    • 专利摘要:
    Abstract Disclosed is an alkyd or hydrocarbon resin-based pre-manufactured thermoplastic airport runway signage that is applied in relatively large sections onto an airport runway where the 5 alkyd or hydrocarbon resin-based composite includes a functionalized wax incorporated in the resin-based composite within the range of 0.2 to 3 percent by weight, thereby allowing the resin-based composite to exist in a molten state within a viscosity range of between 35,000 and 85,000 centipoise and wherein the top surface provides an area for surface indicia materials existing on the top surface together with retroreflective glass beads with an index of 10 refraction of 1.9 such that when the beads are suspended in and applied on the surface of the resin-based composite in a molten state the beads do not sink into the resin-based composite provide for allowing and maintaining an overall retroreflectivity of about 1000 millicandellas/m 2/lux (mcd). Page 18 of 18
    公开号:AU2013200560A1
    申请号:U2013200560
    申请日:2011-09-22
    公开日:2013-04-04
    发明作者:Catherine Binder；Robert W. Greer；Simon Yakopson
    申请人:Flint Trading Inc；
    IPC主号:E01F9-04
    专利说明:
    Invention Disclosure Anti-Skid High Retroreflectivity Preformed Thermoplastic Composites for Runway Applications 5 Priority This application takes priority under 35 USC 120 from US patent application number 11/732,056 filed on April 2, 2007 which resulted in granted US patent number 7,744,306. In addition, the entire contents of US patent number 7,744,306 is hereby incorporated by reference. 10 Field of Invention The present invention relates to preformed thermoplastic surface guidance indicia that are applied to runways and taxiways to convey information to aircraft and aircraft support operators. More specifically, the invention involves the additional features of high 15 retroreflectivity and anti-skid properties while maintaining the necessary bonding characteristics to ensure the indicia is properly adhered to the runway and taxiway surfaces. Background of Invention Airport pavement indicia and signs provide information that is useful to a pilot during 20 takeoff, landing, and taxiing. Generally airport indicia are grouped into four categories: runway indicia, taxiway indicia, holding position indicia, and other indicia. Indicia for runways are white. Indicia for taxiways, areas not intended for use by aircraft (closed and hazardous areas), and holding positions (even if they are on a runway) are yellow. Indicia for heliports are white with the exception of medical helicopter areas which are white with a red 25 cross. Presently much of the runway and taxiway information is painted onto the concrete or asphalt. This paint may last for several weeks or several months depending on the amount of use, the size of the aircraft traffic using it and/or severity of environmental conditions. 30 It has been found that uniformity in airport indicia and signs from one airport to another enhances safety and improves efficiency. FAA Standards AC 150/5340-1 "Standards for Airport Indicia" and AC 150/5340-18 "Standards for Airport Sign Systems" are both Page 1 of 18 references that define the minimum requirements for airport indicia and signage. Non maintenance of painted indicia may allow indicia to become deteriorated to a point where the information being conveyed is confusing or illegible. 5 Runway indicia may also be divided into the following groups: visual runway indicia, non precision instrument indicia and precision instrument indicia. Additional indicia are required for runway lengths over 4000 feet and for runways serving international commercial transports. 10 Maintenance of the painted surfaces require that runways and taxiways be shut down while the surface is prepared, paint applied and for curing time. Maintenance of a particular runway may impact the holding and taxiways of adjacent or intersecting pavement. The pavement warnings of adjacent or intersecting pavement must change to denote changes in holding areas, and thresholds to avoid ground collisions with other aircraft. 15 Presently many airports have allocated budgets for painting the warning, identification and directional indicia. Painting the runway surfaces is performed on a rotational basis of about every three weeks depending on the volume and size of the aircraft traffic. Although the painting of the runway surface is relatively quick, the runway traffic needs to be rerouted to 20 other runways causing flight delays while the painting and drying of the painting occurs. It also is expensive in that full time painting crews are continually rotating from runway to runway. Ground safety remains a problem at busy airports across the United States and the world. The 25 movement of aircraft in and around busy airports along taxiways between terminal gates and runways presents numerous opportunities for runway incursions, particularly when visibility is poor. A runway incursion is the entry