    The present invention relates to high-strength, including pigment-containing - for example, flame retarded - cellulosic Regeneratfilamente with improved textile properties, in particular with regard to strength and uniformity, their use for the production of fabrics and a method for producing these filaments.
    公开号:AT511638A1
    申请号:T905/2011
    申请日:2011-06-21
    公开日:2013-01-15
    发明作者:
    申请人:Chemiefaser Lenzing Ag；
    IPC主号:
    专利说明:

    «· • *« · • * • · ·
    Lenzing AG, PL0518
    High strength cellulosic filament its use as well
    Process for its preparation
    The present invention relates to high-strength cellulosic regenerated filaments with improved textile properties, in particular with regard to strength and uniformity, their use for the production of fabrics and a method for producing these filaments. These high strength filaments may also contain pigments, such as flame retardant pigments.
    State of the art:
    Cellulosic regenerated filaments have long been known. They are especially for textiles, but - in a high-strength form - for technical applications, such. B. used as a tire cord. Under "Cellulosic Regenerate Fibers" For the purposes of this invention, fibers are to be understood which are produced from a cellulose-containing spinning solution by spinning into a spinning bath (often also called precipitation bath), the cellulose being present in the spinning solution as cellulose derivative, in particular as cellulose xanthate, and regeneration in the precipitation bath to pure cellulose takes place. The regenerated fibers and filaments produced via the xanthate are commonly referred to as "viscose" or "rayon". The cellulose-containing spinning solution is also referred to as "viscose" or "viscose spinning solution". The manufacturing process itself is therefore referred to as Viskoseverfahren.
    Viscous processes for staple fibers and continuous filaments have been known in principle for many years and described in detail, for example, in K. Götze, Chemiefasern nach den Viskoseverfahren, 1967. However, the textile properties of the resulting fibers and filaments are significantly affected by many parameters. In addition, limits are set for many influencing factors due to the design of the existing production facilities, which can not be exceeded for technical or economic reasons, so that any variations in the product range can be exceeded
    • »• * • • • • • * • ·
    »»
    Lenzing AG, PL0518
    Parameters are often not possible and therefore would not cause the expert to do so.
    In the course of time, different variants of the viscose process were developed and partly used industrially to this day. The individual variants differ mainly in the composition of the spinning solution and the precipitation bath, whereby the mechanical properties of the products can be greatly influenced. Examples of these are the modal and polynosic fibers, which are produced on a commercial scale only in the form of staple fibers. The basics of the modal process for producing staple fibers are described in AT 287905. In the field of filaments, it has meanwhile also been possible, with the help of mechanical engineering improvements, to spin continuously, instead of the earlier, discontinuous centrifuge processes, by means of so-called "continue" processes.
    Standard viscose filaments are now widely used in the textile and clothing industry, especially in the field of linings. The low strength, especially when wet, the high elongation and the high surface shrinkage put the use of viscose filaments in the textile sector but limits. In particular, light, d. H. thin, but nevertheless solid textiles, which are also easy to wash, are therefore not possible. Also for more heavily used textiles, eg. B.
    Work clothes and uniforms are not suitable. Although there are possibilities here by synthetic filaments, for example made of polyester or polyamide, but these are in particular in wearing comfort, much worse than the cellulosic materials. There is therefore still a need for high strength cellulosic filaments for textile applications which can not be economically produced by the known processes.
    A well-known, commercial, high-strength regenerated filament is, for example, CORDEN KA®, which is produced by a modified viscose process. It is manufactured with single fiber titers of approx. 1.8 dtex and strengths (conditioned) of approx. 45 to approx. 52 cN / tex. It will be submitted later in technical] 2
    Lenzing AG, PL0518; ::: · * ♦. ··.
    Range, for the reinforcement of rubber articles, in particular high-quality vehicle tires used. For textile applications, such a filament is too coarse and too expensive to manufacture. Here, the composition of spinning solution and precipitation bath were changed in comparison to standard viscose in particular.
    It has also long been known in principle to spin various pigments into cellulosic regenerated fibers, especially into fibers by the viscose process. The pigments may be flame-retardant pigments, in particular those based on phosphorus, or else colourants or matting agents. Such pigment-containing viscose fibers are produced worldwide for standard applications in the textile and nonwovens sector with a single fiber titer between 0.8 and 16 dtex. The pigments are added to the cellulose-containing spinning solution by means of suitable metering devices. This pigment-containing spinning solution is then extruded through spinnerets and precipitated according to the known methods and further treated. The pigments introduced into the fibers in this way are stored very firmly and can not be washed out, for example, by conventional washing processes.
    For the flame-retardant finish of viscose fibers various chemicals are described in the literature. Above all, flame retardants based on halogens, silicon and phosphorus are used.
    Patents DE4128638A1 or DE102004059221A1 disclose flame retardant dispersions based on a 2,2'-oxybis [5,5-dimethyl-1, -S'-dioxaphosphorinane) disulfide using various dispersant systems and also mention the use of these dispersions for flame retardant finishing of viscose fibers.
    EP1882760 also describes the preparation of flame-retarded viscose fibers using flame retardant dispersions based on a 2,2'-oxybis [5,5-dimethyl-1,3,2-dioxaphosphorinan] 2,2'disulfide. There will be | REPLACED | 3 • · · · · · · ·
    Lenzing AG, PL0518 described as an important feature of the invention that the particle size may be at most 10 μιτι and that the spinning mass must therefore be cleaned before spinning through filters with a maximum mesh size of 10 pm. However, it has been found that this criterion is not sufficient to produce fibers that meet the requirements described here. The maximum particle size of 10 μιτι described in EP1882760 is perhaps for Viskoseendlosfilamente or. Monofilaments with a high titre are sufficient, but by far no longer meet the requirements of a modern staple fiber production with fiber finenesses of about 1 to 4 dtex; a 1.3 dtex fiber has a diameter of about 10 pm.
    The fibers described in the prior art or commercially available are all prepared by standard viscose methods. Although they show comparatively good mechanical fiber data for flame-retardant viscose fibers, since the phosphorus contents are very low. Investigations with various flame retardants on the basis of phosphorus have shown, however, that only from a phosphorus content of about 2.8%, a sufficient flame retardant effect is achieved. The flame retardancy correlates very well with the content of flame retardant converted to pure phosphorus.
