    • 专利摘要:
    Process of decorating with tracing of previously glazed and cooked tableware products, using inkjet inks, characterized in that it comprises the application of a composition 1, which does not include frits, and a composition 2, which always includes at least 1 frit and, Using an inkjet ink that does not include frit in its composition, adequate adhesion, resistance to the dishwasher test, colorimetric intensity and aesthetic effect are achieved. (Machine-translation by Google Translate, not legally binding)
    公开号:ES2799477A1
    申请号:ES201930538
    申请日:2019-06-12
    公开日:2020-12-17
    发明作者:Vega Oscar Ruiz；Seco Laura Brugada；Heydorn Carlos Concepción；Ripoll Juan Vicente Corts
    申请人:Torrecid SA；
    IPC主号:
    专利说明:

    [0004] The present invention is part of the field of decoration of previously enameled and cooked tableware, using decals and decorating them with inkjet inks ( inkjet) using the technology called drop on demand ( Dropon-demand, whose acronym in English are DoD), which are subjected to a heat treatment between 850 ° C and 1400 ° C.
    [0006] STATE OF THE ART
    [0007] The sector of tableware decorated through the use of decals is made up of different types of products such as porcelain, stoneware, bone-china and earthenware. Likewise, different decoration methodologies are distinguished such as direct screen printing, brush or tracing. In the case of decoration with tracing, the procedure used in the state of the art consists of using a tracing paper on which the ink or inks that make up the decoration are deposited. Subsequently, a covering layer (better known by its English term "cover coat") is deposited on the decoration by means of screen printing and it is left to dry for a time that can reach up to 48 hours. Next, the tracing paper with the decoration and the covering layer are placed in a water bath, which causes the decoration and the covering layer to come off the tracing paper. Finally, the whole decoration and covering layer are deposited on the tableware product to be decorated and subjected to the corresponding cooking cycle. However, this procedure has the limitation that it is necessary that the inks or pastes used to decorate contain frit in their formulation to achieve correct adhesion and integration of the ink in the enamel of the tableware product. However, when frit inkjet inks are used in their formulation, it has been observed that the colorations and effects that are achieved do not meet the requirements in terms of colorimetric coordinates (La * b * values) or final decorative effect (gloss , matte, luster, metallic, etc.).
    [0009] In the current state of the art there are other solutions for decoration of tableware by screen printing on decals. Thus, patent application US2018 / 0297393 is intended to obtain low-temperature decoration through the use of non-laminated pigments that are applied by screen printing on the decal to obtain either a metallic effect, using pigments with an aluminum, brass or copper effect. bronze, or well a colorimetric effect, using organic pigments. The decal decoration process according to the application US2018 / 0297393 consists of screen printing a first layer called protective on the tracing paper, followed by a screen printing also by screen printing of a layer containing the non-laminated pigments and, on this second, another protective layer is also applied by screen printing. Preferably the tracing paper is characterized in that it contains dextrin or polyvinyl alcohol. Especially in the decoration of plastics, it also describes the application by screen printing of a bonding layer on the layer containing the non-laminated pigments in order to achieve adhesion. In the case of ceramic and glass decoration, in addition to the decal, the need for an application of silanes on the surface to be deposited is required to achieve adhesion and integration. However, said patent application US2018 / 0297393 does not describe the use of frits in the protective layer. In addition, the application of silanes on the ceramics and glass to be decorated causes changes in tone and problems of incompatibility with the inks that translate into defects in the final decoration.
    [0010] For its part, patent EP3037451B1 provides a method of preparing a paste for decoration by screen printing on tracing that allows obtaining metallic effects on glass and ceramics. The decal paste comprises precious metals together with at least one binding composition in a percentage by weight of between 17% and 27%. The anchor composition comprises a mixture of at least one polyamine and an epoxy compound, at least one solvent selected from a C1-C10 monocarboxylic organic acid or a polar aprotic solvent of the cyclohexanone, cyclohexanol or combination thereof. Additionally, the preparation of the anchor composition requires a heating step at a temperature between 140 ° C and 200 ° C for a time between 5 minutes and 20 minutes. The decoration procedure, as described in patent EP3037451B1, consists of a single application of the paste on the tracing paper substrate with a 120 threads / cm2 screen printing. However, patent EP3037451B1 does not describe the use of frits in the anchoring composition that, as is known in the state of the art, would prevent its application in decoration with inkjet inks containing inorganic pigments or raw materials, since Adhesion of the decoration to the substrate to be decorated is not achieved, as the integration of pigments or raw materials is not carried out.
