    • 专利摘要:
    A composite sensor fibre comprising a filamentary core (12) and an outer layer (30) encapsulating an intermediate sensor layer (20) of a detectably thermoresponsive material. Also disclosed are a method of making composite sensor fibres, a dressing comprising a fabric having a matrix of the fibres, and a method of monitoring a wound that utilises the dressing.
    公开号:AU2012372758A1
    申请号:U2012372758
    申请日:2012-08-02
    公开日:2014-09-25
    发明作者:Robin William Cranston；Ilias Louis Kyratzis；Lance Victor Nichols；Michael Shane O'shea；Gary Peeters；Louise Catherine VAN DER WERFF
    申请人:Commonwealth Scientific and Industrial Research Organization CSIRO；
    IPC主号:G01K11-20
    专利说明:
    WO 2013/131120 PCT/AU2012/000916 1 Composite sensor fibres and applications therefor Field of the invention This invention relates generally to composite sensor fibres containing thermoresponsive 5 material, and to methods of making such fibres. In a particularly advantageous application, the invention relates to composite thermochromic fibres and to fabrics or non-wovens incorporating such fibres. In one aspect, the invention is concerned with a dressing or other garment that includes the thermochromic fabric and provides a method of monitoring a wound in which such a dressing is applied to the wound. The composite sensor fibres of the invention can also be used 10 for the monitoring of temperatures over engineering surfaces such as building elements (e.g. walls, floors and ceilings), wires, cables and pipes. Background of the invention A number of textile products have been described for applications including bedding,. apparel, hygiene and toys in which microencapsulated thermochromic pigments are incorporated 15 into synthetic fibres as a dispersed phase (e.g. US patent 6,444,313 and US patent application 2003/0087566), or as a coating on the surfaces of the fibres using a binding medium (e.g. US patent 4,681,791). Thermochromic yarns, fabrics and garments are also disclosed in Japanese patent publications 59144613 and 4756267. Japanese patent publication 48044522 discloses composite fibres containing cholesteric liquid crystals. 20 US patent application 2008/0279253 discloses thermochromic garments to track body temperature regulation of patients and children for use by clinicians, parents and caregivers. The garment contains at least two thermochromic dyes or colourants, each being sensitive to a different temperature range. This provides a facility to identify whether a body is overheating or is too cool, or to ascertain whether a heating or cooling device is working sufficiently. Described 25 embodiments include the addition of mincroencapsulated leuco dyes into polymer fibrous webs by melt -blowing techniques. Another garment incorporating thermochromic pigments or thermochromic strip thermometers is described in US patent application 2009/00467760. The garment is proposed as a means of providing early detection and prevention of cold exposure to skin surfaces, or venous insufficiencies.
    WO 2013/131120 PCT/AU2012/000916 2 There have been a range of disclosures of medical or clinical applications for thermochromic liquid crystalline materials. In US patent 5,806,528, such materials are proposed as temperature indicators for fluids intravenously delivered to patients, to ensure that they are not at a temperature that is either uncomfortable or harmful to a patient. US patent application 5 2011/0028804 discloses a topical product that exhibits thermochromic behaviour when applied to the skin. The product is intended to be used for diagnosing the onset of conditions such as necrosis and decubitus ulcers in the skin of a patient, by identifying increased temperatures due to inflammation present in the early stages of ulcer formation. The topical product is described as being a liquid and is possibly applied as a spray. The patent application suggests the use of either 10 liquid crystalline mixtures or leuco dyes as a thermochromic component, dispersed into a body lotion or soap. US patent 5,181,905 discloses a wound dressing containing a thermochromic indicator for monitoring the condition of an underlying wound while the dressing is being worn. The thermochromic component is in the form of a temperature sensitive liquid crystal tape that has a 15 plurality of labelled boxes containing liquid crystalline mixtures tuned to appear coloured at different temperatures. Temperature determination is dependent on which box or boxes appear coloured while the dressing is being worn. US patent 4,433,637 describes a thin flexible sheet coated with liquid crystals, microencapsulated or otherwise, over a black backing as a means for measuring temperatures of 20 the surface of the skin. It is an object of the invention, at least in one or more aspects, to provide a novel and useful composite sensor fibre. Reference to any prior art in the specification is not, and should not be taken as, an acknowledgment or any form of suggestion that this prior art forms part of the common general 25 knowledge in Australia or any other jurisdiction or that this prior art could reasonably be expected to be ascertained, understood and regarded as relevant by a person skilled in the art.
