    • 专利摘要:
    Provided is a comprehensive utilization method for a biomass containing amorphous silicon dioxide. The method comprises: pyrolyzing the biomass under anaerobic conditions, collecting the pyrolyzed gas produced; and then calcining under aerobic conditions so as to obtain the amorphous silicon dioxide. The biomass is rice hulls.
    公开号:AU2012364501A1
    申请号:U2012364501
    申请日:2012-12-27
    公开日:2014-08-21
    发明作者:Minxia Cao；Hong Li；Qi RAO；Yanfeng Zhang
    申请人:Wuhan Kaidi Engineering Technology Research Institute Co Ltd；
    IPC主号:C01B33-12
    专利说明:
    PCT/CN2012/087604 COMPREHENSIVE UTILIZATION METHOD FOR BIOMASS CONTAINING AMORPHOUS SILICON DIOXIDE FIELD OF THE INVENTION [0001] The invention relates to the application of biomass, and more particularly to a method forpreparation of amorphous silica (silicon dioxide) from biomass. BACKGROUND OF THE INVENTION [0002] Although silica is abundant in natural resources, the high purity of amorphous silica is hardly found. Conventional methods for preparation of amorphous silica from inorganic materials involve high production costs, large energy consumption, and serious environmental pollution. Chinese Pat. No. ZL02807291. X discloses a method for preparation of high purity of amorphous silica from biomass, such as rice hull, but the coefficient of utilization of organic matters and energy is rather low. SUMMARY OF THE INVENTION [0003] It is one objective of the invention to provide a method for preparation of amorphous silica from biomass. [0004] To achieve the above objective, in accordance with one embodiment of the invention, there is provided amethod for preparation of amorphous silica from biomass. The method comprises pyrolyzing the biomass under anaerobic conditions to yield pyrolysis gas and solid residues, collecting the pyrolysis gas, and calcining the solid 1 PCT/CN2012/087604 residues under aerobic conditions to yield amorphous silica. [0005] In a class of this embodiment, the biomass containing amorphous silica is rice hull. [0006] In a class of this embodiment, the method further comprises step A: acid-washing and drying the biomass before the pyrolysis of the biomass, or step B: acid-washing and drying the biomass after the pyrolysis of the biomass.The acid-washing and drying of the biomass before the pyrolysis of the biomass can transform metallic elements therein into soluble metal salts, which facilitates the removal of the metallic elements by water washing. Meanwhile, the long chain organic matters of the biomass are reduced, whichfacilitates the subsequent pyrolysis. [0007] In a class of this embodiment, the acid-washing and drying of the biomass comprises soaking the biomass in an acid solution at normal temperature for between 8 and 24 hours, or at between 80 and 100'C for between 2 and 6 hours, washing the biomass to be neutral, and drying the biomass. [0008] In a class of this embodiment, the acid solution is hydrochloric acid, sulfuric acid, or nitric acid, and a weight concentration thereof is between 3 and 10 wt. %. [0009] In a class of this embodiment, the biomass is pyrolyzed at a temperature of between 500 and 1000'C. [0010] In a class of this embodiment, the pyrolysis gas comprises CO, C0 2 , H 2 , CH 4 ,
    C
    2
    H
    2 , C 2
    H
    4 , C 2
    H
    6 , C 3
    H
    8 , C 3
    H
    10 , or a mixture thereof. [0011] In a class of this embodiment, the calcination is carried out in the presence of air, and a calcination temperature of the solid residues is between 500 and 800'C. [0012] In a class of this embodiment, a thermal flue gas resulting from the calcination of 2 PCT/CN2012/087604 the solid residues is conveyed back for the heat cycle of the pyrolysis. [0013] In a class of this embodiment, before the pyrolysis of the biomass or before the step A, the method further comprises washing with water the biomass for removal of impurities. [0014] Advantages according to embodiments of the invention are