    • 专利摘要:
    A method and structure for forming magnetic alloy nanoparticles includes forming a metal salt solution with a reducing agent and stabilizing ligands, introducing an organometallic compound into the metal salt solution to form a mixture, heating the mixture to a temperature between 260° and 300° C., and adding a flocculent to cause the magnetic alloy nanoparticles to precipitate out of the mixture without permanent agglomeration. The deposition of the alkane dispersion of FePt alloy particles, followed by the annealing results in the formation of a shiny FePt nanocrystalline thin film with coercivity ranging from 500 Oe to 6500 Oe.
    公开号:US20010009119A1
    申请号:US09/797,605
    申请日:2001-03-05
    公开日:2001-07-26
    发明作者:Christopher Murray；Shouheng Sun；Dieter Weller
    申请人:International Business Machines Corp；
    IPC主号:B82Y25-00
    专利说明:
    [0001] 1. Field of the Invention [0001]
    [0002] The present invention generally relates to convenient chemical syntheses of stable, nearly monodisperse alloy magnetic nanoparticles and an economic chemical approach to magnetic alloy nanocrystalline thin film production on a solid surface. The coercivity of the thin film can be controlled in the range between 500 Oe and 6500 Oe. This synthesis route offers a viable approach to the production of ultra-high density recording media. [0002]
    [0003] 2. Description of the Related Art [0003]
    [0004] The storage density of commercial magnetic recording media is increasing at a compound rate of 60% per annum. As the storage density increases the individual storage bit size decreases proportionally. To control signal to noise ratios and other recording parameters, it is advantageous to maintain a large number of ferromagnetic grains per bit. Thus, the development of new magnetic media with smaller grains, high coercivity and high magnetization is required. Furthermore, to maximize the signal to noise ratio, the grains should be well isolated from each other to prevent exchange coupling between the grains, and possess a narrow size distribution. However, this scaling approach is limited by the onset of superparamagnetic behavior when the grain size falls below some material-dependent characteristic dimension. [0004]
    [0005] One approach to reduce particle dimensions but still maintain sufficiently high coercivity is to take advantage of the high magnetocrystalline anisotropy found in some metal alloy systems. It is known that an assembly of very small non-interacting magnetic particles with high anisotropy possesses high coercivity. The coercivity arises because the small particles can support only a single domain state and irreversible magnetization rotation is the only possible mechanism of flux reversal. [0005]
    [0006] The CoPt or FePt binary alloys are excellent candidates for this approach because of their chemical stability, and high magnetocrystalline anisotropy (thus high coercivity) arising from the existence of ordered intermetallic phases. For these alloys, magnetocrystalline anisotropies of around 7×10e7 erg/cm[0006] 3 have been obtained, compared to 5×10e 6 erg/cm3 for hcp cobalt-based recording media. Typical Co based recording media today have anisotropies of order 1-2×10e6 erg/cm3. Since the stored magnetic energy scales with the anisotropy constant and the particle volume, KV, smaller particles of high K materials like FePt and CoPt can potentially be used in future media applications. The advantage is narrower transitions and reduced read back noise. Hcp cobalt based granular thin films doped with Pt are being used today in ultra-high density recording applications, a typical composition being CoP10Cr22B6. Accordingly, tremendous research efforts have been focused on synthesis and characterization of near equiatomic CoPt and FePt alloys. These alloys may also have great potential for use as magnetic bias films of magneto-resistive elements, and magnetic tips for magnetic force microscopy.
    [0007] A common procedure leading to CoPt or FePt alloy materials is cosputtering of Co (or Fe) and Pt. This procedure allows little control over particle size or size distribution. The following description discloses that stable, monodisperse magnetic alloy nanoparticles and related nanocrystalline thin film can be easily synthesized by convenient chemical procedures. [0007]
    [0008] The invention includes a convenient chemical way to prepare stable monodisperse Fe/Pt alloy magnetic nanoscale materials, an approach to form smooth nanocrystalline films on a variety of substrates, and exploring the possibility of using the developed materials as ultra-high density recording media. [0008] SUMMARY OF THE INVENTION
    [0009] The principal object of synthesizing magnetic Fe/Pt alloy nanoparticles and nanocrystalline thin films has been achieved in this invention. A combination of reduction of metal salt and decomposition of neutral organometallic precursor has been developed for the formation of the magnetic alloy nanoparticles. For example, in situ reduction of Pt(acac)[0009] 2(acac=acetylactonate, CH3COCHCOCH3 anion) by long chain diol and decomposition of Fe(CO)5 at a high temperature (260° C.-300° C.) solution phase yields high quality nanoparticles.
    [0010] The particles are protected from agglomeration by a combination of long chain carboxylic acid, such as oleic acid, and long chain primary amine, such as oleyl amine. This stabilization is so effective that the particles can be handled easily either in solution phase or as solid form under air. [0010]
    [0011] The particles are easily dispersed in alkane and chlorinated solvent and purified by precipitation through the addition of alcohol. Deposition of the alkane solution of the alloy particles on SiO[0011] 2, Si, Si3N4, or glass leads to the formation of a smooth particulate thin film, offering an economic route for the production of thin film media. The as-synthesized magnetic alloy shows a single-phase FCC and is magnetically soft. Under thermal conditions in the range of 500° C. to 650° C., the precipitated particles undergo long-range ordering to a structure of the CuAu-I type. This structure is tetragonal with the (002) planes, normal to the c axis, occupied alternately by Fe and Pt atoms, giving high magnetocrystalline anisotropy at room temperature. Coercivities between 500 Oe to 6500 Oe have been achieved at room temperature.
    [0012] It is, therefore, an object of the present invention to provide a structure and method forming magnetic alloy nanoparticles, which includes forming a metal salt solution with a reducing agent and stabilizing ligands, introducing an organometallic compound into the metal salt solution to form a mixture, heating the mixture to a temperature between 260° and 300° C., and adding a flocculent to cause the magnetic alloy nanoparticles to precipitate out of the mixture without permanent agglomeration. The organometallic compound includes a solvent including one of phenyl ether and dioctyl ether. The reducing agent includes a long chain diol, which includes one of 1,2-hexadecanediol, 1,2-dodecanediol and 1,2-octanediol. The stabilizing ligands include RCOOH and RNH[0012] 2, where R includes an alkyl, alkenyl hydrocarbon chain (C6 or longer). The flocculent includes an alcohol including one of methanol, ethanol, propanol and butanol. The metal salt includes one of Pt salt, Pt(CH3COCHCOCH3)2, Pt(CF3COCHCOCF3)2, Tetrakis (triphenylphosphine) Platinum(O), or Pt(O) (triphenylphosphine)4-x(CO)x where x is at least 1 and no greater than 3. The organometallic compound includes one of Fe(CO)5, Co2(CO)8, Co4(CO)12, Fe2(CO)9, Fe3(CO)12, Fe(CNR)5, and (Diene) Fe(CO)5 (e.g., Cyclopentadiene, Cyclooctadiene, etc.).
