    • 专利摘要:
    The present invention provides improved methods and compositions for cementing pipe strings in well bores. The methods of the invention are basically comprised of preparing a cement composition comprised of a hydraulic cement, an epoxy resin, a hardening agent for the epoxy resin and sufficient water to form a pumpable slurry. Thereafter, the cement composition is introduced into the annulus between a pipe string and a well bore and the cement composition is allowed to set into a resilient impermeable solid mass.
    公开号:US20010009133A1
    申请号:US09/784,290
    申请日:2001-02-13
    公开日:2001-07-26
    发明作者:Jiten Chatterji；Roger Cromwell；Robert Kuhlman；Bobby King
    申请人:Jiten Chatterji；Cromwell Roger S.；Kuhlman Robert D.；King Bobby J.；
    IPC主号:C04B24-18
    专利说明:
    [0001] 1. Field of the Invention [0001]
    [0002] The present invention relates generally to cementing subterranean wells, and more particularly, to cement compositions which set into resilient impermeable solid masses and methods of using the compositions. [0002]
    [0003] 2. Description of the Prior Art [0003]
    [0004] Hydraulic cement compositions are commonly utilized in primary cementing operations whereby pipe strings such as casings and liners are cemented in well bores. In performing primary cementing, a hydraulic cement composition is pumped into the annular space between the walls of the well bore and the exterior surfaces of the pipe string disposed therein. The cement composition is permitted to set in the annular space thereby forming an annular sheath of hardened substantially impermeable cement therein. The cement sheath physically supports and positions the pipe string in the well bore and bonds the exterior surfaces of the pipe string to the walls of the well bore whereby the undesirable migration of fluids between zones or formations penetrated by the well bore is prevented. [0004]
    [0005] The cement compositions utilized in primary cementing must often be lightweight to prevent excessive hydrostatic pressures from being exerted on formations penetrated by well bores. A particularly suitable technique for making a hydraulic cement composition lightweight is to foam the cement composition with a gas such as air or nitrogen. In primary cementing, a foamed cement composition provides the additional advantage of being compressible whereby formation fluids are less likely to enter the annulus and flow through the cement composition therein during the transition time of the cement composition, i.e., the time after the placement of a cement composition in the annulus during which the cement composition changes from a true fluid to a hard set mass. [0005]
    [0006] The development of wells including one or more laterals to increase production has recently taken place. Such multi-lateral wells include vertical or deviated (including horizontal) principal well bores having one or more ancillary laterally extending well bores connected thereto. Drilling and completion equipment has been developed which allows multiple laterals to be drilled from a principal cased and cemented well bore. Each of the lateral well bores can include a liner cemented therein which is tied into the principal well bore. The lateral well bores can be vertical or deviated and can be drilled into predetermined producing formations or zones at any time in the productive life cycle of the well. [0006]
    [0007] In both conventional single bore wells and multi-lateral wells having several bores, the cement composition utilized for cementing casing or liners in the well bores must develop high bond strength after setting and also have sufficient resiliency, i.e., elasticity and ductility, to resist loss of pipe or formation bond, cracking and/or shattering as a result of pipe movements, impacts and/or shocks subsequently generated by drilling and other well operations. The bond loss, cracking and/or shattering of the set cement allows leakage of formation fluids through at least portions of the well bore or bores which can be highly detrimental. [0007]
    [0008] The set cement in a well, and particularly the set cement forming a cement sheath in the annulus between a pipe string and the walls of a well bore, often fails due to shear and compressional stresses exerted on the set cement. Such stress conditions are commonly the result of relatively high fluid pressures and/or temperatures inside the cemented pipe string during testing, perforating, fluid injection and/or fluid production. The high internal pipe pressure and/or temperature results in the expansion of the pipe string, both radially and longitudinally, which places stresses on the cement sheath causing it to crack or the cement bonds between the exterior surfaces of the pipe and/or the well bore walls to fail whereby the loss of hydraulic seal in the annulus occurs. [0008]
    [0009] Another condition results from exceedingly high pressures which occur inside the cement sheath due to the thermal expansion of fluids trapped within the cement sheath. This condition often occurs as a result of high temperature differentials created during the injection or production of high temperature fluids through the well bore, e.g., wells subjected to steam recovery or the production of hot formation fluids from high temperature formations. Typically, the pressure of the trapped fluids exceeds the collapse pressure of the cement and pipe causing leaks and bond failure. [0009]
    [0010] Yet another compressional stress condition occurs as a result of outside forces exerted on the cement sheath due to formation shifting, overburden pressures, subsidence and/or tectonic creep. [0010]
    [0011] In multi-lateral wells wherein pipe strings have been cemented in well bores using conventional well cement slurries which set into brittle solid masses, the brittle set cement cannot withstand impacts and shocks subsequently generated by drilling and other well operations carried out in the multiple laterals without cracking or shattering. [0011]
    [0012] The above described failures can result in loss of production, environmental pollution, hazardous rig operations and/or hazardous production operations. The most common hazard is the presence of gas pressure at the well head. [0012]
    [0013] Thus, there are needs for improved well cement compositions and methods whereby after setting, the cement compositions are highly resilient and can withstand the above described stresses without failure. That is, there is a need for well cement compositions and methods whereby the cement compositions have improved mechanical properties including elasticity and ductility and failures due to pipe movement, impacts and shocks are reduced or prevented. [0013] SUMMARY OF THE INVENTION
    [0014] The present invention provides improved methods of cementing pipe strings in well bores and improved cement compositions that upon setting form resilient solid masses which meet the needs described above and overcome the deficiencies of the prior art. The improved methods of the invention are basically comprised of the steps of preparing an improved cement composition of this invention, introducing the cement composition into the annulus between a pipe string and a well bore and allowing the cement composition to set into a resilient impermeable solid mass therein. [0014]
    [0015] The improved compositions of this invention are basically comprised of a hydraulic cement, an epoxy resin, an epoxy resin hardening agent and sufficient water to form a pumpable slurry. The compositions can also optionally include amorphous silica powder, a dispersing agent, a set retarding agent and other suitable additives well known to those skilled in the art. Further, when required, the densities of the cement compositions can be reduced by foaming the compositions, i.e., including a gas, a foaming agent and a foam stabilizer in the compositions. [0015]
    [0016] It is, therefore, a general object of the present invention to provide improved methods of cementing pipe strings in well bores and improved cement compositions which set into resilient impermeable solid masses. [0016]
    [0017] Other and further objects, features and advantages of the present invention will be readily apparent to those skilled in the art upon a reading of the description of preferred embodiments which follows. [0017] DESCRIPTION OF PREFERRED EMBODIMENTS
    [0018] The present invention provides improved methods and compositions for cementing pipe strings in well bores. The cement compositions have improved resiliency without compromising strength or fatigue resistance. While the methods and compositions are useful in a variety of well completion and remedial operations, they are particularly useful in primary cementing, i.e., cementing casings and liners in well bores. [0018]
    [0019] A non-foamed cement composition of this invention is basically comprised of a hydraulic cement, an epoxy resin, a hardening agent for the epoxy resin and sufficient water to form a pumpable slurry. A variety of hydraulic cements can be utilized in accordance with the present invention including those comprised of calcium, aluminum, silicon, oxygen and/or sulfur which set and harden by reaction with water. Such hydraulic cements include Portland cements, pozzolana cements, gypsum cements, high aluminum content cements, silica cements and high alkalinity cements. Portland cements or their equivalents are generally preferred for use in accordance with the present invention. Portland cements of the types defined and described in [0019] API Specification For Materials And Testing For Well Cements, API Specification 10, 5th Edition, dated Jul. 1, 1990 of the American Petroleum Institute are particularly suitable. Preferred API Portland cements include classes A, B, C, G and H, with API classes G and H being more preferred and class G being the most preferred.
