alignment property suitable for the use of a vertical alignment liquid crystal display element especially.
    [10] At present, as a liquid crystal display element, the liquid crystal aligning film which consists of a polyamic acid, a polyimide, etc. is formed in the surface of the board | substrate with which the transparent conductive film is provided, and it is set as the board | substrate for liquid crystal display elements, and the two sheets are opposed, and positive dielectric anisotropy is provided between them. TN-type liquid crystal having a so-called TN-type liquid crystal cell in which a nematic liquid crystal layer having a structure is formed to form a sandwich cell, and the long axis of the liquid crystal molecules is continuously twisted 90 degrees from one substrate to the other substrate. Display elements are known. In addition, STN (Super Twisted Nematic) type liquid crystal display elements or vertical alignment type liquid crystal display elements have been developed that have a higher contrast and less visual dependence than TN type liquid crystal display elements. This STN type liquid crystal display element is produced by blending a nematic liquid crystal with a chiral agent which is an optically active substance as a liquid crystal, and is caused by the long axis of the liquid crystal molecules being continuously twisted over 180 degrees between the substrates. It is to use the birefringence effect.
    [11] On the other hand, the vertically-aligned liquid crystal display element vertically aligns a liquid crystal having a negative dielectric anisotropy of the liquid crystal molecules and operates the liquid crystal molecules horizontally by applying a voltage, such as a viewing angle, contrast and rubbingless. Excellent in terms of research and development has been actively made recently.
    [12] In order to make it orientate vertically, a high pretilt angle is needed, and for this reason, it is necessary to include a large amount of components for expressing a pretilt angle in an orientation agent. As a pretilt expression component, aliphatic, cycloaliphatic, and fluorine-based functional groups are often used.
    [13] However, there has been a problem in that aggregation and crystallization of pretilt angle expression components occur, thereby degrading printability.
    [14] Therefore, the development of the vertical alignment agent which is excellent in printability and satisfy | fills vertical alignment property, low afterimage property, and a voltage retention characteristic is calculated | required.
    [15] Therefore, it is an object of the present invention to provide a liquid crystal aligning agent which is excellent in printability, antifoaming property, and has good vertical alignment, low afterimage, and voltage retention characteristics.
    [16] Still other objects and advantages of the present invention will become apparent from the following description.
    [1] BRIEF DESCRIPTION OF THE DRAWINGS The schematic diagram of the liquid crystal cell of the MVA system used for the Example of this invention.
    [2] <Explanation of symbols for the main parts of the drawings>
    [3] 1 Color filter side electrode (ITO)
    [4] 2 liquid crystal aligning film
    [5] 3 pixel electrode (ITO)
    [6] 4 orientation control means (projection)
    [7] 5 orientation control means (slits)
    [8] 6 liquid crystal molecules
    [17] According to the present invention, the above object and advantages of the present invention are firstly (A) tetracarboxylic dianhydride represented by the following general formula (1) (hereinafter also referred to as "specific tetracarboxylic dianhydride") and
    [18] (B) a liquid crystal characterized by containing at least one polyamic acid produced by reacting a diamine represented by the following formula (2) (hereinafter also referred to as "specific diamine") and an imidized polymer produced by dehydrating and closing the polyamic acid. Achieved by the alignment agent.
    [19] <Formula 1>
    [20]
    [21] (Wherein R 1 is a halogen atom, an alkyl group having 1 to 10 carbon atoms or a fluoroalkyl group having 1 to 10 carbon atoms and a is an integer of 0 to 4)
    [22] <Formula 2>
    [23]
    [24] (Wherein X is a divalent organic group and R 2 is a monovalent organic group having an alicyclic skeleton having 4 to 40 carbon atoms)
    [25] It is preferable that the liquid crystal aligning agent of this invention contains the solvent of the composition which is 20-60 weight% of 1-methyl- 2-pyrrolidone and 80-40 weight% of solvents whose surface tension is 32 dyn / cm or less as a solvent. .
    [26] EMBODIMENT OF THE INVENTION Hereinafter, this invention is demonstrated in detail.
    [27] <Polyamic acid>
    [28] The polyamic acid used by this invention is obtained by ring-opening polyaddition of the specific tetracarboxylic dianhydride represented by the said Formula (1), and the specific diamine represented by the said Formula (2).
    [29] In addition, the imidation polymer used by this invention is obtained by dehydrating and ring-closing the said polyamic acid.
    [30] Tetracarboxylic dianhydride
    [31] The liquid crystal aligning agent of this invention has the performance excellent in low afterimage property and voltage retention characteristic by using the specific tetracarboxylic dianhydride represented by the said General formula (1).
    [32] In Chemical Formula 1, R 1 may be selected from halogen atoms such as F, Cl, and Br; Alkyl groups having 1 to 10 carbon atoms such as methyl group, ethyl group, n-propyl group and i-propyl group; C1-C10 fluoroalkyl groups, such as a trifluoromethyl group, etc. are mentioned. In addition, a is an integer of 0-4.
    [33] As a specific example of specific tetracarboxylic dianhydride, it is 1,2,3,4-cyclobutane tetracarboxylic dianhydride, 1,2-dimethyl-1,2,3,4-cyclobutane tetracarr, for example. Acid dianhydride, 1,3-dimethyl-1,2,3,4-cyclobutanetetracarboxylic dianhydride, 1,3-dichloro-1,2,3,4-cyclobutanetetracarboxylic dianhydride And 1,2,3,4-tetramethyl-1,2,3,4-cyclobutanetetracarboxylic dianhydride and the like. Of these, 1,2,3,4-cyclobutanetetracarboxylic dianhydride and 1,3-dimethyl-1,2,3,4-cyclobutanetetracarboxylic dianhydride are particularly preferably used.
