    • 专利摘要:
    A panel (10) for use in furniture and interior design applications comprises a continuous outer skin (12) formed of polystyrene or high impact polystyrene. The skin (12) completely encapsulates a cellular plastic core (14). The core (14) is formed from a heat activated foamable plastic particulate material. The area of the largest face of the panel is greater than 1m
    公开号:AU2013213422A1
    申请号:U2013213422
    申请日:2013-01-22
    公开日:2014-08-21
    发明作者:Nicholas Stillwell
    申请人:PROTOMAX PLASTICS Ltd；
    IPC主号:B32B27-06
    专利说明:
    WO 2013/110930 PCT/GB2013/050134 Large Format Polystyrene Panel The present invention relates to a panel or board formed from polystyrene (PS) or high impact polystyrene (HIPS) with 5 a solid, continuous outer skin and a cellular core structure. In particular, it relates to such a panel which is a large format, that is with a largest face of over 1 m 2 in area, and over 11 mm (and preferably over 14mm) in thickness. 10 Current furniture making methods have moved away from solid wood to using composite materials such as MDF, chipboard and glass fibre, with coatings such as melamine or veneer to create a desired surface finish or colour. 15 Fibreboard and oriented strand board are commonly used in furniture and interior design. However, they are not resistant to moisture and therefore need to be painted or laminated as a secondary process to achieve an acceptable 20 surface finish. This may include adding veneers or melamine coatings. This type of board therefore uses adhesives in its production, in both primary and secondary processes, and they are very difficult to recycle once laminated. Therefore, this type of board is limited to interior use in 25 its primary form as it is not weatherproof. Polystyrene and high impact polystyrene are known materials which are generally used in small, thin walled products such as coat hangers and yoghurt pots. The material is extruded 30 as thin sheets which can then by thermoformed into a desired shape. It is possible using current extrusion technology to produce a solid polystyrene sheet of up to approximately 6mm WO 2013/110930 PCT/GB2013/050134 -2 in thickness. However, such solid sheets of PS or HIPS are very brittle and have poor impact resistance. It is not possible using current technology to extrude a large format board of PS or HIPS which is over 11 mm in thickness. Even 5 if it were possible to produce, a board made of solid PS/HIPS in a format of 2440 x 1220 mm (a typical industry standard size), with a thickness of say 19 mm (a typical desirable thickness in many applications in furniture and interior design) it would weigh approximately 55 kg, which 10 is very heavy and therefore unsuitable for furniture and interior design applications. Furthermore, PS/HIPS is a major polluter since little is currently recycled and discarded PS/HIPS does not biodegrade 15 for hundreds of years and is resistant to photolysis. Since degradation of materials creates potentially harmful liquid and gaseous by-products that could contaminate groundwater and air, today's landfill sites are designed to minimise contact with air and water. However, air and water are 20 necessary for degradation and therefore landfill design practically eliminates the degradation of waste. Thus, current fibreboard products are difficult to recycle, require adhesives, secondary processes, suffer under 25 moisture and have some health hazards associated with their processing. Hardwoods are very expensive, may have an environmental impact, and require various treatments before use. Solid plastic boards of over about 11 mm in thickness become very heavy, may still bend, and are expensive. Boards 30 over 11 mm in thickness formed of PS or HIPS simply do not exist in the market at the current time.
