    • 专利摘要:
    A conformation tooling (100) for the chemical vapor infiltration of a fibrous preform comprises a structural enclosure formed by supports (140, 170) each provided with a multiperforated zone (141; 171). The supports (140, 170) have on their inside a disbursed zone (143; 173) including the multiperforated zone. The conformation tooling (100) further comprises first and second shaping mold functional elements (120, 150) each respectively present in the disbursed area of the supports. Each conformation mold functional element comprises a first face (120a; 150a) having a determined shape corresponding to a part shape to be produced and a second face (120b; 150b) held opposite the inner face of a support. Each functional element has a plurality of perforations (121; 151) and has a number of perforations, a size of perforations or a geometry of perforations different from the number, size or geometry of the perforations present on the support vis-à-vis. -screw.
    公开号:FR3059679A1
    申请号:FR1662040
    申请日:2016-12-07
    公开日:2018-06-08
    发明作者:Simon THIBAUD；Adrien Delcamp；Sebastien Bertrand；Stephane Goujard
    申请人:Safran Ceramics SA；
    IPC主号:
    专利说明:

    ® FRENCH REPUBLIC
    NATIONAL INSTITUTE OF INDUSTRIAL PROPERTY © Publication number: 3,059,679 (to be used only for reproduction orders)
    ©) National registration number: 16 62040
    COURBEVOIE
    ©) Int Cl 8 : C 23 C 16/458 (2017.01), C 23 C 16/455
    A1 PATENT APPLICATION
    ©) Date of filing: 07.12.16. ©) Applicant (s): SAFRAN CERAMICS Société ano- (30) Priority: nyme - FR. ©) Inventor (s): THIBAUD SIMON, DELCAMP ADRIEN, BERTRAND SEBASTIEN and GOUJARD STE- (43) Date of public availability of the PHANE. request: 08.06.18 Bulletin 18/23. (56) List of documents cited in the report preliminary research: Refer to end of present booklet @) References to other national documents ©) Holder (s): SAFRAN CERAMICS Société anonyme. related: ©) Extension request (s): @) Agent (s): CABINET BEAU DE LOMENIE.
    CONFORMATION TOOLS AND INSTALLATION FOR GAS PHASE CHEMICAL INFILTRATION OF FIBROUS PREFORMS.
    FR 3 059 679 - A1 (3g) A shaping tool (100) for the chemical vapor infiltration of a fibrous preform comprises a structural enclosure formed by supports (140, 170) each provided with a multi-perforated zone ( 141; 171). The supports (140, 170) have, on their internal face, a recessed area (143; 173) including the multi-perforated area. The shaping tool (100) further comprises first and second functional shaping mold elements (120, 150) each present respectively in the lowered area of the supports. Each functional element of the shaping mold has a first face (120a; 150a) having a determined shape corresponding to a shape of part to be produced and a second face (120b; 150b) held opposite the internal face of a support. Each functional element comprises a plurality of perforations (121; 151) and has a number of perforations, a size of perforations or a geometry of perforations different from the number, size or geometry of the perforations present on the support opposite. -screw.
    100
    Invention background
    The present invention relates to the production of parts made of composite material and, more particularly, the shaping tool used during consolidation and / or densification by chemical gas infiltration of a fibrous preform intended to form the reinforcement of the part in composite material.
    One field of application of the invention is that of making parts from thermostructural composite material, that is to say from composite material having both mechanical properties which make it suitable for constituting structural parts and the capacity to keep these properties up to high temperatures. Typical examples of thermostructural composite materials are carbon / carbon (C / C) composites having a carbon fiber reinforcement texture densified by a pyrolytic carbon matrix and ceramic matrix composites (CMC) having a fiber reinforcement texture refractories (carbon or ceramic) densified by a ceramic matrix.