    [34] Other tetracarboxylic dianhydrides may be used in the polyamic acid as long as the effects of the present invention are not impaired. As another tetracarboxylic dianhydride, a butane tetracarboxylic dianhydride, a 1,2,3,4- cyclopentane tetracarboxylic dianhydride, a 1,2,4,5-cyclohexane tetracarboxe, for example Acid dianhydrides, 3,3 ', 4,4'-dicyclohexyltetracarboxylic dianhydride, cis-3,7-dibutylcycloocta-1,5-diene-1,2,5,6- Tetracarboxylic dianhydride, 2,3,5-tricarboxycyclopentylacetic dianhydride, 3,5,6-tricarbonyl-2-carboxynorbornane-2: 3,5: 6- dianhydride, 2 , 3,4,5-tetrahydrofurantetracarboxylic dianhydride, 1,3,3a, 4,5,9b-hexahydro-5 (tetrahydro-2,5-dioxo-3-pranyl)- Naphtho [1,2-c] -furan-1,3-dione, 1,3,3a, 4,5,9b-hexahydro-5-methyl-5 (tetrahydro-2,5-dioxo-3 -Pranyl) -naphtho [1,2-c] -furan-1,3-dione, 1,3,3a, 4,5,9b-hexahydro-5-ethyl-5 (tetrahydro-2,5 -Dioxo-3-pranyl) -naphtho [1,2-c] -furan-1,3-dione, 1,3,3a, 4,5,9b-hexahydro- 7-methyl-5 (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] -furan-1,3-dione, 1,3,3a, 4,5, 9b-hexahydro-7-ethyl-5 (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] -furan-1,3-dione, 1,3,3a , 4,5,9b-hexahydro-8-methyl-5 (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] -furan-1,3-dione, 1,3,3a, 4,5,9b-hexahydro-8-ethyl-5 (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] -furan-1 , 3-dione, 1,3,3a, 4,5,9b-hexahydro-5,8-dimethyl-5 (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2 -c] -furan-1,3-dione, 5- (2,5-dioxotetrahydrofural) -3-methyl-3-cyclohexene-1,2-dicarboxylic dianhydride, bicyclo [2 Aliphatic and alicyclic tetracarboxylic dianhydrides such as 2,2] -octo-7-ene-2,3,5,6-tetracarboxylic dianhydride and compounds represented by the following formulas (3) and (4);
    [35]
    [36]
    [37] (In formula, R <3> and R <5> represents the divalent organic group which has an aromatic ring, R <4> and R <6> represents a hydrogen atom or an alkyl group, and two or more R <4> and R <6> may be same or different, respectively. )
    [38] Pyromellitic dianhydride, 3,3 ', 4,4'-benzophenonetetracarboxylic dianhydride, 3,3', 4,4'-biphenylsulfontetracarboxylic dianhydride, 1,4,5 , 8-naphthalenetetracarboxylic dianhydride, 2,3,6,7-naphthalenetetracarboxylic dianhydride, 3,3 ', 4,4'-biphenylethertetracarboxylic dianhydride, 3,3 ', 4,4'-dimethyldiphenylsilanetetracarboxylic dianhydride, 3,3', 4,4'-tetraphenylsilanetetracarboxylic dianhydride, 1,2,3,4-furantetracarboxylic Acid dianhydrides, 4,4'-bis (3,4-dicarboxyphenoxy) diphenylsulfide dianhydrides, 4,4'-bis (3,4-dicarboxyphenoxy) diphenylsulfone dianhydrides, 4 , 4'-bis (3,4-dicarboxyphenoxy) diphenylpropane dianhydride, 3,3 ', 4,4'-perfluoroisopropylidenediphthalic dianhydride, 3,3', 4,4 '-Biphenyltetracarboxylic dianhydride, bis (phthalic acid) phenylphosphineoxide dianhydride, p-phenylene-bis (triphenylphthalic acid) dianhydride , m-phenylene-bis (triphenylphthalic acid) dianhydride, bis (triphenylphthalic acid) -4,4'-diphenyl ether dianhydride, bis (triphenylphthalic acid) -4,4'-diphenylmethane dianhydride , Ethylene glycol -bis (anhydrotrimelitate), propylene glycol -bis (anhydrotrimelitate), 1,4-butanediol-bis (anhydrotrimelitate), 1,6-hexanediol-bis (an Hydrotrimelitate), 1,8-octanediol-bis (anhydro trimellitate), 2,2-bis (4-hydroxyphenyl) propane-bis (anhydrotrimelitate), the following formulas 5 to 8 Aromatic tetracarboxylic dianhydrides, such as a compound represented by these, are mentioned. These are used individually by 1 type or in combination of 2 or more types.
    [39]
    [40]
    [41]
    [42]
    [43] Of these, butanetetracarboxylic dianhydride, 1,2,3,4-cyclopentanetetracarboxylic dianhydride, 2,3,5-tricarboxycyclopentylacetic dianhydride, 5- (2,5-di Oxotetrahydrofural) -3-methyl-3-cyclohexene-1,2-dicarboxylic dianhydride, cis-3,7-dibutylcycloocta-1,5-diene-1,2,5,6 Tetracarboxylic dianhydride, 3,5,6-tricarbonyl-2-carboxynorbornane-2: 3,5: 6- dianhydride, 1,3,3a, 4,5,9b-hexahydro -5- (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] furan-1,3-dione, 1,3,3a, 4,5,9b-hexa Hydro-8-methyl-5- (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] furan-1,3-dione, 1,3,3a, 4, 5,9b-hexahydro-5,8-dimethyl-5- (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] furan-1,3-dione, ratio Cyclo [2,2,2] -octo-7-ene-2,3,5,6-tetracarboxylic dianhydride, pyromellitic dianhydride, 3,3 ', 4,4'-benzophenonetetracarb Acid dianhydride, 3,3 ', 4,4'-biphenylsulfontetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, the compound represented by the formula (3) It is preferable from a viewpoint that the compound represented by following formula (12) among the compound shown, and the compound represented by the said Formula (12) can express favorable liquid-crystal orientation, Especially preferably, 1,2,3,4-cyclobutane tetra Carboxylic acid dianhydride, 1,3-dimethyl-1,2,3,4-cyclobutanetetracarboxylic dianhydride, 2,3,5-tricarboxycyclopentylacetic dianhydride, 1,3,3a, 4 , 5,9b-hexahydro-5- (tetrahydro-2,5-dioxo-3-pranyl) -naphtho [1,2-c] furan-1,3-dione, cis-3,7- Dibutylcycloocta-1,5-diene-1,2,5,6-tetracarboxylic dianhydride, 3,5,6-tricarbonyl-2-carboxynorbornane-2: 3,5: 6 Dianhydride, 1,3,3a, 4,5,9b-hexahydro-8-methyl-5- (tetrahi -2,5-dioxo-3-plastic carbonyl) - naphtho [1,2-c] furan-1,3-dione, pyromellitic dianhydride and the following may be mentioned compounds represented by the formula (9).
    [44]
    [45]
    [46]
    [47]
    [48] It is preferable that the usage-amount of these other tetracarboxylic dianhydride is 50 mol% or less with respect to all the tetracarboxylic dianhydride.
    [49] <Diamine>
    [50] The liquid crystal aligning agent of this invention has the performance excellent in printability and the vertical alignment property by using the specific diamine represented by the said General formula (2).