    [0011] The state of the art also includes patent application US2015 / 0038616 that describes an ink composition for application by inkjet intended for direct decoration (without the use of tracing) of non-porous substrates comprising organic solvents, at least one submicron size vitreous frit and at least one ceramic pigment. The fact that this application is intended for direct decoration prevents its application for decoration with decals. In this sense, it has been observed that when the decal is decorated with these inks according to the procedures used in the state of the art, the final effect is not good since part of the colorimetric intensity or aesthetic effect that is desired is lost (gloss , matte, luster, metallic, etc.).
    [0012] The purpose of the present invention is to make available a process and compositions that do not present the problems described above, that is, a process in which, using an inkjet ink without frit, adequate adhesion, colorimetric intensity and aesthetic effect are achieved, thanks to to the prior application of a composition 1, which does not include frits, and a composition 2, which always includes at least 1 frit and the subsequent application of composition 1; Compositions 1 and 2 made as claimed in the present invention. Process and compositions that overcome the problems previously described and derived from the use of an inkjet ink with frit or from the use of the decoration process on tracing existing in the state of the art.
    [0013] Another additional advantage is that the process and compositions according to the invention are characterized by passing the resistance test to washing with dishwasher according to the ASTM3565 standard.
    [0014] Yet another additional advantage is that the fritless inkjet inks used in the process according to the invention are manufactured in less time, are more economical, require less energy in their production and are more environmentally friendly.
    [0016] EXPLANATION OF THE INVENTION
    [0018] Throughout the specification and claims, the word "comprises" and its variants are not intended to exclude other technical characteristics, additives, components or steps. Furthermore, the word "comprises" includes the case "consists of". For those skilled in the art the subject matter, other objects, advantages and characteristics of the invention will emerge in part from the description and in part from the practice of the invention.
    [0019] The present invention is a process of decoration with tracing of previously enameled and cooked tableware products, using inkjet inks, characterized in that it comprises the following steps:
    [0020] a) Applying on a tracing paper by screen printing a composition 1 comprising at least one binder in a percentage by weight between 35% and 45%, at least one solvent in a percentage by weight between 55% and 65% and a antifoam in a weight percentage comprised between 0.25% and 1%.
    [0021] b) Dry at a temperature between 25 ° C and 40 ° C for a time between 1 hour and 48 hours.
    [0022] c) Apply by screen printing a composition 2, on the previously applied composition 1, which comprises at least one binder in a percentage by weight between 15% and 25%, at least one solvent in a percentage by weight between 35% and 45 %, at least one frit in a percentage by weight between 30% and 40%, with a D100 particle size of 45 microns, with a softening temperature between 875 ° C and 950 ° C and a coefficient of thermal expansion between 25 ° C and 500 ° C, between 40 ° C-1 and 70 ° C-1.
    [0023] d) Dry at a temperature between 25 ° C and 40 ° C for a time between 1 hour and 48 hours.
    [0024] e) Printing, on composition 2, by means of inkjet technology, at least one ink that does not include frit in its composition.
    [0025] f) Applying composition 1 by screen printing to the at least one ink, forming on the tracing paper an application unit that comprises the set of previous applications formed by composition 1, plus composition 2, plus ink and more composition 1.
    [0026] g) Dry at a temperature between 25 ° C and 50 ° C for a time between 1 hour and 48 hours.
    [0027] h) Introduce the tracing paper with the application unit in a water bath at a temperature between 25 ° C and 50 ° C, for a time between 1 minute and 10 minutes.