summarized as follows. The biomass containing amorphous silicais pyrolyzed under anaerobic conditions, that is to say, the cellulose, hemicellulose, and lignin of the biomass are pyrolyzed to yield pyrolysis gas which is recycled for power generation or for preparation of syngas. However, the structure of amorphous silica is not destroyed. The resulting solid residues are calcined under aerobic conditionsfor removal of carbon residue. Thus, high added value of amorphous nano silica is obtained. The method has a simple process, high energy transformation and usage ratio, thereby being environment-friendly and energy-saving. BRIEF DESCRIPTION OF THE DRAWINGS [0015] FIG. 1 is a process flow chart of a method for preparation of amorphous silica from biomass containing amorphous silica in accordance with one embodiment of the invention; [0016] FIG. 2 is ascanning electron microscope (SEM) image of amorphous silica prepared in accordance with Example 1 of the invention; and [0017] FIG. 3 is anX-Ray Diffraction (XRD) spectrum of amorphous silica prepared in accordance with Example 1 of the invention. 3 PCT/CN2012/087604 DETAILED DESCRIPTION OF THE EMBODIMENTS Example 1 [0018] As shown in FIG. 1, rice hull was washed with water for removal of impurities such as mud, soaked in 10 wt. % of hydrochloric acid solution for 24 hours, and washed with water repeatedly until the pH value of the washing solution grew neutral. The washed rice hull was dried in a dry oven at 100'C to achieve constant weight. [0019] The dried rice hull was conveyed to a pyrolysis furnace via a screw conveyer, where the rice hull was pyrolyzed at 600'C under anaerobic conditions to yield pyrolysis gas and solid residues. The pyrolysis gas was conveyed to a purifying device, purified and stored, or directly conveyed to a gasifier for the production of syngas, or conveyed to a boiler and combusted forpower generation. [0020] The solid residues were conveyed to a calcinator and calcined at 650'C in the presence of air to yield thermal flue gas and calcined product. The thermal flue gas was conveyed back to the pyrolysis furnace for the heat cycle.The calcined product was ground to yield amorphous silica. [0021] Measurement results from a gas analyzershowed that, the pyrolysis gas comprised CO, C0 2 , H 2 , CH 4 , C 2
    H
    2 , C 2
    H
    4 , C 2
    H
    6 , C 3 Hs, C 3
    H
    10 , or a mixture thereof. FIG. 2shows ascanning electron microscope (SEM) image of the amorphous silica prepared in the example, andFIG. 3shows anX-Ray Diffraction (XRD) spectrum of the amorphous silica.The amorphous silica isunconsolidatedspherical particles having a particle size of about 80 nm. XRD spectrum showed that there was no specific crystal diffraction peak, which implied that the silica has an amorphous structure. 4 PCT/CN2012/087604 Example 2 [0022] Rice hull was washed with water for removal of impurities such as mud, soaked in 5 wt. % of nitric acid solution for 24 hours, and washed with water repeatedly until the pH value of the washing solution grew neutral. The washed rice hull was dried at 110'C to have amoisture content of less than 20%. [0023] The dried rice hull was conveyed to a pyrolysis furnace via a screw conveyer, where the rice hull was pyrolyzed at 800'C under anaerobic conditions to yield pyrolysis gas and solid residues. The pyrolysis gas was conveyed to a purifying device, purified and stored, or directly conveyed to a gasifier for the production of syngas, or conveyed to a boiler and combusted for power generation. [0024] The solid residues were conveyed to a calcinator and calcined at 800'C in the presence of air to yield thermal flue gas and calcined product. The thermal flue gas was conveyed back to the pyrolysis furnace for the heat cycle. The calcined product was amorphous silica. [0025] Measurement results from a gas analyzer showed that, the pyrolysis gas comprisedCO, C0 2 , H 2 , CH 4 , C 2
    H
    2 , C 2
    H
    4 , C 2