    [0013] Another embodiment of the invention is a method of forming a magnetic alloy nanoparticle film, which includes forming a metal salt solution with a reducing agent and stabilizing ligands, introducing an organometallic compound into the metal salt solution to form a mixture, heating the mixture to a temperature between 260° and 300° C., adding a flocculent to cause the magnetic alloy nanoparticles to produce a precipitate out of the mixture without permanent agglomeration, forming a dispersion with the precipitate, depositing the dispersion on a solid surface, annealing the dispersion in an inert atmosphere at temperature up to 650° C., and cooling the dispersion under an inert atmosphere. The dispersion includes either an alkane dispersion, including pentane, hexane, heptane, octane and dodecane, a chlorinated solvent dispersion, including dichloromethane and chloroform, or an aromatic solvent dispersion, including benzene, toluene and xylene. The dispersion includes an alkane RNH[0013] 2 (where R includes an alkyl or alkenyl chain of C12 or longer) formed by the addition of alcohol. The inert atmosphere includes one of N2 or Ar. The annealing temperature is between 400° C. and 650° C. The annealing forms a layer of amorphous carbon around particles in the precipitate. The organometallic compound includes a solvent including one of phenyl ether and dioctyl ether. The reducing agent includes a long chain diol, which includes one of 1,2-hexadecanediol, 1,2-dodecanediol and 1,2-octanediol. The stabilizing ligands include RCOOH and RNH2, where R includes an alkyl, alkenyl hydrocarbon chain (C6 or longer). The flocculent includes an alcohol including one of methanol, ethanol, propanol and butanol. The metal salt includes one of Pt salt, Pt(CH3COCHCOCH3)2, Pt(CF3COCHCOCF3)2, Tetrakis (triphenylphosphine), Platinum(O), or Pt(O) (triphenylphosphine)4-x(CO)x. The organometallic compound includes one of Fe(CO)5, Co2(CO)8, Co4(CO)12, Fe2(CO)9, Fe3(CO)12, Fe(CNR)5, and (Diene) Fe(CO)5 (e.g., Cyclopentadiene, Cyclooctadiene, etc.).
    [0014] Yet another embodiment is a method of forming a magnetic storage device having magnetic alloy nanoparticles, which includes forming a metal salt solution with a reducing agent and stabilizing ligands, introducing an organometallic compound into the metal salt solution to form a mixture, heating the mixture to a temperature between 260° and 300° C., and adding a flocculent to cause the magnetic alloy nanoparticles to precipitate out of the mixture without permanent agglomeration. The organometallic compound includes a solvent including one of phenyl ether and dioctyl ether. The reducing agent includes a long chain diol, which includes one of 1,2-hexadecanediol, 1,2-dodecanediol and 1,2-octanediol. The stabilizing ligands include RCOOH and RNH[0014] 2, where R includes an alkyl, alkenyl hydrocarbon chain (C6 or longer). The flocculent includes an alcohol including one of methanol, ethanol, propanol and butanol. The metal salt includes one of Pt salt, Pt(CH3COCHCOCH3)2, Pt(CF3COCHCOCF3)2, Tetrakis (triphenylphosphine), Platinum(O), or Pt(O) (triphenylphosphine)4-x(CO)x. The organometallic compound includes one of Fe(CO)5, Co2(CO)8, Co4(CO)12, Fe2(CO)9, Fe3(CO)12, Fe(CNR)5, and (Diene) Fe(CO)5 (e.g., Cyclopentadiene, Cyclooctadiene, etc.).
    [0015] The invention's synthetic method leads to nearly monodisperse particle thin films with controllable coercivity, providing a viable approach to such ultrahigh density recording media. [0015] BRIEF DESCRIPTION OF THE DRAWINGS
    [0016] The foregoing and other objects, aspects and advantages will be better understood from the following detailed description of a preferred embodiment of the invention with reference to the drawings, in which: [0016]
    [0017] FIG. 1 shows a TEM image of as-synthesized FePt alloy particles where the sample was deposited on SiO-coated copper grid from its hexane dispersion and the particles are nearly monodisperse; [0017]
    [0018] FIG. 2 shows the coercivity change of one set of samples (48% at. Pt) as a function of annealing temperature after annealing for 30 min. where coercivity data were collected on 9500 Vibrating Sample Magnetometer at room temperature with thin film paralleling to magnetic field; [0018]
    [0019] FIG. 3 shows the X-ray diffraction patterns of (a) as-synthesized FePt particles, (b)-(e) the thin film formed after annealing for 30 minutes under N[0019] 2 and (f) 45 nm amorphous carbon thin film where the samples were deposited on glass substrate and the diffraction pattern was collected on a Siemens D-S00 diffractometer with Cu K(alpha) radiation (lamda=1.54056 Å);
    [0020] FIG. 4 shows the coercivity change of thin film with various Pt concentration where the film was annealed at 600° C. under N[0020] 2 for 30 minutes;
    [0021] FIG. 5 shows (a) an atomic force microscopy image of the topography of a FePt sample annealed to 600° C., and (b) a magnetic force microscopy image of the same area of the sample in which the as-deposited magnetic domain structure is evident where the topography of the sample has a z-range of 9.3 nm over this 3 μm region, and RMS roughness of 0.999 nm and the magnetic structure shows a fairly broad length scale distribution, as taken from a 2D power spectral density calculation, which peaks at 188 nm; [0021]
    [0022] FIGS. 6[0022] a and 6 b show in plane and out of plane coercivities of 3 FePt nanoparticle samples measured with a Kerr magnetometer where coercivities of 1800 Oe, 2000 Oe and 5000 Oe for the three different annealing conditions indicated at the top of the figure are found and there is little difference between in-plane and out-of-plane coercivities, indicating 3D-random orientation of the magnetic axes;
    [0023] FIG. 7 shows magneto-optical Kerr spectra taken in the energy range 0.8-5.3 eV where characteristic shifts in peak positions and changes in the Kerr angle are observed, consistent with the higher ordering for the higher coercivity sample; [0023]
    [0024] FIG. 8 shows an actual write/read experiment on the 1800 Oe (30 min 600° C.) sample using a static write/read test apparatus; [0024]
    [0025] FIG. 9 shows a so called dynamic coercivity measurement, from which a thermal stability ratio of C[0025] −1≅EB/kBT≅48 has been extracted; and
    [0026] FIG. 10 is a flow diagram showing the process of forming the magnetic alloy nanoparticle film. [0026] DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION
    [0027] Long chain diols such as 1,2-octanediol, 1,2-dodecanediol and 1,2-hexadecanediol, etc. have been used previously to reduce metal salts (such as Pt salt, Fe(OCOCH[0027] 3)2, Fe(CH3COCHCOCH3)2, Co(OCOCH3)2, Co(CH3COCHCOCH3)2, etc. ) to metal nanoparticles, (e.g., see Murray et al., copending U.S. patent application Ser. No. 09/127,005, which is fully incorporated herein by reference). Thermal decomposition of an organometallic compound (such as Fe(CO)5, Co2(CO)8, Fe2(CO)8, [C5H5Fe(CO)2]2, and (C5H5)2Fe) is a known procedure to separate the Fe and its oxide particles (e.g., M. O. Bentzon, et al., Phil. Mag. B., 1989, V. 60(2), 169, fully incorporated herein by reference). The invention combines these two chemical reactions (e.g., the reduction of the metal salt and the decomposition of the organometallic compound) in situ to form magnetic alloy particles that have a very controlled grain size and are nearly monodisperse.
