Modification of surfaces for fluid and solid repellency

专利摘要:
Articles, methods of making, and uses for modifying surfaces for liquid repellency are disclosed. The liquid repellant surfaces comprise a surface comprising an anchoring layer. The anchoring layer, which forms an immobilized molecular anchoring layer on the surface, has a head group that is covalently linked to, or adsorbed onto, the surface and a functional group. The functional group of the treated surface has an affinity for a lubricating layer, which is applied to the treated surface. The anchoring layer and replenishable lubricating layer are held together by non-covalent attractive forces. Together, these layers form an ultra-repellant slippery surface that repels certain immiscible liquids and prevents adsorption, coagulation, and surface fouling by components contained within.
公开号:AU2013207938A1
申请号:U2013207938
申请日:2013-01-10
公开日:2014-08-28
发明作者:Joanna Alzenberg；Michael ALZENBERG；Donald Ingber；Philseok Kim；Daniel C. Leslie；Michael Super；Anna Waterhouse；Alexander L. Watters
申请人:Harvard College；
IPC主号:C09D5-16

专利说明:
WO 2013/106588 PCT/US2013/021056 MODIFICATION OF SURFACES FOR FLUID AND SOLID REPELLENCY CROSS-REFERENCE TO RELATED APPLICATIONS [0001] This application claims priority to U.S. Provisional Patent Application No. 61/585,059 filed January 10, 2012 and U.S. Provisional Patent Application No. 61/692,079 filed August 22, 2012 both of which are hereby incorporated by reference in their entirety. STATEMENT CONCERNING GOVERNMENT RIGHTS IN FEDERALLY-SPONSORED RESEARCH [00021 This invention was made with government support under Grant No. 5U0 1NS073474-.03 awarded by the National Institutes of Health and under N66001-11-1-4180 awarded by the U.S. Department of Defense. The government has certain rights in this invention. TECHNICAL FIELD [00031 The present disclosure relates generally to surfaces that are transformed to reduce friction between, and prevent adhesion, adsorption, and deposition from liquids, semi-solids, and solids. BACKGROUND 100041 There has been limited success in developing materials that prevent molecular or particulate adhesion, adsorption, deposition and biofouling of a variety of commercially available surfaces for use in medical devices, such as catheters, syringes, dialysis instruments, and for the prevention of blood coagulation or clotting, oil pipelines, food and cooking surfaces, and preventing ice adhesion and formation. [00051 Synthetic surfaces have been made that consist of nano/microstructured substrates infused with fluid that is locked in place by a roughened or porous substrate to form a slippery interface capable of repelling liquids. However, such surfaces are limited to particular combinations of lubricating liquids and substrates having a certain roughness or porosity capable of retaining the lubricating fluid. [00061 Silanization of glass and metal oxides is a general method for modifying a material to make its surface less or more attractive to the other substances. A thin perfluorocarbon ("PFC") layer (omniphobic or amphiphobic as discussed in the literature) is generated by - 1 - WO 2013/106588 PCT/US2013/021056 silanization of surfaces to reduce non-specific (usually hydrophobic) interactions from biomolecules in complex fluids. These treatments minimize adsorption of low concentrations of solutes to glass surfaces in chemistry and biology, but are not sufficient on their own to completely prevent blood coagulation or molecular adsorption. [00071 Fluorous surfaces, i.e., surfaces that are treated to contain fluorocarbon moieties, have been used to form microarray surfaces. For example, glass slides having perfluorocarbon domains attached to molecules of interest have been used to immobilize molecules of interest on a surface. [00081 Moreover, fluorous-treated microelectronechanical "MEM" devices have been used to address a well-known problem in the fabrication of MEM-stiction, which occurs when surface adhesion forces are higher than the mechanical restoring force of the micro-structure. One proposed solution has been to coat the MEMS surface with monomolecular coatings that are "Teflon-like" and covalently bonded to the MEMS surface. This approach fails to prevent adhesion of liquids. [00091 The use of polymeric species to minimize protein adsorption and control blood clotting is known in the art. See, e.g. , Barstad, R.M, et al., Thrombosis and haemostasis 79, 302-305 (1998); Niimi, Y., et al., Anesth. Analg. 89, 573-579 (1999); Chen, S. et al., Polymer 51, 5283-5293 (2010). However, such methods are not entirely effective at repelling blood and preventing blood clot formation without the use of anticoagulants. For example, heparinized polymer-coated products are known in the art. However, because heparinized polymer-coated products are not sufficient to prevent blood clot adhesion, soluble heparin or anticoagulants must be added to the blood to fully prevent coagulation on devices. SUMMARY 100101 There is a need for a repellant surface that prevents molecular or particulate adhesion to, fouling, and blood coagulation on a variety of commercially available surfaces. [00111 An article having a slippery surface is disclosed. The article comprises a substrate having an anchoring layer. The anchoring layer comprises a head group that is attached to the substrate and a functional group, which is directly or indirectly attached to the head group. The article also has a lubricating layer that comprises a lubricating liquid, which has an affinity for the functional group. The lubricating layer is disposed over the anchoring layer, and the layers are held together by non-covalent attractive forces. The anchoring layer and the lubricating layer form a slippery surface configured and arranged for contact with a material that is immiscible with the lubricating liquid.
WO 2013/106588 PCT/US2013/021056 [00121 In one aspect, methods for preventing adhesion, adsorption, surface-mediated clot formation, or coagulation of a material are disclosed. A slippery surface includes an anchoring layer, which comprises a head group attached to the substrate and a functional group directly or indirectly attached to the head group. A lubricating liquid that has an affinity for the functional group of the anchoring layer is applied to create a lubricating layer. The anchoring layer and the lubricating layer are held together by non-covalent attractive forces. An immiscible material that is contacted to the thus-formed slippery surface is repelled. [00131 In another aspect, methods of making an article having a slippery surface are disclosed in which a substrate is contacted with a reactive molecule, which has a head group that is reactive with the substrate, and a functional group that is directly or indirectly attached to the head group. Together they form an anchoring layer on the substrate. The anchoring layer is contacted with a lubricating liquid having an affinity for the functional group to form a lubricating layer that is disposed over the anchoring layer. The anchoring layer and the lubricating layer are held together by non-covalent attractive forces. The anchoring layer and the lubricating layer form a slippery surface that is configured and arranged for contact with a material that is immiscible with the lubricating liquid. 100141 Also disclosed are methods for reducing coagulation of blood. Blood is contacted or stored against a surface that resists coagulation of blood. This surface comprises an anchoring layer, which has a head group attached to the substrate and a functional group directly or indirectly attached to the head group. The surface also comprises a lubricating layer that has a lubricating liquid with an affinity for the functional group. The lubricating layer is disposed over the anchoring layer, which are held together by non-covalent attractive forces. In certain embodiments, coagulation of blood is resisted by providing a lubricating layer that includes a perfluorinated liquid. [00151 A method of extracting a solute from a solution is disclosed. A surface comprising an anchoring layer is provided. The anchoring layer comprises a head group that is attached to the substrate and a functional group, which is directly or indirectly attached to the head group. A lubricating layer comprising a lubricating liquid that has an affinity for the functional group is disposed over the anchoring layer. The anchoring layer and the lubricating layer are held together by non-covalent attractive forces. The surface is contacted with a solution comprising one or more solutes, wherein at least one solute has a greater affinity for the lubricating liquid than the solution.
WO 2013/106588 PCT/US2013/021056 [00161 In one or more embodiments, the head group is covalently attached to, or adsorbed onto the surface. 100171 In one or more embodiments, the anchoring layer forms a monomolecular layer on the surface. [00181 In one or more embodiments, the material being repelled is selected from the group consisting of a liquid, solution, suspension, complex fluid, and a solid. [00191 In one or more embodiments, the slippery surface is hydrophobic or even superhydrophobic. In other embodiments, the slippery surface is oleophobic or even superoleophobic. In still other embodiments, the slippery surface is onmiphobic or even superomniphobic. In some embodiments, the surface could be amphiphilic. [00201 In some embodiments, the functional group is a hydrocarbon. [00211 In one or more embodiments, the functional group is a polar group, and the polar group optionally is selected from the group consisting of charged polypeptides, polyanions, polycations, polar polymers, polysaccharides, amines, carboxylic acids, guanidine, alcohols, sulfhydryls, carboxamides, metal oxides, inorganic oxides, and combinations thereof. [00221 In one or more embodiments, the functional group is a perfluorocarbon. In one or more embodiments, the functional group is a partially fluorinated hydrocarbon. [00231 In some embodiments, the functional group could consist of perfluoropolyethers, polyethers, polysuifides, polyolefins, polyesters, polyamides, polyamphiphiles, and polyampholytes as well as oligomeric forms of aforementioned polymers. An exemplar polyether is poly(propylene oxide) and an oligomeric polyether could be oligo(arylene ether sulfone) while an example of a polyolefin includes polypropylene. [00241 In certain embodients, the head groups of the anchoring layer includes ethers, silyl ethers, siloxanes, esters of carboxylic acids, esters of sulfonic acids, esters of sulfinic acids, esters of sulfuric acids, esters of phosphonic acids, esters of phosphinic acids, esters of phosphoric acids, silyl esters of carboxylic acids, silyl esters of sulfonic acids, silyl esters of sulfinic acids, silyl esters of sulfuric acids, silyl esters of phosphonic acids, silyl esters of phosphinic acids, silyl esters of phosphoric acids, oxides, sulfides, carbocycles, heterocycles with at least one oxygen atom, heterocycles with at least one nitrogen atom, heterocycles with at least one sulfur atom, heterocycles with at least one silicon atom, 'click' reactions-derived heterocycles, Diels-Alder reactions--derived carbocycles, Diels-Alder reactions-derived heterocycles, amides, imides, sulfides, thiolates, metal thiolates, urethanes, oximes, hydrazides, hydrazones, physisorbed or chemisorbed or otherwise non-covalently attached moieties, or -4- WO 2013/106588 PCT/US2013/021056 combinations thereof [00251 In certain embodiments, head groups include maleimides, acrylates, acrylamides, epoxides, aziridines, thiiranes, aldehydes, ketones, aides, alkynes, disulfides, anhydrides, carboxylates phosphates, phosphonates, sulfates, sulfonates, nitrates, amidine, silanes, siloxanes, cyanates, acetylenes, cyanides, halogens, acetals, ketals, biotin, cyclodextrins, adamantanes, and vinyls. [00261 In one or more embodiments, the head group is silane, carboxylate, sulfonate or phosphonate. [00271 In one or more embodiments, the surface is selected from the group consisting of acrylic, glass, polymers, metals, carbon, plastics, paper, ceramics, and combinations thereof. [00281 In certain embodiments, the surface may be selected from biocompatible materials such as hydrogels, biopolymers, and polyesters. [00291 In specific embodiments, the surface is selected from the group consisting of poly(dimethyl siloxane) (PDMS), acrylic, polystyrene, tissue-culture polystyrene, metal, polypropylene, acrylic adhesive, silicon wafer, polysulfone, and soda lime glass, the anchoring layer comprises a silyl group covalently attached to a perfluorocarbon tail, and the lubricating layer comprises perfluorocarbon oil. The anchoring layer and the lubricating layer can form an omniphobic slippery surface that repels an immiscible material. [00301 In one or more embodiments, the surface is treated to activate the surface prior to exposure to the anchoring layer. In one or more aspects, activation comprises acid or base treatment, oxidization, ammonization, plasma, and microwave treatment (or combinations thereof). Activation of surfaces also may be carried out through chemical deposition (vapor or solution), aminolysis, acrylation, transesterification, reduction, nucleophilic or electrophilic substitution, ozonolysis, or irradiation to install reactive or functional groups for subsequent modification with an anchoring layer. [00311 In one or more embodiments, the surface prevents coagulation of blood. In one or more embodiments, the substrate has micropassages through which lubricating liquid is replenished. In other embodiments, the substrate comprises a reservoir through which lubricating liquid is replenished. In still other embodiments, the substrate is a tubing through which boluses of lubricating liquid pass. [00321 In any of the preceding embodiments, the immiscible material is a solid, which can be a particulate, including a dry particulate, or a solid surface. In other embodiments, the immiscible material is a liquid selected from the group consisting of viscous liquids, tion -5- WO 2013/106588 PCT/US2013/021056 viscous, semi-solids, tacky liquids, and complex fluids. In other embodiments, the immiscible material is a dissolved molecule. 100331 In one or more embodiments, the immiscible material contains an additive, which is selected from the group consisting of a solute, a particulate or a combination thereof In one embodiment, the immiscible material is repelled by the surface and the additive is attracted to the surface. In another embodiment, both the immiscible material and the additive are repelled by the surface. [00341 In one or more embodiments, the immiscible material is a bodily fluid. The bodily fluid may be selected from the group consisting of whole blood, plasma, serum, sweat, feces, urine, saliva, tears, vaginal fluid, prostatic fluid, gingival fluid, amniotic fluid, intraocular fluid, cerebrospinal fluid, seminal fluid, sputum, ascites fluid, pus, nasopharengal fluid, wound exudate fluid, aqueous hunour, vitreous humour, bile, cerumien, endolyrnph, perilymph, gastric juice, mucus, peritoneal fluid, pleural fluid, sebum, vomit, and combinations thereof [00351 In one or more embodiments, the immiscible material is a solution or suspension containing bacteria. The bacteria may be selected from the group consisting of Actinobacilus, Acinetobacter (e.g., Acinetobacter baumann ii), Aeromonas, Bordetella, Brevibacilus, Brucella, Bacteroides, Burkholderia, Borelia, Bacillus, Camupylobacter, Capnocytophaga, Cardiobacteriun, Citrobacier, Clostridiun, Chlanydia ELiken ella, Enterobacter, Escherichia, Francisella, Fusobacteriun, Flavobacteriuin, Haenophilus, Hlelicobacter, Kingella, Klebsiella, Legionel/a, Lisleria, Leptospirae, Moraxella, Morgan el/a, MVfvcoptasma, Mycobacteriuni, Neisseria, Pasteure/la, Proteus, Prevotella, Plesiononas, Pseudoionas, Providencia. Rickettsia , Stenotrophononas, Staphylococcus, Streplococcus (group A), Streptococcus agalactiae (group B), Streptococcus bovis, Streptococcus pneunoniae, Streptonyces, Sa/none/la, Serratia, Sbige//a, Spiri/lum, Treponenia, Veillonella, Vibrio, Yersinia, Xanthomonas, and combinations thereof. The slippery surface according to one or more embodiments prevents adhesion, growth or bio-fouling by the bacteria. [00361 In one or more embodiments, the immiscible material is a solution or suspension containing fungi. The fungus may be selected from the group consisting of a member of the genus Aspergi//us, B/astomyces dermatitidis, Candida, Coccidioides immitis, Crpi ococcus, Hisftoplasna capsulatuin var. capsulatuin, Histoplasina capsulatun var. duboisii, Paracoccidioides brasiliensis, Sporothrix schenckii, Absidia corymnbifera; Rhizomucor pusi//us, Rhizopus arrhizous, and combinations thereof. The slippery surface according to one or more embodiments prevents adhesion, growth or bio-fouling by the fungus. - 6 - WO 2013/106588 PCT/US2013/021056 [00371 In one or more embodiments, the material is a solution or suspension containing virus. The virus may be selected from the group consisting of cytomegalovirus (CMV), dengue, Epstein-Barr, Hantavirus, human T-cell lytmphotropic virus (HTLV I/II), Parvovirus, hepatitides, human papillomavirus (HPV), human immunodeficiency virus (HIV), acquired immunodeficiency syndrome (AIDS), respiratory syncytial virus (RSV), Varicella zoster, West Nile, herpes, polio, smallpox, yellow fever, rhinovirus, coronavirus, Orthonyxoviridae (influenza viruses), and combinations thereof. The slippery surface according to one or more embodiments prevents adhesion or growth by the virus. [00381 In one or more embodiments, the material is a solution or suspension containing particles selected from the group consisting of normal cells, diseased cells, parasitized cells, cancer cells, foreign cells, stein cells, and infected cells, microorganisms, viruses, virus-like particles, bacteria, bacteriophages, proteins, cellular components, cell organielles, cell fragments, cell membranes, cell membrane fragments, viruses, virus-like particles, bacteriophage, cytosolic proteins, secreted proteins, signaling molecules, embedded proteins, nucleic acid/protein complexes, nucleic acid precipitants, chromosomes, nuclei, mitochondria, chloroplasts, flagella, biomninerals, protein complexes, and minicells. 100391 In yet another aspect, an article having a slippery surface includes a sterile substrate comprising an anchoring layer, the anchoring layer comprising a head group attached to the substrate and a functional group directly or indirectly attached to the head group and a lubricating layer comprising a lubricating liquid having an affinity for the functional group and disposed over the anchoring layer, wherein the anchoring layer and the lubricating layer are held together by non-covalent attractive forces, wherein the anchoring layer and the lubricating layer form a slippery surface configured and arranged for contact with a material that is immiscible with the lubricating liquid. [00401 In one or more embodiments, the substrate is silanized before sterilization. BRIEF DESCRIPTION OF THE DRAWINGS [00411 The following figures are provided for the purpose of illustration only and are not intended to be limiting. [00421 FIG. 1 is a schematic of a slippery liquid innobilized coating surface in accordance with the present disclosure, in which an anchoring layer of inmmobilized molecules that exhibit chemical properties necessary to interact with and retain a lubricating layer of a lubricating liquid molecules that are immiscible with a repellent material.
WO 2013/106588 PCT/US2013/021056 [00431 FIG. 2 is a schematic illustration of an ultra-slippery surface with a reservoir, which replenishes the surface with lubricating liquid, housed below the repellant surface, according to one or more embodiments. [00441 FIG. 3 is a schematic of the generic cross-linking chemistry used to adjust the affinity of the surface to the liquid(s) to which it will be exposed, in which RI represents the reactive moieties of the surface of the substrate, and R2 represents the reactive moieties on the bifunctional molecules used to modify the surface. [00451 FIG. 4 is a series of images of PDMS tubing through which a plug of PFC oil is pumped through silanized and unsilanized tubing (FIG. 4A), followed by ice-chilled untreated human blood demonstrating that the combination of silanized PDMS tubing with an overlaid coating of PFC oil successfully prevented adhesion of untreated human blood on ice for 3 minutes (FIG. 4B) and 45 minutes (FIG. 4C). Clear droplets in figures are PFC oil. [00461 FIG. 5 is a series of images showing fresh human blood without anti-coagulants repelled by an ultra-slippery surface composed of a silanized PDMS surface coated with a thin liquid layer of PFC oil (tridecafluorotetrahydrooctyltrichlorosil ane) (FIG. 5B(i)), but adhering to an untreated and umnodified PDMS surface (FIG. 5A(i)), non-silanized PDMS with PFC oil (FIG. 5A(ii)), and silanized PDMS without a liquid oil layer (FIG. 5B(i)). [00471 FIG. 6 shows a series of images in which a drop of blood has been applied to PDMS sheets having various surface treatments before (FIG. 6A) and after (FIG. 6B) tilting, demonstrating that blood adhered to untreated and unmodified PDMS (FIG. 6B(i)), PDMS with PFC oil (trichloro(1H,IH,2H, 2H-perfluorooctyl)sil ane) (FIG. 6B(ii)), and silanized PDMS (FIG. 6B(iii)), but was completely repelled by silanized PDMS coated with a thin PFC oil layer (FIG. 6B(iv)). 100481 FIG. 7 shows a series of images in which a drop of blood has been applied to acrylic sheets having various surface treatments before (FIG. 7A) and after (FIG. 7B) tilting, demonstrating that blood adhered to untreated and unmodified acrylic (FIG. 7B(i)), acrylic with PFC oil (FIG. 7B(iif)), and silanized acrylic (FIG. 7B(iii)), but was completely repelled by silanized acrylic coated with a thin PFC oil layer (FIG. 7B(v)). [00491 FIG. 8 shows a series of images in which a drop of blood has been applied to tissue cuhure polystyrene sheets having various surface treatments before (FIG. 8A) and after (FIG. 8B) tilting, demonstrating that blood adhered to untreated and unmodified tissue-culture polystyrene (FIG. 8B(i)), tissue-culture polystyrene with PFC oil (FIG. 8B(ii)), and silanized - 8 - WO 2013/106588 PCT/US2013/021056 tissue-culture polystyrene (FIG. 8B(iii).), but was completely repelled by silanized [issue culture polystyrene with a PFC oil coating (FIG. 8B(iv)). 100501 FIG. 9 shows a series of images in which a drop of blood has been applied to polystyrene sheets having various surface treatments before (FIG. 9A) and after (FIG. 9B) tilting, demonstrating that blood adhered to untreated and unrmodified polystyrene (FIG. 9B(i)), polystyrene with PFC oil (FIG. 9B(iiH)), and silanized polystyrene (FIG. 9B(iii)), but was completely repelled by silanized polystyrene with a PFC oil coating (FIG. 9B(iv)). [00511 FIG. 10 shows a series of images in which a drop of blood has been applied to titanium sheets having various surface treatments before (FIG. 10A) and after (FIG. 10B) tilting, demonstrating that blood adhered to untreated and unmodified titanium (FIG. 108(i)), titanium with PFC oil (FIG. 10B(ii)), and silanized titanium (FIG. 10B(iii)), but was completely repelled by silanized titanium with a PFC oil coating (FIG. 10B(iv)). [00521 FIG. 11 shows a series of images in which a drop of blood has been applied to soda lime glass having various surface treatments before (FIG. 11 A) and after (FIG. 118) tilting, demonstrating that blood adhered to untreated and unmodified soda lime glass (FIG. 111(i)), soda line glass with PFC oil (FIG. 11B(i)), and silanized soda lime glass (FIG. 11B(iii)), but was completely repelled by silanized soda lime glass with a PFC oil coating (FIG. I1B(iv)). [00531 FIG. 12 shows a series of images in which a drop of blood has been applied to polypropylene sheets having various surface treatments before (FIG. 12A) and after (FIG. 12B) tilting, demonstrating that blood adhered to untreated and unmodified polypropylene (FIG. 12B(i)), polypropylene with PFC oil (FIG. 12B(ii)), and silanized polypropylene with acrylic adhesive (FIG. 12B(iii)), but was completely repelled by silanized polypropylene with PFC oil coating (FIG. 12B(iv)). 100541 FIG. 13 shows a series of images in which a drop of blood has been applied to polypropylene with acrylic adhesive sheets having various surface treatments before (FIG. 13A) and after (FIG. 13B) tilting, demonstrating that blood adhered to untreated and unmodified polypropylene with acrylic adhesive (FIG. 13B(i)), polypropylene with acrylic adhesive with PFC oil (FIG. 13B(i), and silanized polypropylene with acrylic adhesive (FIG. 13B(iii)), but was completely repelled by silanized polypropylene with acrylic adhesive with a PFC oil coating (FIG. 13B(iv)). [00551 FIG. 14 shows a series of itnages in which a drop of blood has been applied to silicon wafers having various surface treatments before (FIG. 14A) and after (FIG. 14B) tilting, demonstrating that blood adhered to untreated and unmodified silicon wafer (FIG.