    WO 2013/131120 PCT/AU2012/000916 3 Summary of the invention In a first aspect, the invention provides a novel structure of composite sensor fibre that may be usefully adapted as a composite thermochromic fibre. In this aspect, the invention also provides a method of forming the composite sensor fibre. 5 A second aspect of the invention entails a realisation that a fabric or non-woven formed from composite thermochromic fibres may be effectively incorporated in a dressing by which the condition of an underlying wound may be monitored without the use of external electronics or temperature probes. In this aspect, the invention also provides a method of monitoring a wound. In its first aspect, the invention provides a composite sensor fibre comprising a 10 filamentary core and an -outer layer encapsulating an intermediate sensor layer of a detectably thermoresponsive material. In this aspect, the invention further provides a method of making the composite sensor fibre comprising continuously delivering the filamentary core from a supply thereof and co extruding the thermoresponsive material about the core and the outer layer about the 15 thermoresponsive material at a temperature that facilitates the coextrusion but at which the core remains substantially solid and the outer layer does not substantially inhibit delivery of the thermoresponsive material. In an embodiment, the thermoresponsive material is a thermochromic material. Preferred thermochromic materials comprise thermochromic liquid crystalline materials, which may 20 typically be mixtures of liquid crystalline compounds in order to achieve a predetermined temperature indication accuracy over a predetermined temperature range. For thermochromic applications, the outer layer is generally transparent and the filamentary core is preferably configured to provide a contrast for facilitating the observation of temperature or temperature gradient changes in the thermochromic material, for example specific 25 colour appearances or gradients. Advantageous embodiments of the filamentary core exhibit a generally circular or generally trilobal cross section.
    WO 2013/131120 PCT/AU2012/000916 4 The first aspect of the invention extends to materials, e.g. but not limited to fabrics, non wovens and other fibrous materials, formed from or incorporating the composite sensor fibres of the invention. In the second aspect of the invention, there is provided a dressing that includes a fabric 5 having a matrix of thermochromic composite sensor fibres according to the first aspect of the invention, which fibres indicate localised body temperature changes adjacent the dressing by visibly exhibiting a change in colour or colour gradient. In the second aspect, the invention further provides a method of monitoring a wound comprising applying to the wound a dressing that includes a fabric having a matrix of 10 thermochromic composite sensor fibres according to the first aspect of the invention, which fibres indicate localised body temperature changes adjacent the dressing by visibly exhibiting a change in colour or colour gradient. The thermochromic fibres of the second aspect of the invention are preferably composite sensor fibres according to the first aspect in which the intermediate sensor layer contains 15 thermochromic material. For this application, the thermochromic material is preferably but not exclusively a mixture of liquid crystalline materials selected so that the observed colour or colour gradient changes provide an indication of the temperature of the adjacent environment within a predetermined accuracy over a defined temperature range. A suitable temperature range for wound monitoring may be 25" to 45*C but is not limited to this range. Suitable liquid 20 crystalline materials are cholesterol based compounds but may also be non-sterol in nature. As used herein, except where the context requires otherwise, the term "comprise" and variations of the term, such as "comprising", "comprises" and "comprised", are not intended to exclude further additives, components, integers or steps. Further aspects of the present invention and further embodiments of the aspects described 25 in the preceding paragraphs will become apparent from the following description, given by way of example and with reference to the accompanying drawings.