    [0020] A variety of hardenable epoxy resins can be utilized in the cement compositions of this invention. Preferred epoxy resins are those selected from the condensation products of epichlorohydrin and bisphenol A. A particularly suitable such resin is commercially available from the Shell Chemical Company under the trade designation “EPON®RESIN 828.” This epoxy resin has a molecular weight of about 340 and a one gram equivalent of epoxide per about 180 to about 195 grams of resin. Another suitable epoxy resin is an epoxidized bisphenol A novolac resin which has a one gram equivalent of epoxide per about 205 grams of resin. [0020]
    [0021] For ease of mixing, the epoxy resin utilized is preferably pre-dispersed in a non-ionic aqueous fluid. A non-ionic aqueous dispersion of the above described condensation product of epichlorohydrin and bisphenol A is commercially available from the Shell Chemical Company under the trade designation “EPI-REZ®-3510-W-60.” Another non-ionic aqueous dispersion of an epoxy resin comprised of a condensation product of epichlorohydrin and bisphenol A having a higher molecular weight than the above described resin is also commercially available from the Shell Chemical Company under the trade designation “EPI-REZ®-3522-W-60.” The above mentioned epoxidized bisphenol A novolac resin is commercially available in a non-ionic aqueous dispersion from the Shell Chemical Company under the trade designation “EPI-REZ®-5003-W-55.” Of the foregoing non-ionic aqueous dispersions of epoxy resins, the aqueous dispersion of the condensation product of epichlorohydrin and bisphenol A having a molecular weight of about 340 and a one gram equivalent of epoxide per about 180 to about 195 grams of resin is the most preferred. [0021]
    [0022] The epoxy resin utilized is included in the compositions of this invention in an amount in the range of from about 5% to about 20% by weight of hydraulic cement in the composition, most preferably in an amount of about 8% to about 10%. [0022]
    [0023] A variety of hardening agents, including, but not limited to, aliphatic amines, aliphatic tertiary amines, aromatic amines, cycloaliphatic amines, heterocyclic amines, amidoamines, polyamides, polyethyleneamines and carboxylic acid anhydrides can be utilized in the compositions of this invention containing the above described epoxy resins. Of these, aliphatic amines, aromatic amines and carboxylic acid anhydrides are the most suitable. [0023]
    [0024] Examples of aliphatic and aromatic amine hardening agents are triethylenetetraamine, ethylenediamine, N-cocoalkyltrimethylenediamine, isophoronediamine, diethyltoluenediamine, and tris(dimethylaminomethylphenol). Examples of suitable carboxylic acid anhydrides are methyltetrahydrophthalic anhydride, hexahydrophthalic anhydride, maleic anhydride, polyazelaic polyanhydride and phthalic anhydride. Of these, triethylenetetraamine, ethylenediamine, N-cocoalkyltrimethylenediamine, isophoronediamine, diethyltoluenediamine and tris(dimethylaminomethylphenol) are preferred, with isophoronediamine, diethyltoluenediamine and tris(dimethylaminomethylphenol) being the most preferred. [0024]
    [0025] The hardening agent or agents utilized are generally included in the cement compositions of this invention in an amount in the range of from about 0.01% to about 0.02% by weight of hydraulic cement in the compositions. [0025]
    [0026] The water in the cement compositions which is in addition to the water contained in the non-ionic aqueous dispersions of epoxy resin is included in the compositions to make the compositions pumpable. The water can be from any source provided it does not contain compounds that adversely effect other components in the cement compositions. However, fresh water is preferred. Generally, water is present in the compositions in an amount in the range of from about 20% to about 45% by weight of the hydraulic cement in the compositions, more preferably in the range of from about 25% to about 30%. [0026]
    [0027] Another component which can optionally be included in the cement compositions of this invention is a set retarding agent. Set retarding agents are included in a cement composition when it is necessary to extend the time in which the cement composition can be pumped so that it will not thicken or set prior to being placed in a desired location in the well being cemented. Examples of set retarding agents which can be used include lignosulfonates such as calcium and sodium lignosulfonate, such lignosulfonates modified by reaction with formaldehyde and sodium bisulfite, organic acids such as tartaric acid and gluconic acid, a copolymer or copolymer salt of 2-acrylamido-2-methyl propane sulfonic acid and acrylic acid and others. A particularly suitable set retarding agent for use in the cement compositions of the present invention is calcium lignosulfonate modified by reaction with formaldehyde and sodium bisulfite. This set retarding agent is commercially available under the trade name “HR-6L™” from Halliburton Energy Services, Inc. of Duncan, Okla. [0027]
    [0028] The proper amount of set retarding agent required for particular conditions can be determined by conducting a thickening time test for the particular set retarding agent and cement composition. Such tests are described in the [0028] API Specification For Materials And Testing For Well Cements, API Specification 10, mentioned above. Generally, the set retarding agent utilized is added to a cement composition of this invention in an amount in the range of from about 0.1% to about 3% by weight of hydraulic cement in the composition.
    [0029] Other components which can optionally be included in the cement compositions of this invention are amorphous silica powder and a dispersing agent. The amorphous silica powder improves the compressive strength and other mechanical properties of the cement composition and the dispersing agent facilitates the dispersion of the amorphous silica powder and other solids in the compositions. [0029]
    [0030] Suitable amorphous silica powder which can be utilized is commercially available under the trade designation “SILICALITE™” from Halliburton Energy Services, Inc. of Duncan, Okla. While various dispersing agents can be utilized, a particularly suitable such dispersing agent is comprised of the condensation reaction product of formaldehyde, acetone and sodium bisulfite. This dispersing agent is commercially available under the trade designation “CFR-3™” from Halliburton Energy Services, Inc. of Duncan, Okla. [0030]
    [0031] When used, the amorphous silica powder is included in the cement compositions of this invention in an amount in the range of from about 10% to about 20% by weight of hydraulic cement in the compositions. The dispersing agent used is included in the composition in an amount in the range of from about 0.05% to about 1% by weight of hydraulic cement therein. [0031]
    [0032] The above described non-foamed cement compositions of this invention can be foamed by combining a compressible gas with the compositions in an amount sufficient to foam the compositions and produce a desired density along with an effective amount of a foaming agent and an effective amount of a foam stabilizer. As mentioned above, the presence of a compressible gas in the cement compositions helps prevent pressurized formation fluid influx into the cement compositions while they are setting and contributes to the resiliency of the set cement compositions. [0032]
    [0033] The gas utilized is preferably selected from nitrogen and air, with nitrogen being the most preferred. Generally, the gas is present in an amount sufficient to foam the cement compositions and produce a cement composition density in the range of from about 10 to about 16 pounds per gallon, more preferably from about 12 to about 14 pounds per gallon. [0033]
    [0034] The foaming agent functions to facilitate foaming. Suitable foaming agents are surf actants having the general formula:[0034]
    [0035] wherein: [0035]
    [0036] a is an integer in the range of from about 5 to about 15; [0036]
    [0037] b is an integer in the range of from about 1 to about 10; and [0037]
    [0038] X is any compatible cation. [0038]
    [0039] A particularly preferred foaming agent of the above type is a surfactant having the formula:[0039]
    [0040] wherein: [0040]
    [0041] a is an integer in the range of from about 6 to about 10. [0041]
    [0042] This surfactant is commercially available under the trade designation “CFA-S™” from Halliburton Energy Services, Inc. of Duncan, Okla. [0042]
    [0043] Another particularly preferred foaming agent of the above mentioned type is a surfactant having the formula:[0043]
    [0044] wherein: [0044]
    [0045] a is an integer in the range of from about 5 to about 15; and [0045]
    [0046] b is an integer in the range of from about 1 to about 10. [0046]
    [0047] This surfactant is commercially available under the trade name “HALLIBURTON FOAM ADDITIVE™” from Halliburton Energy Services, Inc. of Duncan, Okla. [0047]
    [0048] Another foaming agent which can be utilized in the cement compositions of this invention includes polyethoxylated alcohols having the formula:[0048]
    [0049] H(CH[0049]   2)a(OC2H4)bOH
    [0050] [0050]
    [0051] wherein: [0051]
    [0052] a is an integer in the range of from about 10 to about 18; and [0052]
    [0053] b is an integer in the range of from about 6 to about 15. [0053]
    [0054] This surfactant is available from Halliburton Energy Services under the trade name “AQF-1™.” [0054]
    [0055] Yet another foaming agent which can be used is a sodium salt of alpha-olefinic sulfonic acid (AOS) which is a mixture of compounds of the formulas:[0055]
    [0056] wherein: [0056]
    [0057] n and m are individually integers in the range of from about 6 to about 16; [0057]
    [0058] p and q are individually integers in the range of from about 7 to about 17; and [0058]
    [0059] X and Y are fractions with the sum of X and Y being 1. [0059]
    [0060] This foaming agent is available from Halliburton Energy Services under the trade name “AQF-2™.” [0060]
    [0061] Still another foaming surfactant which can be used is an alcohol ether sulfate of the formula:[0061]
    [0062] wherein: [0062]
    [0063] a is an integer in the range of from about 6 to about 10; and [0063]
    [0064] b is an integer in the range of from about 3 to about 10. [0064]
    [0065] The particular foaming agent employed will depend on various factors such as the types of formations in which the foamed cement is to be placed. Generally, the foaming agent utilized is included in a cement composition of this invention in an amount in the range of from about 1.5% to about 10% by weight of water in the composition. When the foaming agent is one of the preferred surfactants described above, it is included in the composition in an amount in the range of from about 3% to about 5% by weight of water therein. [0065]
    [0066] A foam stabilizer is also included in the foamed cement compositions to enhance the stability of the foam. One such foam stabilizing agent is a compound of the formula: [0066]
    [0067] wherein: [0067]
    [0068] R is hydrogen or a methyl radical; and [0068]
    [0069] n is an integer in the range of from about 20 to about 200. [0069]
    [0070] A particularly preferred foam stabilizing agent of the above type is a methoxypolyethylene glycol of the formula:[0070]
    [0071] wherein: [0071]
    [0072] n is in the range of from about 100 to about 150. [0072]
    [0073] This foam stabilizing agent is commercially available from Halliburton Energy Services under the trade designation “HALLIBURTON FOAM STABILIZER™.” [0073]
    [0074] The most preferred foam stabilizing agent is an amidopropylbetaine having the formula:[0074]
    [0075] wherein: [0075]
    [0076] R is a C[0076] 10 to C18 saturated aliphatic hydrocarbon group, an oleyl group or a linoleyl group.
