    • 专利摘要:
    A method is disclosed for the oxidation and thermal decomposition of metal chlorides, leading to an efficient and effective separation of nuisance elements such as iron and aluminium from value metals such as copper and nickel. In the first instance, oxidation, especially for iron, is effected in an electrolytic reactor, wherein ferrous iron is oxidised to ferric. In a second embodiment, the oxidised solution is treated in a hydrothermal decomposer reactor, wherein decomposable trivalent metal chlorides form oxides and divalent metal chlorides form basic chlorides. The latter are soluble in dilute hydrochloric acid, and may be selectively re-dissolved from the hydrothermal solids, thereby effecting a clean separation. Hydrochloric acid is recovered from the hydrothermal reactor.
    公开号:DK202070078A1
    申请号:DKP202070078
    申请日:2018-06-28
    公开日:2020-02-13
    发明作者:Harris Bryn；White Carl
    申请人:9203-5468 Quebec Inc. Dba Nmr360；
    IPC主号:
    专利说明:

    METHOD FOR THE OXIDATION AND HYDROTHERMAL DISSOCIATION OF METAL CHLORIDES FOR THE SEPARATION OF METALS AND HYDROCHLORIC ACID
    FIELD OF THE INVENTION
    0001 The present invention relates to a method for the oxidation of base metals and ferrous iron and processes for the separation and recovery of metals and hydrochloric acid More specifically, the process relates to the oxidation of ferrous chloride, separation of iron from base metals, and recovery of hydrochloric acid
    BACKGROUND OF THE INVENTION
    0002 Despite the many obvious chemical advantages of using chloride-based hydrometallurgical techniques for recovering metals such as zinc, nickel, copper, cobalt, lead, aluminium, titanium, and magnesium from sulphide and oxide ores, concentrates and intermediates, the metals extraction industry has been reluctant to embrace chloride processes. The reason for this is primarily economic, since hydrochloric acid is much more costly than its sulphuric acid counterpart, costing 3-4 times as much on an equivalent hydrogen ion basis, and hence must be recovered and recycled in the process flowsheet There is also an environmental component, since iron residues from conventional atmospheric chloride processes tend to be more difficult to handle and dispose of than their counterparts from sulphate processes
    0003 In this context, however, most base metal chlorides are generally much more amenable to hydrolysis than the corresponding sulphates, especially at higher temperatures (>100°C), forming an oxide or hydroxide, and releasing the chloride ion, making it potentially available for recovery. The following discussion applies principally to chloride-based leach solutions.
    0004 Chloride-based leaching systems are aggressive, resulting in substantially all of the metals in the feed material being dissolved. This is especially true for iron, which is and has always been considered a major problem in hydrometallurgical processes, usually being present in process solutions in concentrations much greater than the value metals which are the primary target of any process. Moreover, the iron is usually present in both oxidized and reduced forms, and very rarely is it present solely in its ferric (higher oxidation state and less stable form).
    0005 The first objective of most processes, therefore, is to remove iron prior to recovering the target metals. A.J. Monhemius, in an article entitled Precipitation Diagrams for Metal Hydroxides, Sulphides, Arsenates and Phosphates, published in Transactions of IMM, Volume 86, Section C, December 1977, p. C202, reported on the theoretical order of precipitation of various metal hydroxides This was based on the solubility product (Ksp) of the metal hydroxide, and the dissociation constant of water (Kw), using the following equation, where M is any metal of valency n+:
    DK 2020 70078 A1 pH = (logKsp-n logKw-log[M” ])/n (1)
    0006 From this analysis, it was determined that the trivalent and tetravalent meals precipitated at the lowest pH, whereas magnesium and especially calcium were the hardest to hydrolyse.
    0007 In atmospheric processes, iron is usually precipitated as an oxy-hydroxide, where a base such as caustic soda, magnesia or lime is added, since water itself is not sufficiently active to promote hydrolysis. Often, small amounts of copper are added to act as a catalyst in the oxidation of ferrous to ferric. One method of controlling iron in chloride-based solutions is to form FeOOH, either ß-FeOOH (akaganeite) or α-FeOOH (goethite) as described by D. Filippou and Y. Choi, A Contribution to the Study of Iron Removal From Chloride Leach Solutions, in Chloride Metallurgy’ 2002 Volume 2, (E. Peek and G. van Weert, Editors), Proceedings of the 32nd Annual C1M Hydrometallurgical Conference, C1M, Montreal (2002), p. 729. This approach is based to some extent on a controlled supersaturation precipitation technique, and is more efficient than, for example, the turboaeration process proposed by Great Central Mines in their chloride copper process, as described by R. Raudsepp and M.J.V. Beattie, Iron Control in Chloride Systems, in Iron Control in Hydrometallurgy! (J.E. Dutrizac and A.J. Monhemius, Editors), Proceedings of 1601 Annual CIM Hydrometallurgical Meeting, Toronto, October 1986, CIM Montreal (1996), p. 163. A major disadvantage, however, of forming akaganéite is a loss of chloride, since akaganéite precipitates can contain up to 7% chloride.