    However, it has been found that, for example, the incorporation of large amounts (15-25%) of a flame-retardant pigment leads to a further deterioration of the textile parameters of the viscose fiber. Therefore, the limitations of the application areas already mentioned for the standard viscose fibers apply a fortiori to flame-retarded viscose fibers.
    This is all the more regrettable because flame-retardant fibers could be used to particular advantage in products that are also exposed to heavy mechanical loads, for example in workwear for particularly dangerous activities such as fire departments, foundries, military, petroleum and chemical industries. For such products will be
    SUBSEQUENT 4 ♦ * * • ·
    Lenzing AG, PL0518 usually already high performance synthetic fibers such as (aromatic) polyamides, aramids, polyimides and the like used. However, these fibers have a low wearing comfort, since they are not able to absorb moisture sufficiently. A mixture of these fibers with cellulosic fibers, which complement the range of properties by an increased wearing comfort, without the other properties to deteriorate too much, would be desirable.
    It is likewise known to incorporate color pigments or matting agents, especially titanium dioxide, into cellulosic regenerated fibers. Basically, the same problems occur due to the solids content. The problems described here by spinning larger amounts of solids apply to viscose staple fibers, but especially for viscose filaments.
    WO 2011/026159 A1 discloses a process for producing flame-retarded cellulosic staple fibers which is intended to solve these problems. The fiber described there contains as a flame-retardant substance a spun, particulate phosphorus compound, preferably an organophosphorus compound and has a so-called use value between 6 and 35, preferably between 8 and 35 and particularly preferably between 10 and 35. Such a fiber could be produced for the first time by a modified viscose process.
    It has been found that for the production of the fibers described in WO 2011/026159 A1, a cellulose concentration of 4-7% using a pulp having an R-18 content of 93-98% and an alkali ratio (= cellulose concentration / sodium hydroxide concentration, respectively in g / l) from 0.7 to 1.5 represent the ideal conditions. However, the spinning parameters must be adjusted accordingly due to the addition of the flame-retardant FR pigment.
    WO 2011/026159 A1 therefore also describes a process for producing a flame-retarded regenerated cellulose fiber for textile applications 5 ♦ »
    Lenzing AG, PL0518 by spinning a viscose with a content of 4 to 7% cellulose, 5 to 10% NaOH, 36 to 42% (based on cellulose) carbon disulfide and 1 to 5% (based on cellulose) of a modifier in a precipitation bath,
    Peeling off the coagulated filaments using a viscose whose spun yarn value is 50 to 68, preferably 55 to 58, and whose spun viscosity is 50 to 120 falling-seconds; and that the temperature of the precipitation bath 34 to 48 ° C, wherein a. the alkali ratio (= cellulose concentration / alkali content) of ready-to-spray viscose is 0.7 to 1.5, b. the following precipitation bath concentrations are used: • H2S04 68-90 g / l • Na2SC> 4 90-160 g / l • ZnS04 30-65 g / l c. the final discharge from the precipitation bath takes place at a speed between 15 and 60 m / min and d. as a flame-retardant substance a pigmented organophosphorus compound is spun in the form of a pigment dispersion.
    Suitably, a viscose is used, to which the modifier is added only shortly before the spinning of the viscose.
    The proposed in WO 2011/026159 A1 measures adherence to a certain spinning maturity for which the Spinngammawert is characteristic, the maintenance of a certain viscosity, for which the falling ball values are characteristic, and the observance of certain conditions in the precipitation bath together cause the desired fiber properties. The spinngamma value is understood to mean the proportion of the sulfur-carbon molecules bound to 100 cellulose molecules. The spider gamma value is determined according to Zellcheming leaflet draft by R. Stahn [1958] and
    Leaflet III / F 2. The term "falling ball" means the viscosity determined by the falling ball method; it is expressed in terms of bullet seconds. The determination is given in K. Götze, Chemiefasern [1951], p. 175.
    FOLLOW-UP 6
    Lenzing AG, PL0518
    The flame-retardant phosphorus compound which is prepared as a pigment is added according to WO 2011/026159 A1 to the viscose spinning solution in the form of a pigment dispersion. In this case, so much of the flame-retardant substance is spun in that the finished fiber contains at least 2.6%, preferably between 3.2% and 6.0%, particularly preferably between 3.5% and 6.0% phosphorus, based on cellulose.
    As already stated above, a flame retardant organophosphorus compound which is particularly suitable for the purposes of the present invention is 2,2'-oxybis [5,5-dimethyl-1,3,2-dioxaphosphorinane-3'-disulfide.
    In particular, the quality of the pigment dispersion has a significant influence on the fiber properties. This is determined by the average and maximum particle size of the pigments, the concentration of the dispersion in use, d. H. during the addition to the viscose spinning solution, as well as the type and amount of the dispersing aids.
    Contrary to the possible upper particle size of 10 μm described in patent EP1882760, it has been found that an average particle size (x50) of less than 1 μm and a maximum particle size (X99) of less than 5 μm, preferably less than 3 μm, are necessary. Fig. 3 shows a size distribution of a still suitable pigment dispersion.
    Preferably, according to WO 2011/026159 A1, the pigment dispersion should contain between 10 and 50% of the flame-retardant substance.
    In most prior art documents, the influence of the dispersant is not described as fully as it would be appropriate. However, many chemicals that provide a highly stabilized flame retardant dispersion have a negative impact on the spinning process, as they also have a modifying effect on the viscose, but the fiber strength is in contrast to the
    RETURNED 7
    Lenzing AG, PL0518 • · · ♦ · * · · · * * * * * * • * * • • »used modifiers do not influence positively. As ideal dispersants for the flame retardant dispersion for producing the fibers according to the invention which do not adversely affect the fiber strength, in particular those have been found which are selected from the group comprising modified polycarboxylates, water-soluble polyesters, alkyl ether phosphates, end-capped nonylphenol ethoxylates,
    Castor oil alkoxyl esters and carboxymethylated alcohol polyglycol ethers. Preferably, the pigment dispersion should contain between 1.5 and 13% of the dispersing aid.