    [0028] i) Separate the application unit as a unit from the tracing paper.
    [0029] j) Dry at a temperature between 25 ° C and 40 ° C for a time between 1 hour and 48 hours.
    [0030] k) Place the application unit on the previously enameled and cooked tableware product.
    [0031] l) Carry out a heat treatment at a temperature between 850 ° C and 1400 ° C.
    [0032] The term "frit" as used in the present invention refers to a mixture of inorganic compounds that has been subjected to a melting process and subsequent cooling to obtain an amorphous glassy compound, that is, without crystalline structure, and whose composition is expressed in the form of oxide.
    [0033] In accordance with the present invention, the binder used in compositions 1 and 2 is selected from the group comprising glycol acrylates, polyalkyl acrylates, polyakyl acrylate copolymers, dialkyl acrylate copolymers, or a mixture thereof.
    [0034] Another aspect of the present invention is that the solvent used in compositions 1 and 2 is selected from the group comprising 1-butanol, 2-methyl-2-propanol, 1,5-pentanediol, 1-octanol, 1-4- butanediol, water, ethylene glycol, alkanes, naphthenic solvents, aromatic hydrocarbons or a mixture of them.
    [0035] According to the present invention, the composition also comprises an antifoam in a percentage by weight comprised between 0.25% and 1% and which is selected from the group comprising polysiloxanes, polyether-modified polysiloxanes, modified silicones, polydimethylsiloxanes, oil derivatives mineral and fatty acid derivatives.
    [0036] When applying formulations by screen printing, the amount of composition deposited is controlled by the number of threads per cm2 that the screen printing screen contains. In this sense, the printing process according to the present invention contemplates that the serigraphy screen used to apply composition 1 has between 36 threads / cm2 and 68 threads / cm2. For its part, the serigraphy screen for applying composition 2, according to the process of the present invention, has between 21 threads / cm2 and 36 threads / cm2.
    [0037] According to the present invention, the decoration of the decal is carried out using inks that are applied by means of the DoD inkjet technology . In this sense, the amount of ink deposited, according to the invention, is comprised between 1 g / m2 and 35 g / m2. Also, inks can provide different decorative effects. Examples of decorative effects that can be obtained according to the invention, by way of example but not limitation, are color, gloss, matte, satin, luster, metallic, relief, micro-relief, among others.
    [0038] Another aspect of the present invention related to inks is that the ink applied according to the decoration process contains at least one inorganic compound that is selected from the group comprising ceramic pigment or raw material or a mixture of them. Additionally the raw material is selected from the group comprising Al2O3, quartz, ZnO, WO3, Fe2O3, ZrSiO4, sodium feldspar, feldspar potassium, lithium feldspar, nepheline, mullite, wollastonite, kaolinite clay, illite clay, bentonites or a mixture of them.
    [0040] DESCRIPTION OF THE FIGURES
    [0042] Figure 1 is a diagram of the process of decorating with tracing of previously glazed and baked tableware products, using inkjet inks according to the invention.
    [0044] Figure 2 represents the tracing paper (1) with the application unit, composed of composition 1 (2), composition 2 (3) and ink without frit (4) before its immersion in a water bath (5) .
    [0046] Figure 3 represents the application unit, composed of composition 1 (2), composition 2 (3) and ink without frit (4) separated from the tracing paper (1) and ready to be deposited on the previously enameled tableware product. and cooked.
    [0048] PREFERRED FORMS OF REALIZATION
    [0050] The following examples are provided for illustrative purposes, and are not intended to be limiting of the present invention. Furthermore, the present invention covers all the possible combinations of particular and preferred embodiments indicated herein.
    [0051] The wares obtained in each example were subjected to a colorimetric evaluation of the CIE La * b * color space by a spectrophotometer. The La * b * measure was defined by the Commission Internationale de l 'Éclairage (CIE), an organization considered a reference in the science of light, to communicate and express color objectively. The La * b * color space is widely used because it correlates numerical color values with human visual perception. The La * b * color space measure is based on an opponent color theory that states that two colors cannot be red and green at the same time, nor yellow and blue at the same time. From there, L is defined as the luminosity that goes from 0 (absence of luminosity) to 100 (complete luminosity), a * as the red / green coordinates, where positive values of a * indicate red and negative values green, and b * as yellow / blue coordinates, where positive values of b * indicate yellow and negative values of b * indicate blue. Spectrophotometers and colorimeters can quantify all three color variables.
