    A blade insert 4 for a wind turbine blade root attachment for receiving a bolt within an internal thread of the insert, the insert 4 being a hybrid insert comprising an elongate body 6 formed of a first material such as mild steel, having joined thereto an annular end portion 8 formed of a second material such as stainless steel which has high corrosion resistance, the two portions being joined through a friction weld process.
    公开号:DK201570288A1
    申请号:DKP201570288
    申请日:2015-05-18
    公开日:2016-12-12
    发明作者:Lars Lund；Anders Jensen
    申请人:Vestas Wind Sys As；Avk Tooling As；
    IPC主号:
    专利说明:

    BLADE ROOT INSERT AND METHOD OF MANUFACTURE Background of the Invention
    The present invention is directed to a wind turbine blade root insert which has improved corrosion resistance properties, to a blade having such inserts, and to a method of manufacturing such an insert.
    In a utility scale wind turbine the blades are conventionally connected to the hub by a bolted connection. The hub carries a bearing structure which allows the blade to rotate or pitch to a limited degree about its longitudinal axis, including a bearing ring which is rotatable relative to the fixed part of the bearing which is fixed to the hub. This bearing ring is formed with spaced openings for receiving the connecting bolts. The root end of the blade is provided with a series of longitudinally-extending metal inserts sunk into the root end face, spaced evenly around the root end each having an internal screw thread. When the blade is connected to the hub, bolts are passed through the openings in the bearing ring, the bolt ends being screwed into the inserts to make a rigid releasable connection of blade to hub. A large number of inserts are provided such that the high loading to which the blade root is subjected is spread over a large number of bolt connections.
    The inserts, sometimes referred to as “carrots” due to their shape, are largely embedded in the blade, being fitted into drilled openings in blade root and secured therein by adhesive. Only the end faces of the inserts are exposed at the blade root end face. The inserts are typically formed of mild steel, given the need for high strength. However, the environment in which a wind turbine operates may be harsh, being exposed to weather -rain and in offshore environment salt, over the turbine lifetime, which may be 20 to 25 years. Despite measures to reduce the effects of the environment, such as use of oils over exposed metal areas, and use of protective tapes over inserts prior to blade mounting, a degree of corrosion almost inevitably occurs. This arises predominantly at the insert end face but also to a degree along the bondline between insert and blade. Over a long period such corrosion has the potential to reduce the strength of the connection.
    The present invention is directed to providing an insert structure which exhibits improved corrosion properties.
    Summary of the Invention
    According to a first aspect of the invention there is provided a blade insert for a wind turbine blade root attachment for receiving a bolt within an internal thread of the insert, the insert comprising an elongate body formed of a first material, having joined thereto an annular end portion formed of a second material which has higher corrosion resistance than said first material.
    The first material may be a mild steel, chosen for its good mechanical properties and low cost. The second material is preferably a stainless steel, selected for its good corrosion resistance.
    The insert is arranged such that the threaded portion is formed only in the first portion, whilst the end portion forms an annular collar without internal thread through which, in use, the blade bolt extends. In this way, as a bolt is fitted in the insert and tightened as the blade is secure to the bearing, the end portion and joint is maintained in compression.
    In a further aspect the invention resides in a wind turbine blade formed with a plurality of such inserts.
    In a still further aspect the invention resides in a method of forming a root insert for a wind turbine blade, comprising providing a first stock part of a first material for forming a main body of the insert; providing a second stock part of a second material which has higher corrosion resistance than the first material for forming an end portion of the insert; rotation welding the stock parts together; machining the exterior to remove excess material; and drilling and machining the interior to form a longitudinal opening having an internal thread.
    Brief Description of the Drawings
    Embodiments of the invention are now described, by way of example only, with reference to the following drawings in which:
    Figure 1 is an end view of the root end of a wind turbine blade showing blade root inserts;
    Figure 2 is a sectional view of a part of a hybrid blade root insert according to an embodiment of the invention;
    Figure 3(a) shows the first step of forming a hybrid insert by friction welding components of the insert together; and
    Figure 3(b) shows the formation of the hybrid insert from the stock.
    Detailed Description of the Preferred Embodiment
    In a utility scale wind turbine the blade is connected to the hub through a bolted connection comprising a large number of bolts which pass through respective openings in a movable ring of a blade bearing on the hub into respective connections in the blade root.
    As shown in Figure 1 in a conventional wind turbine blade which is typically made of a reinforced fibre composite such as glass and/or carbon fibre in a resin matrix, the blade root end 2 is provided with a plurality of inserts 4 fitted into openings drilled into the blade root end and bonded therein. These are equidistantly spaced round the blade root end and each extend longitudinally within the blade (Figure 1 showing the positions of only a few of the inserts, by dotted lines). These inserts 4 each carry an internal thread into which respective bolts from the blade bearing are tightened. Ends of these inserts 4 are exposed at the blade root end face, from which they extend by a small distance typically less than 5mm. Alternatively, it is also known to employ composite pre-forms in the root end which are layed up with the blade materials before curing. The openings may be drilled into these pre-forms. This may be done after moulding of the blade or alternatively the openings may be pre-drilled in the pre-forms before these are inserted into the layup.