    0008 In higher temperature, higher pressure processes, water becomes sufficiently active, and iron can be precipitated as its oxide, an impure hematite. However, in typical aqueous solutions, expensive autoclave pressure vessels are required to achieve this, and the corresponding chloride cannot be recovered as hydrochloric acid.
    0009 There are two fundamental issues associated with removing iron from chloride process liquors. The first is that, following the sequence outlined above by Monhemius, any ferrous iron needs to be oxidised to ferric before hydrolysis can be effected. The second is that the chloride component associated with the iron (and other base metal chlorides) needs to be recovered in a useful form as hydrochloric acid, rather than an alkali or alkaline earth metal chloride as would be the case with caustic or lime-induced hydrolysis. Most metal chloride leaching solutions are combinations of iron and value metals such as nickel, cobalt, copper, zinc and lead, together with gangue metals such as aluminium, magnesium and calcium.
    0010 Ferrous chloride solution, containing minor amounts of steel alloys such as manganese, vanadium and nickel, is the principal by-product of steel pickling lines (commonly referred to as waste pickle liquor, WPL) This solution is generally treated by a process called pyrohydrolysis, wherein the solution is injected into hot combustion gases at 700-900°C, causing the simultaneous oxidation of the ferrous iron to ferric and subsequent decomposition to recover hydrochloric acid and generate an iron oxide product. The strength of the hydrochloric acid recovered from this process is limited to 18% because the off-gases have to be quenched in water, and using this method it is impossible to exceed the azeotropic concentration of hydrochloric acid in water, 20.4%.
    DK 2020 70078 A1
    0011 Pyrohydrolysis is limited to predominantly ferrous chloride solutions, being highly ineffective if the iron is the ferric form. It is also non-discriminatory, since any other hydrolysable metals in solution, such as aluminium, magnesium, nickel, cobalt and manganese will also convert to their respective oxides. Non-hydrolysable metals, such as calcium, sodium and potassium simply report to the solids as unreacted chlorides. Zinc chloride is a special case, with solutions containing zinc not treatable by this technique due to the zinc chloride becoming very sticky and blocking up the nozzles and valves in the reactor. Recovery of associated metals from pyrohydrolysis solids is difficult due to their refractory nature. Consequently, the other pickle liquor from the steel industry, ZPL, zinc pickle liquor solution is usually disposed of in deep wells. There is not, at present, any commercially-viable process for treating ZPL.
    0012 United States Patent No. 3,682,592 issued to Kovacs describes a process, the PORI Process, for recovering HC1 gas and ferric oxide from waste hydrochloric acid steel mill pickle liquors (WPL). WPL typically contains water, 18 to 25% weight of ferrous chloride (FeCh), less than 1% weight ferric chloride (FeCh), small amounts of free hydrochloric acid and small amounts of organic inhibitors. The process of Kovacs includes two steps namely, a first oxidation step and a second thermal hydrolysis step. During the first oxidation step, the ferrous chloride in the WPL is oxidized using free oxygen to obtain ferric oxide and an aqueous solution containing ferric chloride. No hydrochloric acid is liberated at this stage. The first oxidation step is carried out under pressure (preferably, 100 p.s.i.g.) and at an elevated temperature (preferably, 150°C), and therefore requires an autoclave.
    0013 During the second step, the resultant ferric chloride solution is hydrolysed to obtain ferric oxide and HC1 gas, which is recovered as hydrochloric acid. More specifically, the resultant solution is heated up to 175-180°C at atmospheric pressure, and hydrolysis effected by the water in the fresh ferric chloride being added. The HC1 is stripped off at a concentration of 30% with >99% recovery and good quality hematite is produced.
    0014 While recovery of hydrochloric acid and hematite may be achieved using this process, its application tends to be limited to liquors containing only ferrous/ferric chlorides. It has been found that when other metal chlorides are present in the solution, which is always the case in steel pickling, where manganese and nickel often occur, then the freezing or “drying-out” temperature of the ferric chloride solutions starts to drop as the concentration of other metals increases It has been seen that when the other metals chlorides reach about 30% in concentration, the balance being ferric chloride, then the temperature specified by Kovacs cannot be attained whilst at the same time keeping the system liquid, and the reaction stops
    0015 SMS Siemag of Vienna, Austria, published a paper describing a process almost identical to that of Kovacs The paper, Regenerate Hidrotérmica De Åcido Um Modo Econömico De Regenerar Liquidos De Decapagem E Produzir Oxidos Férricos De Alta Qualidade, published in Portuguese by D Vogel, et al., follows the same procedures as Kovacs. More recently, a patent application describing the SMS Siemag process has been published by N. Takahashi et al., entitled Processing Method for Recovering Iron Oxide and Hydrochloric Acid, International Patent Application W02009153321 Al, December 23, 2009. A further identical patent is one
    DK 2020 70078 A1 published by Kazuo Handa, Murakami KeiHiroshi, Nobuo Nonaka, and Takahashi ShinYoshimi, as JP 2004-137118 A (in Japanese), entitled Process for the Recovery of Hydrochloric Acid from Iron Treatment with Hydrochloric Acid Waste Liquid, published on 13 May 2004.