    WO 2011/026159 A1 expressly relates to the production of staple fibers. Since these usually have a cutting length between about 25 and 90 mm and are mixed intensively several times before their final use in textiles, small differences in the uniformity of the individual fibers as well as small spinning defects do not play a major role in their production. However, the conditions are quite different in the production of (continuous) filaments for textile or technical applications. These are usually spun in thin filament bundles with about 10 to 2000 individual filaments and wound up directly. It takes about 48 hours to fill a bobbin. If, due to a spider error, even a single filament breaks off within 48 hours, this has a significant impact on the product quality and therefore the achievable price. In addition, the filaments are naturally no longer mixed in their use, so that unevenness of the filaments, for example, in textiles clearly visible. This also affects the product quality and thus the achievable price.
    In summary, regenerated cellulose filaments are known in the prior art, which have a high strength, but too coarse titers, on the other hand textile filaments, which are so fine that they offer a textile comfort, but at the same time have only a low strength. In particular, there are no textile regenerated cellulose filaments known which, with high strength, have such a high content of pigment, for example
    | READY 8 • • • • • • • • • • • •
    Lenzing AG, PL0518 flame retardant pigment, have that they actually show good flame retardant properties.
    DESCRIPTION OF THE INVENTION Surprisingly, this problem has been solved by regenerated cellulose filaments which have both a pigment content of more than 20% by weight and a strength of more than 22 cN / tex. These pigments introduce desired additional functionalities into the filaments. This can be z. As a flame retardant, a permanent color or a matting. But for special products, other additives are possible, for example, provide for a particularly good visibility or warning effect, electrical conductivity, absorption of pollutants or radiographic visibility (eg for surgical sewing threads). As pigments, in principle, all solids are suitable which, under the conditions in the viscose spinning solution, d. H. Strongly alkaline and CS2-containing, and the strongly acidic precipitation bath does not change undesirably, especially partially or completely dissolve. A conceivable exception are substances which are present in a strongly alkaline environment in dissolved form and only pass into an acidic precipitation bath in a solid aggregate form. In particular, the pigment is selected from the group consisting of flame-retardant, colored, fluorescent ("high-vis" dyes) and X-ray detectable pigments. Mixtures of these pigments for a combination of several properties in the same filament should also be expressly encompassed by the present invention, for example the combination of color pigments, high-vis color pigments and flame-retardant pigments for use in lightfast, warning-colored, flame-retardant clothing for fire services and rescue services ,
    The described advantageous mechanical properties of the pigment-containing regenerated cellulose filaments according to the invention are
    POSSIBLE 9 • · m ·
    Lenzing AG, PL0518 achieved particularly reliable if the pigment has a particle size distribution with x50 smaller than 1.0 gm and X99 smaller than 5.0 μηη, preferably less than 3.0 gm.
    The object of the prior art can be achieved particularly well and in a surprising manner if the regenerated cellulose filaments according to the invention have a fine single fiber titer of between 0.4 and 4 dtex, preferably between 0.8 and 3.0 dtex. Such fine regenerated cellulose filaments, especially if they contain sufficient amounts of pigment, have not yet been produced with the strengths described above.
    The spun-in pigments preferably have a particle size distribution with x 50 smaller than 1.0 gm and 99 lower than 5.0 gm, preferably below 3.0 gm.
    As the organophosphorus compound, 2,2'-oxybis [5,5-dimethyl-1,3,2-dioxaphosphorinan] 2,2'-disulfide (Formula I) is preferably used. This substance is available under the trade names Exolit and Sandoflam in sufficient quantities and is not washed out of the fibers during the manufacturing process and also in the subsequent application:
    In a preferred embodiment, the filament according to the invention contains at least 2.8%, preferably between 3.2% and 6.0%, particularly preferably between 3.5% and 6.0% phosphorus, in each case based on cellulose. Lower phosphorus content than 2.8% does not provide sufficient flame retardancy. Higher phosphorus contents than 6%
    READY 10 m * # · • · m * # · • · • m
    Lenzing AG, PL0518 worsen the mechanical properties of the filaments and, moreover, are no longer economical.
    In most prior art documents, the influence of the dispersant is not described as fully as it would be appropriate. However, many chemicals that provide a highly stabilized flame retardant dispersion, have negative effects on the spinning process, as they also have a modifying effect in the viscose, but do not positively affect the fiber strength, in contrast to the modifiers used. As ideal dispersants for flame retardant dispersion for the preparation of Regeneratcellulosefilamente invention, which do not adversely affect the fiber strength, have been found in particular those selected from the group containing modified polycarboxylates, water-soluble polyesters, alkyl ether, endgruppenverschlossenyl Nonylphenolethoxylate, castor oil alkoxyl and carboxymethylated alcohol polyglycol. Preferably, the pigment dispersion should contain between 1.5 and 13% of the dispersing aid.
    Likewise provided by the present invention is a pigment-free regenerated cellulose filament having a strength in the conditioned state of more than 36 cN / tex. The regenerated cellulose filaments according to the invention preferably also have a fine single fiber titer of between 0.4 and 4 dtex, more preferably between 0.8 and 3.0 dtex.
    A regenerated cellulose filament having such a high strength and fineness can be processed very well into woven fabrics and other textile fabrics, which have an exceptionally high abrasion resistance compared to standard viscose filaments, which has a strength of about 20 cN / tex. Thus, it is particularly well suited for use in sports, for example for motorcycle, Kartbekleidung and sportswear. With abrasion resistance, the Martindale
    REPLACED 11 * «« * * «« «· ·
    Lenzing AG, PL0518
    The higher temperature resistance compared to synthetic filaments such as polyester and nylon, the high-strength filament is also used in many technical applications, eg. B. for turbocharger hoses in cars and trucks.
    Both (pigment-free) filaments having a conditioned state strength greater than 36 cN / tex and pigment-containing filaments having a pigment content greater than 20% by weight and a strength conditioned greater than 22 cN / tex are intended for the purposes of the present invention Invention also be referred to as "high strength".
    When used, the filaments according to the invention are not used individually but in the form of the filament bundles obtained in the spinning process from in each case a single spinneret, also referred to as filament yarns. In the textile sector, a filament yarn usually contains about 30-200 individual filaments. In technical applications, for example for reinforcing car tires, conveyor belts or other rubber articles, about 700 to 2000 individual filaments in the yarn are common.