    A well-known process of consolidation or densification of fiber preforms to make C / C composite or CMC parts is chemical gas infiltration (CVI). The fibrous preforms to be consolidated or densified are placed in a multi-perforated shaping tool itself placed in a reactor or oven where it is heated. A reactive gas containing one or more gaseous precursors of the material constituting the matrix is introduced into the reactor. The temperature and the pressure in the reactor are adjusted to allow the reactive gas to diffuse within the porosity of the preforms via the perforations of the former and to form there a deposit of the material constituting the matrix by decomposition of one or more constituents reactive gas or reaction between several constituents, these constituents forming the precursor of the matrix. An interphase material can further be deposited with the matrix by this method.
    However, this consolidation / densification technique results in certain cases in the appearance of matrix deposition gradients in the direction of the thickness of the fibrous preform as well as local thickenings or "pustules" on the surface of the preform. Indeed, between the surface and the heart of the preform, the thickness or the quantity of matrix deposited can vary by a factor of 5. These drawbacks are mainly due to an inadequacy between the characteristics of the fibrous preform (thickness of the preform , nature of the fibers, weaving weave, etc.) and the structural characteristics of the shaper (number of perforations, size and shape of the perforations, etc.).
    Subject and summary of the invention
    The invention therefore aims to provide a solution for a shaping tool, the structural characteristics of which can be defined as a function of the fiber preform to be consolidated and / or densified.
    This object is achieved with a shaping tool for chemical vapor infiltration of a fibrous preform, the tool comprising a structural enclosure formed by at least a first support comprising a first multi-perforated zone surrounded by a first contact plane. and a second support comprising a second multi-perforated area surrounded by a second contact plane, the first and second supports being held one against the other at the level of the first and second contact areas, characterized in that the first support comprises on its internal face a first unpacked zone including the first multiperforated zone, in that the second support comprises on its internal face a second unpacked zone including the second multiperforated zone, and in that the shaping tool further comprises at least first and second functional elements of the shaping mold respectively present in the first and second disbursed areas of the first and second supports, each functional element of the shaping mold comprising a first face having a determined shape corresponding to a shape of part to be produced and a second face held opposite the internal face of a support. , each functional element of the shaping mold comprising a plurality of perforations and having at least a number of perforations or a size of perforations or a geometry of perforations different from the number, the size or the geometry of the perforations present on the screw support opposite.
    Thus, the shaping tool according to the invention comprises functional elements of removable shaping mold whose size, number and / or geometry of the perforations can be defined according to the characteristics of the fiber preform to be consolidated or densified in order to '' obtain a more homogeneous matrix and / or interphase deposition in the preform considered. It is thus possible to manufacture parts from composite material having improved mechanical properties.
    The shaping tool of the invention has great flexibility of adaptation while limiting the cost of this adaptation. Indeed, in case of adaptation of the shaping tool to a particular fibrous preform, only the functional elements of the shaping mold are changed, the main part of the tool, namely the supports forming the structural enclosure, being preserved.
    According to a first characteristic of the shaping tool of the invention, a porous depletion layer is interposed between the internal face of each support of the structural enclosure and the second face of the functional element of the shaping mold maintained in vis-à-vis the internal face of the support.
    By consuming a fraction of the precursor gases of the gas phase in a depletion layer before it reaches the fiber preform, the quantity of matrix deposited on the surface of the fiber preform is reduced, which avoids rapid plugging of the porosity on the surface of the preform and preserving a network of porosity longer allowing the gas phase to flow to the heart of the preform. A more homogeneous matrix deposit is thus obtained in the thickness of the preform limiting the deposit gradients in the preform.
    The porous depletion layer may in particular be chosen from one of the following textures: carbon mat, two-dimensional carbon fabric, carbon felt.
    According to a second characteristic of the shaping tool of the invention, the supports and the shaping mold elements are made of a material chosen from at least one of the following materials: graphite, carbon / carbon composite material (C / C) and ceramic matrix composite material (CMC).
    The invention also relates to a load intended to be placed in a densification installation by chemical vapor infiltration, said load comprising a fibrous preform maintained in a shaping tool according to the invention.