    [0052] Next, the tableware products obtained in each example were subjected to a dishwasher resistance test according to the ASTM-D-3565 standard. This standard establishes five evaluation scales for the final product once it has been subjected to the accelerated aging test in which the dishes are vigorously rubbed with a muslin:
    [0053] 0: there is no alteration of the product, there is no loss of pigment by rubbing or deterioration or loss of luster.
    [0054] 1: light: traces of pigment in the fabric; slight loss or matification, first recognizable evidence of alteration.
    [0055] 2: moderate: appreciable pigment in the fabric; obvious loss or matification.
    [0056] 3: considerable: extensive pigment in the fabric; extensive pigment removal.
    [0057] 4: complete: essentially complete removal of pigment after rubbing.
    [0059] Example 1 . Decoration of bone-china type tableware .
    [0060] Bone china type tableware products were decorated by the process according to the present invention. In turn, two types of inkjet inks were used. A typology consisted of four inkjet inks (4) corresponding to the colors cyan (CI), magenta (MI), yellow (YI) and black (KI) and with the characteristic that they did not contain frit in their formulation. The other typology corresponded to a set of four inks for inkjet corresponding to the colors cyan (CFI), magenta (MFI), yellow (YFI) and black (KFI) and with the characteristic that they contained frit in their formulation.
    [0061] For its part, the decoration procedure used with the two sets of inks, according to the present invention, included the following steps:
    [0063] a) Apply on a tracing paper (1) by screen printing, using a 68 threads / cm2 screen, a composition 1 (2) comprising a glycol acrylate binder in a 4% weight percentage, a polyalkyl acrylate binder in a percentage by weight of 39%, 1-butanol in a percentage by weight of 6.5%, xylene in a percentage by weight of 50% and a polysiloxane defoamer in a percentage by weight of 0.5%.
    [0064] b) Dry at a temperature of 45 ° C for 12 hours.
    [0065] c) Apply by screen printing, using a 36 threads / cm2 screen, on composition 1 (2), a composition 2 (3) that comprises a glycol acrylate binder in a percentage by weight of 2%, a polyalkyl acrylate binder in a percentage by weight of 19.5% a naphthenic solvent in a percentage by weight of 40%, a frit in a percentage by weight of 38.5%, with a D100 particle size of 45 microns, with a softening temperature of 885 ° C and a coefficient of thermal expansion between 25 ° C and 500 ° C of 43 ° C-1 .
    [0066] d) Dry at a temperature of 35 ° C for 12 hours.
    [0067] e) Print on composition 2 (3) and alternatively, each of the two sets of inkjet inks, one without a frit (4) and the other with a frit. In both cases, the deposited amount of each ink was 20 g / m2.
    [0068] f) Apply composition 1 (2) by screen printing, using a screen of 68 threads / cm2 on each of the sets of printed inks, giving rise to an application unit that comprises the four previous applications, namely, composition 1 (2), composition 2 (3), ink (4) and again composition 1 (2). g) Dry at a temperature of 50 ° C for 8 hours.
    [0069] h) Introduce the tracing paper assembly (1) with the application unit in a water bath (5) at a temperature of 25 ° C, for 7 minutes.
    [0070] i) Separate the application unit as a unit from the tracing paper (1).
    [0071] j) Dry at a temperature of 40 ° C for 24 hours.
    [0072] k) Place each of the application units on respective previously enameled and cooked tableware products.
    [0073] l) Carry out, in both cases, a heat treatment at a maximum temperature of 1100 ° C.
