    • 专利摘要:
    An optical material including: a silica host; and a Praseodymium dopant; wherein the Praseodymium atoms are configured to form nanoclusters in the silica host. In addition, the optical material may include an Ytterbium co-dopant. The nanoclusters include Ge, Te, Ta, Lu and/or F, Cl to minimize multi-phonon quenching. Moreover, the nanoclusters may be encapsulated in a low phonon energy shell to minimize energy transfer to the host matrix.
    公开号:EP3706260A1
    申请号:EP20157887.9
    申请日:2020-02-18
    公开日:2020-09-09
    发明作者:Robert M. Pafchek
    申请人:Thorlabs Inc；
    IPC主号:C03C13-00
    专利说明:
    [0001] This application claims the benefit of U.S. Provisional Patent Application No. 62/807,521 filed on February 19, 2019 . The disclosure and entire teachings of U.S. Provisional Patent Application 62/807,521 are hereby incorporated by reference. FIELD OF THE INVENTION
    [0002] This invention relates generally to optical materials, and more particularly to a Praseodymium doped fiber. BACKGROUND
    [0003] The 1.3µm transition in Praseodymium (Pr) suffers from multi-phonon quenching due to interactions with the matrix which essentially completely eliminates the radiative emission in silica based hosts. This can be minimized by choosing a low phonon energy host such as fluoride glass. Although the optical loss for fluoride fiber is lower than silica in the mid-Infrared (mid-IR) the loss at 1.3 µm is much lower in silica fiber which is advantageous for fiber lasers and amplifiers. Concentration quenching has also been shown to limit the dopant concentrations in mid-IR hosts such as fluoride glass. SUMMARY
    [0004] To overcome the above discussed shortcomings, the present application proposes that the high efficiencies demonstrated in silica doped with Erbium (Er) nanoclusters can be extended to Pr which may allow higher dopant concentrations and improved performance.
    [0005] Additionally, it may be possible to tailor the nanocluster formation to shift the excited state absorption (ESA) which occurs in the 1.3µm window to longer wavelengths. This would allow devices to extend the operating range in this window which is highly desirable.
    [0006] An objective of the present disclosure is to explore the advantages of Pr doped nanoclusters in silica fiber so that the technology developed for silica fiber can be employed for this application.
    [0007] One embodiment of the present invention provides an optical material including: a silica host; and a Praseodymium dopant; wherein the Praseodymium atoms are configured to form Si rich nanoclusters in the silica host.
    [0008] One embodiment of the present invention provides a fiber amplifier including a fiber made of an optical material that includes: a silica host; and a Praseodymium dopant; wherein the Praseodymium atoms are configured to form Si rich nanoclusters in the silica host.
    [0009] In addition, the optical material may include an Ytterbium co-dopant. The nanoclusters may include or made completely of Ge, Te, Ta, Lu and/or F, Cl with Pr to minimize multi-phonon quenching. Moreover, the nanoclusters may be encapsulated in a low phonon energy shell to minimize energy transfer to the host matrix. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
    [0010] The description of illustrative embodiments according to principles of the present invention is intended to be read in connection with the accompanying drawings, which are to be considered part of the entire written description. In the description of embodiments of the invention disclosed herein, any reference to direction or orientation is merely intended for convenience of description and is not intended in any way to limit the scope of the present invention. Relative terms such as "lower," "upper," "horizontal," "vertical," "above," "below," "up," "down," "top" and "bottom" as well as derivative thereof (e.g., "horizontally," "downwardly," "upwardly," etc.) should be construed to refer to the orientation as then described or as shown in the drawing under discussion. These relative terms are for convenience of description only and do not require that the apparatus be constructed or operated in a particular orientation unless explicitly indicated as such. Terms such as "attached," "affixed," "connected," "coupled," "interconnected," and similar refer to a relationship wherein structures are secured or attached to one another either directly or indirectly through intervening structures, as well as both movable or rigid attachments or relationships, unless expressly described otherwise. Moreover, the features and benefits of the invention are illustrated by reference to the exemplified embodiments. Accordingly, the invention expressly should not be limited to such exemplary embodiments illustrating some possible non-limiting combination of features that may exist alone or in other combinations of features; the scope of the invention being defined by the claims appended hereto.
    [0011] This disclosure describes the best mode or modes of practicing the invention as presently contemplated. This description is not intended to be understood in a limiting sense, but provides an example of the invention presented solely for illustrative purposes by reference to the accompanying drawings to advise one of ordinary skill in the art of the advantages and construction of the invention.
    [0012] An embodiment of the present invention proposes doping Praseodymium nanoclusters into silica preforms with the intent of drawing low loss fiber suitable for fabricating amplifiers at 1.3µm. The nanoclusters would be designed to minimize the effects of quenching from clustering and multi-phonon effects. The advantages of this technique are low loss fiber in the region of interest, cost and potentially a shift in the ESA spectrum to longer wavelengths.