    As indicated above, such a loading carried out with the shaping tool of the invention not only makes it possible to consolidate or densify a preform with a more homogeneous deposition of matrix and / or interphase but also to avoid the formation of local extra thicknesses or "pustules" on the surface of the preform.
    According to a particular aspect of the loading of the invention, the fibrous preform is a preform of an aeronautical engine part.
    The invention also relates to an installation for densification by chemical gas infiltration of a fiber preform, comprising a reaction chamber, a reactive gas inlet pipe situated at a first end of the chamber and opening into a preheating zone. , and a discharge pipe located near a second end, characterized in that the chamber comprises at least one load according to the invention.
    The subject of the invention is also a method of manufacturing a part made of composite material comprising:
    the placement of a fibrous preform in a shaping tool according to the invention,
    - consolidation of the porous preform by chemical gas infiltration of a matrix,
    - densification of the consolidated preform.
    Brief description of the drawings
    Other characteristics and advantages of the invention will emerge from the following description of particular embodiments of the invention, given by way of nonlimiting examples, with reference to the appended drawings, in which:
    - Figure 1 is an exploded schematic view showing the mounting and loading of a shaping tool with a fibrous preform according to an embodiment of the invention;
    - Figure 2 is a top view of the tool of Figure 1 once mounted;
    - Figure 3 is a sectional view along the line III of the tool of Figure 2;
    - Figure 4 is a sectional view along the line IV of the tool of Figure 2;
    - Figure 5 illustrates an alternative embodiment of a shaping mold element;
    FIG. 6 is a schematic perspective view of an installation for densification by chemical infiltration in the gas phase comprising a charge constituted by the tool and the fiber preform of FIG. 1.
    Detailed description of embodiment
    The present invention applies to the manufacture of parts made of composite material and in particular of thermostructural composite material. More particularly, the invention finds an advantageous application during the stages of consolidation and / or densification by chemical gas infiltration of fibrous preforms.
    Figure 1 shows the realization of a load comprising the establishment of a fibrous preform 10 in a shaping tool 100 according to an embodiment of the invention. Once completed, the charge is intended to be introduced into a reaction chamber of an industrial chemical gas infiltration installation. In the example described here, the tool 100 is intended to receive fibrous preforms in the form of plates intended in particular for the characterization of composite materials. The shaping tool of the invention can be used to receive and shape fibrous preforms for the production of parts of various shapes such as, for example, blades or movable flaps of the nozzle of aeronautical engines.
    The fibrous preform 10 corresponds to a “dry” fibrous texture, that is to say one not impregnated with a resin or the like. The fibrous texture can be made of fibers of various natures, in particular ceramic fibers (for example silicon carbide) or carbon fibers. The fibrous texture used can be of various natures and forms such as in particular:
    two-dimensional (2D) fabric,
    - three-dimensional (3D) fabric obtained by 3D or multilayer weaving as described in particular in document WO 2010/061140,
    - braid,
    - knitting,
    - felt,
    - unidirectional ply (UD) of wires or cables or multidirectional ply (nD) obtained by superposition of several UD plies in different directions and bonding of the UD plies together for example by sewing, by chemical bonding agent or by needling.
    It is also possible to use a fibrous structure formed of several superimposed layers of fabric, braid, knit, felt, tablecloths, cables or the like, which layers are linked together for example by sewing, by implantation of threads or rigid elements or by needling .
    The shaping tool 100 comprises a structural enclosure formed here by a first support 140 and a second support 170. The first support 140 comprises a first multi-perforated area 141 comprising a plurality of perforations 1410 passing through the first support in its thickness, the multi-perforated zone 141 being surrounded by a rim 142.
    The second support 170 comprises a second multi-perforated area 171 comprising a plurality of perforations 1710 passing through the second support in its thickness, the multi-perforated area 171 being surrounded by a flange 172.