WO 2013/106588 PCT/US2013/021056 14B(i)), silicon wafer with PFC oil (FIG. 14B(ii)), and silanized silicon wafer (FIG. 14B(iii)), but was completely repelled by silanized silicon wafer with a PFC oil coating (FIG. 14B(iv)). 100561 FIG. 15 shows a series of images in which a drop of blood has been applied to polycarbonate sheets having various surface treatments before (FIG. 15A) and after (FIG. 15B) tilting, demonstrating that blood adhered to untreated and unmodified polycarbonate (FIG. 15B(i)), polycarbonate with PFC oil (FIG. 15B(ii)), and silanized polycarbonate (FIG. 15B(iii)), but was completely repelled by silanized polycarbonate with a PFC oil coating (FIG. [00571 FIG. 16 shows a series of images in which a drop of blood has been applied to polysulfone sheets having various surface treatments before (FIG. 16A) and after (FIG. 16B) tilting, demonstrating that blood adhered to untreated and unmodified polysulfone (FIG. 16B(i)), polysulfone with PFC oil (FIG. 16B(i)), and silanized polysulfone (FIG. 16B(iii)), but was completely repelled by silanized polysulfone with a PFC oil coating (FIG. 16B(iv)). [00581 FIG. 17 shows a series of images in which drops of blood have been applied to smooth PDMS sheets, where the PDMS was cured on a stainless steel surface having an average roughness of 0.1 micrometers, having various surface treatments before (FIG. 17A) and after (FIG. 17B) tilting, demonstrating that blood adhered to untreated and unmodified PDMS (FIG. 17B(i)), PDMS with PFC oil (FIG. 17B(i)), and silanized PDMS (FIG. 17B(iii)), but was completely repelled by silanized PDMS with a PFC oil coating (FIG. 17B(iv)). [00591 FIG. 18 shows a series of images in which drops of blood have been applied to rough PDMS sheets, where the PDMS was cured on a stainless steel surface having an average roughness of 1.0 micrometers, having various surface treatments before (FIG. 18A) and after (FIG. 18B) tilting, demonstrating that blood adhered to rough, untreated and unmodified PDMS (FIG. 18B(i)), rough PDMS with PFC oil (FIG. 18B(ii)), and rough, silanized PDMS (FIG. 18B(iii)), but was completely repelled by rough, silanized PDMS with a PFC oil coating (FIG. 18B(iv)). [00601 FIG. 19 shows a series of images in which drops of blood have been applied to PDMS sheets, where the PDMS was cured on a stainless steel surface having an average roughness of 2.0 micrometers, having various surface treatments before (FIG. 19A) and after (FIG. 19B) tilting, demonstrating that blood adhered to rougher, untreated and unmodified PDMS (FIG. 19B(i)), rougher PDMS with PFC oil (FIG. 19B(ii)), and rougher, silanized - 10 - WO 2013/106588 PCT/US2013/021056 PDMS (FIG. 19B(iii)), but was completely repelled by rougher, silanized PDMS with a PFC oil coating (FIG. 19B(iv)). 100611 FIG. 20 shows two slides of plasma-treated soda lime glass, each containing a droplet of anticoagulant-free blood, in the untilted (FIG. 20A) and tilted (IG. 20B) state. [00621 FIG. 21 shows images of plasma-treated, trifluoropropyltrichlorosilane-treated soda lime glass slides, silanized with a molecule that has a fluoridated carbon tail one carbon long (1-PFC) in the untilted (FIG. 21A) and untilted (FIG. 211B) state, demonstrating that blood adhered to the plasma-treated I -PFC-treated glass side without PFC oil (FIG. 21B(i)), but much of the blood is repelled on the plasma-treated I-PFC-treated glass slide with a PFC oil coating (FIG. 21B(ii)). [00631 FIG. 22 shows images of plasma-treated, nonafluorohexyltrichlorosilane-treated soda lime glass slides, silanized with a molecule that has a fluoridated carbon tail four carbons long (4-PFC) in the untilted (FIG. 22A) and untilted (FIG. 22B) state, demonstrating that blood adhered to the plasma-treated 4-PFC-treated glass side without PFC oil (FIG. 22B(i)), but all of the blood is repelled on the plasma-treated 4-PFC-treated glass slide with a PFC oil coating (FIG. 22B(ii)) 100641 FIG. 23 shows images of plasma-treated, tridecafluorotetrahydrooctyltrichliorosilane-treated soda lime glass slides, are silanized with a molecule that has a fluoridated carbon tail six carbons long (6-PFC) in the untilted (FIG. 23A) and untilted (FIG. 23B) state, demonstrating that blood adhered to the plasma-treated 6-PFC treated glass side without PFC oil (FIG. 23B(i)), but all of the blood is repelled on the plasma treated 6-PFC-treated glass slide with a PFC oil coating (FIG. 23B(ii)). [00651 FIG. 24 shows images of plasma-treated, heptadecafluorotetrahydrodecyltrichl orosil ane-treated soda lime glass slides, silanized with a molecule that has a fluoridated carbon tail eight carbons long (8-PFC) in the untilted (FIG. 24A) and untilted (FIG. 24B) state, demonstrating that blood adhered to the plasma-treated 8 PFC-treated glass side without PFC oil (FIG. 24B(i)), but all of the blood is repelled on the plasnma-treated 8-PFC-treated glass slide with a PFC oil coating (FIG. 24B(ii)). [00661 FIG. 25 shows a series of images of plasma-treated glass slides, for which mineral oil is applied to one slide (FIG. 25A(ii) and FIG. 25B(ii)), anticoagulant-free blood is pipetted onto both slides, and the slide are untilted (FIG. 25A) and tilted (FIG. 25B). [00671 FIG. 26 shows a series of images of plasma-treated glass slides further modified with a silane with a linear octane (G8) tail. for which mineral oil is applied to one slide (FIG. - 11 - WO 2013/106588 PCT/US2013/021056 26A(ii) and FIG. 26B(ii)), anticoagulant-free blood is pipetted onto both slides, and the slides are untilted (FIG. 26A) and tilted (FIG. 26B). . 100681 FIG. 27 is a schematic illustration of slippery surface according to one or more embodiments useful in preventing two substrates from adhering to one another . [00691 FIG. 28 shows a series of images of glass slides that were not plasma treated, for which PFC oil is added to one slide (FIG. 28A(ii)) and mineral oil is applied to another slide (FIG. 28B(iii) and anticoagulant-free blood is pipetted onto each slide in the untilted (FIG. 28A) and tilted (FIG. 28B) state. [00701 FIG. 29 shows three images of 1 nm glass beads silanized in 5 % v/v in ethanol (nonafluorohexyltrichi orosil ane, Gelest, SIN6597.6), and then (i) immersed in PFC oil (Fluorinert FC-70) to create an ultra-slippery surface on the beads; (ii) exposed to human blood without anticoagulant; and (iii) rinsed with PBS solution, demonstrating little to no adhesion of blood material. [00711 FIG. 30 shows (i) washed, unmodified glass beads that have been exposed to antic agulant-free blood, which forms a solid clot around the beads; (ii) silanized, PFC oil coated beads after blood had been pipetted onto the beads were washed with PBS and showed only minor amounts of adhesion of blood material on the beads; and (iii) silanized beads with a PFC oil coating before exposure to anticoagulant-free blood for comparison. [00721 FIG. 31A is a schematic representation of an ultra-slippery surface that prevents repellent liquid, and solutes, solid particulates, or combinations thereof contained in the repellent liquid, from adhering to a substrate according to one or more embodiments. [00731 FIG. 31B is a schematic representation of an ultra-slippery surface that prevents repellent liquid from adhering to a substrate, but allows the solutes, particulates, or combinations thereof to adhere to, or be retained on a substrate or in the lubricating liquid according to one or more embodiments. [00741 FIG. 31C is a schematic representation of an ultra-slippery surface that prevents repellent liquid from adhering to a substrate, but demonstrates selective affinity of the ultra slippery surface for certain solutes andlor particulates according to one or more embodiments [00751 FIG. 32 A-B is a series of images which shows that connercially-available plastic ketchup bottles made of PETE can be modified with silane and treated with PFC oil to create an ultra-slippery surface that prevents deposition of ketchup on the bottle walls. [00761 FIGS. 33A-33E are a series of photographs showing blood residue in untreated or treated medical grade PVC tubes after exposure to anticoagulant-free blood: (FIG. 33A) - 12 - WO 2013/106588 PCT/US2013/021056 untreated tubes; (FIG. 33B) coated with FC-70, non-sterilized; (FIG. 33C) coated with FC 70, sterilized; (FIG. 33D) coated with PFD, non-sterilized; and (FIG. 33E) coated with PFD., sterilized. [00771 FIG. 34 shows contact angle measurements carried out on PMMA, polysulfone and silicon wafer substrate before and after plasma treatment, silanization, and plasma treatment and silanization. [00781 FIG. 35 shows tilt angle measurements using water, hexadecane and blood, carried out on PMMA substrate before and after plasma treatment, silanization, and plasma treatment and silanization followed by a dip-coating in a lubricating liquid. 100791 FIG. 36 shows polysulfone surfaces exposed to human blood with and without various coated surfaces as well as a steel substrate. [00801 FIG. 37 shows scanning electron microscope images of thrombus accumulation on untreated polysulfone surface and a FC-70 coated silanized polysulfone surface at wide and close up views. [00811 FIG. 38 is a plot of percent fibrinogen coated area vs. time to demonstrate thrombus accumulation on PMMA substrate before and after formation of various different coated surfaces. [00821 FIG. 39 A-B shows reduced thrombus accumulation in in vivo study carried out on PMMA substrate before and after formation of various different coated surfaces. [00831 FIG. 40 shows cross sectional images of untreated and coated PVC tubing and catheter demonstrating reduced thrombus accumulation in coated PVC tubing and catheter. [00841 FIG. 41 shows thrombus weight measurement of untreated and coated samples demonstrating reduced thrombus accumulation in coated samples. 100851 FIG. 42 shows FT-IR spectra of bare aluminum (Al), aluminum oxy hydroxide (Al B), fluoro-functionalized aluminum oxy hydroxide (Al-BF), and pure fluoroaliphatic phosphate ester fluorosurfactant (FS 100). [00861 FIG. 43 shows optical images of fibrinogen particles to glass without perfluorocarbon but do not stick to surfaces treated with perfluorocarbon. [00871 FIG. 44 shows optical images of fluorescently labeled thrombi fibrinogen particles to glass without perfluorocarbon but do not stick to surfaces treated with perfluorocarbon. - 13 - WO 2013/106588 PCT/US2013/021056 DETAILED DESCRIPTION [00881 Methods for making most solid surfaces uLira-repellant to liquids, molecules or particulates contained within liquids, and dry solids are described. Further, methods for reducing adhesion and friction between two solid surfaces are provided. The disclosed slippery liquid immobilized coating surfaces are synthetic surfaces that include an anchoring layer secured to an underlying substrate that interacts with and retains a thin layer of a lubricating liquid. The anchoring layer includes moieties having head groups that interact preferentially with the underlying surface and present functional groups to the environment that have surface properties that interact favorably with the lubricating liquid. The moieties are arranged on the underlying surface to form an immobilized molecular anchoring layer on the surface. The lubricating layer forms at least a monomolecular layer over the anchoring layer, and the anchoring layer and the lubricating layer are held together by non-covalent attractive forces. [00891 Certain embodiments of the present invention relate generally to surface coatings of a polymeric, glass, metallic, metal oxide, or composite substrate by organic ligands and mixtures of organic ligands and the uses of such chemically modified substrates for forming slippery surfaces by infusing a liquid lubricant onto a chemically functionalized substrate. [00901 Certain embodiments of the present invention provide compositions of organic ligand and methods of forming coated substrates that offer control of surface energy, affinity, and compatibility with applied liquid lubricant, and improved stability and retention of such lubricant on the functionalized substrates. 100911 The chemically functionalized substrates are useful when forming ultrasmooth, omni -repellent, self-healing, anti-coagulating, and slippery surfaces by infusing lubricant onto the chemically functionalized surfaces. The compositions allow for tailoring of the type of the lubricants to be used as well as the type of foreign materials to be repelled or achieving long term stability of retained lubricant in a variety of host media and shear conditions including liquids, gas, and solid hosts by changing the nature of the ligands. [00921 An illustrative ultra-repellant surface 200 is shown in FIG. 1 (not drawn to scale). Referring to FIG. 1, an anchoring layer 210 of immobilized molecules that exhibit chemical properties that bind and retain an ultra-thin lubricating layer 220 composed of a liquid is attached to a substrate 230. Substrate 230 can be a smooth or roughened surface. The immobilized molecular anchoring layer is covalently attached to, or adsorbed onto, the substrate 230. A lubricating liquid is applied to the surface-modified substrate. The surface modifying anchoring layer enhances the werting properties of the lubricating liquid and allows it to form a thin lubricating layer. The immobilized molecular anchoring layer allows the - 14 - WO 2013/106588 PCT/US2013/021056 lubricating liquid to be added to smooth or roughened substrate 230 and still repel immiscible materials. Repellent material 240 is the material to be repelled, and can be a liquid, particulate contained within a liquid, a complex fluid, a dry solid, or a solid surface. The selection of the lubricating liquid (and thus the composition of the underlying anchoring layer) is made to provide a lubricating layer in which the repellent material is immiscible. [00931 In some embodiments, the anchoring layer is adsorbed onto the underlying surface. In some embodiments, the anchoring layer is formed on the underlying substrate by adhesion. [00941 In other embodiments, the anchoring layer can be covalently bound to the underlying surface, as is illustrated in FIG. 2. A substrate contains an immobilized molecular anchoring layer that attaches to the surface. Referring to FIG. 2, the immobilized molecular anchoring layer 110 includes a head region 120 that provides a chemical linkage to the substrate 100. The immobilized molecular anchoring layer 110 also includes a tail region 130. The tail region of the immobilized molecular anchoring layer alters the surface properties of the substrate to provide a desired property. For example, depending on the nature of the repellent material, the immobilized molecular anchoring layer can increase the lipophobicity, hydrophobicity, or omniphobicity of the surface. The tail region interacts with e.g., solubilized molecules of the lubricating liquid that is applied to the treated surface. Thus, the tail region retains the molecules of the lubricating liquid by non-covalent attachment. The tail region and molecules of the lubricating liquid are arranged on the surface such that the molecules of lubricating liquid form a lubricating layer 140 on the surface. Because of the affinity is based on the interaction of the lubricating liquid with the functional regions of the anchoring layer, the lubricating layer can be very thin and can be no more than one molecular layer. [00951 The lubricating layer 140 is formed by immobilizing the anchoring layer 110 on the surface 100 and applying a lubricating liquid to the surface containing the immobilized monomolecular surface layer 110. The lubricating liquid wets the treated surface of the substrate and forms the lubricating layer 140. The anchoring layer 110 and lubricating layer 140 are held together by non-covalent attractive forces. Together, the substrate and lubricating layers on the substrate form a slippery surface that resists adhesion by molecules and particles, and repels certain immiscible fluids. This allows the passage of materials at various flow rates, including high flow rates, without allowing the material to adhere to, attach, foul the surface, or, in the case of biological fluids such as blood, coagulate. Thus, these surfaces can be used in a wide variety of environments, such as laboratories, on medical devices, medical equipment, for medical applications including amiticoagulation and anti-biofilm formation, industrial - 15 - WO 2013/106588 PCT/US2013/021056 applications, commercial applications, and other practical applications. As used herein, reference to an "environmental material" or "environmental liquid" indicates a fluid or solid or other material, for which the ultra slippery layer according to the disclosure is designed to repel or reduce adhesion. Other terms, such as "repellent material," "repellent liquid," "material to be repelled," "fluid to be repelled," "liquid to be repelled," and the like, are meant to detiote such similar materials. [00961 In one embodiment, perfluorocarbon ("PFC") oil is used as the lubricating liquid, particularly when the materials to be repelled or excluded are immiscible in oleophobic liquids. The "Teflon-like" PFC oil is retained on the surface by a "Teflon-like" layer on the surface, e.g., a fluorous surface, which serves as the anchoring layer. The treated fluorous surface has an affinity for other fluorocarbons, and thus when PFC oil is applied to the treated surface, the surface is wetted by and retains a thin layer of PFC oil that resists adhesion of liquids and repels materials. Substrate [00971 Many types of substrates can be used in accordance with this disclosure. Generally, solids having chemically reactive surfaces (or surfaces that can be activated to provide chemically reactive surfaces) can be used to interact with and immobilize the anchoring layer and the lubricating layer applied to the surface. In one embodiment, the surface is smooth. In other embodiments, the surface is not limited to any degree of surface roughness. [00981 The liquid repellant surfaces disclosed herein have properties that are independent of the geometry of the underlying substrate. Thus, the geometry of the substrate can be any shape, form, or configuration to suit the configuration of a variety of materials. Non-limiting examples of shapes, forms, and configurations that liquid repellant surfaces can take include generally spherical (e.g., beads) (see FIGS. 29 and 30), tubular (e.g., for a cannula, connector, catheter, needle, capillary tube, or syringe) (see FIG. 4A-4C), planar (e.g., for application to a microscope slide, plate, wafer, film, or laboratory work surface) (see FIGS. 5-26 and FIG. 28), or arbitrarily shaped (e.g., well, well plate, Petri dish, tile, jar, flask, beaker, vial, test tube, column, container, cuvette, bottle, drum, vat, or taik) (see FIG. 32). The substrate can be a solid that is flexible or rigid. [00991 In some embodiments, the substrate is flexible, such as for example, a flexible tube or tubing used in medical applications. FIGS. 4A-4C show a flexible PDMS tubing that has - 16 - WO 2013/106588 PCT/US2013/021056 been treated according to one or more embodiments of the invention and made liquid ultra repellant. 101001 The substrate can be any material that is capable of surface modification to form the immobilized molecular anchoring layer. Many suitable materials are commercially available, or can be made by a variety of manufacturing techniques known in the art. Non-limiting examples of surfaces that can be used to prepare the ultra-slippery surfaces described herein include, e.g., glass, polymers (e.g., polysulfone, polystyrene, polydimethylsiloxane ("PDMS"), polycarbonate, polymethylmethacrylate, polyethylene, polypropylene, polyethylene terephthalate, polyvinyl chloride, styrene-ethylene/butylene-styrene, styrene ethylene/propylene-styrene, polyurethane, silicone, etc.), metals (e.g., stainless steel, nitinol, titanium, gold, platinum, silver, aluminum, cobalt-chrome, etc.), paper, plastics, various forms of carbon (e.g, diamond, graphite, black carbon, etc.), metal oxides and other ceramic materials, composite materials, combinations of the above, and the like. [0i011 In certain environments, the substrate is selected to be compatible with the intended use of the device. For example, in medical devices, it is preferred that the solid material comply with FDA standards for safety and biocompatibility. 101021 Suitable substrates contain reactive surface moieties in their native forms, or can be treated to provide suitable reactive moieties for linking with the anchoring compound. Exemplary reactive surface moieties include oxygen-containing surface groups such as oxides, hydroxides, carboxyl, carbonyl, phenol, epoxy, quinone and lactone groups and the like; nitrogen-containing surface groups such as amino, C=N groups, azides, aides, nitrile groups, pyrrole-like structure and the like, sulfur-containing moieties such as thiols, and the like, and reactive carbon containing surface groups such as alkynes and alkenes. 101031 Surfaces can be treated to activate the surface and render it amenable to surface modification using well-understood techniques. Exemplary surface treatments include acid or base treatment, oxidization, arimonization, plasma, microwave treatment, and various etching techniques. Anchoring Layer [01041 According to one or more embodiments, the substrate is modified by providing an anchoring layer that has an affinity for and an ability to retain a lubricating liquid, on the substrate. Materials known to have strong oniniphobic properties do not adhere to or spread out well on most hydrophilic or hydrophobic substrates. Similarly, materials known to have - 17 - WO 2013/106588 PCT/US2013/021056 strong hydrophobic properties do not adhere to or spread out well on most hydrophilic or omniphobic substrates, and materials known to have strong hydrophilic properties do not adhere to or spread out well on most hydrophobic or oniphobic substrates. 