    • 专利摘要:
    The present invention relates to a composition comprising: - from 0.68% to 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group; at least one silylated polymer comprising at least one alkoxysilane group, preferably from 3% to 80% of at least one silylated polymer comprising at least one alkoxysilane group; and at least 25% by weight of at least one carbonated filler, the percentages by weight being expressed relative to the total weight of said composition, as well as its use as putty, in particular as a construction mastic.
    公开号:FR3066765A1
    申请号:FR1754554
    申请日:2017-05-23
    公开日:2018-11-30
    发明作者:Federico SANZ；Jeremy BECQUET
    申请人:Bostik SA；
    IPC主号:
    专利说明:

    Low modulus silylated putty composition
    FIELD OF THE INVENTION
    The present invention relates to a composition suitable for the preparation of low modulus silylated mastic.
    The present invention also relates to the use of at least one silsesquioxane for preparing a low modulus putty composition.
    TECHNICAL BACKGROUND
    Sealants are widely used in the field of construction, in particular for joining - by expansion joints - substrates, for example concrete or steel, and allow, thanks to their mechanical properties, and in particular elastic, to obtain a stable joint to dimensional variations induced in particular by temperature changes.
    Among the desirable properties of a construction putty, one can cite among others, its capacity to adhere to a variety of substrate, its resistance to weather conditions (UV, ozone, water), its elasticity ... The movement capacity is a property closely related to the modulus of elasticity. The modulus of elasticity can be used to predict the expansion or compression properties of a sealant. The module is typically the ratio between the force (“stress” in English) necessary to stretch a putty (“strain” in English) at a certain point, typically 100%. Elongation is the length at which the putty can stretch, expressed as a percentage of its original size. The module has a direct effect on the elongation capacity, because the lower the tensile strength, the easier the putty can stretch.
    Low modulus sealants tend to have a large capacity for deformation and resilience (elastic recovery), which are capable of adapting to significant movements without creating too high a tension on the sealant or the substrate. Low modulus sealants in particular are more flexible, and stretch even more easily. High modulus sealants typically have a lower deformation capacity, and are rather recommended for uses with few expected movements where high tensile forces are required. High modulus sealants are so resistant that they generate a high tension on adhesive joints or substrates. In the case of substrates such as concrete, this tension may be enough to damage the substrates and / or the joint.
    There is in particular a need for new compositions suitable for the preparation of low modulus sealant, having in particular a good compromise between good mechanical properties, good elastic properties (elongation and elastic recovery), and good adhesion properties preferably. without the use of primer.
    DESCRIPTION OF THE INVENTION
    The present invention relates to a composition comprising: from 0.68% to 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group; at least one silylated polymer comprising at least one alkoxysilane group, preferably from 3% to 80% of at least one silylated polymer comprising at least one alkoxysilane group; and at least 25% by weight of at least one carbonated filler, the percentages by weight being expressed relative to the total weight of said composition.
    Silsesquioxane (A)
    Silsesquioxanes are typically organosilicon compounds which can adopt a polyhedral structure or a polymeric structure, with Si-O-Si bonds. They typically have the following general structure: [RSiO3 / 2] t in which R, of identical or different nature, represents an organic radical, and t being an integer which can vary from 6 to 12, preferably t being 6, 8, 10 or 12.
    According to one embodiment, the silsesquioxane (A) has a polyhedral structure (or POSS for "Polyhedral Oligomeric Silsesquioxane" in English).
    Preferably, the silsesquioxane (A) corresponds to the following general formula (I):
    (I) in which each of R’1 to R’8 represents, independently of each other, a group chosen from:
    a hydrogen atom, a radical chosen from the group consisting of a linear or branched C1-C4 alkoxy radical, a linear or branched alkyl radical comprising from 1 to 30 carbon atoms, an alkenyl radical comprising from 2 to 30 atoms of carbon, an aromatic radical comprising from 6 to 30 carbon atoms, an allyl radical comprising from 3 to 30 carbon atoms, an aliphatic cyclic radical comprising from 3 to 30 carbon atoms, an acyl radical comprising from 1 to 30 carbon atoms carbon, and a group -OSiR'9R'10 in which R'9 and R'10 each represents, independently of one another, a hydrogen atom or a radical chosen from the group consisting of linear or branched alkyls in C1-C4, linear or branched alkoxys in C1-C4, alkenyls in C2-C4, a phenyl, an allyl radical in C3-C6, a cyclic aliphatic radical in C3-C8, and d 'a C1-C4 acyl radical; provided: at least one radical from the radicals R’1 to R’8 is a C1-C4 alkoxy radical; and that at least one radical among the radicals R’1 to R’8 is a phenyl radical.
    Preferably, in the above-mentioned formula (I), each of R'1 to R'8 represents, independently of each other, a group chosen from: a hydrogen atom, a radical chosen from the group consisting of a radical linear or branched C1-C4 alkoxy, a linear or branched alkyl radical comprising from 1 to 30 carbon atoms, preferably from 1 to 12 carbon atoms, preferably from 1 to 8 carbon atoms, and for example from 1 to 5 carbon atoms, an aromatic radical comprising from 6 to 30 carbon atoms, preferably from 6 to 12 carbon atoms, and a group -OSiR'9R'10 in which R'9 and R'10 each independently represent the one of the other, a hydrogen atom or a radical chosen from linear or branched C1-C4 alkyls, for example methyl or ethyl, preferably methyl, provided that: at least one radical from the radicals R'1 to R'8 or a C1-C4 alkoxy radical; and that at least one radical among the radicals R’1 to R’8 is a phenyl radical.
    Preferably, in the above-mentioned formula (I), R′1 to R′8 each represent, independently of one another, a radical chosen from the group consisting of phenyl, methyl, and methoxy, provided that at least a radical is a C1-C4 alkoxy radical, and that at least one other radical is a phenyl radical.
    According to the invention, the silsesquioxane (A), preferably of formula (I), can comprise from 10% to 20% by weight, preferably from 12% to 20% by weight, preferably from 15% to 18% by weight of alkoxy group, preferably methoxy, relative to the total weight of said silsesquioxane (A).
    According to one embodiment, the silsesquioxane (A), preferably of formula (I), comprises at least one methyl group. Preferably, the silsesquioxane (A) comprises a weight ratio of phenyl group (s): methyl group (s) ranging from 1:10 to 10: 1, preferably from 1: 5 to 5: 1, advantageously from 1: 4 to 4: 1, especially from 1: 2 to 2: 1. For example, the weight ratio of phenyl group (s): methyl group (s) is 1: 1 or 0.25: 1.
    According to one embodiment, the silsesquioxane (A), preferably of formula (I), has a viscosity at 23 ° C ranging from 10 to 200 mPa.s, preferably from 14 to 180 mPa.s, advantageously ranging from 90 at 150 mPa.s, preferably from 110 to 130 mPa.s. In particular, the silsequioxane (A) has a viscosity at 23 ° C of 14 mPa.s, and preferably a number average molecular weight ranging from 800 g / mol to 1300 g / mol. In particular, silsesquioxane (A) has a viscosity at 23 ° C of 120 mPa.s, and preferably a number average molecular weight ranging from 1000 g / mol to 1500 g / mol.
    Generally, the viscosity can be measured in a manner well known to those skilled in the art. In particular, the viscosity can be measured with a Brookfield viscometer, by choosing the needle and the speed of the module appropriately, according to the viscosity range to be measured.
    According to one embodiment, the silsesquioxane (A), preferably of formula (I), has a number-average molecular mass ranging from 500 g / mol to 3,000 g / mol, preferably from 800 g / mol to 2,000 g / mol, and advantageously from 800 g / mol to 1,500 g / mol. For example, silsesquioxane (A) has a weight average molar mass ranging from 800 g / mol to 1,300 g / mol or from 1,000 to 1,500 g / mol.
    The number and weight average molecular weights of silsesquioxanes can be measured by methods well known to those skilled in the art, for example by size exclusion chromatography using polystyrene standards.
    The aforementioned composition can comprise a silsesquioxane (A) or a mixture of silsesquioxanes (A) of different natures.