    H
    6 , C 3
    H
    8 , C 3
    H
    10 , or a mixture thereof. The amorphous silica was analyzed using ascanning electron microscope (SEM) and anX-Ray Diffraction (XRD), which showed the amorphous silica was unconsolidatedspherical particles having a particle size of about 80 nm. XRD spectrum showed that there was no specific crystal diffraction peak, which implied that the silica had an amorphous structure. Example 3 [0026] Rice hull was washed with water for removal of impurities such as mud, and dried at 120'C to have a moisture content of less than 20%.The dried rice hull was conveyed to 5 PCT/CN2012/087604 a pyrolysis furnace via a screw conveyer, where the rice hull was pyrolyzed at 1000'C under anaerobic conditions to yield pyrolysis gas and solid residues. The pyrolysis gas was conveyed to a purifying device, purified and stored, or directly conveyed to a gasifier for the production of syngas, or conveyed to a boiler and combusted for power generation. [0027] The solid residues were boiled in 5 wt. % of sulfuric acid solution for 4 hours, and washed with water thrice until the pH value of the washing solution grew neutral. The washed rice hull was dried in a dry oven at 102'C to have a moisture content of less than 30%. [0028] Thereafter, thesolid residues were conveyed to a calcinator and calcined at 500'C in the presence of air to yield thermal flue gas and calcined product. The thermal flue gas was conveyed back to the pyrolysis furnace for the heat cycle. The calcined product was amorphous silica. [0029] Measurement results from a gas analyzer showed that, the pyrolysis gas comprised CO, C0 2 , H 2 , CH 4 , C 2
    H
    2 , C 2
    H
    4 , C 2
    H
    6 , C 3 Hs, C 3
    H
    10 , or a mixture thereof. The amorphous silica was analyzed using a scanning electron microscope (SEM) and anX-Ray Diffraction (XRD), which showed the amorphous silica was unconsolidatedspherical particles having a particle size of about 80 nm. XRD spectrum showed that there was no specific crystal diffraction peak, which implied that the silica had an amorphous structure. 6
    权利要求:
    Claims (10)
    [1] 1. A method for preparation of amorphous silica from biomass containing amorphous silica, the method comprising: pyrolyzing the biomass under anaerobic conditions to yield pyrolysis gas and solid residues, collecting the pyrolysis gas, and calcining the solid residues under aerobic conditions to yield amorphous silica.
    [2] 2. The method of claim 1, characterized in thatthe biomass containing amorphous silica is rice hull.
    [3] 3. The method of claim 1, further comprising step A: acid-washing and drying the biomass before the pyrolysis of the biomass, or step B:acid-washing and drying the biomass after the pyrolysis of the biomass.
    [4] 4. The method of claim 1, characterized in that the acid-washing and drying of the biomass comprises soaking the biomass to in an acid solution at normal temperature for between 8 and 24 hours, or at between 80 and 100'C for between 2 and 6 hours, washing the biomass to be neutral, and drying the biomass.
    [5] 5. The method of claim 1, characterized in that the acid solution is hydrochloric acid, sulfuric acid, or nitric acid, and a weight concentration thereof is between 3 and 10 wt. %.
    [6] 6. The method of claim 1, characterized in that the biomass is pyrolyzed at a temperature of between 500 and 1000'C. 7 PCT/CN2012/087604
    [7] 7. The method of claim 1, characterized in that the pyrolysis gas comprises CO, C0 2 , H 2 , CH 4 , C 2 H 2 , C 2 H 4 , C 2 H 6 , C 3 Hs, C 3 H 10 , or a mixture thereof.
    [8] 8. The method of claim 1, characterized in thatthe calcination is carried out in the presence of air, anda calcination temperature of thesolid residues is between 500 and 800 0 C.
    [9] 9. The method of claim 1, characterized in that a thermal flue gas resulting from the calcination of thesolid residuesis conveyed back for the heat cycle of the pyrolysis.