    0016 In these processes, it is specified that the ferric chloride of the bath into which fresh aqueous ferric chloride is injected, should be kept at around a concentration of 65% ferric chloride and 35% water. This obviously means that not all of the iron is hydrolysed, with a substantial amount remaining in this liquid phase of 65% ferric chloride. This, in turn, indicates that a significant proportion of the chloride is also not recovered, which mitigates against the objectives of the process.
    0017 SMS Siemag built a plant based on this patent, but found that it did not work, since there were too many operational difficulties. The reasons and the type of problems encountered were described in a paper by Herbert Weissenbaeck, Benedikt Nowak, Dieter Vogl and Horst Krenn, entitled Development of Chloride Based Metal Extraction Techniques: Advancements and Setbacks, published at ALTA Nickel-Cobalt-Copper Conference, Perth, WA, May 28, 2013. Specifically, it was found that the plant worked well at first, but then the freezing problems indicated in paragraph 14 started to happen.
    0018 The present applicants published a method a method for overcoming the limitations in both the ferrous iron oxidation and ferric iron hydrolysis in US Patent Application 2013/0052104 Al, Process For the Recovery of Metals and Hydrochloric Acid, February 28, 2013. Oxidation was effected by injecting air or oxygen into a novel column reactor at a temperature of 135°C. In this process, a matrix solution is used, described as being any compound which is capable of being oxygenated to form, even transiently, a hypochlorite compound. The matrix solution performed two duties, the first being the hypochlorite formation just referred to, and the second remaining liquid over the temperature range of 135-190°C. This was important, since hematite, the desired form of iron oxide, is not formed easily at lower temperatures, whereas the precursor, ferrous chloride, evaporates to dryness at a temperature around 109°C.
    0019 It has been discovered since, however, that the column reactor has some limitations, particularly in the volume of gas that can be blown through it. Whilst air may be used on small reactors, the volumes of nitrogen present preclude its use in larger reactors, where the surface area to volume ratio is very much lower. In these cases, blowout of the reactants tends to occur.
    0020 A second drawback is the formation of hypochlorites referred to above A major issue in this respect is calcium, its hypochlorite being a very common chemical. Calcium is almost ubiquitously present in mineral ores and concentrates, and hence will almost certainly be present in any processing solution. Complete (100%) removal, as gypsum or other forms of calcium sulphate, is not possible, and thus some calcium will always be present. It has been found that calcium hypochlorite forms at the lower end of the temperature spectrum above, and tends to explosively decompose at 155-160°C. Hence, the system is not practical if significant calcium concentrations are allowed to build up, which will be the case, since calcium chloride doies not hydrolyse.
    DK 2020 70078 A1
    0021 A third drawback of using oxygen at such temperatures is the formation of elemental chlorine through the Deacon Reaction. This reaction was the original method of generating chlorine, using oxygen to react with HCI to form water and chlorine. Small concentrations, up to 300 mg/L, of chlorine have been found in the recovered hydrochloric acid, indicating that the Deacon Reaction does occur.
    0022 In terms of ferric iron hydrolysis, the US Patent application cited above indicated that zinc chloride was a preferred matrix solution for effecting this because of its ability to remain liquid over a large temperature range, and more importantly, to remain inert However, since the application was filed, it has been found that the presence of calcium, again, and/or magnesium has had unforeseen consequences. Calcium chloride on its own evaporates to dryness at around 185-190°C, and magnesium chloride on its own at 195-200°C. However, if either is allowed to build up to a significant (>30%) concentration in zinc chloride, then at temperatures over 210°C, the system remains liquid and white solids are formed having an analysis of 65% Zn, indicating zinc hydrolysis forming either tetra basic zinc chloride (Zns/OHjsCh) or zinc hydroxy chloride (ZnOHCl) or a combination of both
    0023 A further disadvantage of the above system, and also of those of SMS Siemag and PORI, is that there is no obvious end-point of the reaction As noted, the PORI and SMS Siemag systems require a residual ferric chloride of 65%, such that an end-point can never be achieved. With the zinc chloride matrix system, there is always, and constantly, some dissolution of feed solution into the matrix itself, resulting in a continuously changing composition. Several secondary reactors are required, wherein the temperature is changed and additional steam injection carried out to recover residual metals. Even so, complete is recovery is not possible, because there is always some residual solubility.