'The selection of the appropriate immobilized molecular anchoring layer can improve the wetting properties of such liquids and thereby provide a surface with excellent liquid repelling properties. [01051 Generally, the anchoring layer comprises a head group that covalently attaches to, or is adsorbed onto the substrate, and a functional group that non-covalently interacts with the lubricating layer to retain the lubricating layer on the surface. This anchoring layer forms at least a monotnolecular layer on the substrate. In some embodiments, this layer forms more than a monomolecular layer on the substrate. [01061 In some embodiments, the anchoring layer is formed on the underlying substrate by adhesion. Adhesion is the tendency of dissimilar particles and/or surfaces to cling to one another. Non-litniting adhesive forces that may be employed to form the anchoring layer include one or more of mechanical, van der Waals or electrostatic forces. [01071 In some embodiments, the anchoring layer forms a covalent bond with the underlying substrate. The anchoring layer can be prepared by reaction of a reactive head group ("R2" in FIG. 3) of a biftmtional molecule bearing the fumetional tail, with a reactive species ("Ri" in FIG. 3) on the surface of the substrate 310. The reaction of R2 and R-1 forms a covalent linkage 320 that secures the functional group on the surface of the substrate. For example, reactive oxygen moieties on the surface ("R1") react with the trichlorosilane moieties ("R2") of a perfluorinated or polyfluorinated organosilane, to form a siloxy (Si-O) linkage and rendering a niodified surface of exposed perfluorinated or polyfluorinated tails. [01081 By way of example, the reactive head group (R2) is a group that reacts with oxygen containing surface groups (RI) such as oxides, hydroxides, carboxyl, carbonyl, phenol, epoxy, quinone and lactone groups and the like; nitrogen-containing surface groups (RI) such as amino, C=N groups, aniides, azides, nitrile groups, pyrrole-like structure and the like, sulfur containing moieties such as thiols, and the like that are on the surface of the substrate, and reactive carbon containing surface groups such as alkynes and alkenes. [01091 Some examples of groups that form upon reaction of R1 with R2 include ethers, silyl ethers, siloxanes, esters of carboxylic acids, esters of sulfonic acids, esters of sulfinic acids, esters of sulfuric acids, esters of phosphonic acids, esters of phosphinic acids, esters of phosphoric acids, silyl esters of carboxylic acids, silyl esters of sulfonic acids, silyl esters of sulfinic acids, silyl esters of sulfuric acids, silyl esters of phosphoric acids, silyl esters of - 18 - WO 2013/106588 PCT/US2013/021056 phosphinic acids, silyl esters of phosphoric acids, oxides, sulfides, carbocycles, heterocycles with at least one oxygen atom, heterocycles with at least one nitrogen atom, heterocycles with at least one sulfur atom, heterocycles with at least one silicon atom, 'click' reactions-derived heterocycles, Diels-Alder reactions-derived carbocycles, Diels-Alder reactions-derived heterocycles, aides, imides, sulfides, thiolates, metal thiolates, urethanes, oximes, hydrazides, hydrazones, physisorbed or chemisorbed or otherwise non-covalently attached moieties, or combinations thereof. [01101 Non-limiting examples for R2 include carboxylic acids, amines, halides, silanols, thiols, carbonyls., alcohols, phosphonic acids, sulfonic acids, inorganic oxides (e.g., silica, titania, alumina, zirconia, etc.), reactive metals (eg gold, platinum, silver), azides, alkenes and alkynes. [01111 For example, the surfaces with hydroxyl groups (i.e., -OH) can be functionalized with various commercially available substances such as polyfluoroalkylsilanes (e.g., tridecafluoro-1,1,2,2-tetrahvdrooctyl-trichlorosilane, heptadecafluoro-1,1,2,2-tetra-hydrodecyi trichlorosilane, etc.), alkylsilanes, aminosilanes (e.g., (3-aminopropyl)-triethoxysilane, 3-(2 aminoethyl)-amiinopropyltrimethoxysiiane), glycidoxysilanes (e.g., (3-glycidoxypropyl) dimethyl-ethoxysilane), and (mercaptoalkyl)silanes (e.g., (3-mercaptopropyl) trimethoxysilane). In certain embodiments, a variety of materials that have or can easily form oxides on the surface, such as silicon, glass, alumina, and organic polymers, can be activated to contain -OH functional groups using techniques such a plasma treatment. After activation, either vapor or solution deposition techniques can be used to attach various organosilyl moieties to the substrates. Organosilyl moieties can be chosen from perfluorinated, partially fluorinated or non fluorinated ones. 101121 In certain embodiments, non-limiting examples for R2 include thiol groups that reacts with metal substrates, such as gold, copper, silver, platinum, palladium, rhodium, ruthenium, their alloys and intermetallic compounds. [01131 In another embodiment, non-limiting list of exemplary reactive group (R2) includes substituted or unsubstituted carboxylic acids, substituted or unsubstituted sulfonic acids, substituted sulfinic acids, substituted sulfuric acids, substituted phosphonic acids, substituted phosphinic acids, substituted phosphoric acids, and their respective esters, or combinations thereof. [0114] In one or more embodiments, the anchoring layer includes a perfluorocarbon tail having a tail length of at least one carbon. In specific embodiments, the perfluorocarbon tail - 19 - WO 2013/106588 PCT/US2013/021056 can have a carbon length of 1-50, or 2-20 or 4-16 or 6-12. In one or more embodiments, the anchoring group head group is a siloxy group (Si-O) formed in the reaction of a reactive silane group, e.g., thrichlorosilane, with oxygen moieties on the substrate surface. A number of commercially available perfluorocarbon trichlorosilanes are available. As used herein, reference to a "silanized' surface indicates an anchoring layer in which the head group includes and Si-O linkage. [01151 In other embodiments, crosslinking agents can be used to link the reactive surface with the anchoring layer molecules. For example, as shown below, bifunctional linkers such as epichlorohydrin, glutaraldehyde, adipic dihydrazide can attach hydroxyl-, amino- and carboxylic acid terminated compounds to their respectively activated surfaces. -N~ I2 n1, R NH2 gluteraldehyde an 0 -COOI H COOH-Rf -COOH + H 2 N N N NH2 PR adipic dihydrazide 101161 Table 1 shows additional examples of linking chemicals. A non-limiting list of exemplary linking reagents with the same or different reactive groups at either end are shown. The reagents are classified by which chemical groups link (left column) and their chemical composition (right column). Table1I Crossiinking Target Linker Reactive Groups, Features Amine-to-Amine NHS esters Imidoesters Sulfhydryl-to-Sulfhydryl Maleirides Nonselective Ary!l azides Amine-to-Sulfhydryl NHS ester / Maieimide NHS ester / PVridyidithioi NHS esters / Haloacetyl Amine-to-Nonselective NHS ester / Aryl Azide NHS ester I Diazirne Amine-to-Carboxl Carbodjimide Sulfhydryl-to-Carbohydrate Maleimide/ Hydrazide d--id-ithici / Hdrazide Amine-to-DNA NHS ester / Psoralen - 20 - WO 2013/106588 PCT/US2013/021056 [01171 The functional group (tail) used in the anchoring layer can be selected to have an affinity, such as non--covalent interaction, with molecules of the lubricating layer and retain the lubricating layer on the surface. As used herein, high affinity refers to the spreading coefficient of the lubricant over that of the functional group is positive, such as having attractive forces and generally miscible with one another, such that the lubricating liquid has a greater adsorption equilibrium constant with the functional group of the anchoring layer than the material to be repelled does to the functional group of the anchoring layer. Particularly, a no slip condition can develop between the lubricating liquid and the anchoring layer so that there is an outermost molecules of the lubricating liquid that is stuck to the anchoring layer although other parts of the lubricating liquid may be forced away from the substrate (e.g., shear deformation, high impact pressure, etc.) For example, functional groups comprising hydrocarbons such as alkanes, alkenes, alkynes, and aromatic compounds, and combinations thereof can be used to create a hydrophobic surface that has an affinity for lubricating liquids that are also hydrophobic or lypophilie. The combined surface layer and lubricating liquid is useful for repelling hydrophilic or omniphobic fluids. In another embodiment, hydrophilic functional groups can be used to create a hydrophilic surface that has an affinity for hydrophilic liquids. Exemplary hydrophilic groups include charged polypeptides, polyanions (e.g., heparin sulfate, oligonucleotides, dextran sulfate), polycations (e.g. chitosan, chitin, hexadimethrine bromide, diethylatninoethyl cellulose) polar polymers (polyacrylamide, polyethylene glycol, polypropylene glycol), polysaccharides (dextran, agarose, inulin, sepharose), amines (e.g. aminopropyl, diethylaminoethanol), carboxylic acids, guanidine, alcohols, sulfhydryls, carboxamides, and metal oxides. The combined surface layer and lubricating liquid is useful for repelling hydrophobic or oiniphobic fluids. In still another embodiment, functional groups comprise perfluorinated groups (e.g., perfluoropoly (or oligo) ethers, etc.) that have affinity to lubricants to create an omniphobic surface for repelling hydrophilic or hydrophobic fluids. [0118] The substrate can be coated with the anchoring layer by methods well known in the art, including plasma-assisted chemical vapor deposition, chemical functionalization, chemical solution deposition, chemical vapor deposition, chemical cross linking, and atomic layer deposition. For example, chemical vapor deposition can be carried out by exposing the substrate to reactive silane vapors. For chetnical solution deposition, the deposition can be carried out by., e.g., innersing the substrate in a silane solution followed by rinsing and drying. Similarly, other reactive head groups can be brought in contact and made to react with the surface by using gas- and solution-phase tnethods well-established in the art. -21 - WO 2013/106588 PCT/US2013/021056 [01191 The anchoring layer can be applied in a thickness sufficient to cover the surface of the substrate. The actual thickness of the applied layer may be a function of the method of application. The anchoring layer applied in a typical thickness is assumed to be a monomolecular layer, however, the layer may not completely cover the entire surface but still be sufficient to modify the surface properties of the substrate. Similarly, the layer may be more than one monomolecular layer. [01201 Certain embodiments may involve reacting perfluoroalkylamines, with carbon chain lengths ranging from ethyl to dodecyl, such as iH,1-H-perfluorooctylamine, to different surfaces like polyesters, polyurethanes, or polyvinylchloride through aminolysis of the esters and carbamates in the backbone or nucleophilic substitution. [01211 In certain embodiments, the underlying substrate functionalized with the desired anchoring layer via a two-step process, such as by reacting the substrate surface to provide a desired reactive moiety, which can then be further reacted with the desired anchoring layer. For example, an underlying substrate (e.g., silica) can be reacted to provide an isocyanate group, which can then be utilized to carry out a carbamation reaction between hydroxyl or amino terminated fluoro compound (HO-Rf and NH 2 -Rf) and isocyanatopropyl triethoxysilane (ICPTES) to form fluorosilane linker through urethane and urea formation respectively. OEt 0 Rf N c OEt N HO-Rf NHr-RF S0Et H H oEt gg.N. N Et isocyanatopropyltriethoxysilane OI Et Rf: Eluoro group such as: I (2CF2)CIi, in whih n = 1-8, or PEE derivatives 10 122] As another example, as shown below, hydroxylated surfaces can be functionalized with triethoxysilyl butyraldehyde (AiBTES) and further reacted with amino terminated fluoro compounds. - 22 - WO 2013/106588 PCT/US2013/021056 [01231 In certain embodiments, perfluoroalkylamines can react with surfaces bearing acrylates, maleimides, carboxylic acids, anhydrides, aldehydes, and epoxides through Michael addition, amidation, nucleophilic addition, and ring-opening mechanisms. 101241 Other nucleophilic perfluorinated molecules include perfluoroalkylthiols such as perfluorodecanethiol that may react with electrophiles such as maleimides as well as disulfide containing substrates. [01251 In certain embodiments, perfluoroalkyl alcohols like lH,1H,2H,2H-perfluoro- 1 octanol could be anchored to carboxylic acid-containing substrates through esterification. [01261 In certain embodiments, substrates containing amines and relevant nucleophiles can react with perfluoroalkylacrylates, ranging in carbon chain length from ethyl to dodecyl, such as 1, 1,1,3,3-hexafluoroisopropyl acrylate, or perfluoroalkylepoxi des, such as perfluorohexyl propyl epoxide or perfluorooctyl propyl epoxide. [01271 In certain embodiments, perfluoroalkyliodides, with chain lengths ranging from ethyl to dodecyl, such as 2-(perfluorooctyl)ethyl iodide, may be reacted with olefin-bearing surfaces to yield iodide adducts in the presence of an amine and metal salt. [01281 Hydrocarbon analogs of the aforementioned reactions may readily be obtained as well using fatty acids, lipids, alkylamines, alkanethiols, alkyl alcohols, alkyl halides, alkyl acrylates, and alkyl epoxides with varying carbon chain lengths, ranging from C2 to C22. [01291 In certain embodiments, phosphonic acids can be utilized as part of the anchoring layer. As used herein, the term "phosphonic acid" refers to an organic compound having the structure: O HO-P--R OH wherein R is an organic (carbon-containing) radical or residue wherein the phosphorus atom is bonded to a carbon atom of the R- group. Those of ordinary skill in the art are aware that the hydrogens attached to the OH groups of phosphonic acids are acidic and can be removed by bases or at appropriate pH's to form salts of the phosphonic acids having phosphonate mono or - 23 - WO 2013/106588 PCT/US2013/021056 di-anions having the structure: HO--P--R -0-P - R I- | phosphonate anion phosphonate dianion [01301 It is understood that, when present as an anion, the phosphate can include one or more associated counter ions, for example, monovalent cations including lithium, sodium, or potassium or one or more divalent cations including calcium or zinc. The organic "R" radical or residue comprises at least one carbon atom, and includes but is not limited to the many well known carbon-containing groups, residues, or radicals well known to those of ordinary skill in the art. The R radicals can contain various heteroatoms, or be bonded to another molecule through a heteroatom, including oxygen, nitrogen, sulfur, phosphorus, or the like. Examples of suitable R radicals include but are not limited to alkyls such as methyl, butyl, or octadecyl radicals and the like, or substituted alkyls such as hydroxymethyls, haloalkyls, perfluoroalkyls, aromatics such as phenyls or substituted aromatics, such as phenols or anilines; or polymeric residues such as PEG, PPG, silicone, polyethylene, fluoropoly-mers such as perfluoropolyethers, Teflons or Vitons, polycarbonates, etc, and the like. In many non polymeric embodiments, the R radicals of the phosphonates comprise 1 to 18 carbon atoms, I to 15, carbon atoms, I to 12 carbon atoms, I to 8 carbon atoms, or I to 4 carbon atoms. [01311 In certain embodiments, phosphonic acid ligands can be attached to metal oxide substrate surfaces. [01321 In another aspect, the phosphonic acid ligands can form a coating on the surface of metal oxide substrates. [01331 In a further aspect, at least one phosphonic acid ligand comprises a residue of a compound having the structure R,,-X,, wherein R is a ligand group and X is a phosphonic acid group having the structure: 0 * P--OH OH ;and wherein each n is, independently, 1 2, or 3. [01341 In a yet further aspect, each n is 1. In a still further aspect, the compound comprises - 24 - WO 2013/106588 PCT/US2013/021056 the structure R-X. [01351 In one aspect, a chemically functionalized substrate of the invention can comprise at least one phosphonic acid ligand. [01361 In a further aspect, a chemically functionalized substrate of the invention can comprise a plurality of phosphonic acid ligands. [01371 In yet another aspect, a chemically functionalized substrate of the invention can be covered with phosphonic acid ligands. [01381 In yet a further aspect, a chemically functionalized substrate of the invention can be covered with a mixture of more than one type of phosphonic acid ligands. 101391 The term "phosphonic acid ligand" as used herein refers to a radical or residue attached to or capable of attaching to the surface of the metal oxide substrates that is derived from a phosphonic acid. Those of ordinary skill in the art will understand that phosphoric acids or their anionic salts can be readily attached to a surface of a metal oxide, by replacement of one or more of the oxygen atoms of the phosphoric acid with bonds ranging from covalent, to polar covalent, to ionic, and including through hydrogen bonding, between the phosphorus atom and an oxygen atom or ion on a metal oxide surface. 101401 In certain aspects, at least one organic phosphonic acid comprises methylphosphonic acid, octylphosphonic acid, decylphosphonic acid, octadecylphosphonic acid, phenylphosphonic acid, benzylphosphonic acid, pentafluorobenzyiphosphonic acid, I 1 hydroxyundecylphosphonic acid, (11--phosphonoundecyi)phosphonic acid, (3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluorooctyl)phosphonic acid, pentabromobenzylphosphonic acid, (I I-acryloyloxyundecyl)phosphonic acid, or a mixture thereof. [01411 In one aspect, the phosphonic acid ligands are attached to the surface by bonding of one, two, or three of the oxygen atoms of the phosphonic acid ligands to the metal oxide surface. For example, the organic phosphoric acid ligands can be attached to the surface by bonds ranging from covalent, to polar covalent, to ionic, and including through hydrogen bonding, as illustrated by one or more of the structures illustrated below: OH ------ P =P R OH -25 - WO 2013/106588 PCT/US2013/021056 OH 5 0 ------- 0 ------ P ------ R or 0 - O P P or ------- 0 --- P ----- R 00 [01421 In one aspect, R can be an organic radical comprising I to 18 carbon atoms, for example, an organic radical comprising I to 16 carbons, I to 14 carbons, I to 12 carbons, I to 10 carbons, I to 8 carbons, I to 6 carbons, or I to 4 carbons. [01431 In a further aspect, R is an alkyl substituted polyether having the structure: OR' wherein n is I to 25 (including 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, and 25), and R' is a Ci-C4 alkyl (including 1, 2, 3, or 4 carbons). In a yet further aspect, R is selected from methyl, ethyl propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, and dodecyl. [01441 In another aspect, R comprises a substituted or unsubstituted, linear or branched, C 3 to C 5 o aliphatic or cyclic aliphatic, fluoroalkyl, oligo(ethyleneglycol), aryl, or amino group. [01451 In another aspect, R can comprise linear or branched alkyl groups having up to 12 carbons (including 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, and 12 carbons) or having up to 8 carbons (including 1, 2, 3, 4, 5, 6, 7, and 8 carbons), and a and P3 can be, independently, integers from I to 12 (including 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, and 12) or integers front I to 8 (including 1, 2, 3, 4, 5, 6, 7, and 8). [01461 In a further aspect, R is a fluorinated group. For example, R can comprise -(CH)p
(OCH
2 CH2,)F, -OCHCH2-(CF 2 )pCF 3 , -(CF2CF2),-(CF2)CF,, -(CF2)p-(CF2CF2)aCF
(CF
2 CF2),-(CH 2 )pCF 3 , or -(CF 2 )p-(CF 2
CF
2
),CF
3 , wherein a is an integer front 0 to 25 and wherein is an integer from 0 to 25. In various further aspects, a and P can be, independently, integers from I to 12 (including 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, and 12) or integers from I to 8 (including 1, 2, 3, 4, 5, 6, 7, and 8). Lubricating Layer [01471 The lubricating liquid used to form the lubricating layer is applied to the anchoring layer. Thus, the lubricating layer, which flows readily over the substrate, can stably, but non - 26 - WO 2013/106588 PCT/US2013/021056 covalently bind to the functional group of the anchoring layer to form a continuous, repellant layer. The lubricating layer can be selected based on its ability to repel immiscible materials. In one or more embodiments, the lubricating layer is inert with respect to the underlying substrate and environmental material to be repelled. [01481 The lubricating layer can be prepared from a variety of fluids. In one or more embodiments, the ultra-slippery surface is used in a medical setting, in which case the lubricating liquid is selected, e.g., based on its biocompatibility, level of toxicity, anti coagulation properties, and chemical stability under physiologic conditions. For example, compounds that are approved for use in biomedical applications can be used in accordance with the present disclosure. Perfluorinated organic liquids, in particular, are suitable for use in biomedical applications. In some aspects, the lubricating layer is perfluorinated oil, non limiting examples of which include PFC oils such as FC-43, FC-70, perfluorotripropylamine, perfluorotripentylamine, perfluorotributylamine, perfluorodecalin, perfluorooctane, perfluorobutane, perfluoropropane, perfluoropentane, perfluorohexane, perfluoroheptane, perfluorononane, perfluorodecane, perfluorododecane, perfluorooctyl bromide, perfluoro(2 butyl-tetrahydrofarane), perfluoroperhydrophenanthrene, perfluoroethylcyclohexane, perfluoro(butyitetrahydrofuran), perfluoropolyethers (KRYTOX), and combinations thereof. In other aspects, the lubricating layer is fluorinated hydrocarbon oil, non-limiting examples of which include oils such as 3-ethoxy-1,i,1,2,3,4,4,5,5,6,6,6-dodecafluoro-2-trifluoromethyl hexane, trifluoromethane, difluoromethane, pentafluoroethane., hydrofluoroether, etc. In other aspects, the lubricating layer is hydrocarbon oil, non-limiting examples of which include oils such as alkanes (e.g., butane, pentane, hexane, cyclohexane, heptane, octane, nonane, decane, dodecane, hexadecane, octadecane), triacylglycerides, mineral oil, alkenes, cholesterol, aromatic hydrocarbons (e.g., benzene, phenol, naphthalene, naphithol,) and combinations thereof. In other aspects, the lubricating layer is a hydrophilic liquid, non-limiting examples of which include water, aqueous solutions (e.g., acids, bases, salts, poiYmers, buffers), ethanol, methanol, glycerol, ionic liquids (e.g., ethylammonium nitrate, ethyhnethylimidazolium hexafluorophosphate, 1-butiyl-3-methylinidazoliun hexafluorophosphate; for other exanrples of ionic liquids that can be used see: "Ionic Liquids in Synthesis" P. Wasserscheid and T. Welton (Editors) , Wiley-VCH-; 2 edition (Novernber 28, 2007), the contents of which is incorporated by reference herein), and combinations thereof. [01491 In some aspects, the viscosity of the lubricating layer can be chosen for particular applications. For example, the viscosity of the lubricating oil can be < I cSt, <10 eSt, < 100 - 27 - WO 2013/106588 PCT/US2013/021056 cSt, < 1000 eSt, or <10,000 eSt. [01501 In some aspects, the lubricating layer has a low freezing temperature, such as less than -5 "C, -25 "C, or -50 "C. A lubricating layer with a low freezing temperature allows the layer to remain liquid in low temperatures to maintain the ability of the combination of the lubricating layer and functionalized surface to repel a variety of liquids or solidified fluids, such as ice and the like. [01511 In some aspects, the lubricating layer has a low evaporation rate or a low vapor pressure. For example, the vapor pressure of the lubricating liquid can be less than 10 nnHg at 25 'C, less than 5 mmHg at 25 'C, less than 2 mmHg at 25 'C, less than 1 nnHg at 25 'C, less than 0.5 mmHg at 25 'C, or less than 0.1 mmHg at 25 