    [0013] An embodiment of the present invention makes use of highly efficient Pr doped nanoclusters in silica fiber to achieve superior performance relative to fluoride fiber. A preferred embodiment includes co-doping with Yb to achieve optimum performance. In an embodiment of the present invention, the nanoclusters contain but not limited to heavy metals such as Germanium (Ge), Tellurium (Te), Tantalum (Ta), Lutetium (Lu), etc. and/or anions such as Florine (F-) and/or Chlorine (C1-) to minimize the multi-phonon quenching.
    [0014] It may also be advantageous to encapsulate the Pr doped nanocluster in a low phonon energy shell to minimize energy transfer to the host matrix. In an embodiment, the nanoclusters are encapsulated by depleting the Praseodymium from the surface of the nanoclusters. In another embodiment, the nanoclusters are encapsulated by coating the nanoclusters by an un-doped or optimized composition that isolates the active ions from the host matrix.
    [0015] While the present invention has been described at some length and with some particularity with respect to the several described embodiments, it is not intended that it should be limited to any such particulars or embodiments or any particular embodiment, but it is to be construed with references to the appended claims so as to provide the broadest possible interpretation of such claims in view of the prior art and, therefore, to effectively encompass the intended scope of the invention. Furthermore, the foregoing describes the invention in terms of embodiments foreseen by the inventor for which an enabling description was available, notwithstanding that insubstantial modifications of the invention, not presently foreseen, may nonetheless represent equivalents thereto.
    权利要求:
    Claims (18)
    [0001] An optical material comprising:
    a silica host; and
    a Praseodymium dopant;
    wherein the Praseodymium atoms are configured to form nanoclusters in the silica host.
    [0002] The optical material of claim 1, further comprising an Ytterbium co-dopant.
    [0003] The optical material of claim 1, wherein the nanoclusters further comprise at least one of the following metals: Ge, Te, Ta, Lu to minimize multi-phonon quenching.
    [0004] The optical material of claim 1, wherein the nanoclusters further comprise at least one of the following anions: F-, Cl- to minimize multi-phonon quenching.
    [0005] The optical material of claim 1, wherein the nanoclusters are configured to have excited state absorption (ESA) which allows gain in the 1.3 micron wavelength region.
    [0006] The optical material of claim 1, wherein the nanoclusters are configured to have excited state absorption (ESA) which allows the gain spectrum to extend to longer wavelengths in the 1.3 micron region.
    [0007] The optical material of claim 1, wherein the nanoclusters are encapsulated.
    [0008] The optical material of claim 7, wherein the nanoclusters are encapsulated by depleting the Praseodymium from the surface of the nanoclusters.
    [0009] The optical material of claim 7, wherein the nanoclusters are encapsulated by coating the nanoclusters by an un-doped or optimized composition that isolates the active ions from the host matrix.
    [0010] A fiber amplifier comprising fiber amplifier including a fiber made of an optical material that comprises:
    a silica host; and
    a Praseodymium dopant;
    wherein the Praseodymium atoms are configured to form nanoclusters in the silica host.
    [0011] The fiber amplifier of claim 10, wherein the optical material further comprises an Ytterbium co-dopant.
    [0012] The fiber amplifier of claim 10, wherein the nanoclusters further comprise at least one of the following metals: Ge, Te, Ta, Lu to minimize multi-phonon quenching.
    [0013] The fiber amplifier of claim 10, wherein the nanoclusters further comprise at least one of the following anions: F-, Cl- to minimize multi-phonon quenching.
    [0014] The fiber amplifier of claim 10, wherein the nanoclusters are configured to have excited state absorption (ESA) which allows gain in the 1.3 micron wavelength region.
    [0015] The fiber amplifier of claim 10, wherein the nanoclusters are configured to have excited state absorption (ESA) which allows the gain spectrum to extend to longer wavelengths in the 1.3 micron region.
    [0016] The fiber amplifier of claim 10, wherein the nanoclusters are encapsulated.
    [0017] The fiber amplifier of claim 16, wherein the nanoclusters are encapsulated by depleting the Praseodymium from the surface of the nanoclusters.
    [0018] The fiber amplifier of claim 16, wherein the nanoclusters are encapsulated by coating the nanoclusters by an un-doped or optimized composition that isolates the active ions from the host matrix.