    According to one embodiment, the content of silsesquioxane (A) in the above-mentioned composition is chosen from one of the following weight contents: from 0.68% to 1.00%, from 0.69% to 1.00%, 0.70% to 1.00%, 0.71% to 1.00%, 0.72% to 1.00%, 0.73% to 1.00%, 0.74% to 1.00%, 0.75% to 1.00%, 0.76% to 1.00%, 0.77% to 1.00%, 0.78% to 1.00%, 0.79% to 1.00%, 0.80% to 1.00%, 0.81% to 1.00%, 0.82% to 1.00%, 0.83% to 1 .00%, from 0.84% to 1.00%, from 0.85% to 1.00%, from 0.86% to 1.00%, from 0.87% to 1.00%, from 0 , 88% to 1.00%, from 0.89% to 1.00%, from 0.90% to 1.00%, from 0.91% to 1.00%, from 0.92% to 1, 00%, from 0.93% to 1.00%, from 0.94% to 1.00%, or from 0.95% to 1.00% by weight, relative to the total weight of said composition. As an example of silsesquixane (A), there may be mentioned those having one of the following CAS numbers: [68440-65-3], [68957-04-0], [68957-06-2], [1211908 -05-2]
    Mention may, for example, be made of DC 3074® or DC 3037® sold by DOW CORNING.
    Silylated polymer comprising at least one alkoxysilane group
    According to one embodiment, the silylated polymer comprising at least one alkoxysilane group is a polymer comprising at least one, preferably at least two groups of formula (V): -Si (R4) P (OR5) 3-p (V) in which: R4 and R5, identical or different, each represent a linear or branched alkyl radical comprising from 1 to 4 carbon atoms; p is an integer equal to 0, 1 or 2.
    Preferably, the silylated polymers comprising at least one alkoxysilane group are chosen from silylated polyurethanes, silylated polyethers, and their mixtures.
    The silylated polymer comprising at least one alkoxysilane group may have a number-average molecular mass ranging from 500 to 50,000 g / mol, more preferably ranging from 700 to 20,000 g / mol.
    The number-average molecular weight of the polymers can be measured by methods well known to those skilled in the art, for example by size exclusion chromatography using standards of polyethylene glycol type.
    According to one embodiment, the silylated polymer comprising at least one alkoxysilane group is chosen from the polymers of formulas (II), (III) or (IV) as defined below, and their mixtures:
    (II)
    (III)
    (IV) in which: - R1 represents a divalent hydrocarbon-based radical comprising from 5 to 15 carbon atoms which may be aromatic or aliphatic, linear, branched or cyclic, - R ° represents a divalent linear or branched alkylene radical comprising from 3 to 6 carbon atoms, - R3 represents a divalent linear or branched alkylene radical comprising from 1 to 6 carbon atoms, preferably R3 representing methylene or n-propylene, - R2 represents a divalent linear or branched alkylene radical comprising from 2 to 4 atoms carbon, - R4 and R5, identical or different, each represent a linear or branched alkyl radical comprising from 1 to 4 carbon atoms, preferably R4 and R5 representing methyl,
    - R6 represents a hydrogen atom, a phenyl radical, a linear, branched or cyclic alkyl radical comprising from 1 to 6 carbon atoms, or a 2-succinate radical of formula:
    in which R7 is a linear or branched alkyl radical comprising from 1 to 6 carbon atoms, - n is an integer such that the number-average molecular mass of the polyether block of formula - [OR2] n- is 300 g / mol at 40,000 g / mol in the polymers of formulas (II), (III) and (IV), - nr is zero or an integer, - n and nr are such that the number-average molecular mass of the polymer of formula ( III) ranges from 500 g / mol to 50,000 g / mol, preferably from 700 g / mol to 20,000 g / mol, - m is an integer other than zero, - n and m are such that the average molecular mass in number of the polymer of formula (IV) ranges from 500 g / mol to 50,000 g / mol, preferably from 700 g / mol to 20,000 g / mol, - p is an integer equal to 0, 1 or 2, p preferably being 0 or 1.
    Preferably, the radical R1 of formulas (II), (III) and (IV) is chosen from one of the following divalent radicals whose formulas below show the 2 free valences: - a) the divalent radical derived from isophorone diisocyanate (I PDI):
    b) the divalent radical derived from 4,4’- and 2,4’-dicyclohexylmethane diisocyanate (HMDI):
    or - c) the radical derived from 2,4- and 2,6-toluene diisocyanate (TDI)
    or
    - d) the radical derived from 4,4’- and 2,4’-diphenylmethane diisocyanate (MDI)
    or - e) the radical derived from m-xylylene diisocyanate (m-XDI)
    - f) the radical derived from hexamethylene diisocyanate (HDI)
    Preferably, the radical R1 of the formulas (II), (III) and (IV) is the divalent radical derived from isophorone diisocyanate or from xylylene diisocyanate.
    The polymers of formula (III) can be obtained according to a process described in documents EP 2336208 and WO 2009/106699.
    Among the polymers corresponding to formula (III), there may be mentioned for example: GENIOSIL® STP-E10 (available from Wacker): polyether comprising two groups (V) of dimethoxy type (rm equal to 0, p equal to 1 and R4 and R5 represent a methyl group) having a number average molecular weight of approximately 8,889 g / mol where R3 represents a methylene group; GENIOSIL® STP-E30 (available from Wacker): polyether comprising two groups of formula (V) of dimethoxy type (rm equal to 0, p equal to 1 and R4 and R5 represent a methyl group) having a number-average molecular mass about 14,493 g / mol where R3 represents a methylene group; SPUR + ® 1050MM (available from MOMENTIVE): polyurethane comprising two groups of formula (V) of trimethoxy type (rm different from 0, p equal to 0 and R5 represents a methyl group) having a number average molecular weight of approximately 21 000 g / mol where R3 represents an n-propylene group; SPUR + ® Y-19116 (available from MOMENTIVE): polyurethane comprising two groups of formula (V) of trimethoxy type (rm different from 0 and R5 represents a methyl group) having a number average molecular weight ranging from 15,000 to 17,000 g / mol where R3 represents an n-propylene group; DESMOSEAL® S XP 2636 (available from BAYER): polyurethane comprising two groups of formula (V) of trimethoxy type (rm different from 0, p equal to 0 and R5 represents a methyl group) having an average molecular weight in number of about 15,038 g / mol where R3 represents an n-propylene group. As an example of a silylated polymer of formula (III), mention may also be made of GENIOSIL® XB502, a commercial product available from WACKER. This GENIOSIL® XB502 product comprises a mixture of two products (B) and (C) where (B) is a polymer of formula (III) of number average molecular weight of about 14,000 g / mol where rm is zero , p is equal to 1, R5 and R4 each represent a methyl group, R3 represents a methylene group, and the group - [OR2] n- comes from a polypropylene glycol; (C) is a silsesquioxane (A) of number average molecular mass of about 800 g / mol terminated by methoxy groups (CAS 1211908-05-2), the products (B) and (C) being present in a ratio mass (B) / (C) of approximately (25-30) / (70-75).
    The polymers of formula (II) can be obtained by hydrosilylation of polyether diallylether according to a process described for example in document EP 1829928.
    Among the polymers corresponding to formula (II), there may be mentioned: - MS POLYMER ™ S303H (available from KANEKA) corresponding to a polyether comprising two groups of formula (V) of dimethoxy type (p is equal to 1 and R4 represents a methyl group) having a number average molecular mass of approximately 22,000 g / mol and a viscosity of 12.5 Pa.s at 23 ° C; - MS POLYMER ™ S227 (available from KANEKA) corresponding to a polyether comprising two groups of formula (V) of dimethoxy type (p is equal to 1, R5 and R4 each represent a methyl group) having a number average molecular weight about 27,000 g / mol, and a viscosity of 34 Pa.s at 23 ° C.