'C. The lubricating layer can be applied in a thickness sufficient to cover the anchoring layer. In some embodiments, the lubricating layer is applied at a thickness sufficient to form a monomolecular layer on the substrate. In other embodiments, the lubricating layer is applied at a thickness of 10 nm to 10 pim on the substrate. In other embodiments, the lubricating layer is applied at a thickness of 10 pm to 10 mm on the substrate. The lubricating layer applied in a typical thickness, assumed to be a monomolecular layer, can remain liquid repellant for a long period without requiring replenishing. By way of example, the surface can remain liquid repellant for a period longer than I hour, or longer than 6 hours, or longer than 24 hours, longer than a week, or longer than a year or more. [01521 The lubricating liquid can be sprayed, cast, or drawn onto the substrate either once or repeatedly. In certain embodiments, the lubricating layer can be applied to the surface by spinning coating, pipetting drops of lubricating liquid onto the surface, or dipping the surface into a reservoir or channel containing the lubricating liquid, through microscale holes in the wall of the underlying substrate, or by presaturating the surface with lubricating liquid to form a lubricating layer. The lubricating liquid can also be applied by absorption, wicking, thin layer deposition, or by intermittent passing of volumes of lubricating liquid over the surface (e.g., small plugs or bubbles flowing in a catheter). In some embodiments, any excess lubricating liquid can be removed by spinning the coated article or by drawing a squeegee across the surface or flushing and rising with another liquid. [01531 In some embodiments, the lifetime of the liquid repellant surface can be extended by reapplying the lubricating layer at a certain interval. For example, FIGS. 4A-4C show a pump through which plugs of lubricating liquid 405 (shown as light colored areas in tubing) are periodically sent through PDMS tubing 410, 420 that was pre-treated with silane (see also, - 28 - WO 2013/106588 PCT/US2013/021056 Example 2). In some aspects, the lubricating layer is replenished every 1, 5, 10, 15, 20, 30, 40, 50, or 60 seconds. In other aspects, the lubricating layer is replenished every 5, 10, 15, 20, 30, 40, 50, or 60 minutes. In still other aspects, the lubricating layer is replenished every 2, 4, 6, 8, 10, 12, 24, 48, 60, or 72 hours or more. Yet in other aspects, the lubricating liquid can be replenished continuously, at a constant or varying rate. In other embodiments, the surface can be replenished with lubricating liquid front a reservoir 160 housed below the substrate 100 as shown in FIG. 2. The lubricating liquid is drawn through nicropassages 150 to replenish lubricating liquid lost to the environment. Uses [01541 In one or more embodiments, any arbitrary liquid (e.g., a biological fluid), and solid particulates contained therein, may be strongly repelled from the surfaces modified in accordance with the present disclosure. Similarly, adhesion of one solid surface to another solid surface can be prevented, or the friction between two solid surfaces can be reduced using the methods disclosed herein. [01551 For example, FIG. 31A is a representation of an ultra-slippery surface 3100 including an anchoring layer 3110 and a lubricating layer 3120 on a substrate 3130 that is used to prevent an environmental liquid 3140, and solutes and solid particulates 3145 contained in liquid 3140, from adhering to underlying substrate3130. Thus, solutions and suspensions can be prevented from adhering to the surface of articles that have been coated with the ultra slippery coating according to one or more embodiments. In other embodiments, the ultra slippery surface 3100 provides a low friction interface with environmental liquid 3140 (and the entrained solutes and particles 3145). 101561 Medical disciplines ranging from cardiovascular medicine and oncology to orthopedics and ophthalmology rely increasingly on the implantation of medical devices into coronary arteries, jugular and femoral veins, joints, and many other parts of the body. Use of these devices risks the development of implant-induced thronmbogenesis, or blood clotting. Similarly, blood processing equipment such as blood dialysis instruments, in particular, dialysis catheters, must take precautions to prevent blood clotting. In particular, blood naturally coagulates when exposed to glass. In one application, surfaces that normally contact blood can be coated with the ultra slippery coating described herein to reduce thronibogenesis, e.g., blood clotting and coagulation. As demonstrated in the examples below, ultra slippery coatings using a perfluorinated anchor layer and a perfluorohydrocarbon lubricating layer is highly - 29 - WO 2013/106588 PCT/US2013/021056 effective in reducing thrombosis on surfaces that are in prolonged contact with unheparinized blood, even in flowing conditions. 101571 In another embodiment, FIG. 31B shows an ultra-slippery surface 3155 used to prevent an environmental liquid 3160 from adhering to substrate 3130 surface, while simultaneously retaining selected solutes or particles on the surface. The ultra slippery surface includes an anchoring layer 3170 and a lubricating layer3180. In addition to immiscibility with respect to the environmental liquid 3160, the lubricating layer 3180 is selected for its ability to dissolve or retain solutes or particulates 3165. In one or more embodiments, the slippery surface serves as a selective filter that allows the solutes, particulates, or mixtures thereof contained in environmental liquid 3160 to adhere to, or be retained on, substrate, e.g., by dissolving or becoming suspended in lubricating layer 3180. This selective affinity for components contained in environmental liquid 3160 can be achieved by, e.g., using a lubricating liquid in which components contained in the environmental liquid are miscible in Liquid C, or using a lubricating liquid that contains molecules that have an affinity for both the lubricating liquid and specific components contained in the environmental liquid, or molecules that are bound to the substrate having an affinity for specific components contained in the environmental liquid. [01581 FIG. 31C illustrates the selective affinity of the ultra slippery surface 3155 for certain solutes and/or particulates. Substrate 3130 includes an anchoring layer 3170 that wets and binds lubricating layer 3180 containing a lubricating liquid. The slippery surface can be located, for example, on the inner surface of a tube through which an environmental liquid 3160 flows in the direction indicated by the arrow. The environmental liquid contains a first solute (solute 1) that has a low affinity for the lubricating liquid and a second solute (solute 2) that has a high affinity for the lubricating liquid. As the environmental liquid flows over the interface with the lubricating liquid, Solute 2 is preferentially adsorbed into the stationary liquid layer containing the lubricating liquid. [01591 Selective affinity for components contained within a liquid to be repelled is useful in many situations. For example, selective affinity for components contained within a liquid can be useful for modifying chromatography columns to capture or bind desired molecules contained within a liquid passed through the column, but prevent the capture or binding of other molecules. [01601 Blood naturally coagulates when exposed to glass. Therefore, it is particularly useful that glass slides and glass beads can be modified in accordance with the present - 30 - WO 2013/106588 PCT/US2013/021056 disclosure to prevent blood clot formation and cell adhesion on surfaces while having selective affinity for certain blood components. When modified to allow selective affinity for blood components, such surfaces can be used to separate cells, pathogens, and other components from blood. Binding proteins, such as antibodies, lectins, and enzymes can be coupled to glass beads to attract desired free and bound blood components. For example, glass beads coupled to heparinase can be modified in accordance with the methods disclosed herein to attract and remove heparin while repelling blood and other components contained therein. Blood can also be passed through a chromatography column to remove biomolecules, such as autoantibodies, rheumatoid factors, and the like. Surfaces modified for selective affinity for blood components can be used in the dialysis context to remove components such as toxic metabolites before the blood is returned to the patient. Moreover, surfaces can be modified to detoxify blood of components, such as excess glucose present in the blood of diabetic patients. [01611 Thus, the disclosed liquid repellant surfaces can be used in a number of biological applications, including preventing blood clotting, cell adhesion, and fouling of most surfaces. Moreover, these surfaces do not require anticoagulants when used to prevent blood clot formation. 101621 In another embodiment, the surfaces described in accordance with the present disclosure can be used to prevent two substrates from adhering, or to reduce the friction between two substrates. FIG. 27 is a schematic illustration of an ultra-slippery surface 2700 used to prevent a first substrate 2710 and a second substrate 2720 from sticking. Each of solid substrates, 2710, 2720, possess an ultra slippery surface including anchoring layers 2730, 2735, respectively, that interacts with and retains lubricating liquids, 2740, 2745, respectively. Liquids 2740, 2745are selected to be immiscible in one another. In addition, substrate 2710 has a preferential affinity for lubricating liquid 2740,, while substrate 2720 has a preferential affinity for lubricating liquid 2745. When substrates 2710, 2720 are in facing relationship with one another, the liquid/liquid interface defined at lubricating liquids, 2740, 2745allows the friction between the substrates to be reduced. [01631 In some aspects, the surfaces are modified for liquid repellency for industrial, commercial, or practical purposes. For example, surfaces can be modified according to the present disclosure for potential applications such as low friction transport or repulsion of viscous liquids, non-viscous liquids, complex fluids, semi-solids, tacky liquids (e.g., food products, fuel products, resins, and the like), water (e.g,, dew, fog, frost, ice and the like), paints, iron filings, carbon filings, dirt, debris, insects, for coating oil pipelines and tubing to -31 - WO 2013/106588 PCT/US2013/021056 prevent biofouling, in yacht and marine finishes, and the like. FIG. 32 illustrates the application of the ultra slippery coating according to one or more embodiments to the interior surfaces of a food container (here, ketchup). The commercially available plastic bottle made of polyethylene terephthalate ("PETE") was silanized to form a fluorous surface and then treated with PFC oil. The coating prevented adhesion of the ketchup to the inner surface of the treated bottle (FIG. 32B(ii)) ad compared to an untreated bottle (FIG. 32A(i)). [01641 In one or more of the above embodiments, non-limiting examples of surfaces that can be made liquid repellant include beads, cannula, connector, catheter (e.g., central line, peripherally inserted central catheter (PICC) line, urinary, vascular, peritoneal dialysis, and central venous catheters), catheter connector (e.g., Luer-Lok and needleless connectors), clamp, skin hook, cuff, retractor, shunt, needle, capillary tube, endotracheal tube, ventilator, associated ventilator tubing, drug delivery vehicle, syringe, microscope slide, plate, filn, laboratory work surface, well, well plate, Petri dish, tile, jar, flask, beaker, vial, test tube, tubing connector, column, container, euvette, bottle, drum, vat, tank, organ, organ implant, or organ component (e.g., intrauterine device, defibrillator, corneal, breast, knee replacement, and hip replacement implants), artificial organ or a component thereof (e.g., heart valve, ventricular assist devices, total artificial hearts, cochlear implant, visual prosthetic, and components thereof), dental tool, dental implant (e.g., root form, plate form, and subperiosteal implants), biosensor (e.g., glucose and insulin monitor, blood oxygen sensor, hemnoglobin sensor, biological microelectromechanical devices (bioMEMs), sepsis diagnostic sensor, and other protein and enzyme sensors), bioelectrode, endoscope (hysteroscope, cystoscope, amnioscope, laparoscope, gastroscope, mediastinoscope, bronchoscope, esophagoscope, rhinoscope, arthroscope, proctoscope, colonoscope, nephroscope, angioscope, thoracoscope, esophagoscope, laryngoscope, and encephaloscope), extracorporeal membrane oxygenation machines, heart lung machines, surgical applications (e.g., sutures and vascular grafts), vascular applications (e.g., shunts), surgical patches (e.g., hernia patches), and combinations thereof. [01651 In one embodiment, surfaces modified according to the present disclosure can repel a fluid without causing surface adhesion, surface-mediated clot formation, coagulation or aggregation. Non-limiting examples of biological fluids include water, whole blood, plasma, serum, sweat, feces, urine, saliva, tears, vaginal fluid, prostatic fluid, gingival fluid, amniotic fluid, intraocular fluid, cerebrospinal fluid, seminal fluid, sputum, ascites fluid, pus, nasopharengal fluid, wound exudate fluid, aqueous humour, vitreous humour, bile, cerumen, - 32 - WO 2013/106588 PCT/US2013/021056 endolymph, perilymph, gastric juice, mucus, peritoneal fluid, pleural fluid, sebum, vomit, synthetic fluid (e.g., synthetic blood, hormones, nutrients), and combinations thereof 101661 In another embodiment, surfaces modified according to the present disclosure can repel various types of bacteria. In one embodiment, the type of bacteria repelled by these surfaces is gram positive bacteria. In another embodiment, the type of bacteria repelled by the disclosed modified surfaces is a gram negative bacterium. Non-limiting examples of bacteria repelled by surfaces modified in accordance with the present disclosure include members of the genus selected from the group consisting of Actinobacillus (e.g., Actinobacillus actinoniycetemcomitans), Acinetobacter (e.g., Acinetobacter bauniannii), Aeromonas, Bordetella (e.g., Bordetella pertussis, Bordetella bronchiseptica, and Bordetella parapertussis), Brevibacillus, Brucella, Bacteroides (e.g., Bactero ides jagilis), Burkholderia (e.g, Burkholderia cepacia and Burkholderia pseudomallei), Borelia (e.g., Borelia burgdoren), Bacillus (e.g., Bacillus anthracis and Bacillus subti/is), Campylobacter (e.g., Campylobacter jejuni), Capnocytophaga, Cardiobacterium (e.g., Cardiobacterium hominis), Citrobacter, Ciostridi/um eg.Clostridim tetani or Clostricium cifi/cile), Ch/amydia (e.g., Chlamvdia trachomatis, Chlamy9dia pneumoniae, and Ch/amyvdia psgfi), Eikenella (e.g., Eikenella corrodens), Enterobacter, E'scherichia (e.g., Escherichia coli), Francisella (e.g., Francisella tutarensis), Fusobacterium, Flavobacterium, Haemophilus (e-g., Haemophilus ducreyi or Haemophi/us influenzae), Helicobacter (e.g., fHelicobacter pylori), Kingella (e.g., Kingella kingae), Klebsiella (e.g., Klebsiella pneumoniae), Legione//a (e.g., Legionella pneumophila), Listeria (e.g., Listeria monocytogenes), Leptospirae, Moraxella (e.g., Moraxella catarrhais), Morganella, ycoplasma (e.g., Mycojasia hominis and Wycop.'lasmi pneumoniae), Mycobacterium (e.g., Mycobacterium tuberculosis or Mycobacterium leprae), Nei/sseria (ecg. Neissecr/a gonorrhoeae or Neisseria men ingit/dis), Pusteure//a (e a. Pasteurella nu/tocida), Proteus (e.g., Proteus vulgaris and Proteus mirablis), Prevotella, Pessiomonas (e.g., Plesiomonas shigel/oides), Pseucomonas (e.g., Pseudomonas aeruginosa), Providencia, Rickettsia (e.g., Rickettsia ricettsii and Ricketsia typhi), Stenotrophomonas (e.g., Stenotrophomonas maltoph ila), Staphylococcus (e.g., Staphylococcus aureus and Staphylococcus epiermidis), Streptococcus (e.g., Streptococcus viridans, Streptococcus pyogenes (group A), Streptococcus agalactiae (group B), Streptococcus bovis, and Streptococcus pneunoniae), Streptomyces (e.g., Streptomyces hygroscopicus), Salmonella (e a., Samone/la enter/ditis, Salmonella typhi, and Samonella typhimurium), Serratia (e.g., Serratia marcescens), Shigella, Stirilurm (e.g., Spirillum minus), Treponema (e.g., Treponema - 33 - WO 2013/106588 PCT/US2013/021056 pallidum), Veilonella, Vibrio (e.g., Vibrio cholerae, Vibrio parahaemolvticus, and Vibrio rulnificus), Yersinia (e.g., Yersinia enterocolitica., Yersinia pestis, and Yersinia pseudotuberculosis), Xanthonionas (e.g., i) and combinations thereof [01671 Surfaces modified according to the present disclosure can repel various types of fungi. Non-liniting examples of fungi repelled by modified surfaces include members of the genus Aspergillus (e.g., Aspergillus. flavus, Aspergi/lus f Aspergilus glaucus, Aspergillus nidulans, Aspergilus niger, and Aspergi//us terreus), Blastonyces dernatitidis, Candida (e.g., Candida albicans, Candida glabrata, Candida tropicalis, Candida parapsilosis, Candida krusei, and Candida guillerntondii), Coccidioides imnitis, Cryptococcus (e.g., Cryptococcus neojbrmans, Cryptococcus albidus, and Cryptococcus larenii), Histoplasma capsulatom var. capsulatum, Histoplasma capsulatun var. duboisi, Paracoccidioides bras/i/ensis, Sporothrix schenckii, Absidia corymbifera; Rhizotnucor pusillus, Rhizopus arrhizous, and combinations thereof [01681 Surfaces modified according to the present disclosure can also repel various types of viruses and virus-like particles. In one or more embodiments, the virus repelled by these surfaces is selected from the group consisting of dsDNA viruses, ssDNA viruses, dsRNA viruses, (+)ssRNA viruses, (-)ssRNA viruses, ssRNA-RT viruses, dsDNA-RT viruses, and combinations thereof Non-limiting examples of viruses repelled by surfaces modified in accordance with the present disclosure include cytomegalovirus (CMV), dengue, Epstein-Barr, Hantavirus, human T-cell lymphotropic virus (HTLV I/II), Parvovirus, hepatitides (e.g., hepatitis A, hepatitis B, and hepatitis C), human papillomavirus (HPV), human immunodeficiency virus (HIV), acquired immunodeficiency syndrome (AIDS), respiratory syncytial virus (RSV), Varicella zoster, West Nile, herpes, polio, smallpox, yellow fever, rhinovirus, coronavirus, Orthomyxoviridace (influenza viruses) (e.g, Influenzaviru s A, Influenzavirus B, Influenzavirus C, Isavirus and Thogotovirus), and combinations thereof. [01691 In still another embodiment, surfaces modified according to the present disclosure are capable of repelling particles in suspension or solution without causing surface adhesion, surface-mediated clot formation, coagulation, fouling, or aggregation. The omniphobic nature of the disclosed modified surfaces allows them to protect materials from a wide range of contaminants. Non-limiting examples of particles in suspension or solution include cells (e.g., normal cells, diseased cells, parasitized cells, cancer cells, foreign cells, sten cells, and infected cells), microorganisms (e.g., viruses, virus-like particles, bacteria, bacteriophages), proteins and cellular components (e.g., cell organelles, cell fragments, cell membranes, cell - 34 - WO 2013/106588 PCT/US2013/021056 membrane fragments, viruses, virus-like particles, bacteriophage, cytosolic proteins, secreted proteins, signaling molecules, embedded proteins, nucleic acid/protein complexes, nucleic acid precipitants, chromosomes, nuclei, mitochondria, chloroplasts, flagella, biominerals, protein complexes, and minicells). [01701 In yet another embodiment, commercially available devices (e.g., medical-grade apparatus or components) can be treated according to certain aspects of the present disclosure. For example, medical-grade PVC tubes can be treated so that their inner surfaces can possess certain repellant characteristics described in the present disclosure. In one or more embodiments, the surfaces are treated to reduce clotting in blood flowing through the medical tubing. [01711 In some situations, the surfaces can be sterilized before or after the treatment. The uhra slippery coatings as described herein have been demonstrated to be sufficiently robust that they can maintain their slip charateristics, even after sterilization. The surface treatment (e.g., silanization) can be stable or robust enough that the surface maintains its repellant characteristics after an extended period of time (e.g., a day, week, a month, or more) and/or with sterilization process. EXAMPLES [01721 The following examples are presented for the purpose of illustration only and are not intended to be limiting. Example 1 [01731 A silanized PDMS treated with PFC oil (Sigma Fluorinert@ FC-70, Product Number F9880) was found to prevent adhesion and coagulation of blood without anticoagulant. [01741 Perfluorocarbon silane (tridecafluorotetrahydrooctyltrichlorosilane, Sigma) was vapor deposited onto a PDMS sheet (Sylgard 184@, Dow Coming) and PDMS tubing (16 in length, 1.52 mm inner diameter, peroxide-cured silicone, Cole Parmer) over 10 hours under vacuum. Silanized and unsilanized PDMS sheets were coated with PFC oil by application of PFC from a pipette (perfluorotripentylamine, Sigma) (see FIGS. 5B(ii) and 5A(ii), respectively). [01751 A 75 microliter volume of human blood free of anticoagulant was pipetted onto the PDMS sheets and the sheet was tilted. As shown in FIG. 5, blood adhered to the untreated and unmnodified PDMS surface (FIG. 5A(i)), PDMS with perfluorotripentylamine (PFC oil) (FIG. - 35 - WO 2013/106588 PCT/US2013/021056 5A(ii)). and silanized PDMS (FIG. 5B(i)). However, blood did not adhere to, and was successfully repelled from, silanized PDMS with perfluorotripentylamine (PFC oil) (FIG. 5B(ii)). Silanized PDMS with PFC oil successfully repelled blood for over 90 mi-n without replenishing the PFC oil. Blood repellency was also shown with perfluorodecalin as the PFC oil on a silanized PDMS sheet (not shown). Example 2 [01761 Silanized PDMS tubing treated as describe din Example 1 was shown to successfully prevent adhesion and coagulation during peristaltic pumping of blood through the tubing. Referring to FIG. 4A, the insides of both silanized 410 and unsilanized 420 PDMS tubing were coated with 0.5 mL PFC oil. Blood was pumped through the tubing at a rate of about 100 microliters/min for 45 minutes. A plug of PFC oil was pumped through the silanized tubing. No blood was visible in the plug of PFC oil, demonstrating that the blood had not yet bound to the surface of the tubing. Then 0.5 mL of PFC oil and 0.5 mL of deionized water were pumped through both sets of tubing. [01771 Referring to FIG. 4B, after 3 min, blood had not coated the inside of the silanized tubing 410 through which blood and plugs of PFC oil were pumped, as demonstrated by the clear droplets of PFC oil that remained visible. Comparatively, significantly more binding of blood components was observed in the unsilanized tubing 420 compared to the silanized 410 tubing. [01781 After 45 min of blood flow, PFC oil followed by water was pumped through both sets of tubing. As shown by FIG. 4C, silanized PFC oil-coated PDMS tubing 410 showed significantly less binding of blood than unsilanized PFC oil-coated PDMS tubing 420 even after being flushed with water and blood. Example 3 [01791 The ability of functionalized PDMS treated with PFC oil to repel liquid was investigated and compared to the liquid repellency of untreated and unmodified PDMS, PDMS treated with PFC oil, and silanized PDMS. Four sheets of PDMS (Dow Coming Sylgard@! 