    Likewise provided by the present invention is the use of the filaments according to the invention for producing a textile fabric. In addition to the fibers according to the invention, this fabric may also contain other fiber yarns or filament yarns, for example and in particular wool, flame-retardant wool, para-aramides (Kevlar®, Twaron®) and meta-aramids (Nomex®), polybenzimidazole (PBI), p-phenyl 2,6-benzobisoxazole (PBO), polyimide (P84®), polyamideimide (Kermed®), modacrylic, polyamides, flame retarded polyamides, flame retarded acrylic fibers, melamine fibers, polyesters, flame retarded polyesters, polyphenylene sulfide (PPS), polytetrafluoroethylene (PTFE), glass fibers , Cotton, silk, carbon fibers, oxidized thermally stabilized polyacrylonitrile (PANOX®) fibers, elastanes and electrically conductive fibers, as well as blends of these fibers
    RETURNED 12
    Lenzing AG, PL0518
    The fabric structure is preferably a woven, knitted or crocheted fabric. In the case of a woven or knitted fabric, the mixture of filaments according to the invention with the other fiber or filament yarns either by mixing before yarn production, the so-called intimate mixing, or by sharing each pure yarns of different filament and fiber types in weaving, working, Knitting or crocheting possible.
    The cellulosic regenerated filaments according to the invention can be produced by a modified viscose process according to the invention. The present invention therefore also relates to a continuous process for producing a high-strength regenerated cellulose filament by spinning a viscose with a content of 4 to 8% cellulose, 5 to 10% NaOH, 36 to 42% (based on cellulose) carbon disulfide and 1 to 5% (based on cellulose) a modifier in a coagulation bath, stripping off the coagulated filaments, using a viscose whose spin gamma value is 50 to 68, and whose spin viscosity is 50 to 150 fall times; and that the temperature of the precipitation bath is 34 to 65 ° C, a. the alkali ratio (= cellulose concentration / alkali content) of ready-to-spray viscose is 0.7 to 1.5, b. the following precipitation bath concentrations are used: • H2S04 68 - 95 g / l • Na2SO4 90-160 g / l • ZnSO4 30 - 65 g / l c. the final discharge from the Fälibad and the winding at a speed between 15 and 180 m / min takes place, where d. the filaments coagulated in the coagulation bath are then passed through a second bath, the second bath containing aqueous, 3-7% by weight sulfuric acid at a temperature of 80-98 ° C.
    POSSIBLE REVIEW 13 • · • · • · * ·
    Lenzing AG, PL0518
    By spinning such a spinning solution with subsequent stretching and fixation in the second bath to obtain high-strength cellulosic Regeneratfilamente that even after incorporation of flame retardant or coloring pigments filament or Garnfestigkeiten that are well above comparable cellulosic Regeneratfilamenten consisting of textile viscose spinning solution according to the prior the technique was spun.
    Suitably, a viscose is used, to which the modifier is added only shortly before the spinning of the viscose. In the context of the process according to the invention, "continuous" is intended to mean that the spinning out of the viscose into the precipitation bath, drawing, washing, drying and winding takes place continuously in the same operation. In contrast, there are the widely used centrifuge spinning processes in which the wet filaments are wound up in centrifuges and then these so-called spin cakes are washed intermittently and dried.
    The inventively proposed measures of compliance with a certain spinning maturity, for which the Spinngammawert is characteristic, compliance with a certain viscosity, for which the falling ball values are characteristic, and compliance with certain conditions in the precipitation bath, together effect the desired fiber properties. Spinning gamma is the proportion of carbon disulfide molecules bound to 100 cellulose molecules. The spin gamma value is determined according to Zellcheming leaflet draft by R. Stahn [1958] and leaflet III / F 2. The term "ball drop" is understood to mean the viscosity determined by the falling ball method; it is expressed in terms of bullet seconds. The determination is given in K. Götze, Chemiefasern [1951], p. 175.
    In order to achieve the high strength of the filaments reliably, it has proven to be advantageous to use as cellulosic raw material a pulp having an a content of 93-99%. Such a pulp has only small proportions
    SUBSEQUENT 14 * »*» ♦ · *
    Lenzing AG, PL0518 on low molecular weight secondary constituents, which on the one hand reduce the strength in the finished filament and on the other hand can get into the Fällbadkreisläufe where they can be disturbing as pollution in many ways.
    An important feature of the method according to the invention is that the filaments in the second bath are stretched by 70% to 105%. In the prior art, on the one hand no second bath is used, which contains only aqueous sulfuric acid and has a temperature of 80-98 ° C, and on the other hand after leaving the precipitation bath in the continue-spinning process only about 5%, in batch processes stretched by about 10-20% for textile filament ..
    This process makes it possible to produce both pigment-free high-strength regenerated cellulose filaments and those regenerated cellulose filaments which have a pigment content of more than 20% by weight and a strength of more than 22 cN / tex.
    A surprising correlation was found between the strength of a pigment-free regenerated cellulose filament and a pigment-containing regenerated cellulose filament, if only the pigment content in the filament is changed and the other process parameters are kept constant: FFKp = FFKr X Ccel! 2
    Therein, FFKp is the fineness-related strength of the pigmented regenerated cellulose filament, FFKr is the fineness-related strength of the pigment-free regenerated cellulose filament, and cceii is the cellulose content of the pigment-containing regenerated cellulose filament, based on the filament dry content and expressed as a fraction.
    For example, under process conditions according to the invention, under which pigment-free regenerated cellulose filaments are obtained with a
    FOLLOWED 15 "" t
    Lenzing AG, PL0518
    Starch of 35 cN / tex, also pigment-containing regenerated cellulose filaments having a strength of 22 cN / tex and a pigment content of 0.21 (i.e., a cellulose content of 0.79).
    The pigments are preferably spun in the form of a pigment dispersion. It is particularly advantageous if the pigment metering ratio is automatically controlled or adjusted on the basis of the spinning solution flow and adjusted by means of a regulated metering pump. An exact dosage is extremely important, among other things, for a consistent filament quality. Any deviation from the uniformity is clearly visible in the end use in the textile area in the fabric. In the technical field of application, unevenness can lead to failure of the end product.