    [0077] A particularly suitable stabilizing agent of the above type is a cocoylamidopropylbetaine. This foam stabilizing agent is commercially available from Halliburton Energy Services under the trade designation “HC-2™.” [0077]
    [0078] The foam stabilizer is generally included in a cement composition of this invention in an amount in the range of from about 0.75% to about 5% by weight of water therein. When the foam stabilizing agent is one of the particularly preferred agents described above, it is preferably present in the composition in an amount in the range of from about 1.5% to about 2.5% by weight of water. [0078]
    [0079] Thus, an improved well cement composition of this invention is comprised of a hydraulic cement, an epoxy resin selected from the group of a condensation reaction product of epichlorohydrin and bisphenol A and an epoxidized bisphenol A novolac resin present in an amount in the range of from about 8% to about 10% by weight of hydraulic cement in the composition, a hardening agent for the epoxy resin selected from the group of aliphatic amines, aromatic amines and carboxylic acid anhydrides present in an amount in the range of from about 0.01% to about 0.02% by weight of hydraulic cement in the composition, and sufficient water to form a pumpable slurry. [0079]
    [0080] Another composition of the present invention is comprised of a hydraulic cement, an epoxy resin selected from the group of a condensation reaction product of epichlorohydrin and bisphenol A and an epoxidized bisphenol A novolac resin present in an amount in the range of from about 8% to about 10% by weight of hydraulic cement in the composition, a hardening agent for the epoxy resin selected from the group of aliphatic amines, aromatic amines and carboxylic acid anhydrides present in the composition in an amount in the range of from about 0.01% to about 0.02% by weight of hydraulic cement in the composition, a set retarding agent, e.g., an alkali metal or alkaline earth metal lignosulfonate modified by reaction with formaldehyde and sodium bisulfite, present in an amount in the range of from about 0.1% to about 3% by weight of hydraulic cement in the composition, amorphous silica powder present in an amount in the range of from about 10% to about 20% by weight of hydraulic cement in the composition, a dispersing agent, e.g., the condensation reaction product of formaldehyde, acetone and sodium bisulfite, present in an amount in the range of from about 0.05% to about 1% by weight of hydraulic cement in the composition and sufficient water to form a pumpable slurry. [0080]
    [0081] Yet another composition of this invention is comprised of a hydraulic cement, an epoxy resin selected from the group of a condensation reaction product of epichlorohydrin and bisphenol A and an epoxidized bisphenol A novolac resin present in an amount in the range of from about 8% to about 10% by weight of hydraulic cement in the composition, a hardening agent for said epoxy resin selected from the group of aliphatic amines, aromatic amines and carboxylic acid anhydrides present in an amount in the range of from about 0.01% to about 0.02% by weight of hydraulic cement in the composition, water present in an amount of about 25% to about 35% by weight of hydraulic cement in the composition, a gas present in an amount sufficient to form a foam having a density in the range of from about 12 to about 14 pounds per gallon, a foaming agent, e.g., a sodium salt of alpha-olefinic sulfonic acid, present in an amount in the range of from about 3% to about 5% by weight of water in the composition and a foam stabilizer, e.g., cocoylamidopropylbetaine, present in an amount in the range of from about 1.5% to about 2.5% by weight of water in the composition. [0081]
    [0082] Still another composition of this invention is comprised of a hydraulic cement, an epoxy resin selected from the group of a condensation reaction product of epichlorohydrin and bisphenol A and an epoxidized bisphenol A novolac resin present in an amount in the range of from about 8% to about 10% by weight of hydraulic cement in the composition, a hardening agent for the epoxy resin selected from the group of aliphatic amines, aromatic amines and carboxylic acid anhydrides present in an amount in the range of from about 0.01% to about 0.02% by weight of hydraulic cement in the composition, water present in an amount in the range of from about 25% to about 35% by weight of hydraulic cement in the composition, a set retarding agent, e.g., an alkali metal or alkaline earth metal lignosulfonate modified by reaction with formaldehyde and sodium bisulfite, present in an amount in the range of from about 0.1% to about 3% by weight of hydraulic cement in the composition, amorphous silica powder present in an amount in the range of from about 10% to about 20% by weight of hydraulic cement in the composition, a dispersing agent, e.g., the condensation reaction product of formaldehyde, acetone and sodium bisulfite, present in an amount in the range of from about 0.05% to about 1% by weight of hydraulic cement in the composition, a gas selected from the group of air and nitrogen present in an amount sufficient to foam the cement composition, an effective amount of a foaming agent, e.g., the sodium salt of an alpha-olefinic sulfonic acid, present in an amount in the range of from about 3% to about 5% by weight of water in the composition and a foam stabilizer, e.g., cocoylamidopropylbetaine, present in an amount in the range of from about 1.5% to about 2.5% by weight of water therein. [0082]
    [0083] As mentioned, the improved methods of the present invention for cementing a pipe string in a well bore are basically comprised of preparing a cement composition of the present invention as described above, introducing the cement composition into the annulus between a pipe string and a well bore and allowing the cement composition to set into a resilient impermeable mass. [0083]
    [0084] In order to further illustrate the methods and compositions of this invention, the following examples are given. [0084] EXAMPLE 1
    [0085] An unfoamed composition of the present invention having a density of 16.4 pounds per gallon was prepared by mixing 720 grams of Premium cement with 234.6 grams of water, 58.6 grams of a non-ionic aqueous dispersion of an epoxy resin and 0.9 grams of a hardening agent for the epoxy resin. The cement composition was divided into test samples and various quantities of a set retarding agent were added to some of the test samples. [0085]
    [0086] A second unfoamed cement composition of the invention having a density of 16.4 pounds per gallon was prepared by combining 720 grams of Premium cement with 252.8 grams of water, 0.5 grams of a dispersing agent and 80 grams of amorphous silica powder. This cement slurry was also divided into test samples and a set retarding agent was added to some of the test samples. [0086]
    [0087] Foamed cement composition test samples were prepared by first mixing 720 grams of premium cement with 234.6 grams of water, 58.6 grams of an aqueous dispersion of an epoxy resin and 0.9 grams of a hardening agent. This cement slurry having a density of 16.4 pounds per gallon was divided into test samples and a set retarding agent was added to some of the test samples. The test samples were then foamed to a density of 14 pounds per gallon with air after combining a foaming agent, i.e., a sodium salt of an alpha-olefinic sulfonic acid, in an amount of about 1.67% by weight of water and a foam stabilizer, i.e., a cocoylamidopropylbetaine, in an amount of 0.83% by weight of water with the test samples. [0087]
    [0088] Additional foamed cement composition test samples were prepared by mixing 720 grams of premium cement with 252.8 grams of water, 0.5 grams of a dispersing agent and 80 grams of amorphous silica powder. The resulting cement slurry having a density of 16.4 pounds per gallon was divided into test samples and various amounts of a set retarder were added to some of the test samples. The test samples were next foamed with air to a density of 14 pounds per gallon after adding a foaming agent, i.e., a sodium salt of an alpha-olefinic sulfonic acid, to the test samples in an amount of 1.67% by weight of water and a foam stabilizer, i.e., a cocoylamidopropylbetaine to the test samples in an amount of 0.83% by weight of water. [0088]
    [0089] The test samples of the compositions of the present invention described above were tested for thickening times at 140° F. in accordance with the procedures set forth in the API Specification 10 mentioned above. The components and their quantities in the various cement composition test samples described above as well as the results of the thickening time tests are given in Table I below. [0089] TABLE I Cement Composition Test Sample Components, Quantities and Thickening TimesSet Amorphous Cement Retarding Epoxy Epoxy Hardening Dispersing Silica Thickening Composition Unfoamed Foamed Agent1, % Resin2, % Resin3, % Agent4, % Agent5, % Powder6, % Time @ Test Sample Density, Density, by weight by weight by weight by weight by weight by weight of 140° F., No. lb/gal lb/gal of cement of cement of cement of cement of cement cement Hr:Min 1 16.4 — 0.32 7.2 — 1.0 — — 3:05 2 16.4 — — — 7.2  0.86 — — 3:15 3 16.4 — 0.32 — 7.2 1.0 0.062 10 2:35 4 16.4 — 0.10 — — — 0.062 10 — 5 16.4 — 0.10 — — — 0.062 — — 6 — 14 0.32 7.2 — 1.0 — — 3:45 7 — 14 — — 7.2  0.86 — — 3:29 8 — 14 0.32 7.2 — 1.0 0.062 10 2:45 9 — 14 0.10 — 7.2  0.86 0.062 10 1:48 10 — 14 0.10 — — — 0.062 10 — 11 — 14 0.10 — — — 0.062 — —