    WO 2013/131120 PCT/AU2012/000916 5 Brief description of the drawings The invention will now be further described, by way of example only, with reference to the accompanying drawings, in which: Figure 1 is a diagram of alternative idealised cross-sections of embodiments of composite 5 sensor fibre according to the first aspect of the invention; Figure 2 is a schematic of a suitable melt extrusion arrangement for forming composite sensor fibres such as those depicted in Figure 1; Figure 3 is a simplified cross-section of the die of the arrangement illustrated in Figure 2; Figure 4 is a plot of the reflectance spectra in the visible range as a function of 10 temperature for composite sensor fibres incorporating a particular mixture of cholesterol based liquid crystalline materials; and Figure 5 depicts (by greyscale shading) the thermochromic response to the application of a warming human hand to a fabric knitted from composite thermochromic fibres similar to that having the response characteristic illustrated in Figure 4. 15 Detailed description of embodiments of the Invention Figure 1 shows two preferred but non-limiting alternative cross sections for composite sensor fibres 10 according to the invention. Each fibre comprises a solid filamentary core 12 and an outer layer 30 encapsulating an intermediate sensor layer 20 of a detectably thermoresponsive material. Outer layer 30 is of generally tubular configuration. In one case, the core is of solid 20 cylindrical form while in the other the core is symmetrically trilobal. Both illustrations are idealized: real fibres approximate these forms. A particularly useful form of the composite sensor fibre is one in which the intermediate sensor layer 20 comprises thermochromic material, the core 12 provides a contrast for facilitating visibility of colour and/or colour gradient changes in the intermediate layer, and the 25 outer layer 30 is substantially transparent for viewing those colour or colour gradient changes. In embodiments of particular interest, the core 12 is a polymer containing black or dark pigment and the intermediate sensor layer 20 is a thermochromic liquid crystalline mixture. Such a fibre WO 2013/131120 PCT/AU2012/000916 6 reversibly changes colour through the full visible spectrum from red to blue as the temperature is increased through a working temperature range determined by the composition of the liquid crystalline mixture. Consistent with the general behaviour of unencapsulated thermochromic liquid crystalline mixtures, the fibre exhibits clear and reversible thermochromic behaviour. 5 The filamentary core 12 may be a monofilament or multifilament fibre, preferably made from a high temperature stability polymer or metal in view of the process of formation as described below. A particularly suitable such polymer is polyether ether ketone (PEEK) containing black or dark pigment. The core preferably though not essentially provides mechanical support for the further layers of the fibre. 10 In the case where the intermediate layer 20 is a thermochromic material, the trilobal shape of Figure 1 is preferred because this maximises the contrast background when viewed from any given angle without compromising the flowability of the material in the later described' coextrusion process for formation of the composite fibre. In this case, the intermediate layer 20 is divided into three longitudinal segments and the core 12 contacts the outer layer 30 at the tip of 15 each lobe, and is thereby anchored to the outer layer. In the simplest case, however, the core 12 may be generally circular in cross-section. In other embodiments, it may be, for example, linear or elongated with flat sides, or elliptical, or, in more complex shapes, quadralobal, hexalobal, etc. The intermediate sensor layer may in general be a liquid, a low melting point wax, or a 20 solid at room temperature. The preferred liquid crystalline mixtures are waxy or oily at room temperature, 20*C. A preferred process for forming the composite sensor fibre of the invention, in particular the preferred composite thermochromic fibre, is a melt coextrusion process. A schematic of the setup for this process is provided in Figure 2. The three components are fed simultaneously into 25 a die 40 configured for "wire strand coating" coextrusion. A simplified cross-sectional profile of a successful die configuration is shown in Figure 3. A pre-prepared high melting temperature polymer fibre/filament 12' containing black pigment (for example PEEK containing carbon black pigment) is threaded vertically through the WO 2013/131120 PCT/AU2012/000916 7 die 40 via feed point 42 and drawn through from a supply spool 51 at a steady rate as controlled by a downstream godet system 50. At the same time a pre-prepared thermochromic liquid crystalline mixture 20' is fed at a steady rate into feed point 44 from a liquid pump 52, and an appropriate polymer 30' is fed at a steady rate as a melt into feed point 46 by a melt extruder 54. 5 An example of a suitable polymer for the outer transparent layer is polypropylene, which has a melting temperature substantially lower than the inner core material, for example, below 200*C, and was found to perform very well in the illustrated setup. PEEK has a melting temperature of 343*C. The liquid pump 52 is maintained at a temperature to enable the liquid crystal mixture to 10 flow sufficiently, for example in the range 40-80*C. The liquid crystalline and polymer layers are coated onto the core fibre 12' as it passes through the die by co-extrusion of the thermochromic liquid crystalline material 20' about the core 12' and of the outer layer 30' about the liquid crystalline material 20'. On exiting the die at 48 the outer polymer layer solidifies and traps the thermochromic intermediate layer between the 15 core fibre and itself. The resultant composite fibre 10 is then passed through the godet system 50 (which may or may not involve further elongation) and is collected at the winder onto a bobbin 56. The PEEK fibre/filament 12' is drawn/pulled through by the godet system. The liquid crystalline material and polymer melt are simultaneously fed into the die at rates dependent on 20 the throughput speed of the PEEK fibre and the desired loadings. The rate of release of the liquid crystalline material is controlled by the liquid pump 52. The composite sensor fibre formed typically has a diameter in the range 5 to 300 micrometers, preferably 30 to 300 micrometres, most preferably 60 to 300 micrometres, but not limited to these ranges,.depending on the relative amounts of each component in the cross-sectional profile. 