    Therefore, the selection of a suitable controlled metering pump for the success of the method according to the invention is important. For example, eccentric screw pumps have proved to be particularly suitable. Piston pumps, however, are common in large liquid flows, but too imprecise in the present here, low liquid flows because they do not work continuously but impulsively and thus cause a constantly changing pigment concentration. The common in the synthetic fiber range gear pumps are not applicable in the present process, because on the one hand, the pigments used, in particular TiO 2, would lead to a very high abrasion of the gear pumps. On the other hand, there is a risk that the pigment settles between the teeth of the pump gears and closes them, so that the delivery rate is lower and the dispersion enters the viscose spinning solution with a lower pigment content.
    According to the invention, all the solids which are suitable under the conditions in the viscose spinning solution, ie. H. strongly alkaline and CS2-containing, do not change undesirable. In particular, the pigment is selected from the group consisting of flame-retardant, colored, fluorescent ("Fligh-vis" dyes) and X-ray
    POSSIBLE 16 • φ • φ • · • *
    Lenzing AG, PL0518 detectable pigments. It is also intended that mixtures of these pigments for a combination of several properties in the same filament are expressly included in the present invention. In a preferred embodiment of the invention, therefore, the pigment-like substance 5 is at least partially a flame-retardant substance
    In order to achieve an effective flame-retardant effect, so much of the flame-retardant substance is spun in the process according to the invention that the finished fiber is at least 2.8%, preferably between 10 3.2% and 6.0%, particularly preferably between 3.5% and 6.0% phosphorus, based on cellulose. The phosphorus is preferably in the form of the organophosphorus compound 2,2'-oxybis [5,5-dimethyl-1,3,2-dioxaphosphorinane] 2,2'-disulphide (I). The described advantageous mechanical properties of the regenerated cellulose filaments obtained by the process according to the invention are achieved particularly reliably when the pigment dispersion contains between 10 and 50% of the flame retardant substance with an average particle size (x90) smaller than 1.0 μm and a maximum particle size (X99) smaller 5.0 pm, preferably less than 3.0 pm and between 5 and 20% of a dispersing aid.
    This dispersant for the flame retardant dispersion is preferably selected from the group comprising modified polycarboxylates, water-soluble polyesters, alkyl ether phosphates, end-capped nonylphenol ethoxylates, castor oil alkoxyl esters and carboxymethylated alcohol polyglycol ethers.
    The flame retardant phosphorus compound which is prepared as a pigment according to the invention, the viscose spinning solution in the form of a
    Pigment dispersion added. In this case, so much of the flame-retardant substance is spun in that the finished fiber contains at least 2.6%, preferably between 3.2% and 6.0%, particularly preferably between 3.5% and 6.0% phosphorus, based on cellulose,
    POSSIBLE 17 • * «* ··· * · tt
    Lenzing AG, PL0518 i * i * er * »e *
    As already stated above, a flame retardant organophosphorus compound which is particularly suitable for the purposes of the present invention is 2,2'-oxybis [5,5-dimethyl-1,3,2-dioxaphosphorinane] 2,2'-disulphide.
    In particular, the quality of the pigment dispersion has a significant influence on the fiber properties. This is determined by the average and maximum particle size of the pigments, the concentration of the dispersion in use, d. H. during the addition to the viscose spinning solution, as well as the type and amount of the dispersing aids.
    Contrary to the possible upper particle size of 10 μm described in patent EP1882760, it has been found that an average particle size (x 50) of less than 1 μm and a maximum particle size (x 99) of less than 5.0 μm, preferably less than 3 μm, are necessary. Fig. 3 shows a size distribution of a still suitable pigment dispersion.
    Preferably, the pigment dispersion should contain between 10 and 50% of the flame retardant substance,
    The process of the invention will now be described with reference to a possible and well suited embodiment, without the invention being limited to this embodiment. Functionally equivalent solutions are expressly included in the invention.
    The spinning machine with which the process is carried out is shown in principle in FIG. 1: The supply of the viscose or of the viscose dispersion mixture takes place via the pipe system (1). The metering of the titer-dependent amount of viscose is carried out by means of precision gear pumps (2). In the filters (3), the filtration of the metered viscose takes place. In the variant described here, customary spinnerets (4) are installed submerged on so-called spinning pipes for producing the required filament in the precipitation bath (5). Preference is given to coexisting in a coagulation bath 18 ____ _
    SUBSEQUENT
    Lenzing AG, PL0518 j \: j ":: * two filament yarns spun from separate spinnerets (4) and then guided parallel to each other over the entire spinning machine. These spinnerets (4) contain the number of holes corresponding to the desired number of individual filaments in a filament yarn. The precipitation bath (5) is supplied via a level-regulated feed with precipitation bath liquid which has the composition according to the invention. Via a pipe section, the coagulated filaments with the Fällbadflüssigkeit first to a trough (7), which serves as a drain for the precipitation bath. Such a process is commonly referred to as a tube spinning process. The filaments are guided above the trough (7) onto the first godet (8) of the drawing unit, whereby excess precipitation bath is collected by the trough (7). From the galette (8), the filaments run into the second bath (9), where they are simultaneously stretched and fixed. This second bath has an inlet (10) and a drain (11) for the bath liquid described above. From the arranged in the second bath deflection device, which may be a movable (non-driven) pair of rollers or a rigid glass rod or the like, the filaments are guided on an entangled, with a wash water application (12) and a washing water drain (13) pair of rollers where They are washed first and then dried in a drying zone (14). Subsequently, they are scanned in a finishing unit (15) and finally wound on a Doppelspuleinheit (16). The pair of rollers may additionally be equipped with an exhaust (17) for the resulting water vapor and other gaseous by-products.
    The tube spinning process described here allows about 10% higher strength and faster to about three times faster spinning than the conventional dipping spinning process. Without the addition of a pigment dispersion, spinning speeds of up to 180 m / min are possible, with the addition of a pigment dispersion still up to 85 m / min.