    [51] Particular diamine is a compound having a phenylenediamine structure having an alicyclic skeleton having 4 to 40 carbon atoms in the side chain.
    [52] Examples of the alicyclic skeleton having 4 to 40 carbon atoms include alicyclic skeletons derived from cycloalkanes such as cyclobutane, cyclopentane, cyclohexane, and cyclodecane, steroid skeletons such as cholesterol and cholestanol, norbornene skeleton, and adamantane. And burnt skeletons. Among these, the steroid skeleton is particularly preferable. Further, an organic group having an alicyclic skeleton represented by the formula (2) as R 2 but may be substituted by a halogen atom.
    [53] In addition, in Formula 2, as the divalent organic group represented by X, -O-, -COO-, -OCO-, -NHCO-, -CONH-, -CO-, methylene group, alkylene group, phenylene group, etc. Can be mentioned. Among these, especially preferably, it is group represented by -O-, -CO0-, -OCO-.
    [54] As a specific example of specific diamine, the compound represented by following formula (13-18) is mentioned as a preferable thing.
    [55]
    [56]
    [57]
    [58]
    [59]
    [60]
    [61] In the synthesis of the polyamic acid, other diamine compounds may be used in combination so long as the effects of the present invention are not impaired. Other diamine compounds are, for example, p-phenylenediamine, m-phenylenediamine, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylethane, 4,4'-diaminodi Phenylsulfide, 4,4'-diaminodiphenylsulfone, 3,3'-dimethyl-4,4'-diaminobiphenyl, 4,4'-diaminobenzanilide, 4,4'-diaminodi Phenyl ether, 1,5-diaminonaphthalene, 3,3-dimethyl-4,4'-diaminobiphenyl, 5-amino-1- (4'-aminophenyl) -1,3,3-trimethylindan, 6-amino-1- (4'-aminophenyl) -1,3,3-trimethylindane, 3,4'-diaminodiphenylether, 3,3'-diaminobenzophenone, 3,4'-dia Minobenzophenone, 4,4'-diaminobenzophenone, 2,2-bis [4- (4-aminophenoxy) phenyl] propane, 2,2-bis [4- (4-aminophenoxy) phenyl] Hexafluoropropane, 2,2-bis (4-aminophenyl) hexafluoropropane, 2,2-bis [4- (4-aminophenoxy) phenyl] sulfone, 1,4-bis (4-aminophenoxy Benzene, 1,3-bis (4-aminophenoxy) benzene, 1,3-bis (3-a Nophenoxy) benzene, 9,9-bis (4-aminophenyl) -10-hydroanthracene, 2,7-diaminofluorene, 9,9-bis (4-aminophenyl) fluorene, 4,4 ' Methylene-bis (2-chloroaniline), 2,2 ', 5,5'-tetrachloro-4,4'-diaminobiphenyl, 2,2'-dichloro-4,4'-diamino-5 , 5'-dimethoxybiphenyl, 3,3'-dimethoxy-4,4'-diaminobiphenyl, 1,4,4 '-(p-phenyleneisopropylidene) bisaniline, 4,4' -(m-phenyleneisopropylidene) bisaniline, 2,2'-bis [4- (4-amino-2-trifluoromethylphenoxy) phenyl] hexafluoropropane, 4,4'-diamino -2,2'-bis (trifluoromethyl) biphenyl, 4,4'-bis [(4-amino-2-trifluoromethyl) phenoxy] -octafluorobiphenyl, having the formulas 19-21 Aromatic diamines such as a compound to be represented;
    [62]
    [63]
    [64]
    [65] 1,1-methaxylenediamine, 1,3-propanediamine, tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, nonamethylenediamine, 4,4-diaminoheptamethylenediamine, 1 , 4-diaminocyclohexane, isophoronediamine, tetrahydrodicyclopentadienylenediamine, hexahydro-4,7-methanoindenylenedimethylenediamine, tricyclo [6.2.1.O 2,7 ] -undecylene Aliphatic and alicyclic diamines such as dimethyldiamine and 4,4'-methylenebis (cyclohexylamine);
    [66] 2,3-diaminopyridine, 2,6-diaminopyridine, 3,4-diaminopyridine, 2,4-diaminopyrimidine, 5,6-diamino-2,3-dicyanopyrazine, 5, 6-diamino-2,4-dihydroxypyrimidine, 2,4-diamino-6-dimethylamino-1,3,5-triazine, 1,4-bis (3-aminopropyl) piperazine, 2,4-diamino-6-isopropoxy-1,3,5-triazine, 2,4-diamino-6-methoxy-1,3,5-triazine, 2,4-diamino- 6-phenyl-1,3,5-triazine, 2,4-diamino-6-methyl-s-triazine, 2,4-diamino-1,3,5-triazine, 4,6-dia Mino-2-vinyl-s-triazine, 2,4-diamino-5-phenylthiazole, 2,6-diaminopurine, 5,6-diamino-1,3-dimethyluracil, 3,5- Diamino-1,2,4-triazole, 6,9-diamino-2-ethoxyacridine lactate, 3,8-diamino-6-phenylphenanthrizine, 1,4-diaminopiperazine, Two in the molecule, such as 3,6-diaminoacridine, bis (4-aminophenyl) phenylamine, and the compounds represented by the following formulas 22 and 23 Diamines having a primary amino group and a nitrogen atom other than this primary amino group;
    [67]
    [68] (Wherein R 7 represents a monovalent organic group having a ring structure containing a nitrogen atom selected from pyridine, pyrimidine, triazine, piperidine and piperazine, and X represents a divalent organic group)
    [69]
    [70] (Wherein R 8 represents a divalent organic group having a ring structure containing a nitrogen atom selected from pyridine, pyrimidine, triazine, piperidine and piperazine, and X represents a divalent organic group and a plurality of X are present) May be the same or different)
    [71] Diaminoorganosiloxane represented by Formula 24;
    [72]
    [73] (In formula, R <9> represents a C1-C12 hydrocarbon group, two or more R <9> may be same or different, p is an integer of 1-3 and q is an integer of 1-20.)
    [74] The compound represented by following formula (25), (26), etc. are mentioned.
    [75]
    [76]
    [77] (Wherein y is an integer from 2 to 12 and Z is an integer from 1 to 5)
    [78] These diamine compounds can be used individually or in combination of 2 or more types.