    WO 2013/110930 PCT/GB2013/050134 -3 The present invention provides a panel for use in furniture and interior design applications, comprising a continuous outer skin formed of polystyrene or high impact polystyrene completely encapsulating a cellular plastic core formed from 5 a heat-activated foamable plastic particulate material, wherein the area of the largest face of the panel is greater than 1 M 2 . Preferably, the total thickness of the panel is greater than 10 11 mm. Preferably, the outer skin comprises recycled PS or recycled HIPS. The core may also comprise mixed waste plastic. The core may also include reinforcement members. 15 The skin may be moulded to provide a surface texture and/or to incorporate a high temperature printed film. The panel may incorporate at least one of anti-fungal 20 agents, anti-bacterial agents and fire retardant agents to suit a given application. The panel skin is preferably formed from a plastic particulate material applied directly to the surface of a 25 heated mould. The invention will now be described in detail, by way of example only, with reference to the accompanying drawings in which: 30 Figure 1 is a perspective view of a panel in accordance with the present invention; WO 2013/110930 PCT/GB2013/050134 -4 Figure 2 is a cross-section of the panel of Figure 1 along the line 2-2; 5 Figure 3 is a perspective view of a second embodiment of the present invention formed with a non-slip surface; Figure 4 is a perspective view of the third embodiment of the present invention formed with surface graphics; and 10 Figure 5 is a cross-sectional view of the panel of Figure 4 along the line 5-5. Figure 1 illustrates a panel 10 in accordance with the 15 present invention formed of PS or HIPS and with as length 1, width w and thickness t. Typically, the length may be 2440 mm and width 1220 mm which is a typically industry standard size. In the present invention, the thickness is 11 mm or greater, and preferably over 14mm. 20 The panel 10 comprises a continuous, solid outer skin 12 which extends over its entire surface with no openings, vent holes, injection cavities etc. As shown in Figure 2, the skin 12 completely encloses a cellular core 14 which is very 25 strong yet has a lower density and therefore reduced weight for a given volume as compared with the solid skin 12. The cellular core is formed from a heat-activated foamable plastic particulate material. 30 The panel 10 may be produced using a process such as that described in GB 2460838. Here, two heated, open female moulds are provided. Plastic particulate material is placed WO 2013/110930 PCT/GB2013/050134 -5 in both moulds and melts to form a skin lining each mould. An expandable filler material also in particulate form is added to one mould and the two moulds are brought together to form a closed mould cavity. Under the action of heat, the 5 two skins bond together to create a single continuous skin which completely encapsulates the filler material, which expands to form the cellular core, filling the available volume within the continuous skin. 10 Alternatively, the panel 10 may be produced using a moulding machine as described in W02011/114119. This uses a single heated female mould and a non complementary heated lid which may be brought together to form a mould cavity. As above, when the mould and lid are apart, plastic particulate 15 material may be placed in contact with both in order to melt and form the plastic skin. Heat activated foamable plastic particulate filler material is placed in the female mould which is closed by the lid, to create a continuous skin completely encapsulating the filler. Heat from the moulds 20 activates the filler to expand and fill the skin. Thus, the panel 10 is preferably produced by a static mould process in which the mould remains in one place, rather than a process such as extrusion or rotomoulding or one requiring 25 a mould to be moved by conveyers into an oven etc. GB 2460838 describes the use of polyethylene (PE). This shrinks during production allowing easy removal of the finished product from the mould. PS and HIPS were previously 30 considered unsuitable for this method because they undergo considerably less shrinkage. However, as there is less shrinkage, PS/HIPS panels can be formed to precise WO 2013/110930 PCT/GB2013/050134 -6 dimensions, for example for use as concrete formwork in place of plywood. The skin 12 may be formed of virgin or recycled PS or HIPS, 5 which is introduced into the mould in particulate form. The core 14 may be formed of virgin plastic, or mixed plastic waste, which may include PS or HIPS, which is also introduced into the mould in particulate form. 10 The continuous outer skin 12 is moisture proof, scratch resistant and stiff and is supported by the strong but lightweight cellular core 14. The panel 10 can be formed to a desired shape and size 15 depending on the moulds used. Therefore, while a rectangular panel is illustrated other shapes are possible. The panel 10 may also be cut, formed and fabricated by conventional methods to create different end products. 20 Colour may be added to the PS/HIPS skin 12 during manufacture to produce a panel 10 with a desired end-use colour. Therefore, painting or laminating are not required. In a smooth mould, a very smooth outer surface of the skin 25 12 can be achieved. However, a textured or decorated surface can also be formed on the exterior of the panel 10. The walls of the moulds used may be textured to impart a given texture to the skin 12. For example, as in Figure 3, a checker plate pattern of raised projections and/or 30 depressions 16 can be moulded directly into the skin 12 to provide a non-slip surface on at least one face of the panel 10.