    [0075] Once the tableware products with the corresponding decorations were cooked using the two sets of inks, a measurement of the colorimetric coordinates La * b * was made. The data is shown in the following table. It can be seen that the colorimetric results or final decorative effect in the case of the inks without frit are better than the inks with frit using the procedure described in the present invention.
    [0077] Table 1
    [0080] Finally, the resulting tableware products were subjected to a dishwasher resistance test in accordance with ASTM-D-3565. The following table shows the result obtained in each ink composition, observing that it is exceeded in all cases.
    [0085] Example 2 . Porcelain-type tableware decoration.
    [0086] Porcelain-type tableware products were decorated by the process according to the present invention. In turn, two types of inkjet inks were used . One typology consisted of four inks for inkjet corresponding to the colors cyan (CI), magenta (MI), yellow (YI) and black (KI) and with the characteristic that they did not contain frit in their formulation (4). The other typology corresponded to a set of four inks for inkjet corresponding to the colors cyan (CFI), magenta (MFI), yellow (YFI) and black (KFI) and with the characteristic that they contained frit in their formulation.
    [0087] For its part, the decoration procedure used with the two sets of inks, according to the present invention, included the following steps:
    [0089] a) Apply on a tracing paper (1) by screen printing, using a 36 threads / cm2 screen, a composition 1 (2) that comprises a glycol acrylate binder in a percentage by weight of 4.5%, a binder of dialkyl acrylate copolymer in 35% by weight, 1,5-pentanediol in 10% by weight, naphthenic solvent in 50% by weight and a polyether-modified polysiloxane defoamer, in percentage in weight of 0.5%.
    [0090] b) Dry at a temperature of 25 ° C for 48 hours.
    [0091] c) Apply by screen printing, using a 36 threads / cm2 screen, a composition 2 (3) comprising a glycol acrylate binder in a percentage by weight of 5%, a polyalkyl acrylate binder in a percentage by weight of 20% , 2-methyl-2-propanol in a percentage by weight of 5%, ethylene glycol in a percentage by weight of 35%, water in a percentage by weight of 5%, a frit in a percentage by weight of 30%, with a 45 micron D100 particle size, with a
    [0094] softening temperature of 950 ° C and a coefficient of thermal expansion between 25 ° C and 500 ° C of 70 ° C-1.
    [0095] d) Dry at a temperature of 40 ° C for 8 hours.
    [0096] e) Print on composition 2 (3) and alternatively, each of the two sets of inkjet inks, one without a frit (4) and the other with a frit. In both cases, the deposited amount of each ink was 30 g / m2.
    [0097] f) Apply composition 1 (2) by screen printing, using a screen of 68 threads / cm2 on each of the sets of printed inks, giving rise to an application unit that comprises the four previous applications, namely, composition 1 (2), composition 2 (3), ink (4) and again composition 1 (2). g) Dry at a temperature of 40 ° C for 48 hours.
    [0098] h) Introduce the tracing paper assembly (1) with the previous application unit in a water bath (5) at a temperature of 30 ° C for 10 minutes.
    [0099] i) Separate the application unit as a unit from the tracing paper (1).
    [0100] j) Dry at a temperature of 40 ° C for 48 hours.
    [0101] k) Place each of the application units on respective previously enameled and cooked tableware products.
    [0102] l) Carry out, in both cases, a heat treatment at a maximum temperature of 1180 ° C.
    [0104] Once the tableware products with the corresponding decorations were cooked using the two sets of inks, a measurement of the colorimetric coordinates La * b * was made. The data is shown in the following table. It can be seen that the colorimetric results or final decorative effect in the case of inks without frit are better than inks with frit using the procedure described in the present invention.
    [0105] Table 2
    [0110] Finally, the resulting tableware products were subjected to a dishwasher resistance test in accordance with ASTM-D-3565. In the next table the result obtained in each ink composition is shown, observing that it is exceeded in all cases.
    [0115] Example 3 . Low-temperature porcelain-type tableware decoration.