    [79] Among them, p-phenylenediamine, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenyl sulfide, 1,5-diaminonaphthalene, 2,7-diaminofluorene, 4 , 4'-diaminodiphenylether, 2,2-bis [4- (4-aminophenoxy) phenyl] propane, 9,9-bis (4-aminophenyl) fluorene, 2,2-bis [4 -(4-aminophenoxy) phenyl] hexafluoropropane, 2,2-bis (4-aminophenyl) hexafluoropropane, 4,4 '-(p-phenylenediisopropylidene) bisaniline, 4, 4 '-(m-phenylenediisopropylidene) bisaniline, 1,4-cyclohexanediamine, 4,4'-methylenebis (cyclohexylamine), 1,4-bis (4-aminophenoxy) benzene, 4,4'-bis (4-aminophenoxy) biphenyl, a compound represented by Formulas 19 to 21, a compound represented by Formulas 25 and 26, 2,6-diaminopyridine, 3,4-diamino Pyridine, 2,4-diaminopyrimidine, 3,6-diaminoacridine, of the compound represented by the formula (22) It is to be displayed in the displayed compound, and the compound formula 23 The compound represented by formula 28 is preferable.
    [80]
    [81]
    [82] The proportion of the specific diamine in the total diamine component in all the polymers included in the liquid crystal aligning agent of the present invention is preferably 10 mol% or more, more preferably 20 mol% or more based on the total amount of the diamine component. When this use ratio is less than 10 mol%, the effect sufficient for vertical alignment may not be acquired in some cases.
    [83] Synthesis of Polyamic Acid
    [84] The use ratio of the tetracarboxylic dianhydride and the diamine provided in the polyamic acid synthesis reaction is preferably a ratio in which the acid anhydride group of the tetracarboxylic dianhydride is 0.2 to 2 equivalents relative to 1 equivalent of the amino group of the diamine. Preferably it is the ratio which becomes 0.3 to 1.2 equivalent.
    [85] The synthesis reaction of the polyamic acid is usually carried out in an organic solvent under a temperature condition of -120 ° C to 150 ° C, preferably 0 to 100 ° C. The organic solvent is not particularly limited as long as it can dissolve the polyamic acid synthesized. For example, 1-methyl-2-pyrrolidone, N, N-dimethylacetamide, N, N-dimethylformamide, Aprotic polar solvents, such as dimethyl sulfoxide, (gamma) -butyrolactone, tetramethyl urea, and hexamethyl phosphotriamide, phenol solvents, such as m-cresol, xylenol, a phenol, and a halogenated phenol, can be illustrated. In addition, it is preferable that the usage-amount of (alpha) of an organic solvent is an amount which normally makes the total amount (beta) of tetracarboxylic dianhydride and a diamine compound become 0.1-30 weight% with respect to the total amount ((alpha) + (beta)) of a reaction solution.
    [86] In the organic solvent, alcohols, ketones, esters, ethers, halogenated hydrocarbons, hydrocarbons, and the like, which are poor solvents of polyamic acid, can be used in combination without causing precipitation of the resulting polyamic acid. As a specific example of such a poor solvent, for example, methyl alcohol, ethyl alcohol, isopropyl alcohol, cyclohexanol, 4-hydroxy-4-methyl-2-pentanone, ethylene glycol, propylene glycol, 1,4- Butanediol, triethylene glycol, ethylene glycol monomethyl ether, ethyl lactate, butyl lactate, acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, methyl acetate, ethyl acetate, butyl acetate, methyl methoxy propionate, ethyl Ethoxypropionate, diethyl oxalate, diethyl malonate, diethyl ether, ethylene glycol methyl ether, ethylene glycol ethyl ether, ethylene glycol-n-propyl ether, ethylene glycol-i-propyl ether, ethylene glycol-n-butyl Ether, ethylene glycol dimethyl ether, ethylene glycol ethyl ether acetate, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol monomethyl ether , Diethylene glycol monoethyl ether, diethylene glycol monomethyl ether acetate, diethylene glycol monoethyl ether acetate, tetrahydrofuran, dichloromethane, 1,2-dichloroethane, 1,4-dichlorobutane, trichloroethane, chloro Benzene, o-dichlorobenzene, hexane, heptane, octane, benzene, toluene, xylene and the like.
    [87] As described above, a reaction solution in which the polyamic acid is dissolved is obtained. The reaction solution is poured into a large amount of poor solvent to obtain a precipitate, and the polyamic acid can be obtained by drying the precipitate under reduced pressure. In addition, the polyamic acid can be purified by dissolving the polyamic acid again in an organic solvent and then precipitating with a poor solvent once or several times.
    [88] <Synthesis of imidized polymer>
    [89] The imidation polymer which comprises the liquid crystal aligning agent of this invention can be synthesize | combined by dehydrating and ring-closing the said polyamic acid. The dehydration ring closure of the polyamic acid may be carried out by (i) a method of heating the polyamic acid or (ii) dissolving the polyamic acid in an organic solvent, adding a dehydrating agent and a dehydration ring closure catalyst to the solution, and heating it as necessary. Is done. In the imidized polymer used in the present invention, the imidized polymer having a partial dehydration ring closure and an imidization ratio (in which the ratio of the repeating units in which the imide ring is formed in all the repeating units in the polymer in%) is less than 100%. May be included.
    [90] The reaction temperature in the method of heating the polyamic acid of said (i) is 50-200 degreeC normally, Preferably it is 60-170 degreeC. When reaction temperature is less than 50 degreeC, dehydration ring-closure reaction does not fully advance, and when reaction temperature exceeds 200 degreeC, the molecular weight of the polyimide (B) obtained may fall.
    [91] On the other hand, in the method of adding a dehydrating agent and a dehydration ring-closure catalyst to the polyamic-acid solution of said (ii), acid anhydrides, such as acetic anhydride, a propionic anhydride, and trifluoroacetic anhydride, can be used as a dehydrating agent, for example. Although the usage-amount of a dehydrating agent is based on the target imidation ratio, it is preferable to set it as 0.01-20 mol per mol of repeating units of a polyamic acid normally. As the dehydration ring closure catalyst, tertiary amines such as pyridine, collidine, lutidine and triethylamine can be used, for example. However, it is not limited to these. It is preferable that the usage-amount of a dehydration ring-closure catalyst shall be 0.01-10 mol per mol of dehydrating agents used. The imidation ratio can be made higher as there are many dehydrating agents and dehydrating ring closure agents mentioned above. The imidation ratio is preferably 70% or less from the viewpoint of printability. Moreover, the organic solvent illustrated as what is used for the synthesis | combination of a polyamic acid as an organic solvent used for a dehydration ring-closure reaction is mentioned. And the reaction temperature of a dehydration ring-closure reaction is 0-180 degreeC normally, Preferably it is 10-150 degreeC. Moreover, the imidation polymer can be refine | purified by performing the same operation as the purification method of polyamic acid with respect to the reaction solution obtained in this way.
