    • 专利摘要:
    The stamping foil of the present invention is a stamping foil in which a release layer, a colored layer, a metal deposition layer, and an adhesive layer are sequentially formed on a base film, wherein the colored layer is 20 to 90% by weight of melamine based on isocyanate and isocyanate. It is formed by applying a composition for forming a colored layer comprising a resin and 5 to 20% by weight of 1,4-butanediol on the release layer and then curing, and the change in cutting properties with time is substantially changed. It is excellent in heat resistance and excellent in bonding strength between the colored layer and the metal deposition layer.
    公开号:KR19990030664A
    申请号:KR1019970050975
    申请日:1997-10-02
    公开日:1999-05-06
    发明作者:나용훈；이상국
    申请人:장용균；에스케이씨 주식회사；
    IPC主号:
    专利说明:

    Stamping foil
    The present invention relates to a stamping foil, and more particularly, to a hot stamping foil having excellent heat resistance and excellent bonding strength between a colored layer and a metal deposition layer.
    Stamping foil is used for hot stamping process, a kind of dry printing method, and hot stamping process applies heated platen to transfer objects such as plastic, fiber, leather, etc. It is a process about a kind of heat printing method of pasting.
    Therefore, stamping foils are usually transferred by heat and pressure, and are roughly classified into paper, plastic, fiber, leather, and the like depending on the object to be transferred.
    A typical stamping foil has a structure in which a release layer, a coloring layer (or protective layer), a metal deposition layer (or an aluminum layer) and an adhesive layer are sequentially formed on a base film, and the components, composition and thickness of each layer are It may vary depending on the application used.
    As a general requirement for such stamping foil to be preferably used in a hot stamping process, first, it must have gloss, wear resistance and chemical resistance, and second, heat resistance to withstand high temperature heat and compression process after the adhesive liquid application process. Third, in the process of transferring the desired pattern to the transfer object (paper, fiber, leather, etc.) and separating the base film and the release layer, the bonding force between these layers should be good so that the colored layer does not separate from the metal deposition layer. On the other hand, the base film and the release layer should have a peel force suitable for the intended use in order to facilitate separation, and in addition, the solvent resistance should be good.
    Since the colored layer includes a pattern to be specifically transferred, various physical properties, particularly heat resistance, solvent resistance, and abrasion resistance, should be maintained at appropriate levels so that the pattern does not change during or after the transfer.
    In general, the colored layer is formed by coating a coloring composition on a release layer and then curing. The curing process proceeds simultaneously with the process of drying the composition. Here, it is necessary to reduce the drying time in order to speed up the formation of the colored layer. Reducing the drying time may result in insufficient curing reaction, which makes it difficult to form a colored layer having excellent heat resistance. In addition, in the case of the polyurethane resin generally used as the colored layer material, the isocyanate remains unreacted due to insufficient curing reaction. Therefore, due to the functional group -NCO of isocyanate, it is difficult to transfer small letters or patterns as the stamping foil's physical properties, in particular, cutting properties are reduced during long term storage of the stamping foil. In addition, since the dye used in the colored layer is usually a low molecular weight and lacks the bonding strength with the metal deposition layer, when the amount of the dye must be used in a large amount, the bonding strength between the metal deposition layer and the colored layer is further reduced. There is.
    The technical problem to be achieved by the present invention is to minimize the number of functional groups of the unreacted isocyanate when forming a colored layer using a polyurethane resin to minimize the reduction in cutting properties while using a large amount of dye layer and metal It is to provide a stamping foil having excellent bonding strength with the deposition layer.
    Technical problem of the present invention is a stamping foil in which a release layer, a coloring layer, a metal deposition layer, and an adhesive layer are sequentially formed on a base film, wherein the colored layer is 20 to 90% by weight of melamine based on the isocyanate and the isocyanate. A stamping foil is provided, which is formed by applying a composition for forming a colored layer comprising a resin and 5-20% by weight of 1,4-butanediol on the release layer and then curing.
    The principle of the present invention is based on the use of a melamine resin having an imino group as a material having a low molecular weight and rapidly reacting with an isocyanate among the substances capable of reacting with the isocyanate in the colored layer-forming composition. That is, melamine resin was used as an amino resin having an imino group, but the imino group and the isocyanate of the melamine resin react sufficiently at room temperature, leaving little unreacted isocyanate. In addition, melamine resins combined with isocyanates cause self-hardening during drying due to the inherent reaction mechanism of the melamine resins. As a result, high heat resistance due to the polyurethane reaction and solvent resistance due to the reaction of the melamine resin can be obtained at the same time, and since physical properties do not change over time, it is advantageous for long-term storage.