of an aircraft without clearance onto an active runway from an adjacent ramp or taxiway, for which there is a great deal of risk of collision with a landing or departing aircraft. Incursions are often the inadvertent result of pilot 30 disorientation caused by poor visibility. Page 2 of 18 As recently as August 26, 2006, Comair Flight 5191 crashed about half a mile past the end of a runway at the Lexington, Kentucky airport, killing 49 of the 50 people onboard. The plane took off on runway 26, not runway 22 where it was assigned. It was an early morning flight with overcast skies and a slight rain. The NTSB probe is focusing their investigation on 5 recent construction work at the Lexington airport, lighting and the indicia on the taxiways and runways. This does not include incidents such as taxiway collisions or near misses resulting from vehicle operators mistaking one taxiway for another. Runway incursions and other taxiway 10 incidents can still represent inconvenience and expense even when a ground collision does not result. To return an aircraft to a path from which it has strayed requires a considerable expenditure of time and fuel, and a compromise to the safety of all involved. In addition to the need for runway signage that is relatively simply and quick to apply and 15 that exhibits exceptional wear characteristics as well as allowing for delayed intervening scheduled maintenance, thereby assisting with the reduction of the cost of maintenance, delayed flights and confusion due to runway rerouting, the signage should also be highly retroreflective and skid resistant. 20 Specifically, the need for high retroreflectivity nighttime visinility has been increased to near or about 1000 millicandellas/m 2 /lux (mcd) and this high retroreflectivity requires glass beads that must remain at or near the top surface of the signage to ensure that the retroreflectivity is maintained during and after installation. To create the proper composition requires a specific composition of the alkyd-based preformed thermoplastic composite which is one 25 embodiment of the present disclosure. Description of Related Art 30 US Patent No. 7744306 to Greer, et. al., is hereby incorporated by reference and describes an alkyd resin-based pre-manufactured thermoplastic airport runway signage that is applied in relatively large sections onto an airport runway. The pre-manufactured preformed Page 3 of 18 thermoplastic formed as a continuous sheet and wound onto a take-up spool. The runway surface is prepared with a two part primer with a viscosity in the range of 1-300 cps at room temperature and the preformed thermoplastic is unwound from the take-up spool and positioned onto the runway surface. 5 U.S. Patent No. 7,175,362 to Carr, et. al., and unassigned describes a runway/taxiway system comprising a synthetic covering securely installed to an anchor positioned against but not attached to a runway/taxiway so that an edge of the covering is adjacent to an edge of the 10 runway/taxiway and a growth retarding base placed beneath the synthetic covering and along a second side of the anchor with the base holding the anchor against the runway/taxiway. U.S. Patent No. 5,288,163 to Munson, William D, and unassigned describes a method for identifying airport taxiways and taxiway intersections by indicia a first taxiway with a 15 continuous elongated row of first indicia identifying the first taxiway and indicia the first taxiway with a continuous elongated row of second indicia identifying an intersection with a runway or second taxiway beginning at least 100 feet in advance of the intersection. The spacing between the second indicia decreases with proximity to the intersection indicia the intersection along the route to be traversed between the first taxiway and the runway of 20 second taxiway with a row of second indicia and indicia the runway or second taxiway with a row of second indicia after the intersection. The spacing between the second indicia increases with proximity to the intersection and said row of second indicia extends substantially along the centerline of the runway or second taxiway. 25 U.S. Patent Application No. 2003/0070579A1 (abandoned) to Hong, et. al., and unassigned describes a pavement indicia construction comprising a flexible layer with top and bottom surfaces. The top surface of the flexible layer is adapted for vehicular and pedestrian traffic with the flexible layer comprising at least one thermoplastic elastomer, at least one resin and a wax. The resin is substantially miscible with the thermoplastic elastomer upon cooling from 30 a molten state and an adhesive lower layer adjacent the bottom surface of the flexible layer is adapted to adhere the flexible layer to a pavement surface. Page 4 of 18 WIPO Publication No. W09828372A1 to Rogers, Barry Heith, and unassigned describes an indicia composition comprising a binder component and a reflective component comprising thin sheets or pieces of material which are essentially reflective. 