184) were cured at 60 'C on mirror-polished aluminum. Two sheets of PDMS were silanized overnight by vacuum vapor deposition for approximately 12 hours using trichloro(1H,2H,2,2H-perfluorooctyl)silane (Sigma, Product Number 448931). Once silanized, 250 PL PFC oil was applied to one of the two silanized PDMS sheets and to one - 36 - WO 2013/106588 PCT/US2013/021056 unmodified PDMS sheet. Seventy-five [L of human blood without anticoagulant was applied to all four surfaces (see FIG. 6A). 101801 The surfaces were then imaged. Once inaged, the PDMS sheets were tilted by hand and immediately reimaged as shown in FIG. 61. FIG. 6 shows that blood adhered to untreated and unmodified PDMS (FIG. 6B(i)), PDMS with PFC oil (FIG. 6B(ii)), and silanized PDMS (FIG. 6B(iii)), but was completely repelled by silanized PDMS with PFC oil (FIG. 6B(iv)). Exammle 4 101811 The ability of functionalized acrylic treated with PFC oil to repel liquid was investigated by comparing this ability to that of untreated and unmodified acrylic, acrylic treated with PFC oil, and silanized acrylic. Four sheets of Clear Cast Acrylic Sheet, 0.060" Thick, (McMaster Carr, Product Number 8560K171) were further modified with an oxygen plasma treatment at 500 nTorr for 40 seconds. Two sheets of acrylic were silanized overnight with trichloro( 11-1,1H,2 H,2H-perfluorooctyl)silane under vacuum for approximately 13 hours. [01821 Two-hundred and fifty pL of FC-70 was applied to one silanized and one unsilanized sheet of acrylic to create a "PFC-oiled" surface. Seventy-five uL of human blood without anticoagulant was applied to all four surfaces (see FIG. 7A). [01831 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 7B. FIG. 7 shows that blood adhered to untreated and unmodified acrylic (FIG. 7B(i)), acrylic with PFC oil (FIG. 7B(ii)), and silanized acrylic (FIG. 7B(iii)) but was completely repelled by silanized acrylic with PFC oil (FIG. 71(iv)). - 37 - WO 2013/106588 PCT/US2013/021056 Example 5 [0184] The ability of functionalized tissue-culture polystyrene to repel liquid was investigated by comparing this ability to that of untreated and unmodified tissue-culture polystyrene, tissue-culture polystyrene treated with PFC oil, and silanized tissue-culture polystyrene. Four sheets of tissue-culture polystyrene previously treated with plasma by manufacturer (BD Biosciences, Product Number 353025) were used in this experiment. Two of the four sheets of tissue-culture polystyrene were silanized overnight with trichloro(l H,iH,2H,2H-perfluorooctyl)silane under vacuum for approximately 13 hours. [0185] Two-hundred and fifty PL of FC-70 was applied to one silanized and one unsilanized sheet of tissue-culture polystyrene to create a "PFC-oiled" surface. Seventy-five pL of human blood without anticoagulant was applied to all four surfaces (see FIG. 8A). [01861 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 8B. FIG. 8 shows that blood adhered to untreated and unmodified tissue culture polystyrene (FIG. 8B(i)), tissue-culture polystyrene with PFC oil (FIG. 8B(ii)), and silanized tissue-culture polystyrene (FIG. 8B(iIi)), but was completely repelled by silanized tissue-culture polystyrene with PFC oil (FIG. SB(iv)), Example 6 [01871 The ability of finctionalized polystyrene to repel liquid was investigated by comparing this ability to that of untreated and unmodified polystyrene, polystyrene treated with PFC oil, and silanized polystyrene. Four sheets of 1/3:2" thick polystyrene (MeMaster Carr, Product Number 8734K29) were used in this experiment. The sheets were further modified with an oxygen plasma treatment at 500 mTorr for 40 seconds. Two sheets of the four sheets of polystyrene were silanized overnight with trichloro(1H,1 H,2H,2H-perfluorooctyl)silane under vacuum for approximately 13 hours. [01881 Two-hundred and fifty p L of FC-70 was applied to one silanized and one unsilanized sheet of polystyrene to create a "PFC-oiled" surface. Seventy-five PL of human blood without anticoagulant was applied to all four surfaces (see FIG. 9A). [0189] The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 9B. FIG. 9 shows that blood adhered to untreated and unmodified polystyrene - 38 - WO 2013/106588 PCT/US2013/021056 (FLG. 9B(i)), polystyrene with PFC oil (FIG. 9B(ii)), and silanized polystyrene (FIG. 9B(iii)), but was completely repelled by silanized polystyrene with PFC oil (FIG. 9B(iv)). EIam ple 7 [01901 The ability of functionalized titanium treated with PFC oil to repel liquid was investigated and compared to that of untreated and unmodified titanium, titanium treated with PFC oil, and silanized titanium. Four sheets of titanium were further modified with an oxygen plasma treatment at 500 mTorr for 40 seconds. Two sheets of titanium were silanized overnight with trichloro(1 H,1H,2H,2H-perfluorooctyi)silane under vacuum for approximately 13 hours. [01911 Two-hundred and fifty pL of FC-70 was applied to one silanized and one unsilanized sheet of titanium to create a "PFC-oiled" surface. Seventy-five uL of human blood without anticoagulant was applied to all four surfaces (see FIG. 10A). [01921 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 10B. FIG. 10 shows that blood adhered to untreated and unmodified titanium (FIG. 1OB(i)), titanium with PFC oil (FIG. 10B(ii)), and silanized titanium (FIG. 10B(iii)), but was completely repelled by silanized titanium with PFC oil (FIG. 10B(iv)). Example 8 [01931 The ability of soda lime glass slides treated with PFC oil to repel liquid was investigated by comparing this ability to that of untreated and unmodified soda lime glass slides, soda lime glass treated with PFC oil, and silanized soda lime glass. Four soda lime glass slides (Corning, Product Number 2 9 4 7 -75x50) were further modified with an oxygen plasma treatment at 500 mTor for 40 seconds. Two soda lime glass slides were silanized overnight with trichioro(lH,1H,2H,2H-perfiuorooctyl)silane under vacuum for approximately 13 hours. [01941 Two-hundred and fifty pL of FC- 70 was applied to one silanized and one unsilanized soda line glass slide to create a "PFC-oiled" surface. Seventy-five pmL of human blood without anticoagulant was applied to all four surfaces (see FIG. 11A). [01951 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 11B, FIG. 11 shows that blood adhered to untreated and unmodified soda lime glass (FIG. 11B(i)), soda lime glass with PFC oil (FIG. 11B(ii)), and silanized soda lime glass (FIG. 11B(iii)), but was completely repelled by silanized soda lime glass with PFC oil (FIG. - 39 - WO 2013/106588 PCT/US2013/021056 11B(iv)). Example 9 [01961 The ability of functionalized polypropylene treated with PFC oil to repel liquid was investigated and compared to that of untreated and unmodified polypropylene, polypropylene treated with PFC oil, and silanized polypropylene. Four rectangular, 1/8" thick polypropylene bars (McMaster Carr, Product Number 8782K3 1) were further modified with an oxygen plasma treatment at 500 rnTorr for 60 seconds. Two bars of polypropylene were silanized overnight with trichloro(1 H, I H,2H,2H-perfluorooctyl)silane for approximately 13 hours. [01971 Two-hundred and fifty pL of FC-70 was applied to one silanized and one unsilanized polypropylene bar to create a "PFC-oiled" surface. Seventy-five pL of human blood without anticoagulant was applied to all four surfaces (see FIG. 12A). 101981 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 12B, FIG. 12 shows that blood adhered to untreated and unmodified polypropylene (FIG. 121(i)), polypropylene with PFC oil (FIG. 12B(ii)), and silanized polypropylene (FIG. 121(iii)), but was completely repelled by silanized polypropylene with PFC oil (FIG. 12B(iv)). Exan ple 10 [01991 The ability of functionalized tape treated with PFC oil to repel liquid was investigated by comparing this ability to that of untreated and unmodified tape, tape treated with PFC oil, and silanized tape. Four sheets of polypropylene with acrylic adhesive (McMaster Carr, Product Number 75495A36) were silanized adhesive side up overnight with trichloro(IH, IH,2H2H-perfiuorooctyi)silane under vacuum for approximately 13 hours. [02001 Two-hundred and fifty pL of FC-70 was applied to the adhesive side of one silanized and one unsilanized sheet of tape to create a "PFC-oiled" surface. Seventy-five PL of human blood without anticoagulant was applied to the adhesive side of all four surfaces (see FIG. 13A). [02011 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 13B. FIG. 13 shows that blood adhered to untreated and unmodified tape (FIG. 13B(i)), tape with PFC oil (FIG. 131(ii)), and silanized tape (FIG. 13B(ii)), but was completely repelled by silanized tape with PFC oil (FIG. 13B(iv)). - 40 - WO 2013/106588 PCT/US2013/021056 EIam ple II [02021 The ability of fmnctionalized silicon wafer treated with PFC oil to repel liquid was investigated and compared to that of untreated and unmodified silicon wafer, silicon wafer treated with PFC oil, and silanized silicon wafer. The polished side of two silicon prime wafers (University Wafer) was further modified with an oxygen plasma treatment at 500 mTorr for 40 seconds. One silicon wafer was silanized overnight with trichloro(lH,1H,2H,2H perfluorooctyl)silane under vacuum for approximately 13 hours. [02031 Two-hundred and fifty pL of FC-70 was applied to approximately one half of the silanized wafer and one half of the unsilanized wafer to create "PFG-oiled" surfaces. Seventy five p L of human blood without anticoagulant was applied to all both halves of the two surfaces (see FIG. 14A). [02041 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 4B. FIG. 14 shows that blood adhered to untreated and unmodified half of silicon wafer (FIG. 141(i)), the silicon wafer half treated with PFC oil (FIG. 141(ii)), and silanized half of silicon wafer (FIG. 1 4B(iii)), but was completely repelled by silanized half of silicon wafer with PFC oil (FIG. 14B(iv)). Examnpe 12 [02051 The ability of functionalized polycarbonate treated with PFC oil to repel liquid was investigated by comparing this ability to that of untreated and unmodified polycarbonate, polycarbonate treated with PFC oil, and silanized polycarbonate. Four sheets of 1/8" thick scratch-resistant clear polycarbonate (McMaster Carr, Product Number 8707K1 11) were further modified with an oxygen plasma treatment at 500 mTorr for 40 seconds. Two sheets of polycarbonate were silanized overnight with trichloro(11H,1 H,2H,2H-perfluorooetyi)si lane under vacuum for approximately 13 hours. [02061 Two-hundred and fifty pL of FG-70 was applied to one silanized and one unsilanized sheet of polycarbonate to create a "PFC-oiled" surface. Seventy-five pL of human blood without anticoagulant was applied to all four surfaces (see FIG. 15A). [02071 The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 15B. FIG. 15 shows that blood adhered to untreated and unmodified polycarbonate (FIG. 151(i)), polycarbonate with PFC oil (FIG. 151(ii)), and silanized polycarbonate (FIG. 151(iii)), but was completely repelled by silanized polycarbonate with PFC oil (FIG. 151(iv)). -41 - WO 2013/106588 PCT/US2013/021056 Example 13 [02081 The ability of functionalized polysulfone treated with PFC oil to repel liquid was investigated and compared to that of untreated and unmodified polysulfone, polysulfone treated with PFC oil, and silanized polysulfone. Four sheets of polysuifone (MeMaster Carr) were further modified with an oxygen plasma treatment at 500 mTorr for 40 seconds. Two sheets of polysulfone were silanized overnight with trichloro(IlH-1,1 H,2H,2H-perfluorooctyi)silane under vacuum for approximately 13 hours. 102091 Two-hundred and fifty pL of FC-70 was applied to one silanized and one unsilanized sheet of polysulfone to create a "PFC-oiled" surface. Seventy-five uL of human blood without anticoagulant was applied to all four surfaces (see FIG. 16A). [02101 The surfaces were imaged, then tilted by hand, and immediately imaged again as shown in FIG. 16B. FIG. 16 shows that blood adhered to untreated and unmodified polysulfone (FIG. 1613(i)), polysulfone with PFC oil (FIG. 16B(ii)), and silanized polysulfone (FIG. 16B(iii)), but was completely repelled by silanized polysulfone with PFC oil (FIG. 16B(iv)). eiam ple 14 [0211] The effect of PDMS surface roughness on creating a slippery surface was investigated. Four sheets of smooth PDMS were cured at 60 'C on Super Corrosion Resistant Stainless Steel (Type 316), #/8 Mirror Finish (McMaster Carr, Product Number 9759K] 1) with an average roughness of 0. 1 micrometers. Two PDMS sheets were then silanized (trichloro( 11,1 H,2H,2H-perfluorooctyl)silane, Sigma, Product Number 44893 1)) overnight for approximately 12 hours. One sheet of silanized smooth PDMS and one sheet of smooth unsilanized PDMS were coated with 250 .L PFC oil (Sigma Fluorinert@ FC-70, Product Number F9880) by (see FIGS. 17A(ii) and 17A(iv), respectively). [02121 A 75 microliter volume of human blood free of anticoagulant was pipetting onto all four PDMS sheets. As shown in FIG. 17, The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 17B. FIG. 17 shows that blood adhered to untreated and unmodified smooth PDMS (FIG. 17B(i)), smooth PDMS with PVC oil (FIG. 17B(ii)), and silanized smooth PDMS (FIG. 17B(iii)), but was completely repelled by silanized smooth PDMS with PFC oil (FIG. 17B(iv)). - 42 - WO 2013/106588 PCT/US2013/021056 [02131 Four sheets of rough PDMS similarly prepared as shown in FIG. 18. Four sheets of rough PDMS were cured at 60 'C on Super Corrosion Resistant Stainless Steel (Type 316), #4 Satin Finish (McMaster Carr, Product Number 9745K I) with an average roughness of 1.0 micrometers. Two PDMS sheets were silanized (trichloro(lH1,1 H,2H,2F-perfluorooctyl)silane, Sigma, Product Number 448931)) overnight for approximately 12 hours. One sheet of silanized rough PDMS and one sheet of unsilanized rough PDMS were coated with 250 pL PFC oil (Sigma Fluorinert@ FC-70. Product Number F9880) (see FIGS. 18A(ii) and 18A(iv), respectively). [02141 A 75 rnicroliter volume of human blood free of anticoagulant was pipetting onto all four PDMS sheets. As shown in FIG. 18, the surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 18B. FIG. 18 shows that blood adhered to untreated and unmodified rough PDMS (FIG. 18B(i)), rough PDMS with PFC oil (FIG. 18B(ii)), and silanized rough PDMS (FIG. 18B(iii)), but was completely repelled by silanized rough PDMS with PFC oil (FIG. 18B(iv)). [02151 A rougher grade of PDMS cured at 60 'C on Super Corrosion Resistant Stainless Steel (Type 316), #2B Mill Finish (McMaster Carr, Product Number 88885K12) with an average roughness of 2.0 micrometers was similarly tested as shown in FIG. 19. The sheets were silanized and 75 microliters of anticoagulant-f-ce blood was pipetted onto the sheets. The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 19B. FIG. 19 shows that blood adhered to untreated and unmodified rougher PDMS (FIG. 19B(i)), rougher PDMS with PFC oil (FIG. 19B(ii)), and silanized rougher PDMS (FIG. 19B(iii)), but was completely repelled by silanized rougher PDMS with PFC oil (FIG. 19B(iv)). 102161 A comparison of FIGS. 17B(iv) (smooth PDMS), 18B(iv) (rough PDMS), and 19B(iv) (rougher PDMS) shows that anticoagul ant-free hunan blood was completely repelled by silanized PDMS with PFC oil without regard to the smoothness of the PDMS material used. Example 15 [02171 Silanes with tails of different fluorocarbon chain lengths were used to determine whether fluorocarbon chain length affects the ability of a surface to repel liquids and materials. Referring to FIG. 20, two slides of soda lime glass were modified with an oxygen plasma treatment for 40 seconds. One glass slide was coated with 250 pL PFC oil (Sigma Fluorinert@l FC-70, Product Number F9880). and 75 microliters of anticoagulant-free blood was pipetted - 43 - WO 2013/106588 PCT/US2013/021056 onto both slides. The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 20B. Blood adhered to both the plasma-treated glass side without PFC oil (FIG. 20B(i)) and the plasma-treated glass slide with PFC oil (FIG. 20B(ii)). [02181 This process was repeated with plasma-treated, I-PFC-treated soda lime glass slides. Referring to FIG. 21, two slides of soda lime glass were modified with an oxygen plasma treatment for 40 seconds and silanized (-2 hours) (Trilluoropropyltrichlorosilane, Gelest, SIT837 1.0) to achieve I-fluoridated carbon- treated glass. One glass slide was coated with 250 paL PFC oil (Sigma Fluorinert@ FC-70, Product Number F9880), and 75 microliters of anticoagulant-free blood was pipetted onto both slides. The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 218. The blood adhered to the plasma-treated I-PFC-treated glass side without PFC oil (FIG. 21B(i)). Contrastingly, much of the blood was repelled on the plasma-treated I-PFC-treated glass slide with PFC oil (FIG. 21B(i)). [0219] This process was again repeated with plasma-treated 4-PFC-treated soda lime glass slides. As shown in FIG. 22, two slides of soda lime glass were modified with an oxygen plasma treatment for 40 seconds and silanized (-2 hours) (nonafluorohexyltrichlorosilane, Gelest, SIN6597.6) to achieve 4-fluoridated carbon-treated glass. One glass slide was coated with 250 pL PFC oil (Sigma Fluorinert@ FC-70, Product Number F9880), and 75 microliters of anticoagulant-free blood was pipetted onto both slides. The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 22B. The blood adhered to the plasma-treated 4-PFC-treated glass side without PFC oil (FIG. 22B(i)). In contrast, no blood adhered to the plasma-treated 4-PFC-treated glass slide with PFC oil (FIG. 22B(ii)). [02201 Similarly, the ability of 6-PFC-treated glass sides with and without PFC oil to repel blood was compared. This process was again repeated with plasma-treated 4-PFC-treated soda lime glass slides. As shown in FIG. 23, two slides of soda lime glass were modified with an oxygen plasma treatment for 40 seconds and silanized (--2 hours) (Tridecafluorotetrahydrooctyltrichlorosilane, Gelest, SITS174.0) to achieve 6-fluoridated carbon-treated glass. One glass slide was coated with 250 pL PFC oil (Sigma Florinert@ FC 70, Product Number F9880), and 75 microliters of anticoagulant-free blood was pipetted onto both slides. The surfaces were imaged, then tilted by hand and immediately imaged again as shown in FIG. 238. The blood adhered to the plasma-treated 6-PFC-treated glass side without PFC oil (FIG. 23B(i)), In contrast, no blood adhered to the plasma-treated 6-PFC-treated glass slide with PFC oil (FIG. 23B(ii)). - 44 - WO 2013/106588 PCT/US2013/021056 [02211 Likewise, when this process was repeated with 8-PFC-treated glass slides, which were silanized for 2 hours (Heptadecafluorotetrahydrodecyltrichlorosilane, Gelest, SIH5841.0). blood adhered to the plasma-treated 8-PFC-treated glass side without PFC oil (FIG. 24B(i)), but none adhered to the plasma-treated 8-PFC-treated glass slide with PFC oil (FIG. 24B(ii)). Example 16 [02221 Experiments were conducted to determine whether oleophilic surface and hydrocarbon oil can be used to create a slippery surface capable of repelling blood. As a control, two soda lime glass slides were modified with an oxygen plasma treatment for 40 seconds. One glass slide was coated with 250 pl of light mineral oil (Sigma, M8410), and 75 ptL of human blood without anticoagulant was applied to both slides. The surfaces were imaged, tilted by hand, and immediately imaged again (FIG. 25B). Blood adhered to both glass slides without surface deposition (see, FIG. 25B(i) and 25B(ii)). [02231 Referring to FIG. 26, soda lime glass slides were modified with an oxygen plasma treatment for 40 seconds, and then silanized for 2 hours (trichloro(octyl)silane, Sigma, 235725) (FIG. 26C. One glass slide was coated with 250 it of light mineral oil (Sigma, M84 10), and 75 pL of human blood without anticoagulant was applied to both slides. The surfaces were imaged, tilted by hand, and immediately imaged again (FIG. 26B). Blood adhered to the 8 HC-treated glass slide (FIG. 26B(i), but none adhered to the 8-HC-treated glass slide treated with mineral oil (see, FIG. 26B(ii)). [02241 FIG. 28 shows unmodified, soda lime glass slides without plasma treatment, which compare untreated glass, glass with PFC oil (Fluorinert FC-70 (Sigma, F9880)), and glass with 250 pL, of light mineral oil (Sigma, M8410). No slides were silanized. Seventy-five pL of human blood without anticoagulant was applied to each slide. The surfaces were imaged, tilted by hand, and immediately imaged again (FIG. 28B). Blood adhered to the unsilanized soda lime glass (FIG. 28B(i)), unsilanized glass treated with PFC oil (FIG. 28B(ii)), and unsilanized glass treated with light mineral oil (FIG. 28B(iii)). Example 17 102251 The disclosed methods can be used to prevent blood from coagulating or adhering to glass beads. FIG. 29 shows three images of silanized 1 mm glass beads. The beads were subjected to 1 hour of sonication in soapy water, and 1 M of sodium hydroxide is added for 1 - 45 - WO 2013/106588 PCT/US2013/021056 hour. The beads were silanized in 5 % v/v in ethanol (nonafluorohexyltrichlorosilane, Gelest, SIN6597.6) and PFC oil (Fluorinert FC-70) was added to create an ultra-slippery surface on the beads (i). Twenty ml, of human blood without anticoagulant was added to the beads (ii). The beads, rinsed with PBS solution, showed little to no adhesion of blood material (iii). [02261 Similarly, FIG. 30 shows washed, unmodified glass beads that had been exposed to anticoagulant-free blood, which formed a solid clot around the beads (i). Silanized, PFC oil coated beads on which blood had been pipetted and washed with PBS showed small amounts of adhesion of blood material on the beads (ii). Silanized beads with a PFC oil coating before exposure to anticoagulant-free blood showed no blood on the beads (iii). Example 18 [02271 FIG. 32 shows a commercial application of the liquid repellent surfaces described herein. Two commercially available ketchup bottles made of PETE were emptied of ketchup, rinsed with deionized water and ethanol, successively, and baked at 60 C for 18 hours. Nonafluorohexyltrichlorosilane (Gelest, Product number SIN6597.6) was vapor deposited onto the inner surface of one bottle for 5 hours. The inside of one silanized bottle was coated with PFC oil (FC-70, Sigma), and the excess oil was poured out. Ketchup was poured back into both bottles. The contents of the treated and untreated bottles were poured into Erlenmeyer flasks (FIG. 32A) and were allowed to rest vertically (FIG. 32B). After 10 minutes, the untreated, unmodified bottle showed significant adhesion of ketchup on the walls of the bottle (FIG. 321(i)). However, little to no ketchup adhered to the silanized ketchup bottle treated with PFC oil (FIG. 32B(ii)). Example 19 [02281 The following exemplary experiment conditions and procedures can be used to test the robustness and stableness of the surface treatment in some embodiments: 1) 1/4" medical grade PVC tubes (Sorin Group #020463101) were plasma treated under 170 mTorr oxygen for 120 see at 100 V and liquid silanized using 5% tridecafluoro 1,1,2,2-hydrooctyl trichlorosilane (Gilest #SIT8174.0) in ethanol (%v/v) for 1 hour and dried overnight at 60 degrees C; 2) One half of the PVC tubes above were packaged in Self-Seal Sterilization Pouches (Cardinal Health #92713) and sterilized using ethalene oxide under standard hospital - 46 - WO 2013/106588 PCT/US2013/021056 sterilization protocols. The other half of the PVC tubes above were unsterilized and stored covered at room temperature; 3) Seven days later, the sterilized and non-sterilized tubes were coated with either Fluorinert FC-70 (3M) or perfluordecalin (sigma) and allowed to drain briefly; 4) Pig blood that was collected into a CPD bag with 100 unit/kg of Heparin was filtered using a 40um cell strainer (BD) and recalcified with 7.5mM calcium chloride/magnesium chloride (100mM CaCl2, 75mM MgCI2) and deheparinized with 3.5ng/ml protanine sulphate. 