    A particularly uniform addition of the pigments is possible, for example, by a metering device according to FIG. 2: this contains an agitator container (18) for the preparation of the pigment dispersion, a
    FOLLOWED 19 * * * * * * * * * * *
    Lenzing AG, PL0518
    Dispersion metering pump (19) for discharging the dispersion, a corresponding flow measurement (20), and two static mixers (21, 22) for mixing the dispersion with the main stream of Viskosespinnlösung via a line (23), a booster pump (24) and a flow measurement (25) to the static mixers (21, 22) passes. After a further flow measurement (27), the viscose pigment dispersion is fed via a further pipeline (28) to the spinning machine. In addition, a temperature control circuit (27) may be provided for controlling the temperature of the main viscous stream.
    The invention will now be explained by way of examples. These are to be understood as possible embodiments of the invention. By no means is the invention limited to the scope of these examples.
    Example 1: 6 parts by weight of 2,2'-oxybis [5,5-dimethyl-1,3,2-dioxaphosphonnan] 2,2'-disulfide, 6 parts by weight of water and 0.55 parts by weight of alkylpolyglycol ether phosphoric acid ester are added by means of a Dissolver homogenized and ground in a stirred ball mill (Drais, type Perl Mill PML-V / H) with Zirkonoxidmahlkörpern at a temperature of 40-55 ° C until the final dispersion has a x99 < 1.50 pm. Beech pulp (R18 = 97.5%) was alkalized with mash liquor containing 240 g / l NaOH at 35 ° C with stirring and pressed to a Alkalellellulosevlies. The alkali cellulose nonwoven was fiberized, aged and sulfided. The xanthate was dissolved with a dilute sodium hydroxide to a viscose with 5.6% cellulose, 6.8% NaOH and 39% CS2, based on cellulose. The viscose was filtered 4 times and vented. The viscose was dosed 1 hour before spinning 3%, based on cellulose, ethoxylated amine, a modifier causing a shell structure. The viscose was ripened to a spinning gamma value of 57. The viscosity during spinning was 80 falling seconds. The finished flame retardant dispersion is added to this ready-to-spin viscose.
    RETURNED 20 • · • · • ·
    Lenzing AG, PL0518
    The nozzles used have a nozzle hole diameter of 60 gm. The precipitation bath contains 75 g / l of sulfuric acid, 113 g / l of sodium sulfate and 53 g / l of zinc sulfate. The precipitation bath temperature was 39 ° C.
    The coagulated and partially regenerated plastic yarn strand of pale yellow color was passed through a galette (G 1) into a second bath whose temperature was 95 ° C. and contains 4.8% by weight of sulfuric acid, there between G 1 and a second Galette (G 2) stretched by 100%. The final discharge was 30 m / min. The filament was then washed free of acid with hot water, dried and then wound up.
    Table 1: Fiber data:
    Fiber titer [dtex] single filaments [number] FFk [cN / tex] FDk [%] BISFA wet modulus [cN / tex] P- content [%] Example 1 200 76 23.5 6.1 5.2 3.5
    REPLACED 21
    权利要求:
    Claims (20)
    [1]
    cU - JUIN-cMII I C3J VorULHb Ι " Ή I bN I WtbtN 'Wllll + HJ fb fd ffcn έΊΗΟ Hn: + Mj i: od b.cib' JJ ***** «·« t * * * · + * «« A «« * »*« - · · «« < A high-strength pigment-containing regenerated cellulose filament, characterized in that it has a pigment content of more than 20% by weight and a strength in the conditioned state of more than 22 cN / tex having.
    [2]
    2. Pigment-containing Regenerateellulosefilament according to claim 2, wherein the pigment is selected from the group comprising flame-retardant, 1 o colored, fluorescent and X-ray detectable pigments.
    [3]
    3. Regenerateellulosefilament according to claim 2, characterized in that the pigment has a particle size distribution with x $ o less than 1.0 pm and xee smaller than 5.0 μηη. 15
    [4]
    4. regenerated cellulose filament according to claim 2, characterized in that it has a Einzelfasertiter of between 0.4 and 4.0 dtex.
    [5]
    5. A flame-retarded regenerated cellulose filament according to claim 2, which contains 20 at least 2.8%, preferably between 3.2% and 6.0%, particularly preferably between 3.5% and 6.0% phosphorus, based on cellulose,
    [6]
    A flame-retarded regenerated cellulose filament according to claim 2, wherein 25 is the phosphorus compound 2,2'-oxybis [5,5-dimethyl-113,2-dioxaphosphorinane] 2,2'-disulfide (I).
    [7]
    7. A flame retarded regenerated cellulose filament according to claims 3 to 6, characterized in that it contains, in addition to the flame retardant, a dispersant selected from the group consisting of modified polycarboxylates, water-soluble polyesters, alkyl ether phosphates, end-capped nonylphenol ethoxylates, castor oils, and carboxymethylated alcohol polyglycol ethers. 22 21/06/2011 18:53 No .: R396 P.026 / 033 cri-JUM-c; aii yonJLHta rmtNiwtbtN · 'witu Cbfd noi ery ^ ö Hn; + 4o i 3JD b.df'jj &quot; JJ - -1 "'Vi' * '' 99 '' ·« * · »» t * + • »» * * «« * * * * · t · i t r · «* 4 1 <1 '· *. «« • 9 * * * I # * 9 «f ►4» · 9 «99 ·« 9 * 4 Lenzing AG, PL0518
    [8]
    8. Regeneratcellulosefilament, characterized in that it has a strength in the conditioned state of more than 36 cN / tex,
    [9]
    9. Use of the Regeneratcellulosefilaments according to claims 1 5 to 8 for the production of a textile fabric, io
    [10]
    A continuous process for producing a high strength regenerated cellulose filament by spinning a viscose containing 4 to 8% cellulose, 5 to 10% NaOH, 36 to 42% (by weight of cellulose) carbon disulfide and 1 to 5% (by weight of cellulose) of a Modifier in a precipitation bath. Stripping the coagulated filaments, using a viscose whose spin gamma is SO to 66 and whose spin viscosity is 50 to 150 puff seconds; and that the temperature of the precipitation bath is 34 to 65 ° C, 15 a. the alkali ratio (= cellulose concentration / alkali content) of ready-to-spray viscose is 0.7 to 1.5, b. the following Fällbadkonzentrationen be used; • H2S04 66 - 9S g / l • Na2SO4 90 -160 g / l 20 • ZnSO4 30 - 65 g / l c. the final discharge from the precipitation bath and the winding takes place at a speed between 15 and 160 m / min. characterized in that 25 d. the filaments coagulated in the coagulation bath are then passed through a second bath, the second bath containing aqueous, 3-7% by weight sulfuric acid at a temperature of 80-98 ° C.