5 Japanese Publication No. JP1 1209909A2 to Fikute, et. al., and assigned to Port & Harbour Res Inst Ministry of Transport describes a paving structure for paving an airport and its construction method which is excellent in torsion resistance, and dispenses with the provision of a joint and heating in the case of execution. A room temperature asphalt mixture including an aggregate, an asphalt emulsion mixed with the aggregate in a state where a volume is 10 increased by bubbling and a hydraulic setting inorganic material is paved, and after paving, a thermoplastic high-molecular polymer is supplied on the room temperature asphalt mixture and rollingly pressed to form a surface layer integrated with the paved room temperature asphalt mixture. Thus, a paving structure for paving an airport constructed in this way can be provided. 15 Summary of the Invention Specifically, the need for high retroreflectivity nighttime visibility has been increased to near or about 1000 millicandellas/m 2 /lux (mcd) and this high retroreflectivity requires glass beads 20 that must remain at or near the top surface of the signage to ensure that the retroreflectivity is maintained during and after installation. To create the proper composition requires a specific composition of the alkyd-based preformed thermoplastic composite which is one embodiment of the present disclosure. In addition, there still exists the need for runway signage that is relatively simple and quick to apply and that exhibits exceptional wear 25 characteristics as well as allowing for delayed intervening scheduled maintenance, thereby assisting with the reduction of the cost of maintenance, delayed flights and confusion due to runway rerouting, and the signage should maintain skid resistance together with the increased retroreflectivity. Page 5 of 18 AirMarkR is an airport runway signage device that comprises an alkyd resin-based preformed thermoplastic which may be laid out in 90'x120' sections onto airport runways. The original AirMark formula used conventional 1.5 index beads of types I and IV from the table I below: 5 Table I. Glass Bead Gradation (Percent By Weight, Passing, ASTM D1214) Type I Type III Type IV U.S. Microns A B A B Sieve # Min Max Min Max Min Max Min Max Min Max 12 1700 --- --- --- --- --- --- 100 --- 100 -- 14 1400 --- --- --- --- --- --- 95 100 -- -- 16 1180 --- --- --- --- 100 --- 80 95 95 100 18 1000 --- --- --- --- --- --- 10 40 --- -- 20 850 100 --- --- --- 95 100 0 5 35 70 30 600 80 100 --- --- 55 75 --- --- 0 5 40 425 --- --- --- --- 15 35 --- --- --- -- 50 300 18 35 --- --- 0 5 --- --- --- -- 70 212 --- --- 100 --- --- --- --- --- --- -- 80 180 --- --- 85 100 --- --- --- --- --- -- 100 150 0 10 --- --- --- --- --- --- --- -- 140 106 --- --- 15 55 --- --- --- --- --- -- 200 75 0 2 --- --- --- --- --- --- --- -- 230 63 --- _- --- 0 10 --- I _--- --- --- --- --- Table 1 above is from the Federal Aviation Administration's TT-B-1325D Federal Specification Test-pretee4 regarding the use of glass beads with pavement marking. The 10 specification below indicates the both the bead type and correspondence with the features of each bead type. To comply with the specification, the percent of beads passed through the specified sieve should be in the stated in the table limits. The FAA TT-B-1325D Test Bead Categorization is as follows: 15 Type I - Low Index of Refraction recycled glass (fire-polished process) Gradation A (Coarse, Drop-on) Gradation B (Fine, Premix) Page 6 of 18 Type III - High Index of Refraction Type IV - Low Index of Refraction direct melt glass (molten glass kiln process) 5 Gradation A (Large Coarse, Drop-on) Gradation B (Medium Coarse, Drop-on) The density of these (low index of refraction) beads is near or about 2.6 grams per cubic centimeter. This "first generation" AirMarkR produced white retroretroreflectivity in the 100-200 mcd range, essentially an order of magnitude below the standard required and 10 reached by use of the new composite described herewithin. Initially, the high index of refraction (1.9) glass beads (Type III) were provided in the original AirMark formulation and used as drop-on beads. The very surprising result is that less retroreflectivity than the conventional 1.5 index beads occurred (less than 100 mcd). It 15 was discovered that these higher reflectivity beads sank faster in the performed thermoplastic composite due to their higher density (approximately 4 grams per cubic centimeter). The need to use these higher retroreflectivity beads, however, remains. As with the original AirMarkR , this new composite may also be initially rolled and then 20 melted onto the runway surface using an 8 foot to 16 foot wide IR heater. Hand held propane torches may also be used, such as the Flint 2000EX, available from Flint Trading, Inc. The material thickness of this runway signage is nominally .060 inches. The signage without high retroreflectivity and anti-skid properties has a backing