30mL was then flowed through the tubes at 30m1/min driven by a syringe pump; 5) The blood was then gravity drained from the tubing and the tubing was imaged to compare treated vs. untreated tubing and sterilized vs. non sterilized tubing. (Untreated control tubes were not silanized, sterilized or coated with perfluorocarbon oil, but was otherwise handled the same as the treated tubes.) [0229] FIGS. 33A-E demonstrate the test results of a series of blood residue experiments (e.g., as described in the above procedures and conditions) using untreated or treated medical grade PVC tubes. FIG. 33A demonstrates that significant blood residues remain inside untreated tubes. FIG. 33B demonstrates that blood residues are significantly reduced inside FC-70 treated (non-sterilized) tubes. FIG. 33C demonstrates that the repellant characteristics are largely unaffected by sterilization. FIG. 33D demonstrates that blood residues are significantly reduced inside PFD treated (non-sterilized) tubes. FIG. 33E demonstrates that the repellant characteristics are largely unaffected by sterilization. Eiam ple 20 102301 Silicon wafer from University Wafer, acrylic (PMMA) from McMaster Can, and polysulfone from McMaster Carr were plasma treated for I min using oxygen plasma at 160 mTorr and 100W. Silane treatment was then carried out for 1 hour with 5% (tridecafluoro 1,1,2.2--tetrhydroocyl) trichlorosilane (v/v) with pure ethanol (anhydrous), followed by rinses of ethanol, deionized water, and ethanol and by a 65 'C bake for 2 hours. 5 uL of water was placed on each sample with a pipette and average and standard deviation were measured using 3 images for each sample. As shown in FIG. 34, the contact angle decreases after plasma treatment but increases after silanization. Example 21 - 47 - WO 2013/106588 PCT/US2013/021056 [02311 Acrylic (PMMA) from McMaster Carr, % in thick was plasma treated for I min using oxygen plasma at 160 mTorr and 100W. Silane treatment was then carried out for 1 hour with 5% (tridecafluoro-1,1,2,2-tetrhydroocyl) trichlorosilane (v/v) with pure ethanol (anhydrous), followed by rinses of ethanol, deionized water, and ethanol, followed by a 65 'C bake for 2 hours. Atomic Force Microscopy (AFM) surface measurements of acrylic surfaces before and after plasma treatment and silanization was carried out acrylic surfaces (Mcmaster Carr), where the mean and standard deviation of root mean squared surface roughness was carried out. Acrylic surface was plasma treated for 60 seconds under 150 mTorr of oxygen gas at 100 W. and silanized for 1 hour with 5% (tridecafluoro-1,1,2,2-tetrhydroocyl) trichlorosilane (v/v) in pure ethanol (anhydrous), followed by rinses of ethanol, deionized water, and ethanol and by a 65 'C bake for 2 hours. The surface roughness decreases from 3.4 nm + 1.1 nm to about 2.0 -A: 0.2 nm after silanization. [02321 The silanized acrylic samples were dipcoated with perfluorodecalin (FluoroMed) and the tilt angle of water, hexadecane, and human blood with citrate was measured by placing 5 pL of the liquid on the prepared sample with pipette. Then, the samples were tilted manually with a gonionieter (Edmund Scientific). Samples which did not move the liquid after tilt angles reached 10 degrees were not tilted any further and recorded with a tilt angle of 10 degrees.. [02331 FIG. 35 shows that while the liquids did not move on untreated samples even at 10 degree tilt angle, surfaces treated with the perfluorodecalin shows tilt angles that were below 2 degrees. Example 22 [02341 Biological characterization before and after treatment with the lubricating liquid was carried out using in vitro studies. Polysulfone surface was plasma treated for 60 seconds tinder 150 mTorr of oxygen gas at 100 W, and silanized for 1 hour with 5% (tridecafluoro 1,1,2,2-tetihydroocyl) trichlorosilane (v/v) in pure ethanol (anhydrous), followed by rinses of ethanol, deionized water, and ethanol and by a 65 'C bake for 2 hours. "No PFC Oil" samples were plasma/silanized but did not have any lubricating liquid added thereafter. "Perflubron," "Perfluorodecalin," and "Fluorinert FC-70" samples were dipcoated in the respective lubricant and the excess removed by gravity immediately prior to exposure to blood. Samples were photographed after saline rinse. Blood was obtained with informed consent from healthy, male volunteers who had not taken aspirin within 2 weeks of donation and who did not smoke. Blood was drawn in accordance with the Declaration of Helsinki with approval from the - 48 - WO 2013/106588 PCT/US2013/021056 Harvard Committee on Human Studies (Protocol Number M20403-10 1). Blood tilt experiments were conducted at an angle of 90 degrees. . 102351 The rate of thrombosis from whole human blood on slippery PMMA and polysulfone was investigated and quantified the adhesion by spiking the blood with fluorescent fibrinogen. Reduced surface adhesion and fibrin formation was observed on all slippery surfaces investigated over untreated surfaces. For blood adhesion experiments, polysulfone or poly(methyl methacrylap) (PMMA) pieces (I min x 8mm) were incubated for 30, 60 or 90 minutes with heparinized blood (0.25U/rnl) containing 15 ug/mL of fluorescent fibrinogen in wells blocked with BSA (1% (w/v)). Time course of thrombus accumulation from slightly heparinized human blood on polysulfone and PMMA in BSA-blocked polystyrene well plates over 30 min, 60 min and 90 min is shown in FIG. 36. As shown, samples treated with perfluordecalin and FC70 showed the most effective reduction in thrombus accumulation. [02361 FIG. 37 shows the scanning electron microscope images for untreated polysulfone and that which was plasma treated, silanized, and coated with FC-70 after 30 minutes. Similarly to FIG. 36, sample treated with FC-70 showed significant reduction in thrombus accumulation. 102371 The time course of thrombus accumulation from slightly heparinized human blood was further observed with fluorescent fibrinogen on acrylic in BSA-blocked polystyrene well plates over 90 minutes. The samples were measured by fluorescence microscopy after saline rinse and images were analyzed with imageJ software. As shown in FIG. 38, samples treated with FC-70 showed the least amount of fibrinogen-coated areas. Chemical surface modification significantly decreased fibrin adhesion from untreated PMMA (P<0.001). Fibrin formation was reduced by 97% on slippery PMMA with FC-70 after 90 min, which was statistically significant (P<0.00 1). Exanpe 23 [02381 Slippery surface modification and coating with medical grade perfluorinated liquids reduced the thrombogenicity of surfaces when in contact with non-anticoagulated blood in vitro studies. [02391 PVC tubing (Tygon 3603) was plasma treated under 170 mnTorr oxygen for 120 see and liquid silanized (5% tridecafluoro-1,1,2,2-hydrooctyl trichlorosilane in Ethanol) for 1 hour, rinsed with ethanol, deionized water, and ethanol 3X, and dried overnight at 60 degrees C. Half of the PVC tubes were packaged and sterilized by ethylene oxide sterilization. The rest - 49 - WO 2013/106588 PCT/US2013/021056 were stored covered at room temperature. [02401 Seven days later the sterilized and non-sterilized tubing was lubricated with perfluordecalin (FluoroMed). Untreated and Pig blood was filtered through 40um cell strainer before 46,9ul/nl 100mM CaCl2/75mM MgCl2 (3/4) and 3.5ug protamine sulphate (1/2) was added to pig blood. [02411 30ml pig blood was flowed through the tubing at 30mL/min using a syringe pump. The blood was re-activated with 1 00mM CaCi2 and 75mM MgCi2 and protantine sulphate 1 Oug/IJ. Arteriovenous shunts were established in the fenoral artery and vein of Yorkshire swine using SF catheters (Medtronic) and %" tubing (Sorin Group). The tubing was emptied of blood by gravity and imaged immediately horizontally. As shown in FIG. 38, sterilized and unsterilized tubing with perfluorodecalin did not retain blood, while the untreated tubing did. Accordingly, sterilization does not appear to affect the silanization and surfaces remain slippery. Example 24 [02421 Slippery surface modification and coating with medical grade perfluorinated liquids reduced the thrombogenicity of surfaces when in contact with non-anticoagulated blood in vivo studies. [02431 Biological characterization before and after treatment with the lubricating liquid was cared out using in vivo studies. Medical grade plastics with and without the slippery surface treatment were carried out by forming an arteriovenous (AV) bridge between the femoral artery and vein of 40 kg pigs. 8Fr Cannjulae was joined by 24 x % inch PVC tubing. Blood flow at approximately IL/min ( 60L/hr) was tested for 8 hours without use of added anticoagulants. The slippery shunt remained unobstructed (patent) over 8 hours of-I L/min of blood flow, while the untreated shunt occluded completely within 90 minutes. [02441 Medical grade PVC tubing (Sorin group) was plasma treated under 170 inTorr oxygen for ISO see and liquid silanized (5% tridecafluoro- 1,1,2,2 -hydrooctyl trichlorosilane in Ethanol) for 1 hour, rinsed with ethanol, deionized water, and ethanol 3X, and dried overnight at 60 degrees C. [02451 Similarly, medical grade polyurethane catheters were plasma treated under 170 mTorr oxygen for 120 see and liquid silanized (5% tridecafluoro-1,1,2,2-hydrooctyl trichlorosilane in Ethanol) for 1 hour, rinsed with ethanol, deionized water, and ethanol 3X, and dried overnight at 60 degrees C. - 50 - WO 2013/106588 PCT/US2013/021056 [02461 Both samples were sterilized by ethylene oxide before lubrication with perfluorodecalin. 102471 As shown in FIG. 39A, the medical grade cannulae and PVC bridge without the lubricating liquid applied thereon shows significant clotting/obstruction, particularly in the cannula:bridge connectors. Occlusion occurred within 1 to 1.5 hours. In contrast, as shown in FIG. 39B, when a slippery surface formed on the medical grade cannulae and PVC bridge, minimal clotting and minimal platelet activation is observed even after 8 hours. [02481 As shown in FIG. 40, the catheter and tubing were sectioned and imaged. As shown, the samples with the slippery surface showed reduced clotting compared to the untreated control samples. [02491 Moreover, as shown in FIG. 41, the samples were weighed while filled with saline and after the saline was emptied to determine the weight of thrombus in the circuit. Less thrombus accumulation was observed in the treated samples than in the control samples Example 25 [02501 Metal Surface Modification with carboxyl-terminated perfluoropolyethers as an anchoring layer is demonstrated. Krytox 157 FSH (carboxyl terminated poly(hexafluoropropylene oxide), MW 7000-7500, Miller Stephenson) was used as an anchoring layer. FC-70 (Aldrich, lot #MKBF943 IV) or Krytox 1 Ox were used as lubricants. Al alloy 6061 -T6 was used as a substrate. 30% hydrogen peroxide (Aqua Solutions), absolute ethanol (Pharmco), HFE-71 00 (mixture of methyl nonafluorobutyl ether, 30-50%, and methyl nonafluoroisobutyl ether, 70-50%, Miller Stephenson), were used as received. Water used for washes was of Millipore grade. 102511 The representative roughness and waviness data of the flat Al sample are presented in the Table 2. Sample Average RMS Average RMA Roughness Roughness Waviness Waviness Ra pm Rqpm Wagm Wq___ m Al 6061-T6 0.3016 0.4100 0.2848 0.3595 flat Calibration Si 0.001975 0.000247 0.00328 0.003975 1Mech. Grade Table 2. Roughness and waviness data measured for a flat Al sample [02521 Aluminum plates were sonicated for 30 mi sequentially in 30% H 2 0 2 , water, and -51 - WO 2013/106588 PCT/US2013/021056 absolute ethanol, and then dried in an oven in the air at I 00OC for 30 min. [02531 The pre-cleaned samples were put vertically in a Teflon holder and then placed into a 500-rmL three-neck flask, equipped with a reflux condenser, thermocouple, heating mantle and nitrogen blanket (bubbler). The flask was charged with a 3 mM solution of Krytox 157FSH in HFE-7 100 (846 g in 370.5 mL). The solution fully covered the plates as seen in Fig. lb. The mixture was refluxed under nitrogen at 60-C for 3 h, following which the mixture was let to cool down to room temperature, samples were removed, rinsed sequentially in 40 mL of HFE-7 100 and 40 mL of absolute ethanol, and dried in an oven in the air at 80cC for 55 min. Two samples at a time were treated and the solution and the rinses were reused in the treatment of the next sets of samples. [02541 The contact angle measurements were performed at room temperature using a CAM 101 (KSV Instruments LTD) instrument and Millipore grade water. The presented values are left, right and average angles for each location. For each sample one to three locations were tested. The samples were held horizontally during the measurements. The representative contact angle data are presented in the Table 3. Sample CA (L). deg CA(R), deg CA(M), deg Comment Center 120.217 119.267 119.742 a) Edge 109.751 110.147 109.949 a) a) The sample after the reflux was left overnight at room temperature in the reaction mixture Table 3. Contact angle data measured for the surface-functionalized Al 6061-T6 sample [02551 Surface-pretreated aluminum coupon was infused with FC-70 (Aldrich, lot #MKBF9431V) by placing a total of 60 L (~130 ing) of FC-70 on the surface of the sample. The FC-70 was allowed to spread for several minutes. The sample was wetted with the lubricant quite readily, resulting in a smooth shiny surface. [02561 To test the surface of the treated sample for liquid repellency, a single drop of water (30 L, Millipore) was placed on the aluminum surface, and the behavior of the water droplet was observed and videotaped while the surface was tilted in various directions. It was clearly evident that the water droplet slides easily on the functionalized and lubricated surface, with vCy little resistance, at low tilt angles, and without pinning. [02571 The functionalization chemical reaction is shown below. Post functionalization, the flat chemically functionalized sample exhibited contact angle 110-120 deg, close to the maximum reported water contact angle on flat PTFE surface - -120 deg. The observed value indicates that the functionalization did occur. - 52 - WO 2013/106588 PCT/US2013/021056 ............ .. ....... [02581 As expected, the fluorinated lubricant FC-70 spread easily on the functionalized substrate, creating a smooth slippery surface that exhibited fluid-repelling behavior, as evidenced by the free movement of the droplet on the surface at low tilt angles, without resistance, and with no pinning. Example 26 [02591 Chemical functionalization of a solid substrate with a phosphonic acid ligand to match the affinity' with a liquid lubricant to form slippery surfaces is demonstrated. [02601 All chemicals were purchased from Sigma-Aldrich and used without further purification unless specified otherwise. [02611 Solution-phase chemical functionalization of metal oxide substrates using perfluorinated phosphonic acid ligand for matching the affinity of substrate with lubricant 102621 In order to create a monolayer of fluoroalkyl chains on aluminum oxy hydroxide substrate surface, we submerged samples in a I wt. % solution of 1H, 11-1, 2Hf,2H-perfluorooetyl phosphoric acid (F13PA) or FS100 (fluoroaliphatic phosphate ester fluorosurfactant, Mason Chemical Company) in 95:5 ethanol:water for I h at 70 0 C. In another aspect, substrates having a portion that can be damaged at elevated temperature were fluorinated in the same bath at lower temperature for a longer period of time (e.g. 3-4 h at 40'C or overnight at room temperature). In yet another aspect, substrates having a portion that can be damaged by alcohols (e.g. PMMA, medical grade PVC) were fluorinated in an aqueous solution of FS 100 prepared in the presence of I wt. % Pluronic F-68 (EO 7
SPO
3 0EO 7 , FW=8400, Affymetrix) to dissolve FS100, then following the same procedure as for other substrates. [02631 Substrates that are not compatible with solution-phase chemical functionalization methods (e.g. PDMS, PHEMA hydrogel) were fluorinated using C4Fs plasma using an inductively coupled plasma reactive ion etching system (STS MPX/LPX RIE) with C4Fs flow rate of 120 secm (standard cubic centimeter per minute) for 8 see under I mTorr pressure and 600 W/0 W coil/platen power. [02641 All the fluorinated surfaces were lubricated by application of a perfluoropolyether (PFPE) lubricant (DuPont Krytox GPL 100, "K100"). To spread out the lubricant, the - 53 - WO 2013/106588 PCT/US2013/021056 substrates were either tilted or spun on a spin coater. Excess lubricants were typically removed by spinning the substrates at higher spin rate (>3,000 rpn., 1 min) or by pressure washing the substrate in a stream of high-pressure water. [02651 FIG. 42 shows through FTIR spectra that slippery surfaces were successfully formed as evidenced by the characteristic peaks that arise through the four different stages of functionalization from bare aluminum (Al), aluminum oxy hydroxide (Al--B), fluoro functionalized aluminum oxy hydroxide (Al-BF), and pure fluoroaliphatic phosphate ester fluorosurfactatt (FS100). Exam ple 27 102661 Glass bottom 24 well plates (Matek Corporation, P24G-0-13-F) were plasma and silane treated with or without PFD (which was added and then pipetted off). Then, Iml of a 0.Sug/mil solution of fluorescent fibrinogen Alexa Fluor 647 (Invitrogen, F35200) in phosphate buffered saline was added to each well. Images were taken on a Leica TIRF on DM16000B using a 63x oil objective with multipoint positioning. [02671 As shown in FIG. 43 (scale bar = 20um), fibrinogen molecules in saline are repelled from slippery glass. Fluorescent fibrinogen particles (see arrows) stick to glass without perfluorocarbon (top) but do not stick to surface and continue to move over glass treated with the perfluorocarbon material (bottom). Example 28 [02681 Glass bottom 24 well plates (Matek Corporation, P24G-0-13-F) were plasma and silatie treated with or without Vitreon (which was added and then pipetted off). Then, I nil heparinized whole human blood, spiked with 1.5ug/ml solution of fluorescent fibrinogen Alexa Fluor 647 (Invitrogen, F35200), was added to each well. Images were taken with a Leica SP5 X MP Inverted Confocal Microscope using a 20X objective with multipoint positioning. [02691 As shown in FIG. 44 (scale bar = 100am), whole blood repelled from slippery glass. Fluorescent thrombi (arrows) stick to glass without perfluorocarbon (top) but do not stick to surface and continue to move over glass treated with the perfluorocarbon material (bottom). Eamin ple 29 [02701 The ability of functionalized filter paper treated with PFC oil to repel liquid was investigated and compared to that of untreated and unmodified filter paper, filter paper treated with PFC oil, and silanized filter paper. Two pieces of filter paper (Whatman, #JB-2, - 54 - WO 2013/106588 PCT/US2013/021056 10347673) were further modified with an oxygen plasma treatment at 170 mTorr for 60 seconds at 200 MW. Those two filters were silanized overnight with trichloro(iH,1H,2H,2H perfluorooctyhlsilane under vacuum for approximately 13 hours. [02711 Seventy-five pL of perfluorodecalin were applied to one silanized and one unsilanized pieces of filter paper to create "PFC-oiled" surfaces. Twenty-five p L of human blood were applied to all four surfaces. [02721 The surfaces were imaged, then tilted by hand and immediately imaged again. The blood adhered to untreated and unmodified filter paper, the filter paper treated with PFC oil, and the silanized filter paper, but was completely repelled by silanized filter paper with PFC oil. Exanpe 30 [02731 The ability of a functionalized glass fiber filter treated with PFC oil to repel liquid was investigated and compared to that of a untreated and unmodified glass fiber filter, a glass fiber filter treated with PFC oil, and a silanized glass fiber filter. Two glass fiber filters (Millipore, AP2007500) were further modified with an oxygen plasma treatment at 170 mTorr for 60 seconds at 200 W. Those two filters were silanized overnight with trichloro(l IH,H,2H-perfluorooctyl)silane under vacuum for approximately 13 hours. [02741 Seventy-five pL of perfluorodecalin were applied to one silanized and one unsilanized glass fiber filter to create "PFC-oiled" surfaces. Twenty-five uL of human blood were applied to all four surfaces. [02751 The surfaces were imaged, then tilted by hand and immediately imaged again. The blood adhered to untreated and unmodified glass fiber filter, the glass fiber filter treated with - 55 - WO 2013/106588 PCT/US2013/021056 PFC oil, and the silanized glass fiber filter, but was completely repelled by silanized glass fiber filter with PFC oil. Example 31 [02761 The composition of the leaving group on the silane and the composition of the solvent during the silanization was investigated. Perfluorodecalin was used as the solvent for deposition of the silane. The ability of acrylic finctionalized with either triethoxysilane or trichlorosilane and further treated with PFC oil to repel liquid was investigated and compared to that of untreated and unmodified acrylic, acrylic treated with PFC oil, and acrylic functionalized with either triethoxysilane or trichlorosilane. Six sheets of Clear Cast Acrylic Sheet, 0.060" Thick, (McMaster Carr, Product Number 8560K171) were obtained. Two acrylic sheets were silanized in perfluorodecalin with five volurne percent trichloro(lH,,IH,2H,2H-perfluorooctyl)silane (Gelest, SIT8174.0) for 1 hour. Two separate filters were silanized in perfluorodecalin (FluoroMed, AP140-HP) with five volume percent triethoxy (I H,1 H,2H,2H-perfluorooctyl)silane (Gelest, SIT8175.0) for 1 hour. The four silanized sheets were rinsed with 1 milliliter of perfluorodecalin, dried with compressed air, and baked at 60 degrees Celsius for 2 hours. [02771 Seventy-five pL of perfluorodecalin were applied to one silanized with trichlorosilane, on silanized with triethoxysilane, and one unsilanized acrylic sheet to create "PFC-oiled" surfaces. Twenty-five PL of human blood were applied to all six surfaces. [02781 The surfaces were imaged, then tilted by hand and immediately imaged again. The blood adhered to untreated and unmodified acrylic, acrylic treated with PFC oil, and acrylic functionalized with either triethoxysilane or trichlorosilane., but was completely repelled by acrylic functionalized with either triethoxysilane or trichlorosilane and further treated with PFC oil. [02791 As will be apparent to one of ordinary skill in the ati from a reading of this disclosure, aspects of the present disclosure can be embodied in forms other than those specifically disclosed above. For example, a desired functionality, intended to achieve certain medically relevant response (such as anti-clotting, blood or other biological fluid repelling, drug releasing, infection-suppressing, tissue growth promoting, etc.), can be engineered into the composition of the anchoring and lubricating layers. The particular embodiments described above are, therefore, to be considered as illustrative and not restrictive. Those skilled in the art will recognize, or be able to ascertain, using no more than routine experimentation, numerous - 56 - WO 2013/106588 PCT/US2013/021056 equivalents to the specific embodiments described herein. The scope of the invention is as set forth in the appended claims and equivalents thereof, rather than being limited to the examples contained in the foregoing description. [0280] What is claimed is: - 57 -