    As the melamine resin that can be used, one having an imino group may be used, but melamine-formaldehyde resin is preferably used.
    Melamine resin is preferably used 20 to 90% by weight relative to the isocyanate, when using more than 90% by weight is reduced the bonding strength between the colored layer and the metal deposition layer, when used less than 20% by weight This is because the additive effect does not reach the desired level.
    In addition, 1,4-butanediol added to the composition for forming a colored layer may react with isocyanate at room temperature, thereby further reducing the unreacted isocyanate, and at the same time reacting with the isocyanate-melamine resin binder. Therefore, since it promotes a curing reaction, the bonding force between a colored layer and a metal deposition layer is improved. However, when the addition amount of 1,4-butanediol increases, cutting property is inferior, and it is preferable to make the addition amount into 5 to 20 weight% with respect to an isocyanate. In addition, when a large amount of dye is to be used, the cutting property is increased by the dye itself. Therefore, even if the amount of 1,4-butanediol is increased to 20% by weight relative to the isocyanate, there is no problem in the cutting property.
    Hereinafter, although an Example and a comparative example are given and this invention is demonstrated in detail, this invention is not limited to this.
    <Example 1>
    After forming a release layer on a polyester film having a thickness of 12 μm, a composition for forming a colored layer having the following composition was applied and dried at 180 ° C. to form a colored layer (coated dry weight: 1.2 g / m 2 ). .
    10% by weight of isocyanates (TR-50)
    6% by weight of melamine-formaldehyde resin
    1,4-butanediol 1% by weight
    Methyl ethyl ketone 40 wt%
    35% by weight of cyclohexanone
    Dye (Blue 606, Kelly company) 8% by weight
    Aluminum was vacuum deposited on the colored layer to form a metal deposition layer having a thickness of 0.02 μm, and finally, 40% by weight of the acrylic resin and 60% by weight of the mixed resin of vinyl resin were diluted with thaliol. The stamping foil was completed by applying on the metal deposition layer to form an adhesive layer having a thickness of 1 μm. The stamping foil was evaluated for cutting properties, heat resistance, and bonding strength between the colored layer and the metal deposition layer by the following method, and the results are shown in Table 1 below.
    <Evaluation of cutting property>
    Using a stamping mold capable of evaluating the smallest letter of the first grade and the largest letter of the tenth grade, the cutting property was evaluated after the transfer process. In addition, the change in cutting property was evaluated by leaving the stamping foil in a thermo-hygrostat at 60 ° C. and 75% RH for 24 hours and then observing the cutting property after the transfer process.
    <Heat resistance evaluation>
    The heat resistance at this time was evaluated as the preservation of the color and gloss of the colored layer after the transfer, and the temperature when the gloss of the colored layer disappeared when the finished hot stamping foil was stamped with a metal mold maintaining a constant temperature.
    <Evaluation of Interlayer Bonding Force>
    After the stamping foil was transferred, it was peeled off with cellophane tape, and the bonding force at that time was evaluated as three grades of good (○), normal (△), and poor (×).
    <Examples 2-4>
    When preparing a composition for forming a colored layer, a stamping foil was prepared in the same manner as in Example 1 except that each component used was mixed as described in Table 1, and then the properties thereof were evaluated. Table 1 shows.
    <Comparative Example 1>
    In preparing the composition for forming the colored layer, 7% by weight of isocyanate, 2% by weight of nitrocellulose, 7% by weight of diallyl phthalate, 7% by weight of dye, 34% by weight of cyclohexanone and 43% by weight of methyl ethyl ketone A stamping foil was manufactured in the same manner as in Example 1 except that the mixture was prepared by mixing the same, and the properties thereof were evaluated, and the results are shown in Table 1 below.
    <Comparative Example 2-3>
    When preparing a composition for forming a colored layer, a stamping foil was prepared in the same manner as in Example 1 except that each component used was mixed as described in Table 1, and then the properties thereof were evaluated. Table 1 shows.