that is relatively thin and flexible and normally utilizes a relatively low viscosity (50-500 centipoise - cps) two component primer, 25 such as an epoxy primer. An embodiment of the present disclosure, however, requires the need and use of a two part epoxy primer which is nominally in the narrow viscosity range of 50-500 cps at room temperature for ensuring proper and optimal bonding to a runway or taxiway surface. Lower 30 or higher viscosity epoxy primers do not work well for the present disclosure and associated invention due to the change in the functional composition/composite of the runway/taxiway signage. This composition/composite is described, in detail, below; Page 7 of 18 Specifically, a further embodiment requires that the composition of the preformed thermoplastic sheets must include TT-B 1325D Type III glass beads comprised of a barium based glass chemistry such as those sold by Potters Industries, Inc. with a particle size distribution of between 300 and 1180 microns and exhibiting a density in the range of 3.5-4.5 5 gm/cc and an index of refraction of 1.9, within a preformed thermoplastic resin that incorporates the use of a functionalized wax, such as an oxidized microcrystalline wax or a maleic anhydride functionalized wax, or an acrylic acid copolymer with a weight average molecular weight of less than 10,000. An example of an ethylene maleic anhydride copolymer wax is sold by Honeywell Corporation under the tradename of AC 575. It is 10 incorporated in the range of 0.2-3.0 percent by weight of the preformed thermoplastic resin. The wax provides stability of the viscosity of the preformed thermoplastic over a substantially wide temperature range (120-200'C) as opposed to compositions not including the use of such waxes. The glass beads must be suspended in the preformed thermoplastic resin and also there must be an allowance for spreading the same beads onto the surface 15 during the application of the signage to the surface. These beads must not sink into the preformed thermoplastic during heating and application in order to maintain a retroreflectivity of at or about 1000 millicandellas/m 2 /lux (mcd). This retroreflectivity light intensity measurement has been required for most new airport installations in our effort to enhance safety. These beads have been known in the art but have seen limited application 20 due to their higher cost and the fact that they scratch easily and do not hold up to high average daily traffic (ADT) when used with painted or other surface indicia. Use of the beads together with the preformed thermoplastics (either mixed into the resin composition or spread across the surface during installation) has not been known or used prior to this disclosure 25 A preferred embodiment is that the functionalized wax be used in a range of 0.3 to 0.5 percent by weight of the preformed thermoplastic resin. An additional embodiment provides for a preformed thermoplastic is an alkyd resin-based 30 pre-manufactured thermoplastic airport runway signage that is laid out in relatively large sections onto an airport runway. The preformed thermoplastic is initially formed as a Page 8 of 18 continuous sheet and wound onto a take-up spool. To acquire the reflective properties necessary, glass beads with specific sizes such as described in the Federal Aviation Administration (FAA) document TT-B-1325 D, issued June 1, 1993, are both embedded within the sheet and also strategically placed over the sheet during the heating and 5 installation procedure which is described in the next paragraph. In addition to retroreflectivity, skid resistance, which in this case is defined as the raising of the surface friction coefficient of the preformed thermoplastic indicia layer onto the runway/taxiway to prevent slippage of airport personnel, must also be increased. During 10 moist or wet weather conditions, there have been worker accidents attributed to slick painted indicia as well as for preformed thermoplastic AirMarkR signage. Use of anti-skid materials within the preformed thermoplastic sheets including corundum, quartz, sand, etc., all of which are used to increase the coefficient of friction , but must be achieved within the set of parameters as described above, namely the preformed thermoplastic sheets in the molten 15 state, must exhibit a viscosity of between 35,000 and 85,000 cps during installation. This molten state is normally achieved at or about 150 degrees Centigrade or generally above 300 degrees Fahrenheit, and with the incorporation of the anti-skid materials, optimization of the viscosity is more difficult to achieve. A lower viscosity composite will allow the glass beads to sink and thereby greatly diminish or eliminate retroreflectivity intensity, while a higher 20 viscosity preformed thermoplastic will not sufficiently bond with the runway/taxiway surface. The runway surface is prepared with the two-part epoxy primer and the preformed thermoplastic is unwound from the take-up spool and positioned onto the runway surface. 