权利要求:
Claims (65)
[1] 1. An article having a slippery surface, comprising: a substrate comprising an anchoring layer, the anchoring layer comprising; a head group attached to the substrate and a functional group directly or indirectly attached to the head group; and a lubricating layer comprising a lubricating liquid having an affinity for the functional group and disposed over the anchoring layer, wherein the anchoring layer and the lubricating layer are held together by non-covalent attractive forces, wherein the anchoring layer and the lubricating layer form a slippery surface configured and arranged for contact with a material that is substantially immiscible with the lubricating liquid,
[2] 2. The article of claim 1, wherein the immiscible material is selected from the group consisting of a liquid, complex fluid, solution, suspension, and a solid.
[3] 3. The article of claim 1, wherein the slippery surface is hydrophobic.
[4] 4. The article of claim 1, wherein the slippery surface is hydrophilic.
[5] 5. The article of claim 1., wherein the slippery surface is oniphobic.
[6] 6. The article of claim 1, wherein said head group of the anchoring layer includes ethers, silyl ethers, siloxanes, esters of carboxylic acids, esters of sulfonic acids, esters of sulfinic acids, esters of sulfuric acids, esters of phosphonic acids, esters of phosphinic acids, esters of phosphoric acids, silyl esters of carboxylic acids, silyl esters of sulfonic acids, silyl esters of sulfinic acids, sill esters of sulfuric acids, silyl esters of phosphonic acids, silyl esters of phosphinic acids, silyl esters of phosphoric acids, oxides, sulfides, carbocycles, heterocycles with at least one oxygen atom, heterocycles with at least one nitrogen atom, heterocycles with at least one sulfur aton, heterocycles with at least one silicon atom, 'click' reactions-derived heterocycles, Diels-Alder reactions-derived carbocycles, Diels-Alder reactions - 58 - WO 2013/106588 PCT/US2013/021056 derived heterocycles, amides, imides, sulfides, thiolates, metal thiolates, urethanes, oximes, hydrazides, hydrazones, physisorbed or chemisorbed or otherwise non covalently attached moieties, or combinations thereof.
[7] 7. The article of any of the preceding claims, wherein the functional group of the anchoring layer comprises a hydrocarbon, and the lubricating layer comprises hydrocarbon liquid, wherein the anchoring layer and the lubricating layer form an hydrophobic slippery surface.
[8] 8. The article of claim 7, wherein said functional group of the anchoring layer includes alkanes, alkenes, alkynes, and aromatic compounds, and combinations thereof.
[9] 9, The article of any of claims 1-6, wherein the functional group of the anchoring layer comprises charged polypeptides, polyanions, polycations, polar polymers, polysaccharides, amines, carboxylic acids, guanidine, alcohols, sulfhydryls, carboxamides, metal oxides, or combinations thereof.
[10] 10, The article of any of claims 1-6, wherein the functional group of the anchoring layer includes perfluorocarbons, perfluorooligoethers and perfluoropolyethers.
[11] 11, The article of any of clai msi-6, wherein, the anchoring layer comprises a silyl group covalently attached to a hydrocarbon or perfluorcarbon tail, and the lubricating layer comprises hydrocarbon or perfluorcarbon liquid, wherein the anchoring layer and the lubricating layer form a hydrophobic or an omniphobic slippery surface.
[12] 12, The article of any of claimsl-6, wherein, the anchoring layer comprises a phosphonate or carboxylate group covalently attached to a hydrocarbon or perfluorcarbon tail, and the lubricating layer comprises hydrocarbon or perfluorcarbon liquid, wherein the anchoring layer and the lubricating layer form a hydrophobic or an onmiphobic slippery surface.
[13] 13. The article of claim 1, wherein the omniphobic slippery surface is slippery to water based and hydrocarbon- based liquids. - 59 - WO 2013/106588 PCT/US2013/021056
[14] 14. The article of claim 1, wherein the oniphobic slippery surface is slippery to biological fluids.
[15] 15. The article of claim 1, wherein the omniphobic slippery surface is slippery to non heparinized blood.
[16] 16. The article of claim 1, wherein the ornniphobic slippery surface comprises glass beads.
[17] 17. The article of claim 1, wherein the ornniphobic surface comprises medical grade materials or medical devices.
[18] 18. An article having a low friction interface, comprising: a first substrate comprising a first anchoring layer, the anchoring layer comprising; a first head group attached to the substrate and a first functional group directly or indirectly attached to the head group; and a first lubricating layer comprising a lubricating liquid having an affinity for the first functional group and disposed over the first anchoring layer, wherein the first anchoring layer and the first lubricating layer are held together by non-covalent attractive forces; and a second substrate comprising a second anchoring layer, the anchoring layer comprising; a second head group attached to the substrate and a second functional group directly or indirectly attached to the head group; and a second lubricating layer comprising a lubricating liquid having an affinity for the second functional group and disposed over the second anchoring layer, wherein the second anchoring layer and the second lubricating layer are held together by non-covalent attractive forces, wherein the first and second substrates are in facing relationship with each other such that the first lubricating layer opposes the second lubricating layer, and - 60 - WO 2013/106588 PCT/US2013/021056 wherein the first and second lubricating layer are immiscible.
[19] 19. The article of claim 18, wherein the first lubricating layer has a greater affinity for the first substrate than the second substrate.
[20] 20, The article of any of claim 18 or 19, wherein the second lubricating layer has a greater affinity for the second substrate than the first substrate.
[21] 21, The article of any of claim 18-20, wherein one of first or second lubricating layers is hydrophobic.
[22] 22, The article of any of claim 18-20, wherein one of first or second lubricating layers is hydrophilic.
[23] 23. The article of any of claim 18-20, wherein one of first or second lubricating layers is omniphobic.
[24] 24. A system for preferentially sorting a solute or particle from a liquid, comprising: a substrate comprising an anchoring layer, the anchoring layer comprising; a head group attached to the substrate and a functional group directly or indirectly attached to the head group; and a lubricating layer comprising a lubricating liquid having an affinity for the functional group and disposed over the anchoring layer, wherein the anchoring layer and the lubricating layer are held together by non-covalent attractive forces; and an immiscible liquid, statically or dynamically in contact with the lubricating layer, said immiscible liquid comprising one or more of a solute or particle of interest, wherein the lubricating liquid is immiscible with the liquid, but has an affinity for the soluble or particle of interest.
[25] 25. The system of claim 24, further comprising: a conduit for flowing the inniscible layer over the lubricating layer. - 61 - WO 2013/106588 PCT/US2013/021056
[26] 26. The system of any of claims 24-25, wherein the head group is covalently attached to the surface.
[27] 27. The system of any of claims 24-26, wherein the head group is adsorbed onto the surface.
[28] 28. The system of any of claims 24-27, wherein the anchoring layer forms a monomolecular layer on the surface.
[29] 29. The system of any of claims 24-28, wherein the functional group is a hydrocarbon.
[30] 30, The system of any of claims 24-29, wherein the functional group is selected from the group consisting of charged polypeptides, polvanions, polycations, polar polymers, polysaccharides, aimines, carboxylic acids, guanidine, alcohols, sulfhydryls, carboxamides, metal oxides, inorganic oxides, and combinations thereof.
[31] 31, The system of any of claims 24-30, wherein the functional group is a perfluorocarbon.
[32] 32. The system of any of claims 24-31, wherein the surface is selected from the group consisting of acrylic, glass, polymers, metals, carbon, plastics, paper, ceramics, and combinations thereof.
[33] 33. The system of any of claims 24-31, wherein the surface is selected from the group consisting of poly(dimethyl siloxane) (PDMS), acrylic, polystyrene, tissue-culture polystyrene, metal, polypropylene, acrylic adhesive, silicon wafer, polysulfone, and soda lime glass.
[34] 34. The system of any of claims 24-32, wherein the slippery surface is sterile.
[35] 35. A method of preventing adhesion, adsorption, surface-mediated clot formation, or coagulation of a material onto a substrate, comprising providing a slippery surface comprising an anchoring layer, the anchoring layer comprising a head group attached to the substrate and a functional group directly or -62 - WO 2013/106588 PCT/US2013/021056 indirectly attached to the head group; and a lubricating layer comprising a lubricating liquid having an affinity for the functional group and disposed over the anchoring layer, wherein the anchoring layer and the lubricating layer are held together by non-covalent attractive forces; and contacting an immiscible material to the slippery surface.
[36] 36. The method of claim 35, wherein the head group is covalently attached to the surface.
[37] 37. The method of claim 35, wherein the head group is adsorbed onto the surface.
[38] 38, The method of claim 35, wherein the anchoring layer forms a monomolecular layer on the surface.
[39] 39. The method of claim 35, wherein the surface is selected from the group consisting of acrylic, glass, polymers. metals, carbon, plastics, paper, ceramics, and combinations thereof.
[40] 40. The method of claim 35, wherein the surface is treated to activate the surface prior to exposure to the anchoring layer.
[41] 41. The method of claim 40, wherein activation comprises acid treatment, base treatment, oxidization, ammonization, plasma, or microwave treatment.
[42] 42. The method of claim 35, wherein the slippery surface is hydrophobic.
[43] 43. The method of claim 35, wherein the slippery surface is hydrophilic.
[44] 44. The method of claim 35, wherein the slippery surface is oniphobic.
[45] 45. The method of claim 35, wherein the functional group is a hydrocarbon.
[46] 46. The method of claim 35, wherein the functional group is selected from the group consisting of charged po lypeptides, po lyanions, polycations, polar polymers, polysaccharides, amines, carboxylic acids, guanidine, alcohols, sulfhydryls, carboxamides, metal oxides and combinations thereof. - 63 - WO 2013/106588 PCT/US2013/021056
[47] 47. The method of claim 35, wherein the ftinctional group is a perfluorocarbon.
[48] 48. The method of claim 35, wherein the immiscible material is selected from the group consisting of non-viscous and viscous liquids, complex fluids, semi-solids, tacky liquids, and solids.
[49] 49. The method of claim 35, wherein the surface reduces coagulation of blood.
[50] 50, The method of claim 35, wherein the surface reduces adhesion of fibrin, fibrinogen, platelets, leukocytes, red blood cells and coagulation factors,
[51] 51, The method of claim 35, wherein the immiscible material contains an additive, the additive being selected from the group consisting of a solute, a particulate or a combination thereof.
[52] 52. The method of claim 51, wherein the immiscible material is repelled by the surface and the additive is attracted to the surface.
[53] 53. The method of claim 52, wherein the immiscible material and the additive are repelled by the surface.
[54] 54. The method of claim 35, wherein the immiscible material is selected from the group consisting of whole blood, plasma, serum, sweat, feces, urine, saliva, tears, vaginal fluid, prostatic fluid, gingival fluid, amniotic fluid, intraocular fluid, cerebrospinal fluid, seminal fluid, sputum, ascites fluid, pus, nasopharengal fluid, wound exudate fluid, aqueous humour, vitreous humour, bile, cerumen, endolymph, perilymph, gastric juice, mucus, peritoneal fluid, pleural fluid, sebum, vomit, and combinations thereof.
[55] 55. The method of claim 35, wherein the immiscible material is a solution or suspension containing bacteria selected from the group consisting of Actinobacillus, Acinetobacter (e.g., Acinetobacter baumannii), Aeromonas, Bordetella, Brevibacillus, Brucella, Bacteroides, Burkholderia, Borelia, Bacillus, Campylobacter, Capnocytophaga, Cardiobacterium, Citrobacter, Clostridium, Chlamydia, Eikenella, - 64 - WO 2013/106588 PCT/US2013/021056 Enterobacter, Escherichia, Francisella, Fusobacterium, Flavobacterium, Haemophilus, Helicobacter, Kingella, Klebsiella, Legionella, Listeria, Leptospirac, Noraxella, Morganella, Mycoplasma, Mycobacterium, Neisseria, Pasteurella, Proteus, Prevotella, Plesiomonas, Pseudomonas, Providencia, Rickettsia , Stenotrophomonas, Staphylococcus, Streptococcus (group A), Streptococcus agalactiac (group B), Streptococcus bovis, Streptococcus pneumoniae, Streptomyces, Salmonella, Serratia, Shigella, Spirillum, Treponema, Veillonella, Vibrio, Yersinia, Xanthomonas, and combinations thereof.
[56] 56. The method of claim 35, wherein the immiscible material is a solution or suspension containing fungi selected from the group consisting of a member of the genus Aspergillus, Blastomyces dermatitidis, Candida, Coccidioides immitis, Cryptococcus, Histoplasma capsulatum var. capsulatum, Histoplasma capsulatum var. duboisii, Paracoccidioides brasiliensis, Sporothrix schenckii, Absidia corymbifera; Rhizomucor pusillus, Rhizopus arrhizous, and combinations thereof.
[57] 57. The method of claim 35, wherein the material is a solution or suspension containing viruses selected from the group consisting of cytomegalovirus (CMV), dengue, Epstein-Barr, Hantavirus, human T-cell lymphotropic virus (HTLV I/II), Parvovirus, hepatitides, human papillomavirus (HPV), human immunodeficiency virus (HIV), acquired immunodeficiency syndrome (AIDS), respiratory syncytial virus (RSV), Varicella zoster, West Nile, herpes, polio, smallpox, yellow fever, rhinovirus, coronavirus, Orthonivxoviridae (influenza viruses), and combinations thereof.
[58] 58. 'The method of claim 35., wherein the material is a solution or suspension containing particles selected from the group consisting of normal cells, diseased cells, parasitized cells, cancer cells, foreign cells, stem cells, and infected cells, microorganisms, viruses, virus-like particles, bacteria, bacteriophages, proteins, cellular components, cell organelles, cell fragments, cell membranes, cell membrane fragments, viruses, virus-like particles, bacteriophage, cytosolic proteins, secreted proteins, signaling molecules, embedded proteins, nucleic acid/protein complexes, nucleic acid - 65 - WO 2013/106588 PCT/US2013/021056 precipitants, chromosomes, nuclei, mitochondria, chloroplasts, flagella, biominerals, protein complexes, and minicells.
[59] 59. A method of making an article having a slippery surface, comprising: contacting a substrate with a reactive molecule having a head group that is reactive with the substrate and a functional group directly or indirectly attached to the head group to form an anchoring layer on the substrate; and contacting the anchoring layer with a lubricating liquid having an affinity for the functional group to form a lubricating layer disposed over the anchoring layer, wherein the anchoring layer and the lubricating layer are held together by non-covalent attractive forces, wherein the anchoring layer and the lubricating layer form a slippery surface configured and arranged for contact with a material that is immiscible with the lubricating liquid.
[60] 60, The method of claim 59, wherein contacting the anchoring layer with lubricating liquid comprises passing lubricating liquid through micropassages in the substrate.
[61] 61. The method of claim 59, wherein the substrate comprises a reservoir through which lubricating liquid is replenished.
[62] 62. The method of claim 59, wherein the substrate comprises tubing and wherein contacting the anchoring layer with lubricating liquid comprises passing boluses of lubricating liquid through the tube.
[63] 63. The method of claim 59, wherein the lubricating liquid is replenished on the anchoring layer.
[64] 64. A method for reducing coagulation of blood or reducing adhesion or fibrin, fibrinogen, platelets, leukocytes, red blood cells and coagulation factors comprising: contacting or storing blood against a surface that resists coagulation of blood, the surface comprising: - 66 - WO 2013/106588 PCT/US2013/021056 an anchoring layer, the anchoring layer comprising; a head group attached to the substrate and a functional group directly or indirectly attached to the head group; and a lubricating layer comprising a lubricating liquid having an affinity for the functional group and disposed over the anchoring layer, wherein the anchoring layer and the lubricating layer are held together by non-covalent attractive forces,
[65] 65. A method of extracting a solute from a solution comprising: providing a surface comprising an anchoring layer, the anchoring layer comprising a head group attached to the substrate and a functional group directly or indirectly attached to the head group; and a lubricating layer comprising a lubricating liquid having an affinity for the functional group and disposed over the anchoring layer, wherein the anchoring layer and the lubricating layer are held together by non-covalent attractive forces; and contacting the surface with a solution comprising one or more solutes, wherein at least one solute has a greater affinity for the lubricating liquid than the solution. - 67 -