    [0116] Low-temperature porcelain-type tableware products were decorated by the process according to the present invention. In turn, two types of inkjet inks were used . One typology consisted of four inks for inkjet corresponding to the colors cyan (CI), magenta (MI), yellow (YI) and black (KI) and with the characteristic that they did not contain frit in their formulation (4). The other typology corresponded to a set of four inks for inkjet corresponding to the colors cyan (CFI), magenta (MFI), yellow (YFI) and black (KFI) and with the characteristic that they contained frit in their formulation.
    [0117] For its part, the decoration procedure used with the two sets of inks, according to the present invention, included the following steps:
    [0119] a) Apply on a tracing paper (1) by screen printing, using a 68 threads / cm2 screen, a composition 1 (2) that comprises a dialkyl acrylate copolymer binder in a percentage by weight of 22%, a binder of polyalkyl acrylate in a percentage by weight of 20%, ethylene glycol in a percentage by weight of 55%, 1-octanol in a percentage by weight of 2.5% and a polydimethylsiloxane defoamer in a percentage by weight of 0.5%.
    [0120] b) Dry at a temperature of 40 ° C for 24 hours.
    [0121] c) Apply by screen printing, using a 21 threads / cm2 screen, a composition 2 (3) comprising a glycol acrylate binder in a 5% weight percentage, a polyalkyl acrylate binder in a 10% weight percentage , a naphthenic solvent in a percentage by weight of 10%, xylene in a percentage by weight of 35%, a frit in a percentage by weight of 25%, with a D100 particle size of 45 microns, with a softening temperature of 875 ° C and a coefficient of thermal expansion between 25 ° C and 500 ° C of 40 ° C-1, a second frit in a percentage by weight of 15%, with a D100 particle size of 45 micrometers, with a softening temperature of 925 ° C and a coefficient of thermal expansion between 25 ° C and 500 ° C of 66 ° C-1.
    [0122] d) Dry at a temperature of 30 ° C for 48 hours.
    [0123] e) Print on composition 2 (3) and alternatively, each of the two sets of inkjet inks, one without a frit (4) and the other with a frit. In both cases, the deposited amount of each ink was 35 g / m2.
    [0124] f) Apply composition 1 (2) by screen printing on each of the sets of printed inks, using a 36 threads / cm2 screen, giving rise to an application unit that comprises the four previous applications, namely, composition 1 (2), composition 2 (3), ink (4) and again composition 1 (2). g) Dry at a temperature of 50 ° C for 12 hours.
    [0125] h) Introduce the tracing paper assembly (1) with the previous application unit in a water bath (5) at a temperature of 25 ° C for 5 minutes.
    [0126] i) Separate the application unit as a unit from the tracing paper (1).
    [0127] j) Dry at a temperature of 30 ° C for 12 hours.
    [0128] k) Place each of the application units on respective previously enameled and cooked tableware products.
    [0129] l) In both cases, carry out a heat treatment at a maximum temperature of 850 ° C.
    [0131] Once the tableware products with the corresponding decorations were cooked using the two sets of inks, a measurement of the colorimetric coordinates La * b * was made. The data is shown in the following table. It can be seen that the colorimetric results or final decorative effect in the case of inks without frit are better than inks with frit using the procedure described in the present invention.
    [0132] Table 3
    [0137] The resulting tableware products were subjected to a dishwasher resistance test in accordance with ASTM-D-3565. The following table shows the
    [0140] result obtained in each ink composition, observing that it is exceeded in all cases.
    权利要求:
    Claims (10)
    [1]
    1. Procedure of decoration with tracing (1) of previously enameled and cooked tableware products using inkjet inks characterized in that it comprises the following steps:
    a) Apply on a tracing paper (1) by means of a serigraphy screen a composition 1 (2) comprising at least one binder in a percentage by weight between 35% and 45%, at least one solvent in a percentage by weight between 55% and 65% and a defoamer in a percentage by weight between 0.25% and 1%. b) Dry at a temperature between 25 ° C and 40 ° C for a time between 1 hour and 48 hours.