25 During the above process conditions are maintained to ensure a substantially even coating of both components onto the outside of the PEEK fibre. If the die is too cool for example, the polypropylene melt blocks the progress of liquid crystalline material out of the die between the two polymer layers. Thus the temperature of the die is set in a range that facilitates the co extrusion but at which the core remains substantially solid (and therefore typically suffers little WO 2013/131120 PCT/AU2012/000916 8 or no distortion), and the outer layer does not inhibit delivery of the liquid crystalline material. A suitable temperature range that meets these requirements for the described feed components is found to be above the melting temperature of the outer material but below the melting temperature of the inner core material, for example in the range 170*C to 200 0 C. 5 Applications of composite fibres according to the first aspect of the invention include temperature indicator devices for thermal mapping of both engineering surfaces, for example building surfaces (walls, floors and ceilings), wires, cables and pipes, and human body surfaces. A particularly useful application of the illustrated composite fibre, in accordance with the second aspect of the invention, is a wound dressing. In one embodiment, the composite fibre 10 may be 10 woven or knitted into a tubular wound dressing of varying diameter, e.g. between 2mm and 10cm. For this application the thermochromic material of the intermediate sensor layer 20 is tuned to have a working temperature anywhere within the "pathological" temperature range 25 45*C. In more specialist applications, e.g. frostbite patients, the working temperature would be suitably adapted. As a wound dressing, the fibre enables clinicians and patients themselves to 15 monitor, observe or map the temperature distribution across and around wound beds, especially chronic wounds such as leg ulcers, pressure ulcers and diabetic food ulcers, while the dressing is being worn. This type of system is advantageous in that it does not rely on the use of any electronic equipment or probes, which can be invasive, expensive and otherwise impractical. Temperature indication can be achieved by comparing the localised colour observed within the 20 thermochromic fibres with a calibrated colour temperature chart. Absolute temperatures can be recorded as well as temperature differences or gradients between different areas of a wound bed and undamaged surrounding tissue. The observed colour or colour gradient should ideally give an accurate indication of the temperature of the surrounding environment within 0.1 and 0.5*C over a defined pathological temperature range, e.g. the aforementioned 25 0 C to 45*C, or a more 25 focused range e.g. 27-37*C or 33-37*C. Temperature monitoring of wounds can aid in the early detection of problems such as harmful inflammation and infection (typically accompanied by a local increase in temperature), or tissue necrosis and interruptions of blood supply to tissue (typically accompanied by a local decrease in temperature). Early detection of developing problems can lead to more relevant 30 treatment of wounds and therefore faster wound closure.
    WO 2013/131120 PCT/AU2012/000916 9 Other applications for thermochromic fibrous material include garments such as stockings or socks for the temperature monitoring of undamaged skin deemed to be at risk of developing a chronic wound such as a venous leg ulcer, with the hope that the wound formation may be prevented altogether in some cases. 5 By careful selection of a liquid crystalline mixture, the material appears red at the lower range of its working temperature range and the colour shifts through the full visible spectrum (red to yellow to green to blue) as the temperature increases. The behaviour is completely reversible. Liquid crystalline mixtures that have been found to be satisfactory are mixtures of 10 cholesterol based compounds including cholesteryl oleyl carbonate (COC), cholesteryl nonanoate (CN) and cholesteryl 2, 4-dichlorobenzoate (CD). Acceptable mixtures include: i 50% COC, 40%CN, 10% CD ii 40% COC, 40% CN, 20% CD iii 30% COC, 40% CN, 30% CD 15 Other relevant cholesterol based derivatives include but are not limited to cholesteryl benzoate, cholesteryl propionate, cholesteryl oleate, and cholesteryl chloride. The mixture can be prepared by weighing two or more cholesterol based derivatives into a glass vessel and heating to 90-1 10*C with mixing until all components melt and combine to form a homogenous clear liquid. The resultant mixture develops a thick and oily consistency when cooled to room 20 temperature. The compounds chosen and their relative amounts determine the working temperature range of the thermochromic mixture. Other suitable mixtures include both cholesterol based and non sterol based compounds. It has been established that these liquid crystalline mixtures are not dramatically changed, in respect to their thermochromic responses, by their passage through the die and resultant 25 trapping between the PEEK and polypropylene polymer layers. Figure 4 shows how the reflectance spectra in the visible range shifts from the red end of the spectrum to the blue as the temperature is increased for the liquid crystalline mixture (ii) WO 2013/131120 PCT/AU2012/000916 10 above. The behaviour has been found to compare well to that of the unincorporated mixture and is reversible. Composite thermochromic fibre comprising a PEEK core, liquid crystalline mixture (ii) and a polypropylene outer layer was knitted into a tubular fabric dressing of varying diameters 5 from 2mm to 10cm. Figure 5 shows the fabric 100, and depicts (by greyscale shading) the thermochromic response'to the application of a warming human hand to the fabric.