    [0028] In our synthetic conditions, the reduction of the metal salt (e.g., Pt(acac)[0028] 2) by diol and the decomposition of the organometallic compound (e.g., Fe(CO)5) do not occur until the temperature is greater than 180° C. These slow reduction and decomposition processes are useful in forming the high quality magnetic alloy particles.
    [0029] More specifically, the invention forms such high quality magnetic alloy particles by mixing metal salt, diol, stabilizing ligands, organometallic compound and solvent under an inert atmosphere. The mixture is then heated to reflux. The reduction of the metal salt and the decomposition of the organometallic compound lead to homogeneous nucleation for the formation of the magnetic alloy particles. The growth of the magnetic alloy particles is completed in about 30 minutes. The hot black product dispersion is cooled to room temperature. A flocculent (e.g.,alcohol, methanol, ethanol, propanol, ethylene, glycol, etc.) is added to precipitate the product. Indeed, the magnetic alloy particles precipitated out are nearly monodisperse. [0029]
    [0030] The supernatant is discarded and the precipitated magnetic alloy particles are dispersed, in alkane solvent in the presence of oleic acid and amine. The dispersion can include an alkane dispersion, such as pentane, hexane, heptane, octane or dodecane; a chlorinated solvent dispersion, such as dichloromethane or chloroform; or an aromatic solvent dispersion, including benzene, toluene or xylene. Any unsolved impurity can be removed by centrifugation of the hexane dispersion. Purification of the crude product is performed by adding ethanol to the hexane dispersion of the particles, providing nearly monodisperse magnetic alloy nanoparticles which can be easily redispersed in an alkane solvent. [0030]
    [0031] Oleic acid is preferred as a stabilizing ligand in the above process because it is known to stabilize cobalt and iron nanoparticles. Long aliphatic chains of oleic acid present a significant steric barrier for strong interactions between the particles, and magnetic exchange coupling between the particles is eliminated completely by the physical separation induced. Similar long chain carboxylic acids such as erucic acid and linoleic acid can also be used instead of oleic acid. Oleic acid is preferred because it is readily available. [0031]
    [0032] Further, amine-based or other similar ligands, such as RNH[0032] 2 (R>C12H25) R2NH when R═C1 to C22, are included in a preferred embodiment to protect platinum particles. In the invention, long chain primary amine, such as oleyl amine, or alkyl amine RNH2 with R>C12H25, etc., is used to protect the surface Pt component of the magnetic alloy particles. The combination of acid/amine provides good control over the magnetic alloy particles' growth and stabilization.
    [0033] Phenylether or n-dioctylether is preferably used as the solvent. However, as would be known by one ordinarily skilled in the art given this disclosure, any suitable solvent with high boiling point and good solubility of Fe and Pt compounds could be used. Other solvents include mineral oil, paraffin wax and polyethylene glycol. The reaction can be carried out at temperatures ranging from 260° C. to 300° C., depending on the solvent used. [0033]
    [0034] Referring now to the drawings, one example of the invention which forms FePt nanoparticles using the above process is illustrated. More specifically, in this example, Pt salt, diol, stabilizing ligands, Fe(CO)[0034] 5 and solvent are combined under an inert atmosphere. The mixture is then heated to between 260° C. and 300° C. for 30 minutes and allowed to cool to room temperature. Alcohol is added to precipitate the FePt nanoparticles.
    [0035] In FIG. 1, the particle size and distribution are determined by TEM image analysis. To produce the image shown in FIG. 1, carbon- or SiO-coated copper grids were dipped into the hexane solution of the FePt nanoparticles and dried at room temperature. The TEM image (from Philips EM 420, 120 KV) in FIG. 1 shows that the FePt nanoparticles have an average diameter of 4 nm. The FePt nanoparticles are uniformly dispersed in the film and have a narrow size distribution. [0035]
    [0036] The magnetic alloy particles can be processed into well formed particle thin films. As mentioned above, the magnetic alloy particles are well isolated from each other by the protecting ligands. Oleic acid and oleylamine ligands around the particles can be replaced by other aliphatic acids and primary amines. Thus, purification by adding ethanol to hexane dispersion in the presence of 1 octadecylamine, leads to octadecylamine and oleic acid protected magnetic alloy particles. [0036]
    [0037] Depositing the hexane dispersion of magnetic alloy particles on a flat substrate, such as SiO[0037] 2, Si, glass, or carbon and drying the same at room temperature leads to well formed particle thin films. Magnetic measurements of FePt films shows that the magnetic alloy films are magnetically soft with no coercivity at room temperature. Annealing the magnetic alloy films at temperatures between 500° C. and 650° C. produces mirror-like thin films with controlled coercivities between 500 Oe and 6500 Oe.
    [0038] Using the same FePt example as discussed above with respect to FIG. 1, a typical annealing temperature dependent Hc is shown in FIG. 2. The hard magnetic behavior of a FePt alloy is related to the crystalline phase transition. The inventive magnetic alloy usually has a disordered fcc structure which transforms into an ordered fct structure with c/a=0.98 after annealing. This crystalline phase change in the film can be easily detected by X-ray diffraction. [0038]
    [0039] The predominant features in the XRD pattern of the exemplary FePt particle thin film are characteristic of a disordered fcc structure, as shown in FIG. 3([0039] a). Annealing to higher temperatures leads to pronounced structure changes. FIG. 3(b)-(e) show a series of diffraction patterns at different annealing temperatures. These demonstrates that, with respect to the FePt example being discussed, the crystal phase change for FePt (at 48% Pt) particles occurs at about 450° C. and is complete at around 580° C.
    [0040] During the alloying phase change, in the FePt example being discussed, the particle diameter remained about constant at approximately 4 nm, as confirmed by both TEM and high resolution SEM analyses. The strong peaks that appear at 2 φ[0040] 0=24, 33, 41, 47, and 70 correspond to reported (JCODS) tetragonal FePt crystal phase with a=3.8525 angstrom and c=3.7133 angstrom.
    [0041] Further, annealing at high temperatures (greater than 500° C.) under N[0041] 2 did not result in the loss of the stabilizing ligand. Rather, the stabilizing ligand decomposed to give amorphous carbon that covered around the particles. The bumps in FIG. 3(b)-(e) are due to the existence of such amorphous carbon. This can be easily verified by comparing Figures (b)-(e) with the X-ray diffraction pattern of 45 nm amorphous carbon film on a glass substrate shown in FIG. 3(f).