    According to the invention, the shaping tool 100 also comprises a first functional member of the shaping mold 120 and a second functional member of the shaping mold 150. The first functional shaping member 120 is intended to be housed in a first disassembled zone 143 present on the internal face 140a of the first support 140 and including the first multi-perforated zone 141, the first functional element of shaping mold 120 resting on the rim 142 which makes it possible to maintain this element at a distance from the internal face 140a of the first support 140 (Figures 3 and 4). The second functional shaping mold element 150 is intended to be housed in a second recessed area 173 present on the internal face 170a of the second support 170 and including the second multi-perforated area 171, the second functional shaping mold element 150 resting on the rim 172 which allows this element to be kept away from the internal face 170a of the second support 170 (FIGS. 3 and 4). The first and second functional elements of the shaping mold 120 and 150 each have a first face 120a, respectively 150a, having a determined shape corresponding to a shape of part to be produced, here a plate. The first functional element of the shaping mold 120 comprises a second face 120b intended to be held vis-à-vis the internal face 140a of the first support 140 at the level of the first unzipped area 143 by the rim 142 while the second element functional mold 150 has a second face 150b intended to be held vis-à-vis the internal face 170a of the second support 170 at the level of the second recessed area 173 by the rim 172. The first and second functional elements of shaping mold 120 and 150 have a plurality of perforations 121 and 151.
    According to the invention, the number, size and / or geometry of the perforations 121 and 151 present respectively on the first and second functional elements of the shaping mold 120 and 150 differ with respect to the number, size and / or geometry perforations present on the support opposite. In the example described here, the first functional element of the shaping mold 120 has a greater number of perforations 121 than the number of perforations 1410 present on the first support 140. Similarly, the second functional element of the shaping mold 150 comprises a greater number of perforations 151 than the number of perforations 1710 present on the second support 170. This makes it possible to increase the number of entry points of the gas phase into the fibrous texture and to fractionate the gaseous phase entering through the perforations 1410 and 1710 of the supports 140 and 170 before it comes into contact with the fibrous preform. This limits local excess thicknesses and gradients of deposit thicknesses in the thickness of the part to be consolidated or the formation of pustules in the fibrous preform.
    Furthermore, the perforations 121 and 151 are preferably positioned respectively on the first and second functional mold elements of conformation 120 and 150 in a manner offset from the perforations 1410 and 1710 present respectively on the first and second supports 140 and 170 (figures 3 and 4). This makes it possible to further limit the appearance of local excess thicknesses and to limit the gradients of thicknesses of deposit in the thickness of the part to be consolidated or the formation of pustules in the fibrous preform.
    FIG. 5 illustrates an alternative embodiment of a functional element of the shaping mold 200 comprising a plurality of perforations 201 of oblong shape. Other forms of perforation can be envisaged as a function of parameters linked to the fiber preform to be densified. In the case of the shaping mold 200, the overall surface area of the perforations is increased through which the fibrous preform is exposed to the precursor gases entering the tool through the supports of the structural enclosure. In this case, the appearance of local excess thicknesses or pustules in the fibrous preform is also limited.
    According to a particular aspect of the invention, a porous depletion layer can be interposed between a support of the structural enclosure and a functional element of the shaping mold. In the example described here, a first porous depletion layer 130 is interposed between the internal face 140a of the first support 140 and the second face 120b of the first functional element of the shaping mold 120 kept at a distance from the internal face 140a by the rim 142 while a second depletion layer 160 is interposed between the internal face 170a of the second support 170 and the second face 150b of the second functional element of the shaping mold 150 kept at a distance from the internal face 170a by the rim 172. The porous depletion layers 130 and 160 make it possible to “pre-consume” part of the precursor gases of the gaseous phase entering through the performances 141 and 171 of the supports 140 and 170. This limits the gradients of matrix deposits in the preform fibrous. Indeed, by consuming a fraction of the precursor gases of the gas phase before it reaches the fibrous preform, the quantity of matrix deposited on the surface of the fibrous preform is reduced, which avoids rapid clogging of the porosity on the surface of the preform and to preserve a network of porosity longer allowing the gas phase to flow to the heart of the preform. A more homogeneous matrix deposit is thus obtained in the thickness of the preform limiting the deposit gradients in the preform. The porous depletion layers can in particular be produced from two-dimensional fabrics made of silicon carbide fibers (SiC) or of carbon fiber felts.