    The polymers of formula (IV) can be obtained according to the following process: a) reaction of a polyether polyol of the following formula:
    with a stoichiometric excess of diisocyanate of the following formula: NCO-R1-NCO to form a polyurethane-polyether block having at least two terminal groups -NCO, said block preferably comprising from 1.5% to 1.9% by weight of group -NCO, and then b) reaction between a block obtained in the previous step with a stoichiometric quantity or a slight excess of an α-, β- or γ-aminosilane having the following formula: (R5O) 3-p (R4 ) PSi-R3-NHR6
    Such a method is for example described in WO 2013/136108.
    Among the polymers corresponding to formula (IV), there may be mentioned: SPUR + 1050 MM (available from MOMENTIVE) corresponding to polyurethane polyether comprising two groups of formula (V) of trimethoxy type (p is equal to 0, R5 represents a methyl group) having a number-average molecular mass of approximately 20,000 g / mol and a viscosity of 35 Pa at 23 ° C; SPUR + 1015 LM (available from MOMENTIVE) corresponding to a polyether polyurethane comprising two groups of formula (V) of the type
    trimethoxy (p is 0, R5 represents a methyl group) having a number-average molecular mass of approximately 25,000 g / mol and a viscosity of 50 Pa at 23 ° C.
    The composition according to the invention may comprise a polymer of the above formula (II) or a mixture of different polymers of the above formula (II).
    The composition according to the invention may comprise a polymer of the above formula (III) or a mixture of different polymers of the above formula (III).
    The composition according to the invention may comprise a polymer of the above formula (IV) or a mixture of different polymers of the above formula (IV).
    The composition according to the invention can comprise: at least one polymer of formula (II) above, and at least one polymer of formula (III) above; at least one polymer of formula (II) above, and at least one polymer of formula (IV) above; at least one polymer of the above formula (III), and at least one polymer of the above formula (IV); or at least one polymer of formula (II) above, at least one polymer of formula (III) above, and at least one polymer of formula (IV) above.
    According to one embodiment, the above-mentioned composition comprises at least one polymer of the above-mentioned formula (II), and at least one polymer of the above-mentioned formula (III) in a weight ratio of polymer (s) of formula (II) / polymer (s) ) of formula (III) between 1/10 and 10/1, preferably between 1/5 and 5/1, preferably between 2/5 and 5/2, advantageously between 2/5 and 3/5.
    According to one embodiment, the composition according to the invention comprises: • at least one silylated polymer of formula (II), in which: - p = 0 or 1, preferably p = 1, - R ° represents a divalent radical n -propylene, - R4 and R5 each represents a methyl group, - the number-average molecular mass of said polymer ranging from 5,000 to 30,000 g / mol, preferably from 10,000 to 20,000 g / mol. and / or • at least one silylated polymer of formula (III), in which: - rm is an integer equal to or different from 0, - p = 0 or 1, preferably p = 0, - R4 and R5 each represent a methyl radical, - R3 represents a divalent methylene or n-propylene radical, - the number-average molecular mass of said polymer ranging from 5,000 to 30,000 g / mol, preferably from 10,000 to 20,000 g / mol, in particular 14 000 to 16,000 g / mol,
    According to one embodiment, the composition according to the invention comprises: • at least one silylated polymer of formula (III), in which: - rm is an integer equal to or different from 0, - P = 0, - R4 and R5 each represent a methyl radical, - R3 represents a divalent n-propylene radical, - the number-average molecular mass of said polymer ranging from 5,000 to 30,000 g / mol, preferably from 10,000 to 20,000 g / mol, in particular from 14,000 to 16,000 g / mol, and / or • at least one silylated polymer of formula (III), in which: - rm is an integer equal to 0, - P = 1, - R4 and R5 each represent a radical methyl, - R3 represents a divalent methylene radical, - the number-average molecular mass of said polymer ranging from 5,000 to 30,000 g / mol, preferably from 10,000 to 20,000 g / mol, in particular approximately 14,000 g / mol, and / or • at least one silylated polymer of formula (II), in which: - p = 0 or 1, preferably p = 1, - R ° represents a divalent n-propylene radical, - R4 and R5 each represents a methyl group, - the number-average molecular mass of said polymer ranging from 5,000 to 30,000 g / mol, preferably from 10,000 to 20,000 g / mol.
    According to one embodiment, the composition according to the invention comprises from 3% to 80% by weight, preferably from 5% to 60% by weight, preferably from 5% to 50% by weight, advantageously from 10% to 50% , for example from 10% to 40% by weight, advantageously from 20% to 30%, in particular from 22% to 24% by weight of at least one silylated polymer comprising at least one alkoxysilane group, preferably chosen from polymers of formulas (II), (III), (IV) above and their mixtures, relative to the total weight of said composition.
    Carbonate charge
    According to one embodiment, the carbonate filler is chosen from carbonates of alkali or alkaline earth metals and their mixtures, preferably the carbonate filler is calcium carbonate.
    The calcium carbonate can be made hydrophobic, for example with calcium stearate or the like which makes it possible to impart partial or total hydrophobicity to the calcium carbonate particles. The more or less hydrophobic nature of the calcium carbonate can have an impact on the rheology of the composition. In addition, the hydrophobic coating can make it possible to prevent the calcium carbonate from absorbing the constituents of the composition and making them ineffective. The hydrophobic coating of calcium carbonate can represent from 0.1% to 3.5% by weight, relative to the total weight of calcium carbonate.
    The calcium carbonate which can be used in the present invention preferably has a particle size ranging from 0.1 to 400 μm, more preferably from 1 to 400 μm, preferably from 10 to 350 μm, more preferably from 50 to 300 μm . By way of example of calcium carbonate, mention may be made of MIKHART® 1T (available from the company LA PROVENÇALE).
    The composition according to the invention may comprise at least 25% by weight of at least one carbonated filler, preferably at least 30% by weight, preferably at least 40% by weight relative to the total weight of the composition.
    The composition according to the invention preferably comprises from 25% to 80% by weight, preferably from 40% to 60% by weight, in particular from 45% to 55% by weight of at least one carbonated filler, for example carbonate of calcium, relative to the total weight of the composition.
    Composition
    The composition according to the invention can comprise at least one catalyst. Preferably, the composition comprises at least one catalyst.
    The catalyst can be any catalyst known to a person skilled in the art for the condensation of silanol. Examples of such catalysts that may be mentioned include: aminosilanes such as N- (2-aminoethyl) -3-aminopropyltrimethoxysilane (commercially available under the name SILQUEST® A-1120 from the company MOMENTIVE) or 3-aminopropyltrimethoxysilane, organic derivatives titanium such as titanium acetyl acetonate (commercially available under the name TYZOR® AA75 from the company DU PONT DE NEMOURS), aluminum such as aluminum chelate (commercially available under the name K-KAT® 5218 from the company KING INDUSTRIES), amines such as 1,8-diazabicyclo [5.4.0] undec-7-ene (DBU) or 1,5-diazabicyclo [4.3.0] non-5-ene (DBN), diethyl ether-2,2'-morpholine (DMDEE), 1,4-diazabicylo [2.2.2] octane (DABCO), tin-based catalysts such as NEOSTANN® S-1 or TIB- KAT® 216 (available respectively from KANEKA or TIB CHEMICALS). These tin-based catalysts are particularly suitable for silylated polymers of formula (II).
    The catalyst (s) preferably represent from 0.1% to 1% by weight, preferably from 0.1% to 0.6% by weight, advantageously from 0.3% to 0.6% by weight of the total weight of the composition.
    According to one embodiment, the composition also comprises at least one additive chosen from plasticizers, solvents, pigments, adhesion promoters, moisture absorbers, UV stabilizers (or antioxidants), glitter , fluorescent materials, rheological additives, fillers other than carbonate fillers, and mixtures thereof.