    [92] <Terminal modified polymer>
    [93] The polyamic acid and the imidized polymer may be terminal modified with controlled molecular weight. By using this terminal modified polymer, the coating characteristic of a liquid crystal aligning agent, etc. can be improved, without impairing the effect of this invention. Such terminal-modified type can be synthesized by adding an acid anhydride, a monoamine compound, a monoisocyanate compound, or the like to the reaction system when synthesizing the polyamic acid. Here, as an acid anhydride, maleic anhydride, phthalic anhydride, itaconic anhydride, n-decyl succinic anhydride, n-dodecyl succinic anhydride, n- tetradecyl succinic anhydride, n-hexadecyl succinic anhydride, etc. are mentioned, for example. I can lift it. As the monoamine compound, for example, aniline, cyclohexylamine, n-butylamine, n-pentylamine, n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, n-decyl Amines, n-undecylamine, n-dodecylamine, n-tridecylamine, n-tetradecylamine, n-pentadecylamine, n-hexadecylamine, n-heptadecylamine, n-octadecylamine, n-eicosylamine etc. are mentioned. Moreover, as a monoisocyanate compound, phenyl isocyanate, naphthyl isocyanate, etc. are mentioned, for example.
    [94] Logarithmic viscosity of the polymer
    [95] The value of the logarithmic viscosity ((eta) ln) of the polyamic acid and imidation polymer obtained as mentioned above is preferably 0.05-10 dl / g, More preferably, it is 0.05-5 dl / g.
    [96] The value of the logarithmic viscosity (ηln) in this invention uses N-methyl- 2-pyrrolidone as a solvent, the viscosity is measured at 30 degreeC with respect to the solution whose density | concentration is 0.5 g / 100 milliliter, and is represented by the following formula Obtained by 1.
    [97]
    [98] <Liquid crystal aligning agent>
    [99] The said polyamic acid and / or the imidation polymer dissolve and contain normally the liquid crystal aligning agent of this invention, and are comprised.
    [100] The temperature at the time of preparing the liquid crystal aligning agent of this invention is 0 degreeC-200 degreeC normally, Preferably it is 20 degreeC-60 degreeC.
    [101] As an organic solvent which comprises the liquid crystal aligning agent of this invention, the solvent illustrated as what is used for the synthesis reaction of polyamic acid is mentioned. Moreover, the poor solvent illustrated as what can be used together at the time of the synthesis reaction of polyamic acid can also be selected suitably, and can be used together. Among these, it is preferable to use 1-methyl-2-pyrrolidone and the solvent whose surface tension is 32 dyn / cm or less. Examples of the solvent having a surface tension of 32 dyn / cm or less include 4-hydroxy-4-methyl-2-pentanone, ethylene glycol monomethyl ether, butyl lactate, butyl acetate, methyl methoxy propionate, and ethyl ethoxy. Propionate, ethylene glycol methyl ether, ethylene glycol ethyl ether, ethylene glycol-n-propyl ether, ethylene glycol-i-propyl ether, ethylene glycol-n-butyl ether (butyl cellosolve), ethylene glycol dimethyl ether, ethylene Glycol ethyl ether acetate, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monomethyl ether acetate, diethylene glycol monoethyl ether acetate, and the like. Can be.
    [102] The ratio of 1-methyl-2-pyrrolidone and a solvent having a surface tension of 32 dyn / cm or less is 20 to 60 wt% of 1-methyl-2-pyrrolidone and a solvent having a surface tension of 32 dyn / cm or less is 80 to It is preferable that it is 40 weight%. If it is out of the range of this ratio, sufficient printability cannot be obtained because precipitation of a polymer occurs or leveling becomes insufficient.
    [103] Solid content concentration in the liquid crystal aligning agent of this invention is selected in consideration of viscosity, volatility, etc., Preferably it is the range of 1 to 10 weight%. That is, although the liquid crystal aligning agent of this invention is apply | coated to the surface of a board | substrate, and the coating film which becomes a liquid crystal aligning film is formed, when solid content concentration is less than 1 weight%, the film thickness of this coating film becomes too thin and a favorable liquid crystal aligning film cannot be obtained, solid content When the concentration exceeds 10% by weight, the film thickness of the coating film becomes so thick that a good liquid crystal aligning film cannot be obtained, and the viscosity of the liquid crystal aligning agent is increased to reduce the coating properties.
    [104] A functional silane containing compound and an epoxy compound may be contained in the liquid crystal aligning agent of this invention from a viewpoint of improving the adhesiveness to the surface of a board | substrate within the range which does not impair a desired physical property. As such a functional silane containing compound, 3-aminopropyl trimethoxysilane, 3-aminopropyl triethoxysilane, 2-aminopropyl trimethoxysilane, 2-aminopropyl triethoxysilane, N- (2-aminoethyl) -3-aminopropyltrimethoxysilane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, 3-ureidopropyltrimethoxysilane, 3-ureidopropyltree Ethoxysilane, N-ethoxycarbonyl-3-aminopropyltrimethoxysilane, N-ethoxycarbonyl-3-aminopropyltriethoxysilane, N-triethoxysilylpropyltriethylenetriamine, N- Trimethoxysilylpropyltriethylenetriamine, 10-trimethoxysilyl-1,4,7-triazadecan, 10-triethoxysilyl-1,4,7-triazadecan, 9-trimethoxysilyl -3,6-diazanyl acetate, 9-triethoxysilyl-3,6-diazanyl acetate, N-benzyl-3-aminopropyltrimethoxysilane, N-benzyl -3-aminopropyltriethoxysilane, N-phenyl-3-aminopropyltrimethoxysilane, N-phenyl-3-aminopropyltriethoxysilane, N-bis (oxyethylene) -3-aminopropyltrimeth Oxysilane, N-bis (oxyethylene) -3-aminopropyltriethoxysilane, etc. are mentioned. Examples of such epoxy group-containing compounds include ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, tripropylene glycol diglycidyl ether, and polypropylene glycol diglycidyl. Ether, neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, glycerin diglycidyl ether, 2,2-dibromoneopentyl glycol diglycidyl ether, 1,3, 5,6-tetraglycidyl-2,4-hexanediol, N, N, N ', N'-tetraglycidyl-m-xylenediamine, 1,3-bis (N, N-diglycidyl Aminomethyl) cyclohexane, N, N, N ', N'-tetraglycidyl-4,4'-diaminodiphenylmethane, 3- (N-allyl-N-glycidyl) aminopropyltrimethoxy Silane, 3- (N, N-diglycidyl) aminopropyltrimethoxysilane, and the like.