    The supports forming the structural enclosure as well as the functional elements of the shaping mold can be produced in particular from graphite or from other materials capable of withstanding the temperatures encountered during consolidation operations or chemical densification in the gas phase, such as composite materials. carbon / carbon or ceramic matrix (CMC) such as for example C / SiC (carbon fiber reinforcement densified by a silicon carbide matrix) or SiC / SiC (silicon carbide reinforcement and matrix) materials.
    In the example described here, the fiber preform 10 is a preform obtained by three-dimensional weaving of SiC fibers of the HiNicalon® Type S type.
    The fiber preform 10 is placed in the shaping tool 100 (FIGS. 3 and 4) with a view to its consolidation by chemical infiltration in the gas phase. The tool is closed by clamping members constituted here by screws 101 and nut 102, spacers 105 being used to adjust the fit between the two supports 140 and 170. The fiber preform 10 and the tool 100 constitutes a load 200 which is placed in a gas phase chemical infiltration installation or furnace 500 illustrated in FIG. 6. In a manner known per se, the chemical gas infiltration installation 500 comprises a cylindrical enclosure 501 delimiting a reaction 510 closed in its upper part by a removable cover 520 provided with a gas inlet pipe 521 which opens into a preheating zone 522 allowing the gas to be heated before its diffusion into the reaction chamber 510 containing the preform (s) to densify. The residual gases are extracted at the bottom 530 of the installation by an evacuation pipe 531 which is connected to suction means (not shown). The bottom 530 comprises a support 532 on which the load 200 is intended to be deposited.
    The heating in the preheating zone as well as inside the reaction chamber 510 is produced by a graphite susceptor 511 forming an armature electromagnetically coupled with an inductor (not shown). The space present in the reaction chamber 510 between the preheating zone 522 and the support 532 corresponds to the useful loading volume 512 of the infiltration installation 500, that is to say the volume available for loading preforms fibrous to densify.
    The preform 10 is consolidated by chemical gas infiltration. In order to ensure the consolidation of the preform, a reactive gas containing at least one or more precursors of the material of the matrix to be deposited is introduced into the reaction chamber 510. In the case of a ceramic material, as here carbide of silicon (SiC), methyltrichlorosilane (MTS) can be used, as is well known per se, as a SiC precursor. In the case of carbon, for example, gaseous hydrocarbon compounds are used, typically propane, methane or a mixture of the two. The consolidation of the porous preform is ensured, in a manner well known per se, by deposition within it of the matrix material produced by decomposition of the precursor (s) contained in the reactive gas diffusing inside the internal porosity accessible from the preform. The pressure and temperature conditions necessary to obtain deposits of various matrices by chemical gas infiltration are well known in themselves. A pressure gradient is established between the supply line 521 and the evacuation line 531 in order to favor the passage of the reactive gas flows in the preform.
    Consolidation tests of a fibrous preform with a shaping tool according to the invention and of the same type as the tool 100 described above was carried out. More specifically, for these tests the following elements were used:
    - preform obtained by three-dimensional weaving of SiN HiNicalon® Type S fibers, the preform having a plate shape,
    - first and second supports of the shaping tool having perforations in their multi-perforated area with a diameter of 10 mm (phi 10 mm), the perforations being spaced from one another in a center to center pitch of 20 mm,
    - first and second functional elements of the shaping mold comprising perforations with a diameter of 5 mm (phi 5 mm) and spaced from one another in a center to center pitch of 8 mm,
    - porous depletion layer interposed between each support of the shaping tool and each shaping mold element, each layer being made from a felt made up of a tangle of graphite fibers sold by Le Carbone Lorraine , under the reference RVG 2000.