    According to one embodiment, the composition according to the invention comprises: from 3% to 80% by weight, preferably from 5% to 50% by weight, preferably from 10% to 50% by weight, advantageously from 10% to 40 % by weight of at least one silylated polymer comprising at least one alkoxysilane group as defined above, from 0.1% to 1% by weight, preferably from 0.1% to 0.6% by weight, d '' at least one catalyst as defined above, from 25% to 80% by weight, preferably from 40% to 60% by weight, of at least one carbonated filler, preferably calcium carbonate, from 0% to 30% by weight, in particular from 0.1% to 30% by weight, preferably from 0.5% to 20% by weight, preferably from 0.5% to 15% by weight of at least one selected additive among plasticizers, solvents, pigments, adhesion promoters, moisture absorbers, UV stabilizers (or antioxidants), glitter, fluorescent materials, rheological additives, l loads other than carbonated loads, and mixtures thereof; and from 0.68% to 1.00% by weight, preferably from 0.69% to 1.00% by weight, preferably from 0.75% to 1.00% by weight, and advantageously from 0.80% at 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group as defined above, the weight percentages being expressed relative to the total weight of the composition.
    In the context of the invention, the term "filler other than the carbonated filler" or even "filler" means a filler which is not a carbonated filler.
    The filler can be chosen from organic fillers, inorganic fillers and their mixtures. As organic filler (s), any organic filler (s) and in particular polymeric filler (s) typically used in the field of mastic compositions can be used.
    Polyvinyl chloride (PVC), polyolefins, rubber, ethylene vinyl acetate (EVA), aramid fibers such as Kevlar® can be used, for example.
    It is also possible to use hollow microspheres of expandable or non-expandable thermoplastic polymer. Mention may in particular be made of hollow microspheres of vinylidene chloride / acrylonitrile.
    The average particle size of the usable filler (s) is preferably less than or equal to 10 microns, more preferably less than or equal to 3 microns, in order to avoid their sedimentation in the composition according to the invention. during storage.
    The average particle size is measured for a particle size distribution by volume and corresponding to 50% by volume of the sample of particles analyzed. When the particles are spherical, the average particle size corresponds to the median diameter (D50 or Dv50) which corresponds to the diameter such that 50% of the particles by volume have a size smaller than said diameter. In the present application, this value is expressed in micrometers and determined according to Standard NF ISO 13320-1 (1999) by laser diffraction on an apparatus of the MALVERN type.
    Preferably, the filler is an inorganic filler.
    The inorganic fillers can be in the form of particles of various geometry. They may for example be spherical, fibrous, or have an irregular shape.
    According to one embodiment, the filler is chosen from sand, glass beads, glass, quartz, barite, alumina, mica, talc. Preferably, the filler is chosen from sand and glass beads.
    The sand which can be used in the present invention preferably has a particle size ranging from 0.1 to 400 µm, preferably from 1 to 400 µm, more preferably from 10 to 350 µm, more preferably from 50 to 300 µm.
    The glass beads which can be used in the present invention preferably have a particle size ranging from 0.1 to 400 μm, preferably from 1 to 400 μm, more preferably from 10 to 350 μm, more preferably from 50 to 300 μm .
    The filler (s) (other than the carbonated filler (s)) preferably represent (s) from 0% to 30% by weight, preferably from 0% to 10%, preferably from 1 % to 10% by weight, of the total weight of the composition.
    The composition according to the invention may comprise at least one plasticizing agent in an amount of 5% to 30% by weight, preferably from 10% to 30% by weight, preferably from 15% to 25% by weight relative to the total weight of said composition. As an example of a plasticizing agent which can be used, any plasticizing agent usually used in the field of mastic compositions can be used.
    Preferably, the following are used: diisodecyl phthalate, as marketed under the name PALATINOL ™ DI DP by the company BASF, an ester of alkylsulphonic acid and phenol, as marketed under the name MESAMOLL® by the company LANXESS, diisononyl -1,2-cyclohexanedicarboxylate, as marketed under the name HEXAMOLL DINCH® by the company BASF, pentaerythritol tetravalerate, as marketed under the name PEVALEN ™ by the company PERSTORP.
    The composition according to the invention can comprise at least one rheology agent. As an example of a rheology agent (s) which can be used, mention may be made of any rheology agent usually used in the field of putty compositions.
    Preferably, one or more rheology agents are chosen chosen from thixotropic agents, and more preferably from: PVC plastisols, corresponding to a suspension of PVC in a plasticizing agent miscible with PVC, obtained in situ by heating at temperatures ranging from 60 ° C to 80 ° C. These plastisols can be those described in particular in the work "Polyurethane Sealants", Robert M. Evans, ISBN 087762-998-6, fumed silica, - urea derivatives derived from the reaction of an aromatic diisocyanate monomer such as 4,4'-MDI with an aliphatic amine such as butylamine. The preparation of such urea derivatives is described in particular in application FR 1 591 172. - waxes of micronized amides, such as CRAYVALLAC SLX marketed by Arkema.
    The total content of rheology agent (s) that can be used can vary from 1% to 30% by weight, preferably from 5% to 30% by weight, more preferably from 10% to 25% by weight relative to the total weight of the composition according to the invention.
    The solvent is preferably a volatile solvent at room temperature (temperature of the order of 23 ° C). The volatile solvent can for example be chosen from alcohols volatile at room temperature, such as ethanol or isopropanol. The volatile solvent makes it possible, for example, to reduce the viscosity of the composition and to make the composition easier to apply. The volatile nature of the solvent allows the seal, obtained after hardening of the composition, to no longer contain any solvent. Thus, for example, the solvent has no negative influence on the hardness of the joint.
    When a solvent, in particular a volatile solvent, is present in the composition, its content is preferably less than or equal to 5% by weight, more preferably less than or equal to 3% by weight, relative to the total weight of the composition.
    Preferably, the content of solvent (s) in the composition is between 0% and 5% by weight.
    When a pigment is present in the composition, its content is preferably less than or equal to 3% by weight, more preferably less than or equal to 2% by weight, relative to the total weight of the composition. When present, the pigment may for example represent from 0.1% to 3% by weight or from 0.4% to 2% by weight of the total weight of the composition.
    The pigments can be organic or inorganic pigments.
    For example, the pigment is ΤίΟ2, in particular KRONOS® 2059 sold by the company KRONOS. The moisture absorber, if present, can be chosen from vinyltrimethoxysilane (VTMO), vinyltriethoxysilane (VTEO), alkoxyarylsilanes, such as GENIOSIL® XL 70 available from the company WACKER.
    When a moisture absorber is present in the composition, its content is preferably less than or equal to 3% by weight, more preferably less than or equal to 2% by weight relative to the total weight of the composition. When present, the moisture absorber may for example represent from 0.5% to 3% by weight or from 1% to 2% by weight relative to the total weight of the composition.
    Among the UV stabilizers or antioxidants, there may be mentioned benzotriazoles, benzophenones, so-called hindered amines such as bis (2,2,6,6, -tetramethyl-4-piperidyl) sebaceate, and their mixtures.
    Mention may for example be made of the TINUVIN® 328 or TINUVIN ™ 770 products sold by BASF.
    According to one embodiment, the composition according to the invention comprises: from 15% to 80% by weight, preferably from 15% to 50% by weight of at least one silylated polymer comprising at least one alkoxysilane group as defined above above, from 0.1% to 1% by weight, preferably from 0.1% to 0.6% by weight, of at least one catalyst as defined above, from 25% to 55% by weight, preferably from 40% to 55% by weight, of at least one carbonated filler as defined above, from 10% to 30% by weight of at least one plasticizer as defined above, from 0.1 % to 3% by weight of at least one moisture absorber as defined above, from 0.1% to 10% by weight of at least one filler other than the carbonate filler (s) ( es) as defined above; from 0.1% to 20% by weight, preferably from 0.1% to 10% by weight of at least one additive chosen from solvents, pigments, adhesion promoters, UV stabilizers (or anti- oxidants), flakes, fluorescent materials, rheological additives, and mixtures thereof; from 0.68% to 1.00% by weight, preferably from 0.69% to 1.00% by weight, preferably from 0.75% to 1.00% by weight, and advantageously from 0.80% to 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group, as defined above.