    [0090] From Table I it can be seen that the thickening times of the compositions of the present invention are within acceptable limits for cementing pipe strings in well bores. [0090]
    [0091] The cement composition test samples described above were cured for 72 hours at 140° F. Thereafter, Young's moduli, Poisson's ratios and compressive strengths were determined under 0, 500, 1,000 and 2,000 psi confining pressures. The cement composition test samples were also tested for Brazilian tensile strengths and Mohr-Coulomb failure envelopes were created. The results of these tests are set forth in Table II below. [0091] TABLE II Mechanical Properties of Hardened Cement Composition Test Samples Cement Composition Young's Friction Test Sample Confining Compressive Tensile Modulus, Poisson's Angle, No. Pressure, psi Strength, psi Strength, psi 106 psi Ratio degrees 1   0 9852 454 1.4 0.14 26.5  500 8634 1.4 0.20 1000 9919 1.4 0.23 2000 11532  1.0 0.19 2   0 8524 432 1.6 0.15 28  500 8247 1.3 0.20 1000 7696 0.74 0.14 2000 12557  1.1 0.16 3   0 8869 487 1.5 0.16 26  500 10047  1.4 0.13 1000 11584  1.4 0.21 2000 13896  1.4 0.27 4   0 8832 390 1.6 0.14 26.75  500 10258  1.2 0.24 1000 11958  1.3 0.19 2000 13258  0.93 0.20 5   0 8956 467 1.7 0.14 27  500 10401  1.5 0.29 1000 12166  1.6 0.28 2000 14419  1.4 0.23 6   0 2712 247 1.2 0.13 34  500 4825 0.88 0.18 1000 4978 0.75 0.20 2000 9719 1.3 0.16 7   0 3122 286 1.0 0.13 12  500 3938 0.75 0.13 1000 5297 0.95 0.16 2000 6198 0.84 0.12 8   0 4669 262 0.87 0.13 14.5  500 5094 0.95 0.25 1000 6031 1.1 0.17 2000 7849 1.0 0.16 9   0 3922 234 0.87 0.14 8  500 4607 0.81 0.25 1000 5338 0.58 0.16 2000 6490 0.14 0.18 10    0 3833 343 1.0 0.15 24.5  500 5562 1.0 0.24 1000 6600 0.74 0.20 2000 8098 0.37 0.11 11    0 3088 290 0.75 0.13 21.1  500 4074 0.78 0.23 1000 5440 0.86 0.21 2000 7364 0.72 0.18
    [0092] As shown in Table II, unfoamed cement Composition Test Sample No. 3 performed better than the other unfoamed test samples which included epoxy resin and hardening agent. The compressive strengths were nearly the same as unfoamed cement composition test samples 4 and 5 which did not include epoxy resin and hardening agent (hereinafter referred to as “neat test samples”). The elastic properties of Test Sample No. 3 were lower, i.e., Test Sample No. 3 had an average Young's modulus of 1.43×10[0092] 6 psi versus an average Young's modulus of 1.53×106 psi for a neat test sample, i.e., Test Sample No. 5. Poisson's ratio for the test samples containing epoxy resin and hardening agent, i.e., Test Samples Nos. 1, 2 and 3 was an average of 0.18 which is significantly lower then 0.24 for Test Sample No. 5. Test Sample No. 1 which is similar to Test Sample No. 3 did not include amorphous silica powder and a dispersing agent. Test Sample No. 1 performed as well as Test Sample No. 3 at lower confinements, but had a somewhat lower strength at higher confinements. The other test samples containing epoxy resin and hardening agent (Test Sample Nos. 2 and 3) showed similar Young's moduli and Poisson's ratios which means that the inclusion of epoxy resin and hardening agent in the cement composition imparts improved elasticity.
    [0093] Poisson's ratio is a measure of a body's strain growth orthogonal to the direction of applied stress. The results shown in Table II indicate that the cement compositions containing epoxy resin and hardening agent will have better shear bonds with a pipe string because it will be less flexible in lateral directions during loading of the pipe string. Tectonic creep and subsidence of rock formations cause increased stress loading and considerable displacement around the well bore. The lower Poisson's ratios of the test samples including epoxy resin and hardening agent indicate that the set cement compositions of this invention will maintain their original shapes. The low Young's moduli indicate that the cement compositions will be more flexible in situations where there are large changes in loading. Another benefit is the apparent proclivity of a number of the test samples including epoxy resin and hardening agent towards high toughness, allowing a large amount of plastic creep. [0093]
    [0094] As also shown in Table II, the angles of internal friction from the Mohr-Coulomb shear failure envelopes are 20° to 30° which is in the range of more elastic rock. The angle of internal friction is often a measure of a material's shear tendency. A steep angle is interpreted as a stiff, brittle material with high shear strength. The lower the angle of internal friction, the lower shear strength and less stable is the tested material under eccentric or changing compressive loads. Moderate angles of internal friction such as those observed for the various cement compositions including epoxy resin and hardening agent shown in Table II indicate a more malleable, flexible material with reasonable toughness. [0094]
    [0095] Of the foamed cement composition test samples containing epoxy resin and hardening agent, Test Sample No. 8 (equivalent to unfoamed Test Sample No. 3) performed best. It was better than the neat Test Sample No. 11, but slightly weaker than the neat Test Sample No. 10 which contained amorphous silica powder and dispersing agent. The Mohr-Coulomb failure envelope friction angles are also considered to be of high quality. Thus, the unfoamed and foamed cement compositions of this invention containing epoxy resin and hardening agent can withstand a variety of loading conditions. The cement compositions are particularly suitable for cementing pipe strings in well bores and in multi-lateral junctions which undergo rigorous cyclic loading, often in the form of impacts and shocks. In addition, the resilient set cement compositions of this invention have a better resistance to the effects of drawdown and depletion of formations surrounding the well bore as well as to subsidence and tectonic creep which often cause well bore failure and casing collapse. [0095]
    [0096] Thus, the present invention is well adapted to carry out the objects and attain the ends and advantages mentioned as well as those which are inherent therein. While numerous changes may be made by those skilled in the art, such changes are encompassed within the spirit of this invention as defined by the appended claims. [0096]
    权利要求:
    Claims (24)
    [1" id="US-20010009133-A1-CLM-00001] 1. An improved method of cementing a pipe string in a well bore comprising the steps of:
    (a) preparing a cement composition comprised of a hydraulic cement, an epoxy resin, a hardening agent for said epoxy resin and sufficient water to form a pumpable slurry;
    (b) introducing said cement composition into the annulus between said pipe string and said well bore; and
    (c) allowing said cement composition to set into a resilient impermeable solid mass.
    [2" id="US-20010009133-A1-CLM-00002] 2. The method of
    claim 1 wherein said hydraulic cement in said composition is a Portland cement or the equivalent thereof.
    [3" id="US-20010009133-A1-CLM-00003] 3. The method of
    claim 1 wherein said epoxy resin in said composition is selected from the group of a condensation reaction product of epichlorohydrin and bisphenol A and an epoxidized bisphenol A novolac resin and is present in an amount in the range of from about 5% to about 20% by weight of hydraulic cement therein.
    [4" id="US-20010009133-A1-CLM-00004] 4. The method of
    claim 1 wherein said hardening agent in said composition is at least one member selected from the group of aliphatic amines, aromatic amines and carboxylic acid anhydrides and is present in an amount in the range of from about 0.01% to about 0.02% by weight of hydraulic cement therein.
    [5" id="US-20010009133-A1-CLM-00005] 5. The method of
    claim 1 wherein said composition further comprises a set retarding agent present in an amount in the range of from about 0.1% to about 3% by weight of hydraulic cement therein.
    [6" id="US-20010009133-A1-CLM-00006] 6. The method of
    claim 1 wherein said composition further comprises amorphous silica powder present in an amount in the range of from about 10% to about 20% by weight of hydraulic cement therein.
    [7" id="US-20010009133-A1-CLM-00007] 7. The method of
    claim 1 wherein said composition further comprises a dispersing agent present in an amount in the range of from about 0.05% to about 1% by weight of hydraulic cement in said composition.