25 When the preformed thermoplastic signage is in a desired location it is initially rolled conforming to the runway surface. Heat is applied to the rolled surface to a temperature of or about 300'F degrees with this particular preformed plastic sheet composition. Fusing with a wide infra-red (IR) heater to melt the preformed thermoplastic signage into the runway surface allows for adhering the preformed thermoplastic signage to the runway surface. 30 Page 9 of 18 The modified formulation and resulting composition of the present disclosure increases the viscosity of the preformed thermoplastic in order to retard bead sinking. Non-conventional two- part epoxy sealers were necessary (within a narrow - 50-500 cps range at room temperature) were required so that optimal bonding together with optimal 5 retroretroreflectivity could be obtained. In an additional embodiment the pre-manufactured thermoplastic signage is flexible and the material thickness is in a range of .050 inches-.075 inches with a nominal thickness of .060". 10 Additionally the pre-manufactured thermoplastic signage that is manufactured may be shipped as 90 foot x 120 foot sections composed of individual 3 foot x 2 foot sheets of material. Another embodiment includes the ability of the large pre-manufactured thermoplastic 15 signage to be installed quickly and easily to concrete or asphalt surfaces. In another embodiment the pre-manufactured thermoplastic signage may also be applied to fresh asphalt surfaces as soon as the asphalt has cured to a "set". 20 An additional embodiment includes the fact that the pre-manufactured thermoplastic signage may have features such as indents, bumps or marks that are visible indicators such that correct adhesion temperature are attained by the infra-red or other heating means used by those skilled in the art. 25 In an additional embodiment, the pre-manufactured thermoplastic signage is an alkyd thermoplastic product with the addition of a polyurethane composition for flexibility and impact resistance. The polyurethane can be aliphatic or aromatic in combination with either polyester or polyether functionality. The polyurethane must have a suitable viscosity to be used with a typical range at 190'C which provides a viscosity of between 46 Pa-s to 120.9 30 Pa-s (46,000 cps to 120,900 cps). Page 10 of 18 In another embodiment the pre-manufactured thermoplastic signage is prepared to meet specific lengths and widths conforming with FAA Standards AC 150/5340-1 "Standards for Airport Indicia" and AC 150/5340-18 "Standards for Airport Sign Systems" for touchdown indicia, threshold indicia configurations, aiming point indicia and centerlines, as 5 requirements for precision instrument runways. In yet another embodiment the pre-manufactured thermoplastic signage is provided as alpha numeric symbols for specific information signage that is applied to the runway, taxiway or holding surface. 10 In another embodiment the pre-manufactured thermoplastic signage is available in various colors or hues. In another embodiment the pre-manufactured thermoplastic signage has features that allow 15 the edges to physically interconnect and interlock. An embodiment of the disclosure is that the pre-manufactured thermoplastic signage is available for traffic within minutes of adhering the specific signage. 20 Additionally as another embodiment, the pre-manufactured thermoplastic signage identifies areas for aircraft support vehicles or outdoor passenger loading in non-runway areas. An additional embodiment for the pre-manufactured thermoplastic signage identifies specific helicopter landing and takeoff areas including medical transport. 25 Brief Description of the Drawings Figure 1 is an isometric cross-section of the pre-manufactured thermoplastic signage with optional temperature indicating features. 30 Page 11 of 18 Detailed Description of the Drawings Figure 1 is an isometric cross section of the thermoplastic signage [100] with temperature indicating feature such as, but not limited to, an indent [110], a dimple [120] or a bump [130] 5 or any other heat deformable marker that visibly deforms when heating elevates the temperature of the thermoplastic signage [100] to a desired temperature. When the desired temperature is reached the temperature indicating feature [110, 120, 130] visibly reforms becoming a blended surface according to the traffic surface shape to which it applied. Adhesive [140] is relatively thin and flexible and utilizes a low viscosity (50-500 cP) 10 polyurea epoxy primer such as is available from ChemCo Systems. Page 12 of 18
    权利要求:
    Claims (20)
    [1] 2. The pre-manufactured preformed thermoplastic signage of claim 1, wherein said molten state is achieved at or about 150 degrees Centigrade.
    [2] 3. The pre-manufactured preformed thermoplastic signage of claim 1, wherein said 5 functionalized wax has a weight average molecular weight of less than 10,000.