    0024 In light of the foregoing, it is clear that there is no full understanding of, or simple methodology by which ferrous iron can be easily oxidized, nor can such oxidation be coupled with the separation of iron and other nuisance chlorides from base metal chlorides and at the same time effect the recovery hydrochloric acid. Thus, there is needed a clear method of effecting iron oxidation under all process conditions, and allowing for the subsequent recovery of both hydrochloric acid and base metals. In light of the foregoing, it would be advantageous to be able to oxidise ferrous iron without the use of an either an autoclave or large volumes of oxygen and/or air, and furthermore without the intermediate formation of hematite with its attendant propensity to scale. So doing would lead to a much more simple process for the recovery hydrochloric acid, result in complete recovery of iron as an oxide, and effect separation of iron from base metals.
    SUMMARY OF THE INVENTION
    0025 In accordance with a broad aspect of the present invention, processes for separating nuisance elements such as iron and aluminium from more valuable base metals, and for recovering hydrochloric acid from any chloride-based feed solution are disclosed. Such solution may have been generated by treating any base or light metal-containing material with any
    DK 2020 70078 A1 lixiviant comprising acid and a chloride, but in particular with hydrochloric acid generated and recycled within the process, or WPL or ZPL. The chloride solution is then treated to separate and recover therefrom hydrochloric acid and metal oxides as separate discrete products.
    BRIEF DESCRIPTION OF THE DRAWINGS
    0026 Reference will now be made to the accompanying drawings, showing by way of illustration a particular embodiment of the present invention and in which:
    0027 Figure 1 shows a schematic for the oxidation of ferrous iron.
    0028 Figure 2 shows a schematic for the hydrothermal decomposition of metal chlorides and recovery of hydrochloric acid.
    DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION
    0029 The embodiments of the present invention shall be more clearly understood with reference to the following detailed description taken in conjunction with the accompanying drawings.
    0030 In accordance with a broad aspect of the present invention, there is a process described for oxidising ferrous iron and recovering hydrochloric acid from a chloride-based feed solution containing ferrous iron. Such solution may have been generated by treating any base, precious or light metal-containing material with any lixiviant comprising acid and a chloride, but in particular with hydrochloric acid generated and recycled within the process, or being derived from SPL or ZPL It is understood that whilst the description references ferrous iron, which is by far the most common metal requiring oxidation, the principals and practice equally apply to other metals requiring oxidation such as, but not limited to, copper or manganese.
    0031 It is a particular aspect of the invention that ferrous iron oxidation is effected without either recourse to the use of an autoclave, the need to pre-evaporate the incoming solution, or without the need to use a matrix which has to be oxygenated to form an intermediate hypochlorite.
    0032 Ferrous chloride solution, on its own (i.e. no other ions present), cannot be raised to a temperature above 120°C under atmospheric conditions, such that oxidation with oxygen or air is both difficult and very slow. Even under favourable conditions, such as in an autoclave, oxidation with oxygen or air promotes the reaction wherein one third of the iron is converted to hematite solids. Handling such solids can be problematical, especially in terms of scaling and abrasion of valves, such as encountered by SMS Siemag in the publication referenced above. Hematite, especially in the nickel laterite industry, is well-known for its propensity to cause scaling.
    0033 To avoid these problems, namely the need for pre-concentration or the use of an autoclave, along with the formation of abrasive solids, the present invention makes use of the
    DK 2020 70078 A1 fact that free hydrochloric in the ferrous solution may be electrolytically oxidised (at the anode) to form elemental chlorine. Such chlorine, the moment it is formed, is highly reactive due to being in a monatomic state, so-called “nascent” chlorine. The reaction, in a simple form, is shown in equation (1).
    2HC1 -+ CI2+H2 (1)
    0034 The hydrogen produced (at the cathode) is also reactive, and spontaneously reacts with dissolved oxygen in the solution to form water. Alternatively, a stream of air may be blown across the cathode to remove the hydrogen and depolarise it.
    0035 The reactive chlorine reacts instantaneously with ferrous iron to form ferric iron, according to equation (2).
    2FeC12+Ch -+ 2FeCh (2)
    0036 It is a particular aspect of this invention that in this case, the oxidation of ferrous is effected in-situ without the formation of any hematite solids, and also without the need for any elevated temperature.
    0037 However, care has to be taken, since an additional reaction may take place at the cathode, as shown in equation (3), namely the formation of metallic iron.