    [105] <Liquid crystal display element>
    [106] The liquid crystal display element obtained using the liquid crystal aligning agent of this invention can be manufactured, for example by the following method.
    [107] (1) The liquid crystal aligning agent of this invention is apply | coated to the one side of the board | substrate with which the patterned transparent conductive film is provided by methods, such as a roll coater method, a spinner method, and a printing method, and a coating film is then heated by heating a coating surface. Form. Here, as a board | substrate, the transparent substrate which consists of plastics, such as glass, such as float glass and a soda glass, polyethylene terephthalate, a polybutyrene terephthalate, polyether sulfone, polycarbonate, can be used. As a transparent conductive film provided on one surface of the substrate, an NESA film (registered trademark of PPG Co., Ltd.) made of tin oxide (SnO 2 ), an ITO film made of indium tin oxide (In 2 O 3 -SnO 2 ), or the like can be used. The transparent conductive film can be patterned by a photo-etching method or a method using a preliminary mask. In application | coating of a liquid crystal aligning agent, in order to make adhesiveness of a board | substrate surface, a transparent conductive film, and a coating film further favorable, you may apply | coat a functional silane containing compound, a functional titanium containing compound, etc. previously on a board | substrate surface. The heating temperature after apply | coating a liquid crystal aligning agent is 80-300 degreeC, Preferably it is 120-250 degreeC. In addition, the liquid crystal aligning agent of this invention containing a polyamic acid can form the coating film used as an oriented film by removing an organic solvent after application | coating, or it can further dehydrate ring closure by advancing and it can be set as the coating film more imidized. The film thickness of the coating film formed is normally 0.01-1 micrometer, Preferably it is 0.005-0.5 micrometer.
    [108] (2) The rubbing process which rubs the formed coating film surface in the fixed direction with the roll which wound the cloth which consists of fibers, such as nylon, a rayon, a cotton, for example, is performed. Thereby, the orientation ability of a liquid crystal molecule is provided to a coating film, and it becomes a liquid crystal aligning film.
    [109] Moreover, the ultraviolet-ray partially irradiates the liquid crystal aligning film formed by the liquid crystal aligning agent of this invention, for example as disclosed in Unexamined-Japanese-Patent No. 6-222366 or 6-281937. Process to change the pretilt angle or a method of forming an electrode in the same plane as described in "IDW ''97 P 175" (IPS method), or Japanese Patent Application Laid-Open No. 5-107544 As described above, the resist film is partially formed on the surface of the liquid crystal alignment film subjected to the rubbing treatment, the rubbing treatment is performed in a direction different from that of the preceding rubbing treatment, and then the resist film is removed and the liquid crystal aligning ability of the liquid crystal alignment film is changed. Can improve the watch characteristics.
    [110] (3) Two board | substrates with a liquid crystal aligning film were produced as mentioned above, and two board | substrates were opposingly arranged with a clearance gap (cell gap) so that the rubbing direction in each liquid crystal aligning film may be orthogonal or antiparallel, The peripheral part of two board | substrates is bonded together using a bonding agent, a liquid crystal is injected-filled in the cell gap partitioned by the board | substrate surface and the bonding agent, and an injection hole is sealed and a liquid crystal cell is comprised. And the liquid crystal display element is bonded by bonding a polarizing plate to the outer surface of the liquid crystal cell, ie, the other surface side of each board | substrate which comprises a liquid crystal cell so that a polarization direction may correspond with or perpendicular to the rubbing direction of the liquid crystal aligning film formed in one side of the said board | substrate. Obtained.
    [111] As the bonding agent, for example, an epoxy resin or the like containing an aluminum oxide sphere as a curing agent and a spacer can be used.
    [112] Examples of the liquid crystals include nematic liquid crystals and smectic liquid crystals. Among them, nematic liquid crystals are preferred, and for example, Schiffbase liquid crystals, subfamily clock liquid crystals, biphenyl liquid crystals, phenylcyclohexane liquid crystals and ester liquid crystals. , Terphenyl-based liquid crystal, biphenylcyclohexane-based liquid crystal, pyrimidine-based liquid crystal, dioxane-based liquid crystal, bicyclooctane-based liquid crystal, cuban-based liquid crystal and the like can be used. Moreover, it sells to such liquid crystals as cholesteric liquid crystals, such as cholesteryl chloride, cholesteryl nonaate, cholesteryl carbonate, or brand name "C-15" "CB-15" (made by Merck). The chiral agent etc. which are being used can also be added and used. In addition, ferroelectric liquid crystals such as p-decyloxybenzylidene-p-amino-2-methylbutylcinnamate can also be used.
    [113] Moreover, as a polarizing plate joined to the outer surface of a liquid crystal cell, the polarizing plate which consists of a cellulose acetate protective film or the polarizing plate which made the polarizing film called H film which absorbed iodine into the cellulose acetate, while extending | stretching polyvinyl alcohol is mentioned.
    [114] In addition, the liquid crystal aligning agent of this invention can be used suitably for the liquid crystal display element of MVA (Multi-domein vertical alingnment) system. The MVA system refers to a vertical alignment mode using projections as an orientation regulating means, as shown in "liquid crystal Vol. 3 No. 2 117 (1999)" or Japanese Patent Application Laid-open No. 11-258605. The protrusions may be formed on each of the TFT substrate side and the color filter side, may have protrusions on the color filter side, and may have slits on the TFT side.
    [115] <Example>
    [116] Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited to these Examples.
    [117] <Imidation Rate of Polymer>
    [118] After drying the polymer under reduced pressure at room temperature, it was dissolved in deuterated dimethyl sulfoxide, and 1 H-NMR was measured at room temperature using tetramethylsilane as a reference material to obtain a formula represented by the following formula (2).
    [119]
    [120] A 1 : peak area (10 ppm) derived from proton of NH group
    [121] A 2 : peak area derived from other protons
    [122] α: ratio of the number of other protons to one proton of the NH group in the precursor (polyamic acid) of the polymer
    [123] <Printability>
    [124] The board | substrate after post-baking was printed using the Nissha Angstrommer (made by Nippon Shashin Insatsu), and the microscope was observed.