    In accordance with the invention, as shown in Figure 2, the inserts 4 are formed as hybrid inserts formed of a main body part 6 of a relatively lower grade steel and an end portion 8 of steel having a higher corrosion resistance. In the preferred embodiment the main part 6 is formed of mild steel as is conventional, but joined at joint 7 to an end portion 8 of a stainless steel, noting that an exposed end face 5 of the insert is at the right hand side of the figure. By mild steel is meant low carbon steel having a low carbon content of about 0.05 to 0.3% by weight carbon, more typically 0.1 to 0.25% carbon. By stainless steel is meant steel having a high chromium content, typically at least 13% potentially up to 25%, and which may be austenitic, ferritic or martensitic depending on carbon content and the presence and content of other alloy elements.
    The end portion 8 is tubular and preferably has an inner surface that is devoid of internal thread, the internal thread indicated 10 being formed only in the main mild steel body portion 6, whereby the stainless steel portion 8 and joint 7 between main body portion 6 and stainless steel end portion 8 is not directly subjected to loading, notably the torsional loading, from the blade bolts. Indeed, as the joint 7 is arranged towards the outer side of the insert with bolt connection into the thread 10, as a bolt is inserted and tightened, the bearing bears against the insert such that the steel portion 8 and joint is placed in compression. As is usual the insert may be bonded into the opening in the blade root end face by means of an adhesive, whilst other treatments may further improve the adhesion of insert
    In this manner the part of the insert 4 which is exposed at the blade root end face is formed of a material having high corrosion resistance. Moreover, a significant length of insert 4 potentially susceptible to corrosion at the external bondline with the blade root, indicated 12 in Figure 2, is also thereby of high corrosion resistance. In use in order to further improve corrosion resistance of the end portion of the insert an oil film may be applied at the exposed interior, as indicated at 14. The length of the stainless portion 8 may be relatively short for example 20-60mm depending on the length of the insert, or as little as 10mm. It is important that the length of stainless steel portion 8 exceeds the distance by which the insert protrudes from the root end.
    In formation of the hybrid insert, the stainless steel end part may be secured to the main body part 6 using a rotational friction welding technique as is now described with reference to Figure 3. Rotational friction welding requires that a first component is held stationary with respect to a second component spaced therefrom and rotating at high speed, and the components brought together whilst the drive of the rotating part is stopped. The resulting friction and localised heat thereby created causes the materials to bond together, with the rotating part rapidly slowing to rest as it becomes joined to the stationary part. More particularly, as shown in Figure 3(a) in the joining of the parts to form the insert 4 as described above, a cylindrical rod 20 of mild steel destined to form the main body part 6 is held stationary in a chuck 21 whilst a separate stainless steel rod 22 is held in a rotating chuck 23 rotating at high rotational speed. The stainless steel rod 22 is brought into contact with the mild steel part 20 as the rotational drive is disconnected, whereby the mild steel part 20 and stainless steel 22 part are joined through a rotational weld. Depending on the desired length of stainless steel portion, if this is particularly short, due to the difficulty in gripping a short length of stainless steel, it may be arranged that a longer section of stainless steel is provided, for example a 50mm length, and this then cut after welding. The composite rod of joined parts 20, 22 is then machined externally with tool 24 to produce a generally smooth exterior and to remove the excess material at the joint, and drilled internally machined internally to provide the longitudinal opening with thread 10 and smooth interior to the stainless steel portion 8.It is recognised that the friction-welding is an effective way of forming the hybrid insert; indeed, the joint need not be hugely strong since the joint is not subjected to torsional loading, but rather to compressive loading.
    Alternatively, other techniques for joining the main body part and stainless steel end part can be utilised. For example, the two parts may be formed with cooperating structures such as a splined coupling or upstands formed on one part received in openings or slots on the other.
    权利要求:
    Claims (8)
    [1] 1. A blade insert for a wind turbine blade root attachment for receiving a bolt within an internal thread of the insert, the insert comprising an elongate body formed of a first material, having joined thereto an annular end portion formed of a second material which has higher corrosion resistance than said first material.
    [2] 2. A blade insert according to claim 1 wherein said first material is mild steel.
    [3] 3. A blade insert according to claim 1 or 2 wherein the second material is stainless steel.
    [4] 4. A blade insert according to any preceding claim wherein the internal thread is formed only in the main body portion formed of the first material.