    The preform was consolidated by chemical gas infiltration of a BN and SIC phase.
    These tests have shown a reduction in the deposit thickness gradient, in the thickness of the part, by a factor of 5 in comparison with a shaping tool of the prior art. In addition, the deposit thickness gradients on the surface of the workpiece between an area directly exposed to the gas (area of the preform opposite a perforation of a functional element of the shaping mold) and a hidden area (area of the preform located between two perforations of a functional element of the shaping mold) have been reduced by a factor of 5 to 8 in comparison with a shaping tool of the prior art.
    权利要求:
    Claims (8)
    [1" id="c-fr-0001]
    1. Conformation tool (100) for chemical vapor infiltration of a fibrous preform, the tool comprising a structural enclosure formed by at least a first support (140) comprising a first multi-perforated zone (141) and a second support (170) comprising a second multi-perforated area (171), the first and second supports being held one against the other, characterized in that the first support (140) has on its internal face (140a) a first area unpacked (143) including the first multiperforated zone (141), in that the second support (170) has on its internal face (170a) a second unburdened zone (173) including the second multiperforated zone (172), and in that the shaping tool (100) further comprises at least first and second functional shaping mold elements (120, 150) present respectively in the first and second disbursed areas (143,173) of the first and second e supports (140, 170), each functional element of the shaping mold having a first face (120a; 150a) having a determined shape corresponding to a shape of part to be produced and a second face (120b; 150b) held opposite the internal face of a support, each functional element of the shaping mold comprising a plurality of perforations (121; 151) and having at least a number of perforations, a size of perforations or a geometry of perforations different from the number, the size or the geometry of the perforations present on the support opposite.
    [2" id="c-fr-0002]
    2. Tool according to claim 1, in which a porous depletion layer (130; 160) is interposed between the internal face of each support (140; 170) of the structural enclosure and the second face of the functional element of conformation mold (120; 150) held opposite the internal face of the support.
    [3" id="c-fr-0003]
    3. Tool according to claim 2, wherein the porous depletion layer is chosen from one of the following textures: carbon mat, two-dimensional carbon fabric, carbon felt.
    [4" id="c-fr-0004]
    4. Tool according to any one of claims 1 to 3, in which the supports (140, 170) and the functional elements of the shaping mold (120, 150) are made of a material chosen from at least one of the following materials: graphite, carbon / carbon composite material (C / C) and ceramic matrix composite material (CMC).
    [5" id="c-fr-0005]
    5. A load (200) intended to be placed in a densification installation by chemical vapor infiltration (500), said load comprising a fibrous preform (10) held in a shaping tool (100) according to any one of claims 1 to 4.
    [6" id="c-fr-0006]
    6. A load according to claim 5, in which the fibrous preform is a preform for an aeronautical engine part.
    [7" id="c-fr-0007]
    7. Installation for densification by chemical gas infiltration (500) of a fibrous preform, comprising a reaction chamber (510), a reactive gas inlet pipe (521) located at a first end of the chamber and opening out in a preheating zone (522), and a discharge pipe (531) located near a second end, characterized in that the chamber comprises at least one charge (200) according to claim 5 or 6.
    [8" id="c-fr-0008]
    8. Method of manufacturing a part made of composite material comprising:
    the placement of a fibrous preform (10) in a shaping tool (100) according to any one of claims 1 to 4,
    - consolidation of the porous preform by chemical gas infiltration of a matrix,
    - densification of the consolidated preform.