    [11]
    11. The method according to claim 11, wherein a cellulosic raw material used is a pulp having an α content of 93-99%.
    [12]
    The method of claim 11, wherein the filaments in the second bath are stretched by 70% to 105%. 23 21/06/2011 18:53 No .: R396 P.027 / 033 S.Ö3 'JJ ea-JUN-cSaii yonJLHb ι-ή i tm wtbtN'mtu i-HJ rbfd for Hn: + MJ i r> JWc ; H ... --- --- * '- - ♦ ····· * ♦' ·· '· ► # · · * · * · m ----- · - - * · · · « tf · * «« «L m m m m Lenzing AG, PL0518
    [13]
    13, The method of claim 11, wherein in the filaments, a pigment-like substance is spun in the form of a pigment dispersion. 5
    [14]
    14. A method according to claim 13, wherein the pigment dosage ratio is automatically controlled based on the spin solution flow and adjusted by means of a controlled metering pump. 10 1S, method according to claim 14, wherein the controlled metering pump is an eccentric screw pump,
    [15]
    16, The method of claim 15, wherein the pigment-like substance is selected from the group comprising flame-retardant, colored,] 5 fluorescent and X-ray detectable pigments.
    [16]
    17, The method of claim 16, wherein the pigment-like substance is at least partially a flame retardant substance.
    [17]
    18. The method according to claim 17, wherein so much of the flame-retardant substance is spun-in that the finished fiber is at least 2.8%, preferably between 3.2% and 6.0%, particularly preferably between 3.5% and 6.0%. Phosphorus, based on cellulose. 25 1Θ. A process according to claim 18, wherein the phosphorus in the form of the organophosphorus compound is 2,2''Oxybis [5,5-dimethyl-1,3,2 * dioxaphosphorinane] 2,2'-disulphide (I).
    [18]
    20, The method according to claim 17, wherein the pigment dispersion between 10 30 and 50% of the flame retardant substance having an average particle size (x ") less than 1.0 pm and a maximum particle size (Xflo) is less than 5.0 pm and between 1.5 and Contains 20% of a dispersing aid. 24 21/06/2011 18:53 Nr,: R396 P.028 / 033 'ü-JUN-eväii iCis uon: u-ta MH I fcN I WfcbbN' NiBi + HJS rbrd rm Hn: + Hs 1 bJHSH so »b .Cb 'JJ • t · · · * »Ir · · · #« · · • · I «V« * · ♦ • · * * * · t | Lenting AG, PL0518
    [19]
    21. The method according to claim 17, wherein additionally a dispersant for the flameproofing agent dispersion is used which is selected from the group consisting of modified polycarboxylates, water-soluble polyesters, alkyl ether phosphates, end-capped 5-naphthylol ethoxylates, castor oil alkoxyl esters and carboxymethylated alcohol polyglycol ethers.
    [20]
    22. The method according to claim 10, wherein the spinning of the viscose into the precipitation bath takes place in the form of a tube spinning process. 10 25
    类似技术:
    公开号 | 公开日 | 专利标题
    AT511638B1|2016-06-15|HIGHLY CELLULOSIC FILAMENT, ITS USE AND METHOD FOR THE PRODUCTION THEREOF
    EP2473657B1|2014-04-30|Fire-retardant cellulose fiber, use thereof, and method for the production thereof
    DE69723582T2|2004-05-13|REGENERATED CELLULOSE FIBERS AND METHOD FOR THEIR PRODUCTION
    AT501931B1|2007-08-15|CELLULOSE STAPLE FIBER AND ITS USE
    AT508846B1|2012-02-15|FLUORESCENT FIBERS, THEIR USE AND METHOD FOR THE PRODUCTION THEREOF
    WO2006000197A1|2006-01-05|Method and device for the production of molded cellulose bodies
    AT507758A1|2010-07-15|YARN AND THREADS FROM BLENDS OF FIBERS AND ARTICLES THEREFROM
    DE202013011959U1|2014-12-15|Direct-spun cellulose fibers, their preparation and use
    WO1997002315A1|1997-01-23|Regenerated cellulose incorporating phosphorous compounds so as to be flame-retardant
    EP0530652A2|1993-03-10|Device for the high-speed spinning of multifilament yarns and its use
    AT405531B|1999-09-27|METHOD FOR PRODUCING CELLULOSIC FIBERS
    WO2014128128A1|2014-08-28|Regenerated cellulose fibres, production and use thereof
    EP3019647A1|2016-05-18|Spunbonded nonwovens and threads made of lignin-containing fiber-forming polymers and a method for the production thereof
    DE971618C|1959-02-26|Process for the production of viscose artificial silk threads
    EP2707526B1|2015-11-25|Process for the production of regenerated cellulose fibers
    DE1258544B|1968-01-11|Process for the production of regenerated cellulose fibers and threads
    AU2018346452A1|2020-03-12|Flame retardant Lyocell filament
    EP3511371A1|2019-07-17|Reuse of insoluble particles from a cellulose precursor
    EP2664697B2|2018-05-23|Flame retardant cellulose regenerated fibers and process for their preparation
    WO1999057348A1|1999-11-11|Polyester fibres and filaments and method for producing them
    AT367805B|1982-08-10|METHOD FOR PRODUCING FIBERS FROM REGENERATED CELLULOSE
    AT206570B|1959-12-10|Process for the production of artificial threads and staple fibers from viscose
    EP3494249A1|2019-06-12|Reinforcing material for rubber assemblies, in particular in the form of a tire cord construction and method for the production thereof
    DE1494742A1|1969-12-11|Wet spinning process for the production of threads from aliphatic polyamides
    同族专利:
    公开号 | 公开日
    CN103703176B|2017-07-11|
    US20140205830A1|2014-07-24|
    WO2012174578A1|2012-12-27|
    AT511638B1|2016-06-15|
    TWI599686B|2017-09-21|
    EP3014002A1|2016-05-04|
    CN103703176A|2014-04-02|
    TW201319340A|2013-05-16|
    EP3014002B1|2017-08-09|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    WO1997002315A1|1995-07-05|1997-01-23|Lenzing Aktiengesellschaft|Regenerated cellulose incorporating phosphorous compounds so as to be flame-retardant|
    US20090272951A1|2006-03-03|2009-11-05|Birla Research Institute For Applied Research| Process for Preparing A Flame Retardant and Glow Resistent Zinc Free Cellulose Product|
    AT508687A1|2009-09-01|2011-03-15|Chemiefaser Lenzing Ag|FLAME-RESTRICTED CELLULOSIC FIBER, THEIR USE AND METHOD FOR THE PRODUCTION THEREOF|WO2017140428A1|2016-02-18|2017-08-24|Glanzstoff Industries Gmbh|Method for providing an amount of pigment|
    EP3260595A1|2016-06-20|2017-12-27|Glanzstoff Industries GmbH|Method for obtaining highly fire-retarding synthetic fibres from textile scraps, highly fire-retarding synthetic fibres and their use|BE513218A|1951-07-31|
    GB815509A|1956-07-25|1959-06-24|Courtaulds Ltd|Improvements relating to the production of regenerated cellulose filaments|
    NL99080C|1956-10-25|
    US3249450A|1962-09-21|1966-05-03|Interchem Corp|Coloring of regenerated cellulose|
    US3434913A|1964-12-28|1969-03-25|Fmc Corp|Viscose rayon fiber and method of making same|
    AT287905B|1968-09-20|1971-02-10|Chemiefaser Lenzing Ag|Process for the production of thread from regenerated cellulose|
    US3720743A|1970-10-20|1973-03-13|Itt|Process for producing high performance crimped rayon staple fiber|
    GB9019263D0|1990-09-04|1990-10-17|Sandoz Ltd|Improvements in or relating to organic compounds|
    AT401656B|1994-11-07|1996-11-25|Chemiefaser Lenzing Ag|FLAME RESISTANT NON-WOVEN TEXTILE FABRIC|
    CA2205459C|1994-12-12|2006-02-07|Akzo Nobel N.V.|Solvent-spun cellulosic filaments|
    DE10335863A1|2003-08-06|2005-03-03|Clariant Gmbh|Continuous process for the preparation of a pigment masterbatch|
    CN1590605A|2004-02-12|2005-03-09|湖北金环股份有限公司|High strength viscose long filament spinning technology and equipment|
    DE102004059221A1|2004-12-09|2006-06-14|Clariant Gmbh|Acrylic-based, water-based flame retardant dispersion|
    US20080001325A1|2006-06-30|2008-01-03|Mengkui Luo|Method for Processing High Hemicellulose Pulp in Viscose Manufacture|
    AT494406T|2006-07-28|2011-01-15|Chemiefaser Lenzing Ag|METHOD FOR THE PRODUCTION OF FLAME-RESISTANT VISCOSE FIBERS|
    AT508721B1|2009-09-03|2014-07-15|Chemiefaser Lenzing Ag|CELLULOSE FIBERS WITH IMPROVED DOSAGE ABILITY, METHOD FOR THE PRODUCTION THEREOF, AND THEIR USE FOR THE REINFORCEMENT OF COMPOSITE MATERIALS|
    AT508846B1|2009-09-17|2012-02-15|Chemiefaser Lenzing Ag|FLUORESCENT FIBERS, THEIR USE AND METHOD FOR THE PRODUCTION THEREOF|US11034817B2|2013-04-17|2021-06-15|Evrnu, Spc|Methods and systems for processing mixed textile feedstock, isolating constituent molecules, and regenerating cellulosic and polyester fibers|
    JP6399998B2|2015-12-28|2018-10-03|ユニ・チャーム株式会社|Water-decomposable nonwoven fabric and method for producing the same|
    CN106319729A|2016-08-20|2017-01-11|杭州华盛实业有限公司|Jacquard fabric for bags and manufacturing method of jacquard fabric|
    CN106400235B|2016-12-07|2019-03-01|北京赛欧兰阻燃纤维有限公司|Organic silazane system fire resistance fibre is blended with organic phosphorus fire resistance fibre|
    CN107974722A|2017-10-30|2018-05-01|宜宾丝丽雅股份有限公司|A kind of production technology of high-intensity fine denier flame retardant viscose fiber|
    CN107938010A|2017-10-30|2018-04-20|宜宾丝丽雅股份有限公司|A kind of high-intensity fine denier flame retardant viscose fiber and its production technology|
    CN107964693A|2017-10-30|2018-04-27|宜宾丝丽雅股份有限公司|A kind of production technology of high-strength anti-flaming viscose rayon|
    CN110172740B|2019-02-26|2020-12-22|东华大学|Preparation method of flame-retardant cellulose fiber|
    CN111058185B|2019-12-05|2021-02-09|湖北拓盈新材料有限公司|High-strength viscose non-woven fabric and preparation method thereof|
    法律状态:
    优先权:
    申请号 | 申请日 | 专利标题
    ATA905/2011A|AT511638B1|2011-06-21|2011-06-21|HIGHLY CELLULOSIC FILAMENT, ITS USE AND METHOD FOR THE PRODUCTION THEREOF|ATA905/2011A| AT511638B1|2011-06-21|2011-06-21|HIGHLY CELLULOSIC FILAMENT, ITS USE AND METHOD FOR THE PRODUCTION THEREOF|
    US14/128,242| US20140205830A1|2011-06-21|2012-06-18|High strength cellulosic filament its use, and method for the production thereof|
    PCT/AT2012/000170| WO2012174578A1|2011-06-21|2012-06-18|High-strength cellulosic filament, use thereof and method for production thereof|
    EP12747962.4A| EP3014002B1|2011-06-21|2012-06-18|Method for production of cellulosic filaments|
    CN201280030577.6A| CN103703176B|2011-06-21|2012-06-18|High strength fibre element long filament, its purposes and its manufacture method|
    TW101122083A| TWI599686B|2011-06-21|2012-06-20|High-strength cellulosic filament, its use, and method for the production thereof|
    [返回顶部]