    Preferably, the composition according to the invention comprises (preferably consists of): from 15% to 80% by weight, preferably from 15% to 50%, advantageously from 10% to 40% by weight: o at least a silylated polymer of formula (III), in which: - mi is an integer equal to or different from 0, - p = 0 or 1, preferably p = 0, - R4 and R5 each represent a methyl radical, - R3 represents a divalent methylene or n-propylene radical, the number-average molecular mass of said polymer ranging from 5,000 to 30,000 g / mol, preferably from 10,000 to 20,000 g / mol, in particular from 14,000 to 16,000 g / mol, and / or o of at least one silylated polymer of formula (II), in which: - p = 0 or 1, preferably p = 1, - R ° represents a divalent n-propylene radical, - R4 and R5 each represents a methyl group, - the number-average molecular mass of said polymer ranging from 5,000 to 30,000 g / mol, preferably from 10,000 to 20 000 g / mol. from 0.1% to 1% by weight, preferably from 0.1% to 0.6% by weight, of at least one catalyst as defined above, from 25% to 55% by weight, preferably from 40% to 55% by weight of calcium carbonate, from 10% to 30% by weight of at least one plasticizer as defined above, from 0.1% to 3% by weight of at least one absorber humidity as defined above, from 0.1% to 10% by weight of at least one filler other than the carbonated filler (s) as defined above -above; from 0.1% to 20% by weight, preferably from 0.1% to 10% by weight of at least one additive chosen from solvents, pigments, adhesion promoters, UV stabilizers (or anti- oxidants), flakes, fluorescent materials, rheological additives, and mixtures thereof; from 0.68% to 1.00% by weight, preferably from 0.69% to 1.00% by weight, preferably from 0.75% to 1.00% by weight, and advantageously from 0.80% to 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group, as defined above, said silsquioxane (A) preferably corresponding to the compound of formula (I) .
    According to one embodiment, the composition comprises from 2 to 5, preferably from 3 to 4.5, and preferably from 3 to 4.4 parts by weight of silsesquioxane (A) as defined above, per 100 parts in weight of silylated polymer (s) as defined above.
    Preferably, the composition comprises: 100 parts by weight of at least one silylated polymer comprising at least one alkoxysilane group as defined above; from 2 to 5, preferably from 3 to 4.5, and preferably from 3 to 4.4 parts by weight of silsesquioxane (A) as defined above,; from 100 to 300, preferably from 200 to 250 parts by weight of at least one carbonate filler.
    Preferably, the composition comprises: 100 parts by weight of at least one silylated polymer comprising at least one alkoxysilane group as defined above; from 2 to 5, preferably from 3 to 4.5, and preferably from 3 to 4.4 parts by weight of silsesquioxane (A) as defined above, from 100 to 300 parts by weight of at least one filler carbonate as defined above, from 0.6 to 1.2, preferably from 0.5 to 1.0 parts by weight of at least one catalyst as defined above, from 0.6 to 100, in particular from 1 to 50, preferably from 1.5 to 40 parts by weight of at least one additive chosen from plasticizers, solvents, pigments, adhesion promoters, moisture absorbers, UV stabilizers (or antioxidants), flakes, fluorescent materials, rheological additives, fillers other than carbonate fillers, and mixtures thereof.
    According to one embodiment, the composition comprises from 0.7 to 1.00 parts by weight of silsesquioxane (A) as defined above, per 100 parts by weight of the sum of the other constituents of said composition, the sum of other constituents preferably being distributed as follows: from 15 to 80 parts by weight, preferably from 15 to 50 parts by weight of at least one silylated polymer comprising at least one alkoxysilane group as defined above, from 0, 01 to 1 parts by weight, preferably from 0.01 to 0.5 parts by weight, of at least one catalyst as defined above, from 25 to 55 parts by weight, preferably from 40 to 55 parts by weight, of at least one carbonate filler as defined above, from 10 to 30 parts by weight of at least one plasticizer as defined above, from 0.1 to 3 parts by weight of at least one moisture absorber as defined above, from 0.1 to 10 parts by weight of at least a filler other than the carbonated filler (s) as defined above; from 0.1 to 20 parts by weight, preferably from 0.1 to 10 parts by weight of at least one additive chosen from solvents, pigments, adhesion promoters, UV stabilizers (or antioxidants) , flakes, fluorescent materials, rheological additives, and mixtures thereof.
    According to one embodiment, the above-mentioned composition is such that the weight ratio of silylated polymer (s) / silsesquioxane (A) is between 33 and 22, preferably between 32.9 and 22.5, preferably between 32 , 85 and 22.97.
    The composition according to the invention can be in mono-component form, that is to say that all the components are packaged in the same compartment.
    The composition is preferably ready to use, that is to say that the user (individual or professional) can directly apply the composition to make the joint, without having to perform any prior mixing.
    The composition can be prepared by mixing the silylated polymer (s), and filler (s) (carbonate and other fillers) at a temperature ranging from 5 ° C. to 80 ° C., preferably under an inert atmosphere. The catalyst (s) can be added at the same time, or in a second step after mixing the polymer (s) and the filler (s). The silsequioxane (A) can also be added at the same time, or in a second step after mixing the polymer (s) and the filler (s). The other additives are introduced into the composition in accordance with the usual uses.
    The compositions according to the invention comprise a moisture-crosslinkable silylated polymer whose chemical structure is endowed with reactive groups of alkoxysilane type, as well as a silsequioxane (A) comprising reactive groups. The reaction of all of these reactive groups with water from the humidity of the air or of the substrate (called crosslinking reaction) makes it possible in particular, after the introduction of the mastic into the gap between the 2 substrates to assembling, creating a solid three-dimensional polymer network, which gives the adhesive seal thus created the desired mechanical properties. The effective obtaining of these mechanical properties is achieved when the entire quantity of putty introduced is crosslinked, which may require several days.
    This reaction, known as crosslinking, leads after its completion to the formation of an adhesive joint between the 2 substrates which is constituted by the polymer and the silsequioxane (A) crosslinked in a three-dimensional network formed by the polymer chains linked together by siloxane type bonds. This joint ensures in particular the solidity of the assembly of the 2 substrates thus obtained.
    The composition according to the invention is advantageously a mastic composition, in particular an elastic mastic composition.
    The composition according to the invention advantageously has the following characteristics after crosslinking: a module with 100% elongation less than or equal to 0.40 MPa; and an elastic recovery greater than or equal to 70%,
    These characteristics are typical of low modulus putty compositions. Thus, the composition according to the invention is advantageously a composition of low modulus putty, that is to say that it leads to a low modulus putty after crosslinking.
    According to the invention, the module at 100% elongation is the module at 100% elongation at 23 ° C. These include the 100% elongation module for a concrete substrate.
    In the context of the invention, the “module at 100% elongation” is defined as the constraint at 100% elongation. It typically allows you to measure the forces that develop in the sealant when it is stretched.
    In the context of the invention, "elastic recovery" is defined as the ability of a material to return to its initial shape after elongation. It is notably expressed in% relative to its initial length representing 100%.
    When the load that caused the elongation is removed, the sealant specimen can more or less completely return to its original length. A good elastomeric sealant should preferably return to its original length as much as possible, so as to withstand many of the tensile / compression cycles that occur during its service life.
    The mastic composition according to the invention is advantageously classified 25LM according to ISO11600 standard of 2002. According to this standard, the 25LM classification requires in particular: a module with 100% elongation less than or equal to 0.40 MPa; and an elastic recovery greater than or equal to 70%.
    In the context of the present invention, the “100% elongation module” is determined according to the test appearing in ISO11600 of 2002, which refers to ISO8339 of 2005.
    In the context of the present invention, the “elastic recovery” is determined according to the test appearing in standard ISO11600 of 2002, which refers to standard ISO7389 of 2002.
    The composition according to the invention is advantageously a low modulus putty composition, having in particular a good compromise between mechanical properties, elastic properties, and adhesion properties. The composition according to the invention is advantageously useful in the field of construction.
    The composition according to the invention advantageously allows good adhesion between the substrates, and advantageously makes it possible to avoid the use of adhesion primer, in particular for concrete substrates.
    All of the embodiments described above can be combined with each other. In particular, the various aforementioned constituents, and in particular the preferred modes, of the composition can be combined with one another.
    uses
    The present invention also relates to the use of a composition as defined above, as an adhesive, sealant or coating, preferably as a sealant, for example as a construction sealant.