    [125] ○ no print unevenness
    [126] In print stains ×
    [127] <Method of Manufacturing Liquid Crystal Display Element>
    [128] Fabrication of the liquid crystal display device 1:
    [129] On the transparent conductive film which consists of an ITO film | membrane provided on one surface of the glass substrate of thickness 1mm, a liquid crystal aligning agent is apply | coated using a spinner, it dried for 1 minute at 80 degreeC, and then dried at 180 degreeC for 1 hour, and dried film thickness 600 The coating film of VII was formed.
    [130] Subsequently, the rubbing process was performed using the rubbing machine which has the roll which wound the cloth made of rayon, and the orientation ability of liquid crystal molecule was provided to the said thin film, and the liquid crystal aligning film was formed. Here, the rubbing treatment conditions were set to the rotational speed of 400 rpm, the stage moving speed of 30 mm / sec, and the hair indentation length of 0.4 mm.
    [131] Two board | substrates with a liquid crystal aligning film were produced as mentioned above, the epoxy resin adhesive containing an aluminum oxide sphere was apply | coated to each board | substrate outer edge by the screen printing method, and two board | substrates were rubbed through a clearance gap. Opposite arrangements were made so as to be reversed, and the outer edge portions were contacted and pressed to cure the adhesive.
    [132] The negative nematic liquid crystal is injected and filled into the cell gap partitioned by the adhesive on the surface of the substrate and the outer edge, and then the injection hole is sealed with an epoxy adhesive to align the vertically aligned liquid crystal display device (hereinafter referred to as "liquid crystal display device 1). "Is produced".
    [133] Fabrication of the liquid crystal display device 2:
    [134] As shown in FIG. 1, the liquid crystal aligning agent is printed on the glass substrate (A) with ITO which has the processus | protrusion formed using the positive type resist, and the glass substrate (B) which has the pattern of ITO, respectively, and it is 80 minutes at 1 degreeC. After that, the film was dried at 180 ° C. for 1 hour to form a coating film having a dry film thickness of 600 kPa.
    [135] As described above, two substrates on which a liquid crystal alignment film was formed were prepared, and an epoxy resin adhesive containing aluminum oxide spheres having a particle size of 3.5 μm was applied to the outer edge portion of the substrate B by screen printing. Two substrates were bonded together so that a positional relationship might exist.
    [136] A negative liquid crystal MLC6608 made by Merck is filled into the cell gap partitioned by the adhesive on the surface of the substrate and the outer edge, and then the injection hole is sealed with an epoxy adhesive to align the vertically aligned liquid crystal display device (hereinafter referred to as "liquid crystal display device ( 2) ").
    [137] <Pretilt angle>
    [138] The pretilt angle was computed from the shift | offset | difference of the retardation symmetry angle of a liquid crystal at 25 degreeC by Chuo Seiki Co., Ltd. OMS-J3.
    [139] <Voltage retention of liquid crystal display element>
    [140] After a voltage of 5 V was applied to the liquid crystal display element at an application time of 60 microseconds and at intervals of 167 milliseconds, the voltage retention after 167 milliseconds from the release of the application was measured. The measurement apparatus used VHR-1 by Toyo Technica Co., Ltd.
    [141] Residual DC Voltage
    [142] A 30 Hz, 2.0 V square wave superimposed on a liquid crystal display element at 1.0 V is applied at an ambient temperature of 70 ° C. for 1 hour, and the residual voltage in the liquid crystal cell is measured by the flicker elimination method immediately after the DC voltage is cut off. The residual DC voltage was obtained.
    [143] <Synthesis Examples 1, 2, 4, 5, Comparative Synthesis Examples 1 and 2>
    [144] To 450 g of 1-methyl-2-pyrrolidone as a monomer shown in Table 1, diamine and tetracarboxylic dianhydride were added in the order of 20% by weight, and reacted at room temperature for 4 hours to obtain a polyamic acid.
    [145] Synthesis Example 3
    [146] 1-methyl-2-pyrrolidone was added to the polyamic acid obtained in Synthesis Example 2 to obtain a solid concentration of 5% by weight, and then a catalyst was added in the composition shown in Table 1, and the dehydration ring closure reaction was performed at 80 ° C. for 4 hours. Was performed. Subsequently, this reaction solution was poured into diethyl ether, and the precipitate was recovered and dried to obtain an imidization polymer having an imidization ratio of 20%.
    [147] Synthesis ExampleMonomer (mol%)Logarithmic viscosity (dl / g)Imidization catalystImidization rate (%) Acid anhydrideDiaminePyridine anhydride OneCB (100)PDA (50) Diamine (50) of Formula 130.89none0 2CB (80) DMCB (20)PDA (75) Diamine (25) of Formula 130.76none0 3CB (80) DMCB (20)PDA (75) Diamine (25) of Formula 130.761.0 / 1.020 4CB (80) DMCB (20)PDA (75) Diamine (25)0.70none0 5CB (80) DMCB (20)Diamine (100) of Formula 130.65none0 Comparative Synthesis Example 1DSDA (100)PDA (95) Diamine (5) of Formula 131.09none0 2CB (100)PDA (50) n-octadecyloxy-1,4-diaminobenzene (50)0.71none0 CB: 1,2,3,4-cyclobutanetetracarboxylic dianhydride DMCB: 1,3-dimethyl-1,2,3,4-cyclobutanetetracarboxylic dianhydride PDA: p-phenylenediamine DSDA : Diphenyl sulfontetracarboxylic dianhydride
    [148] <Examples 1 to 5 and Comparative Examples 1 to 2>
    [149] It melt | dissolved in the solvent shown in Table 2 using the polymer obtained by the synthesis example, and was filter-aided with a 1 micrometer filter to obtain the liquid crystal aligning agent. The liquid crystal display element 1 was produced using this liquid crystal aligning agent. The evaluation result of this liquid crystal aligning agent and a liquid crystal display element was shown together in Table 2.