    FeCh -+ Fe+Ch (3)
    0038 The formation of metallic iron is highly undesirable for two reasons, namely that it plates on the cathode, thereby reducing the effectiveness of the cathode, and secondly, it has a very high power consumption compared to equation (1). It has been found, therefore, that it is essential to maintain a residual level of ferrous iron in solution, from 0.5-5.0 g/L, optimally from 0.5-1.5 g/L.
    0039 A further advantage of carrying out the ferrous iron oxidation in this manner is that there is no longer any need to adjust the solution composition to maintain the 145-155°C temperature range required by the current processes, whether it be by an autoclave or by the use of a matrix. This further means that the need to inject steam is no longer required, and that the composition of the feed solution may be adjusted prior to the subsequent hydrolysis reaction in such a manner as to generate the required composition of HC1 directly off the reactor. In other words, the amount of water required for the hydrolysis reaction is derived entirely from the incoming feed solution, and thus the need to inject steam for the hydrolysis reaction to occur is eliminated.
    0040 Referring to Figure 1, feed solution 10 containing some ferrous iron is fed into an electrolytic oxidation reactor 11. The temperature of the feed solution may be from ambient to boiling, being whatever the process step which generated it operates at. The oxidation reaction is exothermic, however, and under steady state conditions, the temperature of the reactor will operate at 100-160°C or higher, depending on the initial iron concentration and temperature of
    DK 2020 70078 A1 the feed solution 10. The presence of the formed ferric iron permits the temperature to exceed the boiling point of pure ferrous chloride solution.
    0041 A condition is that the solution contains a molar ratio of free hydrochloric acid to ferrous iron >1 (i.e. HCl/Fe(II) >1). This is necessary in order to supply the requisite amount of chloride ion to effect the oxidation. Ideally, the excess hydrochloric acid will be 5-25%, sufficient to maintain the pH of the resultant ferric chloride at <2.0 in order to prevent premature ferric iron hydrolysis.
    0042 Any simple electrolytic cell 11 may be used, but the preferred configuration is that of a bipolar cell, with a header on the cathodic compartments to collect any hydrogen formed.
    0043 The anodic current density 12 should be in the range 50-500 A/m2, the actual value being dependent upon the ferrous iron concentration and the desired kinetics. Typically, the value will be 300-350 A/m2.
    0044 Hydrogen 14 is liberated from the cathodic compartment of the cell. Stripping of the hydrogen may be facilitated by a small stream of air blown across the faces of the cathodes into a header Some hydrogen will react to form water with dissolved oxygen, but the balance may be collected by any conventional means, such as absorption by palladium metal. The predominant purpose of the air is to depolarise the cathode, and therefore lower the power consumption.
    0045 Oxidised solution 15 is withdrawn from the anodic compartment of the cell.
    0046 Turning to Figure 2, there is shown a schematic representation of a method for hydrothermally decomposing an oxidised metal chloride solution. In the present embodiment, the feed solution 20 is one that might result form the leaching of a laterite or polymetallic base metal sulphide ore.
    0047 The feed solution 20 is fed into a hydrothermal decomposer reactor 21 wherein the temperature is raised to 170-200°C, preferably 175-185°C. It is a condition of the invention that the feed solution contains one of, all of, or a combination thereof of magnesium, calcium or zinc, since the presence of these metals do not decompose under these conditions, and will ensure that the solution does dry out in the decomposer. These metals should comprise at least 10%, and preferably >30% of the overall metal concentration.
    0048 The hydrothermal decomposer reactor 21 may be any agitated vessel, and is preferably acid-brick lined, more preferably with fused alumina. Agitation is necessary, especially if the reactor is externally heated, in order to prevent scaling on the walls In practice, a cascade of several reactors is required to ensure sufficient residence time for the reactions of (4) and (5) below to reach completion. The end-point of the reaction is simply determined in that no further generation of HC1 gas is observed. This is a very simple and easily-observed end-point, unlike what is observed with those processes discussed in the Background section
    DK 2020 70078 A1
    0049 Raising the temperature causes the thermal decomposition of the metal chlorides. The temperature may be raised by heat 22 through an external heat exchanger, or by the addition of steam, or by a jacketed heated vessel. As the metal chlorides decompose, HCl vapour 23 is formed and condensed in any suitable off-gas system. The strength of the HCl vapour is directly proportional to the decomposable metals concentration of the incoming feed solution 20. The following equations show the reactions for iron, aluminium (trivalent metals), copper and nickel (divalent metals)
    2FeCh + 3H2O ->Fe2O3 + 6HC1(4)2A1CU + 3H2O —A12O3 + 6HC1(5)2CuC12 + 3H2O ->Cu(OH)2-Cu(OH)Cl + 3HC1(6)2NiCl2 + 3H2ONi(OH)2»Ni(OH)Cl + 3HC1(7)
    0050 Theoretically, it is possible to selectively decompose the metals in order, according to the order indicated by Monhemius referenced in paragraph 5. However, in practice it is difficult to do so, and nor is it necessary, since the base metals form basic chlorides, and these readily redissolve in dilute hydrochloric acid
    0051 As the metals decompose, the non-reactive metal chlorides (calcium, magnesium and zinc) increase in composition, and the reactor is allowed to overflow into a quench reactor 24, containing dilute hydrochloric acid 25 and operating at atmospheric conditions. The basic chlorides re-dissolve, whereas the metal oxides do not, and in this way, copper and nickel are effectively separated from iron and aluminium, and the associated hydrochloric acid recovered for recycle.