    [0042] This carbon coated FePt nanocrystalline thin film is very stable towards oxidation. Experimentally exposing the annealed FePt samples to the ambient environment did not result in the formation of layers of oxides, as confirmed by X-ray analysis. However, it should be mentioned that N[0042] 2 purity is important for successful alloy phase change during the annealing. The above annealing experiment was performed in a N2 Box with O2 content lower than 10 ppm. Otherwise, oxides formation was observed.
    [0043] The component of FePt particle materials has been studied either by ICPAtomic Emission Spectrometer for as-synthesized particles or by Rutherford Backscattering for the thin film. The FePt ratio can be readily controlled by changing the ratio of starting molecules of Fe(CO)[0043] 5 and Pt(acac)2 from 40% at. Pt to about 20% at. Pt. However, magnetic measurements show that the film containing a little Fe rich component gives high coercivity, as shown in FIG. 4.
    [0044] The roughness of the deposited films in this example has been investigated by atomic force microscopy (AFM), as shown in FIG. 5([0044] a), and RMS roughness values of approximately 1 nm have been achieved over areas of 3×3 μm. The magnetic domain structures which evolve in the as-deposited films have been investigated by magnetic force microscopy (MFM) and it has been found that there is a stable magnetic domain structure with length scales on the order of hundreds of nanometers, as shown in FIG. 5(b). This long range ordering is attributed to the dipolar coupling between the particles.
    [0045] FIG. 6 shows in plane and out of plane coercivities of 3 FePt nanoparticle samples that were measured with a Kerr magnetometer. Coercivities of 1800 Oe, 2000 Oe and 5000 Oe for the three different annealing conditions were found as indicated at the top of FIG. 6. There is little difference between the in-plane and the out-of-plane coercivities, indicating that a 3D-random orientation of the magnetic axes exists. [0045]
    [0046] Further evidence for the presence of chemical ordering and the formation of the high anisotropy FePt L1[0046] 0 phase is gained from magneto-optical Kerr spectroscopy measurements, shown in FIG. 7. Magneto-optical Kerr spectroscopy measurements have been intensively used in the past to establish magneto-structural correlations. The observed shift in the Kerr peak to higher energies upon further annealing is consistent with earlier work on thin FePt films [D. Weller, Spin Orbit Influenced Spectroscopies, 1995].
    [0047] FIG. 8 shows an actual write/read experiment on the 1800 Oe (30 min 600° C.) FePt sample using a static write/read test apparatus. More specifically, FIG. 8 shows a two-dimensional stray field image taken with the MR element of a standard record head. Twenty parallel 100 μm long tracks of written bit transitions varying in linear density from 500 to 5000 flux changes per mm were written and imaged with the record head in physical contact with the sample, indicating the abrasion resistance of these nanoparticle films. The same apparatus has been used to assess the thermal stability of the sample, which is characterized by the ratio of reversal barrier height and thermal energy E[0047] B/kBT.
    [0048] FIG. 9 shows a so called dynamic coercivity measurement, from which this number can be extracted as a slope parameter [0048]
    [0049] H[0049] 0 is an intrinsic switching field reached at short write field pulses tp≅1 ns and C−1≅EB/kBT. We find C−1=48, which indicates sufficient thermal stability for this FePt sample. Improved stability occurs in the higher coercivity samples. This is just a demonstration that these kinds of measurements can be carried out on the present FePt nanoparticle samples.
    [0050] The process of forming the magnetic alloy nanoparticle film includes forming a metal salt solution with a reducing agent and stabilizing ligands [0050] 100, introducing an organometallic compound 101, heating the mixture 102, adding a flocculent to produce a precipitate 103, forming a dispersion 104, depositing the dispersion on a solid surface 105, and annealing the dispersion 106, as shown in FIG. 10.
    [0051] Thus, the deposition of the alkane dispersion of FePt alloy particles, followed by the annealing results in the formation of a shiny FePt nanocrystalline thin film with coercivity ranging from 500 Oe to 6500 Oe. [0051]
    [0052] The following examples demonstrate some of the specific uses of the invention. The first example is for the synthesis of FePt particles. Platinum acetylacetonate/1,2-hexadecanediol/dioctylether in the ratio of 1.0 mmol:1.5 mmol/40 mL were mixed in a glass vessel under nitrogen and heated to 100° C. to give a yellow solution. Oleic acid (1 mmol) and oleylamine (1 mmol) were added and the mixing process was continued with N[0052] 2 flushing for 20 minutes. The N2 flushing was stopped and the N2 was adjusted to by-pass the reaction mixture slowly to insure full protection of the reaction product from oxidation. Fe(CO)5 (2 mmol) was added and the mixture was heated to reflux (293° C.) in a period of about 14 minutes. The refluxing was continued for 30 minutes. The heat source was removed and the black reaction mixture was cooled to room temperature.
    [0053] Ethanol was then added. The black product was precipitated and separated by centrifugation. Yellow-brown supernatant was discarded and the black product was dispersed in hexane in the presence of oleic acid and 1-octadecylamine. The product was precipitated out by adding ethanol and centrifugation. The precipitate was once again dispersed in hexane in the presence of only 1-octadecylamine. Any unsolved precipitation was removed by centrifugation. The particle materials were precipitated out by adding ethanol and centrifugation, re-dispersed in hexane, and stored under N[0053] 2. Although the product can be easily handled without any inert gas protection, it is preferable to store the hexane dispersion under N2 for long term protection.
    [0054] A second example involved the synthesis of nanocrystalline thin films. Hexane dispersion of FePt nanoparticles (0.5 mg/mL) was deposited on a SiO[0054] 2/Si substrate. The solvent hexane evaporated at room temperature. The thickness of particle thin film can be easily controlled by controlling the volume of hexane dispersion deposited on the solid surface. The as-deposited thin film was transferred to a N2 glove box with 02 content lower than 10 ppm and annealed in a oven. The temperature was raised to a desired level (e.g., 550° C.) from room temperature in a course of around 13 minutes and kept at that temperature level. After a certain time (e.g., 30 minutes), the thin film sample was taken out of the oven and cooled down to room temperature. The film produced was stable towards oxidation and could be used for further measurement. The roughness of the deposited films has been investigated by atomic force microscopy (AFM), as shown in FIG. 4, and RMS roughness values of approximately 1 nm have been achieved over areas of 3×3 μm.
    [0055] Another example involves the magnetic domain structure of the nanocrystalline thin films. The magnetic domain structures which evolve in the as deposited films have been investigated by magnetic force microscopy (MFM) and it has been found that there is a stable magnetic domain structure with length scales of order of hundreds of nanometers, as shown in Figure. [0055] 4(b). This long range ordering is attributed to the dipolar coupling between the particles.