    2/6
    100
    类似技术:
    公开号 | 公开日 | 专利标题
    EP3551593B1|2021-01-27|Shaping equipment and facility for gas-phase chemical infiltration of fibrous preforms
    EP2154119B1|2013-01-23|Method of producing a part from a thermostructural composite material and part thus obtained
    EP1851180B1|2018-04-18|Composite material body with ceramic matrix
    EP2315734B1|2013-09-04|Method of producing a nozzle or a divergent nozzle element made of a composite
    EP2831382B1|2016-05-25|Afterbody assembly of an aircraft engine, corresponding aircraft engine and aircraft
    EP2493832B1|2014-12-10|Low-thickness thermostructural composite material part, and manufacture method
    FR2852004A1|2004-09-10|PRODUCTION OF A PREFORM BY REINFORCEMENT OF A FIBROUS STRUCTURE AND / OR BY BINDING BETWEEN THEM OF FIBROUS STRUCTURES AND APPLICATION TO THE PRODUCTION OF PARTS MADE OF COMPOSITE MATERIAL
    FR2886640A1|2006-12-08|METHOD AND PREFORM FOR THE PRODUCTION OF COMPOSITE MATERIAL PARTS BY CVI DENSIFICATION AND PIECES OBTAINED
    FR3001452A1|2014-08-01|METHOD OF MANUFACTURING A CURVED SHAPE ACOUSTICAL ATTENUATION PANEL
    FR2852003A1|2004-09-10|Production of a multi-perforated component in a composite material with a ceramic base involves the insertion and elimination of pins in a consolidated fibrous preformer, notably for the combustion chamber of a jet engine
    FR2936517A1|2010-04-02|METHOD FOR MANUFACTURING THERMOSTRUCTURAL COMPOSITE MATERIAL PARTS
    CA2925836C|2021-09-21|Fibrous structure with grouping of floats
    EP2791080B1|2019-02-27|Part made of cmc
    EP3129200B1|2018-02-28|Process for manufacturing a multiperforated composite part
    WO2014170586A1|2014-10-23|Holding and loading tool and facility for densifying porous rotating preforms
    EP3616906A1|2020-03-04|Part made from composite material with smooth outer surface and method for manufacturing same
    EP3592716B1|2021-08-18|Method for producing a consolidated fibrous preform
    FR3053360A1|2018-01-05|METHOD OF INFILTRATION OR CHEMICAL DEPOSITION IN STEAM PHASE
    FR2989390A1|2013-10-18|PROCESS FOR MANUFACTURING A COMPOSITE MATERIAL PART WITH IMPROVED INTRA-WIRE DENSIFICATION
    FR2950959A1|2011-04-08|SUPPORT DEVICE FOR LOADING PLATES
    同族专利:
    公开号 | 公开日
    CN110062750B|2020-08-14|
    EP3551593B1|2021-01-27|
    JP2020500823A|2020-01-16|
    RU2751708C2|2021-07-16|
    FR3059679B1|2021-03-12|
    CA3046126A1|2018-06-14|
    RU2019120797A3|2021-03-09|
    US10906205B2|2021-02-02|
    US20200061868A1|2020-02-27|
    RU2019120797A|2021-01-11|
    CN110062750A|2019-07-26|
    WO2018104640A1|2018-06-14|
    EP3551593A1|2019-10-16|
    BR112019011729A2|2019-10-22|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    EP0846787A1|1994-11-16|1998-06-10|The B.F. Goodrich Company|Apparatus for use with CVI/CVD processes|
    EP1028926A2|1997-10-27|2000-08-23|Lanxide Technology Company, Lp|Composite materials and methods for making the same|
    EP1452624A2|2002-10-24|2004-09-01|Goodrich Corporation|Process and apparatus for batch and continuous densification by chemical vapor infiltration |
    EP1815975A1|2006-01-20|2007-08-08|United Technologies Corporation|Ceramic matrix laminates|WO2020030875A1|2018-08-07|2020-02-13|Safran Ceramics|Former having a cellular network structure, for densification of a fibrous preform using gas|FR2732962B1|1995-04-12|1997-07-04|Europ Propulsion|PROCESS FOR CHEMICAL VAPOR INFILTRATION OF A MATERIAL COMPOSED OF CARBON AND SILICON AND / OR BORON|