    类似技术:
    公开号 | 公开日 | 专利标题
    Pandozzi et al.2005|A spectroscopic analysis of blue and ultraviolet upconverted emissions from Gd3Ga5O12: Tm3+, Yb3+ nanocrystals
    Bufetov et al.2014|Bi-doped optical fibers and fiber lasers
    Dvoyrin et al.2005|Absorption, fluorescence and optical amplification in MCVD bismuth-doped silica glass optical fibres
    Jackson2004|Single-transverse-mode 2.5-W holmium-doped fluoride fiber laser operating at 2.86 µm
    CN102087378B|2014-04-30|A rare-earth-doped optical fiber having small numerical aperture
    Fornasiero et al.1999|New oxide crystals for solid state lasers
    Tanabe et al.2000|Broad-band 1.5 μm emission of Er3+ ions in bismuth-based oxide glasses for potential WDM amplifier
    US7203407B2|2007-04-10|Rare earth doped single polarization double clad optical fiber and a method for making such fiber
    Engholm et al.2007|Strong UV absorption and visible luminescence in ytterbium-doped aluminosilicate glass under UV excitation
    Li et al.2010|Watt-level∼ 2μm laser output in Tm 3+-doped tungsten tellurite glass double-cladding fiber
    Lin et al.2011|Enhanced mid-infrared emissions of Er 3+ at 2.7 μm via Nd 3+ sensitization in chalcohalide glass
    Ghosh et al.2008|Tuning of crystal phase and luminescence properties of Eu3+ doped sodium yttrium fluoride nanocrystals
    KR101464583B1|2014-12-23|Light emitting devices with phosphosilicate glass
    Chen et al.2011|In-band pumped highly efficient Ho: YAG ceramic laser with 21 W output power at 2097 nm
    Jackson2012|Towards high-power mid-infrared emission from a fibre laser
    Zhou et al.2007|Intense infrared luminescence in transparent glass-ceramics containing β-Ga2O3: Ni2+ nanocrystals
    Zhang et al.2009|Enhanced 2.0 μm emission and gain coefficient of transparent glass ceramic containing BaF 2: Ho 3+, Tm 3+ nanocrystals
    Shen et al.2002|Tungsten–tellurite—a host glass for broadband EDFA
    EP1043281B1|2005-10-12|Method of fabricating preforms doped with rare earth metal for optical fibers
    USRE44288E1|2013-06-11|Optical fiber and method for making such fiber
    Yang et al.2002|Concentration quenching in Yb: YAG
    JP5400587B2|2014-01-29|Amplifying optical fiber and production method
    US20100118388A1|2010-05-13|Amplifying Optical Fiber and Method of Manufacturing
    US7502539B2|2009-03-10|Rare earth doped optical fiber
    JP4755114B2|2011-08-24|Double clad optical fiber with glass core doped with rare earth metal
    同族专利:
    公开号 | 公开日
    US20200266600A1|2020-08-20|
    CN111574061A|2020-08-25|
    CA3072672A1|2020-08-19|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    法律状态:
    2020-08-07| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: THE APPLICATION HAS BEEN PUBLISHED |
    2020-08-07| PUAI| Public reference made under article 153(3) epc to a published international application that has entered the european phase|Free format text: ORIGINAL CODE: 0009012 |
    2020-09-09| AX| Request for extension of the european patent|Extension state: BA ME |
    2020-09-09| AK| Designated contracting states|Kind code of ref document: A1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2021-03-12| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: REQUEST FOR EXAMINATION WAS MADE |
    2021-04-14| RBV| Designated contracting states (corrected)|Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2021-04-14| 17P| Request for examination filed|Effective date: 20210309 |
    2021-07-29| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: GRANT OF PATENT IS INTENDED |
    2021-07-29| GRAP| Despatch of communication of intention to grant a patent|Free format text: ORIGINAL CODE: EPIDOSNIGR1 |
    2021-08-25| INTG| Intention to grant announced|Effective date: 20210730 |
    2021-12-01| GRAS| Grant fee paid|Free format text: ORIGINAL CODE: EPIDOSNIGR3 |
    2021-12-03| STAA| Information on the status of an ep patent application or granted ep patent|Free format text: STATUS: THE PATENT HAS BEEN GRANTED |
    2021-12-03| GRAA| (expected) grant|Free format text: ORIGINAL CODE: 0009210 |
    2022-01-05| AK| Designated contracting states|Kind code of ref document: B1 Designated state(s): AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR |
    2022-01-05| REG| Reference to a national code|Ref country code: GB Ref legal event code: FG4D |
    2022-01-14| REG| Reference to a national code|Ref country code: CH Ref legal event code: EP |
    2022-01-15| REG| Reference to a national code|Ref country code: AT Ref legal event code: REF Ref document number: 1461422 Country of ref document: AT Kind code of ref document: T Effective date: 20220115 |
    2022-01-27| REG| Reference to a national code|Ref country code: DE Ref legal event code: R096 Ref document number: 602020001485 Country of ref document: DE |
    2022-02-02| REG| Reference to a national code|Ref country code: IE Ref legal event code: FG4D |
    优先权:
    申请号 | 申请日 | 专利标题
    [返回顶部]