    [3] 4. The pre-manufactured preformed thermoplastic signage of claim 1, wherein said functionalized wax is of an ethylene maleic anhydride copolymer variety including the wax R known as AC 575 10
    [4] 5. The pre-manufactured preformed thermoplastic signage of claim 1, wherein said wax is present in a range of 0.3 to 0.5 percent by weight of said alkyd resin-based composite.
    [5] 6. The pre-manufactured preformed thermoplastic signage of claim 1, wherein anti-skid 15 particles are also incorporated into said resin-based composite such that preformed thermoplastic sheets include corundum, quartz, sand, and other anti-skid materials thereby increasing the coefficient of friction on the surface of said thermoplastic signage.
    [6] 7. The thermoplastic signage of claim 1, wherein said spool is subsequently unwound such 20 that said signage is rolled and positioned to conform to said large substrates.
    [7] 8. The thermoplastic signage of claim 1, wherein said signage is provided in sheets rather than spooled thereby providing smaller substrate sections that are shipped in boxes for convenience during installation. 25
    [8] 9. The thermoplastic signage as in claim 1, wherein said large substrates include concrete or asphalt.
    [9] 10. The thermoplastic signage as in claim 1, wherein said large substrates are a runway, 30 taxiway, holding position or other airport surfaces. Page 14 of 18
    [10] 11. The thermoplastic signage as in claim 1, wherein said resin-based composite is flexible and conformal, and said composite is present in a thickness range of about 0.050 inches to about 0.075 inches. 5 12. The thermoplastic signage as in claim 1, wherein said resin-based composite is 0.060 inches thick, flexible and conformal to substrate surfaces.
    [11] 13. The thermoplastic signage as in claim 1, wherein said resin-based composite and associated indicia is applied to fresh asphalt immediately after curing. 10
    [12] 14. The thermoplastic signage as in claim 1, wherein said resin-based composite is heated to said predetermined temperature using infra-red heaters or other heating devices and techniques necessary to achieve said predetermined temperature to ensure precision application and bonding of said thermoplastic signage with said aviation substrates. 15
    [13] 15. The thermoplastic signage as in claim 1, where said resin-based composite is an alkyd based thermoplastic composition with the addition of an aliphatic or aromatic polyether or polyester based polyurethane composition that imparts flexibility and impact resistance to the solid sheet form of said thermoplastic signage. 20
    [14] 16. The thermoplastic signage as in claim 1, wherein said resin-based composite is cut to specific lengths and widths conforming with FAA Standards AC 150/53404-1 and AC 150/5340-18 included for touchdown indicia, threshold indicia configurations, aiming point indicia, and centerlines for precision instrument runways. 25
    [15] 17. The thermoplastic signage as in claim 1, wherein said signage includes an alphanumeric symbol on said area for surface indicia materials existing on said top surface.
    [16] 18. The thermoplastic signage as in claim 1, wherein said resin-based compositions and 30 signage is comprised of various colors and hue(s) integral and permanently molded in the resin-based composition. Page 15 of 18
    [17] 19. The thermoplastic signage as in claim 1, wherein said large surfaces of said signage is trafficked within minutes after adhering said signage to any suitable aviation associated substrate. 5
    [18] 20. The thermoplastic signage as in claim 1, wherein said signage displays specific helicopter landing and takeoff indicia including medical transport indicia.
    [19] 21. The thermoplastic signage as in claim 1, wherein said predetermined temperature to 10 ensure proper and optimal adhesion between said signage and any suitable aviation associated substrate is about 400 degrees Fahrenheit.