    [8" id="US-20010009133-A1-CLM-00008] 8. The method of
    claim 1 wherein said composition further comprises a gas, a foaming agent and a foam stabilizer.
    [9" id="US-20010009133-A1-CLM-00009] 9. The method of
    claim 8 wherein said gas in said composition is selected from the group of air and nitrogen and is present in said composition in an amount sufficient to produce a composition density in the range of from about 10 to about 16 pounds per gallon.
    [10" id="US-20010009133-A1-CLM-00010] 10. The method of
    claim 8 wherein said foaming agent in said composition is selected from the group of foaming agents comprised of the sodium salts of alpha-olefinic sulfonic acids and mixtures thereof and is present in an amount in the range of from about 3% to about 5% by weight of water in said composition.
    [11" id="US-20010009133-A1-CLM-00011] 11. The method of
    claim 8 wherein said foam stabilizer in said composition is selected from the group of foam stabilizers having the formula R—CONHCH2CH2CH2N+(CH3)2CH2CO2 wherein R is a C10-C18 saturated aliphatic group, an oleyl group or a linoleyl group and is present in an amount in the range of from about 1.5% to about 2.5% by weight of water in said composition.
    [12" id="US-20010009133-A1-CLM-00012] 12. An improved well cement composition comprising:
    a hydraulic cement;
    an epoxy resin;
    a hardening agent for said epoxy resin; and
    sufficient water to form a pumpable slurry.
    [13" id="US-20010009133-A1-CLM-00013] 13. The composition of
    claim 12 wherein said hydraulic cement is a Portland cement or the equivalent thereof.
    [14" id="US-20010009133-A1-CLM-00014] 14. The composition of
    claim 12 wherein said epoxy resin is selected from the group of a condensation reaction product of epichlorohydrin and bisphenol A and an epoxidized bisphenol A novolac resin and is present in an amount in the range of from about 8% to about 10% by weight of hydraulic cement therein.
    [15" id="US-20010009133-A1-CLM-00015] 15. The composition of
    claim 12 wherein said hardening agent is at least one member selected from the group of aliphatic amines, aromatic amines and carboxylic acid anhydrides and is present in an amount in the range of from about 0.01% to about 0.02% by weight of hydraulic cement therein.
    [16" id="US-20010009133-A1-CLM-00016] 16. The composition of
    claim 12 which further comprises a set retarding agent.
    [17" id="US-20010009133-A1-CLM-00017] 17. The composition of
    claim 16 wherein said set retarding agent is comprised of an alkali metal or alkaline earth metal lignosulfonate modified by reaction with formaldehyde and sodium bisulfite and is present in an amount in the range of from about 0.1% to about 3% by weight of hydraulic cement therein.
    [18" id="US-20010009133-A1-CLM-00018] 18. The composition of
    claim 12 which further comprises amorphous silica powder present in an amount in the range of from about 10% to about 20% by weight of hydraulic cement therein.
    [19" id="US-20010009133-A1-CLM-00019] 19. The composition of
    claim 12 which further comprises a dispersing agent.
    [20" id="US-20010009133-A1-CLM-00020] 20. The composition of
    claim 19 wherein said dispersing agent is the condensation reaction product of formaldehyde, acetone and sodium bisulfite and is present in an amount in the range of from about 0.05% to about 1% by weight of hydraulic cement in said composition.
    [21" id="US-20010009133-A1-CLM-00021] 21. The composition of
    claim 12 which further comprises a gas, a foaming agent and a foam stabilizer.
    [22" id="US-20010009133-A1-CLM-00022] 22. The composition of
    claim 21 wherein said gas is selected from the group of air and nitrogen and is present in said composition in an amount sufficient to produce a composition density in the range of from about 10 to about 16 pounds per gallon.
    [23" id="US-20010009133-A1-CLM-00023] 23. The composition of
    claim 21 wherein said foaming agent is selected from the group of foaming agents comprised of the sodium salts of alpha-olefinic sulfonic acids and mixtures thereof and is present in an amount in the range of from about 3% to about 5% by weight of water in said composition.
    [24" id="US-20010009133-A1-CLM-00024] 24. The composition of
    claim 21 wherein said foam stabilizer is selected from the group of foam stabilizers having the formula R—CONHCH2CH2CH2N+(CH3)2CH2CO2 wherein R is a C10-C18 saturated aliphatic group, an oleyl group or a linoleyl group and is present in an amount in the range of from about 1.5% to about 2.5% by weight of water in said composition.
    类似技术:
    公开号 | 公开日 | 专利标题
    US6350309B2|2002-02-26|Methods and compositions for cementing pipe strings in well bores
    US6593402B2|2003-07-15|Resilient well cement compositions and methods
    US6899177B2|2005-05-31|Methods of cementing subterranean zones with cement compositions having enhanced compressive strengths
    US7441600B2|2008-10-28|Cement compositions with improved mechanical properties and methods of cementing in subterranean formations
    US5875844A|1999-03-02|Methods of sealing pipe strings in well bores
    US5688844A|1997-11-18|Resilient well cement compositions and methods
    US5795924A|1998-08-18|Resilient well cement compositions and methods
    US6210476B1|2001-04-03|Foamed cement compositions and methods
    US6069117A|2000-05-30|Foamed resin compositions for sealing subterranean zones
    US5696059A|1997-12-09|Methods of preventing well cement stress failure
    US6367549B1|2002-04-09|Methods and ultra-low density sealing compositions for sealing pipe in well bores
    US7351279B2|2008-04-01|Cement compositions with improved mechanical properties and methods of cementing in subterranean formations
    US20200071596A1|2020-03-05|Cement compositions including epoxy resin systems for preventing fluid migration
    EP0816300B1|2002-03-27|Well cement compositions
    EP0899415A1|1999-03-03|Method of sealing pipe string in well bores
    US20200317983A1|2020-10-08|Compositions for sealingan annulus of a wellbore
    同族专利:
    公开号 | 公开日
    US6244344B1|2001-06-12|
    EP1028096A2|2000-08-16|
    CA2298138A1|2000-08-09|
    NO20000630D0|2000-02-08|
    US6350309B2|2002-02-26|
    DE60012594D1|2004-09-09|
    NO20000630L|2000-08-10|
    DE60012594T2|2004-12-16|
    EP1028096A3|2000-10-25|
    EP1028096B1|2004-08-04|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US7910223B2|2003-07-17|2011-03-22|Honeywell International Inc.|Planarization films for advanced microelectronic applications and devices and methods of production thereof|
    WO2015126408A1|2014-02-21|2015-08-27|Halliburton Energy Services Inc.|Cementing compositions and methods|
    WO2016024990A1|2014-08-15|2016-02-18|Halliburton Energy Services, Inc.|Napthol-based epoxy resin additives for use in well cementing|
    WO2016043712A1|2014-09-15|2016-03-24|Halliburton Energy Services, Inc.|Cement compositions having an environmentally-friendly resin|
    WO2016048303A1|2014-09-24|2016-03-31|Halliburton Energy Services, Inc.|Compatibilized resin-cement composite compositions|
    WO2016093827A1|2014-12-10|2016-06-16|Halliburton Energy Services, Inc.|Method for using managed pressure drilling with epoxy resin|
    WO2016111674A1|2015-01-05|2016-07-14|Halliburton Energy Services, Inc.|Additive for improving homogeneity of epoxy resin and cement composites|US2815079A|1954-06-29|1957-12-03|Gulf Oil Corp|Method of and composition for recovering circulation of drilling fluids in wells|
    US3082823A|1960-03-31|1963-03-26|Halliburton Co|Composition and method for sealing porous formations|
    FR1315462A|1962-02-19|1963-01-18|Shell Int Research|Method of consolidating an unconsolidated or substantially unconsolidated mass|
    US3208525A|1962-06-25|1965-09-28|Exxon Production Research Co|Recompletion of wells|
    US3310511A|1962-12-31|1967-03-21|Electric Storage Battery Co|Hydraulic cement-epoxy resin compositions|
    US3308884A|1963-12-13|1967-03-14|Shell Oil Co|Plugging underground formations|
    US3310111A|1964-02-17|1967-03-21|Dow Chemical Co|Method of controlling solids in fluids from wells|