    FR2733254B1|1995-04-18|1997-07-18|Europ Propulsion|CHEMICAL VAPOR INFILTRATION PROCESS FOR THE DENSIFICATION OF POROUS SUBSTRATES DISPOSED IN RING STACKS|
    DE10013409C1|2000-03-17|2000-11-23|Daimler Chrysler Ag|Vacuum injection process for manufacturing fiber reinforced composite products involves evacuating second chamber causing resin to flow into preform in adjacent evacuated first chamber|
    FR2936517B1|2008-09-29|2011-07-29|Snecma Propulsion Solide|METHOD FOR MANUFACTURING THERMOSTRUCTURAL COMPOSITE MATERIAL PARTS|
    FR2939129B1|2008-11-28|2014-08-22|Snecma Propulsion Solide|TURBOMACHINE TURBINE IN COMPOSITE MATERIAL AND PROCESS FOR MANUFACTURING THE SAME.|
    FR2939130B1|2008-11-28|2011-09-16|Snecma Propulsion Solide|PROCESS FOR MANUFACTURING COMPOUND FORM SHAPE PIECE OF COMPOSITE MATERIAL|
    CN101787504B|2010-01-21|2011-06-08|上海大学|Preparation method for carbon/carbon-copper composite material|
    US10093586B2|2015-02-26|2018-10-09|General Electric Company|Ceramic matrix composite articles and methods for forming same|FR3101078A1|2019-09-20|2021-03-26|Safran Ceramics|Shaping tools and installation for chemical gas infiltration of fiber preforms|
    FR3112797A1|2020-07-24|2022-01-28|Safran Ceramics|Process for treating a residual gaseous phase resulting from a CVI technique|
    法律状态:
    2017-11-20| PLFP| Fee payment|Year of fee payment: 2 |
    2018-06-08| PLSC| Publication of the preliminary search report|Effective date: 20180608 |
    2019-11-20| PLFP| Fee payment|Year of fee payment: 4 |
    2020-11-20| PLFP| Fee payment|Year of fee payment: 5 |
    2021-11-18| PLFP| Fee payment|Year of fee payment: 6 |
    优先权:
    申请号 | 申请日 | 专利标题
    FR1662040A|FR3059679B1|2016-12-07|2016-12-07|CONFORMATION TOOLS AND PLANT FOR CHEMICAL GAS INFILTRATION OF FIBROUS PREFORMS|
    FR1662040|2016-12-07|FR1662040A| FR3059679B1|2016-12-07|2016-12-07|CONFORMATION TOOLS AND PLANT FOR CHEMICAL GAS INFILTRATION OF FIBROUS PREFORMS|
    US16/467,299| US10906205B2|2016-12-07|2017-12-04|Shaping equipment and facility for gas-phase chemical infiltration of fibrous preforms|
    RU2019120797A| RU2751708C2|2016-12-07|2017-12-04|Forming tool and installation for chemical infiltration of fibrous billets in the gas phase|
    JP2019530456A| JP2020500823A|2016-12-07|2017-12-04|Shaping tools and equipment for chemical vapor infiltration of fiber preforms|
    EP17816980.1A| EP3551593B1|2016-12-07|2017-12-04|Shaping equipment and facility for gas-phase chemical infiltration of fibrous preforms|
    CA3046126A| CA3046126A1|2016-12-07|2017-12-04|Shaping equipment and facility for gas-phase chemical infiltration of fibrous preforms|
    PCT/FR2017/053374| WO2018104640A1|2016-12-07|2017-12-04|Shaping equipment and facility for gas-phase chemical infiltration of fibrous preforms|
    BR112019011729A| BR112019011729A2|2016-12-07|2017-12-04|forming equipment, loading, assembly, and one-piece composite material manufacturing process|
    CN201780076293.3A| CN110062750B|2016-12-07|2017-12-04|Forming device and installation for gas-phase chemical infiltration of fiber preforms|
    [返回顶部]