    [0056] High density recording media uniform particles with an average diameter of 8-10 nm or less and a high Hc of 2500 Oe will soon be required. The invention's synthetic method leads to nearly monodisperse particle thin films with controllable coercivity, providing a viable approach to such ultra-high density recording media. [0056]
    [0057] This alloy may also have great potential for use as magnetic bias films of magneto-resistive elements and magnetic tips for magnetic force microscopy. Specifically, nonvolatile magnetic memory devices and magneto-resistive sensory for magnetic recording systems “Read Head”. [0057]
    [0058] While the invention has been described in terms of preferred embodiments, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims. [0058]
    权利要求:
    Claims (29)
    [1" id="US-20010009119-A1-CLM-00001] 1. A method of forming magnetic alloy nanoparticles, comprising:
    forming a metal salt solution with a reducing agent and stabilizing ligands;
    introducing an organometallic compound into said metal salt solution to form a mixture;
    heating said mixture to a temperature between 260° and 300° C.; and
    adding a flocculent to cause said magnetic alloy nanoparticles to precipitate out of said mixture without permanent agglomeration.
    [2" id="US-20010009119-A1-CLM-00002] 2. The method in
    claim 1 , wherein said organometallic compound includes a solvent comprising one of phenyl ether, dioctyl ether, polyphenyl ether, and polyethylene glycol.
    [3" id="US-20010009119-A1-CLM-00003] 3. The method in
    claim 1 , wherein the reducing agent comprises a long chain diol.
    [4" id="US-20010009119-A1-CLM-00004] 4. The method in
    claim 3 , wherein said long chain diol comprises one of 1,2-hexadecanediol, 1,2-dodecanediol and 1,2-octanediol.
    [5" id="US-20010009119-A1-CLM-00005] 5. The method in
    claim 1 , wherein said stabilizing ligands include RCOOH and RNH2, where R comprises an alkyl, alkenyl hydrocarbon chain (C6 or longer).
    [6" id="US-20010009119-A1-CLM-00006] 6. The method in
    claim 1 , wherein said flocculent comprises an alcohol including one of methanol, ethanol, propanol and butanol.
    [7" id="US-20010009119-A1-CLM-00007] 7. The method in
    claim 1 , wherein said metal salt comprises one of Pt salt, Pt(CH3COCHCOCH3)2, Pt(CF3COCHCOCF3)2, Tetrakis (triphenylphosphine) Platinum(O), or Pt (triphenylphosphine)4-x(CO)x where x is at least 1 and no greater than 3.
    [8" id="US-20010009119-A1-CLM-00008] 8. The method in
    claim 1 , wherein said organometallic compound comprises one of Fe(CO)5, Co2(CO)8, Co4(CO)12, Fe2(CO)9, Fe3(CO)12, Fe(CNR)5, and (Diene) Fe(CO)5 (e.g., Cyclopentadiene, Cyclooctadiene).
    [9" id="US-20010009119-A1-CLM-00009] 9. A method of forming a magnetic alloy nanoparticle film, comprising:
    forming a metal salt solution with a reducing agent and stabilizing ligands;
    introducing an organometallic compound into said metal salt solution to form a mixture;
    heating said mixture to a temperature between 260° and 300° C.;
    adding a flocculent to cause said magnetic alloy nanoparticles to produce a precipitate out of said mixture without permanent agglomeration;
    forming a dispersion with said precipitate;
    depositing said dispersion on a solid surface;
    annealing said dispersion in an inert atmosphere at temperature up to 650° C.; and
    cooling said dispersion under an inert atmosphere.
    [10" id="US-20010009119-A1-CLM-00010] 10. The method in
    claim 9 , wherein said dispersion comprises one of:
    an alkane dispersion, including pentane, hexane, heptane, octane and dodecane;
    a chlorinated solvent dispersion, including dichloromethane and chloroform; and
    an aromatic solvent dispersion, including benzene, toluene and xylene.
    [11" id="US-20010009119-A1-CLM-00011] 11. The method in
    claim 9 , wherein said dispersion comprises an RNH2 (where R comprises an alkyl or alkenyl chain of C12 or longer) formed by the addition of alcohol.
    [12" id="US-20010009119-A1-CLM-00012] 12. The method in
    claim 9 , wherein said inert atmosphere comprises one of N2 or Ar.
    [13" id="US-20010009119-A1-CLM-00013] 13. The method in
    claim 9 , wherein said annealing temperature is between 400° C. and 650° C.
    [14" id="US-20010009119-A1-CLM-00014] 14. The method in
    claim 9 , wherein said annealing forms a layer of amorphous carbon around particles in said precipitate.
    [15" id="US-20010009119-A1-CLM-00015] 15. The method in
    claim 9 , wherein said organometallic compound includes a solvent comprising one of phenyl ether and dioctyl ether.
    [16" id="US-20010009119-A1-CLM-00016] 16. The method in
    claim 9 , wherein the reducing agent comprises a long chain diol.
    [17" id="US-20010009119-A1-CLM-00017] 17. The method in
    claim 16 , wherein said long chain diol comprises one of 1,2-hexadecanediol, 1,2-dodecanediol and 1,2-octanediol.
    [18" id="US-20010009119-A1-CLM-00018] 18. The method in
    claim 9 , wherein said stabilizing ligands include RCOOH and RNH2, where R comprises an alkyl, alkenyl hydrocarbon chain (C6 or longer).
    [19" id="US-20010009119-A1-CLM-00019] 19. The method in
    claim 9 , wherein said flocculent comprises an alcohol including one of methanol, ethanol, propanol and butanol.
    [20" id="US-20010009119-A1-CLM-00020] 20. The method in
    claim 9 , wherein said metal salt comprises one of Pt salt, Pt(CH3COCHCOCH3)2, Pt(CF3COCHCOCF3)2, Tetrakis (triphenylphosphine) Platinum(O), or Pt (triphenylphosphine)4-x(CO)x where x is at least 1 and no greater than 3.
    [21" id="US-20010009119-A1-CLM-00021] 21. The method in
    claim 9 , wherein said organometallic compound comprises one of Fe(CO)5, Co2(CO)8, Co4(CO)12, Fe2(CO)9, Fe3(CO)12, Fe(CNR)5, and (Diene) Fe(CO)5 (e.g., Cyclopentadiene, Cyclooctadiene).
    [22" id="US-20010009119-A1-CLM-00022] 22. A method of forming a magnetic storage device having magnetic alloy nanoparticles, comprising:
    forming a metal salt solution with a reducing agent and stabilizing ligands;
    introducing an organometallic compound into said metal salt solution to form a mixture;
    heating said mixture to a temperature between 260° and 300° C.; and
    adding a flocculent to cause said magnetic alloy nanoparticles to precipitate out of said mixture without permanent agglomeration.
    [23" id="US-20010009119-A1-CLM-00023] 23. The method in
    claim 22 , wherein said organometallic compound includes a solvent comprising one of phenyl ether and dioctyl ether.
    [24" id="US-20010009119-A1-CLM-00024] 24. The method in
    claim 22 , wherein the reducing agent comprises a long chain diol.
    [25" id="US-20010009119-A1-CLM-00025] 25. The method in
    claim 24 , wherein said long chain diol comprises one of 1,2-hexadecanediol, 1,2-dodecanediol and 1,2-octanediol.