    0052 The strength of the dilute hydrochloric acid is sufficient to re-dissolve the base metals. The background metal chlorides which had not decomposed are allowed to build up to a suitable concentration to allow further processing. For example, in the case of magnesium, this would be 300-350 g/L MgCl2, and for zinc chloride 200-250 g/L
    0053 Solid-liquid separation 27 of the quench reactor slurry 26 may be effected by any convenient means, such as, but not limited to, flocculation and thickening, filter press or vacuum belt filter. The solids 28 are a mixture of metal oxides, primarily, but not limited to, hematite and alumina. The solution 29 contains base metals and the non-decomposable metal chlorides, which may be processed by conventional means for the recovery of the separate metals.
    0054 Carrying out the quench reaction in this way thereby solves the issues which were paramount with the PORI and SMS Siemag Processes, and which ultimately resulted in their downfall In the present invention, solid-liquid separation is carried out at ambient and atmospheric temperatures, which is a very simple and effective operation, whereas in the other processes, it has/had to be carried out at 170-180C, with the attendant potential for freezing, particularly of the various valves involved.
    DK 2020 70078 A1
    0055 The objective of this process has been to have an effective and efficient separation of value metals such as nickel and cobalt, from nuisance elements such as iron and aluminium, and at the same time recover the associated hydrochloric acid for recycle.
    0056 The principles of the present invention are illustrated by the following examples, which are provided by way of illustration, but should not be taken as limiting the scope of the invention:
    0057 Example 1
    0058 A saturated solution of ferrous chloride was prepared at room temperature, and deaerated with nitrogen. The de-aeration was carried out in order to preclude any air oxidation. 200 mL of solution were placed in an electrolytic cell, containing a titanium cathode and a graphite anode. An anodic current density of 300 A/m2 was applied, and the ferrous iron concentration was monitored via titration. No chlorine evolution was observed from the anode, and the solution rapidly turned a red colour. Because of the de-aeration, hydrogen was initially observed to be evolved from the cathode. Hydrogen evolution continued as long as ferrous iron was observed in solution, and ceased once there was no detectable ferrous iron in solution. Concurrently, chlorine evolution at the anode was noted, and after the test was stopped, a thin plate of iron foil was noted on the cathode
    0059 This test demonstrates that electrolytic oxidation proceeds, and that it is also necessary to maintain some ferrous iron in solution to prevent the plating of metallic iron
    0060 Example 2
    0061 A solution containing 282 g/L ferric iron, 10.5 g/L Al, 9.96 g/L Cu, 9.61 g/L Co, 9.96 g/L Ni and 11.4 g/L Mg was heated up to 177C for a period of 110 minutes. Hydrochloric acid of 6M concentration was recovered. After quenching, solids analysing 64.4% Fe, 1.43% Al and 0.05% Cu were recovered. The other metals were not detected in the solids. 56% of the HC1 and 67.2% of the iron were recovered.
    0062 This demonstrates the efficiency of separating iron and aluminium from base metals, and at the same recovering hydrochloric acid.
    0063 Example 3
    0064 A solution similar to that in Example 2 was heated to a temperature of 186°C, but allowed to react for 648 minutes. This time, there were no detectable base metals in the solids, and the iron content of the solids was 64 3% 100% of the HC1 was recovered at a concentration of 10.9M.
    权利要求:
    Claims (20)
    [1] 1. A process for the oxidation of ferrous iron in chloride solutions and recovery of hydrochloric acid, comprising:
    i. feeding a solution containing ferrous chloride and hydrochloric acid into a reactor having an anode and a cathode;
    ii. applying a current to the anode and cathode to cause oxidation of the hydrochloric acid forming reactive monatomic chlorine, which immediately reacts with the ferrous iron oxidising it to ferric;
    iii. heating of the so-formed ferric chloride-containing solution to effect hydrothermal decomposition of the metal chlorides contained in the solution, evolving hydrochloric acid and forming a mixture of metal oxides and basic chlorides;
    iv. quenching of the so-formed decomposition slurry in dilute hydrochloric acid, wherein the basic metal chlorides re-dissolve; and
    v. proceeding with solid-liquid separation of the quench slurry for the recovery of metal oxides.