    ExampleComparative Example One234One23 Component (wt.%)Isocyanate1010101071010 Melamine-formaldehyde68682 * 1 1010 1,4-butanediolOneOne1.51.57 * 2 3One Methyl ethyl ketone40404040434040 Cyclohexanone353234.531.5342931 dyes8989788 characteristicCutability (grade)2233264 Change in machinability (grade)3243564 Heat resistance (℃)200200200190150150190 Interlayer Bonding Force○○○○××△
    (Note: * 1 is the content of nitrocellulose, * 2 is the content of diallyl phthalate)
    From the results of Table 1, when nitrocellulose and diallyl phthalate are used in the composition for forming a colored layer (Comparative Example 1), since cutting property decreases with time, it is not suitable for transcription such as small letters. While the stamping foil had poor storage properties, it also had poor heat resistance and interlayer bonding strength. In addition, when 1,4-butanediol was used in excess and the amount of melamine-formaldehyde resin was used in the same amount as that of isocyanate (Comparative Example 2), the cutability, heat resistance, and interlayer bonding force were all poor, and melamine-formaldehyde When only the resin was used in excess (Comparative Example 3), the characteristics of the evaluation targets were somewhat reduced. However, in the case where the melamine resin was added in an appropriate amount (Examples 1 to 4), as the amount of the melamine resin was increased, the cutting property hardly changed and there was no adverse effect on the interlaminar bonding force or the heat resistance.
    Since the stamping foil of the present invention has excellent cutting property and shows little change in cutting property, it is advantageous for long-term storage of the stamping foil, and can effectively transfer small letters, etc., and has excellent interlayer bonding force between the colored layer and the metal deposition layer, and thus coloring after transfer Excellent retention of color and gloss of the layer.
    权利要求:
    Claims (2)
    [1" claim-type="Currently amended] In a stamping foil in which a release layer, a colored layer, a metal deposition layer, and an adhesive layer are sequentially formed on a base film, said colored layer is 20 to 90% by weight of a melamine resin relative to the isocyanate and the isocyanate. And a coating layer for forming a colored layer comprising 5 to 20% by weight of 1,4-butanediol on the release layer and then cured.
    [2" claim-type="Currently amended] The stamping foil of claim 1, wherein the melamine resin is a melamine-formaldehyde resin.
    类似技术:
    公开号 | 公开日 | 专利标题
    US3952131A|1976-04-20|Heat transfer print sheet and printed product
    US6623817B1|2003-09-23|Inkjet printable waterslide transferable media
    US7514138B2|2009-04-07|Hydraulic transfer film and method for producing hydraulic transfer body using the same
    EP0109313B1|1991-01-02|Transfer coating of abrasion-resistant layers
    KR101888708B1|2018-08-14|Decorative sheet and decorative molded product
    CA1319862C|1993-07-06|Composite useful for paint transfer and method of useand preparation thereof
    US4369157A|1983-01-18|Method of automatically decorating articles as they are in-mold formed automatically
    TWI233394B|2005-06-01|Casting film for producing ceramic green sheet
    US3235395A|1966-02-15|Transfers for metallic coatings
    US3892900A|1975-07-01|Masking films
    JP2856862B2|1999-02-10|Paint composition and cosmetic material using the same
    AU713604B2|1999-12-09|Decoration foil for decoration of three-dimensional substrate surfaces
    US6423406B1|2002-07-23|Heat-transfer label including non-wax release layer
    CA2288636C|2007-04-17|Decorative sheet and process for producing the same
    US5104719A|1992-04-14|Heat activated, quick release decals and associated methods
    EP1192043B1|2006-01-04|Abrasion resistant laminate and process for producing same
    CA2268288C|2009-06-09|Transfer material, surface-protective sheet, and process for producing molded article
    US4461793A|1984-07-24|Printable coating for heatshrinkable materials
    EP2402159A1|2012-01-04|Decorative material
    US4421816A|1983-12-20|Dry transfer decal and method of manufacture
    US6399193B1|2002-06-04|Surfacing laminate with bonded with pigmented pressure sensitive adhesive
    US4517044A|1985-05-14|Dry transfer decal and method of manufacture
    US2872340A|1959-02-03|Transfer element and method of making the same
    US4042090A|1977-08-16|Key top
    KR20150090050A|2015-08-05|Transfer film
    同族专利:
    公开号 | 公开日
    KR100258728B1|2000-06-15|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    1997-10-02|Application filed by 장용균, 에스케이씨 주식회사
    1997-10-02|Priority to KR1019970050975A
    1999-05-06|Publication of KR19990030664A
    2000-06-15|Application granted
    2000-06-15|Publication of KR100258728B1
    优先权:
    申请号 | 申请日 | 专利标题
    KR1019970050975A|KR100258728B1|1997-10-02|1997-10-02|Stamping foil|
    [返回顶部]