    [10] 10. The method of claim 1, characterized in that before the pyrolysis of the biomass of claim 1 or before the step A of claim 2, the method further comprises washing with water the biomass for removal of impurities. 8
    类似技术:
    公开号 | 公开日 | 专利标题
    AU2012364501B2|2015-12-24|Comprehensive utilization method for biomass containing amorphous silicon dioxide
    Zhang et al.2010|A study on the consecutive preparation of d-xylose and pure superfine silica from rice husk
    CN103695015B|2015-08-12|A kind ofly accelerate biomass pyrolytic aerogenesis speed and obtain the device and method of nanometer grade silica material
    CN105461758B|2018-09-28|A method of improving lignite humic acid extract content
    CN202558749U|2012-11-28|Improved device for sludge pyrolysis treatment
    CN107233909B|2020-02-21|Preparation method and application of strontium niobate/carbon nitride composite nano material
    CN105502360B|2018-04-06|A kind of preparation method of expandable sulfur-free graphite
    KR101048410B1|2011-07-12|Preparation of superfine purified silica, and fibers simultaneously
    CN104525175A|2015-04-22|Preparation method for preparing biodiesel catalyst
    CN105600790A|2016-05-25|Method for co-producing ultra-pure nano-silica and biological oil by using rice husk
    CN111994907A|2020-11-27|Method for preparing boron-doped porous carbon material with high specific surface area from biomass
    CN1724338A|2006-01-25|Process for producing industrial sulfuric acid using phosphorus gypsum as raw material
    CN100560499C|2009-11-18|A kind of method of from bituminous shale waste slag, extracting aluminum oxide and white carbon black
    CN105238432A|2016-01-13|Method and device for preparing high-quality bio-oil and white carbon black through self-heating acid pickling-pyrolysis-combustion integration
    CN106395816B|2019-11-12|A method of residue prepares adsorbent after extracting humic acid by lignite
    CN203845985U|2014-09-24|Device of accelerating gas-yield speed by biomass pyrolysis and obtaining nanoscale silicon dioxide material
    CN106622137A|2017-05-10|Production method of adsorbent for removing mercury from flue gas
    CN104556056B|2017-07-21|Utilize the method for high silica flour coal ash production of silica white
    CN108821283B|2021-12-07|Method for preparing activated carbon by using fir bark microwave-assisted hydrothermal method
    Javed et al.2009|Characterization of silica from sodium hydroxide treated rice husk
    CN103666515A|2014-03-26|Method for extracting petrologen in oil shale
    CN111842310B|2021-11-30|Biomass gradient deliming pretreatment method
    CN108295856B|2020-06-02|Method for preparing methane dry reforming bimetallic catalyst from fly ash silicon extraction residues
    CN101200292B|2010-07-21|Hydrophobic white carbon black preparing method
    Ilochonwu et al.2015|Effect of temperature in extraction of high purity amorphous silica from rice husk for silicon production
    同族专利:
    公开号 | 公开日
    RU2579447C2|2016-04-10|
    SG11201403802PA|2014-10-30|
    MY175037A|2020-06-03|
    CA2860482A1|2013-07-11|
    US20140322120A1|2014-10-30|
    EP2801552A1|2014-11-12|
    KR20140116185A|2014-10-01|
    MX2014008256A|2015-05-12|
    US9403687B2|2016-08-02|
    AU2012364501B2|2015-12-24|
    RU2014132182A|2016-02-27|
    MX352675B|2017-12-04|
    EP2801552A4|2015-11-04|
    JP2015504036A|2015-02-05|
    WO2013102414A1|2013-07-11|
    IN2014MN01528A|2015-05-15|
    CN102653406A|2012-09-05|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    GB1508825A|1974-04-04|1978-04-26|Refratech Albert Gmbh|Method of producing low-carbon white husk ash|
    US4214920A|1979-03-23|1980-07-29|Exxon Research & Engineering Co.|Method for producing solar cell-grade silicon from rice hulls|
    RU2144498C1|1999-02-01|2000-01-20|Земнухова Людмила Алексеевна|Method of preparing highly pure amorphous silicon dioxide and carbon from rice husk|
    US6444186B1|2000-01-28|2002-09-03|Chk Group, Inc.|Composition and method of forming low-carbon, amorphous siliceous ash from siliceous waste material|
    KR100414888B1|2000-02-09|2004-01-13|알케이케미칼 주식회사|METHOD OF PREPARATION FOR SILICA FROM RICE BRAN|