    [20] 22. A method for adhering large surfaces of thermoplastic signage to a suitable aviation substrate comprising; an alkyd or hydrocarbon resin-based composite wherein said large 15 substrates include a bottom surface and a top surface and edges that surround the perimeter of and are attached to said bottom surface and said top surface, wherein said bottom surface is covered with a two- part sealer treatment; said sealer treatment provided within a viscosity range of between 50 and 500 centipoise for optimal bonding of said alkyd or hydrocarbon resin based composite to said large substrate, wherein said composite includes a 20 functionalized wax incorporated in said resin-based composite within the range of 0.2 to 3 percent by weight, thereby allowing said resin-based composite to exist in a molten state within a viscosity range of between 35,000 and 85,000 centipoise and wherein said top surface provides an area for surface indicia materials existing on said top surface together with retroreflective glass beads, wherein said glass beads are within a particle size 25 distribution of between 300 and 1180 microns and within a density range of 3.5 to 4.5 grams per cubic centimeter, and wherein said beads exhibit an index of refraction of 1.9 such that when said beads are suspended in and applied on the surface of said resin-based composite in said molten state such that said beads do not sink into said resin-based composite and said beads allow for maintaining an overall retroretroreflectivity of about 1000 30 millicandellas/m 2 /lux (mcd), and wherein said resin-based composite is forming a continuous sheet wound onto a take-up spool and wherein said resin-based composite is subsequently Page 16 of 18 unwound providing positioning and conformity to said large substrates and subsequently heating said signage to a predetermined temperature providing optimal adhesion of said resin-based composite to said large substrate; and wherein said signage includes features allowing said edges of said signage to physically interconnect and interlock with edges of 5 other signage with the same or other features allowing for winding or unwinding of said continuous sheet from spools for specific transportation and site placement. Page 17 of 18
    类似技术:
    公开号 | 公开日 | 专利标题
    USRE44184E1|2013-04-30|Preformed thermoplastic indicia for airport runways and taxiways
    US8950971B2|2015-02-10|Composition and system for preformed thermoplastic road marking with sequential features
    US20170306576A1|2017-10-26|Preformed Thermoplastic Pavement Marking and Method Utilizing Large Aggregate for Improved Long Term Skid Resistance and Reduced Tire Tracking
    US20180313046A1|2018-11-01|Durable Debris and Alkaline Resistant Preformed Thermoplastic Runway Pavement Marking Compositions
    US20150140294A1|2015-05-21|Preformed Thermoplastic Pavement Marking and Method for High Skid Resistance with Maintained High Retroreflectivity
    US20180080185A1|2018-03-22|Anti-Skid High Retroreflectivity Preformed Thermoplastic Composites for Runway Applications
    CA2988899A1|2016-12-15|Durable debris and alkaline resistant preformed thermoplastic runway pavement marking compositions
    WO2016081078A1|2016-05-26|Preformed thermoplastic pavement marking and method for high skid resistance with maintained high retroreflectivity
    US11242660B1|2022-02-08|Preformed reflective line marking for roadways and associated methods thereof
    US20210246618A1|2021-08-12|Preformed Reflective Line Marking for Roadways and Associated Methods Thereof
    WO2015053743A2|2015-04-16|Composition and system for preformed thermoplastic road marking with sequential features
    同族专利:
    公开号 | 公开日
    CN104011296B|2016-10-19|
    US20180313046A1|2018-11-01|
    AU2013200560B2|2015-11-19|
    EP2758601A1|2014-07-30|
    PT2758601T|2017-12-01|
    BR112013013456A2|2020-11-03|
    EP2758601A4|2015-08-05|
    CA2794647C|2018-10-16|
    US9951486B2|2018-04-24|
    NO2758601T3|2018-01-20|
    DK2758601T3|2017-12-04|
    WO2013043178A1|2013-03-28|
    US20160186396A1|2016-06-30|
    CA2794647A1|2013-03-22|
    MX340578B|2016-07-13|
    MX2012011238A|2013-10-04|
    ES2647417T3|2017-12-21|
    CN104011296A|2014-08-27|
    EP2758601B1|2017-08-23|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US2897733A|1955-12-22|1959-08-04|Baltimore Paint & Color Works|Traffic marker, material, and method|
    JPS534856B2|1975-02-06|1978-02-21|||