    [5] 5. A blade insert according to claim 1 or 2 wherein the end portion is joined to the elongate body by a friction welding technique.
    [6] 6. A blade insert according to any preceding claim wherein the end portion has a length between 10mm and 60mm.
    [7] 7. A wind turbine blade having a plurality of root inserts according to any preceding claim.
    [8] 8. A method of forming a root insert for a wind turbine blade, comprising: - providing a first stock part of a first material for forming a main body of the insert; - providing a second stock part of a second material which has higher corrosion resistance than the first material for forming an end portion of the insert; -rotation welding the stock parts together; - machining the exterior to remove excess material; -drilling and machining the interior to form a longitudinal opening having an internal thread.
    类似技术:
    公开号 | 公开日 | 专利标题
    EP3133298B1|2019-02-06|Connector
    US10598200B2|2020-03-24|Composite tubular structure
    US4236873A|1980-12-02|Wind turbine blade retention device
    US7419435B2|2008-09-02|Composite torque tube captured end fitting
    US10184509B2|2019-01-22|Composite tension/compression strut
    US11067114B2|2021-07-20|Composite end connections
    CN103032273A|2013-04-10|Arrangement for fixing a component inside of a wind turbine
    EP3298268B1|2019-08-21|Blade root insert and method of manufacture
    CN106795855B|2019-05-07|Wind power plant rotor blade
    CA2845841C|2016-06-07|Bimetallic shaft for gearbox systems to limit wear and corrosion
    WO2018113204A1|2018-06-28|Centering fastener, methods for manufacturing and using same, and wind turbine
    WO2011127096A9|2012-03-01|Riser components and methods for making the same
    EP3022461B1|2019-05-01|Flywheels for energy storage and methods of manufacture thereof
    US10024466B2|2018-07-17|Metal pipe having a connector
    CA3017377A1|2019-04-30|Composite tubular structure
    EP2935870A1|2015-10-28|Turbine blade
    KR102168942B1|2020-10-22|Propulsion System of Ship
    Kim et al.2015|Joining performance evaluation of different types of GEP224 glass/epoxy-to-AZ31B magnesium alloy singlelap joints
    Balyts’kyi et al.2013|Assessment of the fatigue damage to the propeller shaft of a sea craft
    Albiez et al.2022|Hybrid joining of jacket structures for offshore wind turbines–Validation under static and dynamic loading at medium and large scale
    RU147929U1|2014-11-20|ROWING SHAFT OF POLYMERIC COMPOSITE MATERIALS BASED ON PROSPECTIVE CARBON REINFORCING SYSTEMS
    Maslov et al.2018|Improvement of Hole Drilling in High-Strength Polymer Laminate
    CN107819363A|2018-03-20|Motor stator and its manufacture method
    CN105134701A|2015-12-09|Carbon fiber tube connection structure and manufacturing method thereof
    CN111997987A|2020-11-27|Helicopter missile-tail-prevention transmission shaft and manufacturing method thereof
    同族专利:
    公开号 | 公开日
    EP3298268B1|2019-08-21|
    EP3298268A1|2018-03-28|
    WO2016184469A1|2016-11-24|
    CN208702610U|2019-04-05|
    DK178855B1|2017-04-03|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    EP1486415A1|2003-06-12|2004-12-15|SSP Technology A/S|Wind turbine blade and method of manufacturing a blade root|
    GB2465167A|2008-11-07|2010-05-12|Vestas Wind Sys As|A turbine blade having mounting inserts of different lengths|
    CN203498471U|2011-01-28|2014-03-26|维斯塔斯风力系统有限公司|Wind turbine blade with anti-corrosion structure and wind turbine using blade|
    WO2012140039A2|2011-04-11|2012-10-18|Lm Wind Power A/S|Wind turbine blade comprising circumferential retaining means in root regions|
    PL2589796T3|2011-11-04|2015-12-31|Siemens Ag|Manufacture of a root section|CN112814837A|2021-01-20|2021-05-18|东方电气风电有限公司|Wind turbine generator system bolted connection structure, blade root structure, wind turbine blade and unit|
    法律状态:
    优先权:
    申请号 | 申请日 | 专利标题
    DKPA201570288A|DK178855B1|2015-05-18|2015-05-18|Blade root insert and method of manufacture|DKPA201570288A| DK178855B1|2015-05-18|2015-05-18|Blade root insert and method of manufacture|
    PCT/DK2016/050130| WO2016184469A1|2015-05-18|2016-05-17|Blade root insert and method of manufacture|
    EP16724843.4A| EP3298268B1|2015-05-18|2016-05-17|Blade root insert and method of manufacture|
    CN201690000996.9U| CN208702610U|2015-05-18|2016-05-17|Root of blade inserts and wind turbine blade|
    [返回顶部]