    [26" id="US-20010009119-A1-CLM-00026] 26. The method in
    claim 22 , wherein said stabilizing ligands include RCOOH and RNH2, where R comprises an alkyl, alkenyl hydrocarbon chain (C6 or longer).
    [27" id="US-20010009119-A1-CLM-00027] 27. The method in
    claim 22 , wherein said flocculent comprises an alcohol including one of methanol, ethanol, propanol and butanol.
    [28" id="US-20010009119-A1-CLM-00028] 28. The method in
    claim 22 , wherein said metal salt comprises one of Pt salt, Pt(CH3COCHCOCH3)2, Pt(CF3COCHCOCF3)2, Tetrakis (triphenylphosphine) Platinum(O), or Pt (triphenylphosphine)4-x(CO)x where x is at least 1 and no greater than 3.
    [29" id="US-20010009119-A1-CLM-00029] 29. The method in
    claim 22 , wherein said organometallic compound comprises one of Fe(CO)5, Co2(CO)8, Co4(CO)12, Fe2(CO)9, Fe3(CO)12, Fe(CNR)5, and (Diene) Fe(CO)5 (e.g., Cyclopentadiene, Cyclooctadiene).
    类似技术:
    公开号 | 公开日 | 专利标题
    US6302940B2|2001-10-16|Chemical synthesis of monodisperse and magnetic alloy nanocrystal containing thin films
    EP1627699B1|2008-01-09|Face-centered cubic structure alloy particles and method of manufacturing
    Sun et al.2001|Compositionally controlled FePt nanoparticle materials
    US6676729B2|2004-01-13|Metal salt reduction to form alloy nanoparticles
    Sun et al.2000|Monodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattices
    Murray et al.2001|Monodisperse 3d transition-metal | nanoparticles and their assembly intonanoparticle superlattices
    Jeyadevan et al.2003|Towards direct synthesis of fct-FePt nanoparticles by chemical route
    JP3258295B2|2002-02-18|Method for producing transition metal nanoparticles
    US7569115B2|2009-08-04|Assemblages of magnetic alloy nanoparticles
    Kang et al.2003|Synthesis, self-assembly, and magnetic properties of [FEPT]/sub 1-x/au/sub x/nanoparticles
    US8157889B2|2012-04-17|Magnetic metal powder and method of producing the powder
    Petit et al.2004|Magnetic properties of cobalt and cobalt–platinum nanocrystals investigated by magneto-optical Kerr effect
    Nguyen et al.2005|Synthesis of monodispersed fcc and fct FePt/FePd nanoparticles by microwave irradiation
    Sun et al.2004|FePt and CoPt magnetic nanoparticles film for future high density data storage media
    US7964013B2|2011-06-21|FeRh-FePt core shell nanostructure for ultra-high density storage media
    Weller et al.2001|MOKE spectra and ultrahigh density data storage perspective of FePt nanomagnet arrays
    JP4729682B2|2011-07-20|Manufacturing method of metal magnetic powder
    Jia et al.2005|Synthesis of FePtAu nanoparticles in high-boiling-point solvents
    Ram et al.2001|Granular GMR sensors of Co–Cu and Co–Ag nanoparticles synthesized through a chemical route using NaBH4
    Sudfeld et al.2002|Magnetic cobalt nanocrystals organized in patches and chains
    Kim et al.2006|Synthesis and characterization of crystalline FeCo nanoparticles
    JP2005089856A|2005-04-07|Magnetic powder and its manufacturing method
    Morales et al.1999|Origin of switching field distribution in MP pigments
    JP2006045617A|2006-02-16|Aggregate of magnetic alloy particles
    Hattori et al.2004|Synthesis of FePt and FePtCu Nanoparticles by a Reverse Micelle Method and Studies of Magnetic Recording Media Using Them
    同族专利:
    公开号 | 公开日
    US6302940B2|2001-10-16|
    US6254662B1|2001-07-03|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US20040033357A1|2002-05-31|2004-02-19|Fuji Photo Film Co., Ltd.|Magnetic particle, its production method, magnetic recording medium and its production method|
    US20040159821A1|1996-11-16|2004-08-19|Nanomagnetics Limited|Magnetizable device|
    GB2399541A|2003-03-18|2004-09-22|Nanomagnetics Ltd|Production of nanoparticulate thin films|
    US20040231462A1|2003-03-05|2004-11-25|Fuji Photo Film Co., Ltd.|Method of manufacturing magnetic particle, magnetic particle and magnetic recording medium|
    US20050042425A1|2002-04-04|2005-02-24|Fujitsu Limited|Polycrystalline structure of ordered alloy and method of making the same|
    US20050142352A1|2003-02-28|2005-06-30|Fuji Photo Film Co., Ltd.|Magnetic particle coated material containing magnetic particles having CuAu type or Cu3Au type ferromagnetic ordered alloy phase, and method for producing the same|
    US20050155214A1|2002-07-03|2005-07-21|Fuji Photo Film Co., Ltd.|Magnetic recording medium and method of producing the same|
    EP1561530A1|2002-11-15|2005-08-10|Fujitsu Limited|Alloy nano-particle and method for production thereof, and magnetic recording medium using alloy nano-particle|
    US20050235776A1|2004-04-22|2005-10-27|Ting He|Metal and alloy nanoparticles and synthesis methods thereof|
    US20060003163A1|1996-11-16|2006-01-05|Nanomagnetics Limited|Magnetic fluid|
    US6986942B1|1996-11-16|2006-01-17|Nanomagnetics Limited|Microwave absorbing structure|
    US20070289409A1|2004-08-03|2007-12-20|Younan Xia|Synthesis of platinum nanostructures|
    US20080003130A1|2006-02-01|2008-01-03|University Of Washington|Methods for production of silver nanostructures|
    CN100421787C|2007-03-23|2008-10-01|厦门大学|Platinum icosahedron nano crystal catalyst, its preparing method and use|
    US7544230B2|2003-03-05|2009-06-09|Fujifilm Corporation|Method of manufacturing magnetic particle, magnetic particle and magnetic recording medium|
    US20090282948A1|2002-12-09|2009-11-19|The University Of Washington|Methods of nanostructure formation and shape selection|
    CN101787522A|2010-04-02|2010-07-28|南京大学|Method for preparing ordered magnetic nanoparticle composite film with super-high density|
    WO2013103762A1|2012-01-04|2013-07-11|Virginia Commonwealth University|Non-rare earth magnetic nanoparticles|
    US8679444B2|2009-04-17|2014-03-25|Seerstone Llc|Method for producing solid carbon by reducing carbon oxides|
    US9090472B2|2012-04-16|2015-07-28|Seerstone Llc|Methods for producing solid carbon by reducing carbon dioxide|
    US9221685B2|2012-04-16|2015-12-29|Seerstone Llc|Methods of capturing and sequestering carbon|
    US9475699B2|2012-04-16|2016-10-25|Seerstone Llc.|Methods for treating an offgas containing carbon oxides|