    The composition can in particular be used for making sealing and expansion joints in buildings, in particular between concrete / concrete substrates.
    The present invention also relates to the use of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group as defined above, for preparing a composition, in particular a mastic composition, having after crosslinking: a module with 100% elongation less than or equal to 0.40 MPa; and an elastic recovery greater than or equal to 70%, the content of silsequioxane (A) in the composition ranging from 0.68% to 1.00% by weight relative to the total weight of said composition.
    In particular, the invention relates to said composition comprises: from 0.68% to 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group; at least one silylated polymer comprising at least one alkoxysilane group, preferably from 3% to 80% of at least one silylated polymer comprising at least one alkoxysilane group; and at least 25% by weight of at least one carbonated filler, the percentages by weight being expressed relative to the total weight of said composition.
    The ingredients and characteristics described above for the composition also apply for the above-mentioned use.
    In the context of the invention, by "lying between x and y", or "ranging from x to y", is meant an interval in which the limits x and y are included. For example, the range "between 0.68% and 1.00%" notably includes the values 0.68% and 1.00%.
    The following examples illustrate the invention without, however, limiting it.
    EXPERIMENTAL PART
    Preparation of compositions A to F
    The following products were used for the manufacture of the putty compositions according to the invention: the following silylated polymers: • GENIOSIL® XB502 (available from WACKER); • MS POLYMER® S 227 (available from KANEKA); • DESMOSEAL® SXP2636 (available from BAYER); SILQUEST® A-1120: N- (beta-aminoethyl) -gamma-aminopropyltrimethoxysilane type catalyst, available from the company MOMENTIVE; MIKHART® 1T: calcium carbonate with a density of 2.7 and an apparent density without packing of 0.7 g / cm3 and packing of 1 g / cm3, available from the company LA PROVENÇALE; DC 3074 ® (CAS number: 68957-04-0): dimethyl, methoxy phenyl, phenyl silsesquioxanes terminated methoxy, available from the company DOW CORNING; DC 3037® (CAS number: 68957-04-0): dimethyl, methoxy phenyl, phenyl silsesquioxanes terminated methoxy, available from the company DOW CORNING; DBU: diazabicycloundecene crosslinking catalyst, available from SIGMA-ALDRICH; MESAMOLL®: plasticizer ester of alkylsulphonic acid and phenol, available from the company LANXESS; KRONOS® 2059: pigment ΤίΟ2, available from KRONOS; CRAYVALLAC® SLX: rheological additive, available from the company ARKEMA; - TINUVIN ™ 770: antioxidant type bis (2,2,6,6-tetramethyl-4-piperidinyl) sebacate, available from the company BASF; - TINUVIN® 328: UV absorber of the benzotriazole type, available from the company BASF; DYNASYLAN® VTMO: vinyltrimethoxysilane moisture absorber, available from the company EVONIK.
    The compositions A to F were prepared according to the following procedure:
    Table 1: compositions A to F
    In this table 1, the proportions indicated are in parts by weight.
    The compositions A, B and E are comparative compositions, in which the content of silsequioxane (A) is: - equal to 0 (composition A); - less than 0.5% by weight relative to the total weight of the composition (composition B), or - greater than 1.4% by weight relative to the total weight of the composition (composition E).
    Properties of crosslinked compositions
    The properties obtained from the putty compositions A to F are summarized in Table 2 below:
    Table 2
    The measurement of skin formation time (or “skinning time” in English) was carried out in a controlled atmosphere at a temperature of 20 ° C. and a relative humidity of approximately 60%.
    The composition was applied using a wooden spatula and in the form of a thin film of thickness approximately 0.5 mm, on a glass slide of length 76 mm and width 26 mm. Immediately after the application of said film, a stopwatch was started and it was examined every minute using a light finger press if the film is dry or if a composition residue is transferred to the finger . The skin formation time is the time at the end of which the composition film is dry and for which there is no longer any transfer of adhesive residue on the finger. The result is expressed in minutes.
    The measurement of resistance and elongation at break (or "elongation at break" in English) by tensile test was carried out according to the protocol described below.
    The principle of the measurement consists in drawing in a tensile machine, the movable jaw of which moves at a constant speed equal to 100 mm / minute, a standard test tube made up of the crosslinked composition and to record, at the moment when the rupture occurs. of the test piece, the applied tensile stress (in MPa) as well as the elongation of the test piece (in%). The standard test piece is dumbbell-shaped, as illustrated in the international standard ISO 37. The narrow part of the dumbbell used is 20 mm long, 4 mm wide and 500 μm thick.
    Cross-linking after 24 hours ("cure 24h" in English ") consists of applying, at right angle peeling, a flat bead of the product to be examined, of constant width and increasing thickness. This cord was obtained by filling a calibrated gutter, 10 mm wide and linearly varying in depth from 0 to 10 mm. The assembly was carried out in PTFE. After application for 24 h in an air-conditioned enclosure at 23 ° C and 50% RH, the level at which the product, still pasty (not polymerized on the thickness) is bonded to the assembly, was noted using graduations.
    The 100% elongation module was measured according to the test in ISO11600 of 2002, which refers to ISO8339 of 2005.
    The elastic recovery was determined according to the test appearing in the ISO11600 standard of 2002, which refers to the ISO7389 standard of 2002.
    The results of Table 2 show that the compositions according to the invention C, D and E advantageously lead to elastic mastics with low modulus, insofar as: the modulus at 100% elongation is less than or equal to 0.40 MPa; and the elastic recovery is greater than or equal to 70%.
    On the contrary, the comparative compositions A, B and F do not have these characteristics of low modulus sealant. Comparative compositions A and B in particular have a 100% modulus of elongation greater than 0.40 MPa, while comparative composition F exhibits an elastic recovery of less than 70%.
    The compositions C, D and E according to the invention lead to sealants advantageously having a good compromise between good mechanical properties, elastic properties and adhesion. Compositions C, D and E show in particular good adhesion to concrete substrates.
    权利要求:
    Claims (19)
    [1" id="c-fr-0001]
    1. Composition comprising: from 0.68% to 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group; - at least one silylated polymer comprising at least one alkoxysilane group, preferably from 3% to 80% of at least one silylated polymer comprising at least one alkoxysilane group; and at least 25% by weight of at least one carbonated filler, the percentages by weight being expressed relative to the total weight of said composition.
    [2" id="c-fr-0002]
    2. Composition according to claim 1, in which the silsesquioxane (A) has the following general formula (I):

    in which each of R'1 to R'8 represents, independently of each other, a group chosen from: a hydrogen atom, a radical chosen from the group consisting of a linear or branched C1-C4 alkoxy radical, a linear or branched alkyl radical comprising from 1 to 30 carbon atoms, an alkenyl radical comprising from 2 to 30 carbon atoms, an aromatic radical comprising from 6 to 30 carbon atoms, an allyl radical comprising from 3 to 30 carbon atoms , an aliphatic cyclic radical comprising from 3 to 30 carbon atoms, an acyl radical comprising from 1 to 30 carbon atoms, and - a group -OSiR'9R'10 in which R'9 and R'10 each independently represent l '' one of the other, a hydrogen atom or a radical chosen from

    the group consisting of linear or branched C1-C4 alkyls, linear or branched C1-C4 alkoxys, C2-C4 alkenyls, a phenyl, a C3-C6 allyl radical, an aliphatic radical C3-C8 ring, and a C1-C4 acyl radical; provided: at least one radical from the radicals R’1 to R’8 is a C1-C4 alkoxy radical; and - that at least one radical among the radicals R’1 to R’8 is a phenyl radical.
    [3" id="c-fr-0003]
    3. Composition according to any one of claims 1 or 2, in which the silsesquioxane (A) comprises from 10% to 20% by weight, preferably from 12% to 20% by weight, preferably from 15% to 18% by weight. weight of alkoxy group, preferably methoxy.
    [4" id="c-fr-0004]
    4. Composition according to any one of claims 1 to 3, in which the silsesquioxane (A) comprises at least one methyl group.