    GB1019122A|1964-03-26|1966-02-02|Shell Int Research|Method for treating a permeable mass|
    US3416604A|1967-03-20|1968-12-17|Hailiburton Company|Epoxy resin grouting fluid and method for stabilizing earth formations|
    US3467208A|1968-03-29|1969-09-16|Mobil Oil Corp|Lost circulation control|
    GB1286897A|1969-12-23|1972-08-23|Sir Soc Italiana Resine Spa|Process for the manufacture of light building elements|
    US3612181A|1970-02-16|1971-10-12|Exxon Production Research Co|Method for consolidating incompetent formations|
    US3763070A|1970-06-03|1973-10-02|Ici Ltd|Hydraulic cement with polyisocyanate and aliphatic polyepoxide|
    US3769250A|1970-09-10|1973-10-30|Resyn Corp|Epoxy hydraulic cement composition|
    US3750768A|1972-01-27|1973-08-07|Shell Oil Co|Oil base drilling fluid filtrate-effected sand consolidation|
    US3782466A|1972-07-19|1974-01-01|Shell Oil Co|Bonding casing with syntactic epoxy resin|
    US3976135A|1972-10-02|1976-08-24|Halliburton Company|Method of forming a highly permeable solid mass in a subterranean formation|
    US4042032A|1973-06-07|1977-08-16|Halliburton Company|Methods of consolidating incompetent subterranean formations using aqueous treating solutions|
    US3960801A|1973-06-18|1976-06-01|Halliburton Company|Pumpable epoxy resin composition|
    US4072194A|1973-06-18|1978-02-07|Halliburton Company|Pumpable epoxy resin composition|
    US3894977A|1973-08-27|1975-07-15|Southern Line Cleaning Inc|Sealant composition|
    US3933204A|1974-10-15|1976-01-20|Shell Oil Company|Plugging subterranean regions with acrylic-epoxy resin-forming emulsions|
    SU565987A1|1975-03-10|1977-07-25|Всесоюзный Научно-Исследовательский Институт По Креплению Скважин И Буровым Растворам |Cement-polymer plugging up material|
    US4042031A|1975-11-13|1977-08-16|Shell Oil Company|Plugging subterranean earth formations with aqueous epoxy emulsions containing fine solid particles|
    US4107112A|1975-07-28|1978-08-15|Latta Jr Laurence|Epoxy resin soil stabilizing compositions|
    US4074760A|1976-11-01|1978-02-21|The Dow Chemical Company|Method for forming a consolidated gravel pack|
    GB1550713A|1977-05-30|1979-08-15|Shell Int Research|Method of treating an underground formation around a borehole|
    US4127173A|1977-07-28|1978-11-28|Exxon Production Research Company|Method of gravel packing a well|
    US4199484A|1977-10-06|1980-04-22|Halliburton Company|Gelled water epoxy sand consolidation system|
    US4368136A|1977-10-06|1983-01-11|Halliburton Services|Aqueous gel composition for temporary stabilization of subterranean well formation|
    US4216829A|1977-10-06|1980-08-12|Halliburton Company|Gelled water epoxy sand consolidation system|
    US4220566A|1978-03-21|1980-09-02|The Dow Chemical Company|Aqueous based slurry containing enediol breaker and method for forming a consolidated gravel pack|
    US4272384A|1978-07-07|1981-06-09|The Dow Chemical Company|Composition for preventing a resin system from setting up in a well bore|
    US4189002A|1978-07-07|1980-02-19|The Dow Chemical Company|Method for rigless zone abandonment using internally catalyzed resin system|
    DE2840874C3|1978-09-20|1981-12-10|Rütgerswerke AG, 6000 Frankfurt|Use of a binder mixture for the renovation of reinforced concrete parts|
    US4532052A|1978-09-28|1985-07-30|Halliburton Company|Polymeric well treating method|
    US4215001A|1978-10-20|1980-07-29|Halliburton Company|Methods of treating subterranean well formations|
    SU966227A1|1979-03-11|1982-10-15|Всесоюзный научно-исследовательский институт по креплению скважин и буровым растворам|Plugging solution|
    US4367300A|1979-12-14|1983-01-04|Kowa Chemical Industries Co., Ltd.|Synthetic resin compositions to be added to cement, an aqueous paint composition containing said compositions and a method for coating said paint composition|
    US5232741A|1980-08-27|1993-08-03|Phillips Petroleum Company|Composition and method for corrosion inhibition utilizing an epoxy resin, an amine curing agent, an alcohol and optionally a hydrocarbon diluent|
    US4339000A|1980-08-28|1982-07-13|Cronmiller Clifford P|Method and apparatus for a bridge plug anchor assembly for a subsurface well|
    US4336842A|1981-01-05|1982-06-29|Graham John W|Method of treating wells using resin-coated particles|
    US4483888A|1981-09-01|1984-11-20|Phillips Petroleum Company|Carbon dioxide treatment of epoxy resin compositions|
    NO162810C|1982-04-06|1992-08-13|Schlumberger Cie Dowell|CEMENT SUSPENSION AND PROCEDURE FOR CEMENTATION OF OIL BROWNS AND GEOTHERMIC BURNS.|
    DE3361485D1|1982-08-26|1986-01-23|Ruetgerswerke Ag|Epoxy resin system emulsifiable with water and aqueous emulsion produced thereof, as well as process for its manufacture, and use|
    JPS59176347A|1983-03-25|1984-10-05|Toray Silicone Co Ltd|Organopolysiloxane composition|
    JPS6011255A|1983-06-24|1985-01-21|Idemitsu Petrochemical Co|Cement additive|
    US4489785A|1983-07-19|1984-12-25|Halliburton Company|Method of completing a well bore penetrating a subterranean formation|
    US4620993A|1984-03-30|1986-11-04|Ppg Industries, Inc.|Color plus clear coating system utilizing organo-modified clay in combination with organic polymer microparticles|
    US4558075A|1984-03-30|1985-12-10|Ppg Industries, Inc.|High-solids coating composition for improved rheology control containing organo-modified clay|
    DE3414229A1|1984-04-14|1985-10-24|Adlatus Glas- und Gebäudereinigungs GmbH, 6000 Frankfurt|Use of an aqueous epoxy resin emulsion for producing foamed concrete|
    FR2576591B1|1985-01-29|1992-04-17|Schlumberger Cie Dowell|CEMENT COMPOSITIONS FOR WELL CEMENTING FOR FIGHTING AGAINST PRESSURE GAS PATHWAY IN THE CEMENT-BASED DIRECTORY BY "RIGHT-ANGLE" TAP|
    CA1249777A|1985-02-11|1989-02-07|Herman G. Van Laar|Process for passing carbon dioxide through a cased,cemented and perforated well|
    US4665988A|1986-04-04|1987-05-19|Halliburton Company|Method of preparation of variable permeability fill material for use in subterranean formations|
    US4785884A|1986-05-23|1988-11-22|Acme Resin Corporation|Consolidation of partially cured resin coated particulate material|
    US4741401A|1987-01-16|1988-05-03|The Dow Chemical Company|Method for treating subterranean formations|
    US4773482A|1987-06-01|1988-09-27|Conoco Inc.|Reducing permeability of highly permeable zones in oil and gas formations|
    US4829100A|1987-10-23|1989-05-09|Halliburton Company|Continuously forming and transporting consolidatable resin coated particulate materials in aqueous gels|
    DE3805116A1|1988-02-18|1989-08-31|Hilterhaus Karl Heinz|METHOD FOR PRODUCING ORGANOMINERAL PRODUCTS|
    US4921047A|1989-08-10|1990-05-01|Conoco Inc.|Composition and method for sealing permeable subterranean formations|
    NO171308C|1989-08-21|1993-02-24|Borregaard Ind|APPLICATION OF COPOLYMERS AS ADDITIVE FOR CEMENT MORTAL MIXTURES, CEMENT MORTAL MIXTURES, AND COPOLYMER DISPERSION|
    US4972906A|1989-09-07|1990-11-27|Conoco Inc.|Method for selective plugging of a zone in a well|
    US5162060A|1989-12-14|1992-11-10|Rohm And Haas Company|Polymer-modified cements with improved chemical resistance|
    US5090478A|1990-11-30|1992-02-25|Conoco Inc.|Method for reducing water production from a gravel packed well|
    US5133409A|1990-12-12|1992-07-28|Halliburton Company|Foamed well cementing compositions and methods|
    US5095987A|1991-01-31|1992-03-17|Halliburton Company|Method of forming and using high density particulate slurries for well completion|
    US5159980A|1991-06-27|1992-11-03|Halliburton Company|Well completion and remedial methods utilizing rubber latex compositions|
    FR2678761B1|1991-07-03|1994-07-01|Commissariat Energie Atomique|BLOCK CONTAINING CONTAMINATED ION EXCHANGE RESINS AND PROCESS FOR PREPARING THE SAME.|
    JPH0532444A|1991-07-31|1993-02-09|Sumitomo Metal Ind Ltd|Water-permeable block for pavement|
    US5168928A|1991-08-15|1992-12-08|Halliburton Company|Preparation and use of gelable silicate solutions in oil field applications|
    US5232961A|1991-08-19|1993-08-03|Murphey Joseph R|Hardenable resin compositions and methods|