    [2] 2. The process of claim l, wherein in (i), a molar ratio of ferrous iron to hydrochloric acid is >1.
    [3] 3. The process of claim 2, wherein an excess hydrochloric acid is used to maintain the pH < 2.0 to prevent subsequent ferric iron hydrolysis.
    [4] 4. The process of claim l, wherein in (ii), a residual ferrous iron concentration is maintained in the range 0.5-5.0 g/L.
    [5] 5. The process of claim 4, wherein the residual ferrous iron concentration is maintained in the range 0.5-1.0 g/L.
    [6] 6. The process of claim l, wherein in (ii), a feed temperature is from ambient to boiling.
    [7] 7. The process of claim l, wherein in (ii), the current has a density of from 50-500 A/m2.
    DK 2020 70078 A1
    [8] 8. The process of claim 7, wherein the current density is 300- 350 A/m2.
    [9] 9. The process of claim l, wherein in (iii), the ferric solution also contains a metal chloride which remains liquid at a temperature of 180-190°C.
    [10] 10. The process of claim 9, wherein the metal chloride is magnesium.
    [11] 11. The process of claim 9, wherein the metal chloride is calcium.
    [12] 12. The process of claim 9, wherein the metal chloride is zinc.
    [13] 13. The process of claim l, wherein in (iii), the solution also contains one, any or all of aluminum, cobalt, nickel, copper, lead, manganese, titanium, or vanadium.
    [14] 14. The process of claim l, wherein in (iii), the temperature is raised to 180-190°C.
    [15] 15. The process of claim l, wherein in (iii), trivalent and higher valent metals form their oxides, which are insoluble in dilute hydrochloric acid.
    [16] 16. The process of claim 15, wherein iron forms hematite and aluminum forms alumina.
    [17] 17. The process of claim l, wherein in (iii), divalent metals form their basic metal chlorides, which are readily soluble in dilute hydrochloric acid.
    [18] 18. The process of claim l, wherein in (iii), alkali metal chlorides and calcium chloride remain as chlorides, and zinc remains as a chloride.
    [19] 19. The process of claim l, wherein in (iii), the hydrochloric acid is condensed and recycled within the process.
    [20] 20. The process of claim l, wherein in (iii), the reaction is allowed to go to completion, denoted by no more HCl gas being evolved.
    类似技术:
    公开号 | 公开日 | 专利标题
    US9889421B2|2018-02-13|Process for the recovery of metals and hydrochloric acid
    EP2195470B1|2016-08-03|System and method for extracting base metal values from oxide ores
    KR100586271B1|2006-06-07|Chloride assisted hydrometallurgical extraction of nickel and cobalt from sulphide or laterite ores
    EP0013098B1|1982-05-12|Removal of manganese ions from zinc and manganese containing solutions
    JP2000234130A|2000-08-29|Method of recovering valuable metal from oxide ore
    US20200141014A1|2020-05-07|Method for the oxidation and hydrothermal dissociation of metal chlorides for the separation of metals and hydrochloric acid
    WO2001083835A2|2001-11-08|Gold recovery process with hydrochloric acid lixiviant
    WO2015192234A1|2015-12-23|Recovery of zinc and manganese from pyrometallurgy sludge or residues
    EP3575420A1|2019-12-04|Bismuth purification method
    Antuñano et al.2017|Development of a combined solid and liquid wastes treatment integrated into a high purity ZnO hydrometallurgical production process from Waelz oxide
    OA19386A|2020-07-31|Method for the oxidation and hydrothermal dissociation of metal chlorides for the separation of metals and hydrochloric acid.