    c) Apply a composition 2 (3) by means of a screen printing, on the previously applied composition 1 (2), which comprises at least one binder in a percentage by weight between 15% and 25%, at least one solvent in a percentage by weight between 35% and 45%, at least one frit in a percentage by weight between 30% and 40%, with a D100 particle size of 45 microns, with a softening temperature between 875 ° C and 950 ° C and a coefficient of thermal expansion, between 25 ° C and 500 ° C, between 40 ° C-1 and 70 ° C-1.
    d) Dry at a temperature between 25 ° C and 40 ° C for a time between 1 hour and 48 hours.
    e) Printing, on composition 2 (3), by means of ink jet technology, at least one ink (4) that does not include frit in its composition.
    f) Applying composition 1 (2) on the at least one ink (4) by means of a screen printing, giving rise to an application unit comprising the four previous applications, namely, composition 1 (2), composition 2 (3), ink (4) and again composition 1 (2). g) Dry at a temperature between 25 ° C and 50 ° C for a time between 1 hour and 48 hours.
    h) Introduce the tracing paper assembly (1) with the application unit in a water bath (5) at a temperature between 25 ° C and 50 ° C for a time between 1 minute and 10 minutes.
    i) Separate the application unit as a unit from the tracing paper (1), j) Dry at a temperature between 25 ° C and 40 ° C for a time between 1 hour and 48 hours.
    k) Place the application unit on the previously enameled and cooked tableware product.
    l) Carry out a heat treatment at a temperature between 850 ° C and 1400 ° C.
    [2]
    2. Process according to claim 1, wherein the binder of compositions 1 and 2 is selected from the group comprising glycol acrylates, polyalkyl acrylates, polyakyl acrylate copolymers, dialkyl acrylate copolymers or a mixture of them.
    [3]
    3. Process according to any of the preceding claims wherein the solvent of compositions 1 and 2 is selected from the group comprising 1-butanol, 2-methyl-2-propanol, 1,5-pentanediol, 1-octanol, 1-4 -butanediol, water, ethylene glycol, alkanes, naphthenic solvents, aromatic hydrocarbons or a mixture of them.
    [4]
    4. Process, according to any of the preceding claims, wherein the antifoam of composition 1 is selected from the group comprising polysiloxanes, polyether-modified polysiloxanes, modified silicones, polydimethylsiloxanes, mineral oil derivatives and fatty acid derivatives.
    [5]
    5. Method, according to any of the preceding claims, wherein the screen for applying composition 1 (2) has between 36 threads / cm2 and 68 threads / cm2.
    [6]
    6. Process, according to any of the preceding claims, wherein the screen for applying composition 2 (3) has between 21 threads / cm2 and 36 threads / cm2.
    [7]
    7. Method according to any of the preceding claims, wherein the deposited amount of the at least one ink (4) by means of ink jet technology is between 1 g / m2 and 35 g / m2.
    [8]
    8. Process according to any of the preceding claims wherein the ink printed by inkjet contains at least one inorganic compound that is selected from the group comprising ceramic pigment or raw material or a mixture of them.
    1
    [9]
    9. Process according to the preceding claim wherein the raw material is selected from the group comprising Al2O3, quartz, ZnO, WO3, Fe2O3, ZrSiO4, sodium feldspar, potassium feldspar, lithium feldspar, nepheline, mullite, wollastonite, kaolinitic clay, clay illitic, bentonites or a mixture of them.
    [10]
    10. Process, according to claim 1, wherein the tableware product obtained obtains a 0 or 1 scale in the dishwasher resistance test according to the ASTM-D-3565 standard.