    US5211234A|1992-01-30|1993-05-18|Halliburton Company|Horizontal well completion methods|
    US5213161A|1992-02-19|1993-05-25|Halliburton Company|Well cementing method using acid removable low density well cement compositions|
    US5258072A|1992-06-01|1993-11-02|Basf Corporation|Additive composition for oil well cementing formulations|
    US5428178A|1992-10-13|1995-06-27|Shell Oil Company|Polyethercyclipolyols from epihalohydrins, polyhydric alcohols, and metal hydroxides or epoxy alcohols and optionally polyhydric alcohols with thermal condensation|
    NO176878C|1992-11-20|1995-06-14|Sinvent As|Cementing material with regulated curing time, for use in deep, hot oil wells|
    US5377757A|1992-12-22|1995-01-03|Mobil Oil Corporation|Low temperature epoxy system for through tubing squeeze in profile modification, remedial cementing, and casing repair|
    US5314023A|1993-01-19|1994-05-24|Dartez Terry R|Method for selectively treating wells with a low viscosity epoxy resin-forming composition|
    US5361842A|1993-05-27|1994-11-08|Shell Oil Company|Drilling and cementing with blast furnace slag/silicate fluid|
    US5361841A|1993-05-27|1994-11-08|Shell Oil Company|Drilling and cementing with blast furnace slag/polyalcohol fluid|
    US5358044A|1993-05-27|1994-10-25|Shell Oil Company|Drilling and cementing with blast furnace slag/soluble/insoluble alcohol|
    US5337824A|1993-06-28|1994-08-16|Shell Oil Company|Coal slag universal fluid|
    US5373901A|1993-07-27|1994-12-20|Halliburton Company|Encapsulated breakers and method for use in treating subterranean formations|
    US5363918A|1993-08-04|1994-11-15|Shell Oil Company|Wellbore sealing with unsaturated monomer system|
    US5368102A|1993-09-09|1994-11-29|Halliburton Company|Consolidatable particulate material and well treatment method|
    US5388648A|1993-10-08|1995-02-14|Baker Hughes Incorporated|Method and apparatus for sealing the juncture between a vertical well and one or more horizontal wells using deformable sealing means|
    US5358051A|1993-10-22|1994-10-25|Halliburton Company|Method of water control with hydroxy unsaturated carbonyls|
    US5335726A|1993-10-22|1994-08-09|Halliburton Company|Water control|
    US5559086A|1993-12-13|1996-09-24|Halliburton Company|Epoxy resin composition and well treatment method|
    JPH07257952A|1994-03-17|1995-10-09|Tadao Sakurai|Production of hydraulic composition for high strength polymer concrete and molded body of high strength polymer concrete|
    US5547027A|1994-07-14|1996-08-20|Dowell, A Division Of Schlumberger Technology Corporation|Low temperature, low rheology synthetic cement|
    US5458195A|1994-09-28|1995-10-17|Halliburton Company|Cementitious compositions and methods|
    JPH08198654A|1995-01-19|1996-08-06|Asahi Denka Kogyo Kk|Quick-hardening cement-epoxy composition|
    US5588488A|1995-08-22|1996-12-31|Halliburton Company|Cementing multi-lateral wells|
    US5692566A|1996-01-22|1997-12-02|Texaco Inc.|Formation treating method|
    DE19701916C2|1996-01-27|2000-07-20|Colfirmit Rajasil Gmbh|Process for the preparation of a polymer-modified cement mortar dry mix, polymer modified cement mortar dry mix and their use|
    US5711383A|1996-04-19|1998-01-27|Halliburton Company|Cementitious well drilling fluids and methods|
    US5688844A|1996-07-01|1997-11-18|Halliburton Company|Resilient well cement compositions and methods|
    US5795924A|1996-07-01|1998-08-18|Halliburton Company|Resilient well cement compositions and methods|
    US5712314A|1996-08-09|1998-01-27|Texaco Inc.|Formulation for creating a pliable resin plug|
    US5738463A|1996-08-15|1998-04-14|Halliburton Company|Elastomeric grouting of subsurface conduits|
    JP3192986B2|1997-02-17|2001-07-30|ニッコー株式会社|High-strength hardened cement with excellent water resistance and method for producing the same|
    US5913364A|1997-03-14|1999-06-22|Halliburton Energy Services, Inc.|Methods of sealing subterranean zones|
    US6006836A|1997-08-18|1999-12-28|Halliburton Energy Services, Inc.|Methods of sealing plugs in well bores|
    US5873413A|1997-08-18|1999-02-23|Halliburton Energy Services, Inc.|Methods of modifying subterranean strata properties|
    US6124246A|1997-11-17|2000-09-26|Halliburton Energy Services, Inc.|High temperature epoxy resin compositions, additives and methods|
    US6006835A|1998-02-17|1999-12-28|Halliburton Energy Services, Inc.|Methods for sealing subterranean zones using foamed resin|
    JPH11246783A|1998-02-26|1999-09-14|Toagosei Co Ltd|Degradable molded part|
    US6068055A|1998-06-30|2000-05-30|Halliburton Energy Services, Inc.|Well sealing compositions and methods|
    US6059035A|1998-07-20|2000-05-09|Halliburton Energy Services, Inc.|Subterranean zone sealing methods and compositions|
    US6098711A|1998-08-18|2000-08-08|Halliburton Energy Services, Inc.|Compositions and methods for sealing pipe in well bores|
    US6244344B1|1999-02-09|2001-06-12|Halliburton Energy Services, Inc.|Methods and compositions for cementing pipe strings in well bores|
    US6234251B1|1999-02-22|2001-05-22|Halliburton Energy Services, Inc.|Resilient well cement compositions and methods|US6271181B1|1999-02-04|2001-08-07|Halliburton Energy Services, Inc.|Sealing subterranean zones|
    US6328106B1|1999-02-04|2001-12-11|Halliburton Energy Services, Inc.|Sealing subterranean zones|
    US6244344B1|1999-02-09|2001-06-12|Halliburton Energy Services, Inc.|Methods and compositions for cementing pipe strings in well bores|
    US6234251B1|1999-02-22|2001-05-22|Halliburton Energy Services, Inc.|Resilient well cement compositions and methods|
    US6454006B1|2000-03-28|2002-09-24|Halliburton Energy Services, Inc.|Methods and associated apparatus for drilling and completing a wellbore junction|
    US6321841B1|2001-02-21|2001-11-27|Halliburton Energy Services, Inc.|Methods of sealing pipe strings in disposal wells|
    US6767867B2|2001-04-16|2004-07-27|Halliburton Energy Services, Inc.|Methods of treating subterranean zones penetrated by well bores|
    US6367549B1|2001-09-21|2002-04-09|Halliburton Energy Services, Inc.|Methods and ultra-low density sealing compositions for sealing pipe in well bores|
    US7066284B2|2001-11-14|2006-06-27|Halliburton Energy Services, Inc.|Method and apparatus for a monodiameter wellbore, monodiameter casing, monobore, and/or monowell|
    US7267171B2|2002-01-08|2007-09-11|Halliburton Energy Services, Inc.|Methods and compositions for stabilizing the surface of a subterranean formation|
    US7216711B2|2002-01-08|2007-05-15|Halliburton Eenrgy Services, Inc.|Methods of coating resin and blending resin-coated proppant|
    US7343973B2|2002-01-08|2008-03-18|Halliburton Energy Services, Inc.|Methods of stabilizing surfaces of subterranean formations|
    US6713535B2|2002-02-28|2004-03-30|Turbine Controls, Inc.|Low-friction chromate-free coating of epoxy resins and sulfonyldianiline|
    US6691780B2|2002-04-18|2004-02-17|Halliburton Energy Services, Inc.|Tracking of particulate flowback in subterranean wells|
    US6705400B1|2002-08-28|2004-03-16|Halliburton Energy Services, Inc.|Methods and compositions for forming subterranean fractures containing resilient proppant packs|
    GB2398582A|2003-02-20|2004-08-25|Schlumberger Holdings|System and method for maintaining zonal isolation in a wellbore|
    US20040211561A1|2003-03-06|2004-10-28|Nguyen Philip D.|Methods and compositions for consolidating proppant in fractures|
    US7114570B2|2003-04-07|2006-10-03|Halliburton Energy Services, Inc.|Methods and compositions for stabilizing unconsolidated subterranean formations|
    US6978836B2|2003-05-23|2005-12-27|Halliburton Energy Services, Inc.|Methods for controlling water and particulate production|
    US7114560B2|2003-06-23|2006-10-03|Halliburton Energy Services, Inc.|Methods for enhancing treatment fluid placement in a subterranean formation|
    US7413010B2|2003-06-23|2008-08-19|Halliburton Energy Services, Inc.|Remediation of subterranean formations using vibrational waves and consolidating agents|
    US7021379B2|2003-07-07|2006-04-04|Halliburton Energy Services, Inc.|Methods and compositions for enhancing consolidation strength of proppant in subterranean fractures|