    US20170044644A1|2017-02-16|Process of extracting gold and silver from ores and mining by-products
    JP5124824B2|2013-01-23|Method for treating a compound containing gallium
    WO2019161447A1|2019-08-29|Method for the recovery of manganese products from various feedstocks
    WO2011120093A1|2011-10-06|Recovering metals from pickle liquor
    EP0935005B1|2002-04-24|Process for treating metallic dust, mostly oxididised waste, in particular galvanising dust and/or steelworks smoke
    US4030917A|1977-06-21|Hydrometallurgical processing of metal sulfides
    US9017625B2|2015-04-28|Upgrading of titaniferous material
    RU2567609C2|2015-11-10|METHOD OF PRODUCTION OF COPPER CHLORIDE | CuCl
    US6409980B1|2002-06-25|Process and apparatus for treating foundry sludge to recover magnesium
    EP3406745A1|2018-11-28|Processing of a waste metal material comprising an iron component and a non-iron metal component
    JP2000290736A|2000-10-17|Treatment of electric furnace dust
    Lucheva et al.2003|Method for aluminium dross utilization
    CA1338837C|1997-01-14|Production of a magnesium product from a magnesite ore
    KR20170075839A|2017-07-04|Method for fabricating byproduct from nickel extraction
    同族专利:
    公开号 | 公开日
    CL2020000036A1|2020-06-19|
    RU2020105652A|2021-08-09|
    US20200141014A1|2020-05-07|
    AU2018295584A1|2020-02-27|
    EP3649265A1|2020-05-13|
    ZA202000806B|2021-02-24|
    MA51025A|2021-04-07|
    WO2019006545A1|2019-01-10|
    CA3068794A1|2019-01-10|
    JP2020528966A|2020-10-01|
    KR20200093515A|2020-08-05|
    CN111094602A|2020-05-01|
    EP3649265A4|2021-04-07|
    BR112020000358A2|2020-09-01|
    PE20201138A1|2020-10-26|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    GB549148A|1941-05-05|1942-11-09|Du Pont|Improvements in or relating to electrolytic cells|
    US4107011A|1975-03-17|1978-08-15|Vladimir Ilich Kucherenko|Method of regeneration of spent etching solutions|
    US4632738A|1982-09-03|1986-12-30|Great Central Mines Ltd.|Hydrometallurgical copper process|
    US4604175A|1982-12-07|1986-08-05|Naumov Jury I|Process for regeneration of iron-copper chloride etching solution|
    GB9803018D0|1998-02-13|1998-04-08|Tioxide Group Services Ltd|Treatment of metal chloride|
    AUPR045100A0|2000-09-28|2000-10-26|Shipard, Stewart Lloyd|Atmospheric dissolution of sulphide minerals|
    FR2839984A1|2002-05-23|2003-11-28|Afelec|Treatment of a spent pickling bath in an electrolysis cell with a cathodic compartment and an anodic compartment separated by an anion exchange membrane permeable to chloride ions and impermeable to iron ions|
    WO2007071020A1|2005-12-23|2007-06-28|Harris G Bryn|Process for recovering iron as hematite from a base metal containing ore material|
    JP2010504423A|2006-09-21|2010-02-12|キュイテ−フェルエチタンインコーポレイティド|Electrochemical method for recovery of metallic iron and chlorine values from iron-rich metal chloride waste|
    US8961649B2|2007-08-29|2015-02-24|Vale Canada Limited|System and method for extracting base metal values from oxide ores|
    AU2008352881B2|2008-03-20|2013-04-04|Rio Tinto Iron & Titanium Inc.|Electrochemical process for the recovery of metallic iron and chlorine values from iron-rich metal chloride wastes|
    RU2495827C2|2008-06-19|2013-10-20|Смс Симаг Акциенгезельшафт|Method for reclamation of iron oxide and hydrochloric acid|
    MX356807B|2010-02-18|2018-06-13|Brav Metal Tech Inc|Process for the recovery of metals and hydrochloric acid.|
    AR081403A1|2011-02-04|2012-08-29|Neomet Technologies Inc|METHOD FOR RECOVERING CHLORIDE AND METAL ACID FROM A LIQUOR OF CHLORINE, REACTOR USED AND PROCESS FOR THE RECOVERY OF CHLORIDE ACID AND OXIDATION / HYDROLISIS OF IRON FERRING FROM A CLOSURE SOLUTION|
    AU2011202421A1|2010-03-30|2011-10-13|Intec Ltd|Recovering metals from pickle liquor|
    AT13805U1|2013-07-04|2014-09-15|Pureox Industrieanlagenbau Gmbh|Process for the electrochemical oxidation of Fe-2 + chloride solutions|
    CN104263016B|2014-09-11|2016-04-27|福建坤彩材料科技股份有限公司|Extract method prepares pearly pigment method from ilmenite hydrochloric acidolysis liquid altogether|
    CN105776140A|2016-03-17|2016-07-20|芦秀琴|Method for recovering hydrochloric acid and metal oxides from metal chloride solution|
    RU2623948C1|2016-04-06|2017-06-29|Публичное акционерное общество Приаргунское производственное горно-химическое объединение |Method of integrated treatment of pyrite cinders|AR117178A1|2018-11-30|2021-07-14|Nmr360 9203 5468 Quebec Inc|PROCESS FOR THE RECOVERY OF MINES-VALUE METALS, CONCENTRATES, INTERMEDIATES AND ZINC-CARRYING WASTE|
    法律状态:
    2020-02-13| PAT| Application published|Effective date: 20200207 |
    2021-02-25| PHB| Application deemed withdrawn due to non-payment or other reasons|Effective date: 20210101 |
    优先权:
    申请号 | 申请日 | 专利标题
    US201762529571P| true| 2017-07-07|2017-07-07|
    PCT/CA2018/050799|WO2019006545A1|2017-07-07|2018-06-28|Method for the oxidation and hydrothermal dissociation of metal chlorides for the separation of metals and hydrochloric acid|
    [返回顶部]