    [150] ExamplepolymerSolvent (% by weight)PrintabilityPretilt angle (°)Voltage retention rate (%)Residual DC (mV) OneSynthesis Example 11-methyl-2-pyrrolidone (50) butylcellosolve (50)O89.598.320 2Synthesis Example 21-methyl-2-pyrrolidone (50) butylcellosolve (50)O89.598.520 3Synthesis Example 31-methyl-2-pyrrolidone (60) butylcellosolve (40)O89.798.610 4Synthesis Example 41-methyl-2-pyrrolidone (50) butylcellosolve (50)O89.498.820 5Synthesis Example 51-Methyl-2-pyrrolidone (30) butylcellosolve (70)O89.896.530 Comparative Example 1Comparative Synthesis Example 11-methyl-2-pyrrolidone (50) butylcellosolve (50)O79.379.0100 2Comparative Synthesis Example 21-methyl-2-pyrrolidone (50) butylcellosolve (50)×89.698.020
    [151] <Examples 6 to 10, Comparative Example 3>
    [152] It melt | dissolved in the solvent shown in Table 3 using the polymer obtained by the synthesis example, and was filter-prepared with the filter of 1 micrometer, and the liquid crystal aligning agent was obtained. The liquid crystal display element 2 was produced using this liquid crystal aligning agent. The evaluation result of this liquid crystal aligning agent and a liquid crystal display element was shown in Table 3 together.
    [153] ExamplepolymerSolvent (% by weight)Voltage retention rate (%)Residual DC (mV) 6Synthesis Example 11-methyl-2-pyrrolidone (50) butylcellosolve (50)98.130 7Synthesis Example 21-methyl-2-pyrrolidone (50) butylcellosolve (50)98.330 8Synthesis Example 31-methyl-2-pyrrolidone (60) butylcellosolve (40)98.420 9Synthesis Example 41-methyl-2-pyrrolidone (50) butylcellosolve (50)98.640 10Synthesis Example 51-Methyl-2-pyrrolidone (30) butylcellosolve (70)96.260 Comparative Example 3Synthesis Example 61-methyl-2-pyrrolidone (50) butylcellosolve (50)97.8190
    [154] According to the present invention, a liquid crystal aligning agent suitable for a vertically oriented liquid crystal display element capable of forming a liquid crystal aligning film excellent in the vertical alignment of liquid crystals and excellent in high voltage retention, low afterimage, and printability when used as a liquid crystal aligning film is provided. I can provide it.
    权利要求:
    Claims (3)
    [1" claim-type="Currently amended] (A) Tetracarboxylic dianhydride represented by the following formula (1)
    (B) The liquid crystal aligning agent containing the polyamic acid produced | generated by reacting the diamine represented by following formula (2), and the imidation polymer produced | generated by dehydrating and ring-closing this polyamic acid.
    <Formula 1>

    (Wherein R 1 is a halogen atom, an alkyl group having 1 to 10 carbon atoms or a fluoroalkyl group having 1 to 10 carbon atoms and a is an integer of 0 to 4)
    <Formula 2>

    (Wherein X is a divalent organic group and R 2 is a monovalent organic group having an alicyclic skeleton having 4 to 40 carbon atoms)
    [2" claim-type="Currently amended] The liquid crystal aligning agent of Claim 1 which further contains the solvent which consists of 20-60 weight% of 1-methyl- 2-pyrrolidone and 80-40 weight% of other solvents whose surface tension is 32 dyn / cm or less.
    [3" claim-type="Currently amended] The liquid crystal aligning agent of Claim 1 used for a vertically-aligned liquid crystal display element.
    类似技术:
    公开号 | 公开日 | 专利标题
    JP5668904B2|2015-02-12|Liquid crystal aligning agent and liquid crystal display element
    KR100852578B1|2008-08-18|Vertical Liquid Crystal Aligning Agent and Vertical Liquid Crystal Display Having a Repeller
    KR100942883B1|2010-02-17|Liquid crystal alignment agent
    DE69732949T2|2006-02-23|Liquid crystal alignment agent
    JP4844721B2|2011-12-28|Liquid crystal alignment agent, liquid crystal alignment film, and liquid crystal display element
    KR101481834B1|2015-01-12|Liquid crystal aligning agent and liquid crystal display device
    JP5273357B2|2013-08-28|Liquid crystal aligning agent and liquid crystal display element
    KR100798245B1|2008-01-24|Materials for Aligning Liquid Crystals and Liquid Crystal Display Apparatus
    JP3613421B2|2005-01-26|Liquid crystal alignment agent
    KR100834801B1|2008-06-05|Vertical liquid crystal alignment agent and vertical liquid crystal display
    JP4525906B2|2010-08-18|Liquid crystal aligning agent and liquid crystal display element
    JP4344935B2|2009-10-14|Liquid crystal aligning agent and liquid crystal display element
    KR100803507B1|2008-02-14|Vertical Alignment Type Liquid Crystal Aligning Agent and Liquid Crystal Display Device Using the Same
    JP4900560B2|2012-03-21|Novel diamine compound, polymer and liquid crystal aligning agent
    JP4645823B2|2011-03-09|Vertical liquid crystal aligning agent and vertical liquid crystal display element
    KR100850242B1|2008-08-04|Liquid crystal aligning agent, liquid crystal aligning film and liquid crystal display device
    JP4788896B2|2011-10-05|Vertical alignment type liquid crystal aligning agent and vertical alignment type liquid crystal display element
    KR100871780B1|2008-12-05|Liquid Crystal Aligning Agent for Horizontal Electric-field Type Liquid Crystal Display Device, and Horizontal Electric-field Type Liquid Crystal Display Device
    JP5041163B2|2012-10-03|Liquid crystal aligning agent and liquid crystal display element
    KR100794075B1|2008-01-10|Liquid crystal aligning agent and liquid crystal display device
    JP5296135B2|2013-09-25|Process for producing treated polymer for liquid crystal aligning agent, treated polymer and liquid crystal aligning agent produced thereby, liquid crystal aligning film, and liquid crystal display device comprising the aligning film
    JP5120047B2|2013-01-16|Vertical alignment type liquid crystal aligning agent and liquid crystal display element
    JP3206401B2|2001-09-10|Liquid crystal alignment agent and liquid crystal display device
    KR100841868B1|2008-06-27|Liquid Crystal Aligning Agent and Liquid Crystal Display Device
    JP5077048B2|2012-11-21|Vertical alignment type liquid crystal alignment agent
    同族专利:
    公开号 | 公开日
    JP2001311080A|2001-11-09|
    KR100773684B1|2007-11-05|
    TWI299057B|2008-07-21|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2000-04-28|Priority to JP2000-129346
    2000-04-28|Priority to JP2000129346A
    2001-04-27|Application filed by 마쯔모또 에이찌, 제이에스알 가부시끼가이샤
    2001-11-08|Publication of KR20010098921A
    2007-11-05|Application granted
    2007-11-05|Publication of KR100773684B1
    优先权:
    申请号 | 申请日 | 专利标题
    JP2000-129346|2000-04-28|
    JP2000129346A|JP2001311080A|2000-04-28|2000-04-28|Agent for orienting liquid crystal|
    [返回顶部]