    [5" id="c-fr-0005]
    5. Composition according to claim 4, in which the silsesquioxane (A) comprises a weight ratio of phenyl group (s): methyl group (s) ranging from 1:10 to 10: 1, preferably from 1: 5 to 5: 1 , advantageously from 1: 4 to 4: 1, in particular from 1: 2 to 2: 1, and preferably said ratio is 1: 1 or 0.25: 1.
    [6" id="c-fr-0006]
    6. Composition according to any one of claims 1 to 5, in which the silsesquioxane (A) has a viscosity at 23 ° C ranging from 10 to 200 mPa.s, preferably ranging from 90 to 150 mPa.s, preferably from 110 to 130 mPa.s.
    [7" id="c-fr-0007]
    7. Composition according to any one of claims 1 to 6, in which the silsesquioxane (A) has a weight-average molar mass ranging from 500 g / mol to 3000 g / mol, preferably from 800 g / mol to 2000 g / mol, and advantageously from 800 g / mol to 1500 g / mol, for example from 800 g / mol to 1300 g / mol or from 1000 g / mol to 1500 g / mol.
    [8" id="c-fr-0008]
    8. Composition according to any one of claims 1 to 7, characterized in that the content of silsesquioxane (A) in said composition is chosen from one of the following weight contents: from 0.68% to 1.00%, from 0.69% to 1.00%, from 0.70% to 1.00%, from 0.71% to 1.00%, from 0.72% to 1.00%, from 0.73% to 1.00%, 0.74% to 1.00%, 0.75% to 1.00%, 0.76% to 1.00%, 0.77% to 1.00%, 0.78% to 1.00%, 0.79% to 1.00%, 0.80% to 1.00%, 0.81% to 1.00%, 0.82% to 1 .00%, from 0.83% to 1.00%, from 0.84% to 1.00%, from 0.85% to 1.00%, from 0.86% to 1.00%, from 0 , 87% to 1.00%, 0.88% to 1.00%, 0.89% to 1.00%, 0.90% to 1.00%, 0.91% to 1, 00%, from 0.92% to 1.00%, from 0.93% to 1.00%, from 0.94% to 1.00%, or from 0.95% to 1.00%.
    [9" id="c-fr-0009]
    9. Composition according to any one of claims 1 to 8, in which the silylated polymer (s) / silsesquioxane (A) weight ratio is between 33 and 22, preferably between 32.9 and 22.5, preferably between 32.85 and 22.97.
    [10" id="c-fr-0010]
    10. Composition according to any one of claims 1 to 9, comprising from 2 to 5, preferably from 3 to 4.5, and preferably from 3 to 4.4 parts by weight of silsesquioxane (A) per 100 parts by weight of silylated polymer (s).
    [11" id="c-fr-0011]
    11. Composition according to any one of claims 1 to 10, in which the silylated polymer comprising at least one alkoxysilane group is chosen from the polymers of formulas (II), (III) or (IV) as defined below, and their mixtures:

    (II)

    ï (III)

    (IV)



    in which: - R1 represents a divalent hydrocarbon radical comprising from 5 to 15 carbon atoms which can be aromatic or aliphatic, linear, branched or cyclic, - R ° represents a divalent linear or branched alkylene radical comprising from 3 to 6 carbon atoms , - R3 represents a linear or branched divalent alkylene radical comprising from 1 to 6 carbon atoms, preferably R3 representing methylene or n-propylene, - R2 represents a linear or branched divalent alkylene radical comprising from 2 to 4 carbon atoms, - R4 and R5, identical or different, each represent a linear or branched alkyl radical comprising from 1 to 4 carbon atoms, preferably R4 and R5 representing methyl, - R6 represents a hydrogen atom, a phenyl radical or a linear alkyl radical , branched or cyclic comprising from 1 to 6 carbon atoms, a 2-succinate radical of formula:

    in which R7 is a linear or branched alkyl radical comprising from 1 to 6 carbon atoms, - n is an integer such that the number-average molecular mass of the polyether block of formula - [OR2] ,, - ranges from 300 g / mol to 40,000 g / mol, - rm is zero or an integer, - n and mi are such that the number-average molecular mass of the polymer of formula (III) ranges from 500 g / mol to 50,000 g / mol, preferably from 700 g / mol to 20,000 g / mol, - m is an integer other than zero, - n and m are such that the number-average molecular mass of the polymer of formula (IV) ranges from 500 g / mol at 50,000 g / mol, preferably from 700 g / mol to 20,000 g / mol, - p is an integer equal to 0, 1 or 2, p being preferably 0 or 1.
    [12" id="c-fr-0012]
    12. Composition according to claim 11, comprising: at least one polymer of formula (II), and at least one polymer of formula (III); or at least one polymer of formula (II), and at least one polymer of formula (IV); or at least one polymer of formula (III), and at least one polymer of formula (IV); or

    at least one polymer of formula (II), at least one polymer of formula (III), and at least one polymer of formula (IV).
    [13" id="c-fr-0013]
    13. Composition according to any one of claims 11 to 12, in which the polymer of formula (III) is such that: - mi is an integer equal to or different from 0, - p = 0 or 1, preferably p = 0, - R4 and R5 each represent a methyl radical, - R3 represents a divalent methylene or n-propylene radical, - the number-average molecular mass of said polymer ranges from 5,000 to 30,000 g / mol, preferably from 10,000 to 20 000 g / mol, in particular from 14,000 to 16,000 g / mol.
    [14" id="c-fr-0014]
    14. Composition according to one of claims 11 to 13, in which the polymer of formula (II) is such that: - p = 0 or 1, preferably p = 1, - R ° represents a divalent n-propylene radical, - R4 and R5 each represents a methyl group, - the number-average molecular mass of said polymer ranges from 5,000 to 30,000 g / mol, preferably from 10,000 to 20,000 g / mol.
    [15" id="c-fr-0015]
    15. Composition according to any one of claims 1 to 14, comprising: from 3% to 80% by weight, preferably from 5% to 50% by weight, preferably from 10% to 50% by weight, advantageously from 10% at 40% by weight of at least one silylated polymer comprising at least one alkoxysilane group, - from 0.1% to 1% by weight, preferably from 0.1% to 0.6% by weight, at least a catalyst, from 25% to 80% by weight, preferably from 40% to 60% by weight, of at least one carbonated filler, - from 0 %% to 30% by weight, in particular from 0.1% to 30% by weight, preferably from 0.5% to 20% by weight, preferably from 0.5% to 15% by weight of at least one additive chosen from plasticizers, solvents, pigments, adhesion promoters , moisture absorbers, UV stabilizers, flakes, fluorescent materials, rheological additives, fillers other than carbonate fillers, and mixtures thereof; and from 0.68% to 1.00% by weight, preferably from 0.69% to 1.00% by weight, preferably from 0.75% to 1.00% by weight, and advantageously from 0.80% at 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group.
    [16" id="c-fr-0016]
    16. Composition according to any one of claims 1 to 15, comprising: - from 15% to 80% by weight, preferably from 15% to 50% by weight of at least one silylated polymer comprising at least one alkoxysilane group, - from 0.1% to 1% by weight, preferably from 0.1% to 0.6% by weight, of at least one catalyst, - from 25% to 55% by weight, preferably from 40% to 55 % by weight, of at least one carbonated filler, from 10% to 30% by weight of at least one plasticizer, from 0.1% to 3% by weight of at least one moisture absorber, from 0, 1% to 10% by weight of at least one filler other than the carbonated filler (s); from 0.1% to 20% by weight, preferably from 0.1% to 10% by weight of at least one additive chosen from solvents, pigments, adhesion promoters, UV stabilizers, flakes, fluorescent materials, rheological additives, and mixtures thereof; and - from 0.68% to 1.00% by weight, preferably from 0.69% to 1.00% by weight, preferably from 0.75% to 1.00% by weight, and advantageously from 0.80 % to 1.00% by weight of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group.
    [17" id="c-fr-0017]
    17. Composition according to any one of claims 1 to 16, in which the carbonate filler is chosen from alkali or alkaline earth metal carbonates and their mixtures, preferably the carbonate filler is calcium carbonate.