    权利要求:
    Claims (26)
    [1] 1. A composite sensor fibre comprising a filamentary core and an outer. layer encapsulating an intermediate sensor layer of a detectably thermoresponsive material.
    [2] 2. A composite sensor fibre according to claim 1 wherein the thermoresponsive 5 material is a thermochromic material.
    [3] 3. A composite sensor fibre according to claim 1 wherein the thermoresponsive material is a thermochromic liquid crystalline material.
    [4] 4. A composite sensor fibre according to claim 3 wherein the thermoresponsive material is a mixture of liquid crystalline compounds selected to achieve a predetermined 10 temperature indication accuracy over a predetermined temperature range.
    [5] 5. A composite sensor fibre according to claim 2, 3 or 4 wherein the outer layer is transparent and the filamentary core is configured to provide a contrast for facilitating the observation of temperature or temperature gradient changes in the thermochromic material.
    [6] 6. A composite sensor fibre according to claim 5 wherein the temperature or 15 temperature gradient changes comprise changes in colour or colour gradient.
    [7] 7. A composite sensor fibre according to claim 5 or 6 wherein the filamentary core is of a cross-section selected from generally circular and generally trilobal sections.
    [8] 8. A composite sensor fibre according to any one of claims 1 to 7 wherein the outer layer has a melting temperature substantially below that of the filamentary core. 20
    [9] 9. A composite sensor fibre according to any one of claims I to 8 wherein the filamentary core is a monofilament or multifilament fibre.
    [10] 10. A composite sensor fibre according to any one of claims 1 to 9 wherein the filamentary core is polyester ether ketone (PEEK) containing black or otherwise dark pigment.
    [11] 11. A composite sensor fibre according to any one of claims 1 to 10 of a diameter in 25 the range 5 to 300 micrometres, preferably 30 to 300 micrometres. WO 2013/131120 PCT/AU2012/000916 12
    [12] 12. A fibrous material formed from or incorporating composite sensor fibres according to any one of claims I to 11.
    [13] 13. A fibrous material according to claim 12 comprising a fabric.
    [14] 14. A clothing item that includes fibrous material according to claims 12 or 13. 5
    [15] 15. A fibrous material according to claim 12 comprising a non-woven.
    [16] 16. A method of making a composite sensor fibre according to any one of claims I to 11 comprising continuously delivering the filamentary core from a supply thereof and co extruding the thermoresponsive material about the core and the outer layer about the thermoresponsive material at a temperature that facilitates the coextrusion but at which the core 10 remains substantially solid and the outer layer does not substantially inhibit delivery of the thermoresponsive material.
    [17] 17. A method according to claim 16 wherein the thermoreponsive material is a mixture of liquid crystalline compounds selected to achieve a predetermined temperature indication accuracy over a predetermined temperature range, which mixture is waxy or oily at 15 about 20*C.
    [18] 18. A method according to claim 17 wherein the mixture of liquid crystalline compounds is fed by a pump at an elevated temperature selected to enable the mixture to flow sufficiently.
    [19] 19. A dressing that includes a fabric having a matrix of thermochromic composite 20 sensor fibres according to any one of claims I to 11, which fibres indicate localised body temperature changes adjacent the dressing by visibly exhibiting a change in colour or colour gradient.
    [20] 20. A dressing according to claim 19 wherein the composite sensor fibres are selected whereby localised body temperature changes adjacent to the dressing within the range 25*C to 25 45*C are visibly exhibited by a change in colour or colour gradient. WO 2013/131120 PCT/AU2012/000916 13
    [21] 21. A dressing according to claim 20 wherein the thermoresponsive material of the composite sensor fibres is a mixture of liquid crystalline compounds selected to achieve a predetermined temperature indication accuracy within the temperature range 25*C to 45*C.
    [22] 22. A dressing according to claim 21 wherein said mixture of liquid crystalline 5 compounds is a mixture of cholesterol based compounds.
    [23] 23. A method of monitoring a wound comprising applying to the wound a dressing that includes a fabric having a matrix of thermochromic composite sensor fibres according to any one of claims 1 to 11, which fibres indicate localised body temperature changes adjacent the dressing by visibly exhibiting a change in colour or colour gradient. 10
    [24] 24. A method according to claim 23 wherein the composite sensor fibres of the fabric are selected whereby localised body temperature changes adjacent to the dressing within the range 25*C to 45*C are visibly exhibited by a change in colour or colour gradient.