    RU2245300C1|2003-12-24|2005-01-27|Институт химии Дальневосточного отделения Российской академии наук |Method of reworking silicon-containing vegetable raw material and plant for realization of this method|
    CN1803599A|2005-05-31|2006-07-19|株洲工学院科技开发部|Process and apparatus for preparing high-purity silicon dioxide by utilizing rice hull|
    RU2307070C2|2005-07-14|2007-09-27|Общество С Ограниченной Ответственностью "Рисилика"|Method of production from the rice husk of the amorphous silicon dioxide|
    RU2292305C1|2005-08-02|2007-01-27|Институт химии Дальневосточного отделения Российской академии наук |Method of extraction of the ions of the heavy metals from the water solutions|
    RU2304559C2|2005-08-22|2007-08-20|Людмила Алексеевна Земнухова|Method of producing sorbent to collect spilt crude oil and petroleum products by using rice husk|
    CN1935648B|2006-09-14|2010-05-12|华南理工大学|Method for preparing polycrystalline silicon for solarcell from rice husk|
    CN101219790B|2007-01-12|2010-09-15|中国科学院过程工程研究所|Method for producing nano-silicon dioxide with stalk|
    JP2008214158A|2007-03-06|2008-09-18|Maywa Co Ltd|Process for manufacturing amorphous silica from chaff|
    FI123180B|2007-10-11|2012-12-14|Valtion Teknillinen|Plant for the preparation of a pyrolysis product|
    CN101417798B|2008-11-26|2011-05-11|吉林大学|Paddy hull burned gas and waste residue comprehensive utilization method|
    CN101673781B|2009-09-25|2010-11-03|邵振亚|Method for preparing solar cell polysilicon raw material from rice hulls|
    CN102190509A|2011-03-16|2011-09-21|吉林大学|Method for producing silicon fertilizer from rice straws|
    CN102653406A|2012-01-05|2012-09-05|武汉凯迪工程技术研究总院有限公司|Comprehensive utilization method of amorphous-silica-containing biomass|CN102653406A|2012-01-05|2012-09-05|武汉凯迪工程技术研究总院有限公司|Comprehensive utilization method of amorphous-silica-containing biomass|
    CN102616793B|2012-03-26|2014-02-26|阳光凯迪新能源集团有限公司|Method for eliminating metal ions in rice hulls by utilizing industrial flue gas|
    EP3083895A2|2013-12-18|2016-10-26|Shell Internationale Research Maatschappij B.V.|Continuous or semi-continuous biomass wash system for hydrothermal hydrocatalytic conversion|
    US9468950B2|2013-12-18|2016-10-18|Shell Oil Company|Continuous or semi-continuous biomass wash system hydrothermal hydrocatalytic conversion|
    US9394486B2|2013-12-18|2016-07-19|Shell Oil Company|Biomass treatment for hydrothermal hydrocatalytic conversion|
    EP3083897A2|2013-12-18|2016-10-26|Shell Internationale Research Maatschappij B.V.|Biomass treatment for hydrothermal hydrocatalytic conversion|
    CN105899645B|2013-12-18|2018-01-30|国际壳牌研究有限公司|Continuous or semicontinuous biomass purging system for the conversion of hydro-thermal hydrogenation catalyst|
    CN103695015B|2014-01-06|2015-08-12|中盈长江国际新能源投资有限公司|A kind ofly accelerate biomass pyrolytic aerogenesis speed and obtain the device and method of nanometer grade silica material|
    DE102014014177B4|2014-09-19|2020-03-26|Green Sugar Ag|Use of plant-based silicates as an additive to improve the material properties of mixtures|
    KR101602219B1|2014-11-19|2016-03-10|한국에너지기술연구원|Biomass fluidized bed gasifier apparatus for medium calorific value syngas and silicon|
    CN106829970A|2017-03-31|2017-06-13|章斐虹|A kind of method that rice husk prepares biomass nano silica|
    TWI671010B|2018-01-24|2019-09-11|綠世紀生物科技股份有限公司|Method for preparing a tea leaf extract|
    KR102091833B1|2018-05-16|2020-03-20|한국세라믹기술원|Method for producing of silica using biomass|
    CN109175351B|2018-10-31|2020-07-10|南京林业大学|Method for preparing powder metallurgy friction material by adopting bio-based amorphous silicon dioxide|
    CN109384237B|2018-10-31|2021-09-14|昆明理工大学|High-purity SiO extracted from rice hulls2Method |
    法律状态:
    2016-04-21| FGA| Letters patent sealed or granted (standard patent)|
    2020-07-23| MK14| Patent ceased section 143(a) (annual fees not paid) or expired|
    优先权:
    申请号 | 申请日 | 专利标题
    CN201210002005.9||2012-01-05||
    CN2012100020059A|CN102653406A|2012-01-05|2012-01-05|Comprehensive utilization method of amorphous-silica-containing biomass|
    PCT/CN2012/087604|WO2013102414A1|2012-01-05|2012-12-27|Comprehensive utilization method for biomass containing amorphous silicon dioxide|
    [返回顶部]