    US7066258B2|2003-07-08|2006-06-27|Halliburton Energy Services, Inc.|Reduced-density proppants and methods of using reduced-density proppants to enhance their transport in well bores and fractures|
    US7104325B2|2003-07-09|2006-09-12|Halliburton Energy Services, Inc.|Methods of consolidating subterranean zones and compositions therefor|
    US7017665B2|2003-08-26|2006-03-28|Halliburton Energy Services, Inc.|Strengthening near well bore subterranean formations|
    US7156194B2|2003-08-26|2007-01-02|Halliburton Energy Services, Inc.|Methods of drilling and consolidating subterranean formation particulate|
    US7237609B2|2003-08-26|2007-07-03|Halliburton Energy Services, Inc.|Methods for producing fluids from acidized and consolidated portions of subterranean formations|
    US7059406B2|2003-08-26|2006-06-13|Halliburton Energy Services, Inc.|Production-enhancing completion methods|
    US7345011B2|2003-10-14|2008-03-18|Halliburton Energy Services, Inc.|Methods for mitigating the production of water from subterranean formations|
    US7063150B2|2003-11-25|2006-06-20|Halliburton Energy Services, Inc.|Methods for preparing slurries of coated particulates|
    US20050145385A1|2004-01-05|2005-07-07|Nguyen Philip D.|Methods of well stimulation and completion|
    US7131493B2|2004-01-16|2006-11-07|Halliburton Energy Services, Inc.|Methods of using sealants in multilateral junctions|
    US7143828B2|2004-01-29|2006-12-05|Halliburton Energy Services, Inc.|Emulsion admixtures for improving cement elasticity|
    US20050173116A1|2004-02-10|2005-08-11|Nguyen Philip D.|Resin compositions and methods of using resin compositions to control proppant flow-back|
    US7156172B2|2004-03-02|2007-01-02|Halliburton Energy Services, Inc.|Method for accelerating oil well construction and production processes and heating device therefor|
    US7211547B2|2004-03-03|2007-05-01|Halliburton Energy Services, Inc.|Resin compositions and methods of using such resin compositions in subterranean applications|
    US7063151B2|2004-03-05|2006-06-20|Halliburton Energy Services, Inc.|Methods of preparing and using coated particulates|
    US20050194142A1|2004-03-05|2005-09-08|Nguyen Philip D.|Compositions and methods for controlling unconsolidated particulates|
    US20050263283A1|2004-05-25|2005-12-01|Nguyen Philip D|Methods for stabilizing and stimulating wells in unconsolidated subterranean formations|
    US7541318B2|2004-05-26|2009-06-02|Halliburton Energy Services, Inc.|On-the-fly preparation of proppant and its use in subterranean operations|
    US7299875B2|2004-06-08|2007-11-27|Halliburton Energy Services, Inc.|Methods for controlling particulate migration|
    US7281580B2|2004-09-09|2007-10-16|Halliburton Energy Services, Inc.|High porosity fractures and methods of creating high porosity fractures|
    US7757768B2|2004-10-08|2010-07-20|Halliburton Energy Services, Inc.|Method and composition for enhancing coverage and displacement of treatment fluids into subterranean formations|
    US7281581B2|2004-12-01|2007-10-16|Halliburton Energy Services, Inc.|Methods of hydraulic fracturing and of propping fractures in subterranean formations|
    US7273099B2|2004-12-03|2007-09-25|Halliburton Energy Services, Inc.|Methods of stimulating a subterranean formation comprising multiple production intervals|
    US7398825B2|2004-12-03|2008-07-15|Halliburton Energy Services, Inc.|Methods of controlling sand and water production in subterranean zones|
    US7883740B2|2004-12-12|2011-02-08|Halliburton Energy Services, Inc.|Low-quality particulates and methods of making and using improved low-quality particulates|
    US7334635B2|2005-01-14|2008-02-26|Halliburton Energy Services, Inc.|Methods for fracturing subterranean wells|
    US7334636B2|2005-02-08|2008-02-26|Halliburton Energy Services, Inc.|Methods of creating high-porosity propped fractures using reticulated foam|
    US7318473B2|2005-03-07|2008-01-15|Halliburton Energy Services, Inc.|Methods relating to maintaining the structural integrity of deviated well bores|
    US7673686B2|2005-03-29|2010-03-09|Halliburton Energy Services, Inc.|Method of stabilizing unconsolidated formation for sand control|
    US7318474B2|2005-07-11|2008-01-15|Halliburton Energy Services, Inc.|Methods and compositions for controlling formation fines and reducing proppant flow-back|
    US7650940B2|2005-12-29|2010-01-26|Halliburton Energy Services Inc.|Cement compositions comprising particulate carboxylated elastomers and associated methods|
    US7645817B2|2005-12-29|2010-01-12|Halliburton Energy Services, Inc.|Cement compositions comprising particulate carboxylated elastomers and associated methods|
    US8132623B2|2006-01-23|2012-03-13|Halliburton Energy Services Inc.|Methods of using lost circulation compositions|
    US7776797B2|2006-01-23|2010-08-17|Halliburton Energy Services, Inc.|Lost circulation compositions|
    US7926591B2|2006-02-10|2011-04-19|Halliburton Energy Services, Inc.|Aqueous-based emulsified consolidating agents suitable for use in drill-in applications|
    US8613320B2|2006-02-10|2013-12-24|Halliburton Energy Services, Inc.|Compositions and applications of resins in treating subterranean formations|
    US7819192B2|2006-02-10|2010-10-26|Halliburton Energy Services, Inc.|Consolidating agent emulsions and associated methods|
    US7665517B2|2006-02-15|2010-02-23|Halliburton Energy Services, Inc.|Methods of cleaning sand control screens and gravel packs|
    US7407010B2|2006-03-16|2008-08-05|Halliburton Energy Services, Inc.|Methods of coating particulates|
    US20080060811A1|2006-09-13|2008-03-13|Halliburton Energy Services, Inc.|Method to control the physical interface between two or more fluids|
    US7934557B2|2007-02-15|2011-05-03|Halliburton Energy Services, Inc.|Methods of completing wells for controlling water and particulate production|
    US20090038801A1|2007-08-08|2009-02-12|Ravi Krishna M|Sealant Compositions and Methods of Use|
    US8276666B2|2007-08-08|2012-10-02|Halliburton Energy Services Inc.|Sealant compositions and methods of use|
    US7530396B1|2008-01-24|2009-05-12|Halliburton Energy Services, Inc.|Self repairing cement compositions and methods of using same|
    US7762329B1|2009-01-27|2010-07-27|Halliburton Energy Services, Inc.|Methods for servicing well bores with hardenable resin compositions|
    US8689873B2|2011-10-27|2014-04-08|Schlumberger Technology Corporation|Compositions and methods for improving the toughness of set cements|
    US10093770B2|2012-09-21|2018-10-09|Schlumberger Technology Corporation|Supramolecular initiator for latent cationic epoxy polymerization|
    US9896269B2|2015-05-01|2018-02-20|Halliburton Energy Services, Inc.|Method of forming a subterranean gas storage vessel|
    US10428261B2|2017-06-08|2019-10-01|Csi Technologies Llc|Resin composite with overloaded solids for well sealing applications|
    US10378299B2|2017-06-08|2019-08-13|Csi Technologies Llc|Method of producing resin composite with required thermal and mechanical properties to form a durable well seal in applications|
    JP2020536985A|2017-10-10|2020-12-17|サウジ アラビアン オイル カンパニーＳａｕｄｉ Ａｒａｂｉａｎ Ｏｉｌ Ｃｏｍｐａｎｙ|Thixotropic cement slurry and placement method to repair lost circulation|
    WO2020050857A1|2018-09-07|2020-03-12|Halliburton Energy Services, Inc.|Accelerating agents for resin cement composite systems for oil well cementing|
    CN109504356A|2018-11-21|2019-03-22|西南石油大学|A kind of high strength, low elasticity water-soluble resin mortar architecture and its application|
    法律状态:
    2002-02-12| STCF| Information on status: patent grant|Free format text: PATENTED CASE |
    2005-07-28| FPAY| Fee payment|Year of fee payment: 4 |
    2009-06-22| FPAY| Fee payment|Year of fee payment: 8 |
    2013-03-18| FPAY| Fee payment|Year of fee payment: 12 |
    优先权:
    申请号 | 申请日 | 专利标题
    US09/247,813|US6244344B1|1999-02-09|1999-02-09|Methods and compositions for cementing pipe strings in well bores|
    US09/784,290|US6350309B2|1999-02-09|2001-02-13|Methods and compositions for cementing pipe strings in well bores|US09/784,290| US6350309B2|1999-02-09|2001-02-13|Methods and compositions for cementing pipe strings in well bores|
    [返回顶部]