    WO 2013/110930 PCT/GB2013/050134 -7 Surface decoration can also be provided by placing a high temperature printed film 18 in one or both moulds before forming the panel 10. For example, as shown in Figures 4 and 5 5 a wood grain effect can be provided on at least one face by a film 18 which bonds to the skin 12 during the moulding process. Therefore, veneers or laminates are not required. The skin 12 and core 14 of the panel 10 may also incorporate 10 materials and agents to improve the performance for particular customer applications. For example, fire retardants, anti-fungal agents or anti-bacterial agents and so on may be added. 15 Reinforcing members, such as a steel mesh, may be embedded within the core 14 during production to add strength and stiffness to the panel 10. The thickness of the skin 12 of the panel 10 can be adjusted 20 to suit the application. A thin skin 12 will give a lighter panel 10, whereas a thicker skin 12 will increase weight, strength and stiffness. Thus, a panel in accordance with the present invention 25 provides an environmentally friendly alternative to MDF, plywood, fibreboard and chipboard. The panel can be produced from waste materials and recycled again into another panel of the same type at the end of its life. In particular it can be provided from PS and HIPS which are seldom recycled 30 at present. The panel also has improved performance in relation to the known alternative materials since it is moisture proof, scratch resistant, and strong yet WO 2013/110930 PCT/GB2013/050134 -8 lightweight. Different surface finishes can be incorporated at the primary production stage so that secondary processes are unnecessary. 5 10 15 20 25 30
    权利要求:
    Claims (10)
    [1] 1. A panel for use in furniture and interior design applications, comprising a continuous outer skin formed of 5 polystyrene or high impact polystyrene completely encapsulating a cellular plastic core formed from a heat activated foamable plastic particulate material, wherein the area of the largest face of the panel is greater than 1 M 2 . 10
    [2] 2. A panel as claimed in claim 1, wherein the total thickness of the panel is greater than 11 mm.
    [3] 3. A panel as claimed in any preceding claim, wherein the continuous outer skin is formed of recycled polystyrene or 15 recycled high impact polystyrene.
    [4] 4. A panel as claimed in any preceding claim, wherein the core comprises mixed waste plastic. 20
    [5] 5. A panel as claimed in any preceding claim, wherein the core includes reinforcement members.
    [6] 6. A panel as claimed in any preceding claim, wherein the skin is moulded to provide a surface texture. 25
    [7] 7. A panel as claimed in any preceding claim, wherein the skin incorporates a high temperature printed film.
    [8] 8. A panel as claimed in any preceding claim, 30 incorporating at least one of anti-fungal agents, anti bacterial agents and fire retardant agents. WO 2013/110930 PCT/GB2013/050134 - 10
    [9] 9. A panel as claimed in any preceding claim, wherein the skin is formed from a plastic particulate material applied directly to the surface of a heated mould. 5 10. A panel substantially as herein before described and with reference to the accompanying drawings.