类似技术:

---

公开号 | 公开日 | 专利标题

---

AU2017201081B2|2018-09-27|Modification of surfaces for fluid and solid repellency

---

US10982100B2|2021-04-20|Slippery liquid-infused porous surfaces and biological applications thereof

---

US10245355B2|2019-04-02|Modification of surfaces for fluid and solid repellency

---

Villegas et al.2019|Liquid-infused surfaces: a review of theory, design, and applications

---

US8632877B2|2014-01-21|Ultra-thin photo-polymer coatings and uses thereof

---

US9895470B2|2018-02-20|Non-fouling, anti-microbial, anti-thrombogenic graft—from compositions

---

US20140287016A1|2014-09-25|Immobilization of an active agent on a substrate

---

Mackie et al.2019|Clinical potential of immobilized liquid interfaces: perspectives on biological interactions

同族专利:

---

公开号 | 公开日

---

US20140342954A1|2014-11-20|

---

HK1205753A1|2015-12-24|

---

CA2860934A1|2013-07-18|

---

AU2017201081A1|2017-03-09|

---

KR20140111338A|2014-09-18|

---

WO2013106588A1|2013-07-18|

---

EP3441433A1|2019-02-13|

---

JP2015507507A|2015-03-12|

---

EP3441433B1|2020-06-17|

---

EP2802630B1|2018-05-30|

---

EP2802630A1|2014-11-19|

---

JP6388541B2|2018-09-12|

---

CN104254579B|2018-05-29|

---

AU2013207938B2|2016-11-17|

---

CN104254579A|2014-12-31|

---

AU2017201081B2|2018-09-27|

引用文献:

---

公开号 | 申请日 | 公开日 | 申请人 | 专利标题

---

EP0166998B1|1984-06-04|1991-05-08|TERUMO KABUSHIKI KAISHA trading as TERUMO CORPORATION|Medical instrument and method for making|

---

JPH0133181B2|1984-06-04|1989-07-12|Terumo Corp||

---

JPH01170932A|1987-12-25|1989-07-06|Nippon Sheet Glass Co Ltd|Production with low-friction thin film|

---

US5013717A|1988-04-18|1991-05-07|Becton, Dickinson And Company|Blood compatible, lubricious article and composition and method therefor|

---

GB9026687D0|1990-12-07|1991-01-23|Vascutek Ltd|Process for providing a low-energy surface on a polymer|

---

EP0497204B1|1991-01-28|2001-04-18|Matsushita Electric Industrial Co., Ltd.|Medical member and method of manufacturing the same|

---

CA2060294C|1991-02-06|2000-01-18|Kazufumi Ogawa|Chemically absorbed film and method of manufacturing the same|

---

EP0501298B1|1991-02-27|1996-06-05|Matsushita Electric Industrial Co., Ltd.|Self-lubricating device|

---

WO1993017077A1|1992-02-21|1993-09-02|Dunton Ronald K|Poly coatings|

---

US6887836B2|2002-05-09|2005-05-03|The Procter & Gamble Company|Home care compositions comprising a dicarboxy functionalized polyorganosiloxane|

---

US20070166344A1|2006-01-18|2007-07-19|Xin Qu|Non-leaching surface-active film compositions for microbial adhesion prevention|

---

CA2745204C|2008-12-05|2017-01-03|Semprus Biosciences Corp.|Layered non-fouling, antimicrobial, antithrombogenic coatings|

---

AU2012207205C1|2011-01-19|2016-09-08|President And Fellows Of Harvard College|Slippery surfaces with high pressure stability, optical transparency, and self-healing characteristics|

---

US20130110222A1|2011-08-19|2013-05-02|Joram Slager|Medical devices including superhydrophobic or superoleophobic surfaces|SG10201402278VA|2009-05-13|2014-07-30|Sio2 Medical Products Inc|Pecvd coating using an organosilicon precursor|

---

US9878101B2|2010-11-12|2018-01-30|Sio2 Medical Products, Inc.|Cyclic olefin polymer vessels and vessel coating methods|

---

AU2012207205C1|2011-01-19|2016-09-08|President And Fellows Of Harvard College|Slippery surfaces with high pressure stability, optical transparency, and self-healing characteristics|

---

EP2665783A2|2011-01-19|2013-11-27|President and Fellows of Harvard College|Slippery liquid-infused porous surfaces and biological applications thereof|

---

US11116695B2|2011-11-11|2021-09-14|Sio2 Medical Products, Inc.|Blood sample collection tube|

---

CA2855353C|2011-11-11|2021-01-19|Sio2 Medical Products, Inc.|Passivation, ph protective or lubricity coating for pharmaceutical package, coating process and apparatus|

---

US10780228B2|2012-05-07|2020-09-22|Medline Industries, Inc.|Prefilled container systems|

---

AU2013289879B2|2012-07-12|2017-04-06|President And Fellows Of Harvard College|Slippery self-lubricating polymer surfaces|

---

WO2014012039A1|2012-07-13|2014-01-16|President And Fellows Of Harvard College|Slippery liquid-infused porous surfaces having improved stability|

---

EP2872573A1|2012-07-13|2015-05-20|President and Fellows of Harvard College|Multifunctional repellent materials|

---

EP3327090A1|2012-07-18|2018-05-30|President and Fellows of Harvard College|Modification of surfaces for simulataneous repellency and targeted binding of desired moieties|

---

US9937099B2|2013-03-11|2018-04-10|Sio2 Medical Products, Inc.|Trilayer coated pharmaceutical packaging with low oxygen transmission rate|

---

WO2014164928A1|2013-03-11|2014-10-09|Sio2 Medical Products, Inc.|Coated packaging|

---

WO2014209441A2|2013-03-13|2014-12-31|President And Fellows Of Harvard College|Solidifiable composition for preparation of liquid-infused slippery surfaces and methods of applying|

---

FR3003482B1|2013-03-19|2016-06-24|Aptar France Sas|METHOD FOR SURFACE TREATMENT OF A DOSING VALVE|

---

EP3693493A1|2014-03-28|2020-08-12|SiO2 Medical Products, Inc.|Antistatic coatings for plastic vessels|

---

US10189113B2|2014-04-24|2019-01-29|GM Global Technology Operations LLC|Resistance spot welding method|

---

CN104451811A|2014-11-20|2015-03-25|哈尔滨工程大学|Method for forming super-lubricating surface on metal surface|

---

EP3285927A2|2015-04-22|2018-02-28|Berkeley Lights, Inc.|Freezing and archiving cells on a microfluidic device|

---

SG10202107069UA|2015-10-27|2021-07-29|Berkeley Lights Inc|Microfluidic electrowetting device apparatus having a covalently bound hydrophobic surface|

---

RU2017140844A|2015-04-27|2019-05-27|Те Риджентс Оф Те Юниверсити Оф Мичиган|LONG-TERM ANTI-EDUCATION SURFACE|

---

US11077233B2|2015-08-18|2021-08-03|Sio2 Medical Products, Inc.|Pharmaceutical and other packaging with low oxygen transmission rate|

---

GB2546319B|2016-01-15|2019-07-03|Cook Medical Technologies Llc|Coated medical device and method of coating such a device|

---

EP3463665A4|2016-05-26|2020-03-25|Berkeley Lights, Inc.|Covalently modified surfaces, kits, and methods of preparation and use|

---

US20170349313A1|2016-06-01|2017-12-07|Centurion Medical Products Corporation|Methods for manufacturing non-glass prefilled syringes|

---

WO2018015099A1|2016-07-18|2018-01-25|Unilever N.V.|A method of modifying the dispensing properties of a container|

---

KR102309049B1|2016-09-30|2021-10-07|도레이 카부시키가이샤|Copolymers and medical materials using them|

---

CN110072694A|2016-11-18|2019-07-30|宾夕法尼亚州立大学研究基金会|Repel liquid and visco-elastic material and the coating of anti-biological pollution|

---

KR101912605B1|2017-03-10|2018-10-30|경기대학교 산학협력단|Super-Hydrophobic Particle and Composite having the Same|

---

US10563069B2|2017-03-30|2020-02-18|International Business Machines Corporation|Prevention of biofilm formation|

---

US10507267B2|2017-04-25|2019-12-17|International Business Machines Corporation|Highly hydrophobic antifouling coatings for implantable medical devices|

---

US10696849B2|2017-08-08|2020-06-30|International Business Machines Corporation|Tailorable surface topology for antifouling coatings|

---

US10745586B2|2017-08-08|2020-08-18|International Business Machines Corporation|Fluorinated networks for anti-fouling surfaces|

---

KR102013196B1|2017-11-16|2019-08-22|한양대학교 산학협력단|Method for Preparing Film with Slippery Surfaces|

---

US20200338484A1|2018-01-17|2020-10-29|Chungang University Industry Academic Cooperation Foundation|Dust collection filter target-coated with liquid film|

---

US20200339850A1|2018-02-13|2020-10-29|Central Glass Company, Limited|Chemical solution for forming water-repellent protective film, method for preparing same, and method for manufacturing surface-treated body|

---

CA3098872A1|2018-05-14|2019-11-21|The Penn State Research Foundation|Slippery surfaces on common substrates|

---

US11155732B2|2018-08-21|2021-10-26|Board Of Trustees Of Michigan State University|Biodegradable omniphobic coated articles and method for making|

---

EP3860754A1|2018-10-02|2021-08-11|President and Fellows of Harvard College|Hydrophobic barrier layer for ceramic indirect evaporative cooling systems|

---

CN109304228A|2018-11-21|2019-02-05|晶准生物医学（深圳）有限公司|The surface modification method and micro fluidic device of PDMS substrate|

---

CN109837028B|2019-02-21|2021-11-26|宁波激智科技股份有限公司|Transparent paint surface protective film and application thereof|

---

CN110424000B|2019-07-02|2021-02-12|重庆大学|Preparation method of beaded condensation surface with intelligent self-driving characteristic|

---

WO2021183575A1|2020-03-09|2021-09-16|Massachusetts Institute Of Technology|Composite anti-fouling coatings and associated systems and methods|

法律状态:
2017-03-16| FGA| Letters patent sealed or granted (standard patent)|

优先权:

---

申请号 | 申请日 | 专利标题

---

US201261585059P| true| 2012-01-10|2012-01-10||

---

US61/585,059||2012-01-10||

---

US201261671442P| true| 2012-07-13|2012-07-13||

---

US201261671645P| true| 2012-07-13|2012-07-13||

---

US61/671,645||2012-07-13||

---

US61/671,442||2012-07-13||

---

US201261692079P| true| 2012-08-22|2012-08-22||

---

US61/692,079||2012-08-22||

---

PCT/US2013/021056|WO2013106588A1|2012-01-10|2013-01-10|Modification of surfaces for fluid and solid repellency|AU2017201081A| AU2017201081B2|2012-01-10|2017-02-17|Modification of surfaces for fluid and solid repellency|