    [25] 25. A method according to claim 24 wherein the thermoresponsive material of the composite sensor fibres is a mixture of liquid crystalline compounds selected to achieve a 1-5 predetermined temperature indication accuracy within the temperature range 25"C to 45*C.
    [26] 26. A method according to claim 25 wherein said mixture of liquid crystalline compounds is a mixture of cholesterol based compounds. WO 2013/131120 PCT/AU2012/000916 14 AMENDED CLAIMS received by the International Bureau on 25 June 2013 1. A composite sensor fibre comprising a filamentary core and an outer layer encapsulating an intermediate sensor layer of a detectably thermochromic liquid crystalline material, wherein the outer layer is transparent and the filamentary core is configured to provide 5 a contrast for facilitating the observation of temperature or temperature gradient changes in the thermochromic material. 2. A composite sensor fibre according to claim 1 wherein the thermochromic liquid crystalline material is a mixture of liquid crystalline compounds selected to achieve a predetermined temperature indication accuracy over a predetermined temperature range. 10 3. A composite sensor fibre according to claim I or 2 wherein the temperature or temperature gradient changes comprise changes in colour or colour gradient. 4. A composite sensor fibre according to claim 1, 2 or 3 wherein the filamentary core is of a cross-section selected from generally circular and generally trilobal sections. 5. A composite sensor fibre according to any one of claims I to 4 wherein the outer 15 layer has a melting temperature substantially below that of the filamentary core. 6. A composite sensor fibre according to any one of claims 1 to 5 wherein the filamentary core is a monofilament or multifilament fibre. 7. A composite sensor fibre according to any one of claims I to 6 wherein the filamentary core is polyester ether ketone (PEEK) containing black or otherwise dark pigment. 20 8. A composite sensor fibre according to any one of claims 1 to 7 of a diameter in the range 5 to 300 micrometres, preferably 30 to 300 micrometres. 9. A fibrous material formed from or incorporating composite sensor fibres according to any one of claims 1 to 8. 10. A fibrous material according to claim 9 comprising a fabric. 25 11. A clothing item that includes fibrous material according to claims 9 or 10. 12. A fibrous material according to claim 9 comprising a non-woven. WO 2013/131120 PCT/AU2012/000916 15 13. A method of making a composite sensor fibre according to any one of claims I to 8 comprising continuously delivering the filamentary core as a solid from a supply thereof and co-extruding the thermochromic liquid crystalline material about the core and the outer layer about the thermochromic liquid crystalline material at a temperature that facilitates the s coextrusion but at which the core remains substantially solid and the outer layer does not substantially inhibit delivery of the thermochromic liquid crystalline material. 14. A method according to claim 13 wherein the thermochromic liquid crystalline material is a mixture of liquid crystalline compounds selected to achieve a predetermined temperature indication accuracy over a predetermined temperature range, which mixture is waxy 10 or oily at about 20'C. 15. A method according to claim 14 wherein the mixture of liquid crystalline compounds is fed by a pump at an elevated temperature selected to enable the mixture to flow sufficiently. 16. A dressing that includes a fabric having a matrix of thermochromic composite 15 sensor fibres according to any one of claims 1 to 8, which fibres indicate localised body temperature changes adjacent the dressing by visibly exhibiting a change in colour or colour gradient. 17. A dressing according to claim 16 wherein the composite sensor fibres are selected whereby localised body temperature changes adjacent to the dressing within the range 25'C to 20 45'C are visibly exhibited by a change in colour or colour gradient. 18. A dressing according to claim 17 wherein the thermochromic liquid crystalline material of the composite sensor fibres is a mixture of liquid crystalline compounds selected to achieve a predetermined temperature indication accuracy within the temperature range 25*C to 45 0 C. 25 19. A dressing according to claim 18 wherein said mixture of liquid crystalline compounds is a mixture of cholesterol based compounds. 20. A method of monitoring a wound comprising applying to the wound a dressing that includes a fabric having a matrix of thermochromic composite sensor fibres according to any one of claims 1 to g, which fibres indicate localised body temperature changes adjacent the 30 dressing by visibly exhibiting a change in colour or colour gradient. WO 2013/131120 PCT/AU2012/000916 16 21. A method according to claim 20 wherein the composite sensor fibres of the fabric are selected whereby localised body temperature changes adjacent to the dressing within the range 25*C to 45"C are visibly exhibited by a change in colour or colour gradient. 22. A method according to claim 21 wherein the thermochromic liquid crystalline 5 material of the composite sensor fibres is a mixture of liquid crystalline compounds selected to achieve a predetermined temperature indication accuracy within the temperature range 25*C to 45 0 C. 23. A method according to claim 22 wherein said mixture of liquid crystalline compounds is a mixture of cholesterol based compounds.