    [18" id="c-fr-0018]
    18. Use of a composition according to any one of claims 1 to 17, as adhesive, sealant or coating, preferably as sealant, for example as construction sealant.
    [19" id="c-fr-0019]
    19. Use of at least one silsesquioxane (A) comprising at least one phenyl group and at least one alkoxy group to prepare a composition having, after crosslinking: a modulus at 100% elongation less than or equal to 0.4 MPa; and an elastic recovery greater than or equal to 70%, the content of silsequioxane (A) in the composition ranging from 0.68% to 1.00% by weight relative to the total weight of said composition.
    类似技术:
    公开号 | 公开日 | 专利标题
    FR3066765B1|2019-06-14|SILYL LOW MODULE MASTIC COMPOSITION
    JP5251493B2|2013-07-31|Curable composition
    FR2753708A1|1998-03-27|AQUEOUS SILICONE DISPERSION, CROSS-LINKABLE BY CONDENSATION INTO AN ADHERENT ELASTOMER ON MANY SUBSTRATES AND SEALANT CONSTITUTED BY LEDIT ELASTOMER
    JP2013076094A|2013-04-25|Curable composition
    WO2016174009A1|2016-11-03|Use of a composition made from silylated polymers as jointing mortar for a surface coating
    EP3768424B1|2022-03-02|Catalytic composition for an adhesive composition based on a cross-linkable silylated polymer
    FR3052457A1|2017-12-15|ADHESIVE COMPOSITIONS BASED ON RETICULABLE SILYLENE POLYMERS
    WO2021099746A1|2021-05-27|Silylated polymer-based moisture-crosslinkable composition
    FR3101079A1|2021-03-26|COMPOSITION OF SEALULATING SEALANT TO HUMIDITY FOR EXPOSURE OF THE JOINT TO HIGH TEMPERATURE
    EP3596183A1|2020-01-22|Plasticised mastic adhesive composition without phthalate
    EP3947499A1|2022-02-09|Method for preparing a cross-linkable composition
    EP3394144A1|2018-10-31|Superelastic polyurethane mastics
    EP3595805B1|2021-06-02|Thixotropic composition that can be used as an anti-running agent for mastics
    EP3397708B1|2020-04-08|Liquid composition for a waterproofing membrane
    FR3102481A1|2021-04-30|IONIC SILYL COPOLYURETHANE AND SEALANT COMPOSITION CONTAINING IT
    EP3838957A1|2021-06-23|Polyimines and uses thereof
    EP3728386A1|2020-10-28|Method for producing a composition comprising a polyurethane with nco end groups
    WO2018178319A1|2018-10-04|Polyaddition-crosslinkable silicone composition useful for overmolding parts
    FR3068633A1|2019-01-11|PREPARATION OF AN ADHESIVE COMPOSITION IN AN EXTRUDER
    同族专利:
    公开号 | 公开日
    CN110637051A|2019-12-31|
    EP3630878A1|2020-04-08|
    EP3630878B1|2021-03-17|
    FR3066765B1|2019-06-14|
    WO2018215463A1|2018-11-29|
    US11104803B2|2021-08-31|
    BR112019022339A2|2020-05-19|
    US20200095377A1|2020-03-26|
    CN110637051B|2021-11-16|
    JP2020521034A|2020-07-16|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20100267879A1|2007-10-25|2010-10-21|Idemitsu Kosan Co., Ltd|Polycarbonate resin composition, polycarbonate resin molded article, and method for producing the same|
    EP2886575A1|2013-12-18|2015-06-24|Bostik Sa|Use of an adhesive composition based on silylated polymers for cryogenic applications|
    WO2016174009A1|2015-04-28|2016-11-03|Bostik Sa|Use of a composition made from silylated polymers as jointing mortar for a surface coating|
    WO2016202359A1|2015-06-15|2016-12-22|Bison International B.V.|High strength and moisture resistant adhesive|WO2021099746A1|2019-11-21|2021-05-27|Bostik Sa|Silylated polymer-based moisture-crosslinkable composition|
    EP3878909A1|2020-03-09|2021-09-15|Bostik SA|Silylated sealing composition with improved adhesion on metallic substrates|US3547848A|1967-11-03|1970-12-15|Armour Ind Chem Co|Thixotropic coating compositions comprising a varnish and a di-substituted urea|
    US6602964B2|1998-04-17|2003-08-05|Crompton Corporation|Reactive diluent in moisture curable system|
    US6310170B1|1999-08-17|2001-10-30|Ck Witco Corporation|Compositions of silylated polymer and aminosilane adhesion promoters|
    WO2006049087A1|2004-11-01|2006-05-11|Kaneka Corporation|Process for production of polyether polymers and compositions containing the polymers|
    FR2925517B1|2007-12-21|2010-01-08|Bostik Sa|ADHESIVE SENSITIVE TO ADHESIVE PRESSURE STABLE IN TEMPERATURE.|
    JP5509312B2|2009-03-23|2014-06-04|ダウコーニングコーポレーション|Chemically curable integrated warm edge spacers and seals|
    FR2954341B1|2009-12-21|2014-07-11|Bostik Sa|ADHESIVE COMPOSITION RETICULABLE BY HEATING|
    US8859674B2|2011-03-31|2014-10-14|Momentive Performance Materials Inc.|Moisture curable silylated polymer compositions with improved adhesion to concrete|
    WO2012145636A1|2011-04-20|2012-10-26|Dow Corning Corporation|Aqueous stable compositions of alkali metal alkyl siliconates with arylsilanes, silsesquioxanes, or fluorinated alkylsilanes, and surface treatment methods using the compositions|
    DE102011081264A1|2011-08-19|2013-02-21|Wacker Chemie Ag|Crosslinkable compositions based on organyloxysilane-terminated polymers|
    MX355532B|2012-03-12|2018-04-20|Bostik Sa|Breathable self-adhesive articles.|
    DE102012223422A1|2012-12-17|2014-06-18|Henkel Ag & Co. Kgaa|Low-modulus silane-terminated PU prepolymers|
    DE102015201099A1|2015-01-22|2016-07-28|Wacker Chemie Ag|Crosslinkable coating compositions based on organyloxysilane-terminated polymers|FR3090679B1|2018-12-20|2020-12-11|Bostik|NEW HEATING CURLABLE COMPOSITIONS AND CORRESPONDING SELF-ADHESIVE ARTICLES|
    FR3101079B1|2019-09-19|2022-01-21|Bostik Sa|MOISTURE-CURABLE SEALANT COMPOSITION FOR EXPOSURE OF JOINT TO HIGH TEMPERATURES|
    法律状态:
    2018-04-11| PLFP| Fee payment|Year of fee payment: 2 |
    2018-11-30| PLSC| Publication of the preliminary search report|Effective date: 20181130 |
    2019-04-10| PLFP| Fee payment|Year of fee payment: 3 |
    2020-02-28| CA| Change of address|Effective date: 20200122 |
    2020-04-14| PLFP| Fee payment|Year of fee payment: 4 |
    2021-04-12| PLFP| Fee payment|Year of fee payment: 5 |
    优先权:
    申请号 | 申请日 | 专利标题
    FR1754554|2017-05-23|
    FR1754554A|FR3066765B1|2017-05-23|2017-05-23|SILYL LOW MODULE MASTIC COMPOSITION|FR1754554A| FR3066765B1|2017-05-23|2017-05-23|SILYL LOW MODULE MASTIC COMPOSITION|
    US16/614,478| US11104803B2|2017-05-23|2018-05-22|Low modulus silylated mastic composition|
    PCT/EP2018/063381| WO2018215463A1|2017-05-23|2018-05-22|Low modulus silylated mastic composition|
    JP2019564900A| JP2020521034A|2017-05-23|2018-05-22|Low modulus silylated mastic composition|
    EP18724583.2A| EP3630878B1|2017-05-23|2018-05-22|Low modulus silylated mastic composition|
    CN201880033874.3A| CN110637051B|2017-05-23|2018-05-22|Low modulus silylated adhesive compositions|
    BR112019022339A| BR112019022339A2|2017-05-23|2018-05-22|low modulus silylated mastic composition|