    US4497941A|1981-10-16|1985-02-05|Exxon Research & Engineering Co.|Ethylene copolymers for hot melt systems|
    US5194113A|1990-12-24|1993-03-16|Minnesota Mining And Manufacturing Company|Process for making conformable thermoplastic marking sheet|
    US5288163A|1991-06-20|1994-02-22|Munson William D|Airport pavement marking system for surface movement guidance|
    CN1131403A|1993-09-20|1996-09-18|美国3M公司|Pavement marking material and base sheet|
    US6692566B2|1994-02-16|2004-02-17|Beadcrete Pty, Ltd.|Surface finish of cementitious nature and containing glass beads|
    CN1189867A|1995-06-29|1998-08-05|美国3M公司|Wide range vertical retroreflective delineator and method for making it|
    CN1133316A|1996-01-29|1996-10-16|郑振乾|Light reflection sign for road and adhesion agent preparation method|
    SE506055C2|1996-02-19|1997-11-03|Cleanosol Int Ab|Prefabricated coating mainly consisting of thermoplastic material for roads, parking spaces etc.|
    AUPO430296A0|1996-12-20|1997-01-23|Rogers, Barry Heith|Marking composition|
    CN1241158A|1996-12-23|2000-01-12|美国3M公司|Conformable marker sheet|
    BR9810107A|1997-06-13|2000-10-17|Eastman Chem Co|Compositions of traffic beacon of hot fusion, yellow|
    HU224066B1|1997-10-21|2005-05-30|The Dow Chemical Co.|Thermoplastic marking compositions|
    JP3438065B2|1998-01-27|2003-08-18|独立行政法人港湾空港技術研究所|Airport pavement pavement structure and its construction method|
    WO2001042349A1|1999-12-10|2001-06-14|Abildgaard Roadvision Aps|A reflective road marking and a method of producing and applying a reflective road marking composition|
    DE10044300A1|2000-09-07|2002-04-04|Ernst B Buechner|Retroreflective coating system for horizontal markings on roads and other traffic areas is based on one- or two-component composition containing white and colored pigment and strewn with glass and sharp-edged particles|
    US6492521B2|2000-11-03|2002-12-10|Cytec Technology Corp.|Hindered amine light stabilizers based on multi-functional carbonyl compounds and methods of making same|
    WO2002103115A2|2000-11-30|2002-12-27|Avturf L.L.C.|Artificial turf for an airport filed|
    US20020115752A1|2001-02-21|2002-08-22|Basf Corporation|Asphalt-based formulation and method of making and using same for paving applications|
    US20030012599A1|2001-06-29|2003-01-16|Magnus Wallgren|Markings on roads with a fixed road surface, such as asphalt, concrete or the like for motor vehicles|
    US7169831B2|2001-09-27|2007-01-30|3M Innovative Properties Company|Pavement marking composition comprising ceramic fibers|
    US20030070579A1|2001-10-01|2003-04-17|Hong Le Hoa|Preformed thermoplastic pavement marking construction|
    US7179531B2|2002-09-12|2007-02-20|Rohm And Haas Company|Polymer particles having select pendant groups and composition prepared therefrom|
    MXPA06004844A|2003-11-06|2006-07-06|3M Innovative Properties Co|Retroreflective elements comprising a bonded resin core and pavement markings.|
    US7317051B2|2003-11-14|2008-01-08|Chem Link|Moisture curable sealer and adhesive composition|
    US9732481B2|2004-04-02|2017-08-15|Flint Trading, Inc.|Preformed thermoplastic pavement marking and method utilizing large aggregate for improved long term skid resistance and reduced tire tracking|
    DE102004048536B4|2004-10-06|2008-09-18|Clariant Produkte Gmbh|Use of hot melt compounds in road markings|
    TW200630449A|2004-12-21|2006-09-01|Dow Global Technologies Inc|Polypropylene-based adhesive compositions|
    US7744306B2|2007-04-02|2010-06-29|Greer Robert F|Preformed thermoplastic indicia for airport runways and taxiways|
    US8573882B2|2009-11-25|2013-11-05|Robert W. Greer|Composition and system for preformed thermoplastic road marking with sequential features|
    US9080296B2|2013-03-15|2015-07-14|Flint Trading, Inc.|Alkali resistant preformed thermoplastic pavement marking composition|AR111452A1|2017-04-07|2019-07-17|Henkel IP & Holding GmbH|HIGH PERFORMANCE THERMOPLASTIC ADHESIVES AND THEIR USES|
    US20200095739A1|2018-09-25|2020-03-26|Potters Industries, Llc|Thermoplastic pavement marking composition|
    CN109503943A|2018-11-23|2019-03-22|福建乐动体育场材料有限公司|A kind of anti-aging athletic tracks material|
    法律状态:
    2016-03-17| FGA| Letters patent sealed or granted (standard patent)|
    优先权:
    申请号 | 申请日 | 专利标题
    PCT/US2011/052733|WO2013043178A1|2011-09-22|2011-09-22|Anti-skid high retroreflectivity preformed thermoplastic composites for runway applications|
    [返回顶部]