    类似技术:
    公开号 | 公开日 | 专利标题
    AU2012372758B2|2016-08-11|Composite sensor fibres and applications therefor
    EP2417430B1|2017-06-14|A temperature sensor for body temperature measurement
    US8029190B2|2011-10-04|Method and articles for sensing relative temperature
    US20100268112A1|2010-10-21|Thermocromatic patch for monitoring/detecting body temperature
    DE102008013052A1|2008-09-18|Temperature measuring tissue
    DE112007003135T5|2009-12-24|Thermomastographic device for the differential diagnosis of breast cancer in women and the application of the thermomastographic device
    WO2009015901A1|2009-02-05|Cooling device
    Van Der Werff et al.2013|Thermochromic composite fibres containing liquid crystals formed via melt extrusion
    US8162862B2|2012-04-24|Dressing material
    Soukup et al.2014|Textile based temperature and humidity sensor elements for healthcare applications
    US10660571B2|2020-05-26|Thermochromic fabrics utilizing cholesteric liquid crystal material
    NZ630024B2|2015-09-01|Composite sensor fibres and applications therefor
    Haghighat et al.2019|Thermal performance of electrospun core-shell phase change fibrous layers at simulated body conditions
    GB2531612A|2016-04-27|Colour-changing bandage for indicating wound infection
    Decaens et al.2018|Specific testing for smart textiles
    Wang et al.2017|12‐3: Smart Fabrics Functionalized by Liquid Crystals
    Legerská et al.2013|Thermal analysis of the polyester profiled fiber
    Wang et al.2017|Developing Liquid‐Crystal Functionalized Fabrics for Wearable Sensors
    Van der Werff2012|Thermochromic composite fibres for thermal mapping in the physiological temperature range
    US20190274902A1|2019-09-12|Integrated temperature sensitive wound dressing device
    US20130131540A1|2013-05-23|Thermocromatic patch for monitoring/detecting body temperature
    WO2013177112A1|2013-11-28|Thermocromatic patch for monitoring/detecting body temperature
    GB2581588A|2020-08-26|Fibre
    JP2019181017A|2019-10-24|Composite laminated body
    Bakan et al.1984|Liquid crystal microcapsule medical device used for thermographic examination of the human female breast
    同族专利:
    公开号 | 公开日
    CN104246459B|2018-08-03|
    US20150088027A1|2015-03-26|
    WO2013131120A1|2013-09-12|
    NZ630024A|2015-05-29|
    EP2823271B1|2016-10-19|
    EP2823271A4|2015-11-25|
    US9810587B2|2017-11-07|
    JP2015511003A|2015-04-13|
    EP2823271A1|2015-01-14|
    CN104246459A|2014-12-24|
    AU2012372758B2|2016-08-11|
    引用文献:
    公开号 | 申请日 | 公开日 | 申请人 | 专利标题
    US3651695A|1970-04-24|1972-03-28|Environmental Metrology Corp|Colorimetric temperature sensor|
    JPS5012483B2|1971-10-11|1975-05-12|||
    US4433637A|1979-06-04|1984-02-28|Vectra International Corporation|Microencapsulated cholesteric liquid crystal temperature measuring device for determining the temperature of non-planar or planar surfaces|
    US4301023A|1980-06-23|1981-11-17|American Thermometer Co., Inc.|Cholesteric compositions|
    IT8220097D0|1982-03-11|1982-03-11|Cinzia Ruggeri|FABRIC.|
    JPS59144613A|1983-02-04|1984-08-18|Fujii Keori Kk|Yarn for clothing and its preparation|
    CA1240883A|1985-01-30|1988-08-23|Norikazu Nakasuji|Thermochromic textile material|
    US4642250A|1986-01-13|1987-02-10|Donald Spector|Fabrics and garments formed thereby having thermally-sensitive chromatic properties|
    JP2824130B2|1989-07-25|1998-11-11|株式会社クラレ|Thermochromic composite fiber|
    CA2029172C|1989-11-28|2002-04-02|Eric Flam|Dressing including an indicator|
    US5181905A|1989-11-28|1993-01-26|Eric Flam|Method of monitoring the condition of the skin or wound|
    US5361320A|1993-02-19|1994-11-01|University Of Colorado Foundation|Liquid crystal fiber waveguide|