    类似技术:
    公开号 | 公开日 | 专利标题
    CN101804762B|2013-01-02|Manufacturing method of embossment layer halftone and manufacturing method of famille-rose embossment porcelain
    CN107602152B|2021-04-13|Green and white glaze for Jun porcelain and process for preparing Jun porcelain by using green and white glaze for Jun porcelain
    CN106116696A|2016-11-16|A kind of preparation method of three-dimensional cover-coat enamel
    CN105819690B|2018-08-28|The preparation method of colour enamels porcelain in a kind of glaze
    CN100455549C|2009-01-28|Medium and high temperature sintered coarse crystalline Fe-Ti glaze and its prepn process
    CN104478494B|2016-05-11|Under glaze, sprinkle the preparation method of color ceramic
    CN105272376B|2017-04-05|Transmutation temmoku glaze and preparation method thereof
    ES2578358T3|2016-07-26|Method for obtaining optical interference effects by means of a digital inkjet technique
    ES2799477B2|2021-05-17|DISHES DECORATION PROCEDURE THROUGH DECAL
    ES2676757T3|2018-07-24|Ceramic ink for injection printing for reduced expansion glass and / or reduced expansion glass ceramics, and their use
    KR101141262B1|2012-05-04|Multi-color and marbling frit glaze and method of ceramic ware using the same
    CN107586038B|2020-04-14|Process for preparing jun porcelain from green and white glaze for jun porcelain
    CN108437675B|2020-02-11|Preparation method and application method of ceramic decorative stained paper for paper-cut
    JP2015020918A|2015-02-02|Fritted glaze for pottery
    CN105152684B|2018-05-15|Lightweight porcelain low temperature transmutation erythema glaze, method of preparation and use
    PT1306355E|2007-07-04|Formulation and method for achieving metallic effects in ceramic tiles and the applications thereof
    CN103360120B|2014-07-02|Method for quickly producing porcelain pot with different colors on inner surface and outer surface
    JP2001233637A|2001-08-28|Glass ceramic with pearl-like muffle painting and method for producing the same
    CN107628751B|2020-10-09|Apple green crystalline glaze and method for firing apple green crystalline glaze
    CN1544698A|2004-11-10|Computer-aided novel method for making overglaze color
    CN108238720A|2018-07-03|Glaze silk screen oil, silk screen bottom print glaze and preparation method thereof
    JP4029414B2|2008-01-09|Cooker top plate
    JPH05301496A|1993-11-16|Transfer paper for over-grazing ceramic article
    KR102346312B1|2022-01-03|method of making living pottery having phosphorescent part and transfer paper for the same
    CN105034628A|2015-11-11|Low light baked stained paper and preparation method thereof
    同族专利:
    公开号 | 公开日
    WO2020249839A1|2020-12-17|
    EP3964367A1|2022-03-09|
    ES2799477B2|2021-05-17|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US6357868B1|1999-05-12|2002-03-19|Dmc2 Degussa Metals Catalysts Cerdec Ag|Method of decorating hard materials|
    WO2002051649A2|2000-12-22|2002-07-04|Lamberti Spa|Decal transfer for decorating ceramic articles or glassware|
    US20060134554A1|2003-02-28|2006-06-22|Ferro Gmbh|Radiationhardenable printing media, transfer pictures produced therewith, and method for producing ceramic decorations|
    ES2424775B1|2012-02-23|2014-07-17|Torrecid, S.A|Ink composition for decoration of non-porous substrates|
    ES2616133T3|2014-12-23|2018-01-05|Cabro S.P.A.|Bonding composition for decals|
    DE102015117711A1|2015-10-16|2017-04-20|Ferro Gmbh|Decal for creating a decoration|
    法律状态:
    2020-12-17| BA2A| Patent application published|Ref document number: 2799477 Country of ref document: ES Kind code of ref document: A1 Effective date: 20201217 |
    2021-05-17| FG2A| Definitive protection|Ref document number: 2799477 Country of ref document: ES Kind code of ref document: B2 Effective date: 20210517 |
    优先权:
    申请号 | 申请日 | 专利标题
    ES201930538A|ES2799477B2|2019-06-12|2019-06-12|DISHES DECORATION PROCEDURE THROUGH DECAL|ES201930538A| ES2799477B2|2019-06-12|2019-06-12|DISHES DECORATION PROCEDURE THROUGH DECAL|
    PCT/ES2020/070360| WO2020249839A1|2019-06-12|2020-06-01|Method for decorating dishware by way of tracing|
    EP20823529.1A| EP3964367A1|2019-06-12|2020-06-01|Method for decorating dishware by way of tracing|
    [返回顶部]