    US9598286B2|2012-07-13|2017-03-21|Seerstone Llc|Methods and systems for forming ammonia and solid carbon products|
    US9604848B2|2012-07-12|2017-03-28|Seerstone Llc|Solid carbon products comprising carbon nanotubes and methods of forming same|
    CN106541147A|2016-11-15|2017-03-29|哈尔滨工业大学|A kind of method for preparing hard magnetic nanometer Fe-Pt particle as presoma with inorganic salts|
    US9650251B2|2012-11-29|2017-05-16|Seerstone Llc|Reactors and methods for producing solid carbon materials|
    US9731970B2|2012-04-16|2017-08-15|Seerstone Llc|Methods and systems for thermal energy recovery from production of solid carbon materials by reducing carbon oxides|
    US9779845B2|2012-07-18|2017-10-03|Seerstone Llc|Primary voltaic sources including nanofiber Schottky barrier arrays and methods of forming same|
    US9783421B2|2013-03-15|2017-10-10|Seerstone Llc|Carbon oxide reduction with intermetallic and carbide catalysts|
    US9796591B2|2012-04-16|2017-10-24|Seerstone Llc|Methods for reducing carbon oxides with non ferrous catalysts and forming solid carbon products|
    US9896341B2|2012-04-23|2018-02-20|Seerstone Llc|Methods of forming carbon nanotubes having a bimodal size distribution|
    US10322832B2|2013-03-15|2019-06-18|Seerstone, Llc|Systems for producing solid carbon by reducing carbon oxides|
    US10815124B2|2012-07-12|2020-10-27|Seerstone Llc|Solid carbon products comprising carbon nanotubes and methods of forming same|US3965046A|1974-09-26|1976-06-22|Graham Magnetics Incorporated|Process of making metal powders and products produced thereby|
    US4940596A|1987-06-12|1990-07-10|Minnesota Mining And Manufacturing Company|Process for metal fibers|
    US5240493A|1992-01-16|1993-08-31|Institute Of Gas Technology|Process for preparing submicron/nanosize ceramic powders from precursors incorporated within a polymeric foam|
    US5698483A|1995-03-17|1997-12-16|Institute Of Gas Technology|Process for preparing nanosized powder|
    US5824409A|1995-11-13|1998-10-20|Board Of Regents|High coercivity longitudinal recording media and method for its preparation|
    US5914361A|1996-08-26|1999-06-22|Sumitomo Chemical Company, Limited|Cyclic phosphonites and their use as stabilizers for organic materials|
    US6262129B1|1998-07-31|2001-07-17|International Business Machines Corporation|Method for producing nanoparticles of transition metals|US6815063B1|1996-11-16|2004-11-09|Nanomagnetics, Ltd.|Magnetic fluid|
    GB2319253A|1996-11-16|1998-05-20|Eric Leigh Mayes|Composition, for use in a device, comprising a magnetic layer of domain-separated magnetic particles|
    JP3205793B2|1996-12-19|2001-09-04|株式会社巴製作所|Ultrafine particles and method for producing the same|
    JP5008216B2|2000-10-13|2012-08-22|株式会社アルバック|Inkjet ink manufacturing method|
    US20040055419A1|2001-01-19|2004-03-25|Kurihara Lynn K.|Method for making metal coated powders|
    JP3693647B2|2001-02-08|2005-09-07|日立マクセル株式会社|Metal alloy fine particles and method for producing the same|
    US8618595B2|2001-07-02|2013-12-31|Merck Patent Gmbh|Applications of light-emitting nanoparticles|
    US6918946B2|2001-07-02|2005-07-19|Board Of Regents, The University Of Texas System|Applications of light-emitting nanoparticles|
    US6846565B2|2001-07-02|2005-01-25|Board Of Regents, The University Of Texas System|Light-emitting nanoparticles and method of making same|
    KR100438408B1|2001-08-16|2004-07-02|한국과학기술원|Method for Synthesis of Core-Shell type and Solid Solution type Metallic Alloy Nanoparticles via Transmetalation Reactions and Their Applications|
    US6566665B2|2001-08-17|2003-05-20|International Business Machines Corporation|Method and apparatus for linking and/or patterning self-assembled objects|
    US20030059604A1|2001-09-05|2003-03-27|Fuji Photo Film Co., Ltd.|Material coated with dispersion of ferromagnetic nanoparticles, and magnetic recording medium using the material|
    JP3728411B2|2001-09-18|2005-12-21|ソニー株式会社|Method for producing magnetic particle, magnetic particle and magnetic material|
    WO2003039791A1|2001-11-02|2003-05-15|The Trustees Of Princeton University|Methods for the preparation of metallic alloy nanoparticles and compositions thereof|
    US6846345B1|2001-12-10|2005-01-25|The United States Of America As Represented By The Secretary Of The Navy|Synthesis of metal nanoparticle compositions from metallic and ethynyl compounds|
    US6676729B2|2002-01-02|2004-01-13|International Business Machines Corporation|Metal salt reduction to form alloy nanoparticles|
    JP2003248916A|2002-02-20|2003-09-05|Fujitsu Ltd|Nanoparticles for magnetic recording medium, magnetic recording medium using them and its manufacturing method|
    US6805904B2|2002-02-20|2004-10-19|International Business Machines Corporation|Process of forming a multilayer nanoparticle-containing thin film self-assembly|
    US20030228488A1|2002-06-05|2003-12-11|Seagate Technology Llc|Magnetic read head using 100-xCux as a permanent magnet material|
    AU2003213086A1|2002-06-28|2004-01-19|Seagate Technology Llc|Increased packing density in self-organized magnetic array|
    US6878184B1|2002-08-09|2005-04-12|Kovio, Inc.|Nanoparticle synthesis and the formation of inks therefrom|
    KR100487905B1|2002-10-02|2005-05-06|한국과학기술연구원|Shape anisotropic iron oxide nano-particles and synthetic method thereof|
    US6737364B2|2002-10-07|2004-05-18|International Business Machines Corporation|Method for fabricating crystalline-dielectric thin films and devices formed using same|
    JP2004165630A|2002-10-21|2004-06-10|Fuji Photo Film Co Ltd|Magnetic particle coated object, manufacturing method therefor, magnetic recording medium, and electromagnetic shield material|
    JP2004152385A|2002-10-30|2004-05-27|Fuji Photo Film Co Ltd|Magnetic recording medium|
    US20040084298A1|2002-10-31|2004-05-06|Y.D. Yao|Fabrication of nanocomposite thin films for high density magnetic recording media|
    US7078276B1|2003-01-08|2006-07-18|Kovio, Inc.|Nanoparticles and method for making the same|
    US6972046B2|2003-01-13|2005-12-06|International Business Machines Corporation|Process of forming magnetic nanocomposites via nanoparticle self-assembly|
    JP2004220670A|2003-01-14|2004-08-05|Hitachi Ltd|Method for forming nanoparticle film aligned in axis of easy magnetization, magnetic recording medium using the same and manufacturing method and apparatus thereof|
    WO2004076056A2|2003-02-26|2004-09-10|Lake Shore Cryotronics Inc.|Microfluidic chemical reactor for the manufacture of chemically-produced nanoparticles|
    US7470308B2|2004-02-10|2008-12-30|Fujifilm Corporation|Method of producing magnetic particles and reaction method using microreactor and microreactor|
    US7029514B1|2003-03-17|2006-04-18|University Of Rochester|Core-shell magnetic nanoparticles and nanocomposite materials formed therefrom|
    JP4392186B2|2003-04-14|2009-12-24|大日本印刷株式会社|High-speed response liquid crystal device and driving method|
    AU2003902785A0|2003-06-04|2003-06-19|Microtechnology Centre Management Limited|Magnetic nanoparticles|
    AU2004244668B2|2003-06-04|2007-07-05|Mems-Id Pty Ltd|Magnetic nanoparticles|
    GB0313259D0|2003-06-09|2003-07-16|Consejo Superior Investigacion|Magnetic nanoparticles|
    JP2005048250A|2003-07-30|2005-02-24|Dowa Mining Co Ltd|Magnetic metal particle aggregate and method of producing the same|
    JP2005056489A|2003-08-04|2005-03-03|Fuji Photo Film Co Ltd|Magnetic recording medium|
    JP4221484B2|2003-09-09|2009-02-12|Ｄｏｗａエレクトロニクス株式会社|Metallic magnetic powder and method for producing the same|
    US20050089683A1|2003-09-12|2005-04-28|Fuji Photo Film Co., Ltd.|Magnetic particles and method of producing the same and magnetic recording medium|
    US7029773B2|2003-10-10|2006-04-18|Seagate Technology Llc|Method and system for magnetic recording using self-organized magnetic nanoparticles|
    DE60312872T2|2003-12-10|2007-07-12|Freescale Semiconductor, Inc., Austin|Method of making an element containing an electrical conductor surrounded by magnetic material|
    WO2005060610A2|2003-12-11|2005-07-07|The Trustees Of Columbia University In The City Ofnew York|Nano-sized particles, processes of making, compositions and uses thereof|
    US7053021B1|2004-04-22|2006-05-30|The Research Foundation Of The State University Of New York|Core-shell synthesis of carbon-supported alloy nanoparticle catalysts|
    US7754444B2|2004-06-24|2010-07-13|The Hong Kong University Of Science And Technology|Biofunctional magnetic nanoparticles for pathogen detection|
    JP4490201B2|2004-08-04|2010-06-23|Ｄｏｗａホールディングス株式会社|Fine alloy particle powder having irregular surface and method for producing the same|
    JP4390693B2|2004-12-17|2009-12-24|富士通株式会社|Method for producing fuel cell catalyst and method for producing fuel cell|
    US20070134902A1|2005-12-12|2007-06-14|The Curators Of The University Of Missouri|Patterning of Substrates with Metal-Containing Particles|
    US7829140B1|2006-03-29|2010-11-09|The Research Foundation Of The State University Of New York|Method of forming iron oxide core metal shell nanoparticles|
    US8167972B2|2006-06-30|2012-05-01|N.E. Chemcat Corporation|Process for producing metal nanoparticle and metal nanoparticle produced by the process|
    KR100830871B1|2006-10-11|2008-05-21|삼성전기주식회사|Method for surface modification of nondispersible metal nanoparticles and modified metal nanoparticles for inkjet by the same method|
    US20090297626A1|2006-11-03|2009-12-03|The Trustees Of Columbia University In The City Of New York|Methods for preparing metal oxides|
    US7632332B2|2006-12-12|2009-12-15|Honda Motor Co., Ltd.|Preparation of iron-titanium nanoparticles|
    US8343627B2|2007-02-20|2013-01-01|Research Foundation Of State University Of New York|Core-shell nanoparticles with multiple cores and a method for fabricating them|
    US8465855B2|2008-07-16|2013-06-18|International Business Machines Corporation|Protective coating of magnetic nanoparticles|
    WO2010071459A1|2008-12-19|2010-06-24|Victoria Link Limited|Magnetic nanoparticles|
    US7972410B1|2009-02-02|2011-07-05|Sandia Corporation|Magnetic agglomeration method for size control in the synthesis of magnetic nanoparticles|
    US7964013B2|2009-06-18|2011-06-21|University Of Louisiana At Lafayette|FeRh-FePt core shell nanostructure for ultra-high density storage media|
    US8591751B2|2011-09-30|2013-11-26|Headway Technologies, Inc.|Very thin high coercivity film and process for making it|
    WO2021123074A1|2019-12-18|2021-06-24|F. Hoffmann-La Roche Ag|Methods of sequencing by synthesis using a consecutive labeling scheme|
    法律状态:
    2003-01-08| AS| Assignment|Owner name: MARIANA HDD B.V., NETHERLANDS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:INTERNATIONAL BUSINESS MACHINES CORPORATION;REEL/FRAME:013663/0348 Effective date: 20021231 |
    2003-02-04| AS| Assignment|Owner name: HITACHI GLOBAL STORAGE TECHNOLOGIES NETHERLANDS B. Free format text: CHANGE OF NAME;ASSIGNOR:MARIANA HDD B.V.;REEL/FRAME:013746/0146 Effective date: 20021231 |
    2005-04-08| FPAY| Fee payment|Year of fee payment: 4 |
    2009-03-26| FPAY| Fee payment|Year of fee payment: 8 |
    2012-10-25| AS| Assignment|Owner name: HGST, NETHERLANDS B.V., NETHERLANDS Free format text: CHANGE OF NAME;ASSIGNOR:HGST, NETHERLANDS B.V.;REEL/FRAME:029341/0777 Effective date: 20120723 Owner name: HGST NETHERLANDS B.V., NETHERLANDS Free format text: CHANGE OF NAME;ASSIGNOR:HITACHI GLOBAL STORAGE TECHNOLOGIES NETHERLANDS B.V.;REEL/FRAME:029341/0777 Effective date: 20120723 |
    2013-05-24| REMI| Maintenance fee reminder mailed|
    2013-10-16| LAPS| Lapse for failure to pay maintenance fees|
    2013-11-11| STCH| Information on status: patent discontinuation|Free format text: PATENT EXPIRED DUE TO NONPAYMENT OF MAINTENANCE FEES UNDER 37 CFR 1.362 |
    2013-12-03| FP| Lapsed due to failure to pay maintenance fee|Effective date: 20131016 |
    优先权:
    申请号 | 申请日 | 专利标题
    US09/359,638|US6254662B1|1999-07-26|1999-07-26|Chemical synthesis of monodisperse and magnetic alloy nanocrystal containing thin films|
    US09/797,605|US6302940B2|1999-07-26|2001-03-05|Chemical synthesis of monodisperse and magnetic alloy nanocrystal containing thin films|US09/797,605| US6302940B2|1999-07-26|2001-03-05|Chemical synthesis of monodisperse and magnetic alloy nanocrystal containing thin films|
    [返回顶部]