    US5806528A|1995-10-05|1998-09-15|Urosurge, Inc.|In-line temperature sensing devices, systems and methods|
    US6004691A|1995-10-30|1999-12-21|Eshraghi; Ray R.|Fibrous battery cells|
    WO2000000004A1|1998-06-26|2000-01-06|Medical Indicators, Inc.|Liquid crystal thermometer|
    US6444313B1|2001-01-05|2002-09-03|The Pilot Ink Co., Ltd.|Thermochromic acrylic synthetic fiber, its processed article, and process for producing thermochromic acrylic synthetic fiber|
    EP1446519A4|2001-10-23|2005-09-14|Polymer Group Inc|Meltspun thermochromic fabrics|
    US7354478B2|2004-02-20|2008-04-08|Certainteed Corporation|Insulation product having bicomponent fiber facing layer and method of manufacturing the same|
    GB0411349D0|2004-05-21|2004-06-23|Koninkl Philips Electronics Nv|A filament of fibre|
    JP4756267B2|2006-02-06|2011-08-24|学校法人慶應義塾|Threads and fabrics using discolorable fibers|
    US8728373B2|2007-03-20|2014-05-20|Albany International Corp.|Industrial fabric having a thermochromic sensor|
    US8029190B2|2007-05-10|2011-10-04|Kimberly-Clark Worldwide, Inc.|Method and articles for sensing relative temperature|
    US20090046760A1|2007-08-14|2009-02-19|John Peter Matheson|Thermochromic Temperature-Monitoring Clothing|
    US7976944B2|2009-01-02|2011-07-12|The Hong Kong Polytechnic University|Temperature-regulating fiber and a method of making the same|
    WO2011014552A1|2009-07-28|2011-02-03|Lisa Jernigan|Use of heat sensitive color changing formula to detect and prevent the onset of decubitus ulcers|
    US8257639B2|2009-09-22|2012-09-04|Kent State University|Method of making stimuli responsive liquid crystal-polymer composite fibers|
    US20110077527A1|2009-09-30|2011-03-31|Yang Seungrim|Self-cooling gel substrate for temperature differentiated imaging|
    CN202051689U|2011-03-23|2011-11-30|上海市同济医院|Anesthesia plane test strip|EP2958865B1|2013-02-24|2021-04-28|Esmaeil Banaei|Method of thermally drawing structured sheets|
    BR112015028905A2|2013-05-21|2017-07-25|Orpyx Medical Tech Inc|pressure data acquisition set and method of acquiring pressure data|
    CA2920664C|2013-08-09|2021-06-22|WestPoint Home LLC|Laundry process temperature indicators / markers and fabrics incorporating same|
    US20170325520A1|2014-11-25|2017-11-16|Cornell University|Thermochromic apparel for detecting physical exhaustion and process for preparation thereof|
    KR20160076784A|2014-12-23|2016-07-01|다이텍연구원|Process for coating polyketone yarn|
    DE102015207165A1|2015-04-21|2016-10-27|Robert Bosch Gmbh|A battery system and method for monitoring a temperature of a battery system|
    CN105078418B|2015-09-09|2017-06-30|南京理工大学|Skin temperature collection and imaging method based on flexible liquid crystal temperature sensor|
    EP3634506A4|2017-05-17|2021-03-10|UVIC Industry Partnerships Inc.|Wound covering for wound monitoring and therapeutic agent delivery|
    EP3697949A4|2017-10-18|2021-07-14|University of Central Florida Research Foundation, Inc.|Fibers having electrically conductive core and color-changing coating|
    GB2581512A|2019-02-21|2020-08-26|Theunseen Ltd|Fibre|
    GB2581782A|2019-02-21|2020-09-02|Theunseen Ltd|Polymer fibre|
    法律状态:
    2016-12-08| FGA| Letters patent sealed or granted (standard patent)|
    2021-03-04| MK14| Patent ceased section 143(a) (annual fees not paid) or expired|
    优先权:
    申请号 | 申请日 | 专利标题
    AU2012900852||2012-03-05||
    AU2012900852A|AU2012900852A0||2012-03-05|Composite sensor fibres and applications therefor|
    PCT/AU2012/000916|WO2013131120A1|2012-03-05|2012-08-02|Composite sensor fibres and applications therefor|
    AU2012372758A|AU2012372758B2|2012-03-05|2012-08-02|Composite sensor fibres and applications therefor|AU2012372758A| AU2012372758B2|2012-03-05|2012-08-02|Composite sensor fibres and applications therefor|
    [返回顶部]