    [10] 10 15 20 25 30
    类似技术:
    公开号 | 公开日 | 专利标题
    US20200147941A1|2020-05-14|Patterned Composite Product
    US20210162703A1|2021-06-03|Composite products
    AU621884B2|1992-03-26|Foam composite and method of forming same
    CA2535627C|2012-04-03|Composite door structure and method of making same, and composite door and method of making same
    GB2464541A|2010-04-28|Laminate of porous material, curable material and veneer
    CA2861843C|2020-01-07|Large format polystyrene panel
    CZ302660B6|2011-08-24|Process for producing moldings and molding per se
    WO2008070916A1|2008-06-19|Materials, systems and methods involving plastics material
    CN211000308U|2020-07-14|Environment-friendly composite board for railway vehicle
    AU2013248209B2|2016-08-11|Method of forming composite products by pressure, related products and apparatus
    CN208035586U|2018-11-02|A kind of PP composite honeycombs sandwich sheet
    CN111315579A|2020-06-19|Multi-laminated plastic bearing plate and production method thereof
    CN112248562A|2021-01-22|Continuous fiber reinforced plastic-suction honeycomb plate for interior trim panel and preparation method thereof
    CN110626021A|2019-12-31|Environment-friendly composite board for railway vehicle
    RU1460U1|1996-01-16|PANEL WITH DECORATIVE COATING FROM POLYMERIC COMPOSITE MATERIAL
    EP1944156A1|2008-07-16|A thermoformable layered material and the production process thereof
    AU2016208360A1|2016-08-11|Method of forming composite products by pressure, related products and apparatus
    WO2005105433A1|2005-11-10|A timber substitute
    KR20000019518A|2000-04-15|Assembly type ceiling panel for bathroom consisted of thermoplastic resin sheet, foaming resin and frame and production method thereof
    同族专利:
    公开号 | 公开日
    GB201201039D0|2012-03-07|
    GB2498717B|2014-06-25|
    CA2861843A1|2013-08-01|
    AU2013213422B2|2016-05-12|
    CA2861843C|2020-01-07|
    GB2498717A|2013-07-31|
    JP2015511134A|2015-04-16|
    HK1185585A1|2014-02-21|
    WO2013110930A1|2013-08-01|
    US20160001529A1|2016-01-07|
    RU2618053C2|2017-05-02|
    CN104271349A|2015-01-07|
    EP2807027A1|2014-12-03|
    CN104271349B|2016-09-21|
    RU2014134441A|2016-03-20|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    ZA718171B|1971-01-12|1972-09-27|Lavorazione Mat Plast|Synthetic resin laminate and its manufacturing process|
    GB1408592A|1972-07-20|1975-10-01|Monsanto Ltd|Foamed resin sheet|
    US4136220A|1976-07-14|1979-01-23|Union Carbide Corporation|Process for the molding of plastic structural web and the resulting articles|
    US5695870A|1995-04-06|1997-12-09|The Dow Chemical Company|Laminated foam insulation board of enhanced strength|
    JP2001027009A|1999-07-13|2001-01-30|Sumitomo Chem Co Ltd|Thermoplastic resin panel|
    JP2001062864A|1999-08-31|2001-03-13|Noritz Corp|Resin panel having heat insulation and its manufacture|
    JP2002144495A|2000-11-16|2002-05-21|Idemitsu Unitech Co Ltd|Laminate, and material for building, sub-material for package, member for automobile and partition using the same|
    JP2002327530A|2001-03-02|2002-11-15|Nkk Corp|Plastic composite panel and its manufacturing method|
    US7445840B2|2003-12-29|2008-11-04|Seiki Kogyo Co., Ltd.|Weather-resistant synthetic wood material|
    WO2005105433A1|2004-04-30|2005-11-10|Armacel Pty Limited|A timber substitute|
    TWI609788B|2008-04-14|2018-01-01|波利渥克股份有限公司|Deep draw method of making impact and vibration absorbing articles and the articles formed thereby|
    GB2460838C|2008-06-09|2013-11-06|Nicholas Stillwell|Process for moulding plastic articles|
    GB2478796B|2010-03-19|2014-01-08|Upcycle Holdings Ltd|Process for forming a mould|
    RU105621U1|2010-09-15|2011-06-20|Общество С Ограниченной Ответственностью "Интер-Ремонт"|CELLULAR MATERIAL|ITPS20140014A1|2014-10-24|2016-04-24|Angelo Candiracci|PRODUCTION PROCESS OF PREFABRICATED PANELS AND DRUMS FOR THE FURNITURE INDUSTRY AND PRODUCTS WITH THIS PROCESS OBTAINED|
    法律状态:
    2016-06-16| PC1| Assignment before grant (sect. 113)|Owner name: UPCYCLE HOLDINGS LIMITED Free format text: FORMER APPLICANT(S): PROTOMAX PLASTICS LTD |
    2016-09-08| FGA| Letters patent sealed or granted (standard patent)|
    优先权:
    申请号 | 申请日 | 专利标题
    GB1201039.3||2012-01-23||
    GB1201039.3A|GB2498717B|2012-01-23|2012-01-23|Large format polystyrene panel|
    PCT/GB2013/050134|WO2013110930A1|2012-01-23|2013-01-